Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The Brazilian civil construction showed in the last few years a large increase in technology, thus increasing the competitiveness in the labor market. In order to remain in compliance with the standard requirements, builders need to improve, both in workmanship as in materials used questions. The masonry had an important growth in the last few years, thus increasing the need to develop studies and constantly improve the National Standards. The compressive strength is the most important factor in structural masonry, than a study and deep knowledge of the subject is necessary for designers can accomplish the projects in the best possible manner. For the use of ceramic block, NBR 15812-1 recommends that the efficiency factor walls/prism that must be used is 0,70, but there is no standardized value for the efficiency factor prism/block, leaving only to designer the choice of this value. For the project to be well specified, with the components selected as best as possible, the efficiency factor prism block have decisive role, as thought the designer calculate the prism designer strength, he must specify the mean compressive strength of mortar as the characteristic compressive strength of blocks and, if necessary, grout. With the aid of the Building Construction Material Laboratory of the Federal University of Santa Maria, which provided its tests results of the years 2007 to 2014, a study was conducted to calculate the efficiency factor of prism/block in different strength ranges of the blocks. Following this study, analyzes were made to try to predict behavior of efficiency factor due to the compressive strength of the block and be able to get a usual value for the conditions of the tested components. Only ceramic hollow blocks with no grout were approached in this study because they were in a large amount, providing greater reliability to the results. / A Construção Civil no Brasil apresentou nos últimos anos um grande aumento na área tecnológica, aumentando com isso a competitividade no mercado de trabalho. Para poderem se manter atuais e cumprindo com os requisitos de normas, as empresas da área da construção necessitam se aprimorar, tanto no quesito mão de obra como no quesito dos materiais utilizados. O método construtivo de alvenaria estrutural obteve um crescimento muito importante nos últimos anos, aumentando assim a necessidade de se desenvolver estudos e melhorar cada vez mais as normas que regem tal método. A resistência à compressão é o fator mais importante na alvenaria estrutural, logo um estudo e conhecimento aprofundado do tema se faz necessário para os projetistas poderem conseguir realizar os projetos da melhor maneira possível. Para a utilização de blocos cerâmicos, a NBR 15812-1 preconiza que o fator de eficiência parede/prisma que se deve utilizar é de 0,70, porém, não existe um valor normatizado para o fator de eficiência prisma/bloco, deixando apenas para o projetista a escolha desse valor. Para o projeto ser bem especificado, com os componentes escolhidos da maneira mais condizente com o cenário, o fator de eficiência prisma/bloco têm função determinante, visto que apesar de o projetista calcular a resistência de projeto do prisma, ele precisa especificar a resistência à compressão média da argamassa como a resistência característica à compressão de blocos e, quando necessário, grautes. Com a ajuda do Laboratório de Materiais de Construção Civil da Universidade Federal de Santa Maria, que disponibilizou os seus ensaios dos anos de 2007 até 2014, foi realizado um estudo para se calcular o fator de eficiência/prisma bloco em diferentes faixas de resistência dos blocos. Após este estudo, foram feitas análises para tentar prever o comportamento do fator de eficiência frente à resistência à compressão dos blocos e poder se chegar em um valor usual para as condições dos componentes ensaiados. Apenas blocos cerâmicos de parede vazada e não grauteados foram abordados no estudo pois eram em uma quantidade maior, fornecendo uma maior confiabilidade aos resultados obtidos.

A alvenaria estrutural é um dos mais antigos sistemas construtivos existentes. Atualmente estruturas em alvenaria encontram uma vasta aplicação em construções residenciais, sobretudo em obras de interesse social. No entanto, ao contrário das estruturas de concreto, cujo comportamento durante exposição ao fogo e sua resistência residual tem estudos e resultados amplamente disseminados, pouco se sabe a respeito do comportamento de estruturas de alvenaria submetidas à ocorrência de sinistros dessa natureza. Com a intensificação das preocupações acerca da segurança das edificações e de seus usuários em situações de incêndio, faz-se cada vez mais imprescindível o conhecimento do comportamento dos sistemas empregados atualmente na construção civil perante a ação de altas temperaturas. Tendo isso em vista, o presente trabalho teve por objetivo a realização de uma análise dos danos e do comportamento apresentados por amostras de alvenaria com função estrutural ao serem expostas ao aquecimento excessivo. Foram avaliadas nesse estudo paredes de pequenas dimensões executadas com blocos estruturais cerâmicos. Visando simular condições mais próximas da realidade, foram restringidas, com o auxílio de macacos hidráulicos, as laterais das amostras, para que houvesse contenção da dilatação das mesmas. Com o intuito de verificar diferentes tipologias de alvenarias, foram utilizados três blocos distintos: de 14 cm de largura, com resistências de 7 e 10 MPa, e de 19 cm de largura, com 7 MPa de resistência à compressão. Também foram variadas as espessuras das juntas entre as unidades e a argamassa de assentamento das mesmas, a fim de compreender a importância desses fatores para o comportamento das amostras, e, por fim, foram ensaiadas amostras com revestimento na face exposta As miniparedes foram acopladas a um forno de resistências elétricas e submetidas a um aquecimento próximo à curva padrão determinada por norma, até a temperatura máxima de 950ºC, a qual foi mantida pelo período de 4 horas. Foram mensurados, além da temperatura dentro do forno, no interior da parede e na superfície das amostras, os deslocamentos transversais ocorridos durante o ensaio. Também se utilizaram transdutores de deslocamento para verificar a dilatação dos blocos e o esmagamento ou abertura das juntas. Imagens termográficas da face oposta ao aquecimento foram capturadas no decorrer da exposição. Ao final das análises, pôde-se inferir que as miniparedes ensaiadas apresentaram bom desempenho frente à ação das altas temperaturas, mantendo sua estanqueidade, isolamento térmico e resistência mecânica. A restrição lateral não ocasionou desplacamentos dos blocos, no entanto, pôde-se observar transferência de tensão para os mesmos quando utilizadas nas juntas argamassas pouco flexíveis. O deslocamento transversal apresentado pelas amostras indicou deflexão em direção ao forno durante o aquecimento, com posterior reversão do sentido. Tal deflexão foi atenuada pela redução da espessura das juntas, pelo uso de argamassas menos flexíveis e pelo aumento da resistência e largura dos blocos. As alvenarias de 19 cm de largura e, especialmente, as dotadas de revestimento apresentaram melhor desempenho térmico que as demais. / Structural masonry is one of the oldest existing building systems. Nowadays, masonry structures find a wide application in residential constructions, mainly in those with social interest. However, unlike concrete structures, whose behavior during fire exposure and its residual resistance have widely disseminated studies and results, there is a lack of knowledge about the behavior of masonry structures submitted to fire. Because of the spread of concerns about the safety of buildings and their users in fire situations, it becomes essential to know the behavior of the systems currently used in civil construction when exposed to high temperatures. With this in view, the present study intended to analyze the damage and the behavior of structural masonry samples exposed to heating. This study evaluated clay hollow-bricks small walls, and, in order to simulate real conditions, the boundaries of the samples were restrained, with the aid of hydraulic jacks, aiming to restrain the deformation. In order to verify different types of masonry, three different blocks were used: 14 cm wide, with nominal strength of 7 and 10 MPa, and 19 cm wide, with 7 MPa of compressive strength. The thicknesses of the joints and the mortar were also varied, in order to understand the importance of these factors in the behavior of the samples, and, finally, samples were tested with a mono-layer coating at the exposed face. The small walls were coupled to an electrical furnace and subjected to a heating approximately equal to the standard curve, up to the maximum temperature of 950ºC, which was maintained for 4 hours The deflections of the samples during the test were measured, beyond the temperature inside the furnace, in the center of wall and at the non-exposed surface. Clip gages were also used to verify the expansion of the blocks and the crushing or opening of the mortar joints. Thermographic images of the opposite face were captured during the testing. At the end of this research, it was possible to affirm that the walls had good behavior against the high temperatures, maintaining their integrity, thermal insulation and load-bearing capacity. The restriction of the boundaries did not cause the spalling of the blocks, however, it was possible to observe the stress transfer to them in samples with rigid joint mortar. The deflection of the samples increases towards the furnace during the heating, and, then, they show the phenomenon of “reverse bowing”, changing the direction of the displacements. Reducing the thickness and increasing the stiffness of the joint mortars, as well as the increase in block strength and width attenuated such deflection. The masonry 19 cm width and, specially, the ones with coating shows better thermal performance, comparing to the others.

A alvenaria estrutural é um dos mais antigos sistemas construtivos existentes. Atualmente estruturas em alvenaria encontram uma vasta aplicação em construções residenciais, sobretudo em obras de interesse social. No entanto, ao contrário das estruturas de concreto, cujo comportamento durante exposição ao fogo e sua resistência residual tem estudos e resultados amplamente disseminados, pouco se sabe a respeito do comportamento de estruturas de alvenaria submetidas à ocorrência de sinistros dessa natureza. Com a intensificação das preocupações acerca da segurança das edificações e de seus usuários em situações de incêndio, faz-se cada vez mais imprescindível o conhecimento do comportamento dos sistemas empregados atualmente na construção civil perante a ação de altas temperaturas. Tendo isso em vista, o presente trabalho teve por objetivo a realização de uma análise dos danos e do comportamento apresentados por amostras de alvenaria com função estrutural ao serem expostas ao aquecimento excessivo. Foram avaliadas nesse estudo paredes de pequenas dimensões executadas com blocos estruturais cerâmicos. Visando simular condições mais próximas da realidade, foram restringidas, com o auxílio de macacos hidráulicos, as laterais das amostras, para que houvesse contenção da dilatação das mesmas. Com o intuito de verificar diferentes tipologias de alvenarias, foram utilizados três blocos distintos: de 14 cm de largura, com resistências de 7 e 10 MPa, e de 19 cm de largura, com 7 MPa de resistência à compressão. Também foram variadas as espessuras das juntas entre as unidades e a argamassa de assentamento das mesmas, a fim de compreender a importância desses fatores para o comportamento das amostras, e, por fim, foram ensaiadas amostras com revestimento na face exposta As miniparedes foram acopladas a um forno de resistências elétricas e submetidas a um aquecimento próximo à curva padrão determinada por norma, até a temperatura máxima de 950ºC, a qual foi mantida pelo período de 4 horas. Foram mensurados, além da temperatura dentro do forno, no interior da parede e na superfície das amostras, os deslocamentos transversais ocorridos durante o ensaio. Também se utilizaram transdutores de deslocamento para verificar a dilatação dos blocos e o esmagamento ou abertura das juntas. Imagens termográficas da face oposta ao aquecimento foram capturadas no decorrer da exposição. Ao final das análises, pôde-se inferir que as miniparedes ensaiadas apresentaram bom desempenho frente à ação das altas temperaturas, mantendo sua estanqueidade, isolamento térmico e resistência mecânica. A restrição lateral não ocasionou desplacamentos dos blocos, no entanto, pôde-se observar transferência de tensão para os mesmos quando utilizadas nas juntas argamassas pouco flexíveis. O deslocamento transversal apresentado pelas amostras indicou deflexão em direção ao forno durante o aquecimento, com posterior reversão do sentido. Tal deflexão foi atenuada pela redução da espessura das juntas, pelo uso de argamassas menos flexíveis e pelo aumento da resistência e largura dos blocos. As alvenarias de 19 cm de largura e, especialmente, as dotadas de revestimento apresentaram melhor desempenho térmico que as demais. / Structural masonry is one of the oldest existing building systems. Nowadays, masonry structures find a wide application in residential constructions, mainly in those with social interest. However, unlike concrete structures, whose behavior during fire exposure and its residual resistance have widely disseminated studies and results, there is a lack of knowledge about the behavior of masonry structures submitted to fire. Because of the spread of concerns about the safety of buildings and their users in fire situations, it becomes essential to know the behavior of the systems currently used in civil construction when exposed to high temperatures. With this in view, the present study intended to analyze the damage and the behavior of structural masonry samples exposed to heating. This study evaluated clay hollow-bricks small walls, and, in order to simulate real conditions, the boundaries of the samples were restrained, with the aid of hydraulic jacks, aiming to restrain the deformation. In order to verify different types of masonry, three different blocks were used: 14 cm wide, with nominal strength of 7 and 10 MPa, and 19 cm wide, with 7 MPa of compressive strength. The thicknesses of the joints and the mortar were also varied, in order to understand the importance of these factors in the behavior of the samples, and, finally, samples were tested with a mono-layer coating at the exposed face. The small walls were coupled to an electrical furnace and subjected to a heating approximately equal to the standard curve, up to the maximum temperature of 950ºC, which was maintained for 4 hours The deflections of the samples during the test were measured, beyond the temperature inside the furnace, in the center of wall and at the non-exposed surface. Clip gages were also used to verify the expansion of the blocks and the crushing or opening of the mortar joints. Thermographic images of the opposite face were captured during the testing. At the end of this research, it was possible to affirm that the walls had good behavior against the high temperatures, maintaining their integrity, thermal insulation and load-bearing capacity. The restriction of the boundaries did not cause the spalling of the blocks, however, it was possible to observe the stress transfer to them in samples with rigid joint mortar. The deflection of the samples increases towards the furnace during the heating, and, then, they show the phenomenon of “reverse bowing”, changing the direction of the displacements. Reducing the thickness and increasing the stiffness of the joint mortars, as well as the increase in block strength and width attenuated such deflection. The masonry 19 cm width and, specially, the ones with coating shows better thermal performance, comparing to the others.

Made available in DSpace on 2017-07-21T20:43:45Z (GMT). No. of bitstreams: 1 Celia Regina Lucas Miara.pdf: 4383974 bytes, checksum: c59cd4d33b30dfef1ffbf4309bf08ab5 (MD5) Previous issue date: 2014-07-31 / The CONAMA 357/05 lays down the conditions and emission standards adopted for the control of effluent discharges in the receiving body. The sewage treatment systems seek to reduce the impact of the release of effluents into water bodies receiver, given this resolution. On the other hand, the sludge generated in sewage treatment plants has become a growing problem being considered as waste. This work aims to verify the feasibility of incorporating sludge sewage treatment plant (ETE) in the composition of traditional ceramics. For this sludge samples were collected at the ETE Verde SANEPAR in the city of Ponta Grossa-PR and clay Ceramic in the city of São Geronimo, Prudentópolis-PR. The sludge in the ETE Verde is subjected to a cleaning process, significantly reducing the concentration of pathogens in the waste. The sludge in the ETE Verde is subjected to a cleaning process, significantly reducing the concentration of pathogens in the waste. The process used is caleação, which promotes stabilization, thermal and chemical disinfection by the addition and mixing of the lime sludge to a percentage of 30% to 50% by dry weight sludge. For the characterization of silt and clay were analyzed X-ray diffraction, differential thermal and thermogravimetric analysis, fluorescence spectroscopy X-ray and particle size distribution were made. The compositions studied were made with additions of 5 to 50% by weight of the ceramic mass sludge. After mixing the sludge with clay, the samples were processed by uniaxial pressing and sintered at temperatures of 900°C, 1000°C e 1100°C. The sintered samples were characterized by measurements of bulk density, water absorption, apparent porosity, mechanical strength, X-ray diffraction and scanning electron microscopy. After verifying the feasibility of using sludge WWTP in ceramic body, these were processed by extrusion and sintered ceramics in the city of São Gerônimo, Prudentópolis-PR. The results showed that the addition of sludge to 15% of the mass of the clay meets all parameters recommended by current standards. / O CONAMA 357/05 determina as condições e padrões de emissão adotados para o controle de lançamentos de efluentes no corpo receptor. Os sistemas de tratamento de esgoto buscam diminuir o impacto do lançamento dos efluentes nos corpos d’água receptores, atendendo a esta Resolução. Por outro lado o lodo gerado nas estações de tratamento de esgoto tem se tornado um problema crescente sendo considerado como resíduo. Este trabalho busca verificar a viabilidade da incorporação do lodo de estação de tratamento de esgoto (ETE) na massa cerâmica para produção de blocos cerâmicos. Para isso, amostras de lodo foram coletadas na ETE Verde da SANEPAR no Município de Ponta Grossa-PR e de argila da Cerâmica São Gerônimo no Município de Prudentópolis-PR. O lodo na ETE Verde é submetido a um processo de higienização, reduzindo significativamente a concentração de patógenos no resíduo. O processo utilizado é a caleação, que promove a estabilização, desinfecção química e térmica através da adição e mistura da cal ao lodo numa porcentagem de 30% a 50% do peso seco de lodo. Para a caracterização do lodo e da argila foram realizadas análises de difração de raios X, análise térmica diferencial e termogravimétrica, espectroscopia de fluorescência de raios X e distribuição granulométrica. As composições estudadas foram feitas com adições de 5 a 50% em peso do lodo na massa cerâmica. Após a mistura do lodo com as argilas, as amostras foram conformadas por prensagem uniaxial e sinterizadas nas temperaturas de 900oC, 1000oC e 1100oC. As amostras sinterizadas foram caracterizadas por medidas de densidade aparente, absorção de água, porosidade aparente, resistência mecânica, difração de raios X e microscopia eletrônica de varredura. Após verificar a viabilidade do uso do lodo de ETE na massa cerâmica, essas foram conformadas por extrusão e sinterizadas na Cerâmica São Gerônimo no Município de Prudentópolis-PR. Os resultados mostraram que a adição do lodo até 15% da massa da argila atende a todos os parâmetros preconizados pelas normas vigentes.

Submitted by JOSIANE SANTOS DE OLIVEIRA (josianeso) on 2017-06-05T14:55:48Z No. of bitstreams: 1 Bruna Liliane Brenner_.pdf: 2490760 bytes, checksum: 60445eff926b3f639cef6a24f01ba88f (MD5) / Made available in DSpace on 2017-06-05T14:55:48Z (GMT). No. of bitstreams: 1 Bruna Liliane Brenner_.pdf: 2490760 bytes, checksum: 60445eff926b3f639cef6a24f01ba88f (MD5) Previous issue date: 2017-03-14 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / A necessidade da minimização dos impactos ambientais causados pelas mais diversas atividades humanas fica mais evidente a cada ano. Esta realidade leva pesquisadores a buscar alternativas para a otimização do uso de recursos naturais como a água e a energia. A energia proveniente de fontes hidrelétricas e termoelétricas é um recurso largamente consumido no Brasil, em grande parte pelas edificações. Diversas discussões a respeito da ampliação da eficiência energética nos edifícios levam, consequentemente, à questão do desempenho térmico. Em alternativa às soluções para ampliação do desempenho térmico com custo elevado, exigência de mão de obra especializada e acréscimo de tempo ao cronograma da obra em edificações, esta pesquisa teve como objetivo analisar o efeito do uso de isolantes térmicos no interior das cavidades dos blocos cerâmicos componentes da alvenaria. Esta apresenta-se como uma opção de isolamento facilitada em relação a outras técnicas conhecidas no mercado. O estudo foi realizado através de análises em protótipos de escala reduzida. Foram construídos quatro protótipos experimentais na cidade de São Leopoldo, RS sendo um deles utilizado como referência, representando a forma convencional de construção da alvenaria de blocos e os demais com as cavidades de seus blocos constituintes preenchidas com três diferentes tipos de isolantes térmicos: Esferas soltas de EPS, EPS de baixa densidade e perlita expandida. Nesta pesquisa foi utilizado EPS em forma de resíduo de uma empresa da região. Após a realização da pesquisa, coleta de dados e análise dos resultados verificou-se que os protótipos com isolamento apresentaram oscilações térmicas diárias minimamente menores em relação ao referência sendo as mais baixas obtidas pelo protótipo com preenchimento em EPS de baixa densidade, seguido pela perlita expandida e EPS em esferas. Apesar disto devido ao fato de estas terem sido muito pequenas não é possível afirmar que a utilização de isolantes térmicos no interior das cavidades de blocos cerâmicos constituintes da alvenaria pode trazer benefícios para o desempenho térmico em edificações em escala real. A utilização de isolantes em forma de resíduos apresentou-se como uma alternativa para reduzir custos com isolamento. / The need to minimize the environmental impacts caused by the most diverse human activities is more evident each year. This reality leads researchers to seek alternatives for optimizing the natural resources use such as water and energy. Energy from hydroelectric and thermoelectric sources is a widely used resource in Brazil, largely by buildings. Several discussions about increase energy efficiency in buildings therefore lead to the issue of thermal performance. As an alternative to solutions to increase the thermal performance with high cost, demand of specialized labor and increase of time to the work schedule in buildings, this research had as objective to analyze the effect of the use of thermal insulation inside the cavities of the ceramic blocks components of masonry. This is presented as an easier insulation option in relation to other techniques known in the market. The study was carried out through small scale prototype analyzes. Four experimental prototypes were constructed in São Leopoldo, RS, one of them being used as reference, representing the conventional construction form of the blocks masonry and the others with the cavities of its constituent blocks filled with three different thermal insulation types: EPS spheres, low density EPS and expanded perlite. In this research EPS was used in waste form from a company in the region. After the research, data collection and the results analysis, it was verified that the prototypes with insulation presented daily thermal oscillations minimally smaller in relation to the reference, being the lowest ones obtained by the prototype with low density EPS filling, followed by the expanded perlite and EPS spheres. Despite the fact that these diferences were very small, it is not possible to state that the use of thermal insulation inside the ceramic block cavities constituent of the masonry can bring benefits to the thermal performance in real buildings. The use of insulators in the form of residues was presented as an alternative to reduce costs with insulation.

Este trabalho apresenta uma análise comparativa com três tipos de ligações entre paredes de alvenaria estrutural submetidas a ações verticais. O primeiro tipo de ligação é feito através de amarração direta de paredes de alvenaria. O segundo por amarração indireta solidarizada por telas metálicas e o terceiro, também com amarração indireta, porém, enrijecida por grampos metálicos ancorados em furos grauteados. O estudo é baseado em resultados obtidos por meio de um programa experimental realizado no laboratório de estruturas da EESC-USP. Os modelos utilizados são paredes em formato H, com cinco fiadas, em escala reduzida 1:3, os quais foram propostos por Capuzzo Neto (2005). A partir da análise experimental é obtida a resistência ao cisalhamento da interface no plano vertical de ligação entre a parede central e o flange todos os modelos ensaiados. Conclui-se que os modelos com amarração direta possuem maiores resistências ao cisalhamento, o que reforça o fenômeno da interação de paredes submetidas a ações verticais, além de apresentarem forma de ruptura caracterizada como frágil. Os modelos com amarração indireta, tanto com telas quanto com grampos, possuem resistências ao cisalhamento aproximadamente igual a 60% da encontrada para amarração direta, contudo, apresentam ruptura dúctil, com destaque para a ligação com grampos. / This work presents a comparative analysis of three types of connections between structural masonry walls under vertical loads. The first type is a set of running bond interconnected masonry walls. The second connection is obtained by means of steel meshes and the third, also stack bond, is hardened by metallic staples anchored in grouted holes. The study is based on an experimental program carried out in the laboratory of structures of the EESC-USP. The test specimens are H shaped third scale walls, with five courses, as proposed by Capuzzo Neto (2005). The experimental analysis allows for the evaluation of the shear strength of the vertical interface between the central wall and the flanges. The study shows that the models with running bond provide the largest shear strength, which corroborates the phenomenon of the walls’ interaction under vertical loads, and a fragile failure type. Both the stack bond specimens present a shear strength of roughly 60% of the running bond type, with ductile failure, specially for the stapled connection.

Este trabalho apresenta uma análise comparativa com três tipos de ligações entre paredes de alvenaria estrutural submetidas a ações verticais. O primeiro tipo de ligação é feito através de amarração direta de paredes de alvenaria. O segundo por amarração indireta solidarizada por telas metálicas e o terceiro, também com amarração indireta, porém, enrijecida por grampos metálicos ancorados em furos grauteados. O estudo é baseado em resultados obtidos por meio de um programa experimental realizado no laboratório de estruturas da EESC-USP. Os modelos utilizados são paredes em formato H, com cinco fiadas, em escala reduzida 1:3, os quais foram propostos por Capuzzo Neto (2005). A partir da análise experimental é obtida a resistência ao cisalhamento da interface no plano vertical de ligação entre a parede central e o flange todos os modelos ensaiados. Conclui-se que os modelos com amarração direta possuem maiores resistências ao cisalhamento, o que reforça o fenômeno da interação de paredes submetidas a ações verticais, além de apresentarem forma de ruptura caracterizada como frágil. Os modelos com amarração indireta, tanto com telas quanto com grampos, possuem resistências ao cisalhamento aproximadamente igual a 60% da encontrada para amarração direta, contudo, apresentam ruptura dúctil, com destaque para a ligação com grampos. / This work presents a comparative analysis of three types of connections between structural masonry walls under vertical loads. The first type is a set of running bond interconnected masonry walls. The second connection is obtained by means of steel meshes and the third, also stack bond, is hardened by metallic staples anchored in grouted holes. The study is based on an experimental program carried out in the laboratory of structures of the EESC-USP. The test specimens are H shaped third scale walls, with five courses, as proposed by Capuzzo Neto (2005). The experimental analysis allows for the evaluation of the shear strength of the vertical interface between the central wall and the flanges. The study shows that the models with running bond provide the largest shear strength, which corroborates the phenomenon of the walls’ interaction under vertical loads, and a fragile failure type. Both the stack bond specimens present a shear strength of roughly 60% of the running bond type, with ductile failure, specially for the stapled connection.