Este estudo teve o objetivo de avaliar as propriedades físicas de resinas compostas restauradoras pré-aquecidas e de resinas fluidas com finalidade de cimentação de facetas de cerâmicas em comparação aos cimentos resinosos. Foram produzidos corpos de prova de duas marcas comerciais 3M ESPE e Ivoclar Vivadent, sendo: duas resinas restauradoras (Filtek Z250XT e Tetric N Ceram) nas condições: temperatura ambiente (RZ e RT), aquecidas à 45°C (RZ45 e RT45), aquecidas à 60°C (RZ60 e RT60); duas resinas fluidas (Filtek Z350 Flow e Tetric N Flow) denominadas FZ e FT e dois cimentos resinosos (Relyx Veneer e Variolink N) denominados CR e CV. Os grupos experimentais foram avaliados quanto à espessura de película por duas metodologias, resistência à flexão biaxial (RFB) e módulo de elasticidade (ME) executados em máquina de ensaio universal (modelo 5565, Instron Corp, Canton MA, EUA), microdureza Knoop feitas em microdurômetro (Shimadzu HMV-2, Tóquio, Japão) e diferença de cor (?E), razão de contraste e opalescência realizadas no espectrofotômetro CM-3770 (Konica Minolta, Japão). Os dados foram avaliados por análise de variância e teste de Tukey (p<0,05). As resinas restauradoras apresentaram películas com espessura maiores que 100 ?m, enquanto as resinas fluidas e os cimentos resinosos apresentaram valores menores que 50 ?m. Os grupos experimentais RZ, RZ45 e RZ60 apresentaram os maiores valores de KHN, RFB e ME. Os grupos RT, RT45, RT60, FT, CV e CR apresentaram os menores valores de RFB e semelhantes entre si. Para a KHN, os grupos RT, RT45, RT60, FZ e CR apresentaram valores intermediários e semelhantes entre si, e superiores aos grupos FT e CV. Os resultados de ?E mostraram valores acima de 2 para todos os grupos experimentais, com exceção do RZ60. Os maiores valores de ?E foram evidenciados nos grupos RT45 e RT60. A razão de contraste foi estatisticamente menor para o grupo CV e os maiores valores de opacidade foram encontrados nos grupos RZ, RZ45 e FZ. A opalescência foi superior nos grupos FZ, CR, FT e CV. Considerando as limitações do presente estudo, concluiu-se que os tratamentos térmicos não alteraram as propriedades mecânicas das resinas restauradoras e não promoveram uma redução da espessura de película que atenda aos requisitos da ISO4049. As resinas fluidas e os cimentos apresentaram espessura de película inferior à 50?m e propriedades mecânicas que atendem à normativa ISO4049. A opalescência maior foi encontrada nos cimentos resinosos e a diferença de cor e razão de contraste apresentaram resposta grupo dependente. / The objectives of this study were to evaluate the physical properties of preheated restorative resin composites and fluid resins with the purpose of cementation of ceramic veneers in comparison to resin cements. Specimens were prepared with two restorative resin composites (Filtek Z250XT and Tetric N Ceram), in the following conditions: room temperature (RZ; RT), heated at 45°C (RZ45; RT45), and heated at 60°C (RZ60; RT60). Two flowable resins (Filtek Z350 Flow and Tetric N Flow) named FZ and FT and two resin cements (Relyx Veneer and Variolink N), called CR and CV, were also used. The experimental groups were evaluated in regards to film thickness with two methodologies; biaxial flexure strength (BFS) and modulus of elasticity (ME) (model 5565, Instron Corp, Canton MA, USA); Knoop microhardness test (KMT) (Shimadzu HMV-2, Tokyo, Japan), color difference (?E), contrast ratio and opalescence test (CM-3770d, Konica Minolta, Japan). Data were assessed by ANOVA and a post-hoc Tukey test (p<0.05). The restorative resins presented film thickness larger than 50?m, whereas the flowable resins and resin cements showed inferior values. The experimental groups RZ, RZ45 and RZ60, revealed greater values of KHN, BFS and ME. The RT, RT45, RT60, FT, CV and CR groups showed lower values for BFS and similar to each other. For KHN the RT, RT45, RT60, FZ and CR groups exposed intermediate and similar values to each other, and superior values to FT and CV groups. Color difference (?E) results demonstrated results superior than 2 for all experimental groups, with the exception of RZ60 group. The greater values of ?E were shown in RT45 and RT60 groups. Contrast ratio was statistically lower for the CV group and the highest values of opacity were verified in RZ, RZ45 and FZ groups. Opalescence was superior in FZ, CR, FT and CV groups. Considering the limitations of this study, the results demonstrated that preheated treatments did not modify the mechanical properties of restorative resin composites and didn\'t reduce film thickness which attend to ISO4049 parameters. Flowable resins and cements obtained film thickness inferior to 50?m and biaxial flexure strength results that are presented by the ISO4049. The greater opalescence was shown in the resin cements, also color difference and contrast ratio revealed results that were group dependent.

Novas demandas de aplicação tem sido a principal motivação para a produção de materiais estruturais associando boas propriedades mecânicas e baixo custo de fabricação. A indústria aeroespacial vem desenvolvendo estudos com titânio e suas ligas, devido, a sua elevada resistência mecânica e baixa massa específica. Alguns estudos afirmam que, em temperaturas acima de 500°C as ligas de titânio possuem baixa resistência à oxidação restringindo a sua aplicabilidade. Localizada na parte inferior das turbinas em aviões comerciais, a liga Ti ?-21S tem mostrado bom desempenho em até 700°C com grande potencial para substituir alguns componentes, diminuindo os gastos com manutenção e aumentando a autonomia das turbinas a gás. Diante desse cenário, o objetivo deste trabalho foi desenvolvimento de revestimentos visando o aumento da resistência a oxidação na liga Ti ?-21S mantendo as suas características iniciais. O processo de revestimento foi feito em diferentes condições de temperatura × tempo via HAPC (CVD in situ). A faixa de temperatura analisada foi de 560 à 760°C entre 1 à 25h. A microestrutura de todos os coupons (não revestidos, revestidos e oxidados) foram caracterizados por difração de raios X (DRX) e microscopia eletrônica de varredura (MEV). A cinética de crescimento aparente da camada de revestimento foi feita medindo a espessura de revestimento nas condições analisadas e a cinética de oxidação foi feita através da variação de massa superficial dos coupons. Os resultados do DRX e MEV mostraram que os revestimentos produzidos foram monofásicos com composição química TiAl3. A cinética de crescimento entre 660 à 760°C apresentou energia de ativação de 108 kJ/mol e constante pré-exponencial de 1,21 × 10-3 cm²/s, esses resultados sugerem que a cinética de crescimento é controlada pela difusão dos átomos de alumínio no volume da liga Ti ?-21S formando a camada de TiAl3. Os coupons revestidos foram oxidados à 750 e 850°C por 100, 200 e 300h, os resultados da caracterização microestrutural mostrou que nos coupons revestidos foi formada uma camada de Al2O3 e a variação de massa superficial após 300h à 850°C foi de 0,60 mg/cm². Portanto, após a oxidação dos coupons revestidos, foi observado que o revestimento promoveu a formação de óxidos protetores como Al2O3 aumentando a resistência a oxidação da liga Ti ?-21S revestida. / New application demands have been the main motivation for the production of structural materials associating good mechanical properties and low manufacturing cost. The aerospace industry has been developing studies with titanium and its alloys, due to its high mechanical strength and low specific mass. Some studies report that, at temperatures above 500°C, titanium alloys have low oxidation resistance, restricting their applicability. Located at the bottom of turbines in commercial aircraft, the Ti ?-21S alloy has shown good performance up to 700°C with great potential to replace some components, reducing maintenance costs and increasing the autonomy of gas turbines. In view of this scenario, the objective of this work was the development of coatings aiming at increasing the resistance to oxidation in the Ti ?-21S alloy while maintaining its initial characteristics. The coating process was done at different temperature × time conditions via Pack Cementation (CVD in situ). The temperature range analyzed was 560 - 760°C between 1 - 25h. The microstructure of all coupons (uncoated, coated and oxidized) were characterized by XRD and SEM. The kinetics of apparent growth of the coating layer were made by measuring the coating thickness under the analyzed conditions and the oxidation kinetics was done by varying the surface mass of the coupons. The results of the DRX and MEV showed that the coatings produced were monophasic with TiAl3 chemical composition. The kinetics of growth between 660 - 760°C showed activation energy of 108 kJ/mol and pre-exponential constant of 1.21 × 10-3 cm²/s, these results suggest that the kinetics of growth is controlled by the diffusion of atoms of aluminum in the volume of the Ti ?-21S alloy forming the TiAl3 layer. The coated coupons were oxidized at 750 and 850°C for 100, 200 and 300h, the results of the microstructural characterization showed that in the coated coupons an Al2O3 layer was formed and the surface mass variation after 300h at 850°C was 0.60 mg/cm². Therefore, after oxidation of the coated coupons, it was observed that the coating promoted the formation of protective oxides like Al2O3 increasing the oxidation resistance of the coated Ti ?-21S alloy.

Gas hydrate is a naturally occurring crystalline compound formed by water molecules and encapsulated gas molecules. The interest in gas hydrate reflects scientific, energy and safety concerns - climate change, future energy resources and seafloor stability. Gas hydrates form in the pore space of sediments, under high pressure and low temperature conditions. This research focuses on the fundamental understanding of hydrate bearing sediments, with emphasis on mechanical behavior, thermal properties and lens formation. Load-induced cementation and decementation effects are explored with lightly cemented loose and dense soil specimens subjected to ko-loading; the small-strain stiffness evolution inferred from shear wave velocity measurement denounces stiffness loss prior to structural collapse upon loading. Systematic triaxial tests address the intermediate and large strain response of hydrate bearing sediments for different mean particle size, applied pressure and hydrate concentration in the pore space; hydrate concentration determines elastic stiffness and undrained strength when Shyd>45%. A unique sequence of particle-level and macro-scale experiments provide new insight into the role of interparticle contact area, coordination number and pore fluid on heat transfer in particulate materials. Micro-mechanisms and necessary boundary conditions are experimentally analyzed to gain an enhanced understanding of hydrate lens formation in sediments; high specific surface soils and tensile stress fields facilitate lens formation. Finally, a new instrumented high-pressure chamber is designed, constructed and field tested. It permits measuring the mechanical and electrical properties of methane hydrate bearing sediments recovered from pressure cores without losing in situ pressure (~20MPa).

Este estudo teve o objetivo de avaliar as propriedades físicas de resinas compostas restauradoras pré-aquecidas e de resinas fluidas com finalidade de cimentação de facetas de cerâmicas em comparação aos cimentos resinosos. Foram produzidos corpos de prova de duas marcas comerciais 3M ESPE e Ivoclar Vivadent, sendo: duas resinas restauradoras (Filtek Z250XT e Tetric N Ceram) nas condições: temperatura ambiente (RZ e RT), aquecidas à 45°C (RZ45 e RT45), aquecidas à 60°C (RZ60 e RT60); duas resinas fluidas (Filtek Z350 Flow e Tetric N Flow) denominadas FZ e FT e dois cimentos resinosos (Relyx Veneer e Variolink N) denominados CR e CV. Os grupos experimentais foram avaliados quanto à espessura de película por duas metodologias, resistência à flexão biaxial (RFB) e módulo de elasticidade (ME) executados em máquina de ensaio universal (modelo 5565, Instron Corp, Canton MA, EUA), microdureza Knoop feitas em microdurômetro (Shimadzu HMV-2, Tóquio, Japão) e diferença de cor (?E), razão de contraste e opalescência realizadas no espectrofotômetro CM-3770 (Konica Minolta, Japão). Os dados foram avaliados por análise de variância e teste de Tukey (p<0,05). As resinas restauradoras apresentaram películas com espessura maiores que 100 ?m, enquanto as resinas fluidas e os cimentos resinosos apresentaram valores menores que 50 ?m. Os grupos experimentais RZ, RZ45 e RZ60 apresentaram os maiores valores de KHN, RFB e ME. Os grupos RT, RT45, RT60, FT, CV e CR apresentaram os menores valores de RFB e semelhantes entre si. Para a KHN, os grupos RT, RT45, RT60, FZ e CR apresentaram valores intermediários e semelhantes entre si, e superiores aos grupos FT e CV. Os resultados de ?E mostraram valores acima de 2 para todos os grupos experimentais, com exceção do RZ60. Os maiores valores de ?E foram evidenciados nos grupos RT45 e RT60. A razão de contraste foi estatisticamente menor para o grupo CV e os maiores valores de opacidade foram encontrados nos grupos RZ, RZ45 e FZ. A opalescência foi superior nos grupos FZ, CR, FT e CV. Considerando as limitações do presente estudo, concluiu-se que os tratamentos térmicos não alteraram as propriedades mecânicas das resinas restauradoras e não promoveram uma redução da espessura de película que atenda aos requisitos da ISO4049. As resinas fluidas e os cimentos apresentaram espessura de película inferior à 50?m e propriedades mecânicas que atendem à normativa ISO4049. A opalescência maior foi encontrada nos cimentos resinosos e a diferença de cor e razão de contraste apresentaram resposta grupo dependente. / The objectives of this study were to evaluate the physical properties of preheated restorative resin composites and fluid resins with the purpose of cementation of ceramic veneers in comparison to resin cements. Specimens were prepared with two restorative resin composites (Filtek Z250XT and Tetric N Ceram), in the following conditions: room temperature (RZ; RT), heated at 45°C (RZ45; RT45), and heated at 60°C (RZ60; RT60). Two flowable resins (Filtek Z350 Flow and Tetric N Flow) named FZ and FT and two resin cements (Relyx Veneer and Variolink N), called CR and CV, were also used. The experimental groups were evaluated in regards to film thickness with two methodologies; biaxial flexure strength (BFS) and modulus of elasticity (ME) (model 5565, Instron Corp, Canton MA, USA); Knoop microhardness test (KMT) (Shimadzu HMV-2, Tokyo, Japan), color difference (?E), contrast ratio and opalescence test (CM-3770d, Konica Minolta, Japan). Data were assessed by ANOVA and a post-hoc Tukey test (p<0.05). The restorative resins presented film thickness larger than 50?m, whereas the flowable resins and resin cements showed inferior values. The experimental groups RZ, RZ45 and RZ60, revealed greater values of KHN, BFS and ME. The RT, RT45, RT60, FT, CV and CR groups showed lower values for BFS and similar to each other. For KHN the RT, RT45, RT60, FZ and CR groups exposed intermediate and similar values to each other, and superior values to FT and CV groups. Color difference (?E) results demonstrated results superior than 2 for all experimental groups, with the exception of RZ60 group. The greater values of ?E were shown in RT45 and RT60 groups. Contrast ratio was statistically lower for the CV group and the highest values of opacity were verified in RZ, RZ45 and FZ groups. Opalescence was superior in FZ, CR, FT and CV groups. Considering the limitations of this study, the results demonstrated that preheated treatments did not modify the mechanical properties of restorative resin composites and didn\'t reduce film thickness which attend to ISO4049 parameters. Flowable resins and cements obtained film thickness inferior to 50?m and biaxial flexure strength results that are presented by the ISO4049. The greater opalescence was shown in the resin cements, also color difference and contrast ratio revealed results that were group dependent.

Orientador: Rodolfo Bruniera Anchieta / Resumo: O objetivo deste trabalho foi avaliar “in vitro” e “in silico” a integridade estrutural da interface de cimentação, o comportamento biomecânico, e a resistência de união da interface dentina/cimento de diferentes técnicas de cimentação de pinos de fibra de vidro (PFV) em canais amplos. Para tanto, foram utilizados 33 incisivos bovinos. Após o tratamento endodôntico, os espécimes foram divididos aleatoriamente em três grupos (n=11): PCN- Pino convencional cimentado em dente com conduto normal; PCA- Pino convencional cimentado em dente com conduto amplo; PAA- Pino anatômico cimentado em dente com conduto amplo. Em seguida, foram executados os preparos intrarradiculares de acordo com cada grupo com brocas pré-estabelecidas, tratamento de superfície dos PFV (WhitePost nº3 DC, FGM) e cimentação dos mesmos com o cimento resinoso autoadesivo (Rely X U200, 3M ESPE). Então, 6 espécimes de cada grupo foram submetidos ao escaneamento em um microtomógrafo de alta resolução (SkyScan 1272) para avaliação da integridade, volume e presença de bolhas na interface de cimentação. Posteriormente, com base nos dados do µCT e imagens de microscopia (n=1), dois modelos tridimensionais de cada grupo foram confeccionados para a análise de elementos finitos, sendo que o primeiro foi considerado ideal (G1, G3 e G5), sem defeitos na interface, e o segundo continha as condições encontradas pela análise de µCT(G2, G4 e G6). Após o envelhecimento em estufa por 7 meses, todos os espécimes foram submetidos a... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The objective of this study was to evaluate “in vitro” and “in silico” the structural integrity of the cementation interface, the biomechanical behavior and the bond strength of different fiberglass post cementation techniques in flared root canal. To this end, 33 bovine incisors were used. After the endodontic treatment, the specimens were randomly divided into three groups (n = 11): PCN - conventional post cemented in tooth with normal canal lumen; PCA- Conventional fiberglass post cemented in flared root canal; PAA- Fiberglass post relined with composite resin and cemented in flared root canal; Then, the intra-radicular preparations were performed according to each group with pre-established drills, surface treatment of PFV (WhitePost Nº. 3DC, FGM) and cementation with self-adhesive resin cement (Rely X U200, 3M ESPE). Then, 6 specimens from each group were submitted to scanning in a high resolution microtomograph (SkyScan 1272) to evaluate the integrity, volume and presence of bubbles at the cementation interface. Then, based on the μCT data and the microscopic images (n = 1), two three-dimensional models of each group were made to analyze finite elements, the first one being considered ideal (G1, G3 and G5), without interface defects and the second contained the conditions found by μCT analysis (G2, G4 and G6). After being stored for 7 months, all specimens were submitted to the pushout bond strength test (n = 10). Data were submitted to ANOVA with repeated measures and ... (Complete abstract click electronic access below) / Mestre

O Objetivo deste estudo é avaliar in vitro, a resistência que diferentes materiais resinosos têm a passagem de fluidos que atravessam a dentina na ausência de cemento radicular. Foram utilizados 60 dentes humanos cedidos pelo banco de dentes da FOUSP. Os dentes foram submetidos a tratamento endodôntico segundo a técnica de Paiva e Antoniazzi e armazenados a uma temperatura de 37°C em umidade 100% por 24 horas para o preparo do retentor intra -radicular respeitando o limite apical de 4 mm. Os retentores intra-radiculares foram modelados com resina tipo Duralay e fundidos com liga de prata e cimentados com os seguintes materiais: Oxifosfato de Zinco (SS White), Enforce (Dentsply), Panavia F (Kuraray) e Rely X (3M) . Após a cimentação, delimitou-se uma janela na região cervical da raiz onde o cemento foi removido com uma broca diamantada, a parte externa da raiz foi impermeabilizada com cianocrilato de etila e esmalte cosmético para posterior imersão em uma solução de azul de metileno a 1% por 48 horas. Decorrido este período, a camada impermeabilizante foi removida, os dentes foram desgastados no sentido mésio distal e avaliados com o programa Imagelab. A comparação da área impregnada pelo agente traçador na película dos cimentos, nos terços cervical e médio, revelou diferenças estatisticamente significantes (p < 0,01) do Panavia F (Kuraray) em relação aos outros três materiais, demonstrando a superioridade desse material no que se refere à impermeabilização do sistema de canais radiculares. Podemos concluir que dentre os materiais avaliados o cimento Panavia F (Kuraray) apresentou diferença estatisticamente significante, tanto para no segmento cervical quanto terço médio. / This study objective is to evaluate in vitro, the resistance that different resinous materials have through the fluids passage cross through the dentine in the absence of radicular cementum. 60 human teeth given by FOUSP bank of teeth were used. The teeth were submitted to endodontic treatment according to Paiva's and Antoniazzi´s technique and stored in a temperature of 37°C in humidity 100% during 24 hours for the preparation of the intra-radicular retainer, respecting the 4 mm apical limit. The intra -radicular retainers were modeled with Duralay resin type and melted with silver league and cemented with the following materials: Zinc Oxiphosfate (SS White), Enforce (Dentsply), Panavia F (Kuraray) and Rely X (3M). After the foundation, a window was delimited in the root cervical area where the cementum was removed with a diamond drill. The external part of the root was made waterproof with etile cyanocrylate and cosmetic enamel for subsequent immersion in a 1% blue methylen solution for 48 hours. Elapsed this period, the waterproof layer was removed, the teeth were consumed in the mesio-distal direction and appraised with the Imagelab software. The impregnated area by the tracer agent of the in the film of the cements comparison, in the cervical and medium thirds, revealed significant statistical differences (p <0,01) of Panavia F (Kuraray) in relation to the other three materials, demonstrating the superiority of that material in relationship to the radicular chanal “waterproofing" system. It’s possible to conclude that among the appraised materials, the Panavia F (Kuraray) cement presented significant statistical difference, in the cervical segment as well as the medium third.

A raspagem e o aplainamento radicular removem o cemento presente nesta área, o qual funcionaria como barreira de dentina contra a penetração de bactérias, toxinas e outros produtos vindos da superfície externa do dente. O objetivo deste estudo foi avaliar, in vitro, em dentes tratados endodonticamente, a resistência apresentada por diferentes materiais de cimentação na infiltração do azul de metileno, que poderia atravessar a dentina radicular, quando submetido a duas diferentes situações: a) raspagem e aplainamento do cemento radicular e b) remoção de cemento com pontas diamantadas. Para isso, utilizou-se 48 dentes humanos unirradiculares, cedidos pelo banco de dentes da FOUSP, tratados endodonticamente e preparados para receberem pinos. Estes foram modelados com resina acrílica para que, por meio de fundição, fossem obtidos os retentores intrarradiculares metálicos. Os dentes foram divididos em 4 grupos com 12 espécimes, e a cada um dos grupos, destinado um tipo de material diferente para a cimentação: Cimento de Zinco® (SS White, Rio de Janeiro, Rio de Janeiro, Brasil), Cimentos resinosos Panavia F® (Kuraray, Kurashiki, Okayama, Japan), Rely X U 100® (3M Dental, Seefeld, Alemanha) e Rely X Luting 2® (3M Dental, Sant Paul, Estados Unidos). Após esse procedimento, delimitaram-se duas janelas na região cervical da raiz, sendo que num dos lados o cemento foi removido com uma ponta diamantada e no lado oposto, com 40 golpes de cureta Gracey 5-6 (Neumar, São Paulo, São Paulo, Brasil) paralelos ao longo eixo do dente. Exceto nas regiões instrumentadas, o dente foi impermeabilizado externamente e exposto à solução de azul de metileno a 1% e pH 7,2 durante 48 horas. As amostras foram desgastadas no sentido do longo eixo até o maior diâmetro do pino e a área impregnada pelo corante foi digitalizada e mensurada com o programa Imagelab®. A comparação da área impregnada pelo agente traçador na película dos cimentos, nos terços cervical e médio, revelou diferenças estatisticamente significantes entre si (p < 0,05). No lado em que a dentina foi removida com broca, houve diferença estatisticamente significante quando os três materiais adesivos foram comparados com o Cimento de Zinco (SS White, Rio de Janeiro, Rio de Janeiro, Brasil). Na comparação entre os cimentos resinosos houve diferença estatisticamente significante (p<05) somente entre os cimentos Panavia F® (Kuraray, Kurashiki, Okayama, Japan) e Rely X U 100® (3M Dental, Seefeld, Alemanha) para o terço apical. Na superfície tratada com curetas periodontais, verificou-se diferença estatisticamente significante entre os grupos estudados (p < 0,05) apenas quando comparados o cimento Rely X U 100® (3M Dental, Seefeld, Alemanha) com Rely X Luting 2® (3M Dental, Sant Paul, Estados Unidos) para o terço cervical. Concluiu-se que para o tratamento com ponta diamantada, que os cimentos Panavia F® (Kuraray, Kurashiki, Okayama, Japan), Rely X U 100® (3M Dental, Seefeld, Alemanha) e Rely X Luting 2® (3M Dental, Sant Paul, Estados Unidos) têm comportamento semelhante para os terços cervical e médio, diferindo apenas no terço apical. Já para o tratamento com curetas periodontais, os cimentos Panavia F® (Kuraray, Kurashiki, Okayama, Japan), Rely X U 100® (3M Dental, Seefeld, Alemanha) e Rely X Luting 2® (3M Dental, Sant Paul, Estados Unidos) mostraram resultados similares para os terços médio e apical, diferindo apenas no terço cervical. / Scaling and root planning remove cementum present in this area, which would acts as a dentin barrier against penetration of bacterias, toxins and other products coming from the surface of the tooth. The objective of this study was to evaluate in vitro endodontically treated teeth, the resistance of different materials to methylene blue, which could cross the root dentin when submitted to two different situations: a) scaling and root planning b) removal of cementum with drills. It was used 48 human uniradicular teeth, assigned by FOUSPs teeth bank and were endodontically treated and prepared to receive pins. These were modeled with an acrylic resin in order to obtain the metallic intraradicular posts. The teeth were divided into four groups with twelve specimens. Each one of the groups received a different material for cementing: Cement of Zinc® (SS White, Rio de Janeiro, Rio de Janeiro, Brazil), Panavia F® Resin Cements (Kuraray, Kurashiki, Okayama, Japan), Rely X U 100® (3M Dental, Seefeld, Germany) and Rely X Luting 2® (3M Dental, Sant Paul, United States). After this procedure, it was delimited two windows in the cervical region of the root. One of the sides the cementum was removed with a diamond drill and on the other side, with 40 Gracey 5-6 curette strokes (Neumar, São Paulo, Brazil) parallel to the long axis of the tooth. Except on the instrumented regions, the tooth was externally sealed and exposed to a 1% methylen blue solution and pH 7.2 during 48 hours. The samples were scraped from the long axis until the largest post diameter. The impregnated area with the dye were scanned and measured with the Imagelab® program. The comparison between the impregnated area through the tracer agent on the cement film in the cervical and medium thirds revealed statistically significant differences (p<0,05). On the side where the dentin was removed with a drill, there was a statistically significant difference when the three adhesive materials were compared to the Zinc Cement (SS White, Rio de Janeiro, Rio de Janeiro, Brazil). In the comparison between the resin cements there was a statistically significant difference (p<0,05) only between the cements: Panavia F® (Kuraray, Kurashiki, Okayama, Japan) and Rely X U 100® (3M Dental, Seefeld, Germany) for the apical third. On the surface treated with periodontal curettes, it was identified a meaningful statistical difference between the studied groups (p<0,05) only when compared the cements: Rely X U 100® (3M Dental, Seefeld, Germany) with Rely X Luting 2® (3M Dental, Sant Paul, United States) for the cervical third. The conclusion was that when the treatment uses a drill, the cements: Panavia F® (Kuraray, Kurashiki, Okayama, Japan), Rely X U 100® (3M Dental, Seefeld, Germany) and Rely X Luting 2® (3M Dental, Sant Paul, United States) have similar behavior to the cervical and medium third. The unique difference comes from the apical third. On the other hand, the treatments using periodontal curettes, the cements Panavia F® (Kuraray, Kurashiki, Okayama, Japan), Rely X U 100® (3M Dental, Seefeld, Germany) and Rely X Luting 2® (3M Dental, Sant Paul, United States) resulted in similar results for the medium and apical thirds, only differing on the cervical third.

Pouco se sabe sobre o comportamento do tecido ósseo em relação à profundidade da linha de cimentação em próteses sobre implantes. Por isso, o presente estudo radiográfico utilizou os implantes Cone Morse com o intuito de definir a posição exata na qual se pode estabelecer a profundidade da linha de cimentação protética. Foram utilizados cinco cães, os quais tiveram todos os pré-molares inferiores extraídos numa primeira fase cirúrgica. Após três meses, realizou-se a segunda fase cirúrgica na qual foi utilizada a técnica da carga imediata, com a instalação dos implantes juntamente com os pilares protéticos. Foram instalados trinta implantes numa profundidade de 3mm infra óssea e eles foram igualmente divididos entre os grupos Controle e Experimental. Os pilares protéticos tinham diferentes dimensões transmucosas de 1.5, 3.5, e 5.5mm. Isto fez com que a linha de cimentação se posicionasse a 1.5mm infra óssea, a 0.5mm supra óssea e a 2.5mm supra óssea. No grupo Controle, foi realizada a instalação dos implantes e dos pilares protéticos somente. No grupo Experimental, foi realizada a instalação dos implantes, dos pilares protéticos e, sobre estes, foram cimentados cilindros de alumina. Foram realizadas tomadas radiográficas periapicais, através da técnica do paralelismo, em todas as fases do experimento. As radiografias foram escaneadas e analisadas através do programa AutoCAD. Foram utilizados os testes estatísticos t de Student para amostras pareadas e independentes com o nível de significância de p<0.05. Os resultados mostraram que não houve diferenças estatisticamente significantes entre os grupos Controle e Experimental nas diferentes profundidades em relação ao tecido ósseo. Adicionalmente, também não houve diferenças estatisticamente significantes na crista óssea nas variações das dimensões das cintas transmucosas dos pilares testados e nas variações entre os tempos Inicial e Final do experimento no grupo Controle e no grupo Experimental. Conclui-se que não há influência da profundidade da linha de cimentação no comportamento da crista óssea e a utilização de diferentes dimensões dos pilares protéticos não altera o tecido ósseo marginal ao redor dos implantes Cone Morse. / Little is known about the behavior of bone tissue in relation to the depth of the cement line position in dental implants. Therefore, this radiographic study used the Morse taper implants in order to define the exact location in which it can be established the depth of the prosthetic cementation line. Five dogs were used and had all their lower premolars extracted in the first stage surgery. After three months, was performed a second surgical procedure in which was used the technique of immediate loading, installing together implants and abutments. Thirty implants were installed at a depth of 3 mm below the bone and they were equally divided between the Control and Experimental group. The abutments had different transmucosal dimensions of 1.5, 3.5, and 5.5mm. This meant that the depth of cementation line was positioned respectively to 1.5mm below the bone, 0.5 above the bone and 2.5mm above the bone. In the Control group, was performed the installation of implants and abutments only. In the Experimental group, was performed the installation of implants, abutments and, over these, was cemented cylinders of alumina. Periapical radiographs were taken, using the paralleling technique, in all phases of the experiment. The radiographs were scanned and analyzed with the program AutoCAD. Statistical t Student test of samples paired and independent were used with the level of significance of p<0.05. The results showed no differences statistically significants between the Control and Experimental group at different depths in relation to bone tissue. Additionally, there were no differences statistically significant in the crest bone in the variations of dimensions of the transmucosal abutments tested and in the variations between the Start and End time of the experiment in the Control and Experimental groups. It is concluded that there is no influence of the depth of cementation line on the behavior crest bone and the different dimensions of the abutment does not change the marginal bone around Morse taper implants.

Submitted by Angela Maria de Oliveira (amolivei@uepg.br) on 2018-07-24T13:33:46Z No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) Bruna Hilgemberg.pdf: 2456286 bytes, checksum: 1f094c1efd8bce8788da73b56ecf38e8 (MD5) / Made available in DSpace on 2018-07-24T13:33:46Z (GMT). No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) Bruna Hilgemberg.pdf: 2456286 bytes, checksum: 1f094c1efd8bce8788da73b56ecf38e8 (MD5) Previous issue date: 2018-02-22 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / O objetivo do presente estudo foi avaliar o efeito de diferentes protocolos adesivos na resistência de união de diferentes compósitos CAD/CAM por meio do teste de microcisalhamento (μSBS). Para esse experimento, três tipos de compósitos CAD/CAM foram utilizados: 1) [Lava™ Ultimate CAD/CAM Restorative (3M ESPE) - LU], 2) [Brava block CAD/CAM (FGM)- BR] e 3) [Vita Enamic (Vita Zanhfabrik) - VE]. Quarenta e cinco secções retangulares (10 × 10 × 6 mm) de compósitos CAD/CAM foram utilizados para a avaliação de microcisalhamento, esses blocos foram distribuídos de acordo com as variáveis: Compósitos CAD/CAM (1- LU, 2-BR, 3- VE) vs. sistema de cimentação [1- Prime & Bond Elect (PBE) + Enforce, 2- Scotch Bond Universal (SBU) + Rely X Ultimate, 3- Ambar Universal (AU) + All cem, 4- Silano sem MDP + Enforce, 5- Silano sem MDP + Rely X Ultimate, 6- Silano sem MDP + All Cem, 7- Silano com MDP + Enforce, 8- Silano com MDP + Rely X Ultimate, 9- Silano com MDP + All cem], resultando em 27 grupos experimentais. O sistema adesivo foi aplicado e matrizes de Tygon foram preenchidas com cimento resinoso e fotoativadas. Os espécimes foram armazenados em água (37 °C por 24h) e submetidos ao teste de μSBS, seus resultados foram submetidos ao teste de ANOVA 2-fatores seguido pelo teste de Bonferroni, α = 5%). Quinze secções retangulares adicionais foram avaliados em Microscopia eletrônica de varredura (MEV/EDS) para a análise da morfologia e composição após tratamento de superfície conforme recomendação de cada fabricante. Para os três cimentos utilizados, maiores valores de μSBS foram observados na superfície VE, seguido do LU e do BR respectivamente. A diferença significativa entre os sistemas de cimentação foi observada apenas no compósito VE, que apresentou maiores valores de μSBS, com exceção dos grupos silano com MDP + All Cem, silano sem MDP + Rely X Ultimate e SBU + Rely X Ultimate. Foi encontrado para todos os grupos, pouca ou nenhuma porcentagem de falha coesiva em cimento, maior porcentagem de falha adesiva/mista, com exceção dos grupos VE/AU e VE/silano com MDP/All Cem, VE/silano sem MDP e VE/SBU/Rely X Ultimate e VE/AU e VE/silano com MDP/ Enforce, em que foi encontrado maior porcentagem de falha coesiva em compósitos CAD/CAM. Todos os compósitos apresentaram irregularidades após o tratamento de superfície na análise de MEV, porém maior irregularidade foi observada na superfície do VE, seguido do LU e do BR respectivamente. A análise por EDS, confirmou a composição de cada compósito CAD/CAM e após o tratamento de superfície, houve diminuição da porcentagem de sílica e zircônia apenas para LU. Pode-se concluir que a efetividade do protocolo de cimentação está relacionada ao tipo de compósito CAD/CAM e suas diferentes composições e que independente do protocolo de cimentação, o VE apresentou os melhores valores de resistência ao microcisalhamento em comparação aos outros compósitos CAD/CAM avaliados. / The objective of the present study was to evaluate the effect of different adhesive protocols on the bond strength of different CAD / CAM composites by means of the micro-shear test (μSBS). For this experiment, three types of CAD / CAM composites were used: 1) [Lava ™ Ultimate CAD / CAM Restorative (3M ESPE) - LU], 2) [Brava block CAD / CAM (FGM) Vita Enamic (Vita Zanhfabrik) - VE]. Forty-five rectangular sections (10 × 10 × 6 mm) of CAD / CAM composites were used for the evaluation of micro-shear, these blocks were distributed according to the following variables: CAD / CAM composites (1 LU, 2-BR, 3 - VE) vs. (1) Prime & Bond Elect (PBE) + Enforce, 2- Scotch Bond Universal (SBU) + Rely X Ultimate, 3- Ambar Universal + All Cem, 4- Silane without MDP + Enforce, 5- Silane without MDP + Rely X Ultimate, 6- Silane without MDP + All Cem, 7- Silane with MDP + Enforce, 8- Silane with MDP + Rely X Ultimate, 9- Silane with MDP + All Cem], resulting in 27 experimental groups . The adhesive system was applied and Tygon matrices were filled with resin cement and photoactivated. The specimens were stored in water (37 ° C for 24h) and submitted to the μSBS test, their results were submitted to the 2-factor ANOVA test followed by the Bonferroni test, α = 5%). Fifteen additional rectangular sections were evaluated in Scanning Electron Microscopy (SEM / EDS) for analysis of morphology and composition after surface treatment as recommended by each manufacturer. For the three cements used, higher values of μSBS were observed on the VE surface, followed by LU and BR respectively. The significant difference between the cementation systems was observed only in the composite VE, which presented higher values of μSBS, except for the silane groups with MDP + All Cem, silane without MDP + Rely X Ultimate and SBU + Rely X Ultimate. A higher percentage of adhesive / mixed failure was found for all groups, except for the VE / AU and VE / silane groups with MDP / All Cem, VE / silane without MDP and VE / SBU / Rely X Ultimate and VE / AU and VE / silane with MDP / Enforce, in which a higher percentage of cohesive failure was found in CAD / CAM composites. All the composites presented irregularities after the surface treatment in the SEM analysis, but greater irregularity was observed on the surface of the VE, followed by the LU and the BR respectively. The EDS analysis confirmed the composition of each CAD / CAM composite and after the surface treatment, the percentage of silica and zirconia was reduced only for LU. It can be concluded that the effectiveness of the cementation protocol is related to the type of CAD / CAM composite and its different compositions and that regardless of the cementation protocol, the VE presented the best values of micro-shear strength compared to other CAD / CAM composites evaluated.

O desenvolvimento de novos sistemas cerâmicos propicia a possibilidade de escolha do tipo de restauração que se deseje utilizar. Entretanto, os benefícios advindos deste progresso devem ser avaliados frente à possibilidade de comportamento clínico insatisfatório. Este trabalho se propõe a avaliar infra-estruturas cerâmicas quanto à influência do ajuste interno na adaptação, o desajuste vertical após a simulação da cimentação, a espessura de película nas superfícies axiais e oclusal e a ocorrência de assentamento oblíquo. Um troquel-padrão metálico com preparo para coroa total em pré-molar superior foi confeccionado e trinta troquéis de gesso foram obtidos e dividos em três grupos de dez espécimes cada. Sobre os troquéis de gesso foram confeccionadas infra-estruturas metálicas para o grupo MC, infra-estruturas cerâmicas In-Ceram Zirconia, para o grupo IZ, e Procera AllZircon, para o grupo PZ. As infra-estruturas tiveram sua posição, em relação ao troquel-padrão, mensurada durante ajuste interno e simulação da cimentação com silicone de consistência fluida (cimento-análogo). A película de cimento-análogo abaixo das infra-estruturas foi seccionada no sentido vestíbulo-lingual e mensurada nas paredes axiais e oclusal. A análise dos resultados demonstrou que: 1) o ajuste interno das infra-estruturas metalo-cerâmicas e In-Ceram Zirconia resultou em redução do desajuste vertical; 2) o desajuste vertical das infra-estruturas Procera AllZircon foi estatisticamente diferente das infra-estruturas metalo-cerâmicas e In-Ceram Zirconia; 3) a espessura de película das infra-estruturas Procera AllZircon foi significantemente maior que das infra-estruturas metalo-cerâmicas e In-Ceram Zirconia; 4) todas as infra-estruturas apresentaram assentamento oblíquo. / The development of new ceramic systems creates the possibility of choice above the type of restoration one could mean to choose. Thus, benefits from this progress must be appraised on the possibility of unsatisfactory clinical behavior. This work intends to evaluate ceramic copings to the influence of internal adjustment on adaptation, vertical misfit after cementation, film thickness of axial and occlusal surfaces and occurrence of oblique seating. A metallic superior premolar analogue with full crown preparation was yield and thirty casts were obtained and divided into three groups of ten specimens each. Metal copings were yield for group MC and ceramics copings of In-Ceram Zirconia and Procera AllZircon were yield for group IZ and group PZ, respectively. The copings had their position, in relation to the metallic analogue, measured during adjustment and cementation with light body silicon. Cement film, below the copings, was sectioned and measured at the axial and occlusal surfaces. The analysis of the results demonstrated that: 1) internal adjustment of metal and In-Ceram Zirconia copings reduced the vertical misfit; 2) vertical misfit after cementation of Procera AllZircon copings was statistically different from metal and In-Ceram Zirconia copings; 3) film thickness of Procera AllZircon copings was significantly greater than metal and In-Ceram Zirconia copings; 4) all copings presented oblique seating.