Orientador: Monica Campos Serra / Dissertação (mestrado) - Universidade Esatdual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-24T19:47:05Z (GMT). No. of bitstreams: 1 Basting_RobertaTarkany_M.pdf: 5364710 bytes, checksum: fb93ea48edd3f4d2de1426ce80e72d18 (MD5) Previous issue date: 1999 / Resumo: Propriedades dos materiais híbridos de ionômero de vidro/resina composta têm sido extensamente analisadas, podendo-se observar que os testes laboratoriais são os mais utilizados como metodologia de pesquisa. O objetivo deste trabalho foi avaliar a dureza superficial in situ de materiais híbridos de ionômero de vidro/resina composta em função do tempo após a fotopolimerização, através de uma metodologia que possa predizer o desempenho clínico dos materiais. Foram analisados cinco materiais: Fuji II LC / GC Corporation (Fu), Vitremer / 3M (Vi), Freedom / SDI (Fr), Dyract / Dentsply (Dy) e Z 100/ 3M (Zl). Um dispositivo acrílico intra-bucal palatal foi confeccionado para cada um dos 24 voluntários participantes do experimento, no qual foi fixado um corpo de prova de cada material. Os tempos estudados foram: 30 min, 1 h, 2 h, 4 h, 8 h, 24 h, 48 h, 7 dias, 10 dias, 14 dias, 17 dias e 21 dias após a fotopolimerização. A Análise de Variância, seguida do teste de Tukey ao nível de 1%, mostrou diferenças significativas de dureza entre todos os materiais (Fu < Vi < Fr < Dy < ZI) até 48 horas. A partir do sétimo até o décimo quarto dia;, não se verificaram diferenças estatísticas entre os materiais Fr e Dy (Fu < Vi < Fr = Dy < Zl). No décimo sétimo e vigésimo primeiro dias, os materiais Vi, Fr e Dy apresentaram igualdade estatística, diferindo dos demais (Fu < Vi = Fr = Dy < Zl). A regressão polinomial mostrou um aumento de dureza em função do tempo para cada um dos materiais híbridos, exceto para o material Z 1. A metodologia in situ utilizada permitiu concluir que houve um aumento da dureza superficial de todos os híbridos de ionômero de vidro/resina composta testados em função do tempo após fotopolimerização, embora houvesse diferenças de dureza entre esses materiais / Abstract: The properties of glass-ionomer / hybrid composite resin materiaIs have been widely analyzed and laboratory tests are used more as a research methodology. The purpose of this paper was to evaluate the superficial hardness of glass-ionomer / composite resin hybrid materiaIs in situ at different post-iITadiation times, by means of a methodology that can predict the clinical performance of the materiaIs. Four hybrid materiaIs were analyzed: Fuji rI li,C / GC Corporation (Fu), Vitremer / 3M (Vi), Freedom / SDI (Fr) and Dyract / Dentsply (Dy). One composite was used as a control group: Z 100 / 3M (ZI). Palatal intra-oral acrylic appliances were made for each one ofthe 24 volunteers in the experiment. In each appliance, a specimen of each material was fixed. Microhardness testing was performed at 30 min, 1 h, 2 h, 4 h, 8 h, 24 h, 48 h, 7 days, 10 days, 14 days, 17 days and 21 days after initial Iight-curing. The Analysis of Variance, folIowed by the Tukey test, showed significant dift'erences of hardness among alI materiaIs (Fu < Vi < Fr < Dy « ZI) up to 48 hours. From t.he seventh to the fourteenth day, statistical differences were not found between Freedom and Dyract (Fu < Vi < Fr = Dy < ZI). On the seventeenth and twenty-first days, Vitremer, Freedom and4Dyract presented statistical equality, but differed ITom the others (Fu < Vi = Fr = Dy < ZI). The polynomial regression showed an increase of hardness over time for the hybrid materiaIs, but not for the composite. The in situ methodology used allowed the conclusion to be reached that there was an increase in the superficial hardness of alI the glass-ionomer / composite resin hybrid materiaIs tested at each post-irradiation time, although there were differences of hardness among these materiaIs / Mestrado / Dentística / Mestre em Clínica Odontológica

Orientador: Mario Fernando de Goes / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-25T05:42:21Z (GMT). No. of bitstreams: 1 Guimaraes_PriscillaSantos_M.pdf: 4440699 bytes, checksum: f24c42055485725bffa0c006ac4cf4e4 (MD5) Previous issue date: 1999 / Resumo: o propósito deste estudo foi avaliar a influência da armazenagem em água na resistência à flexão de porcelana associada a cimentos a base de resina. Para isso foram confeccionados 120 discos (21 mm de diâmetro X 2mm de espessura) de porcelana feldspática, compostos de duas camadas distintas. A primeira camada formada por porcelana de média fusão (Duceram-Degussa), seguida da aplicação da porcelana de baixa fusão (Duceram LFC - Degussa) para completar a amostra. Todos os discos cerâmicos foram condicionados com ácido fluorídrico a 10%, durante 4 minutos e divididos em 6 grupos de 20 amostras cada. Em seguida, os materiais resinosos (Scotchbond Resin Cement - 3M, Enforce com flúor - Dentsply) foram manipulados e aplicados de acordo com as instruções dos respectivos fabricantes sobre a superfície condicionada do disco cerâmico. Sobre o cimento recém-aplicado, foi colocada uma folha de polietileno e uma placa de vidro, e o conjunto disco cerâmico cimento-folha de polietileno e placa de vidro for posicionado em uma prensa hidráulica e comprimido com uma carga de 1500 gramas. Sob compressão o cimento foi fotopolimerizado por 20 segundos em 4 posições diametralmente opostas. Após a remoção da carga, o cimento foi polimerizado por mais 20 segundos na região central. Os corpos-de-prova assim obtidos foram armazenados em água destilada por períodos de 24h, 3 meses e 6 meses. A seguir os corpos-de-prova foram submetidos ao ensaio de flexão biaxial, a uma velocidade de 1 mm/min, em uma máquina Instron (Modelo 4411). Os valores obtidos foram submetidos a cálculos matemáticos para deteminação da tensão de fratura. Em seguida, estes valores foram submetidos à Distribuição de Weibull, análise de variância e ao teste de Tukey. Os resultados demonstraram que não houve diferença estatisticamente significante (p<O, 01) nos valores de resistência I encontrados para os diferentes períodos de armazenagem. No entanto os grupos onde I utilizou-se o material Enforce, apresentaram valores estatisticamente superiores (p<O,01) àqueles encontrados para os grupos com o material Scotchbond. O Material Enforce I . apresentou maior módulo de Weibull e conseqüentemente, menor probabilidade de : falha em relação ao material Scotchbond Resin Cement / Abstract: The purpose of this study was to evaluate the influence of water storage on the tensile strength of feldspathic porcelain associated to resin cements. One hundred twenty porcelain discs (21 mm in diameter x 2 mm thick) were fabricated in two different layers. The first one was done of medium fuse porcelain (Duceram - Degussa), followed by the application of a layer of low fusion porcelain (LFC -Degussa). Ali discs were conditioned with 10% fluoridric acid, for 4 minutes and divided in 6 groups of 20 samples each. After, the resin cements (Scotchbond Resin Cement - 3M, Enforce fluoride containing Dentsply) were manipulated according to manufacturers instructions and, applied over the conditioned surface of the porcelain disco Over it a polyethylene sheet and a glass slab was placed, and the assembly was taken to a hydraulic press and squeezed with a load of 1500 g. Under compression cement was photopolimerized for 20 seconds in 4 different positions. After the removal of the load, the cement was photopolimerized for 20 seconds on the middle of the disco The samples were then stored in distilled water for 24 hours, 3 and 6 months. The biaxial flexure test was conducted in a universal test méilchine (Instron - model 4411), at a cross speed of 1 mm/min. The data was then submitted to Tukey's test and Weibull Distribution. From the results, there was no statistic difference (p<0.01) on the strength values for the different periods of storage in water. However the strength values for groups with Enforce was statistically higher (p<0.01) than those for Scotchbond Resin Cement. The material Enforce showed a higher Weibull modulus and lower probability of failure in comparison with Scotchbond Resin Cement / Mestrado / Materiais Dentarios / Mestre em Ciências

Orientador: Jose Roberto Lovadino / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-25T09:20:22Z (GMT). No. of bitstreams: 1 Murrer_RodrigoDutra_D.pdf: 4795919 bytes, checksum: 6c2dda55823cbc92098c1cd0776f5e18 (MD5) Previous issue date: 1999 / Resumo: O objetivo do trabalho foi estudar a resistência à fratura de pré-molares superiores em função da restauração com técnicas adesivas e o efeito de ciclagens térmicas nessa resistência. Para isso, 80 dentes extraídos, íntegros e . livres de trincas ou manchas, foram divididos, aleatoriamente, em oito grupos de dez dentes. Os dentes dos grupos 1 e 2 não receberam preparo nem restauração. Os dentes dos grupos 3 ao 8 receberam um preparo MOD, sem caixas proximais e com o assoalho plano, de largura correspondente a 1/4 da distância intercuspidal e de profundidade correspondente a 3/4 da altura da coroa dental, sendo que os dos grupos 3 e 4 não foram restaurados, os dos grupos 5 e 6 foram restaurados com uma técnica de amá/gama-adesivo e os dos grupos 7 e 8 com resina composta. As amostras dos grupos 2,4,6 e 8 foram submet~das a 2000 ciclos térmicos intercalando banhos de 1 minuto de duração entre 5 e 55°C. Todos os grupos foram submetidos a teste de resistência à compressão em máquina universal de ensaios. O carregamento foi aplicado axialmente através de uma esfera de aço posicionada de maneira a manter contato apenas com as vertentes das cúspides e nunca com as restaurações ou as margens das cavidades. As médias das forças necessárias para fraturar as amostras de cada grupo foram (em kgf): G1=208,04(a); G2=200,9(a); G3=66,28(b); G4=67,90(b); G5=168,20(c); G6=118,44(d); G7=202,66(a); G8=172,02(c). As letras diferentes denotam diferenças estatisticamente significantes entre os grupos, demonstradas pela análise estatística dos resultados, através do Teste t de Student. Esses resultados mostram que restaurações com potencial de união à estrutura dental têm a capacidade de recuperar, em maior ou memor grau, a resistência à fratura de pré-molares superiores perdida no preparo cavitário. Entretanto, mostra também que o envelhecimento artificial, através de ciclagens térmicas, tem um efeito deletério no reforço da estrutura dental exercido por restaurações adesivas, sugerindo uma transitoriedade da união entre sistemas adesivos e tecido dental / Abstract: The aim ot this study was to evaluate the tracture resistance ot maxillary premolars with MOD cavities preparations, restored with adhesive materiais. Eighty sound and tree trom cracks extracted maxillary premolars were randomly assingned to eight groups ot ten teeth. The teeth trom group 1 and 2 did not receive either cavity preparation or restoration. From the group 3 to 8 , the teeth received a MOD cavity preparation without proximal steps and flat floor. The preparation had the isthmus width equal to 1/4 ot the intercuspidal distance and the cavity deep was 3/4 ot the crown height. Teeth trom group 3 and 4 were not restored, trom group 5 and 6 were restored with: bonded-amalgam and teeth trom group 7 and 8 were restored with composite resin with a dentin bonding system. Samples trom groups 2, 4, 6 and 8 were submitted to 2000 thermal cicies between 5 and 55°C, with a dwell time of 1minute. Ali groups were' also submitted to tracture resistance test in a universal test machine. The load was applied vertically through a metalic sphere of 4,5 mm diameters positioned to touch only the cusps and never the restorations or margins ot cavities. The mean load necessary to tracture the samples in each group were (in kgf): G1 =208,04(A); G2=200,9(A); G3=66,28(B); G4=67,90(B); G5=168,20(C); G6=118,44(D); G7=202,66(A); G8=172,02(C). These data were submitted to Student's test that demonstrated diterences among some groups showed above with different letters. Those results show that restorations with adhesive materiais can recover, in some degree, the fracture resistance of maxillary premolars lost in cavity preparation. H oweve r, it also shows that the artificial aging, through thermal ciclying, has a deleterious effect on reinforcement of the dental structure, suggesting a transitoriness of the bond between adhesive systems and dental tissues / Doutorado / Dentística / Doutor em Clinica

Orientador: Monica Campos Serra / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-25T21:21:31Z (GMT). No. of bitstreams: 1 Magalhaes_ClaudiaSilamide_D.pdf: 3601451 bytes, checksum: 40e0276b094752f2e3dcbfd845829566 (MD5) Previous issue date: 2000 / Resumo: Este estudo teve como objetivo avaliar a rugosidade superficial de duas resinas modificadas por poliácidos e de um ionômero de vidro modificado por resina, submetidos a doistrattmrentos superfzciais de acabamento e polimento, em função do tempo, através de um modelo experimental in situo Vinte voluntários utilizaram, durante 28 dias cansecutivos, dispositivos acrz1icos intra-bucais, contendo corpos-de-proVQ confeccionados com um ionômero de vidro modificado por resina - Fuji 11 LC lmproved (aC) e com duas resinas compostas modificadas por poliácidos - Compoglass F (Vivadent) e Dyract AP (Dentsply I DeTrey). Os corpos-de-prova de dimens&s padronizadas (n=20) foram submetidos a acabamento e polimento com um sistema de discos de lixa a base de óxido de alumínio (Sof-Lex - 3M) ou com pontas de resina impregnadas com éxido de alumínio (Enhance - Dentsply). O grupo controle não recebeu acabamento e polimento, sendo apenas polimerizado contra a superjIcie de uma tira de matriz de poliéster. A cada voluntário foi fornecido o mesmo tipo de escova dental e dentifrício, além de instruç1Jes especifzcas sohre a utilização e higieniz(Jfâo do dispositivo intra-hucal. A rugosidade superficial dos materiais foi quantificada através da medida da rugosidade média (RcJ de nove segmentos lineares predeterminad()s de cada c()rpo-de-pr()va, imediatamente após os procedimentos de acabamento e polimento (/'.0) e após 1 (1'J), 2(1'2), 3(1'3), 7(1'7), 14(1'14), 21 (l'21) e 28 (l' 28) dias de permanência no meio bucal. Para cada tempo estudado foi realizada uma análise .de covariância, considerando T{) como covariáveL Foram aplicadas a decomposição de soma de quadrados e a diferença mínima significativa de Tukey para estudar as interações signifzcativas e as comparações pareadas, ao nível de signiflCância de 5%. Os resultados foram significativos para o efeito da interação Material x Tratamento, exceto no T 28. Inicialmente, para os materiais Compoglass F e Dyract AP, o tratamento com Sof-Lex promoveu maior lisura superficial que Enhance. Os tratamentos com Sof-Lex e Enhance não .cliferiram entre si e aumentaram a rugosidade superficial de Fuji II LC Improved em relação ao controle. A() término da perÍOlJ() de ()bservaÇÕ(), ()S materiais híbridas de ionômer() de vidr() e resina composta submetidos a acabamento e polimento apresentaram rugosidade superficial semelhante ao controle, a despeit() da técnica utilizada / Abstract: The purpose of this study was to evaluate the surface roughness of two polyacid modified composite resins and a resin modified glass-ionomer submitted to two finishing and polishing treatments, as afunction oftime, using an in situ experimental modelo A resin modified glass­ionomer Fuji II LC lmproved (GC) and two polyacid modified composite resins Compoglass F (Vivadent) and Dyract AP (Dentsply / DeTrey) were analyzed. Cylindrical specimens with standardized dimensions were made using each material (n= 20). Surface treatments were erformed with Sof-Lex (3M) discs or Enhance (Dentsply) tips. Specimens of control groups were not submitted to surface treatments. Twenty volunteers ware palatal appliances in which nine specimens were flXed, during 28 days. The same kind of toothbrush and dentifrice were supplied to each volunteer. Standardized brushing technique was directed to them in order to clean the appliances up. Average surface roughness (Ra) was measured with a roughness tester (Surfcorder SE 1700) immediatelyafter the treatment (1'0) and after 1 (1'1), 2 (1'2),3(1'3), 7 (1'7J, 14 (1'14), 21 (1'21), 28 (1'28) days, under oral conditions. Nine readingsfor each specimen were averaged to give a single value. Data were submitted to Analysis of ovariance considering To values the covariate. Sums of squares decompositions followed by Tukey's Least-significant difference were used to study significative interactions and pairwise comparisons, at 5% significance levei. There was statistically significant effect of interaction Material X Treatment at each time period, excepted T28. lnitially, specimens of materiais Compoglass F and Dyract AP treated with Sof-Lex were smoother than which were treated with Enhance. There was not statistically significant difference between treatments with Sof­Lex and Enhance for Fuji 11 LC lmproved, but both increased its roughness, comparing to controlo After the exposed time to the oral conditions, it was possible to conclude that glass­ionomer composite resin hybrid materiais finished and polished surfaces presented roughness that was similar to untreated ones, regardless of the polishing method / Doutorado / Dentística / Doutor em Clínica Odontológica

Orientador: Luiz Antonio Ruhnke / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-13T23:52:27Z (GMT). No. of bitstreams: 1 Werner_SusanaMaria_M.pdf: 3021991 bytes, checksum: 8f77f820c874c190eb5e44251aeafb88 (MD5) Previous issue date: 1991 / Resumo: O objetivo deste trabalho foi avaliar "in vitro" a inflitração marginal de restaurações de amalgama em cavidades forradas com o adesivo Panavia EX e submetidas ou não ao condicionamento acido do esmalte cavo-superficial. Foram utilizados trinta dentes humanos recem-extraidos, entre os grupos de caninos e pré-molares que receberam preparos cavitarios de Classe V no terço medio da face vestibular, padronizados com o auxilio de um microscopio modificado ...Observação: O resumo, na íntegra poderá ser visualizado no texto completo da tese digital / Abstract: The purpose of this study was to evaluate, "in vitro", the effect of the adhesive resin cement lining (Pavia EX), in reducing microleakage of amalgam restorations with or without a enamel acid etching treatment. Thirty human canines and pre-molars recently extracted had received cavities preparations on the half third of the bucal face ...Note: The complete abstract is available with the full electronic digital thesis or dissertations / Mestrado / Materiais Dentarios / Mestre em Ciências

Orientador: Wolney Luiz Stolf / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-14T02:45:22Z (GMT). No. of bitstreams: 1 Duarte_RosangelaMarques_M.pdf: 1986447 bytes, checksum: 79b15a0794e37d92b9166336f4432e2e (MD5) Previous issue date: 1992 / Resumo: A infiltração marginal em restaurações de cavidades classe I com compósito e base de cimento de ionômero de vidro foi observada neste estudo "in vitro". Cavidades classe I em 21 dentes humanos do grupo dos pré-molares foram preparadas. Os dentes foram divididos em 3 grupos, sendo que as cavidades foram assim tratadas: No grupo A foram forradas com base de cimento de ionômero de vidro e restauradas com resina fluida e compósito. No grupo B foram forradas com base de cimento de ionômero de vidro, submetidas ao condicionamento ácido da base e das paredes de esmalte. em seguida restauradas com resina fluida e compósito, e no grupo C foram forradas com uma base de cimento de ionômero de vidro, as paredes de esmalte foram submetidas ao condicionamento ácido e restauradas com resina fluida e compósito. Após restaurados, os dentes permaneceram por 24 horas à temperatura de 37°C e 100% de umidade relativa do ar. Em seguida foram submetidos a 100 ciclos térmicos com temperatura variando entre 4 e 60°C. O selamento marginal foi medido usando avaliação da penetração do corante. Através de uma lupa est.ereoscópica (Carl Zeiss) os níveis de infiltração margi nal foram documentados e f'otografados. A análise dos resultados revelou que houve diferenças estatisticamente significativas quando se realizou o condicionamanto ácido do esmalte dentário, que demonstrou diminuir ou prevenir a inf'iltração marginal. O condicionamen~o ácido da base de cimento de ionômero de vidro, diferiu estatisticamente de quando não f'oi utilizado este tratamento. O uso de uma base de cimento de ionômero de vidro associado ao condicionamento ácido das paredes de esmalte impadiu a infiltração marginal em restaurações de cavidadas classe I com compósito / Abstract: The microleakage of composite resin/glass ionomer cement class I restorations was evaluated i n this "in vitro" study. A classic I cavity was prepared in 21 human pre-molares. The teeth were divided in three groups and the cavity preparations were treated as follows: in group A were lined up with a glass ionomer cement base and restored with, unfilled resin and composite resin. In group B ware lined up with a glass ionomer cement base, submitted to enamel and base acid base acid etching treatment and restored with unfilled resin and composite resin, and in group C were lined up with a glass ionomer cement base submitted to enamel acid etching treatment and restored with unfilled resin and composite resin. After being restored the teeth ware stored for 24 hs at 37°C and 100% relative air humidity. In the following step they ware submited to 100 thermal cycles in water baths ranging in temperature from 4 to 60ºC. The marginal seal were measured using a dye penetration evaluation. Using a stereoscopic microscope the levels of microleakage Were recorded and photographed . The analysis of the results showed significant statistical difference when enamel acid etching treatmen'l was used, which proved to reduce or prevent miroleakage. The use of a base acid etching treatment differed statisticaly when was not used . The use of a glass ionomer cement base with acid etching the enamel walls prevented microleakage in composite/glass ionomer class I restorations / Mestrado / Materiais Dentarios / Mestre em Odontologia

Tese (Livre-docencia) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-24T00:12:03Z (GMT). No. of bitstreams: 1 Martins_LuisRobertoMarcondes_LD.pdf: 1195672 bytes, checksum: 0aa1d6adba4c46153d9fa1b4155cbab4 (MD5) Previous issue date: 1995 / Resumo: Várias exodontias de raízes são indicadas em função de cárie, preparo intra-radicular incorreto, remoção de pinos e núcleos. A preservação dessas raizes pelo preenchimento do conduto radicular com materiais adesivos tem sido relatada na literatura. O objetivo desta pesquisa foi avaliar a resistência à fratura de raízes debilitadas preenchidas com materiais adesivos, empregando-se dentes uni-radiculares com núcleos fundidos cimentados, nas seguintes condições: controle positivo (preparo convencional), controle negativo (raízes debilitadas), raízes preenchidas com ionômeros, raízes preenchidas com ionômero fotoativado, raízes preenchidas com sistemas adesivo/compósito. Os materiais testados foram: ionômero tipo II modificado (Chelon-Silver), ionômero tipo III (Ketac-Bond), ionômero fotoativado (Vitremer), compósitos (Herculite XRV e Z 100). Após remoção da coroa clínica dos dentes, eram preparadas as raízes para receberem os devidos tratamentos. Confeccionados os padrões em resina acrílica, os mesmos eram incluídos e fundidos. Obtidos os núcleos em liga de Cu-Al, eram adaptados e cimentados no interior do conduto. Os corpos de prova eram então submetidos a carregamento em máquina de ensaio universal até ruptura da raiz. Os resultados foram expressos em kgf, tabulados e analisados estatisticamente. Concluiu-se que: entre os materiais testados o compósito Z 100 teve melhor desempenho que todos os demais e inclusive quanto ao controle positivo; o ionômero Vitremer, o compósito XRV e o Chelon-Silver apresentaram resultados semelhantes entre si e ao controle positivo; o ionômero Ketac-Bond teve comportamento desfavorável em relação a todos os outros e semelhante ao controle negativo / Abstract: Several dental roots extractions have been indicated due to carie, incorrected intra-root preparations, remotions of pin and post. The aim of this research was to evaluate the resistence fracture of debilitated root filled with adhesive materials. Unirradicular with cast and cemented post were utilized in the following conditions: positive control (conventional preparation), negative control (debilitated root), roots filled with glass ionomer (Chelon-Silver and Ketac Bond), root filled with light cured glass ionomer (Vitremer), root filled with composite/adhesive system (Herculite XRV and Z 100). After remotion of clinical crown teeth, the roots were prepared and acrilic resin mold were obtained and after, included and cast. The metallic post in Cu-Al were adapted and cemented in the root. The samples were submited to compressive strenght in an universal testing machine until rupture. The results were expressed in Kgf and analized statistically. It was concluded that: among the tested materials, the composite Z 100 presented the best performance if compared with whole materials including positive control; the Vitremer ionomer, the composite XRV, Chelon-Silver and positive control presented similar results; the Ketac-Bond ionomer had unfavorable performance in relation of all sample and similar to negative control / Tese (livre-docencia) - Univer / Dentística / Livre-Docente em Clinica Odontologica

Orientador: Simonides Consani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-18T09:58:45Z (GMT). No. of bitstreams: 1 Nobilo_MauroAntoniodeArruda_M.pdf: 3752919 bytes, checksum: 2c3ca1bddc71ac2546349338868c7383 (MD5) Previous issue date: 1993 / Resumo: O objetivo deste estudo foi avaliar in vitro a resistência à tração da união amálgama de prata-cimento de ionômero de vidro, sob a influência de sistemas adesivos. Foram confeccionados corpos de prova com diferentes dimensões para cada material em matrizes cilindricas de Teflon, possuindo na região central uma cavidade de formato tronco-cônico retentivo. A base ionomérica foi confeccionada com cimento de ionômero de vidro VID ION F. Após o acondiciomento do sistema adesivo e perfeita estabilização da matriz e contra-matriz, foi efetuada a condensação do amálgama de prata TRUE DENTALOY I I contendo alto teor de cobre ... Observação: O resumo, na íntegra poderá ser visualizado no texto completo da tese digital / Abstract: The purpose of this study was to evaluate in vitro, the bond strengths of amalgam to glass ionomer cement, under the influence of adhesive systems. Specimens with distinct dimensions were used to each material in a manufactored cylindric Teflon matrix, with a conic-retentive central cavity. The glass ionomer used as base was the VIDRION F glass ionomer cement. After the conditioning of the adhesive systems and perfect stabilization of the matrix and over-matrix, a TRUE DENTALOY II high copper amalgam was condensed ...Note: The complete abstract is available with the full electronic digital thesis or dissertations / Mestrado / Materiais Dentarios / Mestre em Ciências

Orientador: Mario Fernando de Goes / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-18T11:16:33Z (GMT). No. of bitstreams: 1 Rodrigues-Garcia_RenataCunhaMatheus_M.pdf: 3097748 bytes, checksum: da5c17bc6a20a0105ad09c6972652475 (MD5) Previous issue date: 1993 / Resumo: O propósito deste estudo foi verificar a influência de materiais protetores sobre a solubilidade em água de cimentos de ionômero de vidro restauradores, empregando o teste gravimétrico indicado pela Associação Dentária Americana, na sua Especificação n° 09 para cimento de silicato. Foram utilizados dois cimentos de ionômero de vidro restauradores (Chelon-Fil e Vidrion-R) e confeccionadas 30 amostras, com 20 mm de diâmetro por 5 mm de espessura, de cada material. Grupos experimentais de cinco amostras foram protegidos com a re¬sina fotoativada Scotchbond e Verniz-V. o grupo que não recebeu proteção foi considerado controle. Os tempos de imersão em água destilada foram de 1 hora e 24 horas, após o tempo de geleifica¬ção. Os resultados demonstraram que, independente do tempo e materiais utilizados, as amostras que não receberam proteção su¬perficial apresentaram valores de solubilidade estatisticamente diferentes ao nível de 5% de probabilidade, em relação às amos¬tras que foram protegidas. As amostras protegidas com Verniz-V apresentaram os menores índices de solubilidade e estatisticamen¬te diferentes em relação àquelas protegidas com Scotchbond. Com relação aos materiais, o Vidrion-R apresentou meno¬res índices de solubilidade em relação ao Chelon-Pil quando as amostras não foram protegidas durante o período de 1 hora. Com relação ao tempo, as amostras de Chelon-Pil sem proteção, ou protegidas não apresentaram diferenças significantes entre os dois períodos de tempo estudados, enquanto que as amos¬tras de Vidrion-R sem proteção ou protegidas com Scotchbond dife¬riram estatisticamente ao nível de 5% de probabilidade durante 1 e 24 horas, sendo que durante o período de 1 hora as amostras deste cimento foram menos solúveis em relação ao período de 24 horas / Abstract: The purpose of study was to elucidate the influence of the coating materials on water solubility of glass-ionomer filling cements using the number 09 American Dental Association guide lines for silicate cements. It was used two brands of glass-ionomer filling cements: Chelon-Fil and Vidrion-R. Thirty samples measuring 20 mm diameter and 1,5 mm in thickness were prepared from each material. Group tests of five samples were protected by light-activited bonding resin Scotchbond and other five samples by V-Varnish. The samples in wich no protection was applied were Considered controlo The time imersion in destilated water was 1 hour and 24 hours, after the inicial setting. The results were showed significantly different at 5% confidence leveI, related to solubility for the samples wich had no superficial protection applied. On the other hand, for the samples coating with scotchbond, an increased solubility significantly different was found when compared to the ones coated with V-Varnish either to Chelon-Fil as to Vidrion-R at 1 and 24 hours time. Considering the solubility, Vidrion-R was significantly different at 5% confidence leveI when compared to Chelon-Fil for the control group. The samples were protected by Scotchbond or V-Varnish, the results didn't show significantly differences, for both cements at one hour time.The Chelon-Fil samples, at 24 hours time showed results estatisticaly different when compared to Vidrion-R, when protection was applied with scotchbond. The control and the samples with V-Varnish, didn't show significantly different results, when compared between them / Mestrado / Materiais Dentarios / Mestre em Ciências

Orientador: Simonides Consani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-18T11:19:19Z (GMT). No. of bitstreams: 1 Mesquita_MarceloFerraz_M.pdf: 2921307 bytes, checksum: f7f6816179f5c37b6cabb8e216b02876 (MD5) Previous issue date: 1993 / Resumo: Este trabalho teve como objetivo avaliar in vitro o efeito do tempo de armazenagem e do condicionamento ácido sobre a resistência à tração da união entre cimento de ionômero de vidro e resina composta. Foram utilizadas 100 amostras divididas em 4 grupos de variáveis, com 5 repetições cada variável, nos períodos de tempo de: 1 hora, 1 dia, 1 semana, 1 mês e 3 meses. Para a confecção das amostras, foi utilizada uma matriz de teflon dividida em duas partes, uma para receber o cimento de ionômero de vidro e a outra para receber a resina composta. Após a confecção das amostras, as mesmas foram armazenadas em estufa, a 37°C e umidade relativa de 100% durante os períodos propostos...Observação: O resumo, na íntegra poderá ser visualizado no texto completo da tese digital / Abstract: The purpose of this study was to evaluate, in vitro, the effect of storage time and the acid atack on the tensile bond strenght between glass ionomer cement and composite resin. Hundred specimens were used divided into four variable groups with five repetitions each one, in the followed periods of time: 1 hour, 1 day, 1 week, 1 month e 3 months. To make specimens, were used a matrix of teflon divided into two portions: one for glass ionomer cement another for composite resin. After preparation, the specimens were stored in 37ºC and 100% relative umidity during the periods proposed ...Note: The complete abstract is available with the full electronic digital thesis or dissertations / Mestrado / Materiais Dentarios / Mestre em Ciências