Orientadores: Mario Fernando de Goes, Marcela Rocha de Oliveira Carrilho / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-13T06:17:38Z (GMT). No. of bitstreams: 1 Almeida_JulioCesarFranco_D.pdf: 499079 bytes, checksum: 777476c1e47008d96a6038604656dce4 (MD5) Previous issue date: 2009 / Resumo: O objetivo geral deste estudo foi avaliar in vitro os efeitos de variações na umidade dentinária no estabelecimento e durabilidade da união resina-dentina através da associação de materiais e técnicas que apresentam potencial para uso em restaurações adesivas. Para atender ao objetivo geral, dois estudos com objetivos específicos foram propostos: 1) avaliar os efeitos da condição de umidade da dentina na durabilidade da resistência da união (RU) à dentina obtida por meio da associação de oxalato de potássio com primers a base de água ou etanol. 2) avaliar os efeitos da técnica úmida utilizando etanol na durabilidade da RU à dentina obtida através do uso de primers com características hidrofílicas e hidrofóbicas. Os primers experimentais foram preparados utilizando-se a proporção 35% monômeros / 65% solventes (v/v), como se segue: HEMA/água, HEMA/etanol, Bis-GMA/etanol e um agente de união com características hidrofóbicas (Adper Scothbond Multi-Purpose adhesive, 3M/ESPE) foi usado nos dois estudos. A RU foi avaliada pelo teste de resistência à microtração 24 h após a realização do procedimento adesivo ou após 6 meses de armazenamento em água, utilizando-se dentes humanos hígidos recém extraídos para confecção das amostras de acordo com os objetivos específicos de cada estudo. Os resultados do estudo 1 mostraram que de uma maneira geral a associação de oxalato de potássio com primers a base de água e etanol reduziu significativamente a RU imediata e a longo prazo para os primers a base de água e etanol, independente da condição de umidade da dentina. Os resultados do estudo 2 indicaram que a técnica úmida com etanol resultou em maior RU imediata para os primers com características hidrofílicas e hidrofóbicas enquanto o armazenamento em água por 6 meses diminuiu a RU para o primer hidrofílico, independente da técnica utilizada. / Abstract: The overall goal of this investigation was to evaluate in vitro the effects of dentin moisture variations in the establishment and durability of the resin-dentin bonds by the association of materials and techniques with potential for use in adhesive restorative procedures. In order to meet the overall objective, two studies with specific goals were proposed. 1) to evaluate the effects of dentin moisture condition on the durability of the bond strength (BS) to dentin produced by the association of potassium oxalate with experimental water-and ethanolbased primers; 2) to evaluate the effects of the ethanol wet-bonding technique on the durability of the BS produced with the use of experimental primers with hydrophilic and hydrophobic characteristics. The experimental primers were prepared using the proportion 35% monomers / 65% solvents (v/v) as follows: HEMA/water, HEMA/ethanol, Bis-GMA/ethanol and the same bonding agent with hydrophobic characteristics was used in both studies (Adper Scothbond Multi- Purpose adhesive, 3M/ESPE). A microtensile bond strength test was performed 24 h after bonding procedures and 6 months after water storage, using freshly extracted noncarious human teeth for specimen preparation according to the specific goals of each study. In general, the results of study 1 showed that the association of potassium oxalate with water-and ethanol-based primers reduced significantly the immediate and long-term BS, regardless of the dentin moisture condition. The results of study 2 showed that the ethanol wet-bonding technique resulted in higher immediate BS for the hydrophilic and hydrophobic primers, while 6-month water storage reduced the BS for the hydrophilic primer, regardless of the employed bonding technique. / Doutorado / Doutor em Materiais Dentários

Orientador: Marcelo Giannini / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-13T10:19:14Z (GMT). No. of bitstreams: 1 Oliveira_MarceloTavaresde_D.pdf: 15233943 bytes, checksum: f6125d2132f3fd48d81be1d3cda778aa (MD5) Previous issue date: 2009 / Resumo: O uso de técnicas alternativas para preparo cavitário vem ganhando grande importância na Odontologia moderna. Entre estas tecnologias, o laser tem sido alvo de inúmeros estudos e para a realização de preparos cavitários o laser de Er:YAG é um dos mais indicados. Os objetivos deste estudo foram avaliar os efeitos de diferentes parâmetros de irradiação do substrato dentinário com laser de Er:YAG nos procedimentos restauradores adesivos e suas conseqüências sobre o substrato e sobre a união resina-dentina. Os testes foram realizados em superfícies dentinárias planificadas de terceiros molares humanos hígidos unidos a três diferentes sistemas adesivos (Single Bond 2 - 3M ESPE, Clearfil Protect Bond - Kuraray Medical Inc. e Clearfil Tri-S Bond - Kuraray Medical Inc.). Estas avaliações compreenderam o estudo da permeabilidade dentinária, da resistência de união, da longevidade e qualidade da união, além da análise da ultra-estrutura da interface de união através de microscopia eletrônica de transmissão e microscopia de varredura confocal laser. Os dados de permeabilidade e resistência de união foram analisados e submetidos à análise estatística com ANOVA 1-critério e ANOVA 3-critérios, respectivamente; ao encontrar diferenças significativas, o teste de Tukey foi utilizado. O nível de significância foi fixado em 5%. Os resultados mostraram ocorrer uma redução significativa na permeabilidade dentinária e que o parâmetro de 120mJ/4Hz foi o que promoveu a maior redução. Quanto à resistência de união, este estudo demonstrou que inicialmente, a irradiação com laser de Er:YAG reduz os valores de resistência de união, no entanto após 6 meses os valores são semelhantes tanto para o grupo controle, quanto para os grupos que foram irradiados. Além disso, pôde ser observado, que os sistemas autocondicionantes foram menos susceptíveis aos efeitos da irradiação do substrato, apresentando um comportamento mais uniforme. O sistema autocondicionante de dois passos também se mostrou mais estável ao longo do tempo. As imagens em microscopia eletrônica de transmissão e microscopia de varredura confocal laser, mostraram a formação de camada híbrida para todos os adesivos estudados com diferentes espessuras, quando aplicados sobre a dentina abrasionada. Não foi possível identificar camada híbrida uniforme e bem definida quando os sistemas foram aplicados em dentina irradiada com laser de Er:YAG, independentemente do parâmetro utilizado. Diante disso, os resultados sugerem que a irradiação da dentina com laser de Er:YAG reduz a permeabilidade dentinária, podendo influenciar na união dos adesivos à dentina nos períodos iniciais, entretanto após 6 meses os grupos irradiados foram iguais ao grupo controle. O exame ao microscópio revelou que a formação da camada híbrida é irregular e não-uniforme quando a dentina foi irradiada. / Abstract: The use of alternative techniques for cavity preparation is more common nowadays. Among these technologies, laser is the target of a great number of studies. The objectives of this study were to evaluate the effects of different parameters of dentin irradiation with Er:YAG laser on the adhesive procedures and their consequences over the substrate and resin dentin interface. Procedures were performed over flat dentin surfaces of human third molars bonded to three different adhesive systems ((Single Bond 2 - 3M ESPE, Clearfil Protect Bond - Kuraray Medical Inc. e Clearfil Tri-S Bond - Kuraray Medical Inc.). The evaluation tests were: dentin permeability, microtensile bond strengths, durability and the analysis of the ultra-structure using transmission electron microscope (TEM) and confocal laser scanning microscope (CSLM). Dentin permeability data and microtensile bond strength data were analyzed with one-way ANOVA and three-way ANOVA, respectively. Tukey test was used to point out differences among the tested groups. The significance level was fixed at 5%. Results showed a significative reduction on the dentin permeability and the 120mJ/4Hz parameter promoted the greatest reduction. For the microtensile bond strength test, this study showed that the irradiation with Er:YAG laser reduce the bond strength values at the baseline. After six months all groups became similar. Furthermore, self-etching systems were less affected by the Er:YAG laser irradiation. The two-step self-etching system seemed the more stable over time. TEM and CLSM images showed the hybrid-layer formation for all adhesive tested. The hybrid-layers had different thicknesses when the adhesive systems were bonded to abraded dentin. The observation of a uniform and well defined hybrid-layer was not possible when the adhesive systems were bonded to laser irradiated dentin, regardless of the used parameter. According to the data presented, dentin irradiation with Er:YAG laser reduce the permeability of the substrate, interfering on the bonding strength to dentin at the baseline, however, after six months laser irradiated groups were similar to control groups. Microscope analysis revealed that hybrid layer formation was irregular and non-uniform when dentin was laser irradiated. / Doutorado / Doutor em Materiais Dentários

Submitted by Divisão de Documentação/BC Biblioteca Central (ddbc@ufam.edu.br) on 2017-07-18T14:35:48Z No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Reprodução Não Autorizada.pdf: 47716 bytes, checksum: 0353d988c60b584cfc9978721c498a11 (MD5) / Approved for entry into archive by Divisão de Documentação/BC Biblioteca Central (ddbc@ufam.edu.br) on 2017-07-18T14:36:03Z (GMT) No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Reprodução Não Autorizada.pdf: 47716 bytes, checksum: 0353d988c60b584cfc9978721c498a11 (MD5) / Approved for entry into archive by Divisão de Documentação/BC Biblioteca Central (ddbc@ufam.edu.br) on 2017-07-18T14:36:19Z (GMT) No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Reprodução Não Autorizada.pdf: 47716 bytes, checksum: 0353d988c60b584cfc9978721c498a11 (MD5) / Made available in DSpace on 2017-07-18T14:36:19Z (GMT). No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Reprodução Não Autorizada.pdf: 47716 bytes, checksum: 0353d988c60b584cfc9978721c498a11 (MD5) Previous issue date: 2016-03-07 / CNPq - Conselho Nacional de Desenvolvimento Científico e Tecnológico / The copaiba oleoresin, extracted from Copaifera multijuga Hayne is used popularly for various purposes. Because of biological properties, a copaiba oil emulsion was formulated to be used before applying the adhesive in order to improve the quality of dentin bonding. The aim of this study was to evaluate the morphological characteristics of the dentin surface and the hybrid layer formed with etch-and-rinse and self-etching adhesive systems in sound and caries-affected dentin after using copaiba oil emulsion. 96 third molars from Biobank of the School of Dentistry, University Federal of Amazonas, were used. Half of the teeth underwent artificial induction of dental caries and the other half was formed by sound teeth. All teeth had their roots removed; yielding dentine disks were divided into groups according to test substances (2% chlorhexidine, copaiba oil emulsion, calcium hydroxide solution and distilled water), the dentin (sound or caries-affected) and the adhesive system (Adper Single Bond 2® or Clearfil SE Bond®). The dentin surface and the hybrid layer of the obtained specimens were analyzed by SEM according to the experimental groups. The treatment of dentin surface with copaiba oil emulsion showed no physical barrier to the adhesive penetration. The dentin surface treated with 2% chlorhexidine showed phosphate salts in two types of dentin. The treatment of the dentin surface with calcium hydroxide solution resulted in the deposition of mineral precipitate obstructing the lumen of the tubules in sound dentin. The calcium hydroxide solution applied on the conditioned sound dentin was different from the other substances (p<0.05). In smeared surface, distilled water in sound dentin showed a significant difference from all experimental groups (p <0.05). There was no statistical difference between the hybrid layer formed with the Adper Single Bond 2® adhesive in sound and caries-affected dentin treated with the test substances. The hybrid layer with Clearfil SE Bond® in caries-affected dentin treated with copaiba oil emulsion showed no statistical difference in relation to the tested substances, shown statistical difference only with calcium hydroxide solution in caries-affected dentin (p <0.05). In sound dentin, there was no statistical difference in the hybrid layer with Clearfil SE Bond® irrespective of the tested substances. The application of copaiba oil emulsion showed no morphological change in sound and caries-affected dentin, regardless of phosphoric acid etching; and presented a uniform hybrid layer, regular and large monomer infiltration in sound and caries-affected dentin, regardless of the adhesive system. / O óleo-resina de copaíba, extraído da Copaifera multijuga Hayne é usado, popularmente, com diversas finalidades. Diante das suas propriedades biológicas, foi criada uma emulsão à base de óleo de copaíba para ser usada antes da aplicação do adesivo com a finalidade de melhorar a qualidade da adesão dentinária. O objetivo do estudo foi avaliar as características morfológicas da superfície dentinária e da camada híbrida formada com os sistemas adesivos convencional e autocondicionante nas dentinas hígida e afetada por cárie após o uso da emulsão à base de óleo de copaíba. Foram utilizados 96 terceiros molares humanos hígidos do Biobanco da Faculdade de Odontologia da Universidade Federal do Amazonas (FAO – UFAM). Metade dos dentes sofreu indução artificial de cárie e a outra metade foi formada pelos dentes hígidos. Todos os dentes tiveram suas raízes removidas, obtendo-se discos de dentina que foram divididos em grupos de acordo com as substâncias testes (clorexidina a 2%, emulsão à base de óleo de copaíba, solução de hidróxido de cálcio e água destilada), o substrato dentinário (hígido ou cariado) e o sistema adesivo (Adper Single Bond 2® ou Clearfil SE Bond®). A superfície dentinária e a camada híbrida dos espécimes obtidos foram analisadas em MEV, de acordo com os grupos experimentais. O tratamento da superfície dentinária com emulsão à base de óleo de copaíba não apresentou nenhuma barreira física aparente à penetração do adesivo. A superfície dentinária tratada com clorexidina a 2% apresentou sais de fosfato nos dois tipos de dentina. O tratamento da superfície com solução de hidróxido de cálcio resultou na deposição de precipitado mineral, obstruindo a luz dos túbulos dentinários em dentina hígida. A solução de hidróxido de cálcio aplicada sobre a dentina hígida condicionada foi diferente das demais substâncias (p<0,05). Na superfície não condicionada, a água destilada em dentina hígida apresentou diferença significativa em relação a todos os grupos experimentais (p< 0.05). Não houve diferença estatística entre as camadas híbridas formadas com o adesivo Adper Single Bond 2® nas dentinas hígidas e afetadas por cárie tratadas com as substâncias testes. A camada híbrida com Clearfil SE Bond® na dentina afetada por cárie tratada com emulsão à base do óleo de copaíba não apresentou diferença estatística em relação às substâncias testes, apresentando diferença somente em relação à solução de hidróxido de cálcio na dentina afetada (p<0,05). Na dentina hígida, não houve diferença estatística na camada híbrida com Clearfil SE Bond®, independente das substâncias testadas. A aplicação da emulsão à base de óleo de copaíba não apresentou nenhuma alteração morfológica nas superfícies dentinárias hígida e afetada por cárie, independente do condicionamento com ácido fosfórico; e apresentou uma camada híbrida uniforme, regular e com grande infiltração monomérica nas dentinas hígida e afetada por cárie, independente do adesivo utilizado.

Com o intuito de elevar os valores de resistência à fratura dos dentes que sofreram tratamento endodôntico, várias técnicas restauradoras têm sido desenvolvidas. Atualmente os sistemas de pinos de fibras de carbono e de vidro são os dispositivos mais utilizados, devido às suas vantagens de possuírem módulo de elasticidade próximo ao da dentina, o que causa menor estresse e conseqüentemente menor quantidade de fraturas radiculares, além de não necessitarem da fase laboratorial. A escolha do cimento utilizado para a cimentação desses pinos, tem grande importância e o advento dos cimentos resinosos e dos sistemas adesivos que com eles podem ser empregados, representam uma grande evolução em razão das possibilidades de se obter retenções micromecânicas no interior dos condutos. Assim, o objetivo deste estudo foi avaliar a resistência à extrusão de pinos de fibras de vidro cimentados com cimento resinoso Rely X ARC com a aplicação de três diferentes sistemas adesivos: Scotchbond, Single bond e Adper Prompt LPop. Após a cimentação os espécimes foram seccionados em duas regiões, apical e cervical, que constituía cada uma um corpo de prova. Para possibilitar a realização do teste de extrusão, utilizou-se um dispositivo de aço inoxidável que estabilizava o corpo de prova. Este dispositivo tinha um orifício central que permitia o deslocamento do pino ou do cimento, durante o teste de extrusão. Para o teste de extrusão o corpo de prova foi adaptado no dispositivo com a face cervical voltada para baixo e uma ponta ativa com extremidade plana (1mm de diâmetro) foi adaptada à máquina de ensaios universal que exercia uma força de extrusão o mais próximo possível do centro do pino. O teste foi realizado com um deslocamento de 0,5mm por minuto, onde a carga máxima de falha foi registrada em kgf. No que diz respeito ao cimento resinoso Rely X ARC, em combinação com os adesivos utilizados, os melhores resultados na região cervical da raiz foram obtidos com o cimento Rely X com o sistema adesivo Scotchbond, seguido pelos sistemas Adper Prompt e Single bond. Na região apical o Scotchbond foi melhor que o Adper Prompt e o Single bond, mas não houve diferença estatisticamente significante entre o Adper Prompt e Single bond. / In order to increase strength to fracture of endodontically treated teeth, a number of restorative techniques were developed. Nowadays, carbon and glass fiber post systems are the most used due to their advantages of modulus of lasticity similar to dentin, which lead to lower stress and consequently lower number of root fractures, besides no laboratorial work is needed. The choice of the best cement for luting these posts is an important step and the development of resin cements and adhesive systems that can be use with posts are a great evolution due to the possibility of micromechanical retention in roots. Therefore, the aim of this study was to evaluate extrusion strength of glass fiber posts cemented with resin luting cement Rely X ARC using three different adhesive systems: Scothbond, Single bond and Adper Prompt L Pop. After luting, samples were seccionated in two regions, apical and cervical, each one representing one sample. A stainless steel device was used to perform extrusion test, stabilizing samples. This device had a central orifice that allowed movement of post or cement, during extrusion test. For extrusion test, sample was adapted in the device with cervical face directed to down and a plane surface active point (1 mm diameter) was adapted to the universal test machine which exerted an extrusion force in the center of post. Test was performed with 0.05 mm per minute and the maximum load at failure was registered in kgf. Regarding resin luting cement Rely X ARC combining with adhesive systems, the best results at cervical were obtained with Rely X and Scotchbond adhesive, followed by Adper Prompt and Single bond systems. At apical region Scotchbond was better than Adper Prompt and Single bond, but there was no statistically significant difference between Adper Prompt and Single bond.

Este estudo avaliou a influência do uso do digluconato de clorexidina como inibidor de metaloproteinase na resistência adesiva e dureza da camada de adesivo e camada hibrida de uma resina composta à dentina humana, por meio de ensaio de microtração e nanoedentação. Os fatores de variação estudados foram dois sistemas adesivos com estratégias de aplicação distintas Adper Scotchbond Multi-Purpose (3M ESPE, St. Paul, MN, USA) e Clearfil SE Bond (Kuraray Co., Osaka, Japan), e ainda foram realizados tratamentos no substrato dentinário utilizando duas concentrações de digluconato de clorexidina sendo estas 2% e 0,2% e grupos controle sem tratamento com clorexidina. As unidades experimentais foram compostas por 48 molares humanos hígidos divididos aleatoriamente em 6 grupos (n=8). Nestes foram aplicados os procedimentos adesivos e realizados os tratamentos de superfície, com clorexidina, previamente aos procedimentos adesivos. Após esta etapa foram confeccionadas as restaurações com espessura de 5mm sobre as superfícies dentinárias. Após 24h de armazenamento em água destilada, os dentes restaurados foram cortados para a obtenção de corpos de prova em forma de palito, com secção transversal de aproximadamente 1mm2. De cada grupo foram selecionados aleatoriamente 5 palitos para o ensaio de dureza. O restante dos palitos viáveis de cada dente foram submetidos ao teste de microtração a uma velocidade de 0,5mm/min até que ocorresse a fratura da interface adesiva. Para o teste de nanoedentação cada um dos 5 palitos referentes aos 6 grupos estudados receberam 10 endentações, sendo 5 na camada de adesivo e 5 na camada hibrida, com distância de 10m entre si. Essas endentações foram realizadas com ultramicrôdurometro (DUH-W211S, Shimadzu Co., Tokyo, Japan). Os dados referentes aos testes de microtração dos seis grupos foram submetidos à análise de variância e teste de Tukey (p<0,05). As médias dos grupos foram: Grupo 1: Clearfil SE controle ( 28.50±0.47); Grupo 2: Adper Scotchbond controle (43.90±7.26); Grupo3: Clearfil SE/ clorexidina 2% (30.43±6.59); Grupo 4: Adper Scotchbond/ clorexidina 2% (39.21±4.69); Grupo 5: Clearfil SE 0,2%( 27.28±7.05); Grupo 6: Adper Scotchbond/ clorexidina 0,2% (35.70±6.43). Na comparação entre as médias dos grupos obteve-se que nenhum dos adesivos testados apresentou alteração na sua resistência de união com o uso do digluconato de clorexidina a 2% ou a 0,2% em análise imediata. Os grupos em que foi utilizado o adesivo Scotchbond apresentaram maiores valores de resistência de união que os grupos em que foi utilizado o sistema adesivo autocondicionante (Clearfil) independente da realização ou não do tratamento de superfície com digluconato clorexidina. Os valores de dureza da camada de adesivo não apresentaram diferenças estatisticamente significantes entre os grupos controle ou entre tratamentos, apenas o grupo com tratamento prévio Clearfil SE/Clorexidina 0,2% apresentou maior valores de dureza na camada de adesivo quando comparado ao grupo Scotchbond com a mesma concentração de clorexidina. Quanto aos valores de dureza da camada híbrida o grupo controle Clearfil SE quando comparado ao grupo Clearfil SE/Clorexidina 2% apresentou menor valor de dureza da camada hibrida. O Scotchbond controle apresentou menor valor de dureza na camada hibrida quando comparado ao grupo Scotchbond com clorexidina a 0,2%. O uso do digluconato de clorexidina nas concentrações 2% e 0,2% em dentina humana, apesar de ter apresentado discretas alterações na dureza da camada hibrida e camada de adesivo, não tiveram a capacidade de afetaram os valores de adesão à dentina dos diferentes adesivos testados. / This study evaluated the influence of the use of chlorhexidine gluconate as an inhibitor of metalloproteinase bond strength and hardness of the adhesive layer and hybrid layer of a composite resin to dentin, using microtensile test and nanoindentation. The variation factors studied were two adhesive systems with different implementation strategies Adper Scotchbond Multi-Purpose (3M ESPE, St. Paul, MN, USA) and Clearfil SE Bond (Kuraray Co., Osaka, Japan), and were still held treatments to dentin using two concentrations of chlorhexidine digluconate and these 2% and 0.2% untreated control groups with chlorhexidine. The experimental units were composed of 48 human molars were randomly divided into 6 groups (n = 8). These procedures were applied adhesives and surface treatments performed with chlorhexidine prior to bonding procedures. After this step the restorations were made with 5mm thickness on the dentin surfaces. After 24 hours storage in distilled water, the samples were cut to obtain specimens toothpick shaped cross-section of approximately 1mm2. Each group were randomly selected 5 toothpicks for hardness testing. The remaining viable sticks of each tooth were subjected to microtensile testing at a crosshead speed of 0.5 mm / min until the fracture of the adhesive interface. To test nanohardness each of the five toothpicks referring to six groups received 5 indentations in the adhesive layer and 5 indentations in the hybrid layer with 10m away from each other. These indentations were performed with the equipament DUH-W211S (Shimadzu Co., Tokyo, Japan). The data relating to microtensile test of the six groups were subjected to analysis of variance and Tukey test (p <0,05). The means of the groups were: Group 1: Clearfil SE control (28.50 ± 0:47), Group 2: Adper Scotchbond control (43.90 ± 7.26); Group3: Clearfil SE / 2% chlorhexidine (30.43 ± 6:59), Group 4: Adper Scotchbond / 2% chlorhexidine (39.21 ± 4.69), Group 5: Clearfil SE 0.2% (27.28 ± 07.05), Group 6: Adper Scotchbond / chlorhexidine 0.2% (35.70 ± 6:43). Comparing the means of the groups it was found that none of the adhesives tested showed a change in its bond strength with the use of chlorhexidine gluconate 2% or 0.2% in immediate analysis. The groups that used Scotchbond showed higher bond strength than the groups that used the adhesive system (Clearfil) regardless of performance or not the surface treatment with chlorhexidine digluconate. The hardness values of the adhesive layer did not show statistically significant differences between the control groups or between treatments, the group previously treated with Clearfil SE / Chlorhexidine 0.2% showed higher hardness values in the adhesive layer when compared to Scotchbond with the same concentration of chlorhexidine. As for the hardness of the hybrid layer control group Clearfil SE when compared to Clearfil SE / 2% Chlorhexidine showed lower hardness value of the hybrid layer. The Scotchbond control showed lower hardness value in the hybrid layer when compared to Scotchbond with 0.2% chlorhexidine.The use of chlorhexidine gluconate at concentrations 2% and 0.2% in human dentin, despite having discrete changes in the hardness of the hybrid layer and adhesive layer, did not have the ability to affect the values of adhesion to dentin of different adhesives tested.

Diante da grande preocupação atual por sorrisos que também embelezem um rosto, a escolha por materiais estéticos impulsiona pesquisas, que tem como objetivo não só melhorar a qualidade, mas, facilitar o uso desses materiais pelos profissionais. Assim, a proposta desse trabalho foi avaliar a influência da ciclagem mecânica na resistência de união de uma resina composta associada a um sistema adesivo convencional e um autocondicionante à dentina humana hígida por meio de teste de microtração. Para o estudo, foram utilizados 40 terceiros molares humanos hígidos, nos quais as faces oclusais foram lixadas até a obtenção de uma superfície plana com exposição do tecido dentinário. Os dentes foram divididos, aleatoriamente, em quatro grupos (n=10) de acordo com o sistema adesivo utilizado e a realização ou não da ciclagem mecânica: G1 Sistema adesivo Adper Single Bond 2 sem ciclagem mecânica (SB); G2 Sistema adesivo Clearfil SE Bond sem ciclagem mecânica (CF); G3 - Sistema adesivo Adper Single Bond 2 com ciclagem mecânica (SBC); G4 - Sistema adesivo Clearfil SE Bond sem ciclagem mecânica (CFC). Blocos de resina composta foram confeccionados nas superfícies dentinárias após aplicação do sistema adesivo correspondente. Após esse passo, os espécimes dos grupos 3 e 4 passaram por ciclagem mecânica enquanto o restante ficou armazenado em água destilada, mantidos em estufa à 37ºC até o momento do recorte dos espécimes para o teste de microtração. Os corpos de prova foram seccionados em planos perpendiculares à área de união para obtenção de espécimes com área de secção transversal aproximada de 1,0 mm², que foram tracionados, em máquina de ensaios universal, a velocidade de 0,5mm/min. Os resultados de resistência de união foram analisados usando o teste estatístico análise de variância e os modos de fratura foram avaliados em lupa estereoscópica (25X). Não foram encontradas diferenças estatísticas entre os grupos (p<0,05). Pôde-se concluir que não houve influência da ciclagem mecânica nos valores de resistência de união da resina composta associada a ambos os sistemas adesivos utilizados. / In face of an increasing concern about a smile profile that also enhances the overall facial appearance (esthetics), the choosing for more esthetic restorative materials, set in motion researches that have as objective not only the improvement of the quality, but also the easiness of use of these materials by clinicians. The purpose of this in vitro study was to evaluate, by means of a micro tensile test, the influence of the mechanical cycling, on the bond strength of a resin composite, associated to a total etch and a self etching adhesive systems, on the surfaces of sound human dentin. For this study, forty freshly extracted third molars had their oclusal surfaces grounded parallel-flat, until the dentin surfaces were completely exposed. The teeth were randomly divided in four groups (n=10) in accordance with the type of adhesive system and the mechanical cycling treatment, being: G1 Adper Single Bond 2 without mechanical cycling (SB); G2 Clearfill SE Bond without mechanical cycling (CF); G3 - Adper Single Bond 2 with mechanical cycling (SBC); G4 - Clearfill SE Bond without mechanical cycling (CFC).Following the application of the adhesive systems, regarding to each experimental condition, blocks of Z-250 composite were built, on the dentinal surfaces. After this step, the G3 and G4 specimens were submitted to the mechanical cycling test, while the G1 and G2 specimens were kept stored in distilled water at 37°C, until the moment of sectioning for the microtensile test. The specimens were seccionated perpendicularly to their adhesive area to obtain beam shaped specimens with approximate cross-section area of 0.8mm2, which were readily submitted to the microtensile test in a universal test machine with a crosshead speed of 0.5mm/min. The fracture modes were evaluated by means of a stereoscopic microscope (25x). There were no significant statistical differences founded in the bond strength values among the tested groups.

Investigou-se a influência da inclinação das paredes de dentina (paralela ou perpendicular à ação da gravidade) e da variação regional dos espécimes (terços cervical ou oclusal) na resistência adesiva e na espessura da camada de adesivo. Vinte e cinco molares humanos foram seccionados no sentido mésio-distal e paralelamente ao seu longo eixo, obtendo-se secções vestibulares e linguais, as quais foram lixadas produzindo-se superfícies planas de dentina. Sistemas adesivos (Adper Single Bond-SB e Prime & Bond 2.1- PB2.1) foram aplicados na dentina, ora paralelamente ora perpendicularmente à ação da gravidade, padronizando-se o volume de adesivo (3,5 µl por gota) através do uso de uma micropipeta e seguindo-se as instruções dos fabricantes. Os grupos de estudo foram: 1A (SB, paralelo), 1B (SB, perpendicular), 2A (PB2.1, paralelo) e 2B (PB2.1, perpendicular). Após 24h de armazenamento em água deionizada a 37°C, espécimes foram preparados na forma de palitos de dentina com área adesiva de 0,8 mm2, aproximadamente. Na seqüência, foi determinada a espessura do adesivo de cada espécime, em micrômetros (µm), sob microscopia óptica (200X de aumento) e auxílio do programa Image Pro-Plus 4.5. Posteriormente, os espécimes foram submetidos à microtração sob velocidade de 0,5 mm/min. Todos os espécimes fraturados foram examinados sob microscopia óptica (40X de aumento) para a determinação dos planos de fratura. Os dados coletados foram submetidos aos testes ANOVA a 1 e 2 critérios e SNK (? = 0,05). Para determinação da correlação entre resistência adesiva e espessura do adesivo foi utilizado o teste de Correlação de Pearson. Os valores médios (MPa±d.p.) de resistência adesiva dos grupos 2A (52,93±15,19) e 2B (52,27±16,54) foram superiores àqueles dos grupos 1A (39,09±12,90) e 1B (32,94±12,42), independente da inclinação das paredes de dentina dos mesmos. Não houve diferença nos valores de resistência adesiva à dentina, independente da variação regional do espécime. Os valores médios (µm±d.p.) de espessura da camada de adesivo dos grupos 1A (11,24±2,92) e 1B (18,11±7,31) foram superiores àqueles dos grupos 2A (4,20±1,81) e 2B (3,87±1,29) (p > 0,05). O grupo 1B promoveu os maiores valores de espessura de adesivo, seguido do grupo 1A. As espessuras do adesivo nos grupos 2A e 2B apresentaram-se similares entre si. Houve influência da variação regional do espécime na espessura de adesivo somente para o grupo 1B. Não houve correlação entre resistência adesiva e espessura de adesivos para ambos SB e PB2.1 (r = -0,224, p = 0,112 e r = 0,099, p = 0,491, respectivamente). Conclui-se que a influência da inclinação das paredes de dentina e da variação regional dos espécimes na espessura da camada de adesivo é material-dependente, porém não influem na resistência adesiva dos sistemas adesivos à dentina. / To determine the effect of the inclination of dentin surfaces (parallel or perpendicular to the force of gravity) and the regional variation of specimens (cervical or occlusal thirds) on the dentin bond strength and adhesive layer thickness. Twenty-five extracted human molars were sectioned in a mesio-distal direction to expose flat dentin. Standardized drop volumes of adhesive systems (Single Bond-SB and Prime & Bond 2.1-PB2.1) were applied to dentin according to manufacturers instructions. Teeth were randomly divided into the following groups: 1A (SB, parallel), 1B (SB, perpendicular), 2A (PB2.1, parallel) and 2B (PB2.1, perpendicular). Teeth were stored in 37°C distilled water for 24h and then serially sectioned to obtain sticks with cross-sectional area of approximately 0.8 mm2 for microtensile bond strength test (MTBS). The thickness of adhesive layer of the MTBS specimen was determined in a light microscope at 200X magnification. Forty-eight hours after adhesion procedures the specimens were subjected to MTBS at a crosshead speed of 0.5 mm/min. After testing, the fracture modes of each specimen were determined by examination under a 40X magnification. One and two-way ANOVA and Student- Newman-Keuls-SNK tests were performed do determine differences in MTBS and in adhesive layer thickness among groups. The correlation between MTBS and adhesive layer thickness was compared with Pearson Product Moment Correlation ('alfa' = 0.05). Mean values (MPa±s.d.) for bond strength were higher for groups 2A (52.93±15.19) and 2B (52.27±16.54) than for groups 1A (39.09±12.90) and 1B (32.94±12.42), regardless of the position of dentin surfaces. There was no difference in MTBS, despite the regional variation of specimens. The thickness of adhesive systems (µm±s.d.) was higher for groups 1A (11.24±2.92) and 1B (18.11±7.31) than those for groups 2A (4.20±1.81) and 2B (3.87±1.29). Group 1B provided the greater mean values of adhesive thickness followed by the Group 1A. Similar adhesive thicknesses were found for Groups 2A and 2B, but significantly lower than the other groups. There was a significant influence of the regional variation of specimens on the adhesive thickness of group 1B. No correlation was found between bond strength and adhesive layer thickness for both SB and PB 2.1 (r = -0.224, p = 0.112 and r = 0.099, p = 0.491, respectively). The inclination of dentin surface and the regional variation of specimens on the adhesive layer thickness are materialdependent. These variables do not influence the adhesive systems bond strength to dentin.

Este estudo teve como objetivo a análise da interface de adesão à dentina humana, de um sistema restaurador adesivo à base de silorano. Foram confeccionadas cavidades com 4mm X 3mm X 5mm em 40 molares humanos extraídos divididos em 4 grupos aleatoriamente: Grupos SB e SB-6m: sistema adesivo (Adper&#x2122; Single Bond) + resina composta (Filtek Z250); Grupos P90 e P90-6m: sistema adesivo (P90 System Adhesive) + resina composta (Filtek P90&#x2122;). Em todos os grupos, as restaurações foram inseridas em 4 incrementos oblíquos. Após a restauração, os dentes foram seccionados em fatias de 0,8mm de espessura em uma máquina de cortes com um disco de diamante. Uma fatia de cada dente foi separada aleatoriamente para análise em microscópio óptico para verificação de fendas na interface adesiva. As demais fatias foram seccionadas em palitos (0,8mm X 0,8mm) para os testes de microtração em uma máquina de ensaios universal EMIC. Os e dos grupos SB e P90 permaneceram em água deionizada em estufa a 370C por 24 horas e os grupos SB-6m e P90-6m permaneceram em água deionizada em estufa a 370C por um período de 6 meses. Os resultados de resistência de união foram submetidos à análise de variância a 2 critérios ANOVA e a presença de fendas internas foi analisada pelo testeChi-quadrado. Houve diferença estatisticamente significante na resistência de união entre os materiais (p>0,05) e tempo de armazenagem. Quanto à presença de fendas internas, foi evidenciada sua presença em todos os grupos, sem diferença etatisticamente significante entre eles (p>0,05). Conclui-se que não houve diferença entre os sistemas restauradores á base de Bis-GMA e de silorano os 2 períodos avaliados (24h e 6 meses). / This study aimed to analyse the adhesive interface to human dentin of a silorane based adhesive system. Cavities were fabricated with 4.0 mm X 3mm X 5mm in 40 extracted human molars randomly divided into 4 groups: Groups SB and SB-6m: adhesive system (Adper&#x2122; Single Bond) + composite (Filtek Z250); Groups P90 and P90- 6m: adhesive system (P90 System Adhesive) + composite (Filtek&#x2122; P90). In all groups, the restorations were inserted in 4 oblique increments. After 24 hours, teeth were sectioned buccolingually into 0.8mm slices with diamond saw. One slice of each tooth was randomly separated for microscope analysis. The other slices were sectioned into 0.8mm X0.8mm sticks for microtensile tests in a universal testing machine EMIC. Sticks of groups SB and P90 remained in deionized water at 370C C for 24 hours and sticks of groups SB-6m and P90-6m remained in deionized water at 370C for a period of six months. After storage period . The results of bond strength were analysed by Two-way ANOVA and the presence of internal gaps was analyzed by chi-square test. There was no significant difference in bond strength between materials (p> 0.05) and storage time. Regarding the presence of internal rifts, their presence was evident in all groups, with no statistically significant difference between them (p> .05).

Este estudo avalia a resistência de união à microtração de dois cimentos resinosos (RelyXTM U200 - 3M/ESPE e RelyXTM ARC - 3M/ESPE), na fixação de restauração cerâmica, em função do tipo de tratamento ao substrato dentinário: G1, sem tratamento (cimento autoadesivo RelyX U200); G2, sistema adesivo autocondicionante de dois passos (ClearfilTM SE Bond, Kuraray /RelyXTM ARC); e G3, sistema adesivo convencional de três passos (AdperTM ScotchbondTM Multi- Purpose, 3M/ESPE /RelyXTM ARC). Trinta dentes bovinos foram selecionados, limpos e armazenados em solução neutra de timol a 0,1% a 37oC, sendo divididos aleatoriamente em três grupos experimentais (n=10). O esmalte da face vestibular foi desgastado para expor a superfície dentinária com área de 8 mm x 8 mm e submetido, em seguida, a planificação com lixas de carbeto de silício no 180, 320 e 600. Trinta blocos cerâmicos de dissilicato de lítio, IPS e-max - Ivoclar Vivadent, medindo 8 mm x 8 mm x 2 mm, foram confeccionados e suas superfícies de cimentação jateadas com partículas de óxido de alumínio (50&#x3BC;m). Previamente à cimentação, todos os blocos cerâmicos tiveram suas superfícies internas condicionadas com ácido fluorídrico e foram aplicados agentes silano. Os tratamentos em dentina e os procedimentos de cimentação seguiram as normas dos fabricantes correspondentes para cada grupo. Decorridas 24 horas da cimentação, os conjuntos dente/cimento/cerâmica foram seccionados em forma de vigas, com área aproximada de 1 mm2, adaptados à máquina universal de ensaios (INSTRON) para realização do teste de microtração, utilizando-se a célula de carga de 500N com velocidade de 0,5 mm/minuto. Os valores médios de resistência à microtração (MPa) encontrados foram: G1 (16,16 ± 7,16), G2 (27,92 ± 6,17) e G3 (25,06 ± 6,09). Os dados foram submetidos à análise de variância e ao teste de Tukey em nível de significância de 5%. O cimento resinoso autoadesivo RelyXTM U200 apresentou menor potencial de resistência de união com diferença estatística significante, quando comparado ao cimento resinoso convencional RelyXTM ARC e tratamento prévio com os adesivos convencional de três passos e autocondicionante de dois passos. Entretanto, a associação do cimento RelyXTM ARC tanto ao sistema adesivo convencional quanto ao acondicionante apresentou valores médios similares de resistência de união aos substratos dentinário e cerâmico. Dentre os tipos de fratura, após o teste de microtração, o cimento RelyXTM U200 demonstrou maior ocorrência de falhas do tipo adesiva em dentina (AD), com menor interação adesiva junto à dentina. A associação do sistema adesivo convencional ao cimento resinoso convencional evidenciou menor ocorrência de fraturas AD e maior ocorrência junto à cerâmica, quando comparada à associação do sistema adesivo autocondicionante ao cimento resinoso convencional, apesar de os resultados de resistência de união demonstrarem similaridade de valores e estatística. / This study evaluates the microtensile bond strength of two resin cements (RelyXTM U200 - 3M/ESPE and RelyXTM ARC - 3M/ESPE), in the retention of ceramic restorations according to the treatment type of the dentin substrate; G1: no treatment (RelyX U200 self-adhesive cement); G2: two-step self-etch adhesives (ClearfilTM SE Bond, Kuraray /RelyXTM ARC); and G3: three-step etch and rinse adhesives (AdperTM ScotchbondTM Multi-Purpose, 3M/ESPE /RelyXTM ARC). Thirty bovine teeth were selected, cleaned and stored in a neutral 0,1% thymol solution at 37oC, divided randomly into three experimental groups (n=10). The facial surface enamel was scaled in order to expose an area of 8mm x 8mm of the dentin surface, and subsequently planed with no 180, 320 and 600 silico n carbide sandpaper. Thirty lithium disilicate ceramic blocks, IPS e-max Ivoclar Vivadent, measuring 8mm x 8mm x 2mm were made and their surfaces sandblasted with aluminum oxide particles (50&#x3BC;m). Before cementation, the internal surfaces of all the ceramic blocks were conditioned with hydrofluoric acid and silanized. The dentin treatments and the cementation procedures followed the manufacturers norms for each group. Twentyfour hours after cementation, the tooth/cement/ceramic blocks were sectioned into beam-like structures, each with an approximate area of 1mm2, adapted to the universal testing machine (INSTRON) in order to test microtensile strength, with the load cell set at 500N, at a speed of 0.5mm/min. The mean values found for microtensile strength (MPa) were: G1 (16,16 ± 7,16), G2 (27,92 ± 6,17) and G3 (25,06 ± 6,09). The data were submitted to analysis of variance and to Tukeys test, with a 5% significance level. The self-adhesive resin cement RelyXTM U200 presented the lowest potential bond strength, with a statistically significant difference when compared to the conventional resin cement RelyXTM ARC and prior treatment with three-step etch and rinse adhesives and two-step self-etch adhesives. However the association of the RelyXTM ARC cement, both with the conventional adhesive system and with the self-etch adhesives produced similar mean values for bond strength in the dentin and ceramic substrates. Among the types of fracture, following the test for microtensile strength, the RelyXTM U200 cement presented the highest incidence of faults of the dentin adhesive (DA) type, and the lowest adhesive interaction with the dentin. The association of the conventional adhesive system with conventional resin cement presented a lower incidence of DA fractures and a higher incidence along the ceramics, when compared to the association of the self-etch adhesive system and conventional resin cement, despite the similarity in the numbers and statistics of the bond strength results.

O LASER tem sido utilizado previamente a polimerização de sistemas adesivos em dentina como uma estratégia para melhorar as suas propriedades. O objetivo deste estudo foi investigar o efeito do LASER de diodo na sorção (SB), solubilidade e grau de conversão das principais categorias de sistemas adesivos. Quatro sistemas adesivos foram testados: convencional de 3 passos (Adper&#x2122; Scotchbond&#x2122; Multi-Purpose-MP), convencional de 2 passos (Adper&#x2122; Single Bond 2-SB), autocondicionante de 2 passos (Clearfil&#x2122; SE Bond-SE) e o sistema universal (Adper&#x2122; Single Bond Universal-SU). O adesivo fluido foi dispensado numa matriz de teflon (6.0 x 6.0 x 1 m),irradiado com laser de diodo com 970 nm e polimerizado com luz LED. Para o teste de sorção e solubilidade foram preparados espécimes em uma matriz de teflon quadrada (n=10): MP, SB, SE e SU (sem irradiação) e MP-L, SB-L, SE-L e SU-L (grupos com irradiação). Essa mensuração foi monitorando a mudança de massa depois dos ciclos de armazenamento de desidratação/ água. Para o grau de conversão, espécimes similares eram preparados e divididos 8 grupos iguais (n=5), utilizando a espectroscopia infravermelho transformada de Fourrrier (FTIR) com reflectância total atenuada (ATR). Cada espécime era comprimido contra o cristal do ATR (diamante/ZnSe) com um pressão micrométrica. As amostras não polimerizadas (&#x2248;3.0&#x3BC;L, n=5) de cada adesivo era escaneada para calcular o grau de conversão. Para sorção (&#x3BC;g/mm3) houve diferença estatisticamente significante para ambos os fatores (p<0.05) sem interação entre eles SB> SU> MP> SE. Para a solubilidade (&#x3BC;g/mm3), somente o fator adesivo foi significante (p<0.05): SB>SU>MP=SE. A irradiação do LASER antes da polimerização aumentou o grau de conversão dos sistemas adesivos SBL> MP-L> SE-L> MP> SB> SE> SU-L> SU. A irradiação aumentou a sorção, mas não afetou a solubilidade dos sistemas adesivos. Além disso, a irradiação com LASER de diodo melhorou o grau de conversão de três sistemas adesivos testados. / Laser irradiation has been used over the dentin bonding systems (DBS) prior to polymerization as a strategy to improve their properties. The aim of this study was to investigate the effect of diode laser on water sorption (WS), solubility (WSB) and conversion degree (DC) of main categories of DBS. Four bonding agents were tested: 3-step total-etch (Adper&#x2122; Scotchbond&#x2122; Multi-Purpose-MP), 2-step total-etch (Adper&#x2122; Single Bond 2-SB), 2-step self-etch Clearfil&#x2122; SE Bond-SE) and universal system (Adper&#x2122; Single Bond Universal-SU). The fluid DBSs were dispensed into Teflon molds (6.0 x 6.0 x 1mm), irradiated with a 970 nm diode laser and then polymerized with a LED curing unit. For WS/WSB tests, square-shaped DBS were prepared (n=10): MP, SB, SE and SU (control groups/ no laser irradiation) and MP-L, SB-L, SE-L and SU-L (laser irradiated groups). WS/WSB were measured by monitoring the mass changes after dehydration/water storage cycles. For DC tests, similar square-shaped specimens were prepared and assigned into eight similar groups (n=5), using Fourier transform infrared spectroscopy (FT-IR) with attenuated total reflectance (ATR). Each cured specimen was compressed against the ATR crystal (diamond/ZnSe) with a micrometric, low-pressure clamp. Uncured resin samples (&#x2248;3.0&#x3BC;L, n=5) of each adhesive were also scanned for DC calculation. For WS (&#x3BC;g/mm3), both factors were statistically significant (p<0.05), without interaction between them SB>SU>MP>SE. For WSB (&#x3BC;g/mm3), only DBS was a significant factor (p<0.05): SB>SU>MP=SE. Laser irradiation immediately before photopolymerization has increased the DC (%) of the tested adhesives: SB-L> MPL> SE-L> MP> SB> SE> SU-L> SU. Irradiation with diode laser improved the conversion degree of all tested dentin bonding systems. Furthermore the diode laser increased the sorption, but did not affect their water solubility.