Made available in DSpace on 2014-06-11T19:31:27Z (GMT). No. of bitstreams: 0 Previous issue date: 2002-10-08Bitstream added on 2014-06-13T19:01:43Z : No. of bitstreams: 1 susin_ah_dr_arafo.pdf: 3155550 bytes, checksum: 3c18f1511d8950d04d4fb3ead12080d0 (MD5) / O objetivo deste trabalho foi realizar, in vitro, avaliação da resistência de união à tração (RUT) e espessura de camada híbrida (ECH), em diferentes condições de substrato dentinário (úmido, S1; desidratado, S2 e reumedecido, S3), proporcionado pelos sistemas adesivos de 4ª geração, Scotchbond Multi Uso (SBMU) - 3M ESPE; Single Bond (SB) - 3M ESPE; Prime & Bond 2.1 (P&B2.1) - Dentsply e One Coat Bond (OCB) - Coltène-Whaledent, e os sistemas adesivos de 5ª geração (autocondicionantes), Clearfil SE Bond (CSEB) - Kuraray e One Up Bond F (OUBF) - Tokuyama. Foram utilizados 180 dentes seccionados na altura do 1/3 médio da coroa, originando duas partes cada um: remanescente dental (utilizado no teste de resistência de união à tração) e fragmento oclusal (utilizado na mensuração de camada híbrida). Para cada um dos 18 grupos foram realizadas 10 repetições em cada um dos dois testes, perfazendo um total de 360 amostras. O teste de RUT, foi realizado na Máquina de Ensaios Mecânicos MTS-810, em velocidade de 2 mm / min., e a ECH, foi mensurada à partir de fotografias obtidas em microscopia eletrônica de varredura (Microscópio Eletrônico JSM 330 A), com o software Image Tool 2.00. No teste de RUT, o desempenho dos sistemas adesivos foi melhor em S1 e, dentre eles, o CSEB foi o que apresentou a maior média, 23,01 MPa, enquanto que a menor, foi apresentada pelo OUBF, 15,69 MPa. Os sistemas adesivos de 4ª geração apresentaram médias intermediárias, às quais não foi possível encontrar diferenças estatisticamente significantes. (SBMU, 18,71 MPa; SB, 19,43 MPa; P&B2.1, 17,45 MPa e OCB, 19,92 MPa). As menores médias de RUT dos sistemas adesivos de 4ª geração, foram constatadas em S2, apresentando a menor média para o SB, 6,64 MPa, enquanto que os sistemas autocondicionantes, apresentaram menores variações de RUT entre os... . / The aim of this work was to perform the evaluation of the tensile bond strength (TBS) and the thickness of the hybrid layer (THL), in different conditions of dentinal substrate (moist, S1; dehydrated, S2 and remoistened, S3), provided by the fourth generation adhesive systems, Scotchbond Multi Uso (SBMU) - 3M ESPE; Single Bond (SB) - 3M ESPE; Prime & Bond 2.1 (P&B2.1) - Dentsply and One Coat Bond (OCB) - Coltène-Whaledent, and the fifth generation adhesive systems (self-etching), Clearfil SE Bond (CSEB) - Kuraray and One Up Bond F - Tokuyama. One hundred and eighty teeth bisected in the 1/3 crown mean level were used, originating two parts each: dental remnant (used in the tensile bond strength testing) and occlusal fragment (used in the hybrid layer measurement). For each of the 18 groups, 10 repetitions were performed for both tests, in a total of 360 samples. The TBS test was performed in a Mechanic Testing Machine MTS-810, in speed 2 mm/ min, and the THL was measured from photographs obtained in scanning electron microscopy (Electron Microscope JSM 330 A), using a software Image Tool 2.00. During the TBS test, the performance of the adhesive systems was better in S1 and, among themselves, CSEB presented the higher average, 23,01 MPa, while the lower average was presented by OUBF, 15,69 MPa. The fourth generation adhesive systems presented intermediate averages, those which did not revealed statistically significant differences. (SBMU, 18,71 MPa; SB, 19,43 MPa; P&B2,1, 17,45 MPa and OCB, 19,92 MPa). The lower averages of the fourth generation adhesive systems in TBS were verified in S2, presenting the lower average for SB, 6,64 MPa, while the self-etching systems presented lower TBS variations among the different substrates. In the THL results, lower variability was verified among the average results obtained, being the higher average presented by SBMU, 4,80 æm... (Complete abstract, click electronic address below).

Made available in DSpace on 2014-06-11T19:31:27Z (GMT). No. of bitstreams: 0 Previous issue date: 2006Bitstream added on 2014-06-13T20:22:10Z : No. of bitstreams: 1 magnani_c_dr_arafo.pdf: 594008 bytes, checksum: d8496d3440da8bb7f9fe9acf656211c7 (MD5) / O presente trabalho teve por objetivo avaliar, comparativamente, in vitro, a resistência de união ao cisalhamento de uma resina composta à dentina humana e à dentina bovina, submetidas ao tratamento com dois sistemas adesivos convencionais simplificados (Prime Bond NT®, Dentsply e Single Bond®/3M) e dois sistemas adesivos autocondicionantes (AdheSE®/Ivoclar-Vivadent e Adpper Prompt-L-Pop®/ 3M). Para a confecção dos corpos-de-prova, foram utilizadas as superfícies vestibulares de 40 dentes molares humanos e de 40 dentes incisivos bovinos, as quais foram divididas aleatoriamente em 8 grupos de 10 amostras cada, de acordo com o tipo de substrato e o sistema adesivo utilizado: Grupo 1 - dentina humana tratada com o sistema adesivo Single Bond; Grupo 2 - dentina humana tratada com o sistema adesivo Prime Bond NT; Grupo 3 - dentina humana tratada com o sistema adesivo AdheSE; Grupo 4 - dentina humana tratada com o sistema adesivo Adpper Prompt-L-Pop; Grupo 5 - dentina bovina tratada com o sistema adesivo Single Bond; Grupo 6 - dentina bovina tratada com o sistema adesivo Prime Bond NT; Grupo 7 - dentina bovina tratada com o sistema adesivo AdheSE; Grupo 8 - dentina bovina tratada com o sistema adesivo Adpper Prompt-L-Pop. Após o tratamento das superfícies, com o auxílio de uma matriz bipartida, foram confeccionados cilindros de resina composta Tetric Ceram apresentando 3mm de diâmetro e 4mm de altura. Os corpos-de-prova foram então armazenados em água destilada a 37ºC por 24 horas e submetidos a termociclagem (550 ciclos à temperatura de 10ºC e 55ºC). Após 48 horas de armazenamento em água destilada a 37ºC, foram levados a uma Máquina de Teste Universal para a realização do teste de cisalhamento utilizando-se uma ponta em forma de cinzel e velocidade do atuador de 0,5 mm/min. Os tipos de fratura foram analisados em lupa estereoscópica com 40X de aumento. / The purpose of this in vitro study was to evaluate, comparatively, the shear bond strength of a composite resin to human and bovine dentin treated with two conventional simplified adhesive systems (Prime Bond NT®/Dentsply and Single Bond®/3M) and two self-etching adhesive systems (AdheSE®/Ivoclar-Vivadent and Adpper Prompt-L-Pop®/3M). For preparation of specimens, the buccal surface of 40 human molars and 40 bovine incisors were obtained and randomly assigned to 8 groups (n=10), according to the type of substrate and adhesive system used. Group1 - human dentin treated with Single Bond; Group 2 - human dentin treated with Prime Bond NT; Group 3 - human dentin treated with AdheSE; Group 4 - human dentin treated with Adpper Prompt-L-Pop; Group 5 - bovine dentin treated with Single Bond; Group 6 - bovine dentin treated with Prime Bond NT; Group 7 - bovine dentin treated with AdheSE; Group 8 - bovine dentin treated with Adpper Prompt-L-Pop. After treatment with the adhesive systems, composite resin (Tetric Ceram) cylinders (3 mm in diameter and 4 mm high) were fabricated using a split matrix and were bonded to the dentin surfaces. The specimens were stored in distilled water at 37ºC for 24 hours and then submitted to a thermocycling regimen (550 cycles between 10ºC and 55ºC). After 48-hour storage in distilled water at 37ºC, the specimens were taken to a universal testing machine and loaded in shear strength until failure using knife-edge-shearing blade running at a crosshead speed of 0.5 mm/min. Failure mode was analyzed using a stereomicroscope at X40. Data were submitted to statistical analysis by analysis of variance at 5% significance level. The results showed that Single Bond and Prime Bond NT adhesive systems presented similar shear bond strength to each other (p>0.05) and significantly higher means than AdheSE and Adper Prompt-L-Pop (p<0.05), regardless of the type of substrate.

Made available in DSpace on 2014-06-11T19:35:03Z (GMT). No. of bitstreams: 0 Previous issue date: 2009-05-08Bitstream added on 2014-06-13T20:06:14Z : No. of bitstreams: 1 melo_rm_dr_sjc.pdf: 3484297 bytes, checksum: 204bf95c70038c23b08cc2d82b5974c4 (MD5) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / Esse estudo avaliou a performance de dois adesivos com condicionamento ácido prévio (All- Bond 2 e One-step Plus - Bisco) e dois sistemas adesivos autocondicionantes (Clearfil SE Bond- Kuraray e Xeno III- Dentsply) quanto à resistência de união à dentina coronária e do canal radicular, penetração do adesivo na dentina desmineralizada e influência sobre o grau de conversão do cimento resinoso. Também foi determinada, com mecânica da fratura, a tenacidade da interface pino/cimento/dentina formada com o adesivo All-Bond 2. O canal radicular de 80 dentes humanos anteriores superiores foi instrumentado e, em seguida, preparado com brocas do sistema de pinos FRC Postec (Ivoclar). A dentina foi tratada com um dos sistemas adesivos e o pino foi cimentado com cimento Duo-link (Bisco). Oito grupos foram formados de acordo com o sistema adesivo e o tempo de armazenagem em saliva artificial (7 d ou 4 m). Seis secções transversais (~1,0 mm) foram obtidas das regiões compreendidas entre 4 mm acima da JEC até 4mm do ápice radicular, isto é, dentina coronária e do canal radicular. Três destas seis secções foram submetidas ao teste de pushout em máquina de ensaio universal Instron (1 mm/min, 50 Kgf). Nas secções restantes foram avaliados o grau de conversão do cimento e a penetração do adesivo na dentina com μ-Espectroscopia Raman. As amostras de tenacidade consistiram de dois hemi-discos de resina reforçada por fibra (pino) cimentados a duas fatias de dentina da câmara pulpar, formando um sanduíche (espécime Brazil nut). Os resultados do teste Anova 3-fatores de medida repetida (p<0.05) indicam que, apenas, a “região” exerceu efeito significante sobre a resistência de união (MPa). Na porção coronária (4,20 MPa) a resistência foi maior que nas regiões média (3,45 MPa) e apical (3,26 MPa) (Tukey, 5%). A tenacidade de fratura da interface cimento-dentina foi maior... / This study evaluated the performance of two etch-and-rinse (All-Bond 2 andOne-step Plus- Bisco) and two self-etch adhesive systems (Clearfil SE Bond- Kuraray and XenoIII-Dentsply) concerning their bonding durability to coronal and root canal dentin, infiltration onto dentin and influence on the degree of cure of a dual-cure cement. It was also determined the interfacial fracture toughness of the post/cement/dentin interface forme with All-Bond 2. The root canals of 80 human incisors and canines were instrumented and prepared with burs (FRC Postec System, Ivoclar). Dentin was treated with one of the four adhesives and FRC Postec posts (Ivoclar) were cemented to the root canal with Duo-link dual-cure resin cement (Bisco). Eight groups were formed according to the adhesive system employed and the aging time in water (7 or 4 m). Six transverse sections (~1.0 mm) were cut from 4 mm above the CEJ up to 4 mm short of the root canal apex, comprising coronal and root canal dentin. Three out of the six sections were submitted to push-out testing in an Instron machine (1 mm/min, 50 Kgf). The degree of conversion of the cement and the infiltration of the adhesive were evaluated in the remaining sections through Raman μ-Spectroscopy. The fracture toughness specimens were made out of two half disks of fiber–reinforced composite (post) cemented to dentin pieces, forming the Brazil nut specimen. The analisys obtained with the 3-way Anova of repeated measures test (p<0.05) showed that only the “region” had statistically significant effects on the bond strengths (MPa). Comparison of the means achieved in each region (Tukey, p < 0.05) revealed that the coronal portion (4.20 MPa) was higher than the cervical (3.45 MPa) and middle portions (3.26 MPa) of the root, which were not statistically different. The interfacial fracture toughness was higher for the cement-dentin interface than... (Complete abstract click electronic access below)

Made available in DSpace on 2014-12-02T11:16:36Z (GMT). No. of bitstreams: 0 Previous issue date: 2013-03-26Bitstream added on 2014-12-02T11:21:11Z : No. of bitstreams: 1 000738257_20160326.pdf: 483238 bytes, checksum: 55b8baebdfcf5e968a88fb759b4e6be6 (MD5) Bitstreams deleted on 2016-03-28T13:37:45Z: 000738257_20160326.pdf,. Added 1 bitstream(s) on 2016-03-28T13:38:48Z : No. of bitstreams: 1 000738257.pdf: 2384428 bytes, checksum: 2f5315a3ccb28b42496282478231b8fd (MD5) / Este estudo tem como objetivo avaliar o efeito de laser de Er: YAG (L) e ponta diamantada (B) sobre a força de resistência ao microcisalhamento (MPa) e o efeito sobre a interface adesiva de adesivos condiciona e lava (CL) – Adper Scotchbond Multiuso e autocondicionante (CS) – Adper EasyOne, ambos da 3M ESPE. Foram constituídos 4 grupos segundo instrumentos e adesivos: B_CL (controle); B_CS; L_CL e L_CS. 60 incisivos bovinos foram randomicamente divididos nos experimentos e grupos: 40 para força de resistência ao microcisalhamento (n=10) e 20 para morfologia da interface adesiva (6 para mensuração da espessura da camada hibrida (CH) e comprimento de tags (t) por MLCF (n=3); 12 para morfologia da interface adesiva por MEV (n=3) e 2 para ilustração o efeito dos instrumentos sobre dentina por MEV (n=1). Para o ensaio de microcisalhamento foram confeccionados 4 cilindros de resina composta Filtek Z350 XT – 3M ESPE (0,7 mm de diâmetro por 1 mm de altura e área de adesão de 0,38 mm2) sobre cada superfície de dentina tratada pelos instrumentos e adesivos. O ensaio de resistência de união ao microcisalhamento foi realizado em máquina de ensaio universal EMIC 2000, com célula de carga de 500 Kgf e velocidade de 0,5 mm/min. A interface adesiva foi caracterizada pela espessura da camada hibrida (CH) e comprimento de tags (t) em μm, com o software UTHSCSA Imagetool. Os valores de resistência adesiva ao microcisalhamento foram L_CL 34,10 ± 19,07 MPa, B_CL 24,26 ± 9,35 MPa, L_CN 33,18 ± 12,46 MPa, B_CN 21,24 ± 13,96 MPa. Anova two-way resultou em diferença estatisticamente significativa somente para instrumentos (p=0,047). Teste de Mann-Whitney identificou os instrumentos determinam diferenças significativas para de espessura de CH e comprimento de (t). Para adesivos estas diferenças só foram observadas para (t). Pode-se concluir que 1) Laser de Er:YAG resulta em maiores valores de... / This study aims to evaluate the effect of Er: YAG (L) and bur (B) on the strength of resistance microshear (MPa) and the effect on the interface adhesive stickers and wash conditions (CL) - Adper Scotchbond Multipurpose and self (CS) - Adper EasyOne, both from 3M ESPE. Were formed 4 groups according tools and adhesives: B_CL (control); B_CS; L_CL and L_CS. 60 bovine incisors were randomly divided into experimental and groups: 40 to force microshear resistance (n = 10) and 20 for the adhesive interface morphology (6 to measure the thickness of the hybrid layer (CH) and length of tags (t) by MLCF (n = 3); 12 to the adhesive interface morphology by SEM (n = 3) and 2 to illustrate the effect of the instruments on dentine by SEM (n = 1). Microshear For testing four cylinders were fabricated composite Filtek Z350 XT - 3M ESPE (0.7 mm in diameter and 1 mm in height and area of adhesion of 0.38 mm) on each dentin surface treated by tools and adhesives. Testing of bond strength was performed in microshear FDMS universal testing machine 2000 with a load cell of 500 kgf and a speed of 0.5 mm / min. Adhesive interface was characterized by layer thickness hybrid (HC) and length of tags (t) in nm, with software UTHSCSA ImageTool. Values of bond strength to microshear L_CL were 34.10 ± 19.07, 24.26 ± 9.35 B_CL, L_CN 33.18 ± 12.46, 21.24 ± 13.96 B_CN. Anova two- way resulted in statistically significant only for instruments (p = 0.047). Mann-Whitney identified instruments to determine significant differences CH thickness and length (t). adhesives for these differences were only observed for (t). It can be concluded that 1) Laser Er: YAG results in higher bond strength to the microshear, regardless of the adhesive system (CL and CS). 2) The tags have no significant effect on bond strength to microshear. 3) The adhesive interface is affected by both instruments for cavity preparation and the type of adhesive system...

O objetivo do presente estudo foi avaliar a remoção da smear layer e a penetração intratubular do cimento obturador AH Plus utilizando diferentes protocolos de irrigação. Após aprovação do Comitê de Ética em Pesquisa da Faculdade de Odontologia de Ribeirão Preto - FORP/USP, noventa incisivos centrais superiores foram selecionados e fornecidos pelo banco de dentes da mesma instituição. Estes foram radiografados no sentido mésio - distal e vestíbulo - lingual para comprovar a presença de canais únicos, sem curvaturas abruptas, reabsorções ou tratamentos endodônticos prévios. Após a remoção da porção coronal para a obtenção de raízes com comprimentos padronizados de 15 milímetros, os diâmetros anatômicos foram determinados e as instrumentações realizadas por meio da técnica coroa ápice estabelecendo os diâmetros cirúrgicos utilizando 3 instrumentos acima dos anatômicos. Durante este processo, os espécimes foram divididos em seis grupos de acordo com os protocolos de irrigação: Grupo 1 (controle - n. 15) - 2,5ml de água destilada a cada troca de instrumentos e 2,5ml de água destilada por 3 minutos ao final da instrumentação; Grupo 2 (n. 15) - 2,5ml de hipoclorito de sódio a 2,5% a cada troca de instrumentos e 2,5ml de hipoclorito de sódio a 2,5% por 3 minutos ao final da instrumentação; Grupo 3 (n. 15) - 2,5ml de hipoclorito de sódio a 2,5% a cada troca de instrumentos e 2,5ml de EDTA a 17% por 3 minutos ao final da instrumentação; Grupo 4 (n. 15) - 2,5ml de hipoclorito de sódio a 2,5% e 2,5ml de EDTA a 17% a cada troca de instrumentos + 2,5ml de EDTA a 17% por 3 minutos ao final da instrumentação; Grupo 5 (n. 15) - 2,5ml de hipoclorito de sódio a 2,5% a cada troca de instrumentos e 2,5ml de ácido cítrico a 10% por 3 minutos ao final da instrumentação; Grupo 6 (n. 15) - 2,5ml de hipoclorito de sódio a 2,5% e 2,5ml de ácido cítrico a 10% a cada troca de instrumentos + 2,5ml de ácido cítrico a 10% por 3 minutos ao final da instrumentação. Após esta fase, cinco espécimes de cada grupo foram clivados no sentido mésio - distal para avaliação da remoção da smear layer em microscopia eletrônica de varredura por meio da análise de 3 imagens de cada terço em aumentos de 300, 1000 e 2000 vezes. Esta variável foi determinada por um score qualitativo estabelecido pelo consenso de 3 avaliadores calibrados. Os demais espécimes foram obturados pela técnica de condensação lateral com cones principais correspondentes ao último instrumento associados ao cimento AH Plus corado com Rodamina B, cones acessórios B8 e mantidos em ambiente com 100% de umidade por 7 dias. Em seguida, os espécimes foram seccionados transversalmente para obtenção de slices de aproximadamente 2mm de espessura em cada terço (cervical, médio e apical) e as faces cervicais submetidas a um tratamento metalográfico para análise da penetração intratubular do cimento obturador em microscopia confocal a laser. Os melhores índices de remoção de smear layer e as maiores porcentagens de penetração intratubular do cimento foram obtidos pelos grupos onde as soluções quelantes foram utilizadas (G3, G4, G5 e G6) com diferenças estatisticamente significantes (p<0,05) em relação aos grupos onde utilizou - se somente a água destilada (G1) e o hipoclorito de sódio a 2,5% (G2) durante o processo de instrumentação. Não foram observadas vantagens em relação ao uso associado do EDTA a 17% e do ácido cítrico a 10% ao hipoclorito de sódio pela ausência de diferenças estatísticas significantes entre os grupos 3 e 4 e 5 e 6, respectivamente. / The aim of this study was to evaluate the smear layer removal and tubular dentine sealer penetration of AH Plus after different irrigation protocols. After approval of the study by the Ethics Committee of the Ribeirão Preto Dental School - FORP/USP, ninety maxillary central incisors were selected and supplied by the tooth bank of the same institution. The teeth were radiographed in the mesiodistal and buccolingual directions to verify the presence of single canals, without abrupt curvatures, resorption or previous endodontic treatment. The coronal portion was removed and roots lengths were standardized at 15 mm. The anatomic diameters were then determined and instrumentations were carried out by the crown-down technique, using 3 higher-diameter instruments to establish the surgical diameters. During this process, the specimens were divided into six groups, according to the following irrigation protocols: Group 1 (control - n. 15) - 2.5ml of distilled water at each change of instruments + 2.5ml of distilled water for 3 minutes at the end of the instrumentation; Group 2 (n. 15) - 2.5ml of 2.5% sodium hypochlorite at each change of instruments + 2.5 ml of 2.5% sodium hypochlorite for 3 minutes at the end of the instrumentation; Group 3 (n. 15) - 2.5ml of 2.5% sodium hypochlorite at each change of instruments + 2.5ml of 17% EDTA for 3 minutes at the end of the instrumentation; Group 4 (n. 15) - 2.5ml of 2.5% sodium hypochlorite and 2.5ml of 17% EDTA at each change of instruments + 2.5ml of 17% EDTA for 3 minutes at the end of the instrumentation; Group 5 (n. 15) - 2.5ml of 2.5% sodium hypochlorite at each change of instruments + 2.5ml of 10% citric acid for 3 minutes at the end of the instrumentation; Group 6 (n. 15) - 2.5ml of 2.5% sodium hypochlorite and 2.5 ml of 10% citric acid at each change of instruments + 2.5 ml of 10% citric acid for 3 minutes at the end of the instrumentation. Following this phase, five specimens from each group were cleaved in the mesiodistal direction to evaluate the smear layer removal by scanning electron microscopy. Evaluation was performed by analyzing 3 images of each third at 300, 1000 and 2000X. This variable was determined by a qualitative score established by the consensus of 3 calibrated examiners. The remaining specimens were filled using lateral condensation with AH Plus sealer labeled with Rhodamine B and kept in an environment with 100% humidity for 7 days. Then, the specimens were sectioned to obtain approximately 2 mm thick slices of each third (cervical, middle and apical). The cervical surfaces were subjected to metallographic treatment for analysis of the tubular dentine sealer penetration by confocal laser microscopy. The highest smear layer removal rates and tubular dentine sealer penetration percentages were obtained by the groups that used chelating solutions (G3, G4, G5 and G6). These showed statistically significant differences (p<0.05) compared with the groups that used just distilled water (G1) and 2.5% sodium hypochlorite (G2) during instrumentation. No benefits were observed for the combined use of 17% EDTA or 10% citric acid with 2.5% sodium hypochlorite, considering that there were no statistically significant differences between groups 3 and 4, and between 5 and 6, respectively.

Orientador: Josimeri Hebling / Banca: Ana Flávia Sanches Borges / Banca: André Figueiredo Reis / Banca: Luis Geraldo Vaz / Banca: Ângela Cristina Cilense Zuanon / Resumo: Objetivo: O objetivo geral deste trabalho, dividido em três estudos, foi avaliar in vitro o efeito da aplicação da clorexidina na morfologia, resistência de união imediata e em longo prazo da união resina-dentina hígida e dentina afetada por cárie produzida por sistemas adesivos convencionais e autocondicionantes. Materiais e Métodos: No estudo 1, espécimes obtidos de interfaces produzidas pelo sistema adesivo Adper Single Bond 2 com a dentina hígida e a dentina afetada por cárie foram armazenados por 24 horas em água, 6 meses em água, clorexidina a 0,12% ou óleo mineral e subseqüentemente preparados para a avaliação do colágeno exposto na interface (coloração de Tricrômico de Goldner). Aos dados foram aplicados os testes de ANOVA e Tukey. No estudo 2, sobre a dentina hígida (n=24) ou artificialmente afetada por cárie (n=24), foram aplicados os sistemas adesivos Adper Scotchbond MP, Adper Single Bond 2, Clearfil SE Bond ou Adper Prompt L-Pop, na presença ou ausência de clorexidina. Espécimes para o ensaio mecânico de microtração foram produzidos (0,81 mm2) e os valores de resistência de união foram confrontados pelos testes de ANOVA e Tukey, para cada sistema adesivo. No estudo 3, 48 dentes foram artificialmente cariados e divididos segundo os mesmos sistemas adesivos utilizados no estudo 2 e aplicação ou não da clorexidina. Os espécimes produzidos (0,81 mm2) foram armazenados em água por 24 horas ou 6 meses sendo em seguida submetidos ao ensaio mecânico de microtração. Os dados obtidos foram analisados pelos testes de ANOVA e Tukey. Para todos os estudos, os testes estatísticos foram considerados ao nível pré-estabelecido de significância de 5%. Resultados: Não houve diferença estatística para as medidas de colágeno exposto dos grupos hígidos e cariados; entretanto foi detectada maior exposição do colágeno no grupo armazenado em água... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Objective: The overall purpose of this work, divided into three studies, was to evaluate the in vitro effect of chlorhexidine application on the morphology, immediate and longterm bond strength of resin-noncarious dentin and resin-caries affected dentin bonds produced by etch-and-rinse and self-etching adhesive systems. Materials and Methods: In the first study, specimens obtained from bonds produced by Single Bond 2 applied on noncarious and caries-affected dentin were stored for 24 h in water, 6 m in water, in 0.12 chlorexidine or mineral oil. Subsequently, they were prepared for collagen identification within the bonds (Goldner's Trichrome stain). Data were submitted to ANOVA and Tukey tests. In the second study, Scotchbond MP, Single Bond 2, Clearfil SE Bond and Prompt were applied on noncarious (n=24) or cariesaffected dentin (n=24) with or without chlorhexidine. Specimens were produced (0.81 mm2) and microtensile tested. The data for each adhesive system were submitted to ANOVA e Tukey tests. For the third study, 48 artificially decayed teeth were divided according to the same adhesive system used in study 2 and the use or not of chlorhexidine. The produced specimens (0.81 mm2) were stored in water for 24 h or 6 m before being stressed to failure. Data were analyzed by ANOVA and Tukey tests. For all the studies, the statistical tests were considered at the preset level of significance of 5%. Results: No statistical significant difference was seen between the width of the exposed collagen zone in bonds produced on noncarious and carious dentin. However, thicker zones were observed after 6 m of water storage for both substrates. Specimens stored in 0.12 chlorhexidine and mineral oil did not differ from those stored in water for 24 h (control). Bond strengths produced on caries-affected dentin were significantly lower than those produced on noncarious dentin when chloherxidine was... (Complete abstract click electronic access below) / Doutor

Orientador: José Roberto Rodrigues / Banca: Eduardo Shigueyuki Uemura / Banca: Carlos Henrique Ribeiro Camargo / Banca: George Miguel Spyrides / Banca: Gorgulho Zanet / Resumo: O objetivo do estudo foi avaliar quatro diferentes sistemas adesivos (Multi- Purpose, Single Bond, SE Plus e Easy Bond - 3M ESPE) no que se refere à resistência adesiva ao microcisalhamento na dentina bovina. Além de avaliar a citotoxicidade desses novos sistemas adesivos por meio do teste de barrerira dentinária e ensaio de MTT em fibroblastos pulpares bovinos. Para o teste de microcisalhamento 80 dentes bovinos tiveram suas raízes seccionadas, foram embutidos em resina acrílica e tiveram a superfície vestibular desgastada expondo-se a dentina, sendo que em 40 dentes a espessura de dentina remanescente foi de 500μm e nos outros 40 de 200μm. Os cdp receberam então o procedimento adesivo de acordo com as instruções do fabricante e com auxílio de uma matriz metálica, cilindros de resina (Z 250 - 3M ESPE) de 0,8 mm de diâmetro e 1mm de altura foram construídos. Após 24h os cdp foram então submetidos ao ensaio de microcisalhamento. Para avaliar a citotoxicidade foi usado o teste de barreira dentinária. Células pulpares bovinas transformadas foram cultivadas em redes de nylon por 2 semanas, obtendo-se uma cultura de 3 dimensões. Essas culturas celulares foram separadas dos materiais testados por fatias de dentina de 500 e 200μm em um dispositivo de perfusão celular. Os materiais foram aplicados na porção cavitária do dispositivo de acordo com as instruções do fabricante, e um material de moldagem a base de silicona (President, Coltene) foi usado como controle negativo (100% de viabilidade celular). Após 24 h de periodo de exposição, a viabilidade celular foi mensurada fotometricamente (teste MTT). Por meio de estatística descritiva verificou-se que a melhor eficiência adesiva foi apresentada pelo adesivo auto-condicionante de um passo só, Easy Bond (21,06 MPa - 200μm; 27,01 MPa- 500μm) seguido pelo Single Bond (15,64 MPa - 200μm; 23,45 MPa- 500μm), SE Plus... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The aim of this study was to evaluate four different adhesive systems (Multi- Purpose, Single Bond, SE Bond Plus and Easy - 3M ESPE) with regard to microshear bond strength to bovine dentin. In addition evaluate the cytotoxicity of these new adhesive systems by means of a dentin barrier test. To test microshear 80 bovine teeth had their roots sectioned and were embedded in acrylic resin. The buccal surface had been worn to expose the dentin, in 40 teeth the remaining dentin thickness was 500μm and 200μm in the other 40. The specimes received the adhesive procedure according to the manufacturer's instructions and with the aid of a metal matrix, cylinders of resin (Z 250 - 3M ESPE) from 0.8 mm in diameter and 1mm in height were built. After 24h the specimes were then subjected to the microshear testing To evaluate the cytotoxicity, a dentin barrier test was used. SV3NeoB transfected bovine pulp derived cells were grown on nylon meshes for 2 weeks achieving a 3-dimensional cell culture as described. These cell cultures were separated from the test materials by dentin slices of 200 or 500μm thickness in a cell cultures perfusion chamber. The materials were applied into the cavity part of the device according to manufacturer's instruction, and a silicon impression material (President, Coltene) served as a negative control material (100% cell viability). After a 24h exposure period, cell viability was measured photometrically (MTT test). Median values (plus 25% and 75% percentiles) of cell viability measurements (n=10) were statistically analyzed (Mann-Whitney test, = 0.05). Descriptive statistics found that the best bonding performance was presented by the single step adhesive Easy Bond (21.06 - 200μm, 27.01 - 500μm) followed by Single Bond (15.64 - 200μm; 23.45 - 500μm), SE Plus (18.23 - 200μm; 20.07 - 500μm) and Multi Purpose (15.24 - 200μm; 17.99 - 500μm). Moreover, it was... (Complete abstract click electronic access below) / Doutor

Orientador: Paulo Henrique dos Santos / Banca: André Luiz Fraga Briso / Banca: Renato Herman Sundfeld / Banca: Cláudia Batitucci dos Santos Daroz / Banca: Anderson Catelan / Resumo: O objetivo deste estudo in vitro foi avaliar o efeito da ciclagem de pH erosiva com soluções que simulam a erosão dental, provenientes de fatores extrínsecos ou intrínsecos, na dureza e módulo de elasticidade da dentina restaurada com materiais restauradores contendo fluoretos. Quarenta e cinco blocos de dentina medindo 6 x 6 mm foram restaurados com cinco materiais restauradores: sistema adesivo de condicionamento total Adper Single Bond 2 + resina composta Filtek Z250; sistema adesivo autocondicionante One Up Bond F + resina composta Filtek Z250; sistema adesivo autocondicionante Clearfil SE Protect + resina composta Filtek Z250; cimento de ionômero de vidro convencional Riva Self Cure; cimento de ionômero de vidro resinoso Riva Light Cure. Mensurações da dureza Martens e módulo de elasticidade da dentina subjacente à interface de união (10μm, 30μm, 50μm e 70μm) foram realizadas em ultramicrodurômetro digital antes e após a imersão em soluções de água deionizada, ácido cítrico ou ácido clorídrico. Após a ciclagem, os valores de dureza da dentina diminuíram para todos os materiais. Para a dentina restaurada com Adper Single Bond 2, os menores valores foram encontrados próximo a camada híbrida (10 μm) enquanto que para a dentina restaurada com os sistemas adesivos autocondicionantes (Clearfil SE Protect e One Up Bond F), esses valores foram mantidos em todas as distâncias avaliadas. Para os materiais Riva Self Cure e Riva Light Cure somente nas leituras iniciais a distância foi determinante na dureza, uma vez que quanto maior a distância da interface de união, maiores eram os valores encontrados. Com relação ao módulo de elasticidade, para a dentina restaurada com Adper Single Bond 2, não houve diferença significante em todas as distâncias avaliadas. Já na dentina restaurada com os sistemas adesivos autocondicionantes ... / Abstract: The aim of this study was to evaluate the effect of erosive pH cycling with solutions that simulate dental erosion in the hardness and elastic modulus of dentin restored with fluoride-releasing restorative materials. Forty five bovine dentine slabs (6,0 mm x 6,0 mm) were restored with 5 restorative materials: Adper Single Bond 2 total-etch adhesive system + Filtek Z250 composite resin; One Up Bond F self-etching adhesive system + Filtek Z250 composite resin; Clearfil SE Protect self-etching adhesive system + Filtek Z250 composite resin; Riva Self Cure conventional glass ionomer cement and Riva Light Cure light curing glass ionomer cement. The values of hardness and elastic modulus of dentin (10μm, 30μm, 50μm e 70μm) were evaluated in digital ultramicrohardner tester before and after immersion in solutions of deionized water, citric acid and hydrochloric acid. After cycling, the hardness of dentin decreased for all materials. For dentin restored with Adper Single Bond 2, the lowest values were found close to hybrid layer (10 μm), while for the dentin restored with One Up Bond F and Clearfil SE Protect, the values remained unaltered in all the evaluated distances. For dentin restored with Riva Self Cure and Riva Light Cure only in the initial measurements, the distance had a significant effect in the hardness values, since the greater the distance to the bonding interface, higher values of hardness were found. For the elastic modulus analysis, dentin restored with Adper Single Bond 2 showed no significant difference when distances from bonding interface were compared. Dentin restored with self-etching adhesive system (One Up Bond F and Clearfil SE Protect) and glass ionomer cements (Riva Self Cure and Riva Light Cure) showed a reduction in the elastic modulus values from the bonding interface, but after 30 μm the difference was not significant. / Doutor

Orientador: Mirela Sanae Shinohara / Coorientadora: Ticiane Cestari Fagundes / Banca: Alberto Carlos Botazzo Delbem / Banca: Eduardo Passos Rocha / Banca: Mario Fernando de Goes / Banca: Rodolfo Bruniera Anchieta / Resumo: O objetivo deste estudo clínico controlado, prospectivo, randomizado e com avaliadores cegos foi avaliar o desempenho clínico de restaurações cervicais não cariosas frente às diferentes estratégias de adesão ao substrato dental. Métodos: foram utilizados um sistema restaurador adesivo (Single Bond Universal/Z350XT) com e sem condicionamento seletivo do esmalte e um cimento de ionômero de vidro modificado por resina (Vitremer) com e sem tratamento prévio com EDTA, seguindo as instruções do CONSORT. Um total de 200 restaurações foram realizadas por dois operadores em 50 pacientes voluntários. Previamente à execução das restaurações e em cada tempo de avaliação foram avaliados os índices de sangramento gengival, placa visível e CPOD. Todas as restaurações foram avaliadas por meio do sistema de avaliação do USPHS modificado. Dois examinadores calibrados, cegos e diferentes dos operadores realizaram as avaliações nos seguintes intervalos de tempo: inicial imediato (baseline), 6, 12 e 24 meses. Ao final de 24 meses os dados foram analisados pelos testes estatísticos de Friedman, Qui-quadrado, Kappa, Cochran, Wilcoxon e análise de regressão logística múltipla, adotando-se nível de significância a 5%. Resultados: a amostra foi composta de 34 homens e 16 mulheres com idade média de 61,8 anos. Em relação ao CPOD, houve um aumento gradativo e significante ao longo do tempo, havendo diferença entre os quatro tempos de avaliação (p≤0,001). Não teve diferença entre os tempos pa... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Introduction: the aim of this study, prospective, randomized controlled clinical trial and with blind evaluators was to evaluate the clinical performance of non - carious cervical restorations to different strategies of adhesion for the dental substrate. Met hods: we used a restorative adhesive system (Universal/Z350XT Single Bond) with and without selective etching of enamel and a modified glass ionomer luting cement for resin (Vitremer) with and without previous treatment with EDTA, following the instruction s of the CONSORT. 200 in total restorations were performed by two operators in 50 patients. Prior to the execution of the restorations and each time, we evaluated the evaluation indexes of gum bleeding, visibly Board and CPOD. All restorations were evaluat ed using the evaluation system USPHS modified. Two calibrated examiners, blind and different operators, performed the evaluations in the following time intervals: immediate initial (baseline), 6, 12 e 24 months. At the end of 24 months data were analyzed b y statistical tests Friedman, Qui - quadrado, Kappa, Cochran, Wilcoxon and multiple logistic regression analysis, adopting the significance level 5%. Results: the sample was composed of 34 men and 16 women with an average age of 61.8 years. Concerning the CP OD, there was a gradual and significant increase over time, difference between the four evaluation times (p≤0,001). There was no difference between the time the visible card index (p=0,28). However, there was a significant reduction of gingival bleeding in dex between the baseline and other times (p≤0,001). There was no statistically significant difference among the 4 groups in each time any of the assessment criteria evaluated (p>0,05), just as happened with the 4 times of evaluation for all groups (p>0,05) . With regards to the logistic regression, although it has not (Complete abstract click electronic access below) / Doutor

Orientador: Osmir Batista de Oliveira Junior / Banca: Mirian Lacalle Turbino / Banca: Edson Alves de Campos / Resumo: Este estudo tem como objetivo avaliar o efeito de laser de Er: YAG (L) e ponta diamantada (B) sobre a força de resistência ao microcisalhamento (MPa) e o efeito sobre a interface adesiva de adesivos condiciona e lava (CL) - Adper Scotchbond Multiuso e autocondicionante (CS) - Adper EasyOne, ambos da 3M ESPE. Foram constituídos 4 grupos segundo instrumentos e adesivos: B_CL (controle); B_CS; L_CL e L_CS. 60 incisivos bovinos foram randomicamente divididos nos experimentos e grupos: 40 para força de resistência ao microcisalhamento (n=10) e 20 para morfologia da interface adesiva (6 para mensuração da espessura da camada hibrida (CH) e comprimento de tags (t) por MLCF (n=3); 12 para morfologia da interface adesiva por MEV (n=3) e 2 para ilustração o efeito dos instrumentos sobre dentina por MEV (n=1). Para o ensaio de microcisalhamento foram confeccionados 4 cilindros de resina composta Filtek Z350 XT - 3M ESPE (0,7 mm de diâmetro por 1 mm de altura e área de adesão de 0,38 mm2) sobre cada superfície de dentina tratada pelos instrumentos e adesivos. O ensaio de resistência de união ao microcisalhamento foi realizado em máquina de ensaio universal EMIC 2000, com célula de carga de 500 Kgf e velocidade de 0,5 mm/min. A interface adesiva foi caracterizada pela espessura da camada hibrida (CH) e comprimento de tags (t) em μm, com o software UTHSCSA Imagetool. Os valores de resistência adesiva ao microcisalhamento foram L_CL 34,10 ± 19,07 MPa, B_CL 24,26 ± 9,35 MPa, L_CN 33,18 ± 12,46 MPa, B_CN 21,24 ± 13,96 MPa. Anova two-way resultou em diferença estatisticamente significativa somente para instrumentos (p=0,047). Teste de Mann-Whitney identificou os instrumentos determinam diferenças significativas para de espessura de CH e comprimento de (t). Para adesivos estas diferenças só foram observadas para (t). Pode-se concluir que 1) Laser de Er:YAG resulta em maiores valores de... / Abstract: This study aims to evaluate the effect of Er: YAG (L) and bur (B) on the strength of resistance microshear (MPa) and the effect on the interface adhesive stickers and wash conditions (CL) - Adper Scotchbond Multipurpose and self (CS) - Adper EasyOne, both from 3M ESPE. Were formed 4 groups according tools and adhesives: B_CL (control); B_CS; L_CL and L_CS. 60 bovine incisors were randomly divided into experimental and groups: 40 to force microshear resistance (n = 10) and 20 for the adhesive interface morphology (6 to measure the thickness of the hybrid layer (CH) and length of tags (t) by MLCF (n = 3); 12 to the adhesive interface morphology by SEM (n = 3) and 2 to illustrate the effect of the instruments on dentine by SEM (n = 1). Microshear For testing four cylinders were fabricated composite Filtek Z350 XT - 3M ESPE (0.7 mm in diameter and 1 mm in height and area of adhesion of 0.38 mm) on each dentin surface treated by tools and adhesives. Testing of bond strength was performed in microshear FDMS universal testing machine 2000 with a load cell of 500 kgf and a speed of 0.5 mm / min. Adhesive interface was characterized by layer thickness hybrid (HC) and length of tags (t) in nm, with software UTHSCSA ImageTool. Values of bond strength to microshear L_CL were 34.10 ± 19.07, 24.26 ± 9.35 B_CL, L_CN 33.18 ± 12.46, 21.24 ± 13.96 B_CN. Anova two- way resulted in statistically significant only for instruments (p = 0.047). Mann-Whitney identified instruments to determine significant differences CH thickness and length (t). adhesives for these differences were only observed for (t). It can be concluded that 1) Laser Er: YAG results in higher bond strength to the microshear, regardless of the adhesive system (CL and CS). 2) The tags have no significant effect on bond strength to microshear. 3) The adhesive interface is affected by both instruments for cavity preparation and the type of adhesive system... / Mestre