Made available in DSpace on 2016-06-02T20:34:09Z (GMT). No. of bitstreams: 1 2107.pdf: 1909260 bytes, checksum: da4d8a10b11de732e1a636989588feb6 (MD5) Previous issue date: 2007-03-08 / Financiadora de Estudos e Projetos / Some properties of the materials, such as ferroelectric and optic, are dependents to structural organization of the material. Thus, to know the order disorder degree at short, intermediate and long range is important to elucidate or predict properties in materials. The PL emission at room temperature will be used to study the structural order disorder at short, intermediate and long range in the CaTiO3:Sm, in function of annealed temperature. Using studies of the structural order disorder in the CaTiO3:Sm system will propose a model that appoint to favorable conditions, in disordered material, to show PL emission at room temperature. / Algumas propriedades em materiais, tais como ferroeletricidade e óptica, estão ligadas à forma como o material encontra se organizado estruturalmente. Sendo assim, conhecer os graus de organização estrutural á curta, média e longa distância em um material são de suma importância para explicar ou prever determinadas propriedades de alguns materiais. Nesse trabalho, a emissão fotoluminescência à temperatura ambiente foi utilizada para estudar a ordem desordem estrutural a curta, a média e a longa distância no material CaTiO3:Sm, em função do tratamento térmico. Foram utilizados estudos experimentais (espectroscopia Raman, difração de raios X, espectroscopia na região do ultravioleta-visível, ressonância paramagnética eletrônica) e cálculos mecânicos-quânticos para estudar a ordem-desordem estrutural do sistema. Através dos resultados de fotoluminescência foi possível evidenciar a desordem estrutural a média distância, apesar de já estabelecida a ordem estrutural a curta e a longa distância. Através do estudo da ordem desordem estrutural no sistema CaTiO3:Sm foi proposto um modelo teórico-experimental, Modelo de Banda Larga, que apontou as condições favoráveis para que os materiais desordenados estruturalmente apresentem emissão FL à temperatura ambiente.

Made available in DSpace on 2016-06-02T20:34:19Z (GMT). No. of bitstreams: 1 2957.pdf: 7430528 bytes, checksum: 359a49ef8e0e1e14ac5d1b86665d9132 (MD5) Previous issue date: 2010-02-26 / Universidade Federal de Sao Carlos / The microwave-assisted hydrothermal method was implemented in the synthesis of alkaline earth titanates under ABO3 stoichiometric known as perovskites, being efficient and innovative. For that, OH- groups played an important role since the coprecipitation of hydroxides to the dehydration of oxides for the formation of barium, calcium and strontium titanate at temperatures of 140 ° C with times from 10 to 160 min under 2.5 bar self-generated. During the dehydration / crystallization process of the hydrogen atoms may remain bound to oxygen causing a redistribution of local charges in the crystal lattice in order to stabilize it like a whole. This effect leads to the network polarizations, generated by small atomic displacements as microstructural distortions and casual vacancies of cations observed for BTO and STO, besides changes in dihedral angles for CTO. These polarizations will be able to cause the appearance or extinction of Raman vibrational modes without a drastic change on the phase symmetry of the materials. In the case of STO, fist order vibrational modes were detected in its cubic structure, for the BTO all observed vibrations correspond to the tetragonal phase and the CTO has an orthorhombic-orthorhombic transition related to the displacements of their vibrational modes. These changes of polarization for systems under study were also obtained from the simulation of Raman spectra, confirming and supporting the experimental results for each system. Thus the trapping of the hydrogen element is linked to local distortions through the formation of complexes clusters, mainly related to the atom network forming in its octahedral site. The formation of these clusters leads to the redistribution of the electronic states as a whole near the valence band and conduction band states by the hybridization of oxygen 2p and titanium 3d respectively. 13 This effect can be detected by absorption spectra of X-rays on the edge of the element titanium, and confirmed by "ab initio" simulations. Soon, new states near the bands may arise or be moved into the gap. In this case, such electronic states act as charge trapping centers, resulting after a specific excitation in the electron-hole pairs within the unstable band gap. Therefore, the different excitations employed in 350 and 415 nm allow us to produce different luminescent emission of individual system when the radioactive decay of these pairs. Thus, there was an intensification and / or disappearance of bands as a function of excitation applied. The CTO compound is the more efficient light emitting tooth the three materials. Thus the perovskites have become attractive materials with hybrid properties which make them even more attractive compounds for scientific research. / O método hidrotérmico assistido por microondas foi implementado na síntese de compostos tipo ABO3 de titanatos de alcalinos terrosos conhecidos como perovskitas, mostrando-se eficaz e inovador. Para tanto, grupos OH- desempenharam papel importante desde a co-precipitação dos hidróxidos até a deshidratação dos óxidos para a formação dos titanatos de bário, cálcio e estrôncio em temperaturas de 140°C com tempos de 10 a 160 min sob preções de 2,5 bar auto-geradas. Durante o processo de deshidratação/cristalização parte dos átomos hidrogênios pode permanecer ligado a oxigênios provocando uma redistribuição local de cargas na rede cristalina a fim de estabilizá-la como um todo. Este efeito leva ao surgimento de polarizações na rede geradas por pequenas distorções microestruturais como deslocamentos atômicos e vacâncias de cátions fortuitas observados para o BTO e STO e mudanças de ângulos diedrais no caso do CTO. Estas polarizações serão capazes de provocar o surgimento ou extinção de modos vibracionais Raman sem que ocorra uma mudança de simetria sobre a fase dos materiais. No caso do STO foram detectados modos vibracionais em sua estrutura cúbica, para o BTO todas as vibrações observadas correspondem a fase tetragonal e o CTO possui um transição ortorrômbica-ortorrômbica relacionadas aos deslocamentos de alguns do modos vibracionais. Tais mudanças de polarização para os sistemas em estudo também foram obtidas a partir da simulação dos espectros Raman, corroborando e suportando os resultados experimentais obtidos para cada sistema. Assim o aprisionamento do elemento hidrogênio está ligado às distorções locais através da formação de clusters complexos , principalmente relacionados ao átomo formador 11 da rede em seu sito octahedral, neste caso o titânio. A formação destes clusters leva a redistribuição dos estados eletrônicos como um todo próximo à banda de valência e a banda de condução pela hibridização dos estados 2p do oxigênio e 3d do titânio respectivamente. Este efeito pode ser detectado pelos espectros de absorção de raios X sobre a borda do elemento titânio e confirmado por simulações ab initio . Logo novos estados próximos às bandas podem surgir ou ser deslocados em direção ao gap . Neste caso, tais estados eletrônicos agem como centros aprisionadores de carga, originando após uma excitação específica pares elétron-buraco instáveis dentro do band gap . Portanto as diferentes excitações empregadas em 350 e 415 nm nos permitem produzir diferentes emissões luminescentes particulares de cada sistema quando do decaimento radiativo destes pares. Assim observou-se a intensificação e/ou o desaparecimento de bandas em função da excitação aplicada, sendo o CTO o composto de maior eficiência luminescente dente os três materiais estudados. Desta forma as perovskitas tornaram-se materiais atraentes com propriedades híbridas o que faz delas compostos ainda mais atraentes à investigação cientifica.

Made available in DSpace on 2016-06-02T20:34:31Z (GMT). No. of bitstreams: 1 4030.pdf: 13326291 bytes, checksum: 9a4aeac353bf0b0bd4921c3178c0817d (MD5) Previous issue date: 2011-12-19 / Financiadora de Estudos e Projetos / In this study, CuMoO4 were synthesized, characterized and crystallized into powders in two structures: monoclinic and triclinic. CuMoO4 powder were synthesized by precipitation, and the reaction s pH were controlled due to the importance of pH in the process of development CuMoO4. The powder was processed at 140°C at different times in hydrothermal assisted by microwave irradiation, it is possible to prepare materials that have different structure organization degrees. The structural and morphologic properties of these materials were analyzed through X ray diffraction, transmission electronic microscopy, photoluminescence spectroscopy and zeta potential, among anothers. Using those techniques, it was possible to observe the pH s influence in the solution and its reflex in the structural development, where there are two differents structures competing in solution (Triclinic and Monoclinic). The structural organization leads the mechanisms of FL by its cluster position (order disorder). The evolution of the structural disorder at short range was controlled by using the HM, and its reflexes could be observed in the FL. The photoluminescent emissions in blue and red were attributed to clusters [Mo4] and [MO6] and its space position, which were modified by HM. The difference between the emission maxima and minimal was assigned to distinct photoemission mechanisms that are related to the electronic structure of these materials / Neste trabalho foi realizada a síntese e caracterização de pós de CuMoO4 que se cristaliza em duas estruturas do tipo monoclinica e triclínica. O material foi sintetizado via precipitação, com controle efetivo de pH do meio reacional devido a sua importância no processo de formação dos CuMoO4. O pó foi processado a 140°C por diferentes tempos em hidrotérmico assistido por irradiação de microondas (HM), o que permite obter material com diferentes graus de organização na mesma estrutura. As propriedades estruturais e morfológicas dos materiais foram analisadas por intermédio de difração de raios X, microscopia eletrônica de transmissão, emissão fotoluminescente, potencial zeta dentre outras. Estas técnicas permitiram observar a influência do pH na solução e seu reflexos no desenvolvimento estrutural, onde há duas estruturas concorrentes competindo na solução (Triclinica e Monoclinica) A organização destas estruturas direciona o mecanismo de Fololuminescencia (FL), pela relaçao de ordem desordem estrutural. A evolução da desordem estrutural a curta distância foi controlada por uso do HM, e seu reflexo poderam ser observado na FL. As emissões fotoluminescentes na região do azul e vermelho foram atribuídos aos clusters [Mo4] e [Mo6] e sua posição na estrutura, que foram modificadas por HM. A diferença entre os máximos e mínimos de emissão foi atribuída aos mecanismos de fotoemissão distintos que estão relacionados com a estrutura eletrônica desses materiais.

Gases de Ijede, nos quais as partículas interagem exclusivamente via repulsão de caroço duro, têm sido utilizados como base para modelos dos mais variados sistemas desde fluidos I e magnetos atlé meios granulares e sistemas biológicos. Nesta tesel estudamos, através de simulações de Monte Carlo, gases de rede compostos por partículasl extensas (que excluem a ocupação de sítios vizinhos) numa rede quadrada bidimensiona11 Exclusões dos primeiros até os quintos vizinhos mais próximos (nearest neighbors, NNi) foram consideradas. Em concordância com resultados prévios, o gás com exclusão lNN I(até primeiros vizinhos) apresenta uma transição ordem-desordem contínua pertencente à classe de universalidade do modelo de Ising. Surpreendentemente, o gás de rede com exclusão até segundos vizinhos (2NN) também passa por uma transição contínua nesta mesma classe de universalidade, enquanto que a teoria de Landau-Lifshitz prediz uma transição pertencente à classe de universalidade do modelo XY com anisotropia cúbica. O gás de rede com exclusão 3NN passa por uma transição ordem-desordem descontínua em acordo com reSultados prévios, obtidos via método da matriz de transferência e teoria de Landau-Lifshitz. Por outro lado, o gás com exclusão 4NN novamente exibe uma transição contínua na cldsse de universalidade do modelo de Ising, em contradição com as previsões da teoria de Lahdau-Lifshitz. Finalmente, o gás com exclusão até os quintos vizinhos mais próximos, 5NN; passa por uma transição descontínua. O compordmento desses sistemas na fase fluida quando os lados dos quadrados são paralelos à redel subjacente é descrito por uma equação de estado baseada na aproximação de Flory para u'ma solução de polímeros na rede, porém modificada convenientemente para sistemas de partículas duras. Os resultados obtidos, quando comparados com as simulações de Monte Carl~, mostram-se bastante efetivos, mesmo para frações de volume bastante altas, desde que a densidade não atinja o ponto onde os sistemas sofrem a transição ordemdesordem. / Lattice gases, in which particles interact only through hard-core repulsion, have been used as a base for modeling different systems ranging from fluids and magnets to granular materiaIs and biological systems. ln this thesis we have studied, using Monte Cado simulations, two dimensionallattice gases composed of particles of extended hard-core which prevents the neighboring sites from being occupied. Exclusion shells of up to five nearest neighbors (NN) were considered. ln agreement with previous results, a Iattice gas of lNN exclusion (first nearest neighbor exclusion) undergoes a continuous order-disorder transition belonging to the lsing universality class. Surprisingly, the gas of 2NN exclusions also undergoes a continuous transition in the same universality class, while the Landau-Lifshitz theory predicts that this transition should be in the universality class of the XY model with cubic anisotropy. Lattice gas of 3NN exclusions undergoes a discontinuous order-disorder transition in agreement with the transfer matrix methods and with the Landau-Lifshitz theory. On the other hand, the gas of 4NN exclusions once again exhibits a continuous transition in the lsing universality class - contradicting the Landau-Lifshitz theory. Finally, the gas of 5NN exclusions undergoes a discontinuous transition. The thesis also shows that the thermodynamics of the fluid phase of oriented parallel hard squares is well described by an equation of state obtained using a modified Flory approximation. The resuIting pressures and chemical potentials are in excellent agreement with the Monte Cado simuIations as Iong as the volume fractions remain not too high.

Submitted by MARCILENE MACHADO DOS SANTOS SARAH (marcilene.m.sarah@gmail.com) on 2018-07-20T14:51:05Z No. of bitstreams: 1 DISSERTAÇÃO - MARCILENE SARAH.pdf: 1469614 bytes, checksum: 7650422035f8634c8664c2ba24e1c108 (MD5) / Approved for entry into archive by Karina Gimenes Fernandes null (karinagi@fcav.unesp.br) on 2018-07-20T17:27:53Z (GMT) No. of bitstreams: 1 sarah_mms_me_jabo.pdf: 1469614 bytes, checksum: 7650422035f8634c8664c2ba24e1c108 (MD5) / Made available in DSpace on 2018-07-20T17:27:53Z (GMT). No. of bitstreams: 1 sarah_mms_me_jabo.pdf: 1469614 bytes, checksum: 7650422035f8634c8664c2ba24e1c108 (MD5) Previous issue date: 2018-06-08 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / A deficiência oculta de potássio (K) é comum em feijoeiro, mas o silício (Si) quando fornecido via solução nutritiva (raiz) ou via foliar pode aliviar os estresses ocasionados pela deficiência deste nutriente, entretanto, isso ainda não é conhecido nesta espécie. A partir disso, objetivou-se verificar a melhor fonte e concentração de Si aplicado via foliar, e se essa fonte fornecida via solução nutritiva e foliar é eficiente em mitigar os estresses por deficiência de potássio em feijoeiro. Para isso, foram desenvolvidos dois experimentos em casa de vegetação com plantas de feijão cultivadas em sistema hidropônico. Um estudo preliminar visou definir a melhor fonte e concentração de Si aplicados via foliar. O segundo experimento foi em esquema fatorial 2x3, com solução nutritiva deficiente (0,2 mmol L-1 de K) e suficiente (6 mmol L-1 de K) em potássio, e o fornecimento de Si foi via solução nutritiva (2 mmol L-1 de Si), foliar (5,36 mmol L-1 de Si) e controle (0 mmol L-1 de Si), disposto em delineamento inteiramente casualizado, em 4 repetições. Foram avaliados parâmetros fisiológicos, nutricionais e crescimento das plantas. E verificou-se que a pulverização foliar com Si foi viável agronomicamente para o feijoeiro, destacando-se o silicato de sódio e potássio estabilizado na concentração de 5,36 mmol L-1. A deficiência de K causou prejuízo no desenvolvimento das plantas de feijão que não receberam Si. O Si mitigou estresses por deficiência de K no feijoeiro devido a melhoria das variáveis nutricionais, fisiológicas e de crescimento, destacando-se o fornecimento de Si via solução nutritiva em relação a via foliar, embora essa última forma de aplicação do elemento benéfico também atenuou os efeitos da deficiência do macronutriente. / Undetected potassium (K) deficiency is common in bean plants. Although silicon (Si) supplied via nutrient solution (roots) or foliar application may alleviate the resulting stress, it remains unknown in this species. This pioneering study aimed to determine the best source and concentration of leaf-applied Si, and whether providing it via nutrient solution and foliar application is efficient in alleviating K deficiency stress in bean plants. To that end, two experiments were conducted in a greenhouse with bean plants grown in a hydroponic system. Due to the lack of reliable information for the bean plant, a preliminary study aimed at determining the best leaf-applied source and concentration of Si. The second experiment used a completely randomized 2x3 factorial design, with deficient (0.2 mmol L-1 of K) and sufficient potassium solution (6 mmol L-1 of K), Si supplied via nutrient solution (2 mmol L-1 of Si), foliar application (5.36 mmol L -1 of Si) and controls (0 mmol L-1 of Si), and 4 repetitions. Physiological, nutritional and plant growth parameters were measured. Foliar spraying with Si was agronomically feasible for the bean plant, with silicate of sodium and potassium stabilized at a concentration of 5.36 mmol L -1 . K deficiency without the addition of Si compromised plant growth. Si mitigated K deficiency stress in the bean plant due to enhanced nutritional, physiological and growth variables, underscoring Si supply via nutrient solution over foliar application, although the latter also attenuated K deficiency.

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The present work studies the counterintuitive phenomenon of inverse transitions (IT). The IT are a class of phase transitions (reversible) in which the ordered phase appears at higher temperatures than the disordered one. Different models have been proposed to describe characteristics of IT. The goal of this work is just to propose a model of disordered interactions, which is able to present general characteristics of a inverse transition type, the inverse freezing (IF). The IF is a reversible transition from a paramagnetic phase (PM) to the spin glass order (SG) on heating. Within this context the van Hemmen SG model is analyzed in a fermionic formulation, in which the spin operators are written as a bilinear combination of fermionic creation and annihilation operators. In this model the random interactions Ji j introduce disorder and frustration, and the chemical potential m controls the average occupancy of fermions per site. The problem is analyzed for two different types of quenched disorders: bimodal (discrete) and gaussian (continuous). It is important to note that the disorder in the model analyzed here were treated without the use of the replica method and its complications. The results depend on the particular disorder. The behavior of the order parameters, entropy and occupation number are analyzed. Phase diagrams of temperature T versus chemical potential m can then be build. A reentrance transition is found for a certain range of m when the gaussian distribution is adopted. This reentrance transition is associated with the IF that occurs in a first-order transition from the paramagnetic to the spin glass phase when the temperature increases. On the other hand, models following disordered interactions of Sherrington-Kirkpatrick (SK) type suggest that the onset of IF can be a consequence of complex scenario for the free energy. In these models the replica method is used to treat the disorder and the solutions present this complex scenario. However, from the results obtained in present fermionic van Hemmen model, it can be concluded that the necessary conditions for a model exhibit IF are the combined effects of frustration and magnetic dilution (favoring states not interacting, controlled by m). Thus, the treatment of model presented in this work does not use the replica method or the complicated scenario of free energy and it is able to reproduces the characteristics of an inverse freezing. This is attributed to the presence of frustration and magnetic dilution. Keywords: Disorder. Quantum Spin Glass. Fermionic model. Inverse transitions / O presente trabalho estuda o fenômeno contraintuitivo das transições inversas (TI), que são uma classe de transições de fase (reversíveis) em que a fase usualmente ordenada aparece em temperaturas mais altas que a fase desordenada. Vários modelos já foram propostos para descrever as TI por apresentarem características desse tipo de transição. O objetivo deste trabalho é justamente buscar um novo modelo, de interações desordenadas, que seja capaz de apresentar características gerais de um tipo de transição inversa, o congelamento inverso (CI). O CI trata de uma transição reversível a partir de uma fase paramagnética (PM) para uma fase vidro de spin (VS) sobre aquecimento. Dentro desse contexto, o modelo VS de van Hemmen é analisado em uma formulação fermiônica, em que os operadores de spins são escritos como uma combinação bilinear dos operadores fermiônicos de criação e destruição. Neste modelo, em que interações aleatórias Jij introduzem desordem e frustração, e o potencial químico µ controla a ocupação média de férmions por sítio, o problema é analisado para dois tipos de desordem temperada: uma dada pela distribuição bimodal e outra dada pela distribuição gaussiana. Vale salientar que ambas as desordens são tratadas sem o uso do méetodo das réplicas, e cada uma delas apresenta resultados particulares. Através da análise do comportamento dos parâmetros de ordem, entropia e número de ocupação médio, diagramas de fases da temperatura T pelo potencial químico µ podem então ser construídos. Uma transição reentrante é encontrada para um certo valor de µ quando a distribuição gaussiana é adotada. Essa transição reentrante está associada ao congelamento inverso, que ocorre em uma transição de primeira ordem entre as fases PM e VS quando a temperatura aumenta. Por outro lado, modelos que seguem as interações desordenadas do tipo proposto por Sherrington-Kirkpatrick (SK), que utilizam o método das réplicas e apresentam o complexo cenário da energia livre, sugerem que essa última possa ter ligação com o aparecimento de CI em tal modelo. Porém, a partir dos resultados obtidos neste modelo de van Hemmen fermiônico, pode-se concluir que as condições necessárias para que determinado modelo apresente uma transição inversa do tipo congelamento, são os efeitos combinados de frustração e diluição magnética (favorecimento dos estados não interagentes, controlada pelo m). Assim, o modelo apresentado neste trabalho, não utiliza o método das réplicas nem o complicado cenário da energia livre e, é capaz de reproduzir as características de um CI.

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2016-02-29T22:23:18Z No. of bitstreams: 1 VivianMontardoEscobar_TESE.pdf: 17648948 bytes, checksum: 23d85bb79cd4d63d8a4cec5ad7c10da7 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2016-03-01T23:57:25Z (GMT) No. of bitstreams: 1 VivianMontardoEscobar_TESE.pdf: 17648948 bytes, checksum: 23d85bb79cd4d63d8a4cec5ad7c10da7 (MD5) / Made available in DSpace on 2016-03-01T23:57:25Z (GMT). No. of bitstreams: 1 VivianMontardoEscobar_TESE.pdf: 17648948 bytes, checksum: 23d85bb79cd4d63d8a4cec5ad7c10da7 (MD5) Previous issue date: 2015-03-27 / Filmes finos de Co2FeAl (CFA) e tricamadas CFA/M/CFA, nas quais M ? Au ou Ag, produzidos por magnetron sputtering em substratos de vidro e orientados de MgO (100), foram investigados com ?nfase em suas propriedades estruturais, magn?ticas est?ticas e din?micas, sendo estabelecida uma rota para produ??o de ligas de Heusler na forma de filmes finos em substratos amorfos e orientados. Atrav?s da an?lise de difra??o de raios-X, destaca-se a forma??o de estrutura cristalina c?bica do CFA, com fase A2 (desordenada estruturalmente), onde os ?tomos se distribuem aleatoriamente na rede. As medidas de magnetoimped?ncia foram realizadas variando o ?ngulo de aplica??o do campo magn?tico externo e a corrente de sonda com rela??o ? anisotropia. As medidas de VSM revelam, em algumas amostras, a presen?a de um patamar ocasionado pela forma??o de sistema bif?- sico. Por esse motivo, os resultados apresentaram efeitos de magnetoimped?ncia assim?trica (AMI). Para filmes simples e tricamadas com espessura da camada magn?tica igual a 500 nm, o efeito AMI ? mais pronunciado. Com o aumento da espessura, apesar do comportamento bif?sico permanecer, os efeitos assim?tricos come?am a diminuir. O comportamento magn?tico quasi-est?tico e din?mico ? interpretado em termos das caracter?sticas estruturais das amostras produzidas. Portanto, foi estabelecida uma rota para produ??o de ligas de Heusler na forma de filmes finos, com fase estrutural A2 e devido ? desordem estrutural foi poss?vel estudar os efeitos hister?ticos e assim?tricos de MI. / Thin films of Co2FeAl (CFA) and trilayers with CFA/M/CFA, where M is Au or Ag, produced by magnetron sputtering onto glass and oriented (MgO (100)) substrates were investigated. The structural, magnetic static and magnetic dynamics properties were analyzed by distinct experimental techniques. Through X-ray diffraction was observed an A2 phase for the samples (completely disordered), where the atoms are randomly located in the lattice. The static magnetic behavior, in some samples, reveal a plateau behavior generated by a biphasic system. The magnetoimpedance measurements were performed by varying the angle between the external magnetic field and current with respect of anisotropy direction. For this reason, the MI results show a asymmetric magnetoimpedance (AMI) behavior. For the single and trilayers samples with 500 nm-thick, the AMI effect is more evident in comparison with samples with 1000 nm-thick. Therefore, in this work was stablished a route to produce Heusler alloy samples with A2 phase in thin film geometry onto amorphous and oriented substrates, and due to structural disorder was possible to study the hysteretic and MI asymmetric effects.

This study conducted convergent validation on participant’s identification with the prototypical values of histrionic personality disorder repertoire, an important part of acceptance and commitment psychotherapy (ACT). The Multiaxial Inventory of Personality (MCMI – III) was administered to two mixed groups of participants (cases versus controls). Participants were also interviewed using the SCID- II,and a structured interview The content analysis of the structured interviews showed that participants with the disorder had the highest mean in the “A-R-VP self-report identification” at all the 12 values examined on a 0 to 5 point scale, with scores closer to 5. Meanwhile, those without the disorder had scores of identification between 0 and 1. The results of the Student t test confirmed the findings. People with histrionic personality disorder identify themselves with a repertoire of twelve characteristic values of this disorder. / El presente estudio validó  convergentemente, tras un análisis de contenido de entrevistas estructuradas, a un grupo de participantes “casos” versus un grupo equivalente de “controles” mixto su identificación con un repertorio de valores prototípicos del trastorno histriónico de la personalidad. Se aplicó la entrevista SCID-II, el  Inventario Multiaxial  de Personalidad MCMI-III  y la entrevista estructurada. Se halló que los participantes con el trastorno mostraron las medias más altas en su reporte de identificación con  un conjunto de 12 valores examinados  una escala de 0-5 en oposición a quienes no tenían dicho trastorno, los cuales tuvieron puntajes de identificación entre 0 y 1. Los resultados de la prueba t de student confirmaron lo anterior. Se concluye  que  las personas evaluadas con trastorno histriónico de la personalidad  se identifican con un repertorio de doce valores característicos de este trastorno. / La présente étude a validé de manière convergente l’identification que les participants de deux groupes mixtes équivalents, l’un de cas et l’autre de contrôles, ont fait sur un répertoire de valeurs prototypiques du trouble de personnalité histrionique, en tenant compte de son importance dans la diffusion et l’acceptation dans la thérapie d’acceptation et d’engagement (ACT). L’interview SCID-II, l’Inventaire Multiaxial de Personnalité MCMI-III et une entretien structurée ont été appliquées. Après avoir analysé le contenu des entretiens structurés et l’auto-rapport (A-R-VP) des identifications avec les valeurs du trouble en question, il a été constaté que les participants avec le trouble de la personnalité histrionique montraient les moyens les plus élevés sur une échelle de 0 -5, avec des valeurs plus proches de 5, alors que celles sans trouble présentaient des scores d’identification entre 0 et 1 sur la même échelle. Les résultats du test t de Student ont confirmé ce qui précède. On conclut que les personnes évaluées avec un trouble de la personnalité histrionique sont identifiées avec un répertoire de douze valeurs caractéristiques de ce trouble / O presente estudo validou a identificação com um repertório de valores prototípicos do transtorno de personalidade histriônica de um grupo de participantes com esse distúrbio em oposição a outro grupo de participantes sem este trastorno de personalidade que são importantes na defusão e na deliteração no Terapia de aceitação e compromisso (ACT). Desta forma, formaram-se um grupo de casos e outro grupo de controles. Ambos os grupos foram misturados. A entrevista SCID-II, o Inventário de Personalidade Multiaxial MCMI-III e a entrevista estruturada foram aplicadas. Os participantes com o transtorno tiveram os meios mais elevados em seu relatório “A-R-VP de identificação com um conjunto de 12 valores con escores perto de 5, examinados em uma escala de 0 a 5, em oposição àqueles que não tinham o referido transtorno, que apresentavam escores entre 0 e 1. Os resultados do teste de Student t confirmaram o acima. Conclui-se que as pessoas avaliadas com transtorno de personalidade histriônica são identificadas com um repertório de doze valores característicos desta desordem.

Orientador: Marcius César Soares Freire / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Artes / Made available in DSpace on 2018-08-17T03:37:30Z (GMT). No. of bitstreams: 1 Souza_BernardoTeodoricoCosta_M.pdf: 2196291 bytes, checksum: e05691f9df0767c35af9ef01b3480a2c (MD5) Previous issue date: 2010 / Resumo: Este trabalho propõe, a partir de uma análise das estratégias narrativas do filme Serras da Desordem (TONACCI, 2006) e seus desdobramentos, uma abordagem das relações entre Cinema e História que enfoca o cinema moderno de acordo com as considerações de Pasolini ("Cinema de Poesia") e Deleuze ("As Potências do Falso") acerca da narrativa neste. Tomado o exemplo de Serras da Desordem como ilustração de cinema moderno a desenvolver uma narrativa que não se orienta por um modelo de verdade, e tampouco se referencia num substrato historiográfico linear, propõe-se uma abordagem histórica capaz de problematizar as imagens cinematográficas em sua imanência e os processos narrativos como pensamento historiográfico, mais propriamente pela perspectiva arqueológica de Foucault ("Arqueologia do Saber") / Abstract: This paper proposes, through an analysis of the narrative strategies in the movie Serras da Desordem (Tonacci, 2006) and its implications, an approach to relations between cinema and history that focuses on modern cinema according to the considerations of Pasolini ("Film Poetry") and Deleuze (" The Powers of the False ") about its narrative. Once taken the example of Serras da Desordem as an illustration of modern cinema to develop a narrative that is not guided by a model of truth, or referenced in a linear historiographical substrate, we propose a historical perspective that is abble to discuss the cinematic images in its immanence and the narrative processes as historiographical propositions, more specifically through the archaeological perspective of Michel Foucault ("Archaeology of Knowledge") / Mestrado / Mestre em Multimeios

A proposta deste estudo foi desenvolver ferramentas que permitam um exame de palpação completo utilizando o algômetro e verificar a validade e confiabilidade intra e interexaminadores. Neste estudo foram examinados 80 indivíduos, sendo 40 pacientes sintomáticos que freqüentavam a clínica de prótese da Faculdade de Odontologia da Universidade de São Paulo, divididos em 20 mulheres e 20 homens com idade média de 43 anos e 40 voluntários assintomáticos divididos em 20 mulheres e 20 homens com idade média de 40 anos. Os pacientes foram examinados com um algômetro digital, ferramenta de palpação intra-oral e em forma de pinçamento em três sessões diferentes de exames com intervalo de uma semana entre si. Na primeira sessão os pacientes sintomáticos foram avaliados por um examinador, e este grupo foi denominado F1. Após uma semana, na segunda sessão, os mesmos pacientes foram reavaliados pelo mesmo examinador, e foram denominados grupoF2, após 30 minutos um segundo examinador avaliou os mesmos pacientes, com os resultados formou-se o grupoJ. Após uma semana, na terceira sessão, os 40 voluntários assintomáticos (controle) foram avaliados pelo examinador F, grupo denominado C. A validade do algômetro foi avaliada comparando-se grupoF2 x grupoC (sintomáticos x assintomáticos). A confiabilidade intra-examinador foi avaliada comparando-se grupoF1 x grupoF2 e a confiabilidade interexaminadores comparando-se grupoF2xgrupoJ. Após a aplicação de testes estatísticos a validade do algômetro foi comprovada, a confiabilidade intraexaminador foi considerada boa, porém a confiabilidade interexaminadores foi de aproximadamente 50%, mostrando que para se atingir altos níveis de confiabilidade é necessário um programa de calibragem e uma padronização da taxa de aplicação da força. / The purpose of this study was to develop tools that allow a complete palpation examination using an algometer to evaluate validity and reliability. This study examined 80 subjects, 40 symptomatics patients from the school of Dentistry, University of São Paulo, divided in 20 women and 20 men, mean age 40 years, were examined using an eletronic algometer, intra-oral tool and pincer ? type pressure tool. The symptomatics patients were examinated in tree different sessions with intervals of one week. In the first session, an examiner (F1 group) evaluated the simptomatics patients. After one week, in the second session, the same examiner (F2 group) evaluated the same patients, 30 minutes later a second examiner evaluated the same patients (J group). One week later, in the third session, the first examiner (C group) evaluated 40 healthy volunteers. The validity of pressure digital algometer was obtained comparing F2 group x C group. The reliability intra examiner was obtained comparing F1 group x F2 group and the reliability inter examiners comparing F1 group x J group. After a statistic study, validity of the pressure digital algometer was obteined, good intra-examiner reliability was found but low interexaminer reliability was found, sugesting that to achieve hight levels of reliability a calibrating program and a padronization of pressure rate is necessary.