Orientadores: Celso Aparecido Betran e Lauro Tasuo Kubota / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Quimica / Made available in DSpace on 2018-07-22T20:37:57Z (GMT). No. of bitstreams: 1 Kawachi_ElizabeteYoshie_M.pdf: 6772711 bytes, checksum: 7770070df8f019dfb8e6dfd5e9062b0e (MD5) Previous issue date: 1997 / Mestrado

Orientador : Celso Aparecido Bertran / Tese (doutorado) - Universidade Estadual de Campinas, Instituto de Quimica / Made available in DSpace on 2018-08-02T08:48:23Z (GMT). No. of bitstreams: 1 Kawachi_ElizabeteYoshie_D.pdf: 4844897 bytes, checksum: 91662f68c8ec103a1d9422aeccc4c090 (MD5) Previous issue date: 2002 / Doutorado

Orientador: Cesar C. Santana / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Quimica / Made available in DSpace on 2018-07-25T21:01:28Z (GMT). No. of bitstreams: 1 Beppu_MarisaMasumi_D.pdf: 4503565 bytes, checksum: 2605c60154965545fc1e47009b90b104 (MD5) Previous issue date: 1999 / Resumo: A quitosana tem despontado nos últimos anos como um biomaterial de grande potencialidade para a aplicação em vários campos, passando por medicina, biotecnologia, alimentos, etc. entretanto, uma face ainda pouco explorada é o comportamento desse biomaterial quando em contato com fluidos corpóreos. Este trabalho objetiva a obtenção de membranas densas e porosas de quitosana de casca de caranguejo, sua mosificação através de reação com glutaraldeído e poli(ácido acrílico)-PAA, e a calcificação promovida sobre esses substratos. Utilizou-se, para tanto, experimentos in vitro, com duração de 7 dias a 1 mês, no qual se mergulhavam os substratos (modificados ou não) em soluções que simulam as concentrações de sais observadas em fluidos corpóreos reais. Estudou-se influências de fatores como: pH, composição do meio calcificante e características físicas (permeabilidade, porosidade) e químicas do substrato de quitosana; sobre o tipo de calcificação observado. A análise dos substratos de quitosana com ou sem calcificação foi realizada através de técnicas como microspia (eletrônica e varredura e força atômica), espectroscopia (EDS, FTIR-ATR) e análises químicas (elementar de Pe Ca) e estruturais (difratometria de RX e adsorções). Observou-se que calcificação dependa: 1) do tratamento ao qual a quitosona era submetida: a deposição em grande extensão era obtida em amostras tratadas com PAA, principalmente devido aos grupos carboxílicos que adsorvem muito bem os íons cálcio... Observação: O resumo, na íntegra, poderá ser visualizado no texto completo da tese digital / Abstract: Chitosan is recently being appointed as a biomaterial with significant potential to use in many fields, such as medical science, biotechnology, food science, etc. However, the behavior when chitosan is contacted with body fluids, is still not completely understood. The present work aims to study: the production of dense and porous chitosan (from crab shells) membranes; their chemical modification (by reaction with glutaraldehyde or addition of poly(acrylie acid)-PAA); and their calcification. In order to do that, in vitro experiments were done: the substrates were soaked in a solution which simulated the salt concentration of body fluids (plasma) from 7 days to 1 month. Effects of pH, calcifying medium composition and physical (porosity, permeability) and chemical characteristics of substrates on calcification quality and degree were observed. Samples were analyzed though microscopy (scanning electron microscopy and atomic force microscopy), spectroscopy (EDS and FTIR-ATR) and chemical (P and Ca) and structural (X-ray diffraction and adsorption) analyses. It was observed that calcification depended on: 1) treatment under which chitosan was submitted: expressive deposition was obtained in samples treated with PAA, mainly due to carboxil groups that adsorb calcium ion. The opposite was observed in samples fixed with glutaraldehyde, which tends to increase the hydrophobicity of matrix, inducing less calcification... Note: The complete abstract is available with the full electronic digital thesis or dissertations / Doutorado / Engenharia de Processos / Doutor em Engenharia Química

A utilização de biomateriais a base de fosfato de cálcio tem revolucionado a medicina no reparo de partes danificadas do sistema ósseo. Dentre estes, os cimentos a base de fosfatos de cálcio de pega hidráulica tem despertado grande interesse em função de sua biocompatibilidade e endurecimento “in situ”, o que permite uma maior facilidade de manipulação e adaptação à forma e dimensões do defeito ósseo. Entretanto, estes cimentos possuem baixa resistência mecânica quando comparados com os ossos do corpo humano. Neste presente trabalho foi estudado a obtenção de pós de cimento de fosfato de cálcio e adicionados a fibras de poli(ácido co-glicólico) (PLGA) e Alginato de Sódio, visando o aumento das propriedades mecânicas destes cimentos. Foi utilizado um novo método de obtenção de fibras por gotejamento em reagente, tanto para o PLGA e o Alginato de Sódio, sendo depois congeladas essas fibras e liofilizadas. Ambos os métodos de obtenção de fibras por gotejamento foram Patenteados, além de publicações em revistas e congressos internacionais. Com este mecanismo foi possível obter-se fibras por método inovador e reforçar a matriz, o que favoreceu o aumento das propriedades mecânicas, permitindo, assim, a obtenção de materiais mais resistentes. Os materiais obtidos foram utilizados na construção de scaffolds para crescimento tecidual, possibilitando manter uma maior integridade mecânica. / The use of biomaterials based on the calcium phosphate has revolutionized the medicine to repair damaged parts of the skeletal system. Among these, the cements based calcium phosphates handle hydraulic has been much interest due to its biocompatibility and hardening "in situ", allowing greater ease of handling and adjustment to the shape and dimensions of the bone defect. However, these cements have lower mechanical strength when compared with the bones of the human body. In the present work to obtain powders of cement of calcium phosphate and added to fibers of poly (co-glycolic acid) (PLGA) and sodium alginate, in order to increase the mechanical properties of these cements. We used a novel method for obtaining fibers in drip reagent for both PLGA and sodium alginate; the fibers are then frozen and lyophilized. Both methods of obtaining fibers were patented drip, as well as publications in international journals and conferences. With this mechanism it was possible to obtain novel method for fibers and strengthen the matrix, thus favoring increased mechanical properties, thus allowing obtaining more resistant materials. The materials were used in the construction of scaffolds for tissue growth, allowing greater maintain mechanical integrity.

A utilização de biomateriais a base de fosfato de cálcio tem revolucionado a medicina no reparo de partes danificadas do sistema ósseo. Dentre estes, os cimentos a base de fosfatos de cálcio de pega hidráulica tem despertado grande interesse em função de sua biocompatibilidade e endurecimento “in situ”, o que permite uma maior facilidade de manipulação e adaptação à forma e dimensões do defeito ósseo. Entretanto, estes cimentos possuem baixa resistência mecânica quando comparados com os ossos do corpo humano. Neste presente trabalho foi estudado a obtenção de pós de cimento de fosfato de cálcio e adicionados a fibras de poli(ácido co-glicólico) (PLGA) e Alginato de Sódio, visando o aumento das propriedades mecânicas destes cimentos. Foi utilizado um novo método de obtenção de fibras por gotejamento em reagente, tanto para o PLGA e o Alginato de Sódio, sendo depois congeladas essas fibras e liofilizadas. Ambos os métodos de obtenção de fibras por gotejamento foram Patenteados, além de publicações em revistas e congressos internacionais. Com este mecanismo foi possível obter-se fibras por método inovador e reforçar a matriz, o que favoreceu o aumento das propriedades mecânicas, permitindo, assim, a obtenção de materiais mais resistentes. Os materiais obtidos foram utilizados na construção de scaffolds para crescimento tecidual, possibilitando manter uma maior integridade mecânica. / The use of biomaterials based on the calcium phosphate has revolutionized the medicine to repair damaged parts of the skeletal system. Among these, the cements based calcium phosphates handle hydraulic has been much interest due to its biocompatibility and hardening "in situ", allowing greater ease of handling and adjustment to the shape and dimensions of the bone defect. However, these cements have lower mechanical strength when compared with the bones of the human body. In the present work to obtain powders of cement of calcium phosphate and added to fibers of poly (co-glycolic acid) (PLGA) and sodium alginate, in order to increase the mechanical properties of these cements. We used a novel method for obtaining fibers in drip reagent for both PLGA and sodium alginate; the fibers are then frozen and lyophilized. Both methods of obtaining fibers were patented drip, as well as publications in international journals and conferences. With this mechanism it was possible to obtain novel method for fibers and strengthen the matrix, thus favoring increased mechanical properties, thus allowing obtaining more resistant materials. The materials were used in the construction of scaffolds for tissue growth, allowing greater maintain mechanical integrity.

A utilização de biomateriais a base de fosfato de cálcio tem revolucionado a medicina no reparo de partes danificadas do sistema ósseo. Dentre estes, os cimentos a base de fosfatos de cálcio de pega hidráulica tem despertado grande interesse em função de sua biocompatibilidade e endurecimento “in situ”, o que permite uma maior facilidade de manipulação e adaptação à forma e dimensões do defeito ósseo. Entretanto, estes cimentos possuem baixa resistência mecânica quando comparados com os ossos do corpo humano. Neste presente trabalho foi estudado a obtenção de pós de cimento de fosfato de cálcio e adicionados a fibras de poli(ácido co-glicólico) (PLGA) e Alginato de Sódio, visando o aumento das propriedades mecânicas destes cimentos. Foi utilizado um novo método de obtenção de fibras por gotejamento em reagente, tanto para o PLGA e o Alginato de Sódio, sendo depois congeladas essas fibras e liofilizadas. Ambos os métodos de obtenção de fibras por gotejamento foram Patenteados, além de publicações em revistas e congressos internacionais. Com este mecanismo foi possível obter-se fibras por método inovador e reforçar a matriz, o que favoreceu o aumento das propriedades mecânicas, permitindo, assim, a obtenção de materiais mais resistentes. Os materiais obtidos foram utilizados na construção de scaffolds para crescimento tecidual, possibilitando manter uma maior integridade mecânica. / The use of biomaterials based on the calcium phosphate has revolutionized the medicine to repair damaged parts of the skeletal system. Among these, the cements based calcium phosphates handle hydraulic has been much interest due to its biocompatibility and hardening "in situ", allowing greater ease of handling and adjustment to the shape and dimensions of the bone defect. However, these cements have lower mechanical strength when compared with the bones of the human body. In the present work to obtain powders of cement of calcium phosphate and added to fibers of poly (co-glycolic acid) (PLGA) and sodium alginate, in order to increase the mechanical properties of these cements. We used a novel method for obtaining fibers in drip reagent for both PLGA and sodium alginate; the fibers are then frozen and lyophilized. Both methods of obtaining fibers were patented drip, as well as publications in international journals and conferences. With this mechanism it was possible to obtain novel method for fibers and strengthen the matrix, thus favoring increased mechanical properties, thus allowing obtaining more resistant materials. The materials were used in the construction of scaffolds for tissue growth, allowing greater maintain mechanical integrity.

Tese de mestrado. Engenharia Biomédica. Faculdade de Engenharia. Universidade do Porto, Instituto Nacional de Engenharia Biomédica. Universidade do Porto. 2009

Submitted by Thales Augusto Garcia Pelizaro (pelizaro.thales@gmail.com) on 2018-08-11T04:11:22Z No. of bitstreams: 1 Pelizaro_t.a.g.pdf: 2749539 bytes, checksum: 985de4c95367a9763a3f49744c2d7d21 (MD5) / Approved for entry into archive by Ana Carolina Gonçalves Bet null (abet@iq.unesp.br) on 2018-08-15T20:29:41Z (GMT) No. of bitstreams: 1 pelizaro_tag_me_araiq_int.pdf: 2698266 bytes, checksum: fd08f46804e8ae8c87783cd8e9da031f (MD5) / Made available in DSpace on 2018-08-15T20:29:41Z (GMT). No. of bitstreams: 1 pelizaro_tag_me_araiq_int.pdf: 2698266 bytes, checksum: fd08f46804e8ae8c87783cd8e9da031f (MD5) Previous issue date: 2018-07-25 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / A busca pelos melhores métodos de produção e com o menor custo possível é uma necessidade para o desenvolvimento de novos biomateriais ou para aprimorar os já existentes. Baseado nessa premissa, o trabalho aqui desenvolvido visou o estudo de diferentes métodos de síntese de diferentes fosfatos de cálcio. Tratam-se de materiais biocerâmicos utilizados na área da Saúde. Para a realização de análise químicas, físicas, físico-químicas, morfológicas e de tamanho de partículas, foram utilizadas as técnicas de difração de raio-X (DRX); espectroscopia no infravermelho (FITR) e microscopia eletrônica de varredura (MEV). A produção dos fosfatos de cálcio envolveu diversas variantes no processo de síntese e obtenção do pó; dentre estas houve diferentes aplicações do ultrassom (momento da aplicação e/ou seu tempo de duração) e diferentes métodos de secagem. De uma forma geral, as características químicas, físicas e físico-química encontradas estavam de acordo com o observado na literatura, o que indica que os métodos aqui empregados atingiram o objetivo de obtenção dos fosfatos de cálcio; ao mesmo tempo, ficou claro que é possível utilizar métodos alternativos, como meio de produção, garantindo uma produção em larga escala, de forma eficiente e menos onerosa, preservando-se as características básicas de cada fase de fosfato de cálcio. / The search for the best methods of production and the lowest costs possible is the major necessity for the development of new and improved biomaterials. Based on this premise, the aime of this work was to develop a study of different methods of synthesis with different calcium phosphates. Which are bioceramic materials used in the Health area. The X-ray diffraction (XRD), the infrared spectroscopy (FTIR) and the scanning electron microscopy (SEM) techniques were used to perform chemical, physical, physicochemical, morphological and particle size analyzes. The production of the calcium phosphates involved several variants in the process of synthesis and obtaining the powder; among them there were different applications of ultrasound (application time and / or duration) and different drying methods. In general, the chemical, physical and physicochemical characteristics found were in agreement with the literature, indicating that the employed methods here reached the objective of obtaining the calcium phosphates. Regarding to this, it has become clear that alternative methods can be used as a mean of production, ensuring the efficience and the least costly production, consequently allowing a large-scale production, preserving the basic characteristics of each phase of calcium phosphate. / CAPES: 88882.180385/2018-01

Made available in DSpace on 2014-06-12T15:53:51Z (GMT). No. of bitstreams: 2 arquivo5170_1.pdf: 2978125 bytes, checksum: 5a4a114e14e6f5c51a7242ab56c46d7d (MD5) license.txt: 1748 bytes, checksum: 8a4605be74aa9ea9d79846c1fba20a33 (MD5) Previous issue date: 2005 / Biocerâmicas de fostato de cálcio são importantes na Odontologia e na Medicina, no tocante aos processos de cárie e cálculo dentais, de preenchimento de feridas ósseas e de recobrimento de implantes metálicos. Este trabalho visa aprimorar o estudo da formação dessas biocerâmicas em modelos in situ de cárie dental em humanos. Aqui relatamos a formação concomitante de cárie e cálculo (biocerâmica de fosfato de cálcio) dentais em modelo in situ de cárie em intervalos de 2-14 dias, mostrando o potencial de se trabalhar com intervalos relativamente curtos de tempo para formar o cálculo dental. Estudando a fluorescência do cálculo dental, revelamos que sua fluorescência em soluções aquosas (em função da concentração de hidrogênio) é similar à da hematoporfirina, e que a fluorescência do cálculo dental sólido se assemelha mais com a de soluções com alta contração de hidrogênio, nas quais hematoporfirina bivalente é o principal cromóforo. Para aprimorar a análise do efeito da formação das biocerâmicas no esmalte dental, um modelo matemático, que conseguiu, pela primeira vez, apresentar consistência entre dados quantitativos teóricos e experimentais da birrefringência do esmalte ao microscópio de luz polarizada, foi proposto. Este modelo tem ampla aplicação na biologia do esmalte por poder analisar os conteúdos mineral, orgânico e de água

Tese de mestrado. Engenharia Biomédica. Faculdade de Engenharia. Universidade do Porto, Instituto Superior de Engenharia do Porto. 2007