O presente trabalho destinou-se a desenvolver um dispositivo para crescer monocristais e a estudar a metodologia vinculada ao assunto. Usando alumínio eletrolítico com 99,8% de pureza, cadinhos de grafite com conicidades simples e dupla, velocidades de deslocamento de 2,44cm/h a 10,14 cm/h (quatro taxas), atmosfera de argônio, um forno com gradiente térmico de 67 ºC/cm e o Método Bridgman Vertical, foram crescidos mono e policristais de alumínio. A partir das amostras obtidas foram feitas análise metalográficas, de microscopia eletrônica e de raio X (método Laue de retrocesso) com a finalidade de avaliar problemas de nucleação e de crescimento de cristais, analisar a segregação de impurezas e examinar a regularidade nos cristais. / The present work is intended to develop an apparatus for growing single crystals and to study the methodology linked to the subject. Using eletrolitical aluminum with 99,8% purity, graphite crucibels with single and double conical ends, dislocation speed between 2,44 cm/h and 10,14 cm/h (in four steps), argon atmosphere, a furnace with a thermal gradient of 67 ºC/cm and the Vertical Bridgman Method, single and poly Al crystais have been grown. Arising from the samples obtained, metallographic tests, Scan Electron Microscopy (SEM) and X-rays (back-reflection Laue method) analysis were effected to evaluate problems on nucleation and growing of crystals, to analyse impurity segregation and to examine the regularity of the crystals.

Este trabalho tem por objetivo o estudo da aplicação de ligas ferromagnéticas obtidas por Metalurgia do Pó em um motor de indução. O núcleo desta máquina, usualmente constituído de chapas laminadas, foi substituído por blocos maciços. No estudo das ligas, empregou-se pó de ferro e ligas deste, obtidas por misturas com diferentes percentuais de fósforo (1, 2 e 3%), silício (1, 3 e 5%) e níquel (50%). Com as formulações pré-estabelecidas efetuou-se as mensurações mássicas, precedendo a mistura. Em seguida, fez-se a compactação de 3 corpos de prova por liga. Estes foram sinterizados em forno com temperaturas controladas. Para caracterizar o material, efetuaram-se ensaios de densidade a verde e sinterizado, traçadas curvas de histerese e magnetização e teste de resistividade. Observou-se que a liga Fe2%P apresentou resultados mais promissores, comparativamente as outras ligas, do ponto de vista para aplicações em máquinas elétricas, onde a indução de saturação ficou em 1,36 T, permeabilidade relativa de 4198 e a coercitividade em 207 A/m. No entanto, em comparação com aço elétrico laminado, a indução de 1,36 T ficou abaixo da média de 1,7 T, apresentada pelo aço elétrico acessita, do grupo Acelor. O fator de interesse são as perdas, uma vez que nas ligas estudadas, a inserção dos elementos de liga citados pode vir a compensar seu formato maciço. Partindo do princípio que a liga Fe2%P apresentou os melhores resultados, seguiu-se para a montagem do motor de indução com esta formulação. A máquina montada foi levada para testes, na empresa Voges Motores, de Caxias do Sul - RS. Os resultados apresentados demonstraram um conjugado abaixo do nominal para máquinas de mesma tipologia, ficando apenas 18% do resultado ideal. O fator de potência ficou acima do motor convencional, no entanto, o escorregamento ficou elevado, principalmente em altas rotações. De acordo com a curva de conjugado apresentada, concluiu-se que o motor apresenta a curva característica “D”, onde o conjugado máximo é alcançado a baixas rotações. / This work aims to study the application of ferromagnetic alloys obtained by Powder Metallurgy in an induction motor. The core of this machine, usually made of rolled sheets, was replaced by massive blocks. In the study of alloys, was used an iron powder and alloys thereof, obtained by mixtures with different percentages of phosphorus (1, 2 and 3%), silicon (1, 3 and 5%) and nickel (50%). With the pre-set formulations, mass measurements were conducted preceding with the mixture. Then 3 specimens per alloy were compacted. These were sintered in a kiln with controlled temperatures. To characterize the material, density tests were performed prior and post sintered curves of Hysteresis and curves of Magnetization were drawn and resistivity test was obtained. At this time, it was observed that the alloy Fe2% P showed the most promising results compared to other alloys, from the point of view of applications in electrical machines where the saturation induction was 1.36 T, the relative permeability was 4198 and coercivity was at 207 A / m. However, compared to laminated electrical steel, the induction of 1.36 T was below the average of 1.7 T, presented by steel plates acessita, Acelor group. The factor of interest are the losses, once at the alloys studied, the insertion of alloy elements may offset their solid form. With the alloy Fe2% P, that showed the best results, it followed with the mounting of the induction motor. The assembled machine was taken for testing at the company Voges Motores, Caxias do Sul - RS. The results presented demonstrated below nominal torque for the same type of machines, but only 18% from the ideal result. The power factor was higher than the conventional motor, however, the slip became high, especially at high speeds. According to the torque curve presented, it was concluded that the motor features the characteristic curve “D”, where maximum torque is achieved at low speeds.

Este projeto tem como objetivo o desenvolvimento de uma máquina síncrona com ímãs permanentes de até 7,5 kW, no qual o núcleo do rotor, usualmente construído de chapas de aço laminadas, foi substituído por um bloco maciço de uma liga ferromagnética obtida através da metalurgia do pó. Para a construção do rotor, foram estudados materiais magnéticos macios sinterizados, a partir de ligas com ferro, onde foram avaliadas propriedades magnéticas, elétricas e mecânicas, os quais influenciam diretamente no desempenho da máquina. A partir destas propriedades foi definida uma liga, considerando que o rotor construído resultaria em um melhor desempenho na máquina. Testes foram efetuados, possibilitando uma comparação com máquinas construídas da maneira convencional. / The aim of this project is to develop a synchronous machine with permanent magnets up to 7.5 kW, where the rotor core, usually built of laminated steel sheets, was replaced by a massive block of a ferromagnetic alloy obtained through Powder Metallurgy. Process soft magnetic materials using iron alloys were studied in order to build the rotor, and the magnetic, electrical and mechanical properties were analyzed, due to their direct influence on the performance of the machine. An alloy was selected according to these analyses considering a better performance of the machine using the rotor built from this alloy. Experiments were carried out to enable a comparison to machines built in traditional processes.

Os aços de alta resistência e baixa liga (ARBL) são aços destinados a diversas aplicações estruturais e apresentam resistência mínima especificada de 550 MPa. Estes aços apresentam baixo teor de carbono e contêm pequenas quantidades de elementos de liga para que possam alcançar a resistência especificada no processo de laminação controlada. Dentre os aços ARBL, destaca-se o S700MC, que pertence à classe dos microligados. É um aço de alta resistência, baixo carbono e baixa liga, sendo que a sua alta resistência deriva do refinamento de grão, transformação de fase e endurecimento por precipitação (precipitados de Ni, Ti e ou V). O processamento deste aço envolve laminação controlada sendo exigidos os seguintes requisitos no produto final: boa soldabilidade, bom comportamento em dobramento, boas propriedades de fadiga e boa tenacidade. Diferentes composições de aços S700MC têm sido desenvolvidas, pois dependendo da composição do aço, os parâmetros de laminação controlada (temperatura final de laminação, temperatura inicial de resfriamento, temperatura final de resfriamento, etc.), para se obter a microestrutura e propriedade mecânica desejada, podem ser diferentes. A microestrutura ferrítica-perlítica convencional dos aços ARBL tem sido substituída nesta classe de aços por microestruturas bainíticas. Muitas vezes a bainita formada é considerada “não-tradicional”, devido à uma mistura de produtos de tranformação, gerando uma certa discussão para a terminologia adequada. Aços com microestrutura bainítica são desejáveis devido ao seu favorável balanço de tenacidade e resistência mecânica mais elevada que nos aços ARBL convencionais. Deste modo, o objetivo deste estudo foi avaliar as microestruturas produzidas (preferencialmente bainíticas) em aços da classe S700MC, desenvolvidos com composições diferentes. Estas microestruturas devem conferir a combinação de propriedades desejada através do controle de parâmetros de tratamento térmico, caracterizando-se as transformações de fase envolvidas. Para alcançar este objetivo, foi aplicada a técnica de dilatometria. Esta técnica é eficaz no estudo das transformações de fase no estado sólido que ocorrem nos aços quando XVIII submetidos a tratamentos térmicos, mostrando a evolução dessas transformações através das mudanças dimensionais do material. Neste trabalho três tipos de aço da classe S700MC foram ensaiados em dilatômetro, aplicando-se dois ciclos térmicos diferentes, com o objetivo de se verificar: a influência da taxa de aquecimento nas temperaturas de transformação de fase, Ac1 e Ac3 (variando a taxa de aquecimento: 1, 10, 50 e 100°C/s) e as transformações de fase ocorridas durante o resfriamento (variando as taxas de resfriamento: 0,2, 1, 5, 10, 25, 50, 100 e 200°C/s). Após os ensaios no dilatômetro foi realizada uma caracterização microestrutural nos corpos-de-prova bem como medições de microdureza. Os materiais apresentaram evolução microestrutural semelhante, porém com formação de morfologias complexas. Os resultados mostraram que determinadas taxas de resfriamento aliadas a outros fatores, desenvolvem microestruturas mais favoráveis à obtenção de alta resistência mecânica. / High strength low alloy (HSLA) steels are intended for various structural applications and have specified minimum strength of 550 MPa. These steels have low carbon content and contain small amounts of alloying elements so that they can reach the strength specified in the process of controlled rolling. Among the HSLA steels, is the S700MC, which belongs to a class of microalloyed. It is a high strength steel and low alloy, where its high strength derives from the grain refinement, phase transformation and precipitation hardening (precipitation of Ni, and Ti or V). The processing of this steel involves controlled rolling, the following requirements being demanded in the final product: good weldability, good behavior in bending, good fatigue properties and good toughness. Different compositions of S700MC steels have been developed, because depending on steel composition, the parameters of controlled rolling (final temperature of rolling, initial temperature of cooling, end temperature of cooling, among others), to obtain the microstructure and mechanical property desired, may be different. The conventional ferritic-pearlitic microstructure of HSLA steels have been replaced in this class of steels for bainitic microstructures. Very often, the bainite formed is classified "non-traditional" due the misture of transformation products, developing a discussion about the correct terminology. Steels with bainitic microstructure, are desirable for their favorable balance of toughness and mechanical strength higher than conventional HSLA steels. Thus, the target of this study was to evaluate the microstructures produced (preferably bainitic) in steels of S700MC grade, developed with different compositions. These microstructures should confer the combination of desired mechanical properties, by controlling the parameters of heat treatment and including characterizing the phase transformations involved. To achieve this goal, we applied the technique of dilatometry. This technique is effective in the study of phase transformations in solid state which occur in steels when submitted to heat treatments, showing the evolution of these changes through the changing dimensions of the material. XX At this work, three kinds of S700MC grade were performed in the dilatometer applying two sets of thermal cycle to analyse: the influence of heating rate on the temperatures of phase transformation, Ac1 and Ac3 (changing the heating rate:, 1, 10, 50 and 100°C/s) and the phase transformations during cooling (changing the cooling rate: 0.2, 1, 5, 10, 25, 50, 100 and 200°C/s). After the tests in the dilatometer, was performed a metallographic characterization of each test piece and microhardness measurements. The materials presented similar microstructural, however with the formation of complex morphologies. The results showed that certain cooling rates combined with other factors develop microstructures more favorable to obtain high mechanical strength.

Estudou-se a atuação do metavanadato de sódio como inibidor da corrosão do aço ABNT 1006 em soluções aquosas neutras, arejadas e desarejadas, na presença e na ausência de íons cloreto, à temperatura ambiente. Utilizou-se como parâmetros de avaliação ensaios de imersão em circuito aberto, curvas de polarização potenciostística, curvas cronogalvanométricas e curvas de variação do potencial de corrosão com o tempo. Observou-se que o vanadato pode inibir a corrosao do aço em concentrações tão baixas quanto 20 ppm, porém sua ação é extremamente dependente de frestas e bordas do corpo de prova. O efeito inibidor estã relacionado ao oxigênio dissolvido, em presença do qual o vanadato desloca o potencial de coE rosão do aço para dentro da zona passiva. O íon cloreto pode provocar o rompimento localizado do filme passivo; quando is to ocorre, o potencial de pite torna-se mais anódico com o aumento na concentração de inibidor. / Sodium metavanadate was evaluated as a corrosion inhibi tor to ABNT 1006 steel in neutral aqueous solutions, at room temperature. Weight loss measurements, polarization curves, current- time transients and potential/time curves were made on specimens exposed to both aerated and deaerated containing vana date solutions. A concentration as low as 20 ppm sodium metavanadate can inhibit corrosion, but inhibition is extremely dependent on crevices and holes or borders of specimen. In order to be ef fective as inhibitor, vanadate requires the presence of oxigen in the solution to prevent corrosion. A potential in the passive region is observed when inhibition is achieved. Chlo ride ion causes pitting of steel in vanadate solutions; pitting potential increases as the inhibitor concentration isin creased.

No presente trabalho verificou-se a viabilidhde do uso de ensaios eletroquímicos para avaliar revestimentos de Óleos na proteção do aço ABNT 1010 contra a corrosão. Curvas de polarização potenciostáticas, curvas de potencial versus tempo e ensaios de câmara de umidade, de nevoa salina e so2 foram feitas com aço revestido com diferentes óleos. Constatou-se que curvas de polarização podem 9er empregadas como uma técnica auxiliar aos ensaios de camaras, e que algumas divergências entre os resultados estão ligadas as diferentes condições de ensaio e sua influência sobre estes revestimentos. Por estes testes notou-se que a presença do revestimento tornou o potencial de corrosao mais nobre e, em alguns casos, houve sensível redução da densidade de corrente crítica de passivação. Estes fatos também foram verificados com a adição de lanolina ao Óleo. A polarização e a natureza da solução eletrolítica exercem uma forte influência no comportamento do revestimento. O efeito inibição, proporcionado pelos óleos, foi mais significativo que a barreira em todos os ensaios. / The present work verified the viabi1ity of the use of e1ectrochemica1 tests to eva1uate oi1 coating in the protection of ABNT 1010 stee1 against corrosion. Potenciostatic po1arization curves, potential versus time curves, and humidity, salt spray and su1fur dioxide chamber tests were made with stee1 coated with differents oils. It was verified that polarization curves can be used as an auxi1iary technique to chamber tests, and that some divergences among the results are connected to differences, in test conditions and to their influence on oil coatings. In the polarization curves it was observed that the presence of the coating shifted the corrosion potential of the steel in the noble direction. In some cases, there was a great reduction in the passivation critical current density. These facts were also verified with the addition of 1anolin to the oil. The polarization have a strong influence on the coating behaviour. The inhibition effect enab1ed by oils was more important than the barrier effectinall tests.

Foi estudada a cinética de formação de filme passivo sobre o ferro anodizado em solução de borato de sodio deçahidratado 0,1 mol/L, em meio desarejado e na temperatura ambiente, utilizando diferentes métodos eletroquímicos. Os voltamogramas çicliços obtidos apresentaram trés picos de corrente anódica que, de acordo com o balanço de massa e carga envolvidas, estariam relacionados com a formação de filmes de Fe(OH)2 e FeOOH que, por desidratação, formaria Fe2O3, levando a passivação. A ausência de picos catódicos mostrou que esse filme se reduz em potenciais tão negativos quanto o da reaçáo de formação de H2. O uso do eletrodo rotatória de disco e anel comprovou que na região de potencial do pico anódico II ocorre uma pequena passagem de íons Fe²+ para o eletrólito, com a corrente de dissolução dependendo da velocidade de varredura do potencial do disco, mas não excedendo 2% da corrente anódica total. Foi feita também uma investigação da influência de cloreto e da variaçáo do pH do meio sobre o perfil voltamétrico. A aplicação do Modelo ohmico para crescimento de filmes passivos pareceu adequada. A formação galvanostática do filme apresentou a existência de três patamares de potencial, com valores próximos aos dos picos anodicos de formação de Fe(OH)2, FeOOH e da reação de formação de O em baixas velocidades de varredura. O estudo da zona passiva de potenciais através da técnica de espectroscopia de irnpedância eletroquimica e da utiilizaçáo da equação de Mott-Schottky mostrou que o filme passivante se comporta como um semicondutor degenerado, devido i alta densidade de doadores. Foi proposto um circuito equivalente ao sistema metallfilrnelsoluç~o,c om boa concordância entre os resultados experimentais e os obtidos por simulação. A medida do potencial de corrosão e a comparação do comportamento eletroquimico do ferro em borato e em solução de outros ânions propiciou uma investigação do caráter inibidor de corrosão daquela espécie. Este estudo foi feito em uma solução de perclorato de sódio 0,l mollL com adição de diferentes quantidades de borato. A utilização das técnicas de eletrodo rotatório de disco e anel, formação e redução galvanostatica de filme e espectroscopia de impedância eletroqu imica possibilitou a determinaçáo de uma ordem de rea@o negativa para a formaeo do filme passivo, em relação ao borato, e a comprovação de seu carater inibidor / The kinetics of passive film formation on iron anodized in 0.1 mol/L sodium borate solution has been studied, in deaerated environment at 25°C, using different electrochemical methods. Cyclic voltammograrns showed three anodic current peaks that, according to mass and charge balance, can be related to Fe(OH)2 and FeOOH film forrnation, which forms Fe203 by dehydratation and leads to passivation. The absence of a cathodic peak showed that the forrned film reduces itself at potentials as negative as those of H2 evolution. The use of rotatory ring and disk electrode has proved that metallic dissolution taks place as Fe²+ ions in the second anodic peak potential range, depending on potential scan raie but in percentages lower than 2% of the total anodic current. The influente of chloride concentraiion and pH on the voltammetric profile has been investigated. The appltcation of the Ohmic Model for passive film growth seemed to be appropriate. The galvanostatiç fiilm formation showed three potential arrests, with values close to that of the anodic peak potentials of Fe(OH)2 and FeOOH formation and O2 evolution in slow potential scan. The study of the passive potential range using electrochemical impedance spectroscopy and Mott-Schottky equation showed that the film behaves as a degenerated semiconductor due to a high density of donors. An equivalent circuit has been proposed for the metallfilmlsolution system with a good agreemeni between the experimental and simulated results. Comparison of iron electrochemical behaviour in borate or in solutions of oiher anions guided to an investigaiion of borate corrosion inhibitive characteristics. This study has been made in 0.1 mol/L sodium perchlorate solution with addition of borate in different concentrations. A negative reaction order with respect to borate for passive film formation has been determined. A galvanostatic technique and electrochernical impedance spectroscopy also confirmed the inhibitive character of borate.

Dissertação (mestrado)—Universidade de Brasília, Faculdade de Tecnologia, Departamento de Engenharia Mecânica, 2012. / Submitted by Alaíde Gonçalves dos Santos (alaide@unb.br) on 2012-09-26T14:00:03Z No. of bitstreams: 1 2012_DiegoAndresCampoCeballos.pdf: 4401374 bytes, checksum: c4b924aaefd628ddfb8238fea176fef6 (MD5) / Approved for entry into archive by Guimaraes Jacqueline(jacqueline.guimaraes@bce.unb.br) on 2012-10-11T14:55:28Z (GMT) No. of bitstreams: 1 2012_DiegoAndresCampoCeballos.pdf: 4401374 bytes, checksum: c4b924aaefd628ddfb8238fea176fef6 (MD5) / Made available in DSpace on 2012-10-11T14:55:28Z (GMT). No. of bitstreams: 1 2012_DiegoAndresCampoCeballos.pdf: 4401374 bytes, checksum: c4b924aaefd628ddfb8238fea176fef6 (MD5) / Pesquisadores alemães desenvolveram o polipropüeno copolímero random PP. na busca de um sistema de condução de água capaz de suportar altas pressões e altas temperaturas. Este material liberou a produção de tubos e conexões resistentes à água quente, mas. por ser um material polimérico. a rigidez destas tubulações decresce com o aumento da temperatura. Este trabalho apresenta a pesquisa do comportamento mecânico ã flexão de vigas compósitas híbridas constituídas de um tubo cilíndrico de polipropüeno (PP) e uma barra circular sólida de liga de Ní-Ti. incorporada na superfície externa do tubo. fixada com uma camada bobinada de nylon impregnada com resina epóxi. Os tubos de PP podem operar em temperaturas de até 80°C. aquecendo as ligas Ní-Tí até temperaturas acima de Aí. permitindo observar a contribuição do fio no aumento da rigidez das vigas compósitas fabricadas. Inicialmente, foi caracterizada a liga de Ni-Ti apresentando temperaturas de transformação de fase de M5= 46.24°C. Mf = 31,72 °C, As= 37.67°C e Af = 60.17°C, obtidas do ensaio de calorimetria diferencial de varredura (DSC), composição química média de 50.05% em peso de Ni a partir da espectroscopia de energia dispersiva (EDS) e presença da fase monoclinica à temperatura ambiente, identificada pela difração de raios X (DRX). Posteriormente, tubos de PP de 500 mm de comprimento foram usados para fabricar vigas compósitas híbridas incorporando fios de aço e camada nylon epóxi para aperfeiçoar o método de fabricação e testar o dispositivo de flexão em três pontos. Finalmente, vigas compósitas com fio de Ní-Ti e camada de nylon/epóxi. foram fabricadas e logo testadas em flexão de três pontos. Os resultados demonstraram que houve um aumento no valor do módulo efetivo em flexão das vigas ExF de 13% a 32% quando o fio de Ní-Ti. alinhado no plano vertical de aplicação da carga do ensaio de flexão. aumentou sua rigidez pela transformação de fase martensita para austenita induzida pela mudança da temperatura de 21°C a 56°C. _______________________________________________________________________________________ ABSTRACT / German researchers have been developed a polypropylene random copolymer PP.in the search for a water transportation system capable of withstand high pressures and temperatures. This material allowed the production of pipes and connections resistant to hot water, however, stiffness decreases with increasing temperature for the polymeric properties. This work presents the mechanical behavior investigation of hybrid composites beams based Ni-Ti alloy. The beams consist of a medium density polypropylene pipe (PP) with a bar of Ni-Ti alloy incorporated in the surface and manual winding with a coated layer of nylon epoxy. PP pipes can work over SO °C heating Ni-Ti alloy to above Af temperature, which would show Ni-Ti contribution to increasing the stiffness of the hybrid composite beams. First. Ni-Ti alloy was characterized with differential scanning calorirnetry (DSC), found the transformation temperatures at Ms = 46.24 °C. Mf = 31.72 °C, A, = 37,67 °C and Af = 60.17 °C. Energy dispersive spectroscopy (EDS) results indicated chemical composition of NiTi alloy of 50.05 wt% of Ni. X-ray diffraction (XRD) showed the monoclinic phase at room temperature. Subsequently. PP pipes of 500 mm in length were used to produce hybrid composite beams incorporating a steel bar coated with nyloa epoxy layer in order to improve the manual winding method and test the three point bending device. Finally, hybrid composite beams with Ni-Ti bar and nylon epoxy layer were fabricated and then tested in three point bending. Results showed an increase on flexural elastic modulus of the beams ExF of 18% to 32% because stiffness increase of Ni- Ti alloy, aligned in the vertical plane of load application in bending test, due thermal transformation from martensite to austenite phase induced by changes of temperature from 21°Cto56°C. _______________________________________________________________________________________ RESÚMEN / Investigadores alemanes desarrollaron el polipropileno copoliniero ramdom PP en la búsqueda de un sistema de conducción de agua capaz de soportar altas temperafuras e presiones. Este material posibilitó la producción de tubos e conexiones resistentes al agua caliente, sin embargo, por ser un material polimérico, su rigidez decrece con el aumento de Ia temperatura. Este trabajo presenta Ia investigacióu del comportamiento mecânico en flexión de vigas cornpósitas hibridas constituídas de un tubo cilíndrico de polipropileno y una barra circular sólida de Ni-Tí incorporada en Ia superfície externa del tubo. y fíjada con una capa de revestimiento de nylon/epoxi. Los tubos de PP pueden trabajar en temperaturas superiores a 80 °C. logrando llevar al material de NiTi a temperaturas mayores que Af, Io que permitiria observar su contribución al aumento de Ia rigidez de Ias vigas compósitas fabricadas. Inicialmente, Ia liga de Ni-Ti fue caracterizada presentando temperaturas de transformation de fase de Ms= 46,24°C Mf= 31,72 °C As= 37,67°C e Af = 60,17°C, obtenidas de Ia calorimetria diferencial de barrido (DSC), composición química media de 50,05% en peso de Ni a partir de Ia espectroscopia de energia dispersiva (EDS) y presencia de fase monoclínica a temperatura ambiente, identificada mediante difracción de rayos X (DRX). Posteriormente, fueron usados tubos de PP de 500 mm de largo, para fabricar vigas compósitas hibridas con barras de acero e capa de revestimiento de nylo/epoxi en Ia superfície, con el fin de perfeccionar el método de fabricación y probar el dispositivo de flexión eu tres puntos. Finalmente, fueron fabricadas Ias vigas compósitas híbridas con barras de Ni-Ti e capa de revestimiento de nylon/epoxi para los ensayos de flexión en três puntos. Los resultados demostraron que hubo un aumento en el valor del módulo efectivo en flexión de Ias vigas compósitas ExF de 18% a 32% cuando la barra de Ni-Ti, alineada en el plano vertical de aplicación de Ia carga en el ensayo de flexión. aumenta su rigidez debido a la transformacion de fase de martensita a austenita inducida por el cambio de temperatura de 21°C a 56°C

Dissertação (mestrado)—Universidade de Brasília, Programa Multiinstitucional e Inter-regional de Pós-Graduação em Ciências Contábeis, 2006. / Submitted by Fernanda Weschenfelder (nandaweschenfelder@gmail.com) on 2009-11-27T15:09:05Z No. of bitstreams: 1 2006_ClesiaCamiloPereira.pdf: 524321 bytes, checksum: 50cc055f47bfbe3127b5ad499c5f5f1f (MD5) / Approved for entry into archive by Daniel Ribeiro(daniel@bce.unb.br) on 2009-12-03T21:04:50Z (GMT) No. of bitstreams: 1 2006_ClesiaCamiloPereira.pdf: 524321 bytes, checksum: 50cc055f47bfbe3127b5ad499c5f5f1f (MD5) / Made available in DSpace on 2009-12-03T21:04:50Z (GMT). No. of bitstreams: 1 2006_ClesiaCamiloPereira.pdf: 524321 bytes, checksum: 50cc055f47bfbe3127b5ad499c5f5f1f (MD5) Previous issue date: 2006-10-24 / Este estudo examina a influência das notícias publicamente divulgadas na imprensa sobre as empresas no período compreendido entre a data de encerramento do trimestre e a divulgação do seu lucro trimestral no efeito surpresa que a divulgação do lucro provoca no mercado. A premissa considerada é a de que o efeito da divulgação do lucro nos retornos das ações das empresas da amostra é inversamente relacionado à quantidade de notícias publicadas, conjuntas ou individualizadas por categorias, ao longo do trimestre que antecede a divulgação do lucro. Os testes empíricos realizados com a utilização do método de dados em painel apresentam evidências empíricas de que, o mercado não reagiu, na média, aos lucros quando divulgados, pois tal reação, significativamente positiva, já ocorrera no momento em que as notícias sobre as empresas foram publicadas na imprensa antes da data da divulgação do lucro. Esse resultado é contrário ao documentado na pesquisa de Christensen, Smith e Stuerke (2004), nos Estados Unidos e apresenta indícios de que o mercado brasileiro apresenta eficiência na sua forma semi-forte. Já na análise das categorias individuais de notícias publicamente disponíveis, os resultados não se mostram consistentes com a análise conjunta apresentando reação negativa e significante para as categorias ANALISTA, LUCRO e DIVJSCP. Esses resultados indicam que, quando analisadas conjuntamente, as notícias positivas por categorias, GERENCIA, OPERACIONAL e OUTRAS, compensam com folga as notícias negativas que são percebidas nas categorias ANALISTA, LUCRO e DIVJSCP. Mas, novamente foram verificadas evidências empíricas de que o mercado não reagiu, na média, aos lucros quando divulgados, o que demonstra que esse efeito já foi capturado antes, quando da publicação das notícias, confirmando a teoria e a segunda hipótese deste estudo. Com o intuito de aferir a robustez dos resultados empíricos encontrados, foi introduzida uma proxy de notícias publicamente disponíveis, também utilizada na pesquisa de Christensen, Smith e Stuerke (2004), o tamanho da empresa, VALORMERC. Os testes de raízes unitárias nas séries e de autocorrelação nos resíduos reforçam a consistência dos resultados apurados. _______________________________________________________________________________ ABSTRACT / This study examines the influence of the public disclosure information on market in the press on the companies in the period understood between the date of closing of the trimester and the spreading of its quarterly profit in the element of surprise that the spreading of the profit provokes in the market. The considered premise is of that the effect of the spreading of the profit in the returns of the actions of the companies of the sample inversely is related to the amount of published notice, the joint ones or for types, to the long one of the trimester that precedes the spreading of the profit. The carried through empirical tests with the use of the method of data in panel present empirical evidences of that, the market did not react, in the average, to the profits when divulged, therefore such reaction, significantly positive, already it occurs at the moment where the notice on the companies had been published in the press before the date of the spreading of the profit. This result is contrary to the registered one in the research of Christensen, Smith and Stuerke (2004), in the United States and presents indications of that the Brazilian market presents efficiency in its semistrong form. Already in the analysis of the individual categories of public available notice, the results do not reveal consistent with the joint analysis presenting negative and significant reaction for the categories ANALYST, EARN and STOCKDIV. These results indicate that, when analyzed jointly, the positive notice by categories, MANAGER, OPERATE and OTHERVAL, compensate with recess the negative notice that. But, empirical evidences of that the market did not react, in the average had been again verified, to the profits when divulged, what it demonstrates that this effect already was captured before, when of the publication of the notice, confirming the theory and the second hypothesis of this study. With intention to survey the robustness of the found empirical results, proxy of public available notice was introduced one, also used in the research of Christensen, Smith and Stuerke (2004), the size of the company, MARKTVAL. The unit root tests on the series as well as autocorrelation ensure the robustness of the results obtained.

Tese (doutorado)-Universidade de Brasília, Faculdade de Tecnologia, Departamento de Engenharia Mecânica, 2013. / Submitted by Albânia Cézar de Melo (albania@bce.unb.br) on 2013-11-19T12:56:33Z No. of bitstreams: 1 2013_VagnerJoaoGobbi.pdf: 96126826 bytes, checksum: dc2ee55d3661eaba1d0ae1bf74964a19 (MD5) / Approved for entry into archive by Patrícia Nunes da Silva(patricia@bce.unb.br) on 2014-01-28T11:28:15Z (GMT) No. of bitstreams: 1 2013_VagnerJoaoGobbi.pdf: 96126826 bytes, checksum: dc2ee55d3661eaba1d0ae1bf74964a19 (MD5) / Made available in DSpace on 2014-01-28T11:28:15Z (GMT). No. of bitstreams: 1 2013_VagnerJoaoGobbi.pdf: 96126826 bytes, checksum: dc2ee55d3661eaba1d0ae1bf74964a19 (MD5) / Materiais com comportamento adequado em temperaturas elevadas tornaram-se uma necessidade nos dias atuais. Superligas são conhecidas desde a década de 1930 e utilizadas, principalmente, em aplicações aeroespaciais e automobilísticas. Com as novas regulamentações para redução das emissões atmosféricas e aumento da eficiência, surgiram projetos que submetem certos componentes de motores como válvulas, a temperaturas e pressões mais elevadas. Assim, exige-se que as ligas utilizadas na fabricação desses componentes possuam maior resistência à alta temperatura, a exemplo da NIMONIC 80A. Esta é uma liga de custo elevado devido à alta quantidade de níquel (70 a 80% em peso) além de possuir tratamento térmico extenso. Uma alternativa é a utilização de ligas com menor teor de níquel (30 a 40% em peso) e tratamento térmico reduzido. Neste contexto a Villares Metals desenvolveu duas novas superligas, as VATS 32 e 36. Essas ligas são concebidas para válvulas de motores de combustão interna, porém podem ser utilizadas nos casos que necessitem de resistência mecânica a quente, resistência à fluência, corrosão a quente, especialmente por gases sulfurosos, e resistência a fadiga substituindo às ligas NIMONIC 80A em diversas aplicações. A Empresa Villares Metals fez algumas caracterizações à quente das ligas VAT 32 e VAT 36 porém, não foram realizados ensaios por fluência medindo a deformação com o tempo. Portanto, este trabalho tem como objetivo fazer um estudo do comportamento em fluência, em termos de taxa de deformação secundária e tempo de fratura, das superligas VAT 36, VAT 32 e NIMONIC 80A. As ligas são submetidas a ensaios de fluência na modalidade de carga constante, na faixa de temperatura de 675 a 750 ºC e na faixa de tensão de 500 a 600 MPa definidas de acordo com suas aplicações. Os ensaios de fluência são realizados conforme a norma ASTM E139. Obtem-se um conjunto de curvas de deformação verdadeira pelo tempo como função das tensões e temperaturas aplicadas. Foi avaliado a ductilidade, a taxa de fluência estacionária e o tempo de vida. Complementou-se o trabalho com caracterização microestrutural das superligas através das técnicas de microscopia ótica, microscopia eletrônica de varredura, microscopia eletrônica de transmissão, difração de raios X, refinamento de Rietveld e ensaios de dureza. Os resultados mostram que a liga VAT 32 apresenta maior resistência à fluência (menor taxa de deformação secundária e maior tempo de fratura) em relação à VAT 36 e NIMONIC 80A. Isto se deve além do efeito benéfico dos compostos intermetálicos γ' (Ni 3(Al,Ti)), ao maior tamanho de grão e a maior fração de carbonetos ligados MC encontrado na VAT 32. Estes precipitados ricos em titânio e nióbio são estáveis a temperaturas elevadas, aumentam a resistência ao movimento de discordâncias e retardam processos difusionais associados à deformação por fluência. Ancoram os contornos de grãos dificultando o deslizamento relativo entre eles afetando a facilidade com que as vacâncias possam ser geradas nestas mesmas regiões. Por meio da análise dos expoentes de tensão, energias de ativação e imagens obtidas por microscopia eletrônica de transmissão após fluência o mecanismo de deformação dominante no estado secundário de fluência das ligas VAT 32, VAT 36 e NIMONIC 80A é movimento de discordâncias envolvendo provavelmente processo de Orowan loops e cisalhamento de precipitados pelas discordâncias, além da presença de deformação por twinning para as ligas VATS e escorregamento e escalagem de discordâncias para a NIMONIC 80A. ______________________________________________________________________________ ABSTRACT / Materials with appropriate behavior at elevated temperatures have become a necessity nowadays. Superalloys have been known since the 1930 and used primarily in automotive and aerospace applications. With the new regulations to reduce air emissions and increased efficiency projects emerged that submit certain engine components such as valves, temperatures and higher pressures. Thus, it is required that the alloys which are used in manufacturing these components have high temperature resistance, such as the NIMONIC 80A. This alloy has high cost due to the high amount of nickel (70 to 80% wt) and extensive heat treatment. An alternative is to use alloys with lower nickel content (30 to 40% wt) and reduced heat treatment. In this context, Villares Metals has developed two new superalloys, the VATS 32 and 36. These alloys are designed for valves internal combustion engines, but can be used in cases requiring mechanical strength hot, strength creep and corrosion, substitute alloy NIMONIC 80A in various applications. Villares Metals Company made some characterizations of the hot alloy VAT 32 and VAT 36 however, no tests were performed measuring creep deformation with time. The objective of this paper is to make a study of the behavior in creep in terms of secondary strain rate and rupture time of the superalloys VAT 36, VAT 32 and NIMONIC 80A. The alloys are subjected for creep tests in constant load mode, of the temperature range 675-750°C and stress range 500-600 MPa defined according to their applications. The creep tests are performed according to ASTM E139. Is obtained a set of curves of deformation real by the time in function of the applied stress and temperatures. Are evaluated ductility, the stationary creep rate and life time. Work is complemented with icrostructural characterization of superalloys through the techniques of optical microscopy, SEM, TEM, X-ray diffraction, Rietveld refinement and hardness tests. The results show that the alloy VAT 32 has a higher creep resistance (lower strain rate secondary and higher fracture time) from the VAT 36 and NIMONIC 80A. This is due to the beneficial effect of the intermetallic compounds γ' (Ni3 (Al, Ti)), the largest grain size and the largest fraction of MC carbides found in the VAT 32. These precipitates rich in titanium and niobium are stable at elevated temperatures, increased resistance to movement of dislocations and retard diffusional processes associated with creep deformation. Anchor the grain boundaries impairing the relative sliding between them affect the ease with which the vacancies may be generated in these same regions. Through analyzing the stress exponents, activation energies and images obtained by transmission electron microscopy after the creep deformation mechanism dominant in state secondary creep alloys VAT 32, VAT 36 and NIMONIC 80A is movement of dislocations probably involving process Orowan loops and shearing of precipitates by dislocations and the presence of deformation twinning for alloys VATS and slip of dislocations and climb for NIMONIC 80A.