Submitted by Pedro Barros (pedro.silvabarros@ufpe.br) on 2018-08-28T19:51:50Z No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) DISSERTAÇÃO Ana Karoline Barros Silva.pdf: 1162134 bytes, checksum: 24d3e22518e0022b7f4bec74f3af803f (MD5) / Approved for entry into archive by Alice Araujo (alice.caraujo@ufpe.br) on 2018-09-05T23:12:51Z (GMT) No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) DISSERTAÇÃO Ana Karoline Barros Silva.pdf: 1162134 bytes, checksum: 24d3e22518e0022b7f4bec74f3af803f (MD5) / Made available in DSpace on 2018-09-05T23:12:51Z (GMT). No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) DISSERTAÇÃO Ana Karoline Barros Silva.pdf: 1162134 bytes, checksum: 24d3e22518e0022b7f4bec74f3af803f (MD5) Previous issue date: 2015-02-25 / CNPq / Análises de microdesgaste dentário e isótopos estáveis de δ¹³C e δ¹⁸O em ossos e dentes, são ferramentas através das quais pode-se fazer inferências paleoecológicas e paleoambientais. Estudos do microdesgaste dentário foram amplamente utilizadas em primatas, mas apenas recentemente vêm sendo utilizados para inferir dietas em xenartros. As marcas ocasionadas pela abrasão das partículas durante a mastigação e a assinatura isotópica de um animal são correlacionadas com as principais categorias tróficas observadas na natureza. Este trabalho teve por objetivo inferir a dieta de Eremotherium laurillardi através de estudo biomecânico e geoquímico. O material estudado pertence à Coleção de Macrofósseis do Laboratório de Paleontologia do Departamento de Geologia da UFPE, composto de 71 molariformes, em diferentes estágios ontogenéticos, de nove localidades dos Estados de Pernambuco, Alagoas e Bahia. Utilizou-se estéreomicroscopia de baixa ampliação para a identificação e qualificação das sete principais variáveis de microdesgaste em ortodentina. Análise descriminante e de variância indicam a predominância de microdesgaste misto de orientação variável. A assinatura isotópica de δ¹³C em bioapatita variaram entre -1,81‰ e -8,59‰ nos indivíduos adultos e -4,23‰ e -7,10‰ nos juvenis, indicando uma dieta mista de plantas C3 e C4. As taxas de δ¹⁸O variam ao longo da latitude, ficando entre 24, 81‰ e 46,18‰, demostrando uma diagênese muito intensa atuando sobre os depósitos e grande modificação da matéria orgânica. Os resultados obtidos corroboram com o relatado na literatura, descrevendo E. laurillardi como megaherbívoro generalizado, sendo capaz de tolerar uma ampla gama de dietas e hábitats. / Dental microwear and stable isotopes δ¹³C and δ¹⁸O analysis in bones and teeth, are tools through which one can make paleoecological and paleoenvironmental inferences. Studies in dental microwear have been widely used in primates, but only recently they have been made to infer xenarthran diets. The marks caused by abrasion of the particles during chewing and the isotopic signature of an animal are correlated with the major trophic categories observed in nature. This study aimed to infer the Eremotherium laurillardi diet through biomechanical and geochemical study. The material studied belongs to the macrofossils collection from the Paleontology Laboratory of the Department of Geology of the UFPE, and is composed of 71 molariforms in different ontogenetic stages, from nine localities in the states of Pernambuco, Alagoas and Bahia. We used a low magnification stereomicroscopy for the identification and characterization of seven major variables microwear in the orthodentine. The discriminant and variance analysis indicate the predominance of mixed microwear variable orientation. The isotopic signature of δ¹³C in bioapatita ranged from -1, 81‰ and -8,59‰ in adults and - 4.23‰ and -7.10‰ in juveniles, indicating a mixed diet of C3 and C4 plants. The rates of δ¹⁸O vary along the latitude, being between 24,81‰ and 46,18‰, showing very intense diagenesis acting on deposits and major change of organic matter. The results corroborate those reported in the literature, describing Eremotherium laurillardi as mega herbivore generalized, being able to tolerate a wide range of diets and habitats.

No description available.

Visando-se determinar as temperaturas mais adequadas de nitretação e carbonitretação por plasma dos aços inoxidáveis austenítico AISI 316L, ferrítico AISI 409 e super duplex ASTM A890 Gr 5A e suas influências nas resistências ao desgaste e à corrosão, amostras desses aços foram tratadas a 400, 450 e 500°C, e submetidas a ensaios micrográficos, de raios X, ensaios microabrasivos e de corrosão. Todas as temperaturas de tratamentos utilizadas nos vários aços estudados produziram camadas com grande regularidade, que tiveram suas espessuras e durezas aumentadas com o aumento da temperatura de tratamento. Em todos os casos, ocorreu um grande aumento nas resistências ao desgaste microabrasivo das amostras nitretadas ou carbonitretadas, em comparação com o substrato, comprovando a efetividade da fase \"S\", produzida nas temperaturas mais baixas, no aumento das durezas e resistências ao desgaste. No caso das amostras tratadas em temperaturas mais elevadas, o nitreto de cromo foi o responsável principal pelo aumento dessa resistência. Verificou-se por meio dos resultados das curvas de polarização anódicas das camadas nitretadas e carbonitretadas a 400°C que, para os três tipos de aços em estudo, tais camadas apresentaram comportamentos semelhantes e superiores aos dos substratos, devido a formação de austenita ou ferrita expandidas. No caso das temperaturas de tratamentos de 450 e 500°C, as amostras carbonitretadas apresentaram desempenho superior ao das nitretadas e, próximos aos dos substratos, não tendo ocorrido degradação dessa propriedade. Os tratamentos de nitretação e carbonitretação por plasma, realizados nas temperaturas adequadas definidas no presente trabalho para os principais tipos de aços inoxidáveis, produziram camadas com elevadas durezas e resistências ao desgaste, sem perdas nas características de corrosão, que inclusive melhoraram em alguns casos, permitem a ampliação do uso dos aços inoxidáveis para situações que requeiram aquelas propriedades. / Aiming to determine the most appropriate temperatures of plasma and carbonitriding of the AISI 316L austenitic stainless steel, AISI 409 stainless steel and ASTM A890 Gr5A super duplex steel and their influence corrosion and wear resistances of those steel samples, they were treated 450 and 500°C, and submitted to micrography analyses, X-ray diffraction, abrasive wear and corrosion tests. All treatment temperatures used in the several studied steels produced layers with great regularity, which increased their thickness and hardness with the increase of the treatment temperature. In all the cases, a great increase occurred in the micro-abrasivive resistance of the nitrided and carbonitrided samples, in comparison with the substrate, proving the effectiveness of the \"S\" phase, produced in the temperatures, in the increase of the hardness and wear resistances. In the the samples treated at higher temperatures, the chromium nitride was the responsible one for the increase in the wear resistance. It was verified through the results of the potenciodinâmicos corrosion the nitrided and carbonitrided layers at 400°C, that for the three types of stee study, such layers presented similar and superior behaviors to that of the substrate, due to austenite or expanded ferrite formation. In the case of the treatment temperatures of 450 and 500°C, the carbonitrided samples presented s performance to the nitrided one and similar performance to the substrates s without the occurrence of any degradation of that property. The plasma nitriding and plasma carbonitriding treatments, carried out in the temperatures defined in the present work, for the principal types of stainless to produce layers with high hardness and wear resistances, without losses corrosion characteristics, which even got better in some cases, allow to expand the use of the stainless steels in situations where those properties are required.

Visando-se determinar as temperaturas mais adequadas de nitretação e carbonitretação por plasma dos aços inoxidáveis austenítico AISI 316L, ferrítico AISI 409 e super duplex ASTM A890 Gr 5A e suas influências nas resistências ao desgaste e à corrosão, amostras desses aços foram tratadas a 400, 450 e 500°C, e submetidas a ensaios micrográficos, de raios X, ensaios microabrasivos e de corrosão. Todas as temperaturas de tratamentos utilizadas nos vários aços estudados produziram camadas com grande regularidade, que tiveram suas espessuras e durezas aumentadas com o aumento da temperatura de tratamento. Em todos os casos, ocorreu um grande aumento nas resistências ao desgaste microabrasivo das amostras nitretadas ou carbonitretadas, em comparação com o substrato, comprovando a efetividade da fase \"S\", produzida nas temperaturas mais baixas, no aumento das durezas e resistências ao desgaste. No caso das amostras tratadas em temperaturas mais elevadas, o nitreto de cromo foi o responsável principal pelo aumento dessa resistência. Verificou-se por meio dos resultados das curvas de polarização anódicas das camadas nitretadas e carbonitretadas a 400°C que, para os três tipos de aços em estudo, tais camadas apresentaram comportamentos semelhantes e superiores aos dos substratos, devido a formação de austenita ou ferrita expandidas. No caso das temperaturas de tratamentos de 450 e 500°C, as amostras carbonitretadas apresentaram desempenho superior ao das nitretadas e, próximos aos dos substratos, não tendo ocorrido degradação dessa propriedade. Os tratamentos de nitretação e carbonitretação por plasma, realizados nas temperaturas adequadas definidas no presente trabalho para os principais tipos de aços inoxidáveis, produziram camadas com elevadas durezas e resistências ao desgaste, sem perdas nas características de corrosão, que inclusive melhoraram em alguns casos, permitem a ampliação do uso dos aços inoxidáveis para situações que requeiram aquelas propriedades. / Aiming to determine the most appropriate temperatures of plasma and carbonitriding of the AISI 316L austenitic stainless steel, AISI 409 stainless steel and ASTM A890 Gr5A super duplex steel and their influence corrosion and wear resistances of those steel samples, they were treated 450 and 500°C, and submitted to micrography analyses, X-ray diffraction, abrasive wear and corrosion tests. All treatment temperatures used in the several studied steels produced layers with great regularity, which increased their thickness and hardness with the increase of the treatment temperature. In all the cases, a great increase occurred in the micro-abrasivive resistance of the nitrided and carbonitrided samples, in comparison with the substrate, proving the effectiveness of the \"S\" phase, produced in the temperatures, in the increase of the hardness and wear resistances. In the the samples treated at higher temperatures, the chromium nitride was the responsible one for the increase in the wear resistance. It was verified through the results of the potenciodinâmicos corrosion the nitrided and carbonitrided layers at 400°C, that for the three types of stee study, such layers presented similar and superior behaviors to that of the substrate, due to austenite or expanded ferrite formation. In the case of the treatment temperatures of 450 and 500°C, the carbonitrided samples presented s performance to the nitrided one and similar performance to the substrates s without the occurrence of any degradation of that property. The plasma nitriding and plasma carbonitriding treatments, carried out in the temperatures defined in the present work, for the principal types of stainless to produce layers with high hardness and wear resistances, without losses corrosion characteristics, which even got better in some cases, allow to expand the use of the stainless steels in situations where those properties are required.

Made available in DSpace on 2016-06-02T19:12:21Z (GMT). No. of bitstreams: 1 4512.pdf: 12085865 bytes, checksum: 9c98b7edb2a0238a143b2c8e9469a515 (MD5) Previous issue date: 2012-03-06 / Ion nitriding is a process of thermo-physical-chemical treatment that provides a surface hardening, originated by interstitial diffusion of nitrogen on the ferrous and nonferrous alloys surfaces. Understanding and controlling the formation of the nitrided layer have considerable industrial interest due to the improvements regarding wear, corrosion and fatigue resistances on the metals and their alloys. In this work, it was performed the surface modification in sintered iron samples by ion nitriding process, with a gaseous mixture of 80% vol H2 and 20% vol N2, during times of 3 and 5 hours, using ion nitriding temperature of 500°C, 540°C and 580°C. The samples were characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD) analyses, and wear and micro-hardness tests, comparing the results with sintered and steam treatment samples. The results showed that both nitride thickness and wear resistance increased with higher nitriding time and temperature, where the temperature was the variable that most influenced the aforementioned characteristics. The XRD analysis indicated that the nitrided layer near to the surface, for all samples, consisted in a mixture of y-Fe4N and e-Fe3N phases. / A nitretação iônica é um processo de tratamento termo-físico-químico que consiste em um endurecimento superficial, provocado pela difusão intersticial de nitrogênio atômico na superfície de ligas ferrosas e não ferrosas. O entendimento e o controle da formação da camada nitretada apresentam considerável interesse industrial devido às melhorias alcançadas nas resistências ao desgaste, corrosão e à fadiga dos metais e suas ligas. Neste trabalho, promoveu-se a modificação superficial de amostras de ferro sinterizado por meio do processo de nitretação a plasma, com uma mistura gasosa de 80% vol H2 e 20% vol N2, nos tempos de 3 e 5 horas, e temperaturas de nitretação de 500°C, 540°C e 580°C. As amostras foram caracterizadas por meios de análise de microscopia eletrônica de varredura (MEV) e difração de raios X (DRX), e quantificadas quanto aos níveis de desgaste e microdureza, em comparação com amostras sinterizada e ferroxidada. Os resultados mostraram que tanto as espessuras das camadas de nitretos como as resistências ao desgaste das amostras aumentaram com o tempo e temperatura de nitretação, sendo a temperatura a variável que mais influenciou nas características mencionadas. A análise de DRX indicou que a camada nitretada próxima a superfície, para todas as amostras, consiste de uma mistura de fases de  -Fe4N e -Fe3N.