Orientador: Sizenando de Toledo Porto Neto / Banca: Alberto Magno Gonçalves / Banca: Edson Alves dos Campos / Maria Salete Machado Cândido / Marcelo Ferrarezi de Andrade / Resumo: O presente trabalho teve por objetivo avaliar, comparativamente, in vitro, a resistência de união ao cisalhamento de uma resina composta à dentina humana e à dentina bovina, submetidas ao tratamento com dois sistemas adesivos convencionais simplificados (Prime Bond NT®, Dentsply e Single Bond®/3M) e dois sistemas adesivos autocondicionantes (AdheSE®/Ivoclar-Vivadent e Adpper Prompt-L-Pop®/ 3M). Para a confecção dos corpos-de-prova, foram utilizadas as superfícies vestibulares de 40 dentes molares humanos e de 40 dentes incisivos bovinos, as quais foram divididas aleatoriamente em 8 grupos de 10 amostras cada, de acordo com o tipo de substrato e o sistema adesivo utilizado: Grupo 1 - dentina humana tratada com o sistema adesivo Single Bond; Grupo 2 - dentina humana tratada com o sistema adesivo Prime Bond NT; Grupo 3 - dentina humana tratada com o sistema adesivo AdheSE; Grupo 4 - dentina humana tratada com o sistema adesivo Adpper Prompt-L-Pop; Grupo 5 - dentina bovina tratada com o sistema adesivo Single Bond; Grupo 6 - dentina bovina tratada com o sistema adesivo Prime Bond NT; Grupo 7 - dentina bovina tratada com o sistema adesivo AdheSE; Grupo 8 - dentina bovina tratada com o sistema adesivo Adpper Prompt-L-Pop. Após o tratamento das superfícies, com o auxílio de uma matriz bipartida, foram confeccionados cilindros de resina composta Tetric Ceram apresentando 3mm de diâmetro e 4mm de altura. Os corpos-de-prova foram então armazenados em água destilada a 37ºC por 24 horas e submetidos a termociclagem (550 ciclos à temperatura de 10ºC e 55ºC). Após 48 horas de armazenamento em água destilada a 37ºC, foram levados a uma Máquina de Teste Universal para a realização do teste de cisalhamento utilizando-se uma ponta em forma de cinzel e velocidade do atuador de 0,5 mm/min. Os tipos de fratura foram analisados em lupa estereoscópica com 40X de aumento. / Abstract: The purpose of this in vitro study was to evaluate, comparatively, the shear bond strength of a composite resin to human and bovine dentin treated with two conventional simplified adhesive systems (Prime Bond NT®/Dentsply and Single Bond®/3M) and two self-etching adhesive systems (AdheSE®/Ivoclar-Vivadent and Adpper Prompt-L-Pop®/3M). For preparation of specimens, the buccal surface of 40 human molars and 40 bovine incisors were obtained and randomly assigned to 8 groups (n=10), according to the type of substrate and adhesive system used. Group1 - human dentin treated with Single Bond; Group 2 - human dentin treated with Prime Bond NT; Group 3 - human dentin treated with AdheSE; Group 4 - human dentin treated with Adpper Prompt-L-Pop; Group 5 - bovine dentin treated with Single Bond; Group 6 - bovine dentin treated with Prime Bond NT; Group 7 - bovine dentin treated with AdheSE; Group 8 - bovine dentin treated with Adpper Prompt-L-Pop. After treatment with the adhesive systems, composite resin (Tetric Ceram) cylinders (3 mm in diameter and 4 mm high) were fabricated using a split matrix and were bonded to the dentin surfaces. The specimens were stored in distilled water at 37ºC for 24 hours and then submitted to a thermocycling regimen (550 cycles between 10ºC and 55ºC). After 48-hour storage in distilled water at 37ºC, the specimens were taken to a universal testing machine and loaded in shear strength until failure using knife-edge-shearing blade running at a crosshead speed of 0.5 mm/min. Failure mode was analyzed using a stereomicroscope at X40. Data were submitted to statistical analysis by analysis of variance at 5% significance level. The results showed that Single Bond and Prime Bond NT adhesive systems presented similar shear bond strength to each other (p>0.05) and significantly higher means than AdheSE and Adper Prompt-L-Pop (p<0.05), regardless of the type of substrate. / Doutor

Orientador: Welingtom Dinelli / Banca: José Roberto Cury Saad / Banca: Silmara Aparecida Milori Corona / Resumo: O objetivo deste trabalho foi avaliar, in vitro, os efeitos da desproteinização da dentina sobre a resistência de união de três diferentes sistemas adesivos. Para tal, 30 terceiros molares humanos hígidos foram seccionados transversalmente, por meio de disco diamantado, na união do terço médio com o terço oclusal e desgastados com discos de lixa de granulação 320 e 600 para completa exposição da superfície dentinária e padronização da "smear layer". Em seguida, os dentes foram divididos aleatoriamente em 6 grupos (n=5), os quais receberam aplicação dos sistemas adesivos Prime & Bond 2.1 (Dentsply), Single Bond (3M) e Clearfil SE Bond (Kuraray) de acordo com as instruções dos fabricantes (Grupos 2, 4 e 6, respectivamente) ou após desproteinização da dentina com hipoclorito de sódio a 5% durante 2 minutos (Grupos 1, 3 e 5, respectivamente). Restaurações de resina composta Z100 foram confeccionadas, de forma incremental, sobre toda a superfície oclusal. Os dentes foram, então, seccionados com disco diamantado com a finalidade de obter amostras em forma de palitos de 1,0 l 0,2mm2 de área adesiva. Vinte e cinco amostras de cada grupo foram selecionadas e armazenadas por 24 horas em água destilada a temperatura de 37ºC. Em seguida, os testes de microtração foram realizados em Máquina Universal de Ensaios MTS, à velocidade do atuador de 0,5mm/min. Os resultados, analisados estatisticamente por meio de Análise de variância e Teste de Tukey (p<0,05), indicaram que a aplicação do NaOCl proporcionou redução da resistência adesiva para todos os grupos (G1- 29,16 l 3,98; G3- 23,06 l 4,87; G5- 26,71 l 5,10) quando comparados com os grupos controle (G2- 33,11 l 5,76; G4- 30,62 l 5,47; G6- 32,09 l 6,43). Em relação aos padrões de fratura, observou-se predominância de fraturas adesivas, sendo que estas, nos grupos onde a dentina foi... (Resumo completo, clicar acesso eletrônico abaixo). / Abstract: The aim of this study was to evaluate, in vitro, the influence of dentin deproteinization on microtensile bond strength of three different adhesive systems. Thirty freshly extracted human molars were transversely wetcut using a diamond disk in order to expose the oclusal dentin surface. The teeth were randomly divided into 6 groups (n=5) and the adhesive systems Prime & Bond 2.1 (Dentsply), Single Bond (3M) e Clearfil SE Bond (Kuraray) were applied according to the manufacturer's instruction (control groups: G2, G4 and G6) or after application of sodium hypochlorite 5% for 2 minutes (G1, G3 and G5). The teeth were restored with Z100 (3M) composite resin and the microtensile specimens, with a bonded area of 1,00l 0,2mm2, were prepared by a slow-speed diamond disk. Twenty-five specimens of each group were selected and stored in distilled-water at 37oC for 24 hours. The microtensile tests were performed in a MTS universal testing machine with a cross-head speed of 0,5mm/min. The results were statistically analyzed by ANOVA and Tukey's test (p=0,05). Sodium hypochlorite pre-treatment significantly decreased the microtensile bond strength values of all adhesive systems (G1- 29,16 l 3,98; G3- 23,06 l 4,87; G5- 26,71 l 5,10) compared to control groups (G2- 33,11 l 5,76; G4- 30,62 l 5,47; G6- 32,09 l 6,43). Analysis of the morphology of the failure pattern revealed that, for the control specimens, debonding had occurred in the composite/teeth interface and in specimens that were etched and deproteinized, debonding was characterized by resin failure through the wide bases of the tag extensions into dentinal tubules. / Mestre

Orientador: Osmir Batista de Oliveira Junior / Banca: Alexandre Henrique Susin / Banca: Oswaldo Scopin de Andrade / Resumo: O propósito deste estudo foi avaliar através do teste de microtração e da análise do padrão de fratura, o efeito da luz halógena e LED, na ativação de um adesivo de frasco único. Superfícies dentinárias planas foram criadas em 16 dentes terceiros molares hígidos. Os dentes foram aleatoriamente divididos em 4 grupos: Grupo G1 - Aparelho de luz halógena - KM-200R®; Grupo G2 - Aparelho LED - Ultraled®; Grupo G3 - Aparelho LED - UltraLume®LED5 e Grupo G4 - Aparelho LED - Biolux Single V®. O procedimento restaurador foi realizado utilizando o adesivo Single Bond® e a resina composta InTen-S®. Após as restaurações, os dentes foram armazenados em água destilada e estufa a 37ºC por 24h. A seguir, os mesmos foram cortados, resultando em espécimes com área de aproximadamente 1 mm2, que foram selecionados e submetidos ao teste de microtração para posterior observação do padrão de fratura no microscópio digital. Os resultados, submetidos a análise estatística mostram que o grupo G2 teve média de resistência de união significativamente menor que os demais grupos, que foram semelhantes entre si. Quanto ao tipo de fratura, houve diferença significativa entre os grupos G1 e G2 e entre os grupos G2 e G4. Entre os outros grupos não houve evidência de diferenças significativas. As falhas de união foram predominantemente do tipo adesivas. Conclui-se que os aparelhos LEDs de segunda e terceira geração utilizados nesta pesquisa podem ser utilizados como uma alternativa viável à luz halógena. / Abstract: The purpose of this study was to evaluate the effect of halogen light and LED on dentin tensile bond strength and fracture mode analysis. Flat dentin surfaces were created on 16 intact human third molars. The teeth were randomly divided in 4 groups: Group G1 - halogen - KM -200R®; Group G2 - LED - Ultraled®; Group G3 - LED - UltraLume LED5® and Group G4 - LED - Biolux Single V®. The restoration procedure used Single Bond® adhesive and InTen-S® composite resin. The teeth were placed in distilled water and stored at 37ºC for 24 hours. Then, they were cut on serial sections to obtain 1 mm2 area. The samples were submitted to micro tensile test and after words, the fractures were analysed with a digital microscope. The statistical analysis showed that all in all groups, except Group G2, which had a significant smaller tensile bond strength ratio. The fracture mode analysis showed that there were significant difference when comparing groups G1 / G2, and G2 / G4. There is no evidence of relevant differences among the other groups. Adhesive fracture was the most common fracture mode. As a conclusion, second and third LED generation used in this research could be use as an alternative to the conventional halogen lamp. Keyword: Dentin-bonding agents; tensile strength. / Mestre

Orientador: Eduardo César Almada Santos / Resumo: Os recentes materiais de colagem dos acessórios ortodônticos têm visado reduzir o tempo de trabalho do clínico, simplificando o procedimento do condicionamento ácido por meio dos sistemas adesivos autocondicionantes. Todavia, as qualidades adesivas desses materiais ainda demandam ser avaliada. Assim, o presente estudo objetivou avaliar a resistência às forças de compressão de três sistemas adesivos. Cento e oitenta incisivos inferiores bovinos foram seccionados e incluídos em matrizes de resina acrílica, nos quais acessórios ortodônticos foram colados com os sistemas Transbond XT (2 grupos de 30), Transbond XT Plus Self Etching Primer (2 grupos de 30) e Tyrian (2 grupos de 30). Para cada sistema, os testes de resistência foram realizados imediatamente (30 dentes) e 24 horas (30 dentes) após a colagem, em uma máquina de ensaio Versat 2000 (Pantec), utilizando célula de carga de 500 Kgf com uma velocidade de 1mm/minuto, de acordo com a literatura. Os sistemas convencional Transbond XT, Transbond XT Self Etching Primer e Tyrian apresentaram, respectivamente, valor médio de resistência à compressão de 7,43, 7,09 e 3,41 MPa no tempo imediatamente após a colagem, e 7,42, 8,81, 5,35 MPa no tempo 24 horas após a colagem, sendo as diferenças estatísticas significantes ao nível de 5% entre os grupos Tyrian e Transbond para ambos os tempos de estudo. Concluiu-se que o material Tyrian apresentou resistência à compressão significativamente inferior em relação aos grupos Transbond que foram similares. / Abstract: Recent orthodontic bonding materials have aimed to reduce the working time of the clinician, by simplifying the acid etching procedure by applying self-etching primer adhesive systems. However, the adhesion quality of these materials still demands investigation. Thus, the present study aimed to evaluate the bond strengths of three different adhesive systems. A hundred and eighty bovine lower incisors were cut and embebbed in acrylic resin matrices, in which orthodontic brackets were bonded with Transbond XT (2n = 60), Transbond XT Self Etching Primer (2n = 60) e Tyrian (2n = 60). For each composite, bond strength tests were executed immediately (n = 30) and 24 hours (n = 30) after the bonding, in the assay machine Versat 2000 (Pantec), by applying 500 Kgf of load at 1mm/min of velocity. Transbond XT, Transbond XT Self Etching Primer and Tyrian presented, respectively, average values of bond strength of 7.43, 7.09 and 3.41 MPa at the time immediately, and 7.42, 8.81 and 5.35 MPa at 24 hours after the bonding, where differences were statistically significant at 5% between Tyrian and Transbond groups at both observation times. It was concluded that Tyrian was the material that presented significant lower bond strength with regard to Transbond groups that were similar. / Mestre

Resumo: Introdução: Embora os sistemas adesivos autocondicionantes se caracterizem por desmineralizar e infiltrar a dentina simultaneamente, a presença de dentina alterada abaixo da camada híbrida tem sido reportada, sugerindo comportamento mecânico distinto. Proposição: Avaliar por meio do método dos elementos finitos tridimensional a influência da espessura da dentina parcialmente alterada no comportamento micromecânico de dois sistemas adesivos autocondicionantes. Materiais e Métodos: Foram elaborados 5 micro-modelos (M) simulando a interface dentina/adesivo (d/a) (82x41x41 μm), sendo: M1-representação da interface d/a baseada em sistema adesivo convencional de 2 passos; M2-representação de um sistema adesivo autocondicionante de 2 passos. Nos M3, M4 e M5 representação de um sistema adesivo autocondicionante de 1 passo, variando a espessura da camada de dentina parcialmente alterada em 0, 1,5 e 3 μm, respectivamente. Os modelos foram considerados isotrópicos, homogêneos e linearmente elásticos. A base de todos os modelos foi fixada nos eixos x, y e z, sendo aplicado um carregamento em tração (90º; 0,03 N) na face superior da resina composta. A análise numérica foi realizada para a obtenção da tensão principal máxima ( max). Resultados: o pico da max (MPa) foi encontrada no M5 (79,5), seguido do M4 (78,0) e do M3 (70). O topo dos tags foi o local mais solicitado em todos os modelos. Conclusão: O aumento da espessura da dentina parcialmente alterada aumentou a tensão na interface d/a; a ausência desta camada contribuiu para a menor concentração de tensão; o topo dos tags foi o local mais exigido na interface d/a. / Abstract: Introduction: Although the self-etching adhesives are characterized by etching and infiltrating simultaneously the dentin, the presence of an altered dentin layer has been showed by literature, which might show specific mechanical behavior. Proposition: To evaluate through 3-D finite element analysis the influence of the partially altered dentin thickness on the micromechanical behavior of the self-etch adhesives. Materials and Methods: 5 micro-models (M) were developed for simulating the dentin/adhesive (d/a) interface (82x41x41 μm): M1-representation of the d/a interface based on 2 steps conventional adhesive system; M2-d/a interface based on 2 steps self-etch adhesive system M3, M4 and M5 - d/a interface based on all-in-one adhesive system, varying the thickness of the partially altered dentin (0, 1.5 and 3 μm, respectively). All the models were considered isotropic, homogeneous and lineally elastic. The bottom of all the models were constrained in the axes x, y and z. A tensile load (90o; 0.03N) was applied on the top of the composite resin. The numeric analysis was accomplished, being obtained the maximum principal stress ( max). Results: The pick of max (MPa) was found in M5 (79.5), followed by M4 (78.0) and M3 (70). The top of the resin tags was the most requested place in all models. Conclusion: The increase of the partially altered dentin thickness raised the max in the d/a interface; the absence of this layer contributed to the smallest tension concentration; the top of the tags showed higher stress concentration. / Orientador: Eduardo Passos Rocha / Coorientador: Renato Herman Sundfeld / Banca: Paulo Henrique dos Santos / Banca: André Figueiredo Reis / Mestre

O objetivo deste trabalho foi avaliar o efeito do selamento dentinário imediato na cimentação definitiva de restaurações cerâmicas (Empress2Ivoclar Vivadent), levando em consideração a influência de diferentes métodos de remoção dos restos de cimento provisório da superfície dentinária previamente selada. Para isso foram utilizados 72 molares, hígidos, conseguidos no banco de dentes da Universidade do Estado do Rio de Janeiro. Os dentes foram divididos em nove grupos, os três primeiros serviram como grupo controle, onde não houve contaminação com nenhum cimento provisório, sendo eles: G1, onde o selamento e a cimentação definitiva foram feitas 15 dias após a confecção dos preparos cavitários; G2, onde o selamento dentinário foi feito imediatamente após o preparo e a cimentação definitiva após 15 dias; G3, onde o preparo, selamento e cimentação definitiva foram feitos no mesmo momento. Os próximos grupos foram os do selamento tardio, onde o sistema adesivo foi aplicado somente no momento da cimentação. Nestes grupos, após o preparo foram cimentadas restaurações provisórias com um cimento livre de eugenol (Temp BondNE) e após 15 dias as restaurações provisórias foram removidas e os restos de cimento limpos com diferentes métodos: G4: remoção com instrumento manual; G5: remoção com jato de bicarbonato; G6: remoção com pontas de ultra-som; após esta limpeza o sistema adesivo foi aplicado e as restaurações cerâmicas cimentadas. Por último foram os grupos do selamento dentinário imediato, onde o sistema adesivo foi aplicado imediatamente após a confecção dos preparos cavitários e em seguida foi feita a cimentação das restaurações provisórias. Após 15 dias as restaurações provisórias foram removidas, os restos de cimento foram limpos com os diferentes métodos: G7: remoção com instrumento manual; G8: remoção com jato de bicarbonato; G9: remoção com pontas de ultra-som. Após a limpeza as restaurações cerâmicas foram cimentadas. Para todos os grupos o sistema adesivo utilizado foi o Optibond FL Kerr e o cimento resinoso foi o Rely X ARC3M/ESPE. Vinte e quatro horas após as cimentações cerâmicas os corpos de prova foram submetidos ao ensaio mecânico de push out em uma máquina de ensaios universais EMIC DL. Os valores de resistência de união foram obtidos em KgF, convertidos em MPa e analisados estatisticamente. O teste de ANOVA mostrou que houve diferença estatisticamente significante entre os grupos (p&#8804;0,05) e em seguida o t-teste mostrou que a técnica do selamento imediato resultou nos melhores valores de resistência de união. Por último, o teste de comparações múltiplas Student-Newman-Keuls (Teste SNK) mostrou que o método de limpeza dos restos de cimento provisório da superfície dentinária apresenta influência na resistência de união das restaurações cerâmicas. Com base nos resultados pôde-se concluir que a técnica do selamento imediato promoveu maior resistência adesiva para as restaurações cerâmicas e quanto ao método de limpeza, o melhor resultado, independente da técnica adesiva utilizada, foi a remoção com as pontas de ultrasson. / The aim of this study was to evaluate the effect of immediate dentin sealing on bond strength of ceramic restorations, taking into account the influence of different techniques used to remove temporary cement remainings from dentin surfaces. Seventy two intacts and caries free human molars were taken from UERJ teeth bank in order to perform the necessary experiments. They were divided into nine groups. The first three groups served as control groups and there was no contamination with temporary cements: G1, the dentin sealing and ceramic cementation were made fifteen days after preparation; G2, the dentin was sealed immediately after preparation and after fifteen days the ceramic restorations were fixed; G3, wich the praparation, dentin sealing and ceramic cementation were made at the same time. The next three groups constituted the delayed dentin sealing group, where the dentin bonding agent were applied only in the moment of ceramic cementation. After preparation, provisional restorations were placed with a provisional cement without eugenol (Temp BondNE) and after fifteen days they were removed and dentin surfaces were cleaned by differents methods: G4: hand instrument; G5: sodium bicarbonate jet; G6: ultra-sonic scaler. The adhesive system was then applied and the ceramics were bonded. The three last groups constituted the immediate dentin sealing, where the dentin bonding agent was applied immediately after preparation, before provisional cementation. Following fifteen days, the provisional restorations were removed and the sealed dentin were cleaned by differents methods: G7: hand instrument; G8: sodium bicarbonate jet; G9: ultra-sonic scaler. After these procedures the ceramic restorations were bonded. The adhesive system used in all groups was Optibond Kerr and the resin cement was Rely X ARC3M/ESPE. Following twenty four hours all specimens were submitted to the push-out test in a universal testing machine EMIC DL. The push out bond strength was obtained in KgF and were then converted into MPa. The results were analysed: one-way ANOVA revealed significant differences between groups (p&#8804;0,05), t-test showed that immediate dentin sealing provided the highest values of bond strength. At least, the Multiple comparisions SNK Test detected that the differents techniques used to remove temporary cement remainings from dentin surfaces had an influence on the ceramic bond strength, and even when immediate dentin sealing or delayed dentin sealing was used, the ultra-sonic scaler showed the better results.

This study aims to understand the traumatic situation of domestic violence in order to investigate the elements of its arrangement and bonding settings. Psychoanalysis of Bonding Configurations emphasizes the constitution of the subject from each encounter, repositioning the impossibility of the subject to be without a social place that composes his/her history. In this sense, trauma will produce different effects as a social and bonding register. The methodology used in this study was the construction of a case of a family being assisted by the psychoanalytic method. The Family Clinic facilitated the writing of the clinical case, a story of pain and suffering that portrays human bonding and entanglements with narratives that reveal repetition of violent scenes. In this perspective, I dare to build an analysis path as trauma possibly unfolding this bonding that enables the outburst of violence. Recollections upon the case accentuate the tone of the family organization, pointing to the binding mesh encompassed by violence. In fitting telescoping family, there are no boundaries to organize the links, but there is a setting that denotes the confusion and disruption of family membership. In households where violence and aggression reign, functions are blurred and trauma acquire transgenerational contours. The body, marked by violence, is the traumatic exposure in the family history and is a place that inhabits all excesses and transgenerational breaks. The family-subject of this study experiences time in alternation. The analytic space reveals the time for each \"thing\" to appear and disappear; the critical time of mourning and the subjectivity of its buildings; setting time as an ally to deal with the traumatic. The family telescoping is accessed in chronological time and becomes emblematic of the violent structuring bonds that tack on redoing the senses acquired in fantasy and appointment of traumatic content. The meanings of the losses will be recovered and a new subjectivity can be drawn in the transference field. The traumatic event points to the intransitive existence of a past that can perpetuate the experience; however, there is a direct correspondence between the size of the painful event and its alienating effect. The trauma interrupts the narrative, but also launches a new story from new subscriptions. From the traumatic event, re-accommodations of borders and the meaning of belonging to the set of characters may come about with effects and resonances that affect the group in various configurations. Traumatic thus could even be the element that feeds the emotional fabric of the family. The subject in the family is balanced between the traumatic event that marks its history and the creative possibilities of reinventing the narrative. / A presente pesquisa tem como objetivo compreender o traumático na situação de violência intrafamiliar, buscando investigar os elementos do arranjo e das configurações vinculares. A Psicanálise das Configurações Vinculares enfatiza a constituição do sujeito a partir de cada encontro, reposicionando a impossibilidade de se fazer sujeito sem um espaço social que componha sua história. Neste sentido, o trauma produzirá diferentes efeitos como inscrição social e vincular. A metodologia utilizada envolveu a construção do caso clínico de um atendimento familiar, ancorada no método psicanalítico. A Clínica de Família viabilizou a escrita do caso clínico, uma história de dor e sofrimento que retrata o vínculo humano, com enredamentos e narrativas que revelam repetições de cenas violentas. Nesta perspectiva, ouso construir como caminho de análise o traumático como possível desdobramento deste campo vinculativo que possibilita a irrupção da violência. As rememorações sobre o caso vão acentuando o tom da organização familiar, apontando para a malhagem vinculativa em torno da violência. No encaixe da telescopagem familiar não há fronteiras que organizem os vínculos, mas há uma configuração que denota a confusão e a ruptura da filiação. Nos núcleos familiares, onde impera a violência e a agressão, as funções se constituem borradas e os traumas adquirem contornos transgeracionais. O corpo, marcado pela violência, é a exposição do traumático na história familiar como lugar que habita todos os excessos e rupturas transgeracionais. A família-sujeito desta pesquisa vivencia o tempo em alternância. O espaço analítico vai revelando o tempo para cada coisa aparecer e desaparecer; o tempo fundamental dos lutos e a subjetividade de suas construções; estabelecendo o tempo como aliado na elaboração do traumático. A telescopagem familiar é acessada no tempo cronológico e se torna emblemática dos vínculos violentos estruturantes que vão se refazendo no alinhavo dos sentidos adquiridos na fantasia e na nomeação dos conteúdos traumáticos. Os sentidos das perdas vão sendo recuperados e uma nova subjetividade pode ser desenhada no campo transferencial. O acontecimento traumático aponta para a existência intransitiva de um passado que pode se perpetuar na experiência; entretanto, não há uma correspondência direta entre a dimensão dolorosa do acontecimento e seu efeito alienante. O trauma interrompe a narrativa, mas também inaugura uma nova história a partir de novas inscrições. A partir do fato traumático podem haver reacomodações das fronteiras e do significado de pertencimento dos personagens do conjunto, com efeitos e ressonâncias que afetam o conjunto em configurações diversas. O traumático, assim, pode, inclusive, ser o elemento que alimenta condição constitutiva do tecido afetivo da família. O sujeito na família equilibra-se entre o acontecimento traumático que marca sua história e as possibilidades criativas de reinventar a narrativa. / Mestre em Psicologia Aplicada

A Odontologia minimamente invasiva tornou-se possível em decorrência do atual avanço alcançado na Odontologia adesiva, e a remoção seletiva do tecido cariado passou a ser recomendada para dentes com lesões de cárie profunda. Tal preparo cavitário preserva a dentina afetada por cárie (DAC), camada mais interna da dentina cariada que é remineralizável. Entretanto, esse substrato apresenta propriedades mecânicas inferiores e diversos estudos relatam uma resistência de união reduzida. O objetivo do presente estudo foi revisar sistematicamente a literatura quanto a resistência da união dos sistemas adesivos à DAC quando comparada à dentina hígida (DH), assim como a influência das variáveis metodológicas dos estudos in vitro. Além disso, desenvolver e caracterizar uma resina adesiva com a incorporação de um fosfato de cálcio, assim como avaliar o potencial de induzir deposição mineral em dentes com DAC. As buscas foram realizadas nas bases de dados PubMed, Scopus, Web of Science e LILACS. Foram incluídos estudos laboratoriais que investigaram a resistência de união à microtração imediata e longitudinal de sistemas adesivos À DAC natural ou artificial, utilizando DH como controle. Oito artigos preencheram os critérios de inclusão, e uma metaregressão foi realizada para a associação das variáveis independentes do modelo com o desfecho de resistência de união. O modelo final com 5 variáveis explicou 75,6% da variabilidade entre os grupos. Todas as variáveis independentes apresentaram influência significativa no desfecho, e a DAC resultou em menor resistência de união. Sendo assim, uma resina adesiva com a incorporação de α-fosfato tricálcico (αTCP) foi desenvolvida e caracterizada. Para a formulação das resinas adesivas, 66,66% em peso de BisGMA, 33,33% em peso de HEMA e um sistema fotoiniciador foram misturados. O αTCP foi adicionado a 2% em peso, originando a resina adesiva teste. Uma resina sem adição de carga foi utilizada como controle. As resinas adesivas foram caracterizadas quanto à taxa de polimerização e grau de conversão, e degradação em solvente. Sessenta dentes permanentes extraídos com lesões de cárie profunda foram submetidos à remoção seletiva do tecido cariado e restaurados utilizando uma das duas resinas adesivas. As amostras foram avaliadas por meio de ensaios imediatos e longitudinais (no decorrer de 6 meses, armazenadas em SBF) de resistência de união à microtração, avaliação da deposição mineral por espectroscopia Raman e dureza Knoop. A dureza Knoop inicial da resina adesiva teste foi maior quando comparada à controle, e não houve diferença entre os grupos em relação ao percentual de variação da dureza Knoop após a imersão em solvente. O grupo teste apresentou maior taxa de polimerização e não houve diferença entres os grupos para o grau de conversão. Não houve diferença entre os grupos para a resistência de união imediata e longitudinal, e ambos os grupos mantiveram estável a resistência de união após 6 meses. A análise da interface em relação à deposição mineral mostrou que houve aumento do conteúdo mineral para os dois grupos. Em relação à dureza Knoop, houve um aumento nos valores após 3 meses, entretanto não houve diferença entre os grupos dentro das diferentes profundidades para cada tempo. Conclui-se que não houve diferença entre os grupos em relação à deposição mineral. / The minimally invasive dentistry became possible due to the current advancement in adhesive dentistry, and the selective removal of carious tissue has been recommended for teeth with deep carious lesions. Such cavity preparation preserves the caries-affected dentin (CAD), the inner layer of carious dentin that is remineralizable. However, this substrate presents low mechanical properties and many studies reported reduced bond strength. The objective of this study was to systematically review the literature on the microtensile bond strength (μTBS) of adhesive systems to (CAD) when compared to sound dentin (SD), as well as on the influence of methodological variables of in vitro studies. Also, to develop and characterize an adhesive resin with the incorporation of a calcium phosphate, as well as evaluate the potential to induce mineral deposition in teeth presenting CAD. The electronic databases PubMed, Scopus, ISI Web of Science and LILACS were systematically searched. Were included in vitro studies that assessed the immediate and aged microtensile bond strength of adhesive systems to natural or artificially created CAD in comparison to SD. Eight studies met the inclusion criteria and were included in a linear meta-regression of microtensile bond strength. The fully adjusted model with 5 methodological variables explained 75.6% of the variability among groups. All methodological variables were associated with microtensile bond strength, and bond strength to CAD was lower than to SD. Thus, an adhesive resin with the incorporation of α-tricalcium phosphate (αTCP) was developed and characterized. To formulate the experimental adhesive resins, 66.66 wt% BisGMA, 33.33 wt% HEMA and a photo-initiator system were mixed. The αTCP at 2 wt% was added, yielding the test adhesive resin. An adhesive resin without filler was used as control. The adhesive resins were characterized regarding polymerization kinetics and degree of conversion, and softening in ethanol. Sixty extracted human posterior permanent teeth with deep carious lesions were submitted to selective removal of carious tissue and restored using one of the two adhesive resins. Samples were evaluated by immediate and longitudinal (6 months, storage in SBF) following tests: microtensile bond strength, mineral deposition by Raman spectroscopy and Knoop hardness. The test adhesive resin showed higher initial Knoop hardness than the control one, and there was no difference between the groups for the percentage of variation of Knoop hardness after solvent immersion. The test group showed increased polymerization rate, and there was no difference between groups for degree of conversion. There was no difference between the groups for immediate and longitudinal microtensile bond strength, and the microtensile bond strength of both groups remained stable after the 6 months. The interface analysis regarding mineral deposition showed an increasing in mineral content for both groups. For Knoop hardness, there was an increase after 3 months, however the groups where not significantly different considering depth and time. It could be concluded that there was no difference between control and test adhesive resin for mineral deposition.

O objetivo deste estudo foi sintetizar e caracterizar monômeros metacrilamidas, desenvolver, caracterizar e avaliar as propriedades de sistemas adesivo convencional de três passos. Foram sintetizadas bis(metacrilamida)s e tris(metacrilamida) e caracterizadas por espectroscopia de Infravermelho por Transformada de Fourier (FTIR), Ressonância Magnética Nuclear (RMN) de 1H e 13C, por Cromatografia Líquida de Alta Eficiência com Espectrometria de Massas (UHPLC-QTOF-MS) e Calorimetria Exploratória Diferencial Modulada (MDSC). Quatro bis(metacrilamidas), (1) N,N’-(propane-1,3-diyl)bis(N-ethyl-2-methylacrylamide), (2) N,N’-(octane-1,8-diyl)bis(2-methylacrylamide), (3) N,N’-(butane-1,4-diyl)bis(2-methacrylamide) e (4) N,N’-(1,4 phenylene)bis(2-methylacrylamide)monômero (1), (2), (3) e (4), e uma tris(metacrilamida) TMA, foram sintetizadas. Pela análise de FTIR-ATR foram observadas as bandas correspondentes ao estiramento do grupo C=O (1660 cm-1), C=C (1610 cm-1), N-H (3300 cm-1) e C-N (1520 cm-1). As análises de RMN identificaram a presença das ligações duplas referentes aos grupos metacrilamidas em deslocamentos químicos entre 5,3 e 5,8 ppm para 1H e entre 120 e 140 ppm para 13C.Os valores de massa exata m/z foram: 267,2068, 281,2222, 225,1595, 245,1283 e 351,2385 g/mol para os monômeros (1), (2), (3), (4) e TMA, respectivamente. A cinética de polimerização do TMA e dos adesivos experimentais contendo 2-hidroxietil acrilamida (HEAA) ou 2-hidroxietil metacrilato (HEMA) com as seguintes formulações foram investigadas por meio de DSC-PCA, n=3: TMA33%/HEAA66%, TMA50%/HEAA50%, TMA66%/HEAA33%, TMA50%/HEMA50%, BisGMA/HEAA/TMA e BisGMA/HEMA.Características e propriedades mecânicas das resinas adesivas BisGMA/HEAA/TMA e BisGMA/HEMA foram avaliadas por resistência coesiva (UTS, n=5), degradação em solvente (ΔKHN, n=5), ângulo de contato (n=5), microtração (μTBS, n=20) e análise de fratura. Um primer a base de acrilamidas foi desenvolvido (H2O/HEAA/AMPS) (2-acrylamida-2-methilpropano ácido sulfônico) para ser utilizado no grupo experimental com metacrilamidas. Os valores de pH e ângulo de contato do primer experimental foram comparados com o primer do ScotchBond Multi-purpose (grupo controle). O monômero (1) resultou em um monômero amarelo claro de baixa viscosidade, entretanto, não apresentou foto ou termopolimerização. A energia de ativação determinada pelo método de Kissinger foi – 165,8 kJmol-1; -182,7 kJmol-1 e -156,7 kJmol-1 para os monômeros (2), (3) e (4), respectivamente. Sistemas adesivos convencionais de três passos a base de metacrilamidas e a base de metacrilatos foram desenvolvidos. Resinas adesivas contendo somente HEAA e TMA (TMA33%/HEAA66%, TMA50%/HEAA50%, TMA66%/HEAA33%) apresentaram grau de conversão abaixo de 40% após 40 s de fotoativação. Alto grau de conversão (acima de 60%) só foi encontrado para as resinas adesivas BisGMA/HEAA/TMA e BisGMA/HEMA e sem diferença significativa entre elas, p>0,05. Os valores de UTS (BisGMA/HEMA- 67,7 ±5 MPa e BisGMA/HEAA/TMA- 60,5 ±7 MPa), μTBS (BisGMA/HEMA- 57 ± 14 MPa e BisGMA/HEAA/TMA- 53,1 ±15 MPa) e ângulo de contato (BisGMA/HEMA- 39,5 ±9 e BisGMA/HEAA/TMA- 46,7 ±15) não apresentaram diferença estatística, p>0.05. O primer experimental apresentou um valor pH mais baixo (2,7) bem como de ângulo de contato (18,5 ±5) em relação ao comercial (pH-4 e θ-33,5 ±4). A síntese proposta para os monômeros (1), (2), (3), (4) e TMA foi caracterizada nesse trabalho. Um primer somente com acrilamidas foi desenvolvido e a presença do novo monômero TMA na resina adesiva BisGMA/HEAA permitiu a formulação de um sistema adesivo convencional de três passos sem a presença do monômero HEMA. / The aim of this study was synthesized and characterizes methacrylamides monomers, development, characterizer and evaluated the properties of 3-step etch-and-rise adhesive system. Bis(methacrylamide)s and tris(methacrylamide) were synthesized. The monomer structures were confirmed by 1H and 13C Nuclear Magnetic Resonance (NMR), Fourier Transform Infrared Spectroscopy (FTIR-ATR), Ultra-high liquid chromatography quadrupole time of flight mass spectrometry (UHPLC-QTOF-MS) and modulated differential scanning calorimetry (mDSC). Four bis(methacrylamide)s monomers (1) N,N’-(propane-1,3-diyl)bis(N-ethyl-2-methylacrylamide), (2) N,N’-(octane-1,8-diyl)bis(2-methylacrylamide), (3) N,N’-(butane-1,4-diyl)bis(2-methacrylamide) and (4) N,N’-(1,4 phenylene)bis(2-methylacrylamide) and one tris(methacrylamide), TMA, were synthesized. All IR spectra of the monomers showed the C=C axial deformation at 1610 cm-1. The 1H NMR spectra the olefinic hydrogens were observed at 5.3 an 5.8 ppm and in the 13C NMR, the vinylic carbons at 120 and 140 ppm. The exact m/z values were: 267.2068, 281.2222, 225.1595, 245.1283 and 351.2385 g/mol for monomers (1), (2), (3), (4) and TMA respectively. Monomer (1) not presented photo (DSC-PCA) or thermal polymerization. The activation energy determined using Kissinger methodology was: - 165.8 kJmol-1; -182.7 kJmol-1 and -156.7 kJmol-1 for monomers (2), (3) and (4), respectively. 3-step adhesive systems with methacrylamides and methcrylates were development. Kinetics of photopolymerization of TMA and experimental adhesive resin containing 2-hydroxyethylacrylamide (HEAA) or 2-hydroxyethylmethacrylate (HEMA) in the following formulations: (TMA 33%/HEAA 66%, TMA 50%/HEAA 50%, TMA66%/HEAA33%, TMA50%/HEMA50%, BisGMA66%/HEAA24%/TMA10% and BisGMA66%/HEMA33%) were investigated through DSC-PCA. Characteristics and mechanical properties for BisGMA 66%/HEAA 24%/TMA 10% and BisGMA 66%/HEMA 33% adhesives were evaluated with ultimate tensile strength (UTS, n=5), softening in solvent (ΔKHN, n=5), contact angle (n=5), microtensile bond strength (μTBS, n=20) and failure analysis. A primer was also formulated with H2O/HEAA/AMPS (2-acrylamido-2-methylpropane sulfonic acid) and the pH and contact angle value were verified and compared to commercial ScotchBond primer. Adhesive resin with HEAA and TMA (TMA33%/HEAA66%, TMA50%/HEAA50%, TMA66%/HEAA33%) showed lower conversion and polymerization rate after 40 s of light activation. Higher conversion (up to 60%) was found for BisGMA/HEAA/TMA and BisGMA/HEMA adhesive resin without significant difference between adhesive resin, p>0.05. UTS (BisGMA/HEMA- 67.7 ±5 MPa e BisGMA/HEAA/TMA- 60.5 ±7 MPa), immediate μTBS (BisGMA/HEMA- 57 ± 14 MPa e BisGMA/HEAA/TMA- 53.1 ±15 MPa), ΔKHN (BisGMA/HEMA- 56 ± 7 e BisGMA/HEAA/TMA- 64 ±4) and contact angle (BisGMA/HEMA- 39.5 ±9 e BisGMA/HEAA/TMA- 46.7 ±15) showed no statistical difference, p>0.05. The experimental primer presented more acidity pH (2.7) and lower contact angle (18.5 ±5) when compared to commercial primer (pH- 4 e θ- 33.5 ±4). A new acrylamide based-primer was formulated and the presence of the new tris(methacrylamide) monomer (TMA) was enable the preparation of a 3-step etch-and-rise adhesive system without HEMA monomer.

Este trabalho apresenta os resultados de um estudo de caso (MINAYO, 1993, 2010; YIN, 2010), de abordagem qualitativa, realizado junto à Universidade Federal do Rio Grande do Sul, com o objetivo de identificar, sob a perspectiva de rito de passagem, como se dá a socialização dos ingressantes técnico-administrativos e que ações institucionais poderiam contribuir para consolidar o vínculo desses servidores. A pesquisa orientou-se pelo pressuposto de que as emoções afloradas durante a socialização de ingressantes na Administração Pública podem tanto contribuir quanto prejudicar a formação de vínculos afetivos, impactando, positiva ou negativamente, a identificação com a organização e o comprometimento com o trabalho. Assim, a socialização é contemplada como um reflexo da relação indissociável e interdependente entre indivíduo e sociedade, e a realidade social como um produto da socialização e da interação humana, em consonância com as concepções de Berger e Luckmann (2011), Cavedon (1990, 2000, 2010) e Setton (2010, 2011). Já a mudança de status, decorrente do ingresso no setor público, é tratada como um rito de passagem constituído de três fases, separação, margem e agregação, conforme teoriza Van Gennep (2011). Os dados foram coletados por meio de pesquisa documental, diários de campo, observação participante, questionários abertos, aplicados a ingressantes do concurso 2010, e entrevistas realizadas com servidores “antigos”, com apoio de um roteiro semi-estruturado. Os resultados sugerem que a fase de margem, correspondente ao estágio probatório de três anos, não é legitimada como um período de aprendizado, e, consequentemente, não há clara definição dos papéis de socializados (ingressantes) e socializadores (“antigos”). Existem expectativas de que os ingressantes adotem uma postura de humildade e deferência em relação aos “antigos”, e de que estes, por sua vez, assumam responsabilidades em relação ao aprendizado dos recém-chegados. Entretanto, em decorrência da indefinição de papéis, essas teatralizações, que são próprias da fase de margem, tendem a ser negligenciadas, causando conflitos que prejudicam o trabalho em equipe e o andamento do trabalho. A importação da lógica de mercado no serviço público também é evidenciada como origem de muitas das dificuldades identificadas, apontando para a necessidade de direcionar esforços visando uma conscientização nesse sentido. Como possível solução para os problemas levantados, sugere-se a realização de procedimentos ritualizados que reforcem o caráter de aprendizado da fase liminar, conduzidos por facilitadores designados e capacitados para tanto, que atuem como mediadores legitimados, em nível de unidade. Por fim, conclui-se que investimentos na socialização de recém-concursados são primordiais, podendo repercutir em maior comprometimento com o trabalho e melhores resultados em relação aos objetivos institucionais do que a implementação de mecanismos coercitivos de controle e de gestão do desempenho, característicos do modelo gerencialista que vêm se consolidando na administração pública desde o Plano Diretor da Reforma do Aparelho do Estado de 1995. / This work presents the results of a qualitative case study (MINAYO, 1993, 2010; YIN, 2010) that took place at the Federal University of Rio Grande do Sul with the aim of identifying, according to the perspective of rite of passage, how the socialization of the administrative staff is carried out and what institutional actions may contribute to the consolidation of organizational bonding. The research had its starting point in the assumption that newcomers who join the public sector experience emotions, triggered by socialization, that have the potential to either enhance or impair bonding processes, impacting identification with the organization and commitment to work in a positive or negative way. Thus, socialization is seen as a reflection of the inseparable and interdependent relation between individual and society whereas social reality is considered a by-product of socialization and human interaction, according to the conceptions of Berger and Luckmann (2011), Cavedon (1990, 2000, 2010) and Setton (2010, 2011). In its turn, the change of status caused by getting a job in the public sector is treated as a rite of passage that can be divided into three phases, separation, margin and aggregation, as theorized by Van Gennep (2011). The data was collected by means of documentary research, field journals, participant observation, open questionnaire applied to the newcomers of the 2010 selection process, and semi-structured interviews with senior level staff members. The results suggest that the margin phase, which corresponds to the three-year probationary period, is not legitimized as a learning period, therefore there‟s no clarity with regard to the different roles of “persons being socialized” and “agents of socialization”, to be respectively assumed by the newcomers and the senior level staff members. The newcomers should adopt a humble and respectful attitude towards their senior level colleagues, who, in turn, should undertake certain responsibilities in the learning process of the former. However, due to the lack of clearly defined roles and responsibilities, these expected theatrical-like behaviors tend to be neglected, leading to conflicts that disrupt teamwork and hinder the workflow. There‟s also evidence that the adoption of the market logic in the public sector may be the cause of many of the identified difficulties, which points to the need of directing efforts to raise awareness about this issue. A possible solution to the problems addressed by this research is the institutionalization of ritualized procedures designed to reinforce the learning-focused nature of the margin phase and conducted by properly trained facilitators, appointed to act as legitimate mediators in each decentralized unit. Finally, it is concluded that investments in the socialization of newcomers are essential and may yield stronger commitment to work and better results for the institution than the implementation of coercive mechanisms of performance management associated with the managerial model that has been consolidating itself in the public administration since the public sector reform of 1995.