No description available.

No description available.

see pdf

Bond strength is classically characterized into two separate factors; area of the bond and specific bond strength. This separation is especially important in pulps that lack strength properties, and are specifically used for their optical properties, such as mechanical pulps. In this research the applicability of the Ingmansson and Thode method for distinguishing between specific bonded area and specific bond strength in mechanical pulps is studied. It is shown that the rigid, non-collapsable, nature of the mechanical pulp can be overcome by press drying the sheets until they approach their 50% relative humidity moisture content. Mechanical pulps have been assumed to operate in a domain where fiber failure can be considered insignificant, and the bonded area to tensile strength relationship is linear. In this study it was shown that most commercial pulps operate in a significant fiber failure domain. However, it is shown that pure fines and fines rich mechanical pulp better follow a linear bonded area to tensile strength relationship rather than a non-linear (significant fiber failure) model, suggesting that only the fiber fraction undergoes fiber failure and the finer fractions predominantly bond failure. The Ingmansson and Thode method relies on the use of scattering coefficient as a measure of specific surface area. It is shown that scattering coefficient is an accurate estimate of mechanical pulp specific surface area at a constant wavelength of light, provided that the wavelength used to measure scattering coefficient is above the significant absorption limit.

This study first examined the kinetic changes of fiber carboxyl group content in bulk fiber, polysaccharide, and residual lignin of oxygen delignified pulps during one-stage oxygen delignification of a low kappa (32.5) kraft pulp. The carboxyl group contents determined in different chemical components of oxygen delignified pulps was used to establish the distribution of carboxyl groups in lignin and pulp polysaccharide and decouple the responses from residual lignin and polysaccharide. Following this study, two high kappa (~ 49.0) SW kraft pulps prepared were delignified through two-stage oxygen delignification. Fiber carboxyl group profiles of these pulps were elucidated to investigate the effect of lignin content of incoming unbleached kraft pulps on fiber carboxyl group formation. Due to a limitation to enhance fiber carboxyl groups only by parameter optimization during one- and two- stage oxygen delignification, a catalytic oxidation program was developed to enhance fiber carboxyl groups by 52.2 116.0 % employing 0.10 - 0.18% of a bismuth ruthenium pyrochlore oxide catalyst during oxygen delignification. The mechanism of fiber carboxyl group formation through the catalytic oxidation was proposed. The main factor on carboxyl group formation in pulp carbohydrate was identified to follow the order: NaOH > oxygen pressure> reaction temperature through a 3-factor at 3-level (L933) orthogonal experimental design and the optimal conditions were found at 2.5% NaOH, 85-100 oC, and 800-960 kPa O2 during the catalytic oxidation. ECF bleaching study was also conducted on these pulps with higher amount of fiber carboxyl group enhanced at early pulping and oxygen delignification processes. The bleaching results demonstrated that the early-stage enhanced fiber carboxyl groups were partially retained through ECF bleaching. Additionally, fiber carboxyl groups of fully bleached kraft pulps were ~ 20% different from typical bleaching protocols, depending on bleaching chemicals used and the bleaching sequences such as DEDED, (D+C)EDED, ODEDD, and OQPZP. This study finally demonstrated that an increase of fiber carboxyl groups by 17.4-62.1% through chemical oxidation resulted in reduced fiber curl, increased fiber WRVs, 4.3-25.5 % increase in paper tensile index at comparable pulp viscosity; and 4.4 -30.1% increase in paper dry tensile stiffness.

Orientador: Fernando Leite Hoffmann / Banca: Miyoko Jakabi / Banca: Crispin Humberto Garcia Cruz / Resumo: As frutas são constituintes importantes da dieta humana devido aos seus valores nutritivos e por satisfazerem os hábitos alimentares de grande parte dos consumidores. A polpa é o produto obtido por esmagamento das partes comestíveis de frutas carnosas por meio de processos tecnológicos adequados. As frutas com atividade de água (Aa) maior que 0,98 são muito susceptíveis à deterioração por bactérias, bolores ou leveduras. O desenvolvimento e o metabolismo microbiano exigem a presença de água numa forma disponível e a Aa é um índice desta disponibilidade. As polpas de frutas apresentam como características gerais: elevada Aa, potencial de óxido-redução positivo e baixo pH. Destes fatores a elevada acidez restringe a microbiota deterioradora, que se limita principalmente a bactérias lácticas e acéticas, bolores e leveduras; sendo que os dois últimos constituem os mais importantes agentes de deterioração de polpas e sucos de frutas. Neste trabalho objetivou-se avaliar a qualidade microbiológica de 62 amostras de polpas congeladas de frutas comercializadas na região de São José do Rio Preto - SP. Os resultados obtidos para coliformes termotolerantes e Salmonella spp revelaram que todas as amostras (100%) encontravam-se em conformidade com o padrão federal em vigor, sendo consideradas, portanto, "produtos em condições sanitárias satisfatórias". Foram ainda isoladas 136 leveduras, as quais foram submetidas, para identificação, aos testes taxonômicos (morfológicos, fisiológicos e de assimilação de fontes de carbono). Os resultados destes testes mostraram a ocorrência de 57 (41,90%) culturas classificadas como Saccharomyces cerevisiae, 24 (17,65%) Debaryomyces hansenii var. fabryi, 13 (9,55%) Dekkera bruxellensis, 13 (9,55%) Torulaspora delbrueckii, 6 (4,40%) Rhodotorula mucilaginosa, 4 (2,94%) Rhodotorula glutinis, 4 (2,94%) Trichosporon beigelii... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The fruits are important constituents of the human diet due to their nutritional values and because they satisfy the food habits of large number of the consumers. The fruit pulp is obtained by crushing the edible parts of fruits by right technological process. Fruits that have water activity (aw) over 0.98 are susceptible to deterioration by bacteria, molds and yeasts. The development and the microbial metabolism require the presence of water in an available way and aw is an indicator of this availability. Fruit pulps have the general characteristics: high aw, positive oxide - reduction potential and low pH. Of these factors the high acidity limits the decay agents, mainly to acetic and lactic bacteria, molds and yeasts; but molds and yeasts are the most important deterioration agents in fruit pulps and juices. In this study was evaluated the microbiological quality of 62 samples of fruit frozen pulps commercialized in the region of São José do Rio Preto - SP. The results obtained for fecal coliforms and Salmonella spp revealed that all samples (100%) were in accordance with the current federal standard, being considered therefore "products in satisfactory sanitary conditions". One hundred and thirty six yeasts were isolated from the samples, which were submitted, for identification, to taxonomic tests (morphological, physiological and to carbon sources assimilation). The results of the taxonomic tests showed the occurrence of 57 (41.90%) cultures classified as Saccharomyces cerevisiae, 24 (17.65%) Debaryomyces hansenii var. fabryi, 13 (9.55%) Dekkera bruxellensis, 13 (9.55%) Torulaspora delbrueckii, 6 (4.40%) Rhodotorula mucilaginosa, 4 (2.94%) Rhodotorula glutinis, 4 (2.94%) Trichosporon beigelii, 2 (1.47%) Hanseniaspora vineae, 2 (1.47%) Sporidiobolus johnsonii, 2 (1.47%) Candida apis, 1 (0.74%) Cryptococcus albidus, 1 (0.74%) Debaryomyces hansenii... (Complete abstract click electronic access below) / Mestre

Conselho Nacional de Desenvolvimento CientÃfico e TecnolÃgico / Nos Ãltimos anos o consumo de frutas tropicais tem aumentado, principalmente, devido aos seus benefÃcios para a saÃde, entre eles à baixa incidÃncia de doenÃas degenerativas. Esses benefÃcios sÃo atribuÃdos, em sua maioria, aos constituintes antioxidantes, como os compostos fenÃlicos e vitaminas. A rutina à um composto fenÃlico que possui vÃrias atividades biolÃgicas, tais como agentes antitumorais e propriedades antibacterianas. Com isso, o presente estudo objetivou avaliar a atividade antimicrobiana e antioxidante de extrato de rutina obtido de polpas e subprodutos de frutos tropicais encapsulado em matriz de goma do cajueiro. As frutas utilizadas foram: acerola, goiaba, manga e cajÃ-umbu. Elas foram despolpadas e caracterizadas fÃsico- e quimicamente. A polpa e o subproduto de acerola apresentaram maior atividade antioxidante total com 91,33 e 51,62 ÂM de Trolox. g-1, respectivamente. Sendo que os subprodutos de manga, goiaba e cajÃ-umbu obtiveram atividade antioxidante superior as suas respectivas polpas. A presenÃa de rutina foi observada em todas as polpas e subprodutos, sendo o subproduto de cajÃ-umbu o que obteve maior teor com 1852,40 Âg.g-1, seguido da polpa de acerola com 184,66 Âg.g-1. Esses extratos com maiores teores de rutina e rutina padrÃo (Sigma-Aldrich) foram encapsulados com goma do cajueiro. As nanopartÃculas formadas foram caracterizadas fisicamente e apresentaram tamanhos mÃdios variando de 174,20 nm a 907,60 nm. Ao avaliar o potencial antibacteriano, observou-se que a rutina e sua respectiva nanopartÃcula nÃo possuem essa propriedade contra as bactÃrias Eschechia coli, Salmonella Enteritidis, Staphylococcus aureus e Listeria monocytogenes na concentraÃÃo de atà 10 mg/mL. Os extratos de polpa de acerola (EPA) e subproduto de cajÃ-umbu (ESC) apresentaram atividade antibacteriana, sendo mais eficientes contra bactÃrias Gram-positivas. Os extratos nÃo encapsulados com goma do cajueiro foram mais efetivos do que os encapsulados. / In recent years the consumption of tropical fruits has increased, mainly due to its health benefits, including the low incidence of degenerative diseases. These benefits are awarded, mostly to the antioxidant constituents, such as phenolic compounds and vitamins. Rutin is a phenolic compound which possesses various biological activities such as antibacterial and antitumor agents. Thus, the present study aimed to evaluate the antimicrobial and antioxidant activities of extract rutin obtained from pulps and by-products of tropical fruits encapsulated array of cashew gum. The fruits used were: acerola, guava, mango and caja-umbu. They were pulped and characterized physico-chemically. The pulp and the by-product of acerola had higher total antioxidant activity with 91.33 and 51.62 mM Trolox. g-1, respectively. Since the by-products of mango, guava and caja-umbu had higher antioxidant activity their respective pulps. The presence of rutin was observed in all pulps and byproducts, and the byproduct of caja-umbu that obtained with higher content 1852.40 μg.g-1, followed of the pulp with 184.66 μg.g-1. These extracts with higher concentrations of rutin and standard rutin (Sigma-Aldrich) were encapsulated with cashew gum. The formed nanoparticles were characterized physically and showed average sizes ranging from 174.20 nm to 907.60 nm. In evaluating the antimicrobial activity, it was found that rutin and its respective nanoparticle do not have this property against bacteria Eschechia coli, Salmonella Enteritidis, Staphylococcus aureus and Listeria monocytogenes at a concentration of up to 10 mg / ml. The extracts of acerola pulp (EPA) and byproduct caja-umbu (ESC) showed antibacterial activity, being more effective against Gram-positive bacteria. Extracts not encapsulated with cashew gum were more effective than encapsulated.

A carbonatação acelerada é um processo químico que têm se tornado muito atrativa para a indústria do fibrocimento, por mitigar a degradação das fibras vegetais utilizadas nos materiais e por melhorar o desempenho físico-mecânico dos compósitos. Nesse contexto, o presente trabalho avaliou a influência da umidade no processo de carbonatação acelerada, em fibrocimentos reforçados com polpas celulósicas de eucalipto. Para o desenvolvimento das atividades experimentais foi realizado primeiramente um estudo da evolução da carbonatação nos compósitos de fibrocimento, considerando diferentes concentrações de umidade relativa (60, 70, 80 e 90%). Posteriormente, foi realizada a caracterização dos compósitos de fibrocimento por meio da avaliação do desempenho físico-mecânico, com ensaio mecânico de flexão em quatro pontos que determinou o módulo de ruptura (MOR), módulo elástico (MOE), limite de proporcionalidade (LOP) e energia específica (EE); e ensaios físicos para obtenção dos valores de absorção de água (AA), densidade aparente (DA) e porosidade aparente (PA). Os compósitos foram também avaliados quanto à durabilidade e microestrutura, através de ensaios de envelhecimento acelerado, composição mineralógica e análise microestrutural. A partir dos resultados obtidos, os compósitos carbonatados com 60% de umidade relativa apresentaram maior formação de carbonato de cálcio, maior densificação da matriz cimentícia e, consequentemente, menor quantidade de espaços vazios logo nas primeiras horas de carbonatação. Em relação ao desempenho dos compósitos de fibrocimento, as umidades de 60 e 70% permitiram que a carbonatação proporcionasse maiores valores de MOR, LOP e MOE, diferindo estatisticamente dos demais compósitos. Os ensaios físicos complementaram os ensaios mecânicos, mostrando que os compósitos carbonatados com 60 e 70% de umidade apresentaram menores valores de AA e PA, junto de maiores valores de DA. O processo de carbonatação acelerada foi favorecido pelas menores concentrações de umidade relativa, como apresentado também pelas análises de TG e DRX, que permitiram que o processo acontecesse de forma mais efetiva, melhorando a interface fibra-matriz. / The accelerated carbonation is a process that can be made very feasible for the fiber cement industry, for mitigating the degradation of the vegetable fibers used in the materials and for improving the physico-mechanical performance of composites. In this context, the present work evaluated the influence of relative humidity in the accelerated carbonation process in fiber cement composites reinforced with eucalyptus cellulosic pulps. For the development of experimental activities, a study of the evolution of carbonation in fiber cement composites was carried out, considering different concentrations of relative humidity (60, 70, 80 e 90%). Subsequently, the characterization of fiber cement composites was evaluated through the physical-mechanical performance evaluation, with a four-point mechanical test that determined the modulus of rupture, modulus of elasticity, limit of proportionality and specific energy; and physical tests to obtain the values of water absorption, bulk density and apparent void volume. The composites were also evaluated for durability and microstructure, through accelerated aging, mineralogical composition and microstructural analysis. From the results obtained, the carbonate composites with 60% relative humidity showed a higher calcium carbonate formation, a higher densification of the cementitious matrix and, consequently, a lower amount of voids in the first few hours of carbonation. In relation of the performance of fiber cement composites, the 60 and 70% humidity allowed the carbonation to provide higher values of mechanical analysis, differing statistically from the other composites. The physical tests complemented the mechanical tests, showing that the carbonated composites with 60 and 70% humidity presented lower values of water absorption and apparent void volume, with a greater filling of the empty spaces of the composites. The accelerated carbonation process was favored by the lower concentrations of relative humidity, as also shown by the TG and XRD analyzes, which allowed the process to happen more effectively, improving the fiber-matrix interface.

O aproveitamento de fibras de origem vegetal, como reforço de matrizes inorgânicas frágeis à base de cimento, é uma alternativa que tem despertado interesse ao redor do mundo pelas suas vantagens a nível econômico, social e ambiental. Porém, seu uso apresenta limitações em relação à baixa durabilidade apresentada por este material de reforço nos compósitos, refletida na perda de resistência das fibras celulósicas degradadas pelo ambiente alcalino da matriz e na instabilidade dimensional-volumétrica. Como alternativa para esse problema, pesquisas têm mostrado que é possível implementar mecanismos que modifiquem certas propriedades das fibras celulósicas antes de serem incorporadas como reforço na matriz cimentícia. Dentro desse contexto, este estudo aplicou e avaliou o efeito do tratamento de hornificação, que consta de quatro ciclos de secagem e umedecimento, sobre polpas celulósicas de eucalipto e pinus branqueadas e não branqueadas, como processo para otimizar as suas características e permitir uma maior durabilidade e desempenho dos compósitos de cimento reforçado. Foram determinadas e analisadas as características químicas, físico-mecânicas, morfológicas e microestruturais das polpas antes e após o processo de hornificação. Posteriormente, em uma segunda etapa do trabalho, foram produzidos compósitos cimentícios reforçados com polpas tratadas e não tratadas e realizada a avaliação de suas propriedades termo-físico-mecânicas, microestruturais e de durabilidade após cura térmica e 200 ciclos de envelhecimento acelerado. Os resultados indicam que o tratamento de hornificação nas fibras provocou a redução dos teores de retenção de água, não gerou diminuição significativa na viscosidade ou índice de cristalinidade e foram observadas mudanças morfológicas em relação ao colapso da fibra e maior rugosidade da sua superfície. Em relação ao desempenho das propriedades físicas dos compósitos com cura térmica ou após envelhecimento acelerado não foi identificada influência significativa das fibras de reforço tratadas, quando comparadas com não tratadas. Considerando as propriedades mecânicas, foram observadas melhorias na energia especifica de compósitos submetidos à cura térmica com fibras tratadas, destacando-se as polpas de eucalipto não branqueado tratadas como a fibra de reforço, com os melhores valores de energia especifica e módulo de ruptura. Após o ensaio de envelhecimento acelerado foi observado uma queda nas propriedades mecânicas de interesse dos compósitos para todos os tipos de fibras tratadas e não tratadas, indicando uma deterioração das polpas e perda da capacidade de reforço ao longo do tempo. Os resultados de condutividade térmica indicam que o fibrocimento com fibras hornificadas apresenta um desempenho térmico que favorece sua aplicação em coberturas de instalações zootécnicas. / The use of vegetable fibers as reinforcement of cement based inorganic matrices, is an alternative that has attracted attention around the world for its economic, social and environmental benefits. However, their use has limitations with respect to low-term reinforcement capacity in composites, reflected in the strength loss of cellulosic fibers which are degraded by the alkaline environment of the matrix and the volumetric-dimensional instability. As an alternative to this problem, several researches have showed that it is possible to implement mechanisms that modify certain properties of cellulosic fibers before their incorporation as cement matrix reinforcement. In this context, this study applied and evaluated the effect of the treatment of hornification, which consists of four drying and wetting cycles on bleached and unbleached eucalyptus and pine pulps, as a process to optimize their characteristics and allow a greater durability and performance of the reinforced cement composites. Chemical, physical-mechanical, morphological and microstructural characteristics of the pulp were determined and analyzed before and after hornification process. Later, in a second stage, cement composites reinforced with treated and untreated pulp were produced and the evaluation of its thermo-physical and mechanical properties, microstructural and durability after thermal curing and 200 cycles of accelerate aging ware assessed. The results indicate that the treatment of hornification on the fibers induced reduction of water retention values, did not cause significant decrease in viscosity or crystallinity index and morphological changes were observed regarding to the collapse of the fiber and its surface roughness increased. In relation to the physical properties of the composites with thermal curing or after accelerated aging not significant influence of treated reinforcing fibers was identified, when compared with untreated. Considering the mechanical properties improvements in specific energy was observed determined for composites subjected to thermal curing with treated fibers, highlighting the treated unbleached eucalyptus as reinforcing fiber, with the best specific energy and modulus of rupture values. After the accelerated aging a decrease in the mechanical properties of the composites was observed for all types of treated and untreated fibers indicating a deterioration of pulp and a loss of its capacity of reinforcement over time. The results of thermal conductivity indicated that the fibercements with hornificated fibers have a thermal performance that would favor its application in livestock roofing facilities.

O aproveitamento de fibras naturais como materiais de reforço em compósitos cimentícios é uma alternativa que apresenta potencial técnico, econômico, social e ambiental. Porém seu uso é limitado pela baixa durabilidade e estabilidade dimensional, refletidas na perda da capacidade de reforço das fibras em consequência da sua rápida degradação dentro da matriz de cimento. Para abordar esta situação, estudos ao redor do mundo mostraram que é possível aplicar tratamentos sobre as fibras e/ou matriz, modificando seu comportamento e obtendo resultados positivos. Dentro deste contexto, o presente estudo teve por objetivo aplicar e avaliar o efeito do tratamento de hornificação sobre polpas vegetais de eucalipto e pinus (não branqueadas) e do tratamento de carbonatação acelerada ou uso de adições pozolânicas sobre a matriz de cimento, alterando sua alcalinidade, buscando assim, maior durabilidade do material de reforço e otimizando o desempenho geral do compósito. Para atingir os objetivos propostos foram determinadas e analisadas propriedades físicas, morfologias e microestruturais das polpas antes e após do processo de hornificação. Posteriormente, em uma segunda etapa do trabalho, foram produzidos compósitos cimentícios com vistas em determinar o teor de reforço ótimo (6%, 8% e 10%) de polpas celulósicas (tratadas e não tratadas), curados por cura térmica sendo avaliados por meio da determinação de propriedades físico-mecânicas, microestruturais e de durabilidade. Seguidamente, em uma terceira etapa do trabalho, foram produzidos compósitos cimentícios com polpas celulósicas (tratadas e não tratadas) curados por carbonatação acelerada, sendo avaliados por meio da determinação de propriedades físico-mecânicas, microestruturais e de durabilidade. Na última etapa, foram avaliadas formulações de compósitos cimentícios reforçados com a polpa celulósica (tratada e não tratada) de melhor desempenho com adição de cinzas de casca de arroz ou resíduo de carvão ativado como material pozolânico, sendo avaliadas suas propriedades físico-mecânicas, microestruturais e de durabilidade. Os resultados obtidos permitem identificar que a hornificação gera modificações na estrutura interna das polpas reduzindo sua capacidade de absorção de água, estabilidade dimensiona, colapso do lúmen e incremento da rugosidade superficial sem ocasionar deterioração da sua estrutura ou componentes. No que concerne à influência da porcentagem de polpa de reforço aplicada, o desempenho das propriedades físico-mecânicas caiu proporcionalmente com o incremento da porcentagem de reforço, sendo este fenômeno acompanhado pela formação de aglomerações de polpas. Assim, os compósitos com 6% de reforço de polpas de eucalipto ou pinus se destacaram pelo desempenho. Em relação ao reforço com fibras hornificadas, foram obtidas melhoras no desempenho do módulo de ruptura e energia específica, com destacável conservação após do material ser envelhecido. Ao ser aplicada a cura por carbonatação acelerada sobre as matrizes, se obtiveram melhoras destacáveis na durabilidade das fibras e no desempenho mecânico antes e após do envelhecimento acelerado em relação aos compósitos curados por cura térmica. Estas melhoras foram mais representativas com o reforço de polpas hornificadas. O uso de substituição parcial do cimento por CCA mostrou o pior desempenho físico-mecânico. Por sua vez, a substituição de 25% de RCA permitiu alcançar melhoras no comportamento das propriedades físico-mecânicas das matrizes, especialmente com o reforço com a polpa hornificada. / The use of natural fibers as reinforcement materials in cement composites is an alternative that offers technical, economic, social and environmental potential. But their use is limited by its low durability and dimensional stability, reflected in a building capacity loss as result of its rapid degradation within the cement matrix. To address this situation, studies around the world show that it is possible to apply treatments on the fibers and/or the matrix, thus, modifying their behavior and obtaining positive results. Within this context, this study aimed to implement and evaluate the effect an hornification treatment on eucalyptus and pine kraft pulps (unbleached); and an accelerated carbonation treatment or use pozzolanic additions on the cement matrix that changes its alkalinity, seeking thus, greater durability of the reinforcing material, optimizing the overall performance of the composite. To achieve the proposed objectives, the physical, and microstructural morphologies of the pulps were determined and analyzed before and after the hornification process. Then, in a second stage of the work, cementitious composites were produced with a view to determining the optimal reinforcement content (6%, 8% and 10%) of cellulosic pulps (treated and untreated), cured by thermal curing, being evaluated by the determination of its durability, physical-mechanical and microstructure properties. Subsequently, in a third stage of the work, cementitious composites were developed with cellulose pulps (treated and untreated) and cured by accelerated carbonation, being evaluated by the determination of its durability, physical-mechanical and microstructure properties. In the last stage, formulations of cementitious composites reinforced with cellulose pulps (treated and untreated) of better performance were evaluated with the addition of rice husk ash (CCA) or activated coal mining waste (RCA) as pozzolanic material, being evaluated their physicomechanical, microstructural and durability properties. Therefore, we expected to obtain a cement matrix of low alkalinity and a reinforcing fiber with lower capacity for water absorption and higher dimensional stability, which acting together would achieve a superior mechanical performance as well as a longer durability over time. The obtained results allow to identify that the hornification generates modifications in the internal structure of the pulps reducing its capacity of water absorption, stability, lumen collapse and increase surface roughness without causing deterioration of its structure or components. Regarding the influence of the percentage of reinforcing pulp applied, the performance of the physical-mechanical properties fell proportionally with the increment of the reinforcement percentage, being this phenomenon accompanied by formation of agglomerations of pulps. Thus, the composites with 6% reinforcement of pulps of eucalyptus or pinus stood out by the performance. In relation to the reinforcement with hornificated fibers, the performance of the modulus of rupture and specific energy were obtained, with detachable conservation after the material was aged. When accelerated carbonatation curing was applied to the matrices, the durability of the fibers and the mechanical performance before and after the accelerated aging were obtained in relation to the heat curing composites. These improvements were more representative with the reinforcement of hornified pulps. The use of partial cement substitution by CCA showed the worst physicomechanical performance. On the other hand, the substitution of 25% or RCA allowed to achieve improvements in the behavior of the physical-mechanical properties of the matrices, especially with the reinforcement with the hornified pulp.