Submitted by Claudia Rocha (claudia.rocha@udesc.br) on 2017-12-15T11:25:42Z No. of bitstreams: 1 PGEF17MA082.pdf: 2704849 bytes, checksum: 402c8ed2d802138ba830b989401226b5 (MD5) / Made available in DSpace on 2017-12-15T11:25:42Z (GMT). No. of bitstreams: 1 PGEF17MA082.pdf: 2704849 bytes, checksum: 402c8ed2d802138ba830b989401226b5 (MD5) Previous issue date: 2017-04-28 / FAPESC / The use of the fiber reinforcement in structural elements of Glued Laminated Timber (Glulam) is advantageous because of increase its strength and stiffness. However, few studies have evaluated the performance of reinforcement on finger joints, which, even under excellent manufacturing conditions, shows less strength than solid wood, making this kind of joint one of the main weaknesses of Glulam. In this context, the present dissertation aims to evaluate the performance of reinforcement with fibers in finger-joints for use in Glulam. The performance analysis was developed under two aspects: (i) the tensile strength parallel to grain performance in two geometries, "A" and "B", on joints, with three reinforcement compositions, "Glass", "Glass2" and "Carbon", in two species of wood, Pinus taeda and Eucalyptus spp. and (ii) the performance of Glulam beams of Eucalyptus spp. with three reinforcement compositions, "Glass", "Glass2" and "Carbon", in tensile strength parallel to grain, normal tensile, strength to shear and three points bending test. All tests were performed according to the guidelines of NBR 7190/1997, using the Scott-Knott and Tukey tests for statistical analysis with 95% of confidence interval. The results show that the finger-joints, even within normative requirements, significantly reduces (up to 43%) the tensile strength parallel to grain, regardless of geometry or species. For the samples of Eucalyptus spp., the treatments "B-Glass2", "B-Carbon" and "A-Glass2" presented average strength equivalent to solid wood. For specimens of P. taeda, the treatments with the same performance as solid wood were "A-Glass2", "A-Carbon", "B-Glass2", "B-Carbon" and "B-Glass". It can be concluded that the application of two layers of reinforcement of glass fibers or one layer of carbon, concentrated in the region of the finger-joints with the geometry B, increases significantly (in up to 71% for P. taeda and 25% for Eucalyptus spp. in the treatments with better performance) the tensile strength parallel to grain in both species evaluated. It was also concluded that the apparent densities (Pinus taeda ρap,m= 0.49 and Eucalyptus spp. ρap,m= 0.60) show poor correlation with the tensile strength parallel to the fibers. The performance of the glulam beams of Eucalyptus spp. did not present significant differences for the evaluation of the bonding lines. However, in the flexural strength, the treatments "Glass 2" and "Carbon" were significantly superior to the glulam beams without reinforcement, reaching at increments of 37.8% and 40.5%, respectively, in the bending strength. The modulus of elasticity did not differ significantly among. It was observed that the mode of rupture was by tensile in the finger-joints region in all the beams evaluated in bending test, however, the bending strengths were higher than tensile strengths parallel to grain, indicating influence of the thickness of the blades and thickness of the reinforcements in the performance of the reinforced finger-joints. In this way, it is possible to conclude that the application of concentrated reinforcement in finger-joints significantly improves the performance of glulam beams of Eucalyptus spp. to bending, as well as the tensile strength parallel to grain for P. taeda / A aplicação de reforço com fibras em elementos estruturais de Madeira Laminada Colada (MLC), na linha de colagem de maior esforço, se apresenta de maneira vantajosa por aumentar sua resistência mecânica e sua rigidez. Todavia, poucos estudos avaliam o desempenho do reforço sobre as emendas longitudinais, que, mesmo em condições excelentes de manufatura, têm resistência menor que a da madeira maciça, tornando as emendas um dos principais pontos de fragilidade da MLC. Nesse contexto, a presente dissertação tem por objetivo avaliar o desempenho do reforço com fibras em emendas por entalhes múltiplos (finger-joints) para utilização em MLC. A análise de desempenho foi desenvolvida sob dois aspectos: (i) desempenho à tração paralela às fibras de duas geometrias, “A” e “B”, para emendas, com três composições de reforço, “Vidro”, “Vidro2” e “Carbono”, em duas espécies de madeira, o Pinus taeda e o Eucalyptus spp. e (ii) o desempenho de vigas em MLC de Eucalyptus spp.com três composições de reforço, “Vidro”, “Vidro2” e “Carbono” quanto à resistência à tração paralela às fibras, tração perpendicular às fibras, cisalhamento e flexão estática. Todos os ensaios foram executados de acordo com as diretrizes da NBR 7190/1997, sendo empregados os testes de Scott-Knott e Tukey para as análises estatísticas com 95% de confiabilidade. Os resultados mostram que as emendas por entalhes múltiplos, mesmo dentro dos referenciais normativos, diminuem significativamente (em até 43%) a resistência à tração paralela às fibras, independentemente da geometria ou da espécie utilizada. Para as amostras de Eucalyptus spp., os tratamentos “B-Vidro2”, “B-Carbono” e “A-Vidro2” apresentaram resistência mecânica média equivalente à madeira maciça. Para as amostras de P. taeda, os tratamentos com desempenho mecânico similar à madeira maciça foram “A-Vidro2”, “A-Carbono”, “B-Vidro2”, “B-Carbono” e “B-Vidro”. Pode-se concluir que a aplicação em duas camadas de reforço de fibras de vidro ou uma camada de carbono, ambos concentrados na região das emendas por entalhes múltiplos com a geometria B, aumenta significativamente (em até 71% para o P. taeda e 25% para o Eucalyptus spp. nos tratamentos com melhor desempenho) a resistência à tração paralela às fibras em ambas espécies avaliadas. Conclui-se ainda que a densidade aparente (P. taeda ρap,m= 0,49 e Eucalyptus spp. ρap,m =0,60 ) apresenta fraca correlação com a resistência à tração paralela às fibras. O desempenho mecânico das vigas MLC de Eucalyptus spp. não apresentou diferenças significativas para a avaliação das linhas de colagem. Entretanto, na resistência à flexão estática, os tratamentos “Vidro 2” e “Carbono” foram significativamente superiores às vigas MLC sem reforço, chegando a incrementos de 37,8% e 40,5%, respectivamente, à flexão estática. Os módulos de elasticidade não diferiram significativamente entre si. Foi constatada ruptura por tração na região das emendas em todas as vigas avaliadas à flexão estática, entretanto as resistências à flexão foram superiores às resistências à tração paralela às fibras, indicando influência da espessura das lâminas e da espessura dos reforços no desempenho mecânico das emendas reforçadas. Desta forma, é possível concluir que a aplicação de reforço concentrado na região das emendas por entalhes múltiplos melhora, significativamente, o desempenho de vigas MLC de Eucalyptus spp. à flexão, bem como a resistência à tração paralela às fibras para o P. taeda

O presente trabalho tem por finalidade estudar e implementar um modelo numérico de análises cinemáticas de sólidos tridimensionais via método dos elementos finitos posicionais, com consideração de fibras longas ou curtas inseridas de maneira aleatória ou não no domínio da análise. O modelo numérico considera material isotrópico para a matriz e não linearidade geométrica. O domínio do sólido é discretizado por meio de elementos finitos tetraédricos de ordem qualquer, cujos parâmetros nodais são suas posições. A medida de deformação utilizada é a de Green, associada à lei constitutiva de Saint-Venant-Kirchhoff, referenciada pela configuração inicial do corpo, caracterizando o sistema de espaço como Lagrangiano total. O cálculo da posição de equilíbrio é baseado no princípio da mínima energia potencial total. Para a resolução do problema não linear geométrico, adota-se o método iterativo de Newton-Raphson. A inserção das fibras no domínio da análise é feita com a associação das mesmas com elementos finitos unidimensionais curvos de ordem qualquer, cujas posições nodais são dadas em função das posições dos nós dos elementos de sólido. Essa abordagem tem como vantagem o fato de não aumentar o número de graus de liberdade do sistema, ao mesmo tempo em que não limita as posições das fibras dentro do domínio por não ser necessária a coincidência das malhas. Exemplos são apresentados para validação dos desenvolvimentos e implementações realizadas. / This study aims to develop and implement a numerical model of kinematic enrichment, to analyze tridimensional solids based on positional finite element method, considering long and short fibers random distributed inside the domain. The numerical model considers isotropic material and geometric nonlinear behavior for both matrix and fibers. Tetrahedral finite elements with any order of approximation are used to discretize the solid domain, with positions as nodal parameters. Green strain and Saint-Venant-Kirchhoff constitutive law are used, referenced in initial configuration of the body, characterizing the developed formulation as total Lagrangian. The equilibrium is obtained with the application of Total Potential Energy Principle, adopting the Newton-Raphson method to solve the resulting nonlinear system of equations. The fibers are considered in the formulation using curved one-dimensional finite elements with any order of approximation, and the nodal positions of the fibers are related with the nodal positions of the solid elements. The coupling method adopted does not increase the number of degrees of freedom of the system, and does not limit the positions of the fiber nodes to be coincident with solid nodes. Examples are presented in order to validate the developed and implemented formulations.

De modo a satisfazer aspectos de resistência, custo ou conforto, o aperfeiçoamento do desempenho das estruturas é uma meta sempre almejada na Engenharia. Melhorias têm sido alcançadas dado ao crescente uso de materiais compósitos, pois estes apresentam propriedades físicas diferenciadas capazes de atender as necessidades de projeto. Associado ao emprego de compósitos, o estudo da plasticidade demonstra uma interessante alternativa para aumentar o desempenho estrutural ao conferir uma capacidade resistente adicional ao conjunto. Entretanto, alguns problemas podem ser encontrados na análise elastoplástica de compósitos, além das próprias dificuldades inerentes à incorporação de fibras na matriz, no caso de compósitos reforçados. A forma na qual um compósito reforçado por fibras e suas fases têm sua representação e simulação é de extrema importância para garantir que os resultados obtidos sejam compatíveis com a realidade. À medida que se desenvolvem modelos mais refinados, surgem problemas referentes ao custo computacional, além da necessidade de compatibilização dos graus de liberdade entre os nós das malhas de elementos finitos da matriz e do reforço, muitas vezes exigindo a coincidência das referidas malhas. O presente trabalho utiliza formulações que permitem a representação de compósitos reforçados com fibras sem que haja a necessidade de coincidência entre malhas. Além disso, este permite a simulação do meio e do reforço em regime elastoplástico com o objetivo de melhor estudar o real comportamento. O modelo constitutivo adotado para a plasticidade é o de von Mises 2D associativo com encruamento linear positivo e a solução deste modelo foi obtida através de um processo iterativo. A formulação de elementos finitos posicional é adotada com descrição Lagrangeana Total e apresenta as posições do corpo no espaço como parâmetros nodais. Com o intuito de averiguar a correta implementação das formulações consideradas, exemplos para validação e apresentação das funcionalidades do código computacional desenvolvido foram analisados. / In order to satisfy strength, cost or comfort aspects, the improvement of the structural performance is a mark always desired in Engineering. Progress has been achieved due to the use of composite materials, because these present different physical properties capable of attending the needs of projects. Associated to the use of composites, the study of plasticity presents an interesting alternative to raise the structural performance by providing an additional resistance capability to the set. However, some problems may be found in the elastoplastic analysis of composites, besides the inherent difficulties of fiber insertion in the matrix, in the case of fiber reinforced composites. The way that the fiber reinforced composite and its phases are represented and simulated are of extreme importance to assure that the obtained results are compatible to the reality. As more refined models are developed, problems arise concerning computational cost and the need of compatibilization of the degrees of freedom between the nodes of the mashes of the matrix and the reinforcement, many times demanding the coincidence of the refered meshes. The present work utilizes formulations that allow the representation of the fiber reinforced composite without the need of mesh coincidence. It also enables the simulation of the medium and the reinforcement at the elastoplastic regime, with the objective study better the real behaviour. The constitutive model for the plasticity adopted is the von Mises 2D associative with a positive linear hardening and the solution of this model was obtained through an iterative procedure. The positional finite element method is adopted with a Total Lagrangean description and uses the positons of the body in space as nodal parameters. With the aim to ensure the correct implementation of the considered formulations, examples for validation and presentation of the functionalities of the developed computacional code were analized.

A utilização de fibras vegetais como reforço constitui um grande interesse na obtenção de novos materiais para a construção civil produto de seu baixo custo, alta disponibilidade e reduzido consumo de energia para sua produção. Este trabalho avalia a incorporação de fibras de sisal, de comprimento 20 e 40 mm, e fração volumétrica de 0,5 e 1%, em concretos para a alvenaria de blocos estruturais e determina o uso destas unidades na execução de prismas e mini-paredes. Foram realizados os testes de caracterização da fibra, blocos e argamassa de assentamento e os ensaios de resistência à compressão axial das unidades, prismas e mini-paredes. O sisal apresentou baixa massa específica aparente e elevada absorção de água, constituindo uma característica comum desse tipo de material pela grande incidência de poros permeáveis. As propriedades físicas dos blocos com e sem adição cumpriram com os requisitos das normas estabelecidas validando sua utilização. Os resultados do ensaio à compressão mostraram que as mini-paredes reforçadas com fibras obtiveram valores muito próximos ou mesmo superiores aos obtidos para as mini-paredes sem fibras, apresentando melhor desempenho que os blocos e prismas. Todos os elementos com adição mostraram um ganho da capacidade de deformação e ductilidade conferida pelas fibras, observado nas curvas tensão x deformação. O modo de ruptura dos blocos, prismas e mini-paredes de referência foi caracterizado por uma fratura brusca e catastrófica e os reforçados mantiveram suas partes unidas pelas fibras, não perdendo sua continuidade e tornando a ruptura um processo progressivo. / The use of natural fibers as reinforcement is a great interest in obtaining new materials for construction, owing of its low cost, high availability and reduced energy consumption for its production. This paper evaluates the incorporation of sisal fibers of 20 mm and 40 mm length and volume fraction of 0.5 and 1%, for concrete for masonry structural blocks, and determines the use of these units in making of prisms and mini-walls. The laboratory tests were carried to characterize physical properties the fiber, blocks and mortar, and besides axial compression tests of the units, prisms, and mini-walls. The sisal had low apparent density and high water absorption, constituting a common feature of such material by the high incidence of permeable pores. The physical properties of the blocks with and without addition complied with the requirements of standards established by validating their use. The axial compression test results showed that mini-walls reinforced with fibers obtained values very close to or even superior to those obtained for the mini-walls without fibers, showing better performance than the blocks and prisms. All elements with the addition had increased the deformation capacity and ductility afforded by the fibers, observed in the curves stress/strain. The rupture mode of blocks, prisms and mini-walls reference was characterized by an abrupt and catastrophic fracture, and elements reinforced maintained their shares together by the fibers, without losing its continuity and becoming a progressive rupture.

Orientador: Marco-Aurelio De Paoli / Tese (doutorado) - Universidade Estadual de Campinas, Instituto de Quimica / Made available in DSpace on 2018-08-06T15:37:34Z (GMT). No. of bitstreams: 1 Morita_AugustoTeruo_D.pdf: 5448584 bytes, checksum: b45ea2a6a097d79180fbd6e43996e982 (MD5) Previous issue date: 2006 / Resumo: O objetivo deste trabalho foi preparar placas e parafusos auto-reforçados a partir do copolímero poli(L/DL ácido láctico), para serem utilizados na fixação interna rígida de fraturas. Este copolímero pode ser hidrolisado quando inserido no corpo humano e seus produtos de degradação são expelidos através do ciclo metabólico. Foi construído um aparelho de autoreforçamento que deve ser acoplado a uma Máquina Universal de Ensaios, capaz de orientar uniaxialmente amostras poliméricas através da passagem por uma matriz aquecida de dimensões menores que a amostra. Foram realizados ensaios prévios de auto-reforçamento com amostras de poliestireno. Ensaios de auto-reforçamento com o copolímero poli(L/DL ácido láctico) mostraram que o auto-reforçamento induziu um aumento nas propriedades mecânicas, medidas sob flexão, de ~60% no módulo de elasticidade e de ~90% na tensão máxima. A amostra moldada apresentou linhas brancas quando dobrada a temperatura ambiente, indicando a fragilização. Por outro lado, as amostras auto-reforçadas podem ser dobradas a temperatura ambiente sem que ocorresse ruptura frágil ou fragilização. Através de ensaios de difração de raios-X determinou-se que a amostra é semi-cristalina após o auto-reforçamento, apesar dos ensaios de calorimetria diferencial de varredura não identificarem positivamente a formação desta estrutura semi-cristalina. A esterilização por raios-g causa uma grande queda na massa molar, porém não altera as propriedades mecânicas. Ensaios de degradação in-vitro, com solução tampão de fosfato numa temperatura de 37 °C, das amostras esterilizadas mostraram que a massa molar sofre uma queda durante todo o ensaio de degradação e as propriedades mecânicas sofrem uma pequena queda após 15 semanas. As amostras auto-reforçadas podem ser usinadas na forma de placas e parafusos. As placas usinadas do copolímero de poli(ácido láctico) ainda podem ser dobradas a temperatura ambiente sem que ocorra quebra ou formação de linhas brancas / Abstract: In this work self-reinforced plates and screws to be used for rigid internal fixation of fractures were produced using the poly(L/DL-lactic acid) copolymer. This copolymer can be hydrolyzed when implanted in the human body and its degradation products are expelled by the metabolic cycle. A self-reinforcement module was built. It can be attached to a Universal Mechanical Testing Machine, which is capable to uni-axially orient the polymeric sample though a heated die. Initial tests of processing and self-reinforcement were conducted with polystyrene. Self-reinforcement tests were conducted with the poly(L/DL-lactic acid) copolymer. The results show that the die-drawing process induced an increase in the flexural mechanical properties of ~60% in the elastic modulus and of ~90% in the maximum tension, both measured under flexion conditions. White lines (crazing) appears when the molded sample was bent at ambient temperature, whereas the self-reinforced sample could be bent in the same conditions without fracture or sample fragilization. X-ray diffraction results indicated that the self-reinforced sample exhibits a semi-crystalline structure; notwithstanding the differential scanning calorimetry results do not conclusively identify the sample morphology. g-rays sterilization caused a decrease in the molar mass, but the mechanical properties were not affected. In-vitro degradation test were conducted at 37 °C in a buffered aqueous solution. Sterilized samples show a larger decrease in the molar mass since the beginning of the test, but the mechanical properties exhibits a smaller decrease during the test. The self-reinforced samples can be molded to the form of plates and screws. The final sample could be bent at ambient temperature without fragilization / Doutorado / Quimica Inorganica / Doutor em Ciências

Submitted by Marlene Santos (marlene.bc.ufg@gmail.com) on 2016-09-21T13:42:33Z No. of bitstreams: 2 Dissertação - Letícia Nunes de Almeida - 2016.pdf: 4956536 bytes, checksum: ff3b7edcf1cb8b45c40f2292cb032676 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Approved for entry into archive by Luciana Ferreira (lucgeral@gmail.com) on 2016-09-21T13:45:21Z (GMT) No. of bitstreams: 2 Dissertação - Letícia Nunes de Almeida - 2016.pdf: 4956536 bytes, checksum: ff3b7edcf1cb8b45c40f2292cb032676 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Made available in DSpace on 2016-09-21T13:45:21Z (GMT). No. of bitstreams: 2 Dissertação - Letícia Nunes de Almeida - 2016.pdf: 4956536 bytes, checksum: ff3b7edcf1cb8b45c40f2292cb032676 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Previous issue date: 2016-02-25 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / The pre-heating and post-curing can improve the mechanical properties of composites, even though there be no studies of fiber reinforced composites. The aim of this study was to evaluate the effect of pre-heating and post-curing autoclave and microwave in flexural strength (FS), diametral tensile strength (DTS), knoop microhardness (KHN) and degree of conversion (DC) of a experimental fiber- reinfoced composite. The experimental material was prepared with 30% glass fibers (3 mm), 22.5% of the resin matrix (40/60 Bis-GMA / TEGDMA) and 47.5% barium silicate particles. Six experimental groups were created by the interaction between the factors under study: heating, on two levels (without heating and heating at 60°C) and post-curing in 3 levels (conventional curing without post-curing, autoclave (120°C for 15 minutes) and microwaves (540 W for 5 minutes) The groups were: F - curing at 1500 mW/cm2 for 40 seconds; F + M - curing and post- polymerization in microwave; F + A - curing and post-curing in an autoclave , AQ + F - the composite heating prior to curing, AQ + F + M - heating prior to curing and post-curing in microwave;. AQ + F + A - heating prior to curing and post-curing and autoclave heating was conducted digital oven for 5 minutes at 60°C. Ten samples of the RF dimensions 25 x 2 x 2 mm and DTS in dimensions of 3 x 6 mm were tested in a universal testing machine Instron 5965, 0.5 mm/min. the KHN test was performed on samples of 3 x 6 mm with a load of 50 g for 30 sec, totaling 50 indentations per group. GC was obtained by Spectroscopy Fourier Transform Infrared (FTIR) on 5 samples. Data were analyzed by a factorial 2x3 and general linear model ANOVA and Tukey tests (α = 0.05). Factor analysis showed significant interaction between the factors just for RTD (p = 0.0001); preheating was significant factor for RF (p = 0.0001), RTD (p = 0.020) and KHN (p = 0.0001); post-curing factor for KHN was significant (p = 0.0001). ANOVA and Tukey tests showed statistically significant differences between groups for DTS (p = 0.001: AQ + F ≥ AQ + F + M = F + A = AQ + F + A = F + M ≥ F), FS (p = 0.016: AQ + F + M ≥ AQ + F + A + F = AQ = AQ + A + M ≥ F ≥ F) and KHN (p = 0.0001: AQ + F + M ≥ AQ + A + F = F = F + A + M ≥ F ≥ M + AQ). GC results showed no statistically significant difference. Through the Pearson correlation coefficient was observed significant positive correlation between the GC and RTD (r = 0.473, p = 0.008) and between DTS and FS (r = 0.263, p = 0.042). The pre-heating and post- polymerization were shown to be favorable to promote better mechanical properties of fiber reinforced composite by studied, specific for each property being analyzed. / O aquecimento prévio à polimerização e a pós-polimerização podem melhorar propriedades mecânicas em compósitos, embora inexistam estudos em compósitos reforçados com fibra. O objetivo deste estudo foi avaliar o efeito do pré- aquecimento e da pós-polimerização em autoclave e microondas na resistência flexural (RF), resistência à tração diametral (RTD), microdureza knoop (KHN) e grau de conversão (GC) de um compósito experimental reforçado por fibra de vidro. O material experimental foi confeccionado com 30% de fibras de vidro (3 mm), 22,5% de matriz resinosa (40/60 Bis-GMA/TEGDMA) e 47,5% de partículas de silicato de bário. Seis grupos experimentais foram criados pela interação entre os fatores em estudo: aquecimento, em dois níveis (controle sem aquecimento e aquecimento a 60oC) e pós-polimerização, em 3 níveis (fotopolimerização convencional sem pós- polimerização, autoclave (120oC por 15 minutos) e microondas (540 W por 5 minutos). Os grupos foram: F - fotopolimerização à 1500 mW/cm2 por 40 segundos; F+M - fotopolimerização e pós- polimerização em microondas; F+A - fotopolimerizacão e pós-polimerização em autoclave; AQ+F - aquecimento do compósito previamente à fotopolimerização; AQ+F+M - aquecimento previamente à fotopolimerização e pós-polimerização em microondas; AQ+F+A - aquecimento previamente à fotopolimerização e pós-polimerização e autoclave. O aquecimento foi realizado em estufa digital por 5 minutos a 60oC. Dez amostras de RF nas dimensões de 25 x 2 x 2 mm e de RTD nas dimensões de 3 x 6 mm foram testadas em máquina de ensaio universal Instron 5965, a 0,5mm/min. O teste de KHN foi realizado em amostras de 3 x 6 mm com carga de 50 g por 30 s, totalizando 50 indentações por grupo. O GC foi obtido através de Espectroscopia de Infravermelho por Transformada de Fourrier (FTIR) em cinco amostras. Os dados foram analisados por um modelo linear geral fatorial 2x3 e testes de ANOVA e Tukey (α=0,05). A análise fatorial mostrou interação significativa entre os fatores apenas para RTD (p=0,0001); o fator pré-aquecimento foi significante para RF (p=0,0001), RTD (p=0,020) e KHN (p=0,0001); o fator pós-polimerização foi significante para KHN (p=0,0001). Os testes de ANOVA e Tukey mostraram diferença estatística entre os grupos para RTD (p = 0,001: AQ+F ≥ AQ+F+M = F+A = AQ+F+A = F+M ≥ F), RF (p = 0,016: AQ+F+M ≥ AQ+F+A = AQ+F = AQ+A ≥ F+M ≥ F) e KHN (p = 0,0001: AQ+F+M ≥ AQ+F+A = F+A= F+M ≥ AQ+F ≥ F). Os resultados de GC não apresentaram diferença estatisticamente significante. Através do coeficiente de correlação de Pearson foi possível observar correlação positiva significante entre o GC e RTD (r = 0,473, p = 0,008) e entre RTD e RF (r = 0,263, p = 0,042) . O pré- aquecimento e a pós-polimerização mostraram-se favoráveis para promover melhores propriedades mecânicas do compósito reforçado por fibra estudado, sendo específicos para cada propriedade analisada.

É cada vez maior a utilização de polímeros reforçados com fibra de vidro no mercado nacional. Entre eles utiliza-se a poliamida 6 que apresenta ótima resistência à tração, ao impacto e à absorção de umidade comparada à poliamida 6 sem reforço de fibra de vidro, sendo atualmente utilizada na indústria automobilística em peças sob o capô, em especial em carcaças de radiadores. Este trabalho foi realizado com o objetivo de estudar o efeito da radiação ionizante nas propriedades mecânicas (resistência à tração, à flexão e ao impacto Izod) e térmicas (resistência ao fio incandescente e temperatura de fusão) da poliamida 6 com reforço de fibra de vidro, submetida à diferentes doses de radiação (100 a 600 kGy). As amostras foram preparadas e irradiadas em um acelerador JOB 188 com feixe de elétrons de energia de 1,5 MeV em diferentes doses e uma taxa de dose de 22,61 kGy/h. Após a irradiação, as propriedades das amostras da poliamida 6 com reforço de fibra de vidro irradiada foram determinadas e comparadas com as amostras não irradiadas e constatou-se que as propriedades mecânicas de resistência à flexão e à tração aumentaram e a de resistência ao impacto diminuiu. Em relação à propriedade térmica de temperatura de fusão diminuiu de 224,4ºC para 212,5ºC mas a perda de massa diante do aumento constante da temperatura também diminuiu. Em relação à propriedade de resistência ao fio incandescente a poliamida 6 com reforço de fibra de vidro irradiada teve um bom desempenho. As imagens captadas por Microscopia Eletrônica de Varredura mostram que a irradiação provocou uma boa integração entre a fibra de vidro e o polímero o que foi responsável pelo bom desempenho na propriedade de resistência ao fio incandescente. / It is each time more common the use of polymers reinforced with fibreglass in the domestic market. Between them it is used polyamide 6 that it presents good tension resistance, to the impact and the humidity absorption compared with non-reinforced, being also at the present time used in the automobile industry in parts underneath the hood, especially in the radiator frames. The aim of this work is to study the effect of ionizing radiation on properties of polyamide 6 with fibreglass reinforcement, undergone to different radiation doses. Samples were prepared and irradiated on JOB 188 accelerator with an electron beam energy of 1.5 MeV in air with different doses (100 to 600 kGy) and a dose rate of 22.61 kGy/h. Afterward the irradiation, the properties of the samples of irradiated polyamide 6 with fibreglass reinforcement were evaluated and compared with the samples non-irradiated. It evidenced that the mechanical properties flexural resistance and tension resistance increased and the resistance to the impact decreased. Regarding the thermal properties of the temperature of fusing decreased of 224,4ºC for 212,5ºC but the loss of mass ahead of the constant increase of the temperature also decreased. In the property of resistance to the glow wire the polyamide 6 with fibreglass reinforcement had a good performance. The images caught for Scanning Electronic Microscopy show that the irradiation provoked a good integration enters the fibreglass and polymer what was responsible for the good performance in the property of resistance to the glow wire.

Os objetivos deste estudo foram: 1) avaliar a resistência à flexão em três pontos de um compósito para uso direto (Filtek Z350 XT, 3M ESPE) e um para uso indireto (Signum, Heraeus, Kulzer) reforçados por uma ou duas camadas de fibras de polietileno (Ribbond -THM, Ribbond®) ou de vidro (Interlig, Ângelus) tratados termicamente (170°C por 10 minutos), comparados com os grupos controle (não reforçados por fibras e/ou não tratados termicamente; 2) avaliar a sorção, a solubilidade e a estabilidade de cor dos compósitos reforçados, após armazenamento em água destilada à 37°C por 14 dias. A estabilidade de cor foi avaliada com auxílio de um espectrofotômetro de contato dental (Vita EasyShade, Vident, CA, USA). Para o ensaio de resistência à flexão, foram confeccionados espécimes retangulares com dimensões de 12 x 2 x 2mm (n=10), com os seguintes fatores de variação: a) compósito (para uso direto ou indireto); b) tipo e número de camadas de fibras (vidro ou polietileno/uma ou duas camadas); c) submetidos ou não a tratamento térmico. O tratamento térmico foi realizado 24 horas após fotoativação em estufa à temperatura de 170°C por 10 minutos. O ensaio foi realizado 24 horas após fotoativação ou tratamento térmico. Para avaliação de sorção/solubilidade e estabilidade de cor, foram confeccionados espécimes em forma de disco com dimensões de 15 x 2mm (n=5), em que foram analisados os seguinte fatores: a) compósito (para uso direto ou indireto); b) tipo de fibra (vidro ou polietileno); c) número de camadas de fibras (uma ou duas). Foi realizada análise dos parâmetros de cor antes e após imersão em água deionizada por 14 dias. Os resultados foram analisados por ANOVA e teste de contraste de Tukey, com nível de significância de 5% e revelaram que a fibra de vidro, quando utilizada em duas camadas, propiciou os maiores valores de resistência à flexão para os dois compósitos testados (165,4 MPa Z350XT e 208,7MPa Signum ). O tratamento térmico não apresentou significância estatística quanto à resistência à flexão do compósito direto. Para o compósito para uso indireto (Signum ) foi encontrada diferença estatisticamente significante para o fator tratamento térmico, que indicou valores de resistência à flexão inferiores para os grupos tratados termicamente. O compósito para uso direto apresentou valor de sorção superior (33,6/cm3) ao do compósito para uso indireto (19,1/cm3). Para solubilidade, foi encontrada interação para os fatores compósito e tipo de fibra, indicando maiores valores para o compósito para uso direto associado à fibra de vidro. A análise de alteração de cor demonstrou maior valor de E para a fibra de polietileno (E =1,5) quando comparado à fibra de vidro (E=1,0). Concluiu-se que: 1) a adição de fibras propicia aumento dos valores de resistência à flexão de compósitos para uso direto e indireto, o aumento da resistência foi observado quando do uso de duas camadas de fibras; 2) o tratamento térmico à 170°C por 10 minutos não indicou melhora nas propriedades mecânicas dos compósitos reforçados; 3) adicionar fibras aos compósitos não aumentou os valores de sorção/solubilidade quando imersos em água; 4) Imersão em água não produziu alterações de cor relevantes para os compósitos reforçados com fibras se comparados aos sem fibras. / The aims of this study were: 1) to evaluate the flexural strength of one composite for direct use (Filtek Z350 XT, 3M ESPE) and one for indirect use (Signum, Heraeus, Kulzer) as a function of the reinforcement by one or two layers of polyethylene (THM-Ribbond, Ribbond ®) or glass fibers (Interlig, Angelus) submitted to heat treatment (170°C for 10 minutes) compared with control groups (not reinforced by fibers and/or not heat-treated; 2) evaluate water sorption, solubility and color stability of the reinforced composites, after storage in distilled water at 37°C for 14 days. Color stability was evaluated using a spectrophotometer (Vita Easyshade, Vident, CA, USA). For three point flexural bending test, rectangular specimens were prepared with dimensions of 12 x 2 x 2 mm (n=10), according to the following variation factors: a) composite (for direct or indirect use); b) type of fibers and number of layers (glass or polyethylene/one or two layers; c) subjected or not to heat treatment. The heat treatment was performed 24 hours after curing, in a furnace, at 170 ° C for 10 minutes. Tests were performed 24 hours after curing or heat treatment. To evaluate the water sorption/solubility and color stability, disc-shaped specimens were prepared with dimensions of 15 x 2 mm (n=5) according to the following variation factors: a) composite (for direct or indirect uses); b) fiber type (glass or polyethylene); c) number of fiber layers (one or two). Color parameters were analyze before and after immersion in deionized water for 14 days. The results were analyzed by ANOVA and Tukeys test with significance level of 5%, and indicated that the glass fiber when used in two layers, showed the highest flexural strength for the two tested composites (165.4 MPa - Z350XT and 208.7 MPa - Signum ). The heat treatment did not significantly affect the flexural strength of the direct composite. For the composite for indirect use (Signum ), a statistical significance for the factor heat treatment was found, indicating lower values of flexural strength for heat-treated groups. The composite for direct use showed higher water sorption value (33.6 /cm3) when compared to the composite for indirect use (19.1 /cm3). For solubility, a significant interaction was found for composite and fiber type, indicating higher values for direct composite and glass fiber. Color stability analysis showed higher color difference value for polyethylene fiber (E =1.5) when compared to glass fiber (E=1.0). It was concluded that: a) adding fibers increased the flexural strength values of the composites for direct or indirect use, the increase in strength was more pronounced when using two fiber layers; 2) heat treatment at 170 ° C for 10 minutes showed no improvement of the mechanical properties of fiber reinforced composites; 3) adding fibers to the composite did not increase the sorption/solubility after water immersion, 4) Immersion in water did not change the color of the fiber reinforced composites when compared with those without fibers.

Utilizando-se um poliuretano derivado de óleo de mamona desenvolvido para implantes ósseos, aonde este vem demonstrando ser biocompatível e apresentando características fisico-químicas semelhantes às dos ossos, estuda-se o comportamento mecânico deste material quando reforçado por fibra de carbono, juntamente com uma metodologia de fabricação de hastes de implante de quadril. Avaliou-se o efeito da fração volumétrica em fibra nas propriedades mecânicas do compósito, bem como, a influência da realização de um tratamento superficial da fibra de carbono por método químico, visando melhorar a adesão interfacial fibra/matriz. Foram realizados ensaios mecânicos nos corpos de prova em compósitos e nas hastes fabricadas para avaliar a resistência mecânica sob carregamentos quase-estáticos. Também foram realizadas simulações computacionais da haste, juntamente com o dispositivo de ensaio projetado, para comparação com os resultados experimentais. Para isto, utilizou-se o programa ANSYS®, que é um sistema de engenharia auxiliado por computador (Computer Aided Engineering - CAE) e utiliza o Método dos Elementos Finitos como ferramenta de análise estrutural. Resultados satisfatórios foram obtidos nos ensaios mecânicos do poliuretano reforçado por fibra de carbono, viabilizando sua aplicação no projeto de hastes de implante de quadril. / The polyurethane derived from castor oil has demonstrated excellent biocompatibility and similarity to the physical and chemical properties of the human bone. In order to use this material in the design of hip implant stems, this work investigates its mechanical behavior when reinforced by carbon fibers. A manufacturing methodology for hip implant stems is also proposed and validated. The effects of fiber volume fraction and superficial treatments on the carbon fibers are evaluated in terms of the mechanical properties of the polyurethane and of the composite. Mechanical tests were performed in the manufactured stems to evaluate the strength under quasi-static loading. Computational simulations of the stem and testing devices were also performed by using the Finite Element Method and the commercial package ANSYS®. The results obtained are quite satisfactory which validates the application of the carbon fiber reinforced polyurethane in hip implant stems.

O presente trabalho consiste na avaliação experimental da influência do avanço da frente de umedecimento no comportamento de protótipos de muros de um solo fino reforçado com geotêxteis não tecidos. O desempenho dos protótipos foi analisado nas condições de eventos de chuvas de intensidade e duração variáveis, bem como na condição de precipitação intermitente com intensidade próxima e inferior à condutividade hidráulica do solo. Para efeito comparativo, avaliou-se o comportamento de um protótipo na condição de umidade de compactação constante. Durante a infiltração, observou-se a formação de barreira capilar sobre o geotêxtil e a eficiência de drenagem proporcionada pelos reforços, não permitindo o desenvolvimento de pressões da água positivas mesmo sob a condição de carregamento rápido. Após quebra da barreira, os valores de grau de saturação mantiveram-se em torno de 90% e as pressões da água ficaram próximas de zero ou negativas. Com relação ao comportamento dos protótipos, evidências mostraram que a formação de barreiras capilares nas interfaces solo-geotêxteis não influenciou negativamente no desempenho dos protótipos. Diante do umedecimento, as deformações e deslocamentos máximos aumentaram exponencialmente com o grau de saturação do solo. Ainda, estes parâmetros relacionaram-se com a sucção matricial de forma semelhante à tendência estabelecida na curva retenção de água do solo. Tais relações foram estritamente associadas às alterações da rigidez média do solo devido ao avanço da infiltração e as alterações na sucção do solo. Na condição umidade constante, constatou-se que o maciço poderia se manter estável mesmo com a ausência dos reforços devido à elevada rigidez proporcionada pela sucção do solo. De modo geral, os deslocamentos e deformações foram relativamente pequenos sob a ação da variável umedecimento. A associação desta com os incrementos de tensões geraram deformações adicionais, embora estas ainda não possam ser consideradas excessivas. Os resultados de uma estrutura real corroboraram o comportamento verificado em laboratório. De modo geral, os níveis de deformações foram bastante semelhantes e a presença de água não prejudicou o desempenho da estrutura. Curiosamente, geotêxteis não tecidos de baixa resistência e rigidez à tração foram tão eficazes na estabilidade quanto geotêxteis tecidos de maior rigidez e resistência. Portanto, a eficiência de estruturas de solos finos reforçados com geotêxteis não tecidos foi constatada, mostrando estas possíveis de compor estruturas permanentes. / The effect of the wetting front advancement on the performance of nonwoven geotextile reinforced soil walls constructed with poorly draining soils was evaluated by laboratory full scale models. The tested models performances were monitored under rainfall conditions with different intensities and duration, as well as under intermittent precipitation with reduced intensity of precipitation (lower than the soil permeability). For comparison purposes, an evaluation of a full scale model was conducted with constant soil water content (compaction water content). As regards infiltration, capillary barrier formation have been observed on the interface soil-geotextile during infiltration process; besides, the drainage function of reinforcements after the breakthrough of water, in which water pressures development have not been allowed to occur even after rapid loading. After breakthrough of water, the degree of saturation was maintained around 90% and water pressures were negatives and close to zero. Besides, there are evidences that capillary barriers did not affect the model performance. As a result of wetting advancement, reinforcement strains and internal displacements have increased exponentially with the average of degree saturation of soil. Additionally, these parameters have shown to be correlated to the matric suction of soil with the same trend of the water retention curve. These relationships are essentially resulted from the soil stiffness alterations due to the wetting advancement and suction reduction. Under water content of compaction, reinforcement tensile forces were approximately zero, as a result of the relatively high stiffness of the unsaturated soil caused by the matric suction. Generally, displacements and reinforcement strains were small under wetting conditions and increased when stress increments were applied. However, these strains levels obtained cannot be considered excessive. A validation of laboratory results was observed in an instrumented geotextile reinforced soil wall, in addition to the comparison between woven and nonwoven geotextile sections, in which similar performances were found. Strains levels registered in field were consistent to the laboratory and the nonwoven geotextile wall was not affected by the wetting occurrence. Therefore, the efficiency of nonwoven geotextiles reinforced walls under wetting conditions is assured with no positive water pressures and relatively low levels of degree of saturation, being able to constitute permanent reinforced walls.