Made available in DSpace on 2014-12-17T14:06:48Z (GMT). No. of bitstreams: 1 HaroldoRAM.pdf: 1140599 bytes, checksum: 95a046b646a7cfa0d6cf0153f138783f (MD5) Previous issue date: 2008-08-20 / Conselho Nacional de Desenvolvimento Cient?fico e Tecnol?gico / Titanium is a biomaterial widely employed in biomedical applications (implants, prostheses, valves, stents). Several heat treatments are usually used in order to obtain physical properties required to different applications. This work studied the influence of the heat treatment on microstructure of commercial pure titanium, and their consequences in growth and proliferation of MC3T3-E1 cells. Discs of titanium were treated in different temperatures, and characterized by optical microscopy, image analysis, wettabillity, roughness, hardness and X-ray diffraction. After the heat treatment, significant modifications in these properties were observed. Pattern images of titanium, before and after the cell culture, were compared by overlapping to analyze the influence of microstructure in microstructure and preferences guidance cells. However, in general, titanium discs that showed a higher residual strength also presented an increase of cells numbers on surface / O tit?nio como biomaterial ? amplamente utilizado em dispositivos biom?dicos (implantes, pr?teses, v?lvulas, stents entre outros). Diversos tratamentos t?rmicos s?o usualmente utilizados na obten??o das propriedades necess?rias para as diferentes aplica??es. Este trabalho estudou a influ?ncia desses tratamentos na microestrutura do tit?nio comercialmente puro e suas conseq??ncias no crescimento, forma e prolifera??o de c?lulas pr?-osteobl?stica. Para tanto foram utilizados discos de tit?nio submetidos a diferentes tratamentos e caracterizados por microscopia ?tica, an?lise de imagens, molhabilidade, rugosidade, dureza e difra??o de raios-X. Ap?s os tratamentos t?rmicos foram verificado modifica??es significantes nestas propriedades. Padr?es de imagens de superf?cies do tit?nio antes e ap?s a cultura de c?lula foram comparados atrav?s de sobreposi??o para analisar a influ?ncia da microestrutura na resposta biol?gica, n?o sendo verificadas correla??es entre a microestrutura e as prefer?ncias orientacionais das c?lulas. Entretanto de um modo geral verificou-se que os discos que presentaram maior estado de tens?o residual apresentaram tamb?m maior n?mero de c?lulas em sua superf?cie

SILVA, J. S. P. Estudo das caracter?sticas f?sico-qu?micas e biol?gicas pela ades?o de osteoblastos em superf?cies de tit?nio modificadas pela nitreta??o em plasma. 2008. 119 f. Tese (Doutorado) - Faculdade de Medicina, Universidade de S?o Paulo. S?o Paulo, 2008. / Submitted by CECILIA SANTOS (cecilia@bczm.ufrn.br) on 2010-09-29T13:32:45Z No. of bitstreams: 2 2008Tese_JSandroPS_Estudo.pdf: 2786183 bytes, checksum: a2ca1d8386a1a0d5d0c3befb46b1ed92 (MD5) license_rdf: 20464 bytes, checksum: d540d98f4c56c073d1d99228e27d53ca (MD5) / Approved for entry into archive by clediane guedes(clediane@bczm.ufrn.br) on 2010-09-29T18:15:54Z (GMT) No. of bitstreams: 2 2008Tese_JSandroPS_Estudo.pdf: 2786183 bytes, checksum: a2ca1d8386a1a0d5d0c3befb46b1ed92 (MD5) license_rdf: 20464 bytes, checksum: d540d98f4c56c073d1d99228e27d53ca (MD5) / Made available in DSpace on 2010-09-29T18:15:54Z (GMT). No. of bitstreams: 2 2008Tese_JSandroPS_Estudo.pdf: 2786183 bytes, checksum: a2ca1d8386a1a0d5d0c3befb46b1ed92 (MD5) license_rdf: 20464 bytes, checksum: d540d98f4c56c073d1d99228e27d53ca (MD5) / PURPOSE: The aim of this study was to evaluated the physico-chemical properties of different titanium surfaces modified by means of low temperature plasma nitridind on rat osteoblast cell adhesion and proliferation. METHODS: Pure Titanium discs grade II was submitted to three different surface preparations (polishing, glowglow discharge plasma nitriding in planar and cathodic cage configurations). Surface parameters as roughness, wettability and chemichal composition was determined to compare influency of gas mixture on the modified surface material properties. Cellular morphology was observed by scanning electron microscopy.To evaluate the effect of the surface on cellular response, osteoblast cells (MC3T3) adhesion and proliferation was quantified and data analised by Kruskal-Wallis and Friedman statistical tests. RESULTS: plasma nitriding discs shows rougher surfaces( p<0,02) in cathodic cage configuration andlower contact angle values. MC3T3 cells attached on rough surfaces produced by cathodic cage configuration was statistically significant p<0,05 compared to polished discs. CONCLUSIONS: Glow discharge plasma nitriding improve titanium surface roughness and wettability. MC3T3 cell adhesion behavior is related to substrate chemical composition and topography. Resumo: INTRODU??O: Superf?cies de tit?nio modificadas por diferentes m?todos foram estudadas com base nos par?metros f?sicos e qu?micos de caracteriza??o superficial e sua influ?ncia no comportamento de c?lulas pr?osteobl?sticas (MC3T3) in vitro. M?TODOS: Discos de tit?nio comercialmente puro grau II foram submetidos a tr?s m?todos de modifica??o de superf?cie (polimento, nitretados em plasma em configura??o planar e gaiola cat?dica). As diferentes superf?cies foram caracterizadas para observar o efeito do processamento na estrutura da camada superficial, na rugosidade e molhabilidade. Ensaios de ades?o e prolifera??o celular usando linhagens de c?lulas pr?-osteobl?sticas MC3T3 foram realizados para avaliar o efeito das novas superf?cies no comportamento celular in vitro. RESULTADOS: Os resultados demonstraram que a nitreta??o em plasma na configura??o de gaiola cat?dica produz superf?cies mais rugosas (p<0,02) e com menores ?ngulos de contato com a ?gua. CONCLUS?ES: A ades?o celular ? maior nas superf?cies mais rugosas do que nas superf?cies polidas (p<0,05) e reagem de modo diferente a composi??o qu?mica do substrato e ? topografia da superf?cie

Made available in DSpace on 2015-04-14T13:58:44Z (GMT). No. of bitstreams: 1 434834.pdf: 2467680 bytes, checksum: d94eca86dabe6ec28377349c07e8a880 (MD5) Previous issue date: 2011-08-31 / O comportamento passivante da camada formada de ?xido de tit?nio ? uma caracter?stica relevante para a aplica??o biom?dica. As intera??es com o meio biol?gico ap?s a implanta??o de uma pr?tese est?o diretamente ligadas, entre outros fatores, com as propriedades f?sico-qu?micas da superf?cie do material implantado. As superf?cies de tit?nio que s?o tratadas qu?mica ou eletroquimicamente tendem a desenvolver camadas espec?ficas com composi??o qu?mica e porosidade que promovem a osseointegra??o. O objetivo deste trabalho ? estudar o processo de anodiza??o para desenvolver o crescimento de nanotubos de TiO2 em substrato de tit?nio comercialmente puro. Foram utilizadas solu??es eletrol?ticas de 1M H3PO4 e 0,2 % de HF variando a tens?o aplicada e alterando o distanciamento entre os eletrodos. Ap?s o processo an?dico as esp?cimes foram tratadas termicamente nas temperaturas de 500, 600, 700, 800 e 900?C. Os film es formados e tratados termicamente foram analisados por microscopia eletr?nica de varredura (MEV), espectroscopia por energia dispersiva (EDS) e difratometria de raios X (DRX). Os resultados indicaram a forma??o de nanotubos nos filmes de ?xidos de tit?nio tratados anodicamente em toda extens?o da superf?cie, al?m de boa uniformidade da camada de ?xido e regularidade do di?metro dos nanotubos de 171nm. As an?lises da composi??o qu?mica indicaram a presen?a de f?sforo, oriundos das condi??es do experimento. A estrutura cristalogr?fica verificada foi hexagonal, a qual corresponde ? estrutura do tit?nio.

Made available in DSpace on 2015-04-14T14:50:47Z (GMT). No. of bitstreams: 1 399015.pdf: 142110 bytes, checksum: c5ffb33c81a7c9cbade03c8428376c8e (MD5) Previous issue date: 2007-12-05 / Uma conex?o est?vel entre a superf?cie de tit?nio e os tecidos a sua volta ? um dos mais importantes pr?-requisitos para o sucesso a longo prazo dos implantes. Para isso, uma forte e efetiva ades?o das c?lulas na superf?cie do biomaterial ? requerida. O objetivo desse estudo foi o de avaliar a ades?o de fibroblastos estimulados por Fator de Crescimento de Fibroblastos b?sico (bFGF) em discos de tit?nio. Para esse estudo foram produzidos 30 discos de tit?nio com superf?cie lisa. Esses discos foram colocados em placas de cultura e sobre eles foi inserido meio com fibroblastos NIH3T3, estimulados por bFGF, no grupo teste e sem este fator de crescimento no controle. As amostras foram obtidas em 3 horas, 24 horas e 48 horas. Foram feitas 10 imagens com Microsc?pio Eletr?nico de Varredura em cada disco, totalizando 300 micrografias. Como resultado foi encontrado que existe uma diferen?a significativa no crescimento de fibroblastos nos tr?s tempos deste experimento, do grupo onde o bFGF foi administrado.

Submitted by Setor de Tratamento da Informa??o - BC/PUCRS (tede2@pucrs.br) on 2015-12-08T16:24:06Z No. of bitstreams: 1 476571 - Texto Completo.pdf: 1876137 bytes, checksum: 9fe390eadadb7a4c4bb1e5c4f411b37c (MD5) / Made available in DSpace on 2015-12-08T16:24:07Z (GMT). No. of bitstreams: 1 476571 - Texto Completo.pdf: 1876137 bytes, checksum: 9fe390eadadb7a4c4bb1e5c4f411b37c (MD5) Previous issue date: 2015-03-13 / This study evaluates the electrochemical anodization process parameters in the formation of titanium nanotubes on titanium sheets in order to determine their implications on the morphology of the tubes and the film/substrate adhesion. The evaluated parameters were the anodization time, applied potential, water content in the electrolyte and the electrolyte stirring (ultrasound bath and magnetic agitation) in an ethylene glycol electrolyte with addition of ammonium fluoride. The obtained results were compared to those obtained from the anodization in an aqueous acid electrolyte (mixed solution of hydrofluoric and phosphoric acid). Analyzes using scanning and transmission electron microscopy were performed for the morphological characterization of the samples. Rutherford backscattering spectrometry was used to determine the composition and density profile of the different oxide layers formed. Tensile tests (pull out) were used in order to determine the adhesion of the titanium nanotubes to the substrate. The results showed that it is possible to form titanium nanotubes with various morphologies by changing the parameters of the electrolytic process. The average adhesive tension of nanotubes ranged from 2,82 ? 0,27 Mpa to 5,18 ? 3,61 MPa, however, it was not possible to observe a direct relationship between the morphologies formed and the obtained adhesive tension values. / No presente trabalho, foram estudados os par?metros do processo de anodiza??o eletroqu?mica para forma??o de nanotubos de tit?nio (NTT) sobre chapas de tit?nio a fim de determinar suas implica??es na morfologia dos tubos e na ades?o NTT/substrato. Os par?metros avaliados foram o tempo de anodiza??o, a tens?o de trabalho, o teor de ?gua no eletr?lito e o tipo de agita??o do eletr?lito (banho de ultrassom e magn?tica) usando um eletr?lito org?nico de etilenoglicol com adi??o de fluoreto de am?nia. Os resultados obtidos foram comparados com os de anodiza??es feitas em eletr?lito aquoso ?cido (mistura de ?cido fluor?drico com ?cido fosf?rico). Para a caracteriza??o morfol?gica das amostras, foram realizadas an?lises de microscopia eletr?nica de varredura (FEGMEV) e de transmiss?o (MET). Para a determina??o de um perfil de composi??o e densidade das diferentes camadas ?xidas formadas foi utilizada espectrometria de retroespalhamento Rutheford (RBS). Para determinar a ades?o dos NTT ao substrato de tit?nio foram utilizados testes de tra??o (pull out). Os resultados mostraram que ? poss?vel crescer NTT com diversas morfologias a partir das altera??es dos par?metros do processo eletrol?tico. As m?dias da tens?o adesiva dos NTT ao Ti apresentaram valores variando entre 2,82 ? 0,27 MPa e 5,18 ? 3,61 MPa, contudo n?o foi poss?vel observar uma rela??o direta entre as morfologias formadas e os valores de tens?o de ades?o obtidos.

Submitted by Setor de Tratamento da Informa??o - BC/PUCRS (tede2@pucrs.br) on 2016-04-06T11:40:47Z No. of bitstreams: 1 DIS_MARCEL_FERREIRA_KUNRATH_COMPLETO.pdf: 1943048 bytes, checksum: f2472fa9da9d6ca1d610f11f2d69bc64 (MD5) / Made available in DSpace on 2016-04-06T11:40:47Z (GMT). No. of bitstreams: 1 DIS_MARCEL_FERREIRA_KUNRATH_COMPLETO.pdf: 1943048 bytes, checksum: f2472fa9da9d6ca1d610f11f2d69bc64 (MD5) Previous issue date: 2016-01-12 / With the growing expansion of implant surfaces and the need for greater speed of osseointegration, methods of analysis of bone tissue and implant surface as well as the quality of the bone implant contact (BIC), they are increasingly being explored by researchers. The aim of this study is to show detail and describe a bone preservation protocol for making implants samples with and without implants without any harm or damage, or the bone tissue or the properties of the metal, preserving the BIC. In a second step, the samples prepared by the protocol preservation were compared with those made by histological analysis method for staining for HE, considered the gold standard for living tissue. Eight samples were used for bone tissue with implants in rabbit tibia and more four fragments of jaws without implants of the same rabbits. Samples with and without implants were made by the two protocols, after preparation of the test specimens, analysis by optical microscopy of transmission and reflection through scanned images were made. Each protocol had advantages when the results were analyzed individually in the implants without samples, becoming further analysis. However, for samples with implants, analysis only by histological method cannot bring good results, while the bone preservation method showed excellent results for osseointegration analysis, bone formation and bone implant interface. It follows that the bone preservation protocol is an excellent method for analyzing samples with implants, and can be complementary to histology, in analysis bone samples without implants. The histological method is not sufficient for analysis of bone formation and bone implant interface. / Com a crescente expans?o de superf?cies de implantes e a necessidade de maior velocidade de osseointegra??o, m?todos de an?lise do tecido ?sseo, an?lises da superf?cie de implantes e a qualidade do contato osso-implante (BIC) est?o cada vez mais sendo explorados pelos pesquisadores. O objetivo do presente estudo foi descrever detalhadamente um protocolo de preserva??o ?ssea para confec??o de amostras com e sem implantes, sem causar danos ou avarias nem ao tecido ?sseo nem ?s propriedades do metal, preservando o BIC. Em uma segunda etapa, as amostras confeccionadas pelo protocolo de preserva??o ?ssea foram comparadas com as amostras preparadas pelo m?todo de an?lise histol?gica por colora??o por Hematoxilina-Eosina, considerado padr?o ouro para tecidos vivos. Foram utilizadas oito amostras de tecido ?sseo com implantes de t?bias de coelhos e, mais quatro fragmentos de mand?bulas sem implantes, dos mesmos coelhos. As amostras com e sem implantes foram confeccionadas pelos dois protocolos e, ap?s a prepara??o dos corpos de prova, foram feitas as an?lises por microscopia ?ptica de transmiss?o e reflex?o atrav?s de imagens digitalizadas. Cada protocolo apresentou vantagens quando os resultados foram analisados individualmente nas amostras sem implantes. Por?m, para as amostras com implantes, a an?lise apenas pelo m?todo histol?gico n?o conseguiu apresentar bons resultados, enquanto que o m?todo de preserva??o ?ssea mostrou excelentes resultados para an?lise de osseointegra??o, neoforma??o ?ssea e interface osso-implante. Conclui-se que o protocolo de preserva??o ?ssea desenvolvido mostrou-se um excelente m?todo para an?lise de amostras com implantes, e que pode ser complementar ? histologia, em an?lises de tecido ?sseo sem implantes. O m?todo histol?gico n?o mostrou-se suficiente para an?lise de neoforma??o ?ssea e interface osso-implante.

Made available in DSpace on 2015-04-14T13:29:36Z (GMT). No. of bitstreams: 1 422228.pdf: 2027786 bytes, checksum: fc45ed715786efb01f83f7fff755ceef (MD5) Previous issue date: 2010-01-14 / Atualmente, o foco de muitas pesquisas cient?ficas em Implantodontia est? voltado para a modifica??o da superf?cie do tit?nio na busca de alternativas que proporcionem maior rapidez e qualidade no processo de osseointegra??o. A osseointegra??o ? um fen?meno que acontece fundamentalmente atrav?s da resposta interfacial das c?lulas ?sseas em contato com a superf?cie do tit?nio. Diferentes m?todos de tratamento podem ser utilizados para modificar as propriedades topogr?ficas e qu?micas da superf?cie do tit?nio a fim de otimizar as rea??es tecido-implante. Neste estudo foi avaliada a influ?ncia de diferentes tratamentos de superf?cie do tit?nio na ades?o e prolifera??o de osteoblastos humanos, atrav?s da an?lise quantitativa do n?mero de c?lulas aderidas em diferentes per?odos de cultura celular. Para isso, 40 discos de tit?nio grau II, comercialmente puro, de 15mm de di?metro e 1mm de espessura, foram divididos em quatro grupos conforme a caracteriza??o de sua superf?cie: G1. maquinada; G2. ?cido-condicionada; G3. com cobertura de hidroxiapatita; e G4. com bisfosfonato imobilizado na cobertura de hidroxiapatita. C?lulas osteobl?sticas derivadas de osteossarcoma humano (SaOS-2) foram cultivadas sobre os discos e a contagem celular foi realizada em 3, 7 e 14 dias. Para determina??o do n?mero de c?lulas, um processo de colora??o dos n?cleos com Iodeto de Prop?dio foi realizado, e os discos foram analisados em microsc?pio ?ptico sob luz ultravioleta. As contagens celulares nos diferentes grupos experimentais e per?odos de cultura foram comparadas por meio de ANOVA, complementado pelo teste de Tukey. Os resultados da an?lise estat?stica permitem concluir que: (1) a superf?cie do tit?nio e o per?odo de cultura celular, bem como a intera??o de ambos, significativamente afetam o crescimento celular; (2) a modifica??o na superf?cie do tit?nio atrav?s de condicionamento ?cido favorece, in vitro, a ades?o e prolifera??o de osteoblastos humanos. Mais pesquisas s?o necess?rias para elucidar a influ?ncia do bisfosfonato imobilizado na superf?cie do tit?nio nos eventos iniciais da osteog?nese.

Made available in DSpace on 2015-04-14T13:29:42Z (GMT). No. of bitstreams: 1 417773.pdf: 1138982 bytes, checksum: 03423e2cddaa5a43349be69c0853e615 (MD5) Previous issue date: 2009-08-31 / Os implantes osseointegrados, em sua maioria, possuem algum tipo de condicionamento da sua superf?cie que visa melhorar a osseointegra??o. O mecanismo de diferencia??o celular in vitro de c?lulas mesenquimais em osteoblastos j? ? bastante conhecido e serve para avalia??o das propriedades de osteoindu??o e osteocondu??o de biomateriais. O presente estudo tem por objetivo avaliar a ades?o, prolifera??o e diferencia??o das c?lulas da medula ?ssea humana em superf?cies de implantes de tit?nio com e sem deposi??o discreta de fosfato de c?lcio. As c?lulas foram obtidas a partir da medula ?ssea de um doador humano. Foram selecionados 12 discos de tit?nio do tipo Bonelike? (Biomet 3I, Brasil) com superf?cie tratada por duplo ataque ?cido; Osseotite (Biomet 3I, USA) com superf?cie tratada por duplo ataque ?cido e Nanotite (Biomet 3I, USA). Ap?s 14 e 21 dias de cultura foi realizado PCR em tempo real para avalia??o da diferencia??o celular e microscopia eletr?nica de varredura para avalia??o da prolifera??o e ades?o celular aos discos de tit?nio. Os resultados indicaram que a rugosidade da superf?cie dos discos de tit?nio possibilita a ades?o, diferencia??o e prolifera??o celular, que a s?ntese de ALP ? maior na superf?cie Bonelike e que as part?culas de fosfato de c?lcio demonstraram maior grau de s?ntese de BGLAP e prolifera??o celular.

Submitted by Setor de Tratamento da Informa??o - BC/PUCRS (tede2@pucrs.br) on 2017-03-17T15:08:38Z No. of bitstreams: 1 DIS_JOSE_CRISTIANO_MENGUE_MODEL_COMPLETO.pdf: 3495211 bytes, checksum: 700bfa91afac93bfa629684755fcc8ce (MD5) / Made available in DSpace on 2017-03-17T15:08:38Z (GMT). No. of bitstreams: 1 DIS_JOSE_CRISTIANO_MENGUE_MODEL_COMPLETO.pdf: 3495211 bytes, checksum: 700bfa91afac93bfa629684755fcc8ce (MD5) Previous issue date: 2017-01-24 / The surface passivation is an important step in solar cell manufacturing since it intends to fix the surface defects. In order to develop p-type crystalline silicon solar cells, solar grade, with surface passivation provided by titanium dioxide film, atmospheric pressure chemical vapor deposition (APCVD) and electron beam deposition (E-Beam) were carried out. For the films deposited by E-Beam, the thickness of TiO2, which has produced the most efficient solar cell, was of 80 nm. It was observed that how thicker the film, higher was the internal quantum efficiency (IQE) for short wavelengths, indicating a surface passivation that changes according to the thickness. The cells in which the film deposition on the front face was performed by APCVD were as efficient in to reduce the reflection as those with films deposited by E-Beam, although the first technique did not produce films with high homogeneity with regard to thickness. When the both techniques to deposit films on the back surface were compared, it was observed that the better results were obtained with APCVD films. Regarding the thickness of the films obtained by APCVD, it was not observed difference between the electrical characteristics of solar cells with thin and thick films. The most efficient solar cell produced in this work used TiO2 films obtained by chemical vapor deposition on both sides, reaching the efficiency of 15.6% and short-circuit current density of 34.9 mA/cm?. / A passiva??o ? uma importante etapa no processo de produ??o de c?lulas solares, pois visa corrigir os defeitos de superf?cie. Com o objetivo de desenvolver c?lulas solares de sil?cio cristalino tipo p, grau solar, com BSF (back surface field ? campo retrodifusor) seletivo e com passiva??o da superf?cie proporcionada por filme de di?xido de tit?nio, realizou-se deposi??o qu?mica em fase vapor a press?o atmosf?rica (APCVD) e por canh?o de el?trons (E-Beam). Para os filmes depositados por E-Beam, verificou-se que a espessura de TiO2 que produziu a c?lula solar mais eficiente foi de 80 nm. Observou-se que quanto maior a espessura do filme, mais elevada foi a efici?ncia qu?ntica interna (EQI) para comprimentos de onda curtos, indicando uma passiva??o de superf?cie vari?vel com a espessura. As c?lulas em que a deposi??o de filme na face frontal foi realizada via APCVD se mostraram t?o eficientes na redu??o da reflex?o quanto as que receberam filme por E-Beam, embora a primeira t?cnica n?o produziu filmes de elevada homogeneidade no que se refere a espessura. Ao comparar as duas t?cnicas utilizadas para deposi??o de filme na face posterior, verificou-se que os melhores resultados foram obtidos com filmes depositados por APCVD. No que se refere a espessura do filme posterior obtido por APCVD, n?o se observou diferen?a entre as caracter?sticas el?tricas de c?lulas solares com filmes finos e espessos. A c?lula solar mais eficiente produzida neste trabalho utilizou filmes de TiO2 obtidos por deposi??o qu?mica em fase vapor em ambas as faces, atingindo 15,6 % de efici?ncia e 34,9 mA/cm? de densidade de corrente de curto-circuito.

Made available in DSpace on 2014-12-17T14:06:51Z (GMT). No. of bitstreams: 1 FranciericAA.pdf: 3105945 bytes, checksum: 434348633df1dedcb6e622baefde201e (MD5) Previous issue date: 2009-03-26 / This work aims to develop a methodology for analysis of images using overlapping, which assists in identification of microstructural features in areas of titanium, which may be associated with its biological response. That way, surfaces of titanium heat treated for 08 (eight) different ways have been subjected to a test culture of cells. It was a relationship between the grain, texture and shape of grains of surface of titanium (attacked) trying to relate to the process of proliferation and adhesion. We used an open source software for cell counting adhered to the surface of titanium. The juxtaposition of images before and after cell culture was obtained with the aid of micro-hardness of impressions made on the surface of samples. From this image where there is overlap, it is possible to study a possible relationship between cell growth with microstructural characteristics of the surface of titanium. This methodology was efficient to describe a set of procedures that are useful in the analysis of surfaces of titanium subjected to a culture of cells / O presente trabalho tem como objetivo desenvolver uma metodologia de an?lise de imagens, utilizando sobreposi??es, que auxilie na identifica??o de caracter?sticas microestruturais, em superf?cies de tit?nio, que possam estar associadas com a sua resposta biol?gica. Desse modo, superf?cies de tit?nio tratadas termicamente de 08(oito) diferentes maneiras foram submetidas a um ensaio de cultura de c?lulas. Buscou-se uma rela??o entre os gr?os, textura e contornos de gr?os da superf?cie de tit?nio (atacada) procurando relacionar com o processo de prolifera??o e ades?o. Foi utilizado um software open source para a contagem das c?lulas aderidas ? superf?cie do tit?nio. A justaposi??o das imagens antes e ap?s a cultura de c?lulas foi obtida com o aux?lio de impress?es de micro-dureza feita sobre a superf?cie das amostras. A partir desta imagem onde h? a sobreposi??o, ? poss?vel o estudo de uma poss?vel rela??o entre o crescimento celular com as caracter?sticas microestruturais da superf?cie de tit?nio. Essa metodologia se mostrou eficiente ao descrever um conjunto de procedimentos que s?o ?teis na analise de superf?cies de tit?nio submetidos a uma cultura de c?lulas