Made available in DSpace on 2015-06-17T19:34:49Z (GMT). No. of bitstreams: 0 Previous issue date: 2014-04-24. Added 1 bitstream(s) on 2015-06-18T12:47:01Z : No. of bitstreams: 1 000829403.pdf: 678241 bytes, checksum: e51ad21d05ccf2fa4a8b92a572ce754a (MD5) / O objetivo deste estudo foi avaliar o efeito de diferentes protocolos de jateamento na resistência à flexão biaxial e transformação de fase cristalina de cerâmica policristalina de Y-TZP. Foram confeccionados 740 discos de zircônia estabilizada parcialmente por ítrio - Cercon®Zirconia (DENTSPLY Ceramco, EUA) e In Ceram 2000 YZ cubes (Vita Zahnfabrik, Alemanha) segundo a norma ISO 6872 (15 mm diâmetro x 2 mm espessura). As amostras foram jateadas com partículas de óxido de alumínio (30 μm) revestido por sílica (RocatecSoft - 3M ESPE) e divididas em 74 grupos (n = 10), incluindo-se os grupos controle (ausência de jateamento)(n = 10) para cada cerâmica, de acordo com os fatores: pressão de jateamento (2, 3 e 4 bar); ângulo formado entre a ponta do jateador e a superfície da cerâmica (45º, 60º, 90º); distância do microjateador à cerâmica (5 e 10 mm) e tempo de jateamento (15 s e 20 s). Foi realizado teste de resistência à flexão biaxial em máquina de ensaio universal (1 mm/min, 1000 kg). Os dados (MPa) foram submetidos a análise de variância e ao teste de Duncan. Parte das amostras (n=3) foram submetidas à difração por raios-X (DRX) para quantificação das fases cristalinas e à microcopia eletrônica de varredura (MEV) para análise da topografia superficial. Pressão (p = 0,00) afetou significativamente os resultados, porém tempo (p = 0,49), distância (p = 0,46) e angulação (p = 0,13) não afetaram a Cercon. Já para Vita YZ, a pressão (p = 0,00) foi estatisticamente significante, porém tempo (p=0,66), distância (p = 0,70) e angulação (p=0,14) não foram. Fase monoclínica foi encontrada nos grupos da Cercon (0 a 11%), enquanto para Vita YZ, nenhuma fase foi encontrada. Para Vita YZ, a pressão 3 bar teve maior resistência à flexão biaxial e 4 bar apresentou menor valor. Angulação de 45° associado a 2 bar foi a melhor combinação (1012,21 ± 108,36 MPa)... / The aim of this study was to evaluate the effect of different sandblasting protocols on biaxial flexural strength and crystalline phase transformation in Y - TZP ceramic. 740 discs of Yttria-Partially-Stabilized Zirconia were made - Cercon ® Zirconia (DENTSPLY Ceramco, USA) and In Ceram 2000 YZ cubes (Vita Zahnfabrik, Germany) according to the standards of ISO 6872 (15 mm diameter x 2 mm thick) . The samples were sandblasted with aluminum oxide - coated silica 30 μm (Rocatec Soft - 3M ESPE ) and divided into 74 groups (n = 10 ) , according: pressure (2, 3 and 4 bar) ; nozzle angle (45°, 60°, 90°); nozzle distance (5 and 10 mm) and time (15 s and 20 s) . The biaxial flexural strength on universal testing machine (1mm/min, 1,000 kg) was performed. Data (MPa) were submitted to ANOVA and to Duncan's test (α = 0.05). Samples (n = 2) were subjected to X- ray diffraction to quantify crystalline phases. Pressure (p = 0.00) significantly affected the results, but deposition time (p = 0.49), nozzle distance (p = 0.46) and nozzle angles (p=0.13) did not affect to Cercon ceramic. Pressure (p = 0.00) affected significantly the results to Vita YZ, but deposition time (p = 0.66), nozzle distance (p = 0.70) and nozzle angles (p = 0.14) did not affect. Some monoclinical phase was achieved in Cercon groups (0 a 11%) and none for Vita YZ. For Vita YZ ceramic, 3 bar pressure had the biggest flexural strength value and 4 bar was the worst one and angle 45° associated to 2 bar were the best combination (1012.21 ± 108.36 MPa) compared to 4 bar (556.65 ± 117.41 MPa) (p < 0.001). EDS analysis demonstrated regular superficial grains. SEM images indicated grain size of 0.712 μm (Vita YZ), and 0.705 μm (Cercon). The Cercon density was 98% compared to the theoretical density of zirconia, while VITA YZ was 99%

O objetivo deste estudo foi analisar as propriedades mecânicas de cerâmicas à base de alumina e alumina-feldspato quando expostas a um meio agressivo (ácido acético 4%). Os corpos cerâmicos de alumina, contendo diferentes quantidades de feldspato (0, 1, 5, 10, 40 ou 100%), foram sinterizados a 1160, 1300, 1600 ou 1700ºC. Os espécimes foram divididos em três grupos de acordo com o tamanho do entalhe infligido (0, 30 ou 50% da largura do corpo-de-prova). Metade dos corpos cerâmicos foi exposta a uma solução de ácido acético a 4%. Os corpos cerâmicos sem e após ataque foram submetidos a ensaios para a determinação da resistência mecânica e do KIC; (por flexão a 4-pontos), área superficial (BET) e porosidade (método de Arquimedes). A microestrutura foi investigada por microscopia óptica e eletrônica de varredura, incluindo mapeamento por EDS, para a determinação da presença e distribuição de elementos químicos de interesse (C, O, Al, Si, K, Na, Mg). A solução lixiviada pelo ataque por ácido acético foi analisa para a determinação da concentração dos íons (Na+, Al+3, Si+4 e K+). Os resultados mostraram que os corpos cerâmicos sinterizados a 1700ºC, quando expostos ao ácido acético, diminuem sua resistência mecânica. Para os corpos cerâmicos sinterizados a 1600ºC a resistência mecânica não foi alterada. Nessas amostras, o KIC até aumentou após a exposição ao ácido acético. O ataque por ácido acético causou aumento na área superficial específica e do volume total de poros, o que foi confirmado pela concentração de íons na solução lixiviada pelo ataque por ácido acético. A fase vítrea, mesmo em pequenas quantidades, auxilia os corpos cerâmicos à base de alumina-feldspato a adquirir as propriedades mecânicas similares, ou até melhores, do que os corpos cerâmicos de alumina, dependendo da temperatura de sinterização. Isso sugere que é possível aperfeiçoar a formulação e a temperatura de queima de cerâmicas baseado na introdução de fase vítrea na microestrutura dos materiais, a fim de enfrentarem o rigor do ambiente oral. / This study investigates the mechanical properties of alumina-feldspar based ceramics when exposed to an aggressive environment (acetic acid 4%). Alumina ceramics containing different concentrations of feldspar (0, 1, 5, 10, 40 or 100%) were sintered at one of the temperatures 1160, 1300, 1600, or 1700oC. The samples were divided according to the inflicted flaws (of height 0, 30, or 50%). Half of these ceramic bodies were exposed to 4% acetic acid. The ceramic bodies whether or not exposed to acetic acid were tested in order to determine mechanical resistance and KIC (4 point bending test), superficial area (BET) and porosity (Archimedes). The microstructure was analyzed by optical and scanning microscopy, including element mapping performed by EDS to determine the presence and distribution of specific chemical elements (C, O, Al, Si, K, Na, Mg). The leachate solution was evaluated to determine the concentration of ions (Na+, Al+3, Si+4 e K+). The results showed that the ceramic bodies sintered at 1700oC decrease their mechanical resistance when exposed to acetic acid. The mechanical resistance for ceramic bodies sintered at 1600ºC was not altered. In these samples, the KIC even increased after acetic acid exposure. The acetic acid attack increased specific superficial area and total pore volume, which was confirmed by the ion concentration on the leachate solution. The glassy phase, even in small amounts, aids the alumina-feldspar based ceramics in acquiring similar or even better mechanical properties than alumina ceramic bodies, depending of sintering temperature. This suggests that is possible to enhance both formulation and sintering temperature of ceramics based on the introduction of glassy phase into the microstructure in order to face the rigors of the oral environment.

Submitted by Pedro Henrique Conde Oliveira Prado (pedrohcop@hotmail.com) on 2018-01-30T04:57:56Z No. of bitstreams: 1 PRADO_phco_me_SJC.pdf: 11588382 bytes, checksum: b5aad78aae05251739002f306dd6e1be (MD5) / Approved for entry into archive by Silvana Alvarez null (silvana@ict.unesp.br) on 2018-02-05T12:03:17Z (GMT) No. of bitstreams: 1 prado_phco_me_sjc.pdf: 11588382 bytes, checksum: b5aad78aae05251739002f306dd6e1be (MD5) / Made available in DSpace on 2018-02-05T12:03:17Z (GMT). No. of bitstreams: 1 prado_phco_me_sjc.pdf: 11588382 bytes, checksum: b5aad78aae05251739002f306dd6e1be (MD5) Previous issue date: 2018-01-12 / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / Com o avanço da ciência e processamento de materiais, a zircônia odontológica deixou de ser um material opaco para apresentar certa translucidez, possibilitando a confecção de peças ultrafinas. Sabe-se que a água em contato com a superfície das zircônias convencionais acarreta na transformação de fase T-M e subsequente decréscimo de resistência, mas esses efeitos nas zircônias translúcidas ainda não foram explorados. Para avaliar, mapear e caracterizar os efeitos da cinética de envelhecimento acelerado em zircônias de alta translucidez, foram cortados 39 blocos de Y-TZP (VITA YZ, VITA HT, InCoris TZI) para cada zircônia comercial, onde posteriormente foram sinterizados (1530 ºC, 2h) e atribuídos a 13 grupos com 3 amostras cada: Um controle e 12 envelhecidos hidrotermicamente a 134 ºC com pressão constante de 2 bars por 6, 10, 14, 18, 22, 26, 30, 40, 60, 80, 100 e 140 horas. A análise em DRX foi utilizada para quantificar a transformação de fase da zircônia (tetragonal-monoclínica) em diferentes profundidades do material ao se trocar o ânodo do tubo irradiador (Cr, Co e Cu). Uma curva cinética de envelhecimento foi feita para cada profundidade para as 3 zircônias comerciais. Para avaliar os efeitos do envelhecimento hidrotermal nas propriedades mecânicas, 270 discos de Y-TZP foram cortados, 90 para cada tipo, sinterizados e atribuídos a 3 grupos: C-Controle; E1- envelhecido até 26h e E2- envelhecido até 140 horas. Os discos foram testados em uma máquina de teste universal (EMIC). A microestrutura dos discos foi avaliada sob MEV. As curvas de cinética do envelhecimento funcionaram de forma semelhante para todas as zircônias utilizadas neste estudo, caracterizadas por uma rápida transformação de fase T-M em função do tempo e estabilização de um platô após uma média de 26 horas. As camadas superficiais apresentam concentrações mais elevadas de fase monoclínica à medida em que essa concentração diminuiu em camadas mais profundas. O envelhecimento hidrotermal através de 140h diminuiu a tenacidade da cerâmica VITA YZ em 17% (681,78 ± 121,18) quando comparado ao seu grupo controle (841,69 ± 56,01), enquanto que as zircônias de alta translucidez não mostraram diferenças estatísticas de resistência flexural após o envelhecimento. O envelhecimento hidrotermal induz a transformação da fase martensítica de fora para dentro do material e não afeta as propriedades mecânicas das cerâmicas VITA HT e INCORIS TZI, enquanto diminui a dureza do material da zircônia VITA YZ. / To evaluate, map and characterize the effects of the accelerated aging kinetics of high translucency zirconias, this study was split into 2 parts: One part evaluating the superficial changes after in vitro hydrothermal aging and the second part aiming the effects of this aging on the mechanical properties of those ceramics. 117 Y-TZP (VITA YZ, VITA HT, InCoris TZI) blocks were cut, 39 for each commercial zirconia, sintered (1530 ºC, 2h) and assigned to 13 groups with 3 samples each: One being a control, aging-free group, and 12 groups that were prematurely aged hydrothermally at 134 ºC and constant pressure of 2 bars through 6, 10, 14, 18, 22, 26, 30, 40, 60, 80, 100 and 140 hours. XRD was used to quantify the amount of zirconia phase transformation (tetragonalmonoclinic) on different depths of the material by swapping the anode tube (Cr, Co, and Cu). An aging kinetic curve was made for each depth for the 3 commercial zirconias. To evaluate the effects of the hydrothermal aging on the mechanical properties, Y-TZP blocks were rounded to a cilindrical shape. 270 discs were cut, 90 for each kind, sintered as mentioned above and assigned to 3 groups: C-Control; E1- Aged through 26h and E2- Aged through 140h. Disks were then tested in a universal testing machine (EMIC) under a load of 1000 kg till fracture of the specimen and the surface was evaluated under SEM. The aging kinetics curves work similarly for all the YTZP used in this study, characterized by phase transformation ascendant and plateau stabilization as far as the aging goes. Superficial layers present higher concentrations of monoclinic phase as it decreases in deeper layers. Hydrothermal aging through 140h decreased VITA YZ toughness by 17% (681,78 ± 121,18) when compared with its control group (841,69 ± 56,01), while high translucency zirconias didn't show any statistical differences after aging.Hydrothermal aging does induce martensitic phase transformation from the outside-to-inside the material and doesn't affect the mechanical properties of VITA HT and INCORIS TZI ceramics, while it decreased the material toughness of VITA YZ zirconia. / FAPESP: 16/03688-1

A característica de superfície representa um fator importante na previsibilidade do comportamento dos materiais cerâmicos quanto ao desgaste. A rugosidade superficial de duas cerâmicas (Duceram Plus e Duceragold) foi avaliada através de dois métodos - análise quantitativa e qualitativa - após diferentes tratamentos. Foram confeccionados 36 corpos de prova de prova para a análise ao rugosímetro, e 24 corpos de prova para a análise ao MEV. Os resultados destas análises demonstraram o comportamento distinto entre os diferentes tratamentos. A análise com o rugosímetro demonstrou que a ação dos polidores EDENTA foi a mais efetiva para devolver lisura à superfície após a realização de desgaste com instrumento abrasivo diamantado rotatório. Todas as técnicas de polimento acarretaram em valores de rugosidade menores que os observados nos espécimes que foram submetidos apenas os “glaze”. Entre as cerâmicas avaliadas, a Duceragold apresentou valores médios de rugosidade inferiores aos observados na porcelana Duceram Plus na maioria dos tratamentos pesquisados. Pela análise ao MEV não foi possível distinguir diferenças entre as cerâmicas ou entre os corpos de prova polidos ou submetidos apenas ao “glaze”. / The surface characteristic of ceramic material is an important factor to predict its wear behavior. The surface roughness of two ceramics (Duceram Plus e Duceragold) was evaluated trough qualitative and quantitative methods after different treatments. 36 specimens were fabricated for the analysis utilizing a surface profiling instrument, and 24 for the SEM analysis. The results determined different behavior between the two ceramics evaluated due the treatment executed. The analysis utilizing a surface profiling instrument showed that the treatment using the EDENTA polishers was the most effective technique to provide the smoothest surface after trimming. All polishing techniques resulted in better surface properties when compared to the treatment glaze. The Duceragold ceramic presented lower roughness values in most treatments executed when compared to Duceram Plus. The perception trough the SEM analysis of significant differences between treatments or between the two ceramics was not achievable.

O objetivo deste estudo foi analisar as propriedades mecânicas de cerâmicas à base de alumina e alumina-feldspato quando expostas a um meio agressivo (ácido acético 4%). Os corpos cerâmicos de alumina, contendo diferentes quantidades de feldspato (0, 1, 5, 10, 40 ou 100%), foram sinterizados a 1160, 1300, 1600 ou 1700ºC. Os espécimes foram divididos em três grupos de acordo com o tamanho do entalhe infligido (0, 30 ou 50% da largura do corpo-de-prova). Metade dos corpos cerâmicos foi exposta a uma solução de ácido acético a 4%. Os corpos cerâmicos sem e após ataque foram submetidos a ensaios para a determinação da resistência mecânica e do KIC; (por flexão a 4-pontos), área superficial (BET) e porosidade (método de Arquimedes). A microestrutura foi investigada por microscopia óptica e eletrônica de varredura, incluindo mapeamento por EDS, para a determinação da presença e distribuição de elementos químicos de interesse (C, O, Al, Si, K, Na, Mg). A solução lixiviada pelo ataque por ácido acético foi analisa para a determinação da concentração dos íons (Na+, Al+3, Si+4 e K+). Os resultados mostraram que os corpos cerâmicos sinterizados a 1700ºC, quando expostos ao ácido acético, diminuem sua resistência mecânica. Para os corpos cerâmicos sinterizados a 1600ºC a resistência mecânica não foi alterada. Nessas amostras, o KIC até aumentou após a exposição ao ácido acético. O ataque por ácido acético causou aumento na área superficial específica e do volume total de poros, o que foi confirmado pela concentração de íons na solução lixiviada pelo ataque por ácido acético. A fase vítrea, mesmo em pequenas quantidades, auxilia os corpos cerâmicos à base de alumina-feldspato a adquirir as propriedades mecânicas similares, ou até melhores, do que os corpos cerâmicos de alumina, dependendo da temperatura de sinterização. Isso sugere que é possível aperfeiçoar a formulação e a temperatura de queima de cerâmicas baseado na introdução de fase vítrea na microestrutura dos materiais, a fim de enfrentarem o rigor do ambiente oral. / This study investigates the mechanical properties of alumina-feldspar based ceramics when exposed to an aggressive environment (acetic acid 4%). Alumina ceramics containing different concentrations of feldspar (0, 1, 5, 10, 40 or 100%) were sintered at one of the temperatures 1160, 1300, 1600, or 1700oC. The samples were divided according to the inflicted flaws (of height 0, 30, or 50%). Half of these ceramic bodies were exposed to 4% acetic acid. The ceramic bodies whether or not exposed to acetic acid were tested in order to determine mechanical resistance and KIC (4 point bending test), superficial area (BET) and porosity (Archimedes). The microstructure was analyzed by optical and scanning microscopy, including element mapping performed by EDS to determine the presence and distribution of specific chemical elements (C, O, Al, Si, K, Na, Mg). The leachate solution was evaluated to determine the concentration of ions (Na+, Al+3, Si+4 e K+). The results showed that the ceramic bodies sintered at 1700oC decrease their mechanical resistance when exposed to acetic acid. The mechanical resistance for ceramic bodies sintered at 1600ºC was not altered. In these samples, the KIC even increased after acetic acid exposure. The acetic acid attack increased specific superficial area and total pore volume, which was confirmed by the ion concentration on the leachate solution. The glassy phase, even in small amounts, aids the alumina-feldspar based ceramics in acquiring similar or even better mechanical properties than alumina ceramic bodies, depending of sintering temperature. This suggests that is possible to enhance both formulation and sintering temperature of ceramics based on the introduction of glassy phase into the microstructure in order to face the rigors of the oral environment.

Orientador: Lourenço Correr Sobrinho / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-17T15:22:38Z (GMT). No. of bitstreams: 1 Ursi_WagnerJoseSilva_D.pdf: 1229988 bytes, checksum: 2fcbeb63eb27770fcbe7f8c7c3ecdd07 (MD5) Previous issue date: 2011 / Resumo: O objetivo neste estudo foi avaliar a influência de sistemas de polimento, da escovação mecânica e do repolimento sobre o brilho, rugosidade e morfologia da superfície de materiais cerâmicos. Três cerâmicas foram avaliadas: IPS Eris (Ivoclar Vivadent), Vita VM7 (VITA Zahnfabrik) e Cercon CS (Degudent). Trinta amostras cilíndricas padronizadas de cada material foram confeccionadas e aleatoriamente divididas em 3 grupos (n=10) sendo que cada grupo foi submetido a um dos três procedimentos de polimento (taça de borracha; disco de feltro+pasta diamantada; taça de borracha + disco de feltro + pasta diamantada). Após o polimento, o brilho da superfície polida foi mensurado com medidor de brilho (ZGM 1120 Glossmeter - Zehntner) e a rugosidade avaliada através de rugosímetro (Surfcorder SE1700 - Kosaka Lab.). As amostras foram submetidas a 30.000 ciclos mecânicos de escovação, utilizando solução de dentifrício e água deionizada. Após a escovação, as mensurações de brilho e rugosidade foram repetidas. Em seguida, as amostras foram submetidas novamente aos procedimentos de polimento, e o brilho e a rugosidade avaliados novamente. Inicialmente foi realizada análise exploratória dos dados pelo aplicativo GUIDED DATA ANALYSIS do SAS (SAS, 2008). A seguir, os dados foram analisados, segundo o conceito de medidas repetidas no tempo, empregando o procedimento PROC MIXED e teste de Tukey-Kramer. Adicionalmente, amostras polidas, escovadas e repolidas foram examinadas em microscopia eletrônica de varredura (5600LV - Jeol) para avaliação qualitativa da integridade da superfície. Com base nos resultados encontrados, pode-se concluir que a superfície dos materiais cerâmicos foi resistente aos efeitos da escovação mecânica dentro das variáveis utilizadas, e que, o uso da pasta diamantada e disco de feltro, embora tenha se mostrado eficiente na diminuição da rugosidade de superfície (Ra) para a maioria das cerâmicas avaliadas, não foi capaz de alterar os valores originais de brilho superficial. / Abstract: The purpose of this in vitro study was to evaluate the influence of polishing systems, mechanical toothbrushing and repolishing on surface gloss, roughness and morphology of dental ceramics. Three ceramic systems were evaluated: IPS Eris (Ivoclar Vivadent), Vita VM7 (VITA Zahnfabrik) and Cercon CS (Degudent). Thirty standardized cylindrical specimens of each material were fabricated and ramdomly divided in three groups (n=10), each group being submitted to one of the three polishing protocols (rubber cup; felt disc + diamond polishing paste; rubber cup + felt disc + diamond polishing paste). After polishing, surface optical gloss was determined using a gloss meter (ZGM 1120 Glossmeter - Zehntner) and surface roughness was measured with a surface profilometer ( Surfcorder SE 1700 -Kosaka Lab.). All specimens were submitted to 30,000 strokes at 2 Hz, with a dentifrice-water slurry. After mechanical toothbrushing, gloss and roughness measurements were evaluated again. Specimens were then repolished and submitted to gloss and roughness evaluations once more. Data were submitted to PROC MIXED and Tukey-Kramer tests. Aditionaly, randomly assigned specimens were evaluated for qualitative surface integrity under scanning electron microscopy (5600 LV-Jeol). Based on the results and the limitations of this in vitro study, it could be concluded that the surface of the ceramic materials tested was resistant to simulated toothbrushing challenge, and, the use of felt disc and diamond polishing paste, showed to be efficient in reducing surface roughness (Ra) for the majority of the tested ceramics, although unable to alter original surface gloss values. / Doutorado / Materiais Dentarios

Orientador: Marcelo Ferraz Mesquita / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-09T19:46:50Z (GMT). No. of bitstreams: 1 Nakaoka_MarciaMika_D.pdf: 1091285 bytes, checksum: 76d1bd5bef1fb0bee757a9f929be3f3a (MD5) Previous issue date: 2007 / Resumo: As distorções oriundas das técnicas de aplicação de revestimentos estéticos sobre infra-estruturas metálicas de próteses fixas podem resultar em margens cervicais desadaptadas. Dessa forma, este trabalho propôs-se a avaliar o efeito do tipo de revestimento estético, da simulação dos ciclos de cocção da cerâmica, e da aplicação da eletroerosão, sobre o desajuste de infra-estruturas implanto-suportadas fundidas em titânio comercialmente puro (Ti c.p.). Foi utilizada uma matriz metálica contendo 5 pilares intermediários do tipo Microunit. Sobre ela, foram enceradas 40 infra-estruturas, posteriormente fundidas em Ti c.p. (Tritan, Dentaurum, Alemanha). Para cada infraestrutura foi confeccionado um index, com 5 análogos parafusados em cada infra-estrutura. Esse conjunto foi posicionado em microscópio para a mensuração dos desajustes antes da aplicação dos revestimentos estéticos, com a finalidade de avaliar apenas desajuste provocado pela aplicação dos revestimentos estéticos e pelo ciclo de cocção da cerâmica. As infra-estruturas foram separadas, aleatoriamente: G1: resina acrílica ativada termicamente (Clássico, Clássico Artigos Odontológicos Ltda., São Paulo, Brasil); G2: resina fotopolimerizável (Versyo.com, Heraeus Kulzer, Brasil); G3: cerâmica (Triceram, Dentaurum J. P. Winkelstroeter KG ¿ Pforzheim - Alemanha); G4: simulação dos ciclos de cocção da cerâmica. Novamente, após a aplicação dos revestimentos estéticos, foi realizada a avaliação do desajuste marginal sobre o index. Procedeu-se o processo de eletroerosão (Tel Med Technologies, Port Huron, Michigan, EUA). As leituras de desajuste foram realizadas após o aperto com 10 Ncm em um único parafuso, correspondente ao implante A. Através desse procedimento, verificou-se a adaptação dos componentes C e E. O procedimento foi repetido com o outro implante mais distal (E), para mensuração nos implantes A e C. As leituras foram realizadas utilizando microscópio mensurador, com aumento de 120X e precisão de 0,5µm (Micro Vision ¿ Leika, Wetzlar, Alemanha), antes e após aplicação dos revestimentos estéticos, e após o processo de eletroerosão. Os resultados obtidos foram submetidos à Análise de Variância e ao teste de Tukey (p<0,05). Os valores de desajuste marginal das infra-estruturas antes da aplicação dos revestimentos estéticos não apresentaram diferença estatística significante entre si: G1: 29,81 'mu' (+ 10,66); G2: 35,30 'mu' (+ 12,15); G3: 44,75 'mu'(+ 13,73); G4: 38,57 'mu' (+ 16,94). A aplicação dos revestimentos estéticos e a simulação dos ciclos de cocção da cerâmica aumentaram significantemente os valores médios de desajuste marginal para todos os grupos: G1: 221,70 'mu' (+14,11); G2: 81,91 'mu' (+15,71); G3: 233,99 'mu' (+39,18); e G4: 119,75 'mu' (+38,08). Os grupos G1 e G3 não apresentaram diferença estatisticamente significante entre si, mas apresentaram diferença quando comparados aos G2 e G4. Após o processo de eletroerosão, apenas para o grupo G3: 161,16 µm (+36,59 ) a média de desajuste marginal apresentou-se com valor significamente menor. As médias de desajuste marginal para os grupos G1: 198,68 mu' (+34,19); G2: 62,03 'mu' (+17,73) e G4: 87,98 'mu' (+39,32) foram numericamente menores, porém, sem diferença estatística. Como ocorrido anteriormente, os grupos G1 e G3 não apresentaram diferença estatística significante, mas ambos apresentaram diferença quando comparados aos grupos G2 e G4. A partir dos resultados obtidos no presente estudo, conclui-se que os revestimentos estéticos em resina acrílica ativada termicamente e em cerâmica produziram os maiores valores de desajuste marginal para próteses implanto-retidas, enquanto a resina fotopolimerizável, os menores. A aplicação de cerâmica nas infra-estruturas produziu maiores valores de desajuste marginal quando comparado à simples simulação dos ciclos de cocção. O processo de eletroerosão mostrou-se eficaz na redução dos desajustes marginais apenas para o grupo com aplicação da cerâmica / Abstract: The demand for a passive fit of frameworks for osseointegrated endousseous implants abutments is well known, because the tightening of an inaccurate framework to the abutments can transmit stress to the bone-metal interface. The purpose of the present study was to evaluate the influence of the veneering application and porcelain firing cycle on the misfit level of implant-supported frameworks. Forty Ti c.p. (Tritan, Dentaurum, Germany) alloy frameworks were fabricated from a metallic index containing 5 Branemark type multi unit abutments. Analogs of the abutments were positioned to the framework, to construct an index for each framework. This index allowed the observation of the marginal gaps caused by the application of the veneering material. The frameworks were grouped (n=10): 1) heat acrylic resin (Clássico, Clássico, São Paulo, Brazil); 2) light polymerized resin (Versyo.com, Heraeus Kulzer, Brazil); 3) porcelain application (Triceram, Dentaurum - Germany); 4) simulation of porcelain firing cycle. Marginal refinement with spark erosion was conducted on specific equipment (Tel Med Technologies, U.S.A.). The marginal gap was obtained before and after the veneering materials and the spark erosion procedure, following the single screw test protocol (using a tightening force of 10 Ncm). A traveling microscope (STN ¿ Olympus Optical Co. Ltd Japan (120X) was used, tightening 10N in the titanium screw of the extremity distal implant, measuring the gaps at the central and distal implants. Data were subject Analysis of Variance followed by Tukey test (5%). Marginal gap mean values of the frameworks before the veneering application were not significantly different: G1: 29.81 'mu' (+ 10.66); G2: 35.30 'mu' (+ 12.15); G3: 44.75 'mu' (+13.73); G4: 38.57 'mu' (+ 16.94). The application veneering materials and the simulation of porcelain firing cycle increased significantly the misfit mean values of all groups: G1: 221.70 'mu' (+14.11); G2: 81.91 'mu' (+15.71); G3: 233.99 'mu' (+39.18); e G4: 119.75 'mu' (+38.08). There were no significant differences between G1 and G3, but they were significantly different from both G2 and G3. After the spark erosion process, marginal gap mean value decreased significantly only G3 group: 161.16 µm (+36.59). G1: 198.68 'mu' (+34.19); G2: 62.03 'mu' (+17.73) and G4: 87.98 'mu' (+39.32) groups decreased the marginal gap mean values, but not significantly after the spark erosion procedure. As occurred after the application of veneering materials, G1 and G3 groups did not show significant difference, but they both were significantly different from G2 and G4 groups. It can be concluded that heat cured acrylic resin and porcelain produced the highest mean values of marginal gaps, while light cured acrylic resin, the lowest. The application of porcelain produced higher misfit values than the simulation of porcelain firing cycles. After the spark erosion process, marginal gap mean value decreased significantly only porcelain application grou / Doutorado / Protese Dental / Mestre em Clínica Odontológica

Os objetivos deste trabalho foram: 1) avaliar o efeito do envelhecimento por ciclagem mecânica (1 milhão de ciclos a uma freqüência de 2 Hz) sobre a resistência à flexão biaxial de três materiais cerâmicos utilizados para a construção infra-estruturas de próteses parciais fixas: a) uma zircônia tetragonal policristalina estabilizada por ítria (Y-TZP); b) uma alumina policristalina (AL) e c) um compósito de alumina e zircônia infiltrado por vidro (ICZ) e 2) determinar a influência da tensão gerada durante a ciclagem sobre a degradação da resistência das cerâmicas estudadas, já que para cada material a ciclagem foi realizada com dois níveis diferentes de tensão. Material e método: Espécimes em forma de disco (12 mm x 2 mm e 12 mm x 1 mm) foram confeccionados conforme as recomendações dos fabricantes. A resistência à flexão desses materiais foi determinada por meio do ensaio de flexão biaxial. Para o grupo controle de todos os materiais estudados (espécimes de 1 mm de espessura), foi realizada estatística de Weibull para determinação da resistência característica (0) e módulo de Weibull (m). Após o envelhecimento por ciclagem mecânica, realizado para todos os materiais nas duas espessuras, os espécimes foram fraturados e os valores obtidos foram comparados com seus respectivos grupos controle. Resultados: O valor de m foi estatisticamente semelhante para todos os materiais, o ICZ (12,2) apresentou o maior valor comparado ao do Y-TZP (9,0) e do AL (8,4). Os valores de resistência característica, 0, apresentaram diferenças significantes para todos os materiais, 828 MPa para a Y-TZP, 405,8 MPa para a AL e 328 MPa para o ICZ. Não houve diferenças estatisticamente significantes entre as resistências medidas para os grupos controle e ciclado para nenhum dos materiais nas duas espessuras avaliadas. Conclusão: O envelhecimento por ciclagem mecânica não causou alterações significativas nos valores de resistência à flexão de nenhuma das cerâmicas testadas. O aumento no nível de tensão aplicada na ciclagem mecânica não gerou um aumento na degradação da resistência dos materiais estudados. / The objectives of this study were: 1) To evaluate the effect of aging by mechanical cycling (1 million cycles at a frequency of 2 Hz) on the biaxial flexural strength of three dental ceramics used as framework materials for fixed partial dentures (FPDs): a) yttria partially stabilized zirconia tetragonal polycrystals (Y-TZP), b) alumina polycrystals (AL) and c) alumina-based zirconia-reinforced glass infiltrated ceramic (ICZ) and 2) determine the influence of stress level generated during mechanical cycling on the flexural strength degradation of the studied ceramics. Materials and Methods: Disc-shaped specimens (12 mm x 2 mm and 12 mm x 1 mm) were prepared according to manufacturer\'s recommendations. The flexural strength of these materials was determined by biaxial flexure test for the control group of all materials. The Weibull statistics was performed to determine the characteristic strength (0) and Weibull modulus (m). After mechanical aging, the specimens were fractured and the values obtained were compared with their respective control groups. Results: No statistically significant differences were founded between the strength obtained for the control and cycled groups for any of the materials in the two thicknesses tested. The m value was similar for all materials, ICZ (12.2) which showed the highest value, followed by the Y-TZP (9) and AL (8.4). The values for characteristic strength (0) showed significant differences for all materials, 828 MPa for Y-TZP, 405.8 MPa for AL and 328 MPa for ICZ. Conclusion: Aging by mechanical cycling did not cause significant changes in the values of flexural strength for all the ceramics tested. The increase in the stress level during cyclic loading did not cause an increase in the strength degradation of the materials studied.

Os objetivos deste trabalho foram: a quantificação da microinfiltração e desadaptação antes e após cimentação de coroas totais cerâmicas, com quatro tipos de sistemas de infra-estrutura e a correlação entre desadaptação e microinfiltração. Após aprovação pelo Comitê de Ética da FOUSP, 40 terceiros molares humanos receberam coroais totais cerâmicas, sendo: 2 cerâmicas infiltradas por vidro (In-Ceram alumina Slip-Cast (S) e o bIoco In-Ceram Alumina CA-12 (CA)) e 2 cerâmicas de alumina policristalina (Procera/Nobel Biocare (P) e o bloco In-Ceram Al-20, CEREC In-Lab (CE)), (n=10). O espaço entre coroa e dente foi medido antes e depois da cimentação das coroas. Foram submetidos à ciclagem mecânica (100.000 ciclos, 8 Kgf, 4 Hz), térmica (700 ciclos, 5/55ºC por minuto), submersos em azul de metileno 0,5% por 4 horas e seccionados nos sentidos mésio/distal e vestíbulo/lingual. As imagens foram obtidas em estereomicroscópio (20X) e os dados de desadaptação foram submetidos à ANOVA (e Tukey). Os escores da microinfiltração foram submetidos à análise da concordância dos avaliadores e Kruskal-Wallis. Não houve diferenças significantes entre os sistemas cerâmicos (S= 38, P= 49, CA= 48 e CE= 39?m). O fator \"região\" da linha de cimentação apresentou diferenças estatísticas. A desadaptação foi maior na parede pulpar (60 ?m), seguida dos ângulos axio-pulpar e gengivo-axial (57 e 48 ?m, respectivamente). As paredes axiais e margens foram os locais de menor desadaptação (27 e 26 ?m, respectivamente). Houve diferença estatística entre as duas técnicas de medida, antes e após a cimentação (46 e 41?m, respectivamente). Houve diferença estatisticamente significante entre os quatro tipos de sistemas cerâmicos avaliados quanto à microinfiltração, onde S e CE apresentaram maiores níveis de infiltração, seguidos de P e CA. Não houve correlação entre microinfiltração e desadaptação. Concluiu-se que os quatro sistemas cerâmicos avaliados produziram coroas totais com linha de cimentação dentro dos limites clinicamente aceitáveis. / The objectives of this study were to quantify the microleakage and the loss of marginal adaptation before and after cementation of all-ceramic crowns, with four types of infrastructure systems, and to compare these parameters. After approval by the Committee on Ethics in Research of Dental School of University of São Paulo, 40 human third molars received all-ceramic crowns, 2 glass-infiltrated ceramics (In-Ceram alumina Slip-Cast (S) and the block In-Ceram Alumina CA-12 (CA) ) and 2 polycrystalline alumina ceramics (Procera / Nobel Biocare (P) and the block Ceram In-Al-20, CEREC In-Lab (EC) (n = 10). The gap between ceramic dental prosthesis and tooth was measured before and after cementation of the crowns. They were subjected to mechanical load cycling (100,000 cycles, 8 Kgf, 4 Hz), thermocycling (700 cycles, 5 / 55 ° C per minute), immersed in 0.5% methylene blue dye for 4 hours and then sectioned in the mesial / distal and buccal / lingual aspects. The images were obtained in stereomicroscope (20X) and the marginal fit data were evaluated by ANOVA (and Tukey test). The microleakage values were analyzed by the correlation analysis of examiners and the Kruskal-Wallis test. There were no significant differences between the ceramic systems (S = 38, P = 49, CA = 50 and CE = 39 ? m). The factor \"region\" of the cementation line has presented statistical differences. The loss of adaptation was higher on the pulpal wall (61 ? m), followed by gingival-axial (49 ? m) and axial-pulpal (58 ? m) angles. The axial walls and margins were the sites of the smallest displacement (27 and 26 ?m, respectively). There was statistical difference between the two techniques of measurement, before and after cementation (47 and 41 ?m, respectively). Statistically significant difference among the four types of ceramic systems was detected for microleakage, whereas S and CE showed higher levels of infiltration, followed by P and CA. However, no correlation was found between microleakage and loss of marginal adaptation. It was concluded that the four systems produced all-ceramic crowns with the line of cementation within clinically acceptable limits.

Objetivos: determinar a resistência à flexão em três pontos (f), módulo de Weibull (m), coeficiente de susceptibilidade ao crescimento subcrítico de trinca (n) e tenacidade à fratura (KIC) de três cerâmicas usadas para confecção de infraestrutura (IE) de próteses parciais fixas (PPFs) (YZ- zircônia tetragonal parcialmente estabilizada por óxido de ítrio; IZ- cerâmica a base de alumina infiltrada por vidro e reforçada com zircônia; AL alumina policristalina) e duas porcelanas (VM7 e VM9); avaliar o efeito da configuração (uma, duas ou três camadas) nos valores de f e modo de fratura dos corpos-de-prova (CP); avaliar a influência do material de IE, do tamanho dos conectores e da ciclagem mecânica (CM) na carga de fratura (CF) e distribuição de tensões de PPFs; relacionar o comportamento mecânico dos materiais cerâmicos testados na configuração de barra e de PPF. Material e Método: Foram produzidos três tipos de CP em forma de barra (2mm x 4mm x 16mm): monolítico, duas camadas e três camadas. As IE das PPFs foram confeccionadas utilizando o sistema CAD-CAM e recobertas com porcelana. Os ensaios de f foram realizados em saliva artificial a 37ºC. Os valores de m e n foram determinados pela análise de Weibull e ensaio de fadiga dinâmica, respectivamente. As PPFs foram carregadas no centro do pôntico até a fratura. Oito PPFs de cada grupo foram submetidas a CM com freqüência de 2 Hz e carga de 140 N durante 106 ciclos e, posteriormente, ensaiadas até a fratura. A distribuição de tensões nas PPFs foi avaliada com análise de elementos finitos (AEF). Os princípios da fractografia foram utilizados para determinar o padrão de fratura e os valores de KIC. Os dados de f e CF foram analisados estatisticamente com Kruskal-Wallis e Tukey (95%). Resultados: A YZ obteve o maior valor de f (860 MPa) seguida dos materiais IZ (411 MPa) e AL (474 MPa) que não apresentaram diferença estatística. Os menores valores de f foram encontrados para as porcelanas (65 MPa). Os valores de m foram semelhantes para os materiais, com exceção dos grupos IZ e VM7, que apresentaram diferença significante. Os maiores valores de n foram encontrados para as cerâmicas YZ (76) e AL (72), seguidos pela IZ (54) e pelas porcelanas (40). A YZ apresentou o maior valor de KIC. O material submetido à tensão de tração durante o ensaio determinou o valor de f das estruturas. As PPFs de YZ com conector de 16mm2 suportaram os maiores valores de CF. Houve influência significativa do tamanho de conector para o material YZ. A CM não influenciou os valores de CF das PPFs. O padrão de distribuição de tensões foi semelhante entre as PPFs. Foi observada uma boa relação entre os valores de tensão de fratura dos materiais de IE em forma de barra e de PPF. Foram encontradas diferenças no modo de falha dos CP em forma de barra e de PPF. Conclusão: a YZ apresentou o melhor comportamento mecânico tanto na configuração de barra como de PPF. / Objectives: to determine the flexural strength (f), Weibull modulus (m), slow crack growth coefficient (n) and fracture toughness (KIC) of three ceramics used as framework materials for fixed partial dentures (FPDs) (YZ- yttria partially stabilized zirconia tetragonal polycrystals; IZ- alumina-based zirconia-reinforced glass infiltrated ceramic; AL alumina polycrystals) and two veneering porcelains (VM7 and VM9); to evaluate the effect of the specimen design (one, two or three layers) in the f and fracture mode; to evaluate the influence of the framework material, connector size and mechanical cycling (MC) in the fracture load (FL) and stress distribution of FPDs; to relate the mechanical behavior of the ceramic materials tested using bar-shaped specimens and FPDs. Materials and Methods: Bar-shaped specimens (2mm x 4mm x 16mm) were produced in three different designs: monolithic, bilayer and trilayer. FPD frameworks were built using CAD-CAM system and veneered with porcelain. Specimens were tested for three point bending in 37ºC artificial saliva. Weibull analysis and dynamic fatigue testing were used to determine m and n values, respectively. FPDs were tested with a load applied in the middle of the pontic. Eight FPDs of each group were subjected to MC using a frequency of 2Hz and load of 140N for 106 cycles and were subsequently loaded to failure. Stress distribution for FPDs was evaluated using finite element analysis (FEA). Fractography principles were used to determine the fracture mode and KIC values. f and FL data were analyzed using Kruskal-Wallis and Tukey (95%). Results: YZ had the highest f value (860 MPa) followed by IZ (411 MPa) and AL (474 MPa). Lower f values were observed for the porcelains (65 MPa). Except for IZ and VM7, m values were similar among the ceramic materials. Higher n values were found for YZ (76) and AL (72), followed by IZ (54) and the veneering materials (40). YZ presented the highest KIC value. The f values were influenced by the material subjected to tensile stress during testing. YZ FPDs with 16mm2 connector showed higher FL values. There was significant influence of the connector size on the FL values for YZ material. MC had no influence in the FL values for the FPDs. The stress distribution was similar for all FPDs. Considering the framework material, there was a good agreement between the fracture strength values obtained for bar-shaped specimens and FPDs. Different fracture modes were observed for bar-shaped specimens and FPDs. Conclusion: YZ presented the best mechanical performance in both bar-shaped and FPD specimen configuration.