Made available in DSpace on 2014-06-12T18:07:11Z (GMT). No. of bitstreams: 2 arquivo7922_1.pdf: 2006759 bytes, checksum: e658b40f8129b04ae2bab24568ef6746 (MD5) license.txt: 1748 bytes, checksum: 8a4605be74aa9ea9d79846c1fba20a33 (MD5) Previous issue date: 2005 / As blendas poliméricas compostas por polímeros sintéticos e amido vêm ganhando importância na área de materiais por apresentarem boas propriedades e maior biodegradabilidade quando descartadas no meio ambiente. O presente trabalho teve por objetivo avaliar a capacidade biodegradadora de uma cultura mista dos fungos Talaromyces wortmannii e Phanerochaete chrysosporium numa blenda biodegradável de polietileno de baixa densidade (PEBD)/Amido, com aplicação na indústria de embalagens. A princípio foi feita uma seleção do tipo de amido pela avaliação do crescimento dos microrganismos. Em seguida, a blenda foi obtida pela mistura de PEBD/Amido 80/20% m/m num reômetro HAAKE a temperatura de 140oC por 10 min. O material foi exposto à cultura mista por um período de 165 dias. Os níveis de biodegradação dos filmes foram caracterizados antes e após a inoculação dos fungos através de análises de variação de massa, calorimetria diferencial exploratória-DSC, microscopia eletrônica de varredura-SEM e determinação da resistência à tração na ruptura e alongamento. Ainda foi realizado um monitoramento da produção de CO2 no processo de biodegradação por 90 dias, e um estudo cinético do crescimento dos fungos em meio Sabouraud modificado com amido. Os resultados mostraram que o amido do tipo anfótero (Foxhead®5901) apresentou um bom desempenho como componente para esse tipo de blenda. O consumo crescente e gradativo da blenda como fonte de carbono alternativa ficou evidente no acompanhamento da produção de CO2. Houve um acréscimo na massa dos filmes após exposição aos fungos pela sua impregnação no material. As análises de DSC mostraram que a processabilidade do PEBD não foi alterada com a adição de amido. O material apresentou uma significativa perda em propriedades mecânicas após contato com os fungos que, segundo evidenciado na SEM, consumiram o amido presente na matriz polimérica, gerando vazios e permitindo uma reorganização de sua estrutura. O fungo Phanerochaete chrysosporium apresentou como parâmetros cinéticos μmáx (h-1) = 0,10 e KS (g/L) = 8,50, enquanto que o fungo Talaromyces wortmannii μmáx (h-1) = 0,04 e KS (g/L) = 0,18, mostrando o quanto pode variar o comportamento de duas espécies de fungos distintas crescendo sobre as mesmas condições

Made available in DSpace on 2014-06-12T23:15:38Z (GMT). No. of bitstreams: 2 arquivo7432_1.pdf: 2032621 bytes, checksum: 08207254498102f66498fd2876c20c69 (MD5) license.txt: 1748 bytes, checksum: 8a4605be74aa9ea9d79846c1fba20a33 (MD5) Previous issue date: 2008 / Faculdade de Amparo à Ciência e Tecnologia do Estado de Pernambuco / A importância de fazer uma blenda, que é uma tecnologia relativamente recente, está associada ao fato de seu desenvolvimento ser menos oneroso do que o desenvolvimento de novos materiais por meio de métodos de síntese. Nesse estudo foi utilizada a blenda de poli(cloreto de vinila)/poliestireno (PVC/PS), nas composições 95/05, 90/10, 70/30, 50/50 e 30/70. Com o objetivo de estudar a miscibilidade da blenda PVC/PS, empregando as técnicas de viscosimetria pelos modelos de Krigbaum-Wall, Garcia et al. e Pan et al. em solução; espectroscopia no infravermelho com transformada de Fourier (FT-IR), índice de refração e microscopia eletrônica de varredura (MEV), foram igualmente utilizadas. Embora a análise de miscibilidade por viscosimetria seja de fácil execução, os resultados da blenda PVC/PS mostraram-se diferentes, quando foram comparados os três modelos propostos. O modelo de Pan et al. foi o que mais se aproximou dos resultados obtidos, junto às técnicas de FT-IR e índice de refração, onde o resultado foi de imiscibilidade da blenda PVC/PS em toda a sua extensão. Por outro lado, quando as blendas foram irradiadas, o PS comportou-se como agente radioprotetor da matriz do PVC, devido a dissipação de boa parte de energia absorvida na ressonância existente no interior dos anéis aromáticos. O fator de proteção do PS foi calculado em 78 e 70% para as proporções de 95/05 e 90/10, respectivamente. A radiação gama, na dose de 50 kGy, também atuou no sistema como agente compatibilizante na blenda de composição 95/05. Mudanças nas propriedades mecânicas dos filmes de PVC, PS e nas blendas PVC/PS, na dose de esterilização (25 kGy) também foram observadas neste estudo

This thesis set out to study the concept of non-human animals in En piga bland pigor (1914)and Kåtornas folk (1916) by the journalist and author Ester Blenda Nordström (1891-1948).By contextualizing contemporary views and ideas of non-human animals by the turn of the20th century, the conceptions are analyzed through different societal perspectives. How is themeeting between Nordström, as an emancipated upper-class woman, and the marginalisedgroups of people depicted in the books affecting her view of the non-human animals? Thisquestion originates from the understanding that the presence of non-human animals inhistorical material testifies not only of hierarchical relations and cultural notions but above allit shows something about humans. That is why this thesis uses contemporary ideas of animalwelfare, gender and hygiene to understand the intersectional connection between theconceptions of humans and animals. The study shows an ambivalence in the way of viewinghumans and animals, where expressed feelings of compassion are used both as a way ofindicating that the rights of exposed groups in society should be defended and at the sametime as a way of reinforcing boundaries. Boundaries between different groups of people,classes, humans and animals.

Den här uppsatsen utgår ifrån reportage ur reportageböckerna En piga bland pigor av Ester Blenda Nordström och Ok, amen: Om kärlek och fientlighet i chassidernas New York av Nina Solomin. Syftet är att, i jämförande form, ta reda på hur de gått till väga för att skildra en ny miljö i de utvalda reportagen ur respektive bok. Massmedieretorisk, lingvistisk och narratologisk analys blandas för att sätta ihop ett frågeschema med frågor som behandlar olika dimensioner av texterna. Det som undersöks är framför allt berättarteknik, berättarperspektiv, reporterroll och dolda värderingar, men också, utifrån narratologisk teori, hur olika typer av berättare påverkar texterna. Slutsatserna är att både Nordström och Solomin använder ett rikt bildspråk som förstärker stämningar och känslor och att de båda har tydliga aktörsroller i texterna. De dolda värderingar som visar sig i texterna hos båda reportrarna riktar framför allt kritik mot könsrollerna i de nya miljöerna. Det som skiljer dem åt är att Nordström i större utsträckning använder sig av värderande ord, överdrifter och adjektiv medan Solomin är mer för kontraster, och att Nordströms berättare är mer synlig och värderande än Solomins, vars texter oftare låter läsaren tolka det som händer själv.

Neste trabalho foram formados, sobre uma superfície de liga de alumínio AA7075-T6, revestimentos de polianilina (PANI) e da blenda polianilina/policloreto de vinila na proporção massa-massa de 1/1 (PANI/PVC 1/1), com diferentes espessuras. Os revestimentos foram avaliados quanto as suas habilidades na proteção da corrosão da liga de alumínio. Utilizou-se uma solução de NaCl 3,5%, como solução corrosiva em todos os ensaios de corrosão. A espessura dos revestimentos de PANI foi variada de 5 a 35 µm e estudou-se a relação entre espessura, rugosidade e hidrofobicidade e a proteção por estes revestimentos. Os revestimentos com espessuras de 12 a 23 µm apresentaram menor rugosidade, maior ângulo de contato e melhor proteção da corrosão verificada por medidas eletroquímicas, tais como espectroscopia de impedância eletroquímica e polarização linear. As imagens obtidas por microscopia eletrônica de varredura mostraram que os revestimentos de PANI são homogêneos e que não exibiam defeitos decorrentes da exposição no ambiente corrosivo. Já a blenda, apresentou um desempenho maior na proteção da corrosão quando comparado com a PANI pura. Medidas de espectroscopia de impedância eletroquímica e de polarização linear mostraram que a blenda possui alta resistência de polarização, com potenciais de corrosão estáveis e deslocados à região anódica para os eletrodos com revestimentos de maior espessura (26,3 ± 0,9 µm). Imagens obtidas por microscopia eletrônica de varredura e de força atômica, juntamente com a análise de composição por espectroscopia de energia dispersiva de raios-X (EDX) contribuíram para entender a maior eficiência de proteção promovida pela blenda. / In this study, an aluminum alloy (AA7075-T6) was coated with polyaniline (PANI) and polyaniline/polyvinyl chloride (PANI/PVC in 1:1 ratio by mass) blend coatings of different thickness. These coatings were evaluated for their ability to protect the aluminum alloy against corrosion. For studying the corrosion of aluminum alloy in saline environment, a 3.5% NaCl solution was used in all the corrosion tests. The thickness of PANI-based films was varied between 5 to 35 µm and the effect of film thickness, roughness and hydrophobicity on the corrosion protection properties of the coatings was evaluated. The coatings with thickness between 12 and 23 µm exhibited lower roughness, higher contact angles and better corrosion protection as confirmed by electrochemical measurements such as electrochemical impedance spectroscopy and linear polarization. Morphological analysis by scanning electron microscopy confirmed that the PANI coatings are homogeneous and present almost no defects upon exposure to the corrosive environment. Compared to pure PANI coatings, the coatings consisting of PANI/PVC blend presented better performance against corrosion. Electrochemical impedance spectroscopy and linear polarization measurements showed that the blends have high polarization resistance with stable corrosion potentials that are shifted to the anodic region for the electrodes with thicker coatings (26.3 ± 0.9 µm). Surface analysis by scanning electron microscopy, atomic force microscopy and elemental analysis by energy-dispersive X-ray spectroscopy were used to gather information that helped understanding the better corrosion resistance of PANI/PVC coatings.

Neste trabalho compósitos foram obtidos a partir da blenda comercial 100% biodegradável Ecovio® C2224 da BASF, uma blenda formada por 55% em massa de um copoliéster biodegradável, o Ecoflex® (poli[(adipato de butileno)-co-(tereftalato de butileno)]) e 45% em massa de PLA poli(ácido láctico). Como carga, utilizaram-se dois tipos de argilas comerciais do grupo das esmectitas, ambas predominantemente montmorilonitas: Cloisite Sódica® e Cloisite 30B®. Também foi utilizado como carga a sílica coloidal comercial Aerosil 200®, com área superficial de 200 m2/g e diâmetro médio de partícula 12nm. Os compósitos estudados, ambos contendo 5% e 10% em massa de cargas, foram preparados em uma extrusora de rosca dupla, acoplada a um reômetro de torque. O estudo foi dividido em três etapas: 1ª) etapa: Obtenção e caracterização dos compósitos de Ecovio®/ argila e Ecovio® / sílica; 2ª) etapa: Avaliação da fotodegradação do Ecovio® puro e dos compósitos obtidos; 3ª) etapa: Avaliação da biodegradabilidade do Ecovio® puro e dos compósitos após exposição em câmara de UV. As propriedades mecânicas dos compósitos antes e depois de serem submetidos à exposição em câmara de UV foram avaliadas por ensaios de resistência à tração e resistência ao impacto Izod. Os resultados obtidos na 1ª etapa deste trabalho indicaram aumento nos valores de módulo de elasticidade de todos os compósitos, em relação à blenda pura. Destacam-se as composições com 5% e 10% em massa de sílica coloidal, que apresentaram aumentos de até 115% nos valores de módulo de elasticidade, sem perdas significativas em resistência à tração, alongamento e resistência ao impacto, quando comparadas à fase matriz. Na 2ª etapa, a partir de 20 dias de exposição, todas as composições (blendas e compósitos) apresentam redução nas propriedades mecânicas em função do aumento do tempo de exposição à radiação UV. Na 3ª etapa, independente do tipo ou teor de carga presente na blenda, todas as composições apresentaram índices de biodegradabilidade, depois de 120 dias, de 40 a 60%, devido à prévia exposição à radiação UV. / In this work, composites were prepared with 100% biodegradable commercial blend Ecovio® C2224 BASF, a polymer blend composed of 55 wt% of a biodegradable copolyester, the Ecoflex®, poly [(butylene adipate) -co- (butylene terephthalate)], and 45 wt% of PLA poly(lactic acid). Two types of commercial clays of the smectite group, predominantly montmorillonites, were used as fillers: Cloisite Na+® and Cloisite 30B®. The commercial colloidal silica Aerosil 200®, with a surface area of 200 m2/g and an average particle diameter of 12 nm, was also used as filler. The composites containing 5 and 10 wt% of filler were obtained in a twin screw extruder coupled to a torque rheometer. This study was divided in three steps: 1st) Preparation and characterization of Ecovio®/clay and Ecovio®/silica composites; 2nd) Evaluation of the photodegradation of pure Ecovio® and of the composites; 3rd) Biodegradability assessment of pure Ecovio® and composites after exposure to UV chamber. The mechanical properties of the composites before and after the exposition to UV were evaluated by tensile and Izod impact strength. The results obtained in the 1st step showed an increase in the tensile modulus of all blends, especially for the compositions with 5 and 10 wt% of colloidal silica, which presented an increase of 115% in their tensile modulus values without significant reduction in impact and tensile strength and elongation, when compared to the pure blend. In the 2nd step, from 20 UV exposure days, all compositions (blends and composites), presented a significant reduction in the mechanical properties as a function of the increase of the UV radiation exposure time. In step 3, regardless of the filler type or content, all blend compositions showed biodegradability index, after 120 days, of 40 to 60%, due to the prior UV exposure.

Submitted by Luciana Ferreira (lucgeral@gmail.com) on 2014-08-12T14:14:55Z No. of bitstreams: 2 license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) Dissertacao Gardenia M Sousa.pdf: 3272476 bytes, checksum: 0bbaf9085a3e001da83af896e8c767aa (MD5) / Made available in DSpace on 2014-08-12T14:14:55Z (GMT). No. of bitstreams: 2 license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) Dissertacao Gardenia M Sousa.pdf: 3272476 bytes, checksum: 0bbaf9085a3e001da83af896e8c767aa (MD5) Previous issue date: 2012-04-18 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / The aim of this study was to produce and evaluate active biodegradable films produced with rice flour, poly(butylene adipate co-terephthalate) (PBAT), glycerol and potassium sorbate (0%, 1% , 3% and 5%) blends as well evaluate its application as active packaging for conservation of fresh lasagna pasta. Biodegradable films were produced by extrusion process and used to separate fresh pasta layers without preservative supplied by a pasta firm and stored at 7,0 ± 2,0 ° C. Films were analised for optical, water vapor permeability, mechanical and microstructural properties, and the latter two were also carried out after storage of fresh pasta for 45 days. A stability study was performed for six weeks in relation to microbiological, physical, and chemical aspects and to quantify the sorbic acid concentration migrated from biodegradable films to product. Films of rice flour, PBAT, glycerol and potassium sorbate blends showed good processability and allowed the production of films by blowing extrusion technology in pilot scale with compatible characteristics compare to commercial films. Rice flour proved to be an excellent material for the formulation of biodegradable films because it is a raw material from renewable source and low cost. The addition of potassium sorbate at a range of 1-5% didn t affect the mechanical properties of films and concentration of not less than 3% sorbate reduced opacity, however increased the water vapor permeability. The microbial multiplication was lower in fresh pasta containing sorbic acid migrated from the films. The moisture content decreased during the storage of fresh pasta with films containing potassium sorbate in which films retained water from products. The pH reduced in all treatments however more pronounced in the treatments without potassium sorbate due to fermentation process by psychrotrophics . This fermentation process was one of the factors determining fresh pasta shelf life. The color difference of fresh pasta ( E) with sorbic acid were superior at fresh pasta without preservative. The migration rate of sorbic acid from the films to fresh pasta was higher at films with 1% potassium sorbate. It is recommended to add 3% of potassium sorbate in biodegradable films of rice flour, poly(butylene adipate co-terephthalate) and glycerol, for conservation of fresh lasagna pasta because this concentration is sufficient to secure product and to promote shelf life extension near to the fresh pasta distributed commercially by the supplier, with the beneficit of having lower concentration of sorbic acid in the final product. / O presente estudo teve por objetivo produzir e avaliar filmes biodegradáveis ativos, produzidos a partir de blendas de farinha de arroz, poli(adipato co-tereftalato de butileno) (PBAT), glicerol e sorbato de potássio, nas concentrações de 0%, 1%, 3% e 5%, e avaliar sua aplicação, como embalagem ativa em massa alimentícia fresca tipo lasanha. Os filmes biodegradáveis foram produzidos por extrusão-sopro em balão, e intercaladas em massas alimentícias frescas sem conservante, fornecidas por uma empresa de massas, e armazenadas a 7,0 ± 2,0 °C. Os filmes foram avaliados quanto às propriedades óticas, de barreira ao vapor de água, mecânicas e microestruturais, sendo as duas últimas realizadas também após aplicação nas massas alimentícias durante 45 dias. Foi feito um estudo de vida útil das massas, por seis semanas, com relação aos aspectos microbiológicos, físicos e químicos, além de quantificar a concentração de ácido sórbico migrada dos filmes biodegradáveis para o produto. Os filmes de blendas de farinha de arroz, PBAT, glicerol e sorbato de potássio apresentaram boa processabilidade e permitem a produção de filmes pelo processo de extrusão-sopro em balão em escala piloto com características compatíveis aos dos filmes comerciais. A farinha de arroz mostrou-se um excelente material para a formulação de filmes biodegradáveis, pois é uma matéria-prima de fonte renovável e de baixo custo. A adição de sorbato de potássio na faixa de 1 a 5% não alterou as propriedades mecânicas dos filmes e concentração igual ou superior a 3% de sorbato reduziu a opacidade, porém, elevou a permeabilidade ao vapor de água. A multiplicação microbiana foi inferior nas massas alimentícias contendo ácido sórbico migrado dos filmes. O teor de umidade diminuiu, durante a armazenagem, nas massas intercaladas com filmes contendo sorbato de potássio, em que estes atuaram retendo a água dos produtos. O pH também sofreu redução, em todos os tratamentos, porém, mais acentuado nos tratamentos sem sorbato de potássio, pela fermentação das massas por microrganismos psicrotrófilos. Este processo fermentativo foi um dos fatores determinantes da vida útil das massas alimentícias. A diferença de cor das massas alimentícias ( E) com ácido sórbico foram superiores às intercaladas com filmes sem conservante. A taxa de migração de ácido sórbico dos filmes para as massas alimentícias foi maior nos filmes com 1% de sorbato de potássio. Recomenda-se a adição de 3% de sorbato de potássio em filmes biodegradáveis de farinha de arroz, poli(adipato co-tereftalato de butileno) e glicerol, para aplicação em massa alimentícia fresca tipo lasanha, uma vez que esta concentração é suficiente para garantir a segurança do produto, e promover a extensão de sua vida útil, próximo ao das massas distribuídas comercialmente pela empresa fornecedora, e com menor concentração de ácido sórbico no produto final.

Neste trabalho foram formados, sobre uma superfície de liga de alumínio AA7075-T6, revestimentos de polianilina (PANI) e da blenda polianilina/policloreto de vinila na proporção massa-massa de 1/1 (PANI/PVC 1/1), com diferentes espessuras. Os revestimentos foram avaliados quanto as suas habilidades na proteção da corrosão da liga de alumínio. Utilizou-se uma solução de NaCl 3,5%, como solução corrosiva em todos os ensaios de corrosão. A espessura dos revestimentos de PANI foi variada de 5 a 35 µm e estudou-se a relação entre espessura, rugosidade e hidrofobicidade e a proteção por estes revestimentos. Os revestimentos com espessuras de 12 a 23 µm apresentaram menor rugosidade, maior ângulo de contato e melhor proteção da corrosão verificada por medidas eletroquímicas, tais como espectroscopia de impedância eletroquímica e polarização linear. As imagens obtidas por microscopia eletrônica de varredura mostraram que os revestimentos de PANI são homogêneos e que não exibiam defeitos decorrentes da exposição no ambiente corrosivo. Já a blenda, apresentou um desempenho maior na proteção da corrosão quando comparado com a PANI pura. Medidas de espectroscopia de impedância eletroquímica e de polarização linear mostraram que a blenda possui alta resistência de polarização, com potenciais de corrosão estáveis e deslocados à região anódica para os eletrodos com revestimentos de maior espessura (26,3 ± 0,9 µm). Imagens obtidas por microscopia eletrônica de varredura e de força atômica, juntamente com a análise de composição por espectroscopia de energia dispersiva de raios-X (EDX) contribuíram para entender a maior eficiência de proteção promovida pela blenda. / In this study, an aluminum alloy (AA7075-T6) was coated with polyaniline (PANI) and polyaniline/polyvinyl chloride (PANI/PVC in 1:1 ratio by mass) blend coatings of different thickness. These coatings were evaluated for their ability to protect the aluminum alloy against corrosion. For studying the corrosion of aluminum alloy in saline environment, a 3.5% NaCl solution was used in all the corrosion tests. The thickness of PANI-based films was varied between 5 to 35 µm and the effect of film thickness, roughness and hydrophobicity on the corrosion protection properties of the coatings was evaluated. The coatings with thickness between 12 and 23 µm exhibited lower roughness, higher contact angles and better corrosion protection as confirmed by electrochemical measurements such as electrochemical impedance spectroscopy and linear polarization. Morphological analysis by scanning electron microscopy confirmed that the PANI coatings are homogeneous and present almost no defects upon exposure to the corrosive environment. Compared to pure PANI coatings, the coatings consisting of PANI/PVC blend presented better performance against corrosion. Electrochemical impedance spectroscopy and linear polarization measurements showed that the blends have high polarization resistance with stable corrosion potentials that are shifted to the anodic region for the electrodes with thicker coatings (26.3 ± 0.9 µm). Surface analysis by scanning electron microscopy, atomic force microscopy and elemental analysis by energy-dispersive X-ray spectroscopy were used to gather information that helped understanding the better corrosion resistance of PANI/PVC coatings.

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2018-01-23T13:48:58Z No. of bitstreams: 1 ErikDosSantosSilva_TESE.pdf: 6543895 bytes, checksum: 29c9b0e4741aa669a76be6f191b18cf7 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2018-01-24T14:05:43Z (GMT) No. of bitstreams: 1 ErikDosSantosSilva_TESE.pdf: 6543895 bytes, checksum: 29c9b0e4741aa669a76be6f191b18cf7 (MD5) / Made available in DSpace on 2018-01-24T14:05:43Z (GMT). No. of bitstreams: 1 ErikDosSantosSilva_TESE.pdf: 6543895 bytes, checksum: 29c9b0e4741aa669a76be6f191b18cf7 (MD5) Previous issue date: 2017-08-30 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior (CAPES) / A pesquisa em nanocomp?sitos de pol?meros e s?lica tornou-se foco de muitos pesquisadores nos ?ltimos anos devido ?s excelentes propriedades apresentadas quando comparadas aos componentes individuais. Neste trabalho foi realizado um tratamento de modifica??o superficial da s?lica com 3-aminopropiltriet?xisilano (APTES) para incorpora??o na blenda poli(metacrilato de metila)/poli(estireno-co-acrilonitrila) (PMMA/SAN) por meio de processamento em extrusora dupla rosca. Foi avaliado o efeito da adi??o de nanopart?culas de s?lica com e sem modifica??o superficial na estrutura e propriedades da blenda PMMA/SAN, com objetivo de promover melhores propriedades mec?nicas, sem comprometer a transpar?ncia dos materiais produzidos. Os materiais foram caracterizados por medidas de ?ndice de fluidez (MFI), ensaios mec?nicos de tra??o uniaxial, flex?o em 3 pontos, dureza Rockwell M (HRM) e Shore D, impacto Izod, reometria de placas paralelas, microscopia eletr?nica de transmiss?o (MET), ensaios de abras?o e risco. Os resultados reol?gicos indicaram que houve rea??o entre as nanopart?culas de s?lica tratadas com os pol?meros puros e com a blenda PMMA/SAN, mostrando-se uma t?cnica ?til para avaliar poss?veis rea??es durante o processo de extrus?o. Os nanocomp?sitos apresentaram um decr?scimo nas propriedades de resist?ncia m?xima ? tra??o, resist?ncia ao impacto e alongamento na ruptura, se comparado a blenda PMMA/SAN, que apresentou sinergismo nas propriedades de resist?ncia m?xima ? tra??o e alongamento na ruptura. Entretanto, as propriedades dos nanocomp?sitos com nanopart?culas de s?lica modificadas foram superiores aos nanocomp?sitos sem tratamento. A adi??o de s?lica tratada promoveu um aumento no m?dulo de elasticidade, dureza, abras?o e risco dos nanocomp?sitos produzidos. / Research on nanocomposites of polymers and silica has become the focus of many researchers in recent years because of the excellent properties presented when compared to individual components. In this work a surface modification treatment of silica with 3-aminopropyltriethoxysilane (APTES) was carried out for incorporation in the poly(methyl methacrylate)/poly(styrene-co-acrylonitrile) (PMMA/SAN) blend by processing in a twin screw extruder. The effect of the addition of silica nanoparticles with and without surface modification on the structure and properties of the PMMA/SAN blend was evaluated, aiming to promote better mechanical properties without compromising the transparency of the materials produced. The materials were characterized by flow index measures (MFI), mechanical tests of uniaxial traction, 3-point flexure, Rockwell M hardness (HRM) and Shore D, Izod impact, parallel plate rheometry, transmission electron microscopy (TEM), abrasion and scratch tests. The rheological results indicated that there was a reaction between the silica nanoparticles treated with the pure polymers and with the PMMA/SAN blend, showing a useful technique to evaluate possible reactions during the extrusion process. The nanocomposites showed a decrease in the properties of maximum tensile strength, impact strength and elongation at break when compared to PMMA/SAN blends, which showed synergism in the properties of maximum tensile strength and elongation at break. However, the properties of the nanocomposites with modified silica nanoparticles were superior to the nanocomposites without treatment. The addition of treated silica promoted an increase in the modulus of elasticity, hardness, abrasion and scratch of the nanocomposites produced.

Submitted by Maria Medeiros (maria.dilva1@ufcg.edu.br) on 2018-06-26T11:43:08Z No. of bitstreams: 1 UÉDSON ALEXANDRE DO NASCIMENTO - TESE (PPGCEMat) 2016.pdf: 2537041 bytes, checksum: 43e8f4d37a08e791d0323dc0ce915cb4 (MD5) / Made available in DSpace on 2018-06-26T11:43:08Z (GMT). No. of bitstreams: 1 UÉDSON ALEXANDRE DO NASCIMENTO - TESE (PPGCEMat) 2016.pdf: 2537041 bytes, checksum: 43e8f4d37a08e791d0323dc0ce915cb4 (MD5) Previous issue date: 2016-02-26 / Neste trabalho, blendas de polietileno de alta densidade com polietileno linear de baixa densidade metalocênico, PEAD/m-PELBD, foram preparadas empregando uma extrusora dupla rosca, cônica, contrarotacional interpenetrante e os efeitos do tipo e do teor do m-PELBD nas propriedades de impacto e de tração foram estudados. A blenda PEAD/m-PELBD com melhor relação de propriedades, tenacidade/rigidez, foi modificada com argila montmorilonita organofílica comercial Cloisite 20A, nos teores de 1, 3, 5 e 10 pcr, visando à obtenção de um híbrido com propriedades comparáveis, particularmente, em processamento e tenacidade/rigidez, às da resina de PEAD importada, PEAD Dowlex IP–10262, utilizada para fabricação de embalagens injetadas para o envase e transporte de produtos químicos perigosos. De acordo com os resultados da caracterização mecânica (impacto e tração), ficou evidenciado que o tipo e o teor de m-PELBD influenciaram nestas propriedades. Dentre os m-PELBDs estudados, Flexus 7200 e Flexus 9200, o Flexus 7200 resultou na melhor relação de propriedades e dentre os teores avaliados (10, 17 e 25%), o teor de 17% foi mais efetivo. A blenda PEAD/17% m-PELBD, blenda 7217, apresentou resistência à tração no escoamento comparável a da resina importada; resistência ao impacto 57,7% superior e módulo elástico 23,6% inferior. Como a rigidez da blenda 7217 foi inferior à da resina importada, a mesma foi modificada com a argila Cloisite 20A. De acordo com os dados de difratometria de raios X (DRX), a incorporação da argila à blenda 7217, em todos os teores estudados, não resultou na formação de nanocompósitos. Apesar disso, as propriedades de cristalinidade (determinada por calorimetria exploratória diferencial – DSC) e de estabilidade térmica (determinada por termogravimetria - TGA) da blenda 7217 modificada com 10 pcr de argila (7217AO-10), foram superiores as da blenda pura. A resistência à tração foi mantida, a resistência ao impacto diminuiu e o módulo elástico aumentou, em relação a blenda pura. Em comparação com a resina importada, a resistência à tração do híbrido 7217AO-10 foi 8% superior, a resistência ao impacto foi 12% inferior e o módulo elástico 7% inferior. De forma geral, a blenda 7217, modificada com 10 pcr de argila, apresentou processabilidade e propriedades mecânicas comparáveis as da resina importada (PEAD Dowlex IP–10262). / Blends of high density polyethylene with metallocene linear low density polyethylene, HDPE/m-LLDPE, were prepared by melt compounding in a twin-screw extruder. The m-LLDPE type and content effects on impact and tensile properties were studied. According to the results, these parameters influenced the properties of m-LLDPE. The blend prepared with m-LLDPE Flexus 7200 with the 17% concentration (7217 blend) showed the best properties. However, their hardness was lower than the HDPE Dowlex IP-10262 resin, used for dangerous chemicals transport containers manufacture. The 7217 blend was modified with organophilic montmorillonite (Cloisite 20A organoclay). The diffraction X-ray data (XRD) showed that the 7217 blend modification, with organoclay, on all studied concentrations, did not result in nanocomposites. Nevertheless, the crystallinity properties (determined by differential scanning calorimetry – DSC) and thermal stability (determined by thermogravimetric analysis – TGA) of the 7217 blend, modified with 10 phr of organoclay (7217AO-10) were higher than the pure blend. In addition, the modified blend showed decreased impact resistance, increased elastic modulus and the same tensile strength. As compared to Dowlex IP-10262 HDPE, the tensile strength of 7217AO-10 hybrid was 8% higher, the impact strength was 12% lower and the elastic modulus was 7% lower. In general, the processability and mechanical properties of 7217 blend, modified with 10phr of Cloisite 20A, were similar to that HDPE Dowlex IP-10262. Therefore, this hybrid has great use potencial for dangerous chemicals transport containers manufacture, replacing the HDPE Dowlex IP-10262 resin.