Made available in DSpace on 2014-06-11T19:31:05Z (GMT). No. of bitstreams: 0 Previous issue date: 2011-12-16Bitstream added on 2014-06-13T19:01:23Z : No. of bitstreams: 1 caruso_m_dr_arafcf_parcial.pdf: 72130 bytes, checksum: 0f5d046d009c41010ce608d7390634e2 (MD5) Bitstreams deleted on 2015-06-25T13:01:08Z: caruso_m_dr_arafcf_parcial.pdf,. Added 1 bitstream(s) on 2015-06-25T13:03:26Z : No. of bitstreams: 1 000682142_20151231.pdf: 71945 bytes, checksum: bd241f7f32244e4999c4ce1cf227b884 (MD5) Bitstreams deleted on 2016-01-04T10:26:47Z: 000682142_20151231.pdf,. Added 1 bitstream(s) on 2016-01-04T10:28:37Z : No. of bitstreams: 1 000682142.pdf: 1232603 bytes, checksum: c1d0330a8cc50cbfbeefd9d4de058538 (MD5) / Universidade Estadual Paulista (UNESP) / O propósito desse trabalho, dividido em dois experimentos, foi estudar os efeitos da Lactoferrina (Lf) em três situações de injúria tecidual. Todas as análises estatísticas consideraram nível de significância (alfa) p < 0,05. O Experimento I abordou a cicatrização de feridas cutâneas abertas, induzidas cirurgicamente. Utilizaram-se seis coelhos da espécie Oryctolagus cuniculus, machos, com seis semanas de idade. Realizaram-se na região dorsal, duas incisões na pele, com 10 mm de diâmetro. A cada 24 horas, uma ferida (FL) recebeu 1mL de Lf a 100µg/mL em solução salina e a outra (FC) somente solução salina. Fotografou-se diariamente para análise morfométrica. No décimo dia removeram-se retalhos do tecido de cicatrização para estudo histológico, histoquímico e imunohistoquímico dos elementos cicatriciais. Os resultados mostraram para FL maior: proliferação vascular (p < 0,01), fibroblástica (p < 0,01) e de mononucleares (p < 0,001); intensidade de colagenização (p < 0,01), reepitelização (p < 0,01), deposição de colágeno tipo I (p < 0,01); e melhor índice de Maturação (IMac) (p < 0,01). O número e área dos miofibroblastos foram maiores para FL com p < 0,001. A redução da área... / The purpose of this work, divided into two experiments, was to study the effects of Lactoferrin (LF) in three situations of tissue injury. All statistical analysis found significance level (alpha) p <0.05. Experiment I addressed the healing of open wounds, surgically induced. We used six species of rabbits Oryctolagus cuniculus, males, six weeks old. Performed in the dorsal region, two skin incisions, with 10mm diameter. Every 24 hours, a wound (FL) received 1 mL of the Lf 100µg/mL saline and the other (FC) only saline. Photographed daily to morphometric analysis. On the tenth day, flaps of the scar tissue were removed, for the histological, histochemical and immunohistochemical evidence of scarring. The results showed greater for FL: vascular proliferation (p < 0.01), fibroblastic (p < 0.01) and mononuclear (p < 0.001), intensity of collagen (p < 0.01), re-epithelialization (p < 0,01), deposition of collagen type I (p < 0.01), and better rate of maturation (iMac) (p < 0.01). The number and area of myofibroblasts were... (Complete abstract click electronic access below)

O estudo sobre tratamentos de feridas é constante por ser uma enfermidade que atinge grande parte da população mundial, abrangendo desde queimaduras até doenças mais graves como diabetes. Com isso, busca-se um melhor recobrimento que substitua as funções epiteliais sem que haja contaminações por microrganismos. Um biopolímero muito estudado para este fim é a quitosana. Ela é derivada da quitina e encontrada principalmente em exoesqueletos de insetos e crustáceos. A uva é uma fruta rica em compostos fenólicos que se concentram principalmente na casca, semente e engaços. Tanto a quitosana quanto a uva possuem propriedades cicatrizantes, anti-inflamatórias e antibacterianas. Assim, por meio deste estudo foram desenvolvidas e caracterizadas membranas de quitosana acrescidas de extrato de uva para potencial aplicação no tratamento de feridas cutâneas. Uma primeira etapa deste estudo foi a obtenção e caracterização do extrato da cultivar Jacques (Vitis bourquina), considerando a baga inteira. O extrato foi obtido por maceração hidroalcoolica de etanol 50% v/v. A partir do extrato pronto, seguiu-se para as análises qualitativas e semi-quantitativas, além da atividade antirradicalar, análise de FTIR, para que fosse possível caracterizar os compostos ali presentes, e análise da atividade antimicrobiana. As análises qualitativas e semi-quantitativas apontaram para a presença de compostos fenólicos e taninos condensados no extrato. O espectro de FTIR comprovou a existência de grupos hidroxilas pertencentes a compostos fenólicos e água. Também pode-se observar a presença de bandas relacionadas a moléculas aromáticas derivados de pirano referente a taninos condensados. O extrato mostrou baixa atividade antirradicalar comparada com os padrões quercetina e ácido gálico, possivelmente em razão da pequena presença de flavonoides. Com relação à análise antimicrobiana, a concentração do extrato empregada não apresentou formação de halo de inibição para as bactérias analisadas. Na segunda etapa da pesquisa, as membranas foram sintetizadas e caracterizadas quanto aos teores de umidade, comportamento hídrico, solubilidade, permeabilidade ao vapor d’água e também analisadas pelo FTIR, DSC, MEV e análise da atividade antimicrobiana. As membranas contendo quitosana e extrato de uva apresentaram uniformidade em sua composição e transparência, fator ideal para a manutenção das feridas cutâneas. Elas também apresentaram umidade, capacidade de absorção de água e passagem de vapores de água satisfatórios, mantiveram a integridade no teste de solubilidade, e ainda, mostraram resistência térmica acima da temperatura corpórea. Por meio destas análises e também pelo expectro de FTIR foi possível averiguar a interação entre a quitosana e o extrato. Entretanto, a atividade antibacteriana não foi observada em nenhuma membrana. Conclui-se que o método de extração empregado foi eficiente, pois no extrato obtido há presença de compostos cicatrizantes de interesse, assim como as membranas de quitosana acrescidas deste extrato apresentaram propriedades satisfatórias para aplicação no tratamento de feridas cutâneas. / The study is a constant on wound treatments illness that affects a large part of the world population, ranging from burns to more serious diseases such as diabetes. Thus, a better coating is proposed that replaces epithelial functions without contamination by microorganisms. A very studied biopolymer for this purpose is chitosan. It is derived from chitin and found mainly in exoskeletons of insects and crustaceans. Grape is a fruit rich in phenolic compounds that concentrate mainly on skin, seed and stalks. Both chitosan and grape have healing, anti-inflammatory and antibacterial properties. Thus, through this study were developed and characterized chitosan membranes plus grape extract for potential application in the treatment of cutaneous wounds. A first step of this study was the obtaining and characterization of the extract of the cultivar Jacques (Vitis bourquina), considering the whole berry. The extract was obtained by hydroalcoholic maceration of 50% v / v ethanol. From the ready-made extract, the qualitative and semi-quantitative analyzes were followed, besides the anti-radicular activity, FTIR analysis, so that it was possible to characterize the compounds present, and analysis of the antimicrobial activity. The qualitative and semi-quantitative analyzes indicated the presence of phenolic compounds and condensed tannins in the extract. The FTIR spectra showed the existence of hydroxyl groups belonging to phenolic compounds and water. It is also possible to observe the presence of bands related to aromatic molecules derived from pyran referring to condensed tannins. The extract showed low antiradical activity compared to the quercetin and gallic acid standards, possibly due to the small presence of flavonoids. Regarding the antimicrobial analysis, the concentration of the extract used did not present inhibition halo formation for the analyzed bacteria. In the second stage of the research, the membranes were synthesized and characterized by moisture content, water behavior, solubility, water vapor permeability and also analyzed by FTIR, DSC, SEM and analysis of antimicrobial activity. The membranes containing chitosan and grape extract presented uniformity in composition and transparency, an ideal factor for the maintenance of cutaneous wounds. They also showed satisfactory moisture, water absorption capacity and passage of water vapors, maintained integrity in the solubility test, and also showed thermal resistance above body temperature. Through these analyzes and also by the FTIR expectation, it was possible to verify the interaction between the chitosan and the extract. However, antibacterial activity was not observed on any membrane. It is concluded that the extraction method employed was efficient, because in the extract obtained there are presence of healing compounds of interest, as well as the chitosan membranes added with this extract had satisfactory properties for application in the treatment of cutaneous wounds.

Atualmente é de grande interesse a fabricação de novos materiais para o recobrimento de feridas de pele. A quitosana (QUIT) é um material funcional por suas características de biodegradabilidade, biocompatibilidade e não toxicidade. Além disso, pode acelerar a cicatrização de feridas e se mostra hemostática e bactericida. A policaprolactona (PCL) é um poliéster com propriedades compatíveis e biodegradabilidade, encontrado em várias aplicações biomédicas, como liberação controlada de fármacos. O copolímero de metoxi polietileno glicol (mPEG) e PCL, o mPEG-PCL, é um copolímero anfifílico biodegradável, tornando possível a interação da PCL (hidrofóbica) com a QUI, que é hidrofílica. A gentamicina (GE), também hidrofílica, é um dos antibióticos mais utilizados devido ao seu baixo custo e boa estabilidade. Nesta pesquisa foram preparadas membranas de QUIT com mPEG-PCL e GE, as quais foram caracterizadas por microscopia eletrônica de varredura (MEV), colorimetria, analise na região do infravermelho (FTIR), termogravimetria (TG), calorimetria diferencial exploratória (DSC), umidade e porcentagem de intumescimento. Ainda, foram realizados ensaios de liberação de GE in vitro e da atividade antimicrobiana, utilizando Escherichia coli e Staphylococcus aureus. A distribuição uniforme do copolímero mPEG-PCL na matriz de QUIT e a presença de GE na superfície das mesmas foram observadas nas micrografias de MEV e comprovadas por FTIR. Além disso, não houve alteração significativa na cor L das membranas, que se mostraram translucidas, propriedade importante para recobrimentos de ferida. Por DSC, obteve-se temperaturas de fusão intermediarias, comparando-se com as da QUIT e do mPEG-PCL, porém superiores à temperatura corpórea (37⁰C). A TG mostrou perda de massa das membranas em temperaturas superiores a 37⁰C. As membranas foram capazes de absorver tampão, simulando os fluidos exsudados da ferida e apresentaram cerca de 15% de umidade. Nos testes de atividade antimicrobiana, foi possível observar halo de inibição ao redor das membranas carregadas com GE, que teve uma liberação inicial menor na membrana com maior concentração de mPEG-PCL no ensaio de liberação in vitro. / It is currently of great interest to the manufacture of new materials for covering skin wounds. Chitosan (QUIT) is a functional material for its biodegradability characteristics, biocompatibility and non-toxicity. Furthermore, it can accelerate wound healing and hemostatic and bactericidal shown. Polycaprolactone (PCL) is a polyester with consistent properties and biodegradability, found in various biomedical applications such as controlled drug release. Methoxy polyethylene glycol copolymer (mPEG) and PCL, mPEG-PCL, is a biodegradable amphiphilic copolymer, making possible the interaction of PCL (hydrophobic) with QUIT which is hydrophilic. Gentamicin (GE) also hydrophilic, is one of the most widely used antibiotics due to its low cost and good stability. In this research were prepared QUIT membranes with mPEG-PCL and GE, which were characterized by scanning electron microscopy (SEM), colorimetry, look in the infrared (FTIR), thermogravimetry (TG), differential scanning calorimetry (DSC) humidity and percentage of swelling. Furthermore, GE release assays and in vitro antimicrobial activity were conducted using Escherichia coli and Staphylococcus aureus. The uniform distribution of the mPEG-PCL copolymer QUIT matrix and the presence of GE on their surface were observed in the SEM micrographs and tested by FTIR. Moreover, there was no significant change in color L membrane, which showed translucent, important property for wound coverings. DSC was obtained intermediate melting temperatures, comparing with the QUIT and mPEG-PCL, but higher than body temperature (37⁰C). The TG showed weight loss of membranes at temperatures above 37⁰C. The membranes were capable of absorbing buffer simulating the exuded fluids from the wound and had about 15% moisture. In the antimicrobial activity test, we observed inhibition halo around the charged membranes with GE, which had a lower initial release in the membrane with the highest concentration of mPEG-PCL in vitro release test.

Made available in DSpace on 2013-08-07T19:03:33Z (GMT). No. of bitstreams: 1 000438172-Texto+Completo-0.pdf: 1191521 bytes, checksum: 237c9b927e3f38af88fb5e0c217da2cf (MD5) Previous issue date: 2012 / Wound healing represents a dynamic physiological process initiated and influenced by many factors. Nanocrystalline silver have been demonstrated to have antimicrobial and anti-inflammatory properties, whereas papain is a proteolytic enzyme, which has been used in different formulations for wound treatment in clinics. Objectives This study was conducted to further evaluate the wound healing activity of nanocrystalline silver dressings as compared to that obtained with 2% papain gel, for the treatment of acute wounds in rats and the impact on VEGF expression. Forty-eight male Wistar rats were randomly divided into four groups. Group 1: treated with saline solution (NaCl 0. 9%); group 2: treated with nanocrystalline silver; group 3: treated with the excipient gel; group 4: treated with 2% papain gel. A full-thickness wound of 1. 5 x 1. 5 cm² was excised from the back of the rats, under aseptic conditions and were anesthetized by a mixture of ketamine and xylazine. All the animals were evaluated on the 3rd, 6th, 9th, 12th and 15th days for wound-healing rating and histological evaluation and imunohistochemistry for VEGF.The statistical analysis was performed ANOVA, followed by Bonferroni’s test. The group treated with the nanocrystalline silver dressing, showed a healing ratio superior, in all periods, when compared to control group and was the unique showing complete wound healing at 15 days of evaluation. The 2% papain gel group, a significantly higher wound healing rate was observed only at the 3th and the 6th days, but the wound showed a bleeding and decrease of wound healing ratio from the 9th day on. Histological evaluation showed a fully matured and compact granulation tissue on the nanocristaline silver group. The others groups displayed thickned epidermis, with extensive areas of inflammation. Evident immunopositivity for VEGF was also seen in the granulation tissue layer at the 9th day, the nanocrystalline silver group showed a higher VEGF expression in blood vessels, epidermal cells and granulation tissue. In this work, based on both the qualitative and the quantitative analysis, the nanocrystalline silver group showed a better wound healing effect in view of a rapid contraction of wound, compared with the others groups. Furthermore, we show for the first time that pro-healing activities of nanocrystalline silver dressings are likely associated to the modulation of VEGF expression. / O processo de cicatrização representa uma cascata de eventos dinâmicos iniciados e influenciados por diversos fatores. A prata nanocristalina tem demonstrado uma ação antimicrobiana e anti-inflamatória em diversos estudos, enquanto a papaína, além da ação anti-inflamatória, é usada no desbridamento de feridas, por ser uma enzima proteolítica. A ação da papaína depende da sua concentração que varia de 1% a 10%. Esse estudo foi conduzido com o objetivo de avaliar a ação da prata nanocristalina e da papaína gel 2% sobre o processo de cicatrização em ratos e o impacto dessas substâncias sobre a expressão de VEGF. Foram randomizados 48 ratos Wistar em 4 grupos. Grupo 1: tratado com solução salina; grupo 2: tratado com prata nanocristalina; grupo 3: tratado com gel excipiente; grupo 4: tratado com papaína gel a 2%. Foi realizado uma excisão de espessura total no dorso do animal, medindo de 1,5 x 1,5 mm. Foi respeitada técnica asséptica rigorosa e o animal foi anestesiado com xilazina e quetamina por via intraperitoneal. Todos os animais foram avaliados no 3º, 6º, 9º, 12º e 15º dia. As lesões foram fotografadas e analisadas pelo Programa Image J para estimar a área. Foram recolhidas amostras das lesões nos diferentes períodos de avaliação para análise histológica e imuno-histoquimica para VEGF.A análise estatística foi feita pelo teste de análise de variância (ANOVA), seguido pelo Teste de Bonferroni, utilizando programa Graphped 4. O grupo tratado com a prata nanocristalina, apresentou cicatrização completa ao final de 15 dias, diferente dos outros grupos. O grupo tratado com papaína gel 2% apresentou uma maior taxa de cicatrização no 3º e 6º dia, que se manteve estável a partir do 9º dia. A avaliação histológica mostrou um tecido de granulação maduro no grupo da prata nanocristalina. Os outros grupos apresentaram uma epiderme espessa com extenso infliltrado inflamatório. Foi evidente a imunopositividade para VEGF no grupo da prata nanocristalina, principalmente no 9º dia de tratamento. Nesse trabalho, baseado tanto na análise quantitativa como qualitativa, o grupo tratado com prata nanocristalina mostrou uma melhor taxa de cicatrização, evidenciado por uma mais rápida contração da ferida, comparada com os outros grupos. Além disso, evidenciamos que a ação pró cicatrização da prata nanocristalina está associada com a modulação da expressão de VEGF.

Made available in DSpace on 2013-08-07T19:05:02Z (GMT). No. of bitstreams: 1 000449056-Texto+Completo-0.pdf: 2018454 bytes, checksum: e1cb8245a85f0c29d0e1f07814420e60 (MD5) Previous issue date: 2013 / Chronic cartilage lesions, like septal and auricular perforations, are easily found at the otolaryngologist office. Its treatment is a challenge for physicians and patients, due to few alternatives and limit success. With the objective to decrease the surgical procedures, it’s been studying alternative methods for the total regeneration of the cartilaginous defects. The use of cellular therapy had been used in some cases, but there are no chronic cartilaginous protocols well written in the medical literature to compare the different results. This paper has the objective to describe a chronic cartilaginous lesion in an experimental model, for future studies with cellular therapy. / Lesões cartilaginosas crônicas, como as perfurações septais e auriculares, são facilmente encontradas no consultório do otorrinolaringologista. Seu tratamento é um desafio tanto para o médico quanto para o paciente, devido a poucas alternativas e sucesso limitado. Com o objetivo de diminuir a morbidade dos procedimentos cirúrgicos, cada vez mais têm sido estudados métodos alternativos para a regeneração completa dos defeitos cartilaginosos. O uso de terapia celular já está sendo utilizado em alguns casos, porém não há protocolos de lesões cartilaginosas crônicas bem descritos na literatura médica a fim de se obter comparações adequadas desses resultados. Este trabalho tem por objetivo descrever uma lesão cartilaginosa crônica em um modelo experimental, para estudos futuros com terapia celular.

Introdução. O tratamento de hérnia, independentemente do sítio anatômico e da técnica utilizada, geralmente envolve o uso de próteses, que, apesar de sua indiscutível vantagem em permitir um reforço seguro, podem causar complicações. Um exemplo é a possível retração, que ocasiona desconforto e recidiva da hérnia. Dentro de muitos biomateriais disponíveis, o polipropileno permanece sendo o mais utilizado. O objetivo deste estudo é avaliar o grau de retração da tela de polipropileno, bem como as reações histológicas que acompanham este fenômeno. Métodos. Foram inseridas telas de polipropileno (MarlexR) anteriormente à aponeurose abdominal íntegra de 25 ratos Wistar (Ratus novergicus albinus). Os animais foram divididos em grupos e reintervidos em 7, 28 e 90 dias, para aferição das dimensões das próteses e cálculo da área final. A análise histológica foi realizada com hematoxilina-eosina para avaliação de neutrófilos, macrófagos, gigantócitos e linfócitos circundando os fios da tela, em 10 campos aleatórios de cada lâmina. Resultados. Em 7 dias da inserção das telas, a taxa média de retração foi de 1,75% (p 0,64); em 28 dias foi de 3,75% (p 0,02) e em 90 dias foi de 2,5% (p 0,01). Quanto à análise histológica, houve um declínio total de neutrófilos e um aumento progressivo de macrófagos, células gigantes e linfócitos, proporcional ao tempo pós-implantação da malha (p < 0,05). Conclusão. Houve retração estatisticamente significativa de 3,75% aos 28 dias e de 2,5% aos 90 dias de inserção da prótese. Há uma seqüência de eventos celulares bem estabelecidos, tendo como destino a síntese de um novo tecido conjuntivo de reforço sobre a tela.

Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Química, Florianópolis, 2015. / Made available in DSpace on 2015-11-17T03:10:21Z (GMT). No. of bitstreams: 1 336046.pdf: 2171162 bytes, checksum: 3d321276a4678c89b18491a4aa1a2fa5 (MD5) Previous issue date: 2015 / A engenharia tecidual é uma área de pesquisa que objetiva tratar, manter ou reparar tecidos animais. A cicatrização de feridas, em particular, é um assunto de grande interesse. Há uma grande necessidade de se desenvolver materiais curativos, para que se obtenha melhores resultados, comparados aos existentes. Novos biomateriais com capacidade de funcionalização são promissores, como é o caso da combinação de nanocelulose e de colágeno. O objetivo deste trabalho foi extrair, caracterizar e incorporar colágeno extraído de pele de Rana catesbeiana (rã-touro) em membranas de nanocelulose, com a finalidade de desenvolver biopolímeros com propriedades aplicáveis à cicatrização de feridas. Foi possível extrair colágeno da pele de rã-touro e quantificar as proteínas totais (214 µg) e a fração de colágeno (172 µg) por grama de pele, ressaltando a quantificação como o diferencial deste trabalho comparado à literatura. O material extraído da pele de rã-touro foi caracterizado quanto ao perfil eletroforético e à temperatura de desnaturação, revelando que o colágeno extraído é do tipo I, com massa molar de 253 kDa e temperatura de desnaturação de 30,08 °C. O biomaterial foi produzido pela incorporação do colágeno em membranas de nanocelulose. As propriedades pretendidas do biopolímero foram caracterizadas quanto à morfologia 2D e 3D, temperatura de transição vítrea e de fusão, estabilidade térmica e quanto aos grupamentos funcionais. As análises 2D e 3D de microestrutura mostraram o entrelaçamento do colágeno nas fibras de nanocelulose quando na forma biopolimérica, enquanto as análises térmicas indicaram que os biopolímeros apresentam estabilidade necessária à aplicação como cobertura de feridas. O colágeno extraído apresentou bandas características de colágeno e as mesmas puderam ser identificadas após a incorporação do mesmo à nanocelulose. A ação do colágeno e do biopolímero na cicatrização in vitro foi avaliada. O ensaio de ferida permitiu concluir que o colágeno de rã-touro atua expressivamente, de modo a acelerar o processo de fechamento da ferida, este processo ocorrendo mesmo em baixas concentrações de colágeno . Este trabalho demonstrou que é possível extrair, quantificar e incorporar colágeno de rã-touro em membranas de nanocelulose e que o biopolímero desenvolvido possui as propriedades necessárias à utilização em processos de cicatrização de feridas.<br> / Abstract : Tissue engineering is a research area that aims to treat, maintain or repair animal tissues. Wound healing, in particular, is a subject of great interest, and there is an increasing need to develop curative materials displaying better healing properties compared to existing ones. New biomaterials showing capacity for functionalization, such as the combination of nanocellulose and collagen, area promising field of research in this area. The objective of this study was to extract, characterize and incorporate collagen from the skin of Rana catesbeiana (bullfrog) in nanocellulose membranes, in order to develop biopolymers with properties suitable for wound healing. The material extracted from bullfrog skin was quantified as the total protein content (214 µg) and collagen (172 µg) per grams of skin, highlighting the quantification as the differential of this work compared to literature. The obtained collagen was characterized for the electrophoretic profile and denaturation temperature, results indicating that the extracted collagen is type I, with molecular weight of 253 kDa and denaturation temperature of 30.08 °C. The biopolymer was produced by the incorporation of collagen in nanocelulose membranes. The desired properties of the biocomposite were characterized for 2D and 3D morphology, glass transition and melting temperature, thermal stability and for functional groups. The 2D and 3D analysis of microstructure showed interlacing collagen fibers amongst nanocelulose, when in the biopolymeric form. The showed collagen characteristic bands and the same was observed when it was incorporated in the nanocelulose. The wound healing assay showed that the bullfrog collagen shows significantly effect in accelerating the process of wound closure, and that this process occurs even at low collagen concentrations. This work showed that it is possible to extract, quantify and incorporate bullfrog collagen in nanocelulose membranes and that the biopolymer obtained has the properties/functions required for use in wound healing.

Dissertação (mestrado) - Pontifícia Universidade Católica do Paraná, Curitiba, 2006 / Inclui bibliografia / A isquemia intestinal é uma das mais sérias alterações intra-abdominais, com morbidade e mortalidade extremamente elevadas. A reoxigenação dos tecidos isquêmicos, fundamental para o reparo tecidual, produz eventos inflamatórios deletérios, com conseqüênci

Dissertação (mestrado) - Pontifícia Universidade Católica do Paraná, Curitiba, 2007 / Bibliografia: f. 42-45 / A Schinus terebinthifolius Raddi (STR) é utilizada pela população do litoral paranaense no tratamento de afecções bucais, porém são pouco conhecidos seus efeitos antiinflamatório e cicatrizante. Sendo assim, esta pesquisa teve como objetivo verificar a aç / Schinus terebinthifolius Raddi (STR) is used by the Paraná coast people in the healing of oral lesions, however its antiinflamatory and healing effects are not well established. Therefore the aim of this research was to verify the action of leaves extract

Dissertação (mestrado) - Pontifícia Universidade Católica do Paraná, Curitiba, 2010 / Bibliografia: f. 81-92 / A cicatrização de feridas é um evento complexo que envolve a interação de diversos componentes celulares e bioquímicos. Vários fatores podem afetar a cicatrização, entre eles a diabetes, doença sistêmica que compromete a cicatrização quando não controlada / Wound healing is a complex event that involves the interaction of several biochemical and cellular components. Many factors can affect the healing process, among them, diabetes, a systemic disease that when uncontrolled compromises healing by decreasing c