Made available in DSpace on 2014-10-09T12:45:56Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:04:42Z (GMT). No. of bitstreams: 1 07541.pdf: 9270192 bytes, checksum: 625d1a8ce146718eee35be24d9a360a3 (MD5) / Tese (Doutoramento) / IPEN/T / Instituto de Pesquisas Energeticas e Nucleares - IPEN/CNEN-SP

Made available in DSpace on 2014-10-09T12:30:17Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:06:23Z (GMT). No. of bitstreams: 1 01404.pdf: 2579767 bytes, checksum: 1ae768daf66388df1c47e6bc6a1e4a56 (MD5) / Tese (Doutoramento) / IPEN/T / Instituto de Pesquisas Energeticas e Nucleares - IPEN/CNEN-SP

Orientador: Francisco das Chagas Marques / Tese (doutorado) - Universidade Estadual de Campinas, Instituto de Fisica "Gleb Wataghin" / Made available in DSpace on 2018-08-14T18:36:55Z (GMT). No. of bitstreams: 1 Barbieri_PauloFernando_D.pdf: 3626831 bytes, checksum: 0f15b74219acbe9e82e54ae2ce3d1ed4 (MD5) Previous issue date: 2009 / Resumo: Esta tese mostra um estudo realizado sobre implantação de xenônio (Xe) em uma matriz amorfa de silício (a-Si) utilizando a técnica de Deposição Assistida com Feixe de Íons (IBAD). Para esta finalidade, um feixe de íons de Xe com energia de 1500 eV, obtido de um canhão tipo Kaufman, foi utilizado para a realização de sputtering de um alvo de silício, produzindo um filme de a-Si em um substrato colocado a 15 cm de distância via deposição. Ao mesmo tempo outro feixe de íons de Xe, obtido por um segundo canhão de energia variável (0 a 300 eV), implantava átomos na rede do a-Si que estava em formação. Foi possível implantar concentrações de xenônio de até 5% com energia da ordem de 50 eV. Esta energia de implantação é de várias ordens de grandeza menor do que a energia utilizada no processo convencional de implantação que utiliza valores de energia de ordem de milhares de eV. Para investigar o Xe dentro da matriz amorfa de Si foram utilizadas técnicas de excitações atômicas XAS (X-Ray Absorption Spectroscopy), XPS (X-Ray Photoelectron Spectroscopy) e XAES (X-Ray Auger Excited Spectroscopy) e também simulações teóricas para XAS. Os resultados experimentais de XAS indicam que os átomos de Xe são implantados majoritariamente de forma dispersa pela matriz, isolados dentro de defeitos estruturais. Medidas de XPS mostram que os níveis eletrônicos de caroço dos átomos de xenônio são alterados em função do sítio de aprisionamento, que por sua vez, estão relacionados com a energia de implantação. Um estudo utilizando uma combinação de XPS e XAES permitiu identificar e separar as contribuições relativas às alterações eletrônicas observadas nos átomos de Xe devido a inserção deles dentro do a-Si. A análise destes resultados, XPS/XAES, forneceu indícios sobre os tamanhos das cavidades hospedeiras dos átomos de Xe. Simulações teóricas de XAS foram bastante satisfatórias e corroboram com as observações realizadas por XPS/XAES e indicam timidamente formações de aglomerados para alguns casos, ou seja, minoritariamente. Dependendo da energia de implantação, a dinâmica de crescimento do filme é alterada possibilitando estruturas diferentes na matriz. Foi também constatado que o aumento da densidade do a-Si por efeito de compactação pode ser mascarado pela introdução de elementos com massas relativamente grandes, como por exemplo, Xe / Abstract: A study of xenon (Xe) implantation in amorphous silicon (a-Si) by Ion Beam Assisted Deposition (IBAD) technique is investigated in this thesis. A Xe ion beam with energy of 1500 eV, obtained from a Kaufman gun, was used for sputtering a Si target, depositing an a-Si film on the substrate holder placed 15 cm apart. Simultaneously, another Xe beam with variable energy (0 ¿ 300 eV), was used to bombard the a-Si for the implantation of Xe atoms. It was obtained Xenon concentration up to 5%, using energy as low as 50 eV, which is orders of magnitude smaller than those usually used by conventional implantation, that requires thousands of eV. For the investigation of the Xe atoms in the a-Si matrix, XAS (X-Ray Absorption Spectroscopy), XPS (X-Ray Photoelectron Spectroscopy) and XAES (X-Ray Auger Excited Spectroscopy) techniques and theoretical simulations of XAS were used. The experimental results of XAS showed that Xe atoms are dispersed in the a-Si matrix as isolated element majoritively into structural defects. XPS measurement shows that the electronic core levels of the Xe atoms are shifted as function of the trapping site, which in turn, are related to the energy implantation. The use of XPS and XAES allowed the identification and the separation of the contribution to the shift in the binding energy due to the relaxation energy. The analysis of this results, XPS/XAES, provided indications as to size of the cavity containing the trapped Xe. XAS theoretical simulations gave satisfactory results and corroborate with XPS/XAES observations and tentativelly indicated small clusters, for a minority of cases. Depending on the implantation energy, the growth dynamics of the films is changed, allowing different structures in the matrix. It was also verified that the increase in the density of the film by the packing effect is obscured by the introduction of heavier elements, for example, Xe / Doutorado / Física da Matéria Condensada / Doutor em Ciências

Neste trabalho propõe-se uma metodologia de estimação de parâmetros da máquina síncrona e do sistema de excitação baseada na técnica de sensibilidade de trajetória e sincronização de sistemas. Diversas metodologias de estimação de parâmetros foram propostas na literatura, cada uma com suas vantagens e desvantagens. Entretanto, poucas são adequadas para a estimação de parâmetros com o gerador em operação (on-line). A metodologia de sensibilidade de trajetória foi escolhida por permitir uma completa representação da máquina síncrona e do sistema de excitação incluindo as não linearidades como, por exemplo, os limites do sistema de excitação e a saturação do gerador. Foram propostas algumas alternativas para esta técnica visando uma futura aplicação on-line. Dentre as propostas destaca-se o uso da teoria de sincronização no processo de estimação de parâmetros. A metodologia desenvolvida é aplicada para identificar os parâmetros do gerador síncrono (modelo clássico, modelo de um eixo, e modelo de dois eixos). Também são relatados alguns dos problemas encontrados no momento de estimar vários parâmetros da máquina síncrona simultaneamente. A metodologia também é aplicada com sucesso para estimar os parâmetros do sistema de excitação (tipo ST1A e DC1). Por fim, analisa-se a influência dos parâmetros estimados na estabilidade transitória. Para tal objetivo são realizados testes de estabilidade em um pequeno sistema de potência sujeito a incertezas nos parâmetros / In this work a methodology to estimate parameters of synchronous machines and their excitation system based on trajectory sensitivity technique and system synchronization is proposed. Many methodologies for parameter estimation have been proposed in the literature, each one with advantages and desadvantages. However, only some of them are adequate to estimate parameters with generator in operation (on-line). The trajectory sensitivity methodology has been chosen as it allows a complete representation of generator and excitation system including non-linearities as, for instance, the limits of excitation system and saturation of generator. Some alternatives were proposed for this technique regarding a future on-line application. Among them, the use of synchronization theories in parameter estimation process is highlighted. The methodology developed is used to estimate the parameters of generators (classical model, one-axis model and two axis-model). Some problems to simultaneously estimate several parameters of a synchronous machine are also presented. The methodology is successfully used to estimate the parameters of the excitation system (type ST1A and DC1). Finally, the influence of the estimated parameters on transient stability is analyzed. For this aim, stability tests were performed in a small power system with uncertain parameters

A partir da hipótese de que carbonetos de ferro podem agir como fonte motora para nucleação de novos domínios magnéticos, o que tenderia a reduzir a taxa de crescimento da dissipação de energia anômala em função da frequência de excitação, três aços de grão não orientado com diferentes teores de carbono foram estudados. A amostra do aço totalmente processado continha 79 ppm de carbono e 2% silício, já o aço semiprocessado continha 340 ppm de carbono e a partir deste um terceiro conjunto foi produzido por descarbonetação contendo 110 ppm de carbono. As amostras foram envelhecidas consecutivamente em atmosfera inerte sob temperatura de 150 e 225 °C e tiveram suas propriedades magnéticas e microestruturais avaliadas em diferentes intervalos de tempos. Métodos, estes, que foram empregados com intuito de se estudar o efeito da precipitação de carbonetos na dissipação de energia anômala. O envelhecimento mecânico do aço com 340 ppm de carbono foi evidenciado após 6 horas de envelhecimento em um único pico, já o aço com 79 ppm de carbono e 2% silício apresentou um pico de envelhecimento mecânico a 75 horas. Por sua vez o aço contento 110 ppm de carbono apresentou um pico de dureza tardio, após 30 horas de envelhecimento sob 225 ºC Ficou evidenciado que o incremento do campo coercivo está ligado ao aumento do diâmetro da partícula. Essa tendência é verdadeira para carbonetos com faixa de tamanho de 0,5-0,65 ?m para a liga com 79 ppm carbono e 2% silício e de 0,55-0,81 ?m relativo à liga contendo 340 ppm de carbono. De maneira oposta, não foi identificado relação clara entre o tamanho dos carbonetos e a majoração de HC nas amostras da liga contento 110 ppm de carbono. O envelhecimento magnético mostrou-se mais deletério às propriedades magnéticas dos aços semiprocessados e totalmente processados quando estas são mensuradas em baixas frequências (f<60Hz). De maneira geral, foi observado que o envelhecimento porcentual (IE%) decresce com o aumento da frequência de excitação para o mesmo tempo e temperatura de envelhecimento. A respeito do emprego das amostras envelhecidas em altas frequências de excitação, a liga do aço totalmente processado apresentou menor dissipação de energia somente em frequência de excitação superiores a 1,5 kHz. Por sua vez, a liga semiprocessada contendo 340 ppm de carbono envelhecida por 6 e 12 horas mostrou-se menos dissipativa quando empregada sob indução de 1T, em frequências superiores a 640 e 900 Hz, respectivamente. O aço contendo 110 ppm de carbono apresentou os melhores resulto das ligas estudadas, como frequência de cruzamento abaixo dos 3 kHz e 700 Hz sob 1 e 1,5T, respectivamente. Elementos teóricos e empíricos dão conta de que o refinamento dos domínios magnéticos tende a ocorrer mais facilmente sob altas indução do que em baixas induções. O que implica em melhores resultados sob indução de 1,5T. O aumento da densidade dos domínios magnéticos foi constatado pelas imagens realizadas com luz polarizadas nas amostras do aço totalmente processado (70 ppm C e 2%Si). Os domínios magnéticos da amostra contendo 110 ppm de carbono, observados pela mesma técnica, apresentaram morfologia mais refinada o que dificultou a sua quantificação. Devido à precipitação dos carbonetos épsilon e cementita em planos de hábito na matriz ferrítica, é possível conjecturar que apenas 1/3 destes terão alta capacidade de ancoramento das paredes de domínios, uma vez que, apenas esta fração de precipitados terão seu menor eixo paralelo à direção de magnetização. / Three non-oriented electrical steels with different carbon content has been studied based on the hypothesis that iron carbides can act as a source of nucleation of new magnetic domains, which would then lead to a reduction in the growth rate of the anomalous energy dissipation as a function of the excitation frequency. Samples of the fully processed steel contained 79 ppm of carbon and 2% silicon, while the semi-processed steel contained 340 ppm of carbon, and from this alloy a third alloy containing 110 ppm of carbon was produced by decarburization. The samples were consecutively aged under inert atmosphere and at temperatures of 150 and 225°C, as well as had their magnetic and microstructural properties evaluated at different time intervals. The mechanical aging of the steel containing 340 ppm of carbon was evidenced after 6 hours of aging in a single peak, the steel containing 79 ppm of carbon and 2% silicon presented even a mechanical aging peak at 75 hours. In turn, samples of the NOES containing 110 ppm of carbon showed a late hardness peak after 30 hours of aging at 225°C. It was found that the increase in the coercive field is linked to the increase in the particle diameter. This trend is true for carbides with a size range of 0.5-0.65 ?m for the alloy containing 79 ppm carbon and 2% silicon, and 0.55-0.81 ?m for the alloy containing 340 ppm carbon. In contrast, no clear relationship was found between the carbide size and the coercive field increase in the samples of the NOES containing 110 ppm of carbon. Magnetic aging has been shown to be less deleterious to the magnetic properties of semi-processed and fully processed steels when they are measured at high frequencies (f >60Hz). Regarding the use of samples aged at high excitation frequencies, the alloy of the fully processed steel showed a lower energy dissipation only at excitation frequencies above 1.5 kHz. On the other hand, the steel containing with 340 ppm of carbon aged for 6 and 12 hours were less dissipative when employed under 1T induction at frequencies above 640 and 900 Hz, respectively. The NOES containing 110 ppm of carbon presented the best results of all the alloys studied, being able to be applied below 3 kHz and 700 Hz under 1 and 1.5T, respectively. Theoretical and empirical elements indicate that the magnetic domains refinement tends to occur more easily under high induction than under low inductions. This implies better results under and induction of 1.5T. The increase in the density of the magnetic domains was verified by light polarized images of the samples of the fully processed steel (70 ppm carbon and 2% silicon). The magnetic domains of the NOES110 sample observed using the same technique presented more a refined morphology, which made it difficult to quantify them. Due to the precipitation of the carbides epsilon and cementite in habit planes in the ferritic matrix, it is possible to conjecture that only a third of these will have a high anchoring capacity of the domain walls, since only this fraction of precipitate will have its smaller axis parallel to direction of magnetization.

Para melhor entender o envolvimento do NER em lesões oxidativas averiguou-se os efeitos da foto-excitação do azul de metileno (MB) in vitro e in vivo. Verificou-se que MB e luz induzem muitos sítios sensíveis a enzima FPG em DNA plasmidial. Mostrou-se que MB é incorporado por fibroblastos humanos proficientes ou deficientes em NER (XP-A e XP-C) e gerou oxigênio singlete (1O2) intracelularmente. A foto-excitação do MB formou também 8-oxoG em núcleos de fibroblastos. Células mutantes XP-A e XP-C foram mais sensíveis ao tratamento e apresentaram mais danos oxidativos em seu DNA genômico do que células selvagens. Contudo, todas as células mostraram a mesma cinética de reparo das lesões formadas. Além disso, houve mais marcação de g-H2AX nas células mutantes após a foto-excitação do MB. Assim, os resultados sugerem que a excitação do MB gera danos oxidativos e quebras na molécula de DNA, tanto in vitro quanto in vivo e que as proteínas XPA e XPC podem ter algum papel na proteção desse estresse, além da sua sabida participação em reparo de lesões induzidas por luz UV. / In order to study the participation of NER mechanisms in the removal of oxidative DNA lesions, we examined the effects of photoactivated methylene blue (MB) in vitro and in vivo. Plasmid DNA presents more FPG sensitive sites when MB was photoactivated than non-photoactivated. MB can be incorporated by NER-proficient or deficient cells and is able to generate singlet oxygen (1O2) inside cells. We detected also the presence of 8-oxoG in genomic DNA after treatment. XP-A and XP-C deficient cells are more sensitive to MB treatment and were found to have more oxidative DNA lesions than proficient cells. Also, there are more g-H2AX foci in mutant cells after treatment. However, there is a clear similarity in lesions repair kinetic between proficient and deficient cells. Therefore, these results suggest that photoactivated MB generates oxidative damage and DNA strand breaks both vitro and in vivo assays and that XPA and XPC proteins may also have a role in the protection of cellular oxidative stress, in addition to its participation in repair of UV-induced DNA damage.

Orientadores: Katia Lucchesi Cavalca, Rainer Nordmann / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-08-12T14:22:54Z (GMT). No. of bitstreams: 1 Furtado_RogerioMendonca_D.pdf: 2160863 bytes, checksum: 4c54a9ce5fcded113554dc24287e591a (MD5) Previous issue date: 2008 / Resumo: Um atuador magnético como fonte de excitação em sistemas rotativos é desenvolvido para emprego na análise modal e em outros estudos, envolvendo a excitação sem contato. Embora os sistemas magnéticos para aplicação de forças em máquinas rotativas sejam empregados com alto desempenho (como por exemplo os mancais magnéticos), o desenvolvimento de um sistema simples, para aplicações laboratoriais, se apresenta como uma contribuição experimental útil, para ser empregado numa bancada de testes utilizada no desenvolvimento de projetos de máquinas rotativas. O conceito apresentado é simples, mas permite a excitação externa sem contatos ou mesmo o controle das amplitudes de vibração, quando associado a um sistema de controle. Contudo, a calibração e o estudo do desempenho dinâmico do sistema não são análises simples. Neste sentido, o trabalho apresenta uma experiência prática e discussões sobre o desenvolvimento do atuador magnético utilizado para testes em máquinas rotativas. A influência da corrente elétrica, entreferro, superfície do pólo do atuador e também da freqüência de excitação, são apresentadas. A força magnética é estimada, baseando-se na medida da densidade de fluxo magnético, medida por sensores hall. / Abstract: A magnetic actuator as excitation source in rotating systems is developed, in order to accomplish modal analysis and other studies involving contacless excitation. Although the use of magnetic systems to apply forces onto rotating machinery has been carried out with high performance level (for example, magnetic bearings), the development of a conveniently easy and simples device for laboratory application presents interesting contribution to experimental methods used in test rigs based on similarity design to rotating machinery. The initial concept of the magnetic actuator proposed here is simple, but enables either the external excitation without contact or the vibration control when associated with a controller system. However, the performance characteristics tunning to attend the dynamic demand of the system is not so trivial. Following this focus, the work brings practical experience and discussion about the development and performance analysis of a magnetic actuator used for rotating machinery tests. The influence of the electrical current in the actuator coils, the air-gap between actuator and rotative system, thetype of surface of the actuator poles (flat or curved) as well as excitation frequency was verified. Force estimation was based on the magnetic flux density, measured by hall sensors. / Doutorado / Mecanica dos Sólidos e Projeto Mecanico / Doutor em Engenharia Mecânica

The picosecond optical response of germanium is investigated by performing excitation-probe experiments on a thin, intrinsic-germanium wafer maintained at 135 K. The results of three distinct experiments are reported: (1) the transmission of a single pulse is measured as a function of irradiance, (2) the probe transmission is measured at a fixed time after excitation as a function of the excitation energy, and (3) the transmission of a probe pulse is monitored as a function of time after excitation. These experiments employ 10-picosecond laser pulses at 1.06 um and Stokes-shifted pulses at 1.55-um.

Cette étude clinique qui est une approche psychopathologique du symptôme acouphènique est parmi les premières recherches qui s'intéressent à ce symptôme peu étudié par la psychanalyse. / This clinical study which is a psychological approach of the tinnitus symptom is among the first studies to be interested in thus symptom poorly studied with psychanalysis.

The ever-expanding need for energy, including those related to fossil fuels, is behind the drive to explore more complicated regions, such as salt and subsalt provinces. This exploration quest relies heavily on recorded surface seismic data to provide precise and detailed subsurface properties. However, conventional seismic processing algorithms including the state-of-the-art full-waveform inversion (FWI) fail to recover those features in many areas of salt provinces. Even the industrial solution with substantial involvement of manual human-interpretation has faced challenges in many regions. In this thesis, I attempt to replace those manual, and somewhat erroneous, steps to the velocity building in salt provinces with a mathematically robust algorithm under the FWI machinery. I, specifically, regularize FWI by penalizing the velocity drops with depth with a new more flexible function. Although promising, FWI is computationally very expensive, especially for large 3D seismic data. It updates an initial guess of the model iteratively using the gradient of the misfit function, which requires lengthy computations and large memory space/disc storage. Based on the adjoint state method, gradient computation usually requires us to store the source wavefield, or include an additional extrapolation step to propagate the source wavefield from its temporary storage at the boundary. To mitigate this computational overburden, I propose an amplitude excitation gradient calculation based on representing the source wavefield history by a single, specifically the most energetic arrival. In this thesis, I also propose a novel-multiscale scheme based on ux-corrected transport (FCT) to reduce artifacts in the gradient direction due to the noise present in seismic data. FCT comprises of two finite difference schemes: a transport and a diffusion to compute the flux at a grid point. I observe a couple of benefits in FCT-based FWI. First, it yields a smooth gradient at the earlier iterations of FWI by promoting the lower frequency content of the seismic data. Second, it is easily compatible with the existing FWI code, and with any objective function. The multiscale strategy starts with a large smoothing parameter and relaxes it progressively to zero to achieve the final inverted model from traditional FWI.