Made available in DSpace on 2015-03-26T14:01:06Z (GMT). No. of bitstreams: 1 Texto completo.pdf: 231615 bytes, checksum: 13f121d907a5378b5839c0f13db46ac3 (MD5) Previous issue date: 2010-07-09 / The increasing demand of the pulp market has stimulated research to find materials that are appropriate and diversified to manufacture. The aim is not only highly productive forests, but also genetically superior materials in yield and quality of pulp. Improving the quality of the wood affects the amount of commercial product to be obtained per unit area and also allows product differentiation in order to improve competitiveness in the global market. The new genetic material of species and hybrids, multiplied by the cloning process, existing in experimental plantings and commercial plantations should be analyzed with respect to parameters of wood quality in the development stages of research. Pulp for the characterization studies of wood quality must involve the chemical composition of wood, the anatomical structural characteristics and the industrial processing of wood pulp. This study aimed to characterize the wood of trees of a clone of Eucalyptus grandis and two hybrid clones of Eucalyptus grandis x urophylla to five years old. We analyzed the characteristics of the fibers, density, chemical composition of wood, carbohydrate analysis and kraft cooks. In general, wood of lower density was more favorable to the production of cellulose, since it required less alkali charge for cooking and had a higher yield pulp with higher viscosity. However he had several disadvantages such as higher specific wood consumption and lower weight of wood in the digester, adversely affecting the cost and industrial productivity. / A crescente demanda do mercado de celulose vem estimulando pesquisas na busca de matérias-primas mais apropriadas e diversificadas à sua fabricação. Busca-se não só florestas altamente produtivas, mas também materiais geneticamente superiores em rendimento e em qualidade de celulose. A melhoria da qualidade da madeira afeta a quantidade do produto comercial a ser obtido por unidade de área e, também, permite a diferenciação de produtos, de forma a melhorar a competitividade das empresas no mercado mundial. Os novos materiais genéticos de espécies e híbridos, multiplicados pelo processo de clonagem, existentes em plantios experimentais e em plantações comerciais necessitam, no desenvolvimento das etapas das pesquisas, serem analisados com relação aos parâmetros de qualidade da madeira. Para polpa celulósica os estudos de caracterização de qualidade da madeira devem envolver a constituição química da madeira, suas características estruturais anatômicas e as características tecnológicas da transformação da madeira em polpa. O presente trabalho teve como objetivo caracterizar a madeira de árvores de um clone de Eucalyptus grandis e dois clones do híbrido Eucalyptus grandis x Eucalyptus urophylla aos cinco anos de idade. Foram realizadas análises das características das fibras, densidade, constituição química da madeira, análise dos carboidratos e realização de cozimentos kraft. De maneira geral, a madeira de densidade mais baixa mostrou-se mais favorável à produção de celulose, uma vez que necessitou de menor carga de álcali para o cozimento, apresentou maior rendimento, polpa com maior viscosidade. Entretanto teve várias desvantagens como maior consumo específico de madeira e menor peso de madeira no digestor, afetando desfavoravelmente o custo e a produtividade industrial.

Made available in DSpace on 2015-03-26T14:01:12Z (GMT). No. of bitstreams: 1 texto completo.pdf: 1791563 bytes, checksum: f9a04c8f80a4b485931431376bcbeb4a (MD5) Previous issue date: 2011-07-22 / Sistemas de tratamento de efluentes de fábricas de celulose recebem efluentes que variam com os processos de produção, mas poucos estudos tem sido realizados para avaliar o desempenho do biorreator durante diferentes campanhas de produção. Neste trabalho, analisou-se o comportamento do sistema de lodos ativados de uma fábrica de celulose kraft durante trocas de produção entre polpa kraft não-branqueada (UKP) e branqueada (BKP) de pinho radiata. Observou-se que predominaram flocos médios a grandes no biorreator com relação alimento/microrganismo (F/M) entre 0,2 e 0,4 para efluente de UKP e entre 0,6 e 0,8 para efluente BKP. Dentre os microrganismos eucariontes, predominaram tecamebas durante o tratamento do efluente UKP devido à menor DQO nesse efluente, mas a falta de fósforo no sistema levou ao aumento de ciliados livre natantes. Após uma parada prolongada, foi necessário sete dias para o biorreator atingir 91% de remoção de DQO durante o tratamento de efluente UKP, e após troca de produção para polpa BKP essa remoção caiu para apenas 71%, indicando a maior facilidade de tratar o efluente UKP. Os menores valores de sólidos suspensos totais nos efluentes UKP e BKP foram encontrados quando o índice volumétrico de lodo variou de 60 a 90 g/ml. / Los sistemas de tratamiento de efluentes de celulosa reciben efluentes que solo tienen las variaciones propias de los procesos de celulosa, sin embargo pocas veces se puede evaluar el desempeño de un bioreactor ante cambios del tipo de producto de la planta de celulosa. En este trabajo se analiza el comportamiento de la planta de efluentes cuando la planta de celulosa cambia su producción entre pulpa no blanqueada (UKP) y blanqueada (BKP) de Pino Radiata en un proceso kraft, encontrándose que el bioreactor predominan los floculos medianos y grandes con relación F/M entre 0,2 a 0,4 para efluente de pulpa UKP y 0,6 a 0,8 para efluente de pulpa BKP, pero efluente de pulpa UKP el tipo de microorganismos predominantes son tecamebas debido al menor DQO. Sin embargo ante un déficit de fosforo en el sistema, en la población de microorganismos aumentan los ciliados libres. Después de una detención prolongada, se ha determinado que el bioreactor requiere siete días para alcanzar niveles de remoción de DQO cercanos al 91% al producir pulpa UKP y al cambiar a producción de pulpa BKP, esta decae valores entorno del 71%, lo cual indica que es más fácil tratar efluente de pulpa UKP. Además los menores valores de sólidos totales en el efluente de pulpa UKP y BKP se alcanzan cuando el índice volumétrico de lodo (IVL), está entre 60 y 90 g/ml.

Made available in DSpace on 2015-03-26T14:01:16Z (GMT). No. of bitstreams: 1 texto completo.pdf: 759588 bytes, checksum: e2b7b4ee20b80410e8d3b44a217a4b82 (MD5) Previous issue date: 2013-12-13 / The demand for the dissolving pulp production has increased in the last decade and many pulp mills are adjusting their operations to produce it. One important parameter which differentiates the dissolving pulp from paper pulp is its high content of alpha cellulose and low levels of hemicelluloses, lignin and ash. Moreover, dissolving pulp is also characterized by low polydispersity, high brightness and reactivity to chemical reagents specific. The amount and different types of hemicelluloses is the most significant chemical trait of such pulps and has an impact on processability and final product quality. Currently, techniques for the production of soluble pulp are: (1) prehydrolysis kraft, which consists of chips prehydrolysis with water or steam before of the kraft cooking, and (2) acid sulphite cooking. In both cases, hemicelluloses are solubilized and depolymerized, and it is possible to achieve high content of alpha cellulose, being the crystallinity also affected. Brazil has a huge potential for pulp paper production, being the fourth largest producer in the world; however, the production of dissolving pulp is limited. The demand for dissolving pulp is growing and the knowledge regarding its production from eucalypt is scarce. This work aimed at optimzinge the oxygen delignification and bleaching steps for a prehydrolysis kraft dissolving pulp from Eucalyptus spp. using elemental chlorine free (ECF) and conventional sequences, to attain desirable market qualities. The main findings of this work were: (1) dissolving pulp bleaching (viscose grade) was feasible by using conventional and ECF sequences, reaching the quality required for this type of pulp, except for mineral content, (2) it is recommended the intensive oxygen delignification in order to have flexibility in controlling the kappa number and especially the pulp viscosity; (3) the dissolving pulp bleaching sequence is perfectly feasible using a ECF sequence with three stages, D(EP)D, which achieved 92% ISO of brightness; (4) using the ECF sequence with the four stage D(EP)DP, may be interesting due to the final peroxidation which deliver a lower viscosity (final pH 10), and low OX level of the bleached pulp; (5) the application of the conventional sequence D(EH)DP produced very satisfactory bleaching results, and good pulp quality (excellent viscosity control by controlling the final pH of the (EH) stage; (6) the use of a chelation stage at the end of the bleaching, in sequences such as D(EP)DPQ and D(EH)DPQ reduced the ash, iron and calcium pulp content, but this step is only recommended if the concentration of these minerals are out of the specification for the dissolving pulp; (7) it is not recommend the use of elemental chlorine in the first stage of bleaching sequences such as (DC)(EP)DP or (DC)(EH)DP; and (8) in the sequences D(EH)DP e D(EH)DPQ it is not recommend operating the D0 stage at pH < 1.7 due to the pulp quality fall under the limit. / A demanda na produção de polpa para dissolução ou polpa solúvel tem aumentado na última década e muitas fábricas de Celulose e Papel estão convertendo suas operações para produzir polpa para dissolução. Um dos fatores que diferencia a polpa para dissolução da polpa para fabricação de papéis é o seu alto teor de alfa celulose e baixos teores de hemiceluloses, lignina e cinzas. Além disso, polpa para dissolução apresenta baixa polidispersividade, elevada alvura e alta reatividade a reagentes químicos específicos. A quantidade e os diferentes tipos de hemiceluloses é a variação química mais significante e tem um impacto na processabilidade e qualidade do produto final. Atualmente as técnicas para produção de polpa solúvel são: (1) pré-hidrólise kraft, que consiste em pré-hidrólise dos cavacos com água ou vapor antes do cozimento kraft, e (2) cozimento sulfito ácido. Em ambos os casos, hemiceluloses são despolimerizadas e solubilizadas, e é possível alcançar alto teor de alfa-celulose, sendo a cristalinidade também afetada. O Brasil possui um papel de destaque no cenário mundial de produção de polpa celulósica, destacando-se como o quarto maior produtor deste produto, no entanto, a produção de polpa para dissolução é ainda reduzida. Tendo em vista a demanda de mercado para polpa solúvel e pouco conhecimento relativo à sua produção a partir da madeira de eucalipto é que foi realizado este trabalho. O objetivo foi aperfeiçoar a deslignificação com oxigênio e o branqueamento de uma polpa pré-hidrólise kraft de Eucalyptus spp. por meio de sequências isentas de cloro elementar (ECF) e convencionais, visando obter polpa solúvel com os padrões de qualidade desejados pelo mercado. Os principais resultados desse trabalho foram: (1) o branqueamento de polpa solúvel (grau viscose) foi viável com sequências ECF ou convencionais, atingindo-se os padrões de qualidade exigidos para esse tipo de polpa, exceto pelo conteúdo mineral; (2) recomenda-se a deslignificação intensiva com oxigênio a fim de se ter flexibilidade no controle do número kappa e, especialmente da viscosidade da polpa; (3) o branqueamento da polpa solúvel é perfeitamente viável pela sequência ECF de três estágios D(EP)D, com a qual se consegue alvuras de 92% ISO; (4) a aplicação da sequência ECF de quatro estágios D(EP)DP pode ser interessante já que a etapa final de peróxido permite abaixamento da viscosidade (pH final 10 e 11) e do nível de OX da polpa branqueada; (5) a aplicação da sequência convencional D(EH)DP produz resultados muito satisfatórios de branqueamento e de qualidade da polpa (ótimo controle de viscosidade pelo controle do pH final da etapa EH); (6) o uso de uma etapa quelante ao final do branqueamento, em sequências tais como D(EP)DPQ e D(EH)DPQ reduz significativamente os teores de cinzas, ferro e cálcio da polpa solúvel, porém essa etapa só é recomendada se o teor desses minerais estiverem acima dos limites desejáveis quando da operação industrial, já que ele não agrega qualquer outro valor; (7) não se recomenda o uso do cloro elementar no primeiro estágio de branqueamento em sequências tais como (DC)(EP)DP ou (DC)(EH)DP; e (8) nas sequências D(EH)DP e D(EH)DPQ não se recomenda operar o estágio D0 em pH < 1,7 por resultar polpa com viscosidade abaixo do limite mínimo.

Made available in DSpace on 2015-03-26T14:01:17Z (GMT). No. of bitstreams: 1 texto completo.pdf: 1134701 bytes, checksum: 187983c0bf93f016a9580bab2e8e7d7c (MD5) Previous issue date: 2013-07-29 / The bleaching washing process in Suzano Papel e Celulose (Mucuri-BA) s -fiberline 2 utilizes condensate from evaporation 2, which contains high COD load. This laboratory study was designed to verify the influence of evaporation condensate COD load and chlorine dioxide consumption in pulp bleachability, in A/DEpDP. Four simulations were performed and industrial condensate from Suzano s Mucuri unit and two other Pulp Plants (A and B) were utilized. The influence of DDW filtrate, both diluted and concentrated, in contrast to condensate, was also evaluated. On the condensate characterization, COD content on Suzano s sample (2910.8 ppm) was eight times higher than the values of Plants A and B (263.3 and 339.2 ppm, respectively) and the methanol content was 74.0% of COD s value. Analysis showed that 98.16% of the pulp s COD variation could be explained by the condensate COD load used to wash the pulp. Simulations 1 and 2 evaluated the bleachability influence of the following condensates: Suzano, Plants A and B, and Suzano s optimized. Suzano s sample, with greater condensate and pulp COD values, presented greater bleachability difficulty, where this variation can be attributed to the COD load of the pulp entering the bleach plant. COD influence on pulp viscosity was not significant. Finally, in order to achieve a final brightness of 89.7% ISO, there was an active chlorine consumption reduction equivalent to 1.3; 0.9 and 1.8 kg/tsa for Plant A, B and Suzano optimized respectively, when compared to Suzano s sample consumption. Simulation 4 evaluated the influence of washing the pulp with condensed and filtrates (diluted and concentrated) that were collected from the DDWs. Washing the pulp with filtrate affected pulp bleachability negatively, increasing Ep kappa number and interfering with brightness development in all bleaching stages. Moreover, there was an increase in active chlorine consumption of 5.0 and 13.0 kg/ADT, for the samples washed with diluted and concentrated filtrates, respectively, when compared with the consumption for pulp washed with condensate, to achieve final pulp brightness equivalent to 89.0% ISO. Thereby, it is possible to infer that the use of washer filtrates is not economically attractive, given the increase in active chlorine consumption in the bleaching step. / O processo de branqueamento na linha de fibras 2 da Suzano Papel e Celulose (Mucuri-BA) utiliza condensado da evaporação 2 com elevado teor da DQO para a lavagem da polpa pré-branqueada. Neste estudo foi analisado, em laboratório, a influência da DQO do condensado no consumo de cloro ativo e parâmetros de branqueabilidade da polpa, na sequência A/DEpDP. Foram realizadas quatro simulações, nas quais foram utilizados condensados industriais da Suzano e duas outras fábricas do Setor (Fábricas A e B). Também foi avaliada a influência de filtrados diluído e concentrado, coletados no lavador DDW, em comparativo à utilização de condensado. Na caracterização dos condensados foi observado que o valor de DQO da amostra Suzano (2910,8 ppm) é oito vezes superior aos valores das Fábricas A e B (263,3 e 339,2 ppm, respectivamente) e que para esta amostra a composição de metanol equivale a 74,0% do valor integral da DQO. Foi observado que 98,16% da variação da DQO da polpa (entrada do branqueamento) é explicada pela DQO do condensado utilizado na sua lavagem. Nas Simulações 1 e 2 foi avaliada a influência dos condensados Suzano, Fábricas A e B e Suzano otimizado, onde observou-se que a amostra Suzano, com maiores valores da DQO do condensado e da polpa, demonstrou maior dificuldade de branqueabilidade. Não foi verificada influência da DQO do condensado nos valores de viscosidade da polpa. Ainda, foi verificada uma redução no consumo de cloro ativo equivalente a 1,3; 0,9 e 1,8 kg/tsa para as amostras da Fábrica A, B e Suzano otimizada, respectivamente, quando comparado ao consumo da amostra Suzano, para atingir uma alvura final de 89,7 %ISO. Por fim, na Simulação 4, onde foi avaliada a influência da lavagem com condensado e filtrados diluído e concentrado, coletados nos lavadores DDW, foi observada que a lavagem da polpa com os filtrados afetou negativamente a branqueabilidade da polpa, aumentando o valor de número kappa no estágio Ep e interferindo nos valores de alvura em todos os estágios de branqueamento. Também, foi verificado um aumento no consumo de cloro ativo, para atingir uma alvura final da polpa equivalente a 89,0 %ISO, inferindo que esta lavagem com filtrados não se viabiliza economicamente.

Made available in DSpace on 2015-03-26T14:01:18Z (GMT). No. of bitstreams: 1 texto completo.pdf: 593051 bytes, checksum: d9d08cce8a3ba750b30b61926a005e98 (MD5) Previous issue date: 2014-07-31 / The objective of this work was to study the correlation between the percentage of survival and overall height of a basic forest inventory information eucalyptus plantation at six months of age between the years 2011-2013 with the results of other inventories in the same settlement. It was also evaluated possible effects of replanting and the first cultural tract and its relation to forest productivity. With the results it was possible to identify some correlations between forest inventories analyzed and mainly identify differences in growth characteristics of cultivars. Based on the results obtained it was concluded that the results of Qualitative Forest Inventory stratified by genetic materials demonstrated differences in the percentages of survival and height, where the genetic material MG 01 showed slight superiority over the other. In the analysis of correlations between the qualitative forest inventory of 6 months for the survival and overall height parameters in relation to the lifting of survival to 23° days and on the 50° day after planting it was found moderate correlations only for the survival parameter at 6 months about the outcome of survival on the 50° day after planting. In the correlation analysis between the qualitative forest inventory of 6 months with the number of days in which it was held the first cultural tract after planting and replanting were also not shown significant correlations. For the analysis of correlation between the qualitative forest inventory of 6 months with the qualitative forest inventory 12 months was possible to identify correlations between survival parameters and correlations between the total height parameters. This same correlation was found when compared with the qualitative forest inventory of 2 years. / O objetivo deste trabalho foi estudar a correlação existente entre os percentuais de sobrevivência e altura total de uma base de informações de inventário florestal de plantio de eucalipto aos seis meses de idade entre os anos de 2011 a 2013 com o resultado de outros inventários realizados no mesmo povoamento. Foi avaliado também possíveis efeitos do replantio e do primeiro trato cultural e sua relação com a produtividade florestal. Com os resultados encontrados foi possível identificar algumas correlações existentes entre os inventários florestais analisados e principalmente, identificar diferenças de características de crescimento entre materiais genéticos. Com base nos resultados obtidos foi possível concluir que os resultados do Inventário Florestal Qualitativo estratificado por materiais genéticos demonstraram diferenças nos percentuais de sobrevivência e altura, onde o material genético MG 01 demonstrou leve superioridade em relação aos demais. Na análise das correlações entre o inventário florestal qualitativo de 6 meses para os parâmetros sobrevivência e altura total em relação ao levantamento de sobrevivência ao 23° dias e no 50° dias após o plantio constatou-se correlações moderadas apenas para o parâmetro sobrevivência aos 6 meses em relação ao resultado de sobrevivência no 50° dia após o plantio. Na análise de correlação entre o inventário florestal qualitativo de 6 meses com relação ao número de dias em que foi realizado o primeiro trato cultural após o plantio, bem como o replantio também não foram evidenciados correlações expressivas. Para a análise de correlação entre o inventário florestal qualitativo de 6 meses com o inventário florestal qualitativo de 12 meses foi possível identificar correlações entre os parâmetros de sobrevivência e correlações entre os parâmetros de altura total. Esta mesma correlação foi encontrada quando comparado com o inventário florestal qualitativo de 2 anos.

Made available in DSpace on 2016-12-08T15:56:17Z (GMT). No. of bitstreams: 1 resumo tese.pdf: 15008 bytes, checksum: b3fcb8e618165bdab7dabdeefc264a32 (MD5) Previous issue date: 2014-08-18 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The use of casting waste powder from industry in mortars brings environmental benefits by minimizing the impact caused by the disposal of waste on the environment. Casting exhaust powder is a waste product from the regeneration of sand molds from the core making process sector from a foundry industry located in Joinville/SC. This work aims to propose a formulation method for laying mortars, and wall and ceiling coating mortars incorporating casting waste powder whose use would result in a product with adequate technical performance. The fine aggregates, the casting waste powder and mortars were characterized by standard assays, electron microscopy and X-ray powder diffraction. The laying and coating mortar compositions were based on a system of equations obtained using the mixture design methodology. Through this study, results of experimental character and a method for formulating mortars that can be useful in the construction sector were obtained, thus contributing to a better understanding of the use of casting waste in mortars. / O uso de resíduos de fundição como o pó de exaustão em argamassas traz benefícios ambientais através da minimização do impacto causado pelo descarte do resíduo no meio ambiente. O pó de exaustão de fundição é um resíduo proveniente da regeneração dos moldes de areias do setor de macharia de uma indústria de fundição localizada em Joinville/SC. Este trabalho tem por objetivo propor um método de formulação para argamassas de assentamento e revestimento de paredes e tetos com incorporação de pó de exaustão cuja utilização resulte em um produto com desempenho técnico adequado. Os agregados miúdos, o resíduo pó de exaustão de fundição e as argamassas foram caracterizados por ensaios normalizados, microscopia eletrônica e difração de raios-X. As composições das argamassas em massa foram obtidas através de planejamento de experimentos de delineamento por misturas. A proposta de formulação de argamassas de assentamento e revestimento de paredes e tetos foi baseada na resolução de sistemas de equações obtidas através do modelamento estatístico das propriedades. Por meio deste estudo, foram obtidos resultados de caráter experimental e um método de formulação de argamassas que podem ser úteis ao setor de construção civil, contribuindo desta forma com o melhor entendimento do uso de resíduos de fundição em argamassas.

Made available in DSpace on 2016-12-08T17:19:14Z (GMT). No. of bitstreams: 1 Capa.pdf: 33668 bytes, checksum: d1e9564709d38250640540f84c86c175 (MD5) Previous issue date: 2005-07-29 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The recycling of poly(ethylene terephthalate) (PET) can be carried through by different techniques, one of them is the chemical recycling, where new aliphatic-aromatic copolymers are synthesized from melt reaction of the PET post-consumer with aliphatic homopolymers. The aliphatic polyesters, such as the poly(ethylene adipate) (PEA) are biodegradable. The synthesis of aliphatic-aromatic copolymers reveals a good alternative. Varying the composition of each polymer; it can be gotten materials with superior properties to either of the pure components and possibly biodegradable in soil can be obtained. In this work we characterized these aliphatic aromatic copolyesters in different compositions before and after soil biodegradation tests by infrared spectroscopy (FTIR), differential scanning calorimetric (DSC), thermal analysis (TGA), gel permeation chromatography (GPC) and proton nuclear magnetic ressonance spectroscopy 1H NMR. In addition a new methodology for GPC analyses to aliphatic-aromatic copolyesters at room temperature is being proposal. The results of FTIR characterization did not show any alteration in the samples composition before and after 7 months of soil biodegradation. The samples were analyzed by DSC and TGA to evaluate the alterations in the thermal behavior. DSC curves of samples without degradation showed, through the values of Tg, that samples with higher percentage of PEA are more flexible, while those with higher PET content are more rigid. The TGA results showed that the thermal stability of the copolymers increase with the PET content. No changes were observed to material after degradation tests. GPC analysis showed a significative change in Mn and Mw results for PET-co-PEA 50-50, indicating that the copolymer suffered greater degradation in this composition. The new methodology proposal for GPC analyses demonstrated excellent performance in the attainment of the molar mass results for aliphatic-aromatic copolymers The 1H-NMR results showed that the adipate and terephthalate composition from copolymers are different from the copolymers before degradation. / A reciclagem do poli(tereftalato de etileno) (PET) pode ser realizada por diferentes técnicas, uma delas é a reciclagem química, em que podem ser sintetizados novos copolímeros alifático-aromáticos através da reação em massa do PET pós-consumo com homopolímeros alifáticos. A síntese de copolímeros alifático-aromáticos mostra-se como uma boa alternativa, pois variando os teores de cada componente, pode-se obter materiais com propriedades mecânicas e térmicas superiores aos polímeros puros, passíveis de sofrerem biodegradação em solo. Neste trabalho foi realizada a caracterização do copolímero PET-co-PEA, nas diferentes composições obtidas antes e após testes de biodegradação em solo compostado, através das análises de espectroscopia no infravermelho (FTIR), calorimetria exploratória diferencial (DSC), análise termogravimétrica (TGA), cromatografia de permeação em gel (GPC) e ressonância magnética nuclear de prótons (1H NMR). Também é proposta uma metodologia alternativa para análises de GPC a temperatura ambiente para poliésteres alifático-aromáticos. Os resultados de caracterização por FTIR não mostraram alterações na composição das amostras antes e depois de 7 meses de biodegradação em solo. As amostras foram analisadas por DSC e TGA para avaliar as alterações no comportamento térmico. As curvas de DSC das amostras sem degradação mostraram, através dos valores de Tg, que as amostras com maior porcentagem de PEA são mais flexíveis, enquanto àquelas com maior conteúdo de PET são mais rígidas. As análises de TGA mostraram que a estabilidade térmica dos copolímeros aumenta com o teor de PET. Não se observa alterações antes e após teste de biodegradação nas amostras que apresentam somente um estágio de degradação.Os resultados das análises GPC mostraram uma diferença significativa nos valores de Mn e Mw para a composição de PET-co-PEA 50-50, indicando que foi nesta proporção que o copolímero sofreu maior degradação. A nova metodologia proposta para análises GPC demonstrou ótimo desempenho na obtenção dos resultados de massas molares para os copolímeros alifático-aromáticos. Os resultados de 1H-NMR obtidos mostraram que a composição em adipato e em tereftalato dos copolímeros é diferente daquela dos copolímeros antes da degradação.

Made available in DSpace on 2016-12-08T17:19:14Z (GMT). No. of bitstreams: 1 CAPA-INTRODUCAO.pdf: 471295 bytes, checksum: 99f6fa2d53c1ccb1e2f39b487739efd6 (MD5) Previous issue date: 2011-11-22 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Recent studies demonstrated that small quantities of nanoparticles, added to a material, are able to modify significantly its properties. In this work was studied the properties of a nanocomposite of epoxy and nanoparticles of alfa alumina or titanium oxide (2,5% wt/wt and 5 wt/wt).The aim here is to determine how much these metallic oxides are able to modify the nanocomposite s properties when compared with the neat resin. For the characterization were applied the following techniques: Fourier Transform Infrared (FTIR), X-ray diffraction, Nanoindentation, Microhardness, Scanning Electron Microscopy (SEM), Thermogravimetry (TGA), Differential Scanning Calorimetry (DSC) and Dielectric Strength. The results showed that the dielectric strength, the hardness and the Young´s modulus are significantly modified by the nanoparticles adding. / Recentes pesquisas têm demonstrado que a adição de pequenas quantidades de nanopartículas a uma matriz pode afetar significativamente suas propriedades. Neste trabalho foram estudadas as propriedades de nanocompósitos de matriz epóxi aditivadas com duas concentrações nanopartículas de alumina alfa ou óxido de titânio (2,5% m/m e 5,0%m/m). O objetivo da investigação é determinar o quanto estes óxidos metálicos podem influenciar nas propriedades do nanocompósito quando comparadas com a matriz pura. Para a caracterização foram utilizadas as seguintes técnicas: Infravermelho por Transformada de Fourier (FTIR), Difratometria de Raio-X, Nanoindentação, Microdureza, Microscopia eletrônica de varredura (MEV), Termogravimetria (TGA), Calorimetria Exploratória Diferencial (DSC) e Rigidez Dielétrica. Os resultados indicam que a rigidez dielétrica, a dureza e o módulo de elasticidade sofrem alterações significativas com a adição de nanopartículas.

Made available in DSpace on 2016-12-08T17:19:16Z (GMT). No. of bitstreams: 1 Carlos Mauricio Sacchelli .pdf: 64226 bytes, checksum: 73274c8d6f55e4c10fb6577ed6dcd062 (MD5) Previous issue date: 2000-02-25 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Este estudo é uma comparação entre os resultados obtidos pelo processo de injeção do copolímero poli (óxido de Metila) POM M90, produzido pelo Hoechst com os de simulação de injeção através do aplicativo Moldflow. Os experimentos foram realizados em dois moldes, um com três cavidades e outro com duas cavidades. A pressão de injeção, para ambos foi ajustada em um valor máximo e as válvulas de vazão totalmente abertas, assim, foi determinado o tempo mínimo de injeção (tm) para completar as cavidades. As pressões de injeção foram reduzidas e o processo de injeção foi interrompido no tempo tm. Como resultado, as cavidades não foram completamente preenchidas, sendo as massas dos corpos de prova injetados determinadas. Na simulação, as cavidades foram modeladas, e simuladas segundo normas do aplicativo, sendo os parâmetros de simulação utilizados iguais ao da injeção. As vazões de injeção na simulação foram determinadas em função da massa do injetado, de sua especifica e do tempo tm. A massa especifica foi obtida experimentalmente através do plastômetro de extrusão (aparelho utilizado para a determinação do índice de fluidez). Após as simulações, foram analisados os seguintes parâmetros de comparação: preenchimento das cavidades no tempo de referencia tm, massas do injetado e do simulado, as vazões simuladas e injetadas e a massa especifica do material. Como parâmetro simples de comparação entre estas técnicas foi utilizado a massa especifica do POM M90. Os resultados encontrados no método de obtenção da massa especifica foram coerentes indicando que o plastômetro de extrusão pode ser utilizado para este fim, os dados obtidos pela simulação de injeção indicaram que a mesma pode descrever com boa aproximação o processo de injeção do POM M90.

Made available in DSpace on 2016-12-08T17:19:17Z (GMT). No. of bitstreams: 1 1 - Introducao.pdf: 683948 bytes, checksum: 323bfbfe06d963d7bfbecaaf890583ab (MD5) Previous issue date: 2012-05-14 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The aim of this work was the development of polyester matrix and taquara-lixa (Merostachys sp.) sticks or fibers composites and mechanical characterization by means of flexural tests for the composites and tension tests for taquara. First, it was determined the average mass distribution from a group of taquara sticks with 150 mm length, taquara medium moisture content and tension tests. Billets measuring 150 x 50 x 50 mm were prepared and were characterized by flexural tests. After the observation of the delamination effect in the composites, due to the poor interaction between matrix and fiber, a study of a chemical treatment of the sticks with sodium hydroxide was performed, for the partial removal of lignin and hemicellulose and to allow the stick s fibers to reorganize and reduce its hydrophilicity. Taquara specimens were made and suffered chemical treatment, varying the type of washing for each group, and flexural tests were performed to verify its mechanical properties. In another experiment, the average mass of a stick with 280 mm length was determined and the composites were made in a mold with 280 x 60 x 50 mm dimensions. To check the effect of the chosen treatment and the compression force during the confection of the composites, it was produced composites with dried taquara sticks and without compression, chemically treated sticks and without compression, dried sticks and with compression, chemically treated sticks and with compression and chemically treated taquara pieces that have its fibers separated by a rolling machine, and with compression. Specimens were extracted from the composites and flexural tests were performed to determine the maximum flexural stress, 1st rupture flexural stress, maximum displacement, 1st rupture displacement and flexural modulus. It was observed that both chemical treatment and the compression force had influence on composites mechanical properties, raising its flexural stress and elasticity modulus and reducing its displacement during flexural tests. / Este trabalho teve por objetivo o desenvolvimento de compósitos de matriz de resina poliéster e gravetos ou fibras de taquara-lixa (Merostachys sp.) e a caracterização mecânica por ensaios de flexão dos compósitos e por ensaios de tração da taquara. Inicialmente, foi realizada a determinação da massa média de um lote de gravetos de taquara de 150 mm de comprimento, o seu teor de umidade médio e a realização de ensaios de tração da taquara. Os compósitos confeccionados foram feitos em um molde de 150 x 50 x 50 mm e caracterizados por ensaios de flexão. Após a observação do efeito de delaminação nos compósitos, devido a fraca interação entre a matriz e a taquara, foi realizado um estudo de tratamento químico dos gravetos com hidróxido de sódio, para realizar a remoção parcial da lignina e hemicelulose e permitir que as fibras do graveto se reorganizassem e reduzissem a sua hidrofilicidade. Corpos de prova de taquara foram confeccionados e sofreram tratamento químico, variando o tipo de enxágüe em cada lote, e os mesmos foram ensaiados na máquina de flexão para verificar as suas propriedades mecânicas. Em outro experimento, foi determinada a massa média de um lote de gravetos de taquara de 280 mm de comprimento e os compósitos foram produzidos em um molde de dimensões de 280 x 60 x 50 mm. Para verificar o efeito do tratamento escolhido e da força de compressão durante a confecção dos compósitos, foram produzidos compósitos com gravetos in natura e sem compressão, gravetos tratados e sem compressão, gravetos in natura e sem compressão, gravetos tratados e com compressão, e pedaços de taquara tratados quimicamente e que tiveram as fibras separadas com o auxílio de uma calandra e com compressão. Os corpos de prova foram extraídos dos compósitos e foram realizados ensaios de flexão para a determinação da tensão máxima de flexão, tensão de flexão na 1ª delaminação, o deslocamento máximo e o deslocamento sofrido no momento da 1ª delaminação e o módulo de elasticidade em flexão. Foi observado que tanto o tratamento químico quanto a força de compressão exerceram influência nas propriedades mecânicas dos compósitos, aumentando sua tensão de flexão e seu módulo de elasticidade e reduzindo o deslocamento durante o ensaio de flexão.