Aim: An in vitro experimental study was carried out in order to evaluate the roughness of enamel and dentin of bovine teeth eroded by isotonic drinks. Materials and Methods: Sixty (60) extracted bovine teeth were used. They were stored in distilled water at room temperature. Thirty (30) 10mmx6mm enamel specimens and thirty (30) 10mmx6mm dentin specimens were cut, which were selected due to their parallelism, uniformity and thickness of 2mm and more. They were divided into 6 groups. Group 1: bovine enamel exposed to the isotonic drink Gatorade® Perform2, Group 2: bovine dentin exposed to the isotonic drink Gatorade® Perform2, Group 3: bovine enamel exposed to the isotonic drink Electrolight®, Group 4: bovine dentin exposed to the isotonic drink Electrolight®, Group 5: bovine enamel exposed to the isotonic drink Powerade® ION4 and Group 6: bovine dentin exposed to the isotonic drink Powerade® ION4. Two coats of nail polish were applied on the middle of the specimens’ surface before subjecting them to the erosive challenge, being it considered as control of the own specimen. The erosive challenge was performed for five-minute periods, three times a day for five days. When the challenge was concluded, the surface wear was analyzed with the Mitutoyo SJ-201® Surface Roughness Tester which shows roughness profiles. Each piece was measured three times over the same surface but in different areas of the enamel and dentin interface subjected to the experiment. The average was obtained from these three results. Results: A significant difference was found between the initial and final roughness of enamel and dentin after the erosive challenge. Statistically significant differences were not found in the measurement of roughness caused by the 3 drinks in each substrate. For enamel specimens, it was found an initial and final average in Group 1 (Gatorade Perform 02) of (0.22±0.78/0.54±0.56), in Group 2 (Electrolight®) of (0.05±0.18/, 0.18±0.05), in Group 3 (Powerade ION4) of (0.04±0.13/0.19±0.12) and in dentin (0.29±0.78/0.47±0.12), (0.32±0.13/0.44±0.13) and (0.31±0.08/0.42±0.1). Conclusion: Isotonic drinks cause an increase in roughness of enamel and dentin after the erosive challenge. / Objetivo: Se realizó un estudio experimental in vitro para evaluar la rugosidad del esmalte y dentina de dientes bovinos erosionados por bebidas isotónicas. Materiales y métodos: Se utilizaron 60 incisivos bovinos extraídos y almacenados en recipientes conteniendo solución de agua destilada a temperatura ambiente. Se cortaron 30 muestras de esmalte y 30 de dentina de 10mmx6mm que fueron seleccionados por su paralelismo, uniformidad, y grosor de 2mm a más. Se dividieron en 6 grupos. Grupo 1: esmalte de bovino expuesto a la bebida isotónica Gatorade® Perform2, Grupo 2: dentina de bovino expuesto a la bebida isotónica Gatorade® Perform2, Grupo 3: esmalte de bovino expuesto a la bebida isotónica Electrolight®, Grupo 4: dentina de bovino expuesto a la bebida isotónica Electrolight®, Grupo 5: esmalte de bovino y expuesto a la bebida isotónica Powerade® ION4, Grupo 6: dentina de bovino expuesto a la bebida isotónica Powerade® ION4. Las muestras recibieron dos capas de esmalte de uñas, en la mitad de la superficie antes del desafío erosivo, la cual fue considerada como control del propio espécimen. El desafío erosivo, fue realizado durante 3 veces al día, por 5 minutos, por 5 días, una vez terminado el desafío se analizó el desgaste de la superficie con el uso de un rugosímetro Mitutoyo SJ-201® que proporciona perfiles de rugosidad. Por cada fragmento se realizó tres mediciones que recorrían la misma superficie respectivamente en diferentes áreas de la interfaz de los cuerpos en esmalte y la dentina sometidos al experimento, la media se obtuvo de estos tres datos. Resultados: Hubo diferencia significativa entre la rugosidad inicial y la final después del desafio erosivo tanto en esmalte como en dentina. No se encontraron diferencias estadísticamente significativas en la medida de rugosidad causada por las 3 bebidas en cada sustrato. Para los especímenes de esmalte se encontró una media inicial y final en el grupo 1 (Gatorade Perform 02) de (0.22±0.78/0.54±0.56), en el grupo 2 (Electrolight®) (0.05±0.18/, 0.18± 0.05) y en el grupo 3 (Powerade ION4) de (0.04±0.13/0.19±0.12) y en dentina (0.29±0.78/0.47±0.12), (0.32±0.13/0.44±0.13), 0.31±0.08/0.42±0.1). Conclusión: Las bebidas isotónicas causaron un aumento en la rugosidad tanto en esmalte como en dentina luego del desafío erosivo. / Tesis

Este trabalho foi desenvolvido com o objetivo de avaliar os efeitos da luz azul na remineralização do esmalte. Adicionalmente foi desenvolvida uma metodologia de análise para a avaliação de alterações minerais do esmalte dental por meio da tomografia por coerência óptica. Lesões foram formadas em amostras de esmalte dental bovino por meio da imersão em solução tampão de acetato subsaturado (2 mL/mm2 e 6,25 mL/mm2) por 32 h. As amostras foram irradiadas com um LED azul com emissão em 455±20 nm, potência de 110 mW, irradiância de 1,4 W/cm2, tempo de irradiação de 10 s e exposição radiante de 13,8 J/cm2. Posteriormente, as amostras foram submetidas à ciclagem de pH durante oito dias à 37 oC para induzir a remineralização. A avaliação do conteúdo mineral foi realizada por meio do teste de dureza seccional e por tomografia por coerência óptica (OCT). Na avaliação por dureza observou-se que as amostras do grupo irradiado apresentaram menor conteúdo mineral que as amostras do grupo não irradiado. A diferença entre os grupos foi mais evidente nas amostras submetidas à formação de lesão em maior volume de solução desmineralizadora. Por meio da técnica de OCT foram observadas diferenças significativas entre o sinal do esmalte hígido e desmineralizado. Após a remineralização, as amostras irradiadas apresentaram menor conteúdo mineral que as não irradiadas; porém, não foram observadas diferenças significativas entre os grupos. Com base nos resultados deste estudo, pode-se concluir que a irradiação com luz azul (l=455nm) promoveu a inibição da remineralização do esmalte dental. A metodologia empregada nas análises por OCT permitiu a avaliação quantitativa da perda mineral no esmalte; porém, este resultado não foi alcançado na avaliação da remineralização. / This study aimed to investigate the effects of blue radiation on dental enamel remineralization. In addition, a methodology of analysis was developed to evaluate alterations of enamel mineral content by optical coherence tomography. Artificial lesions were formed in bovine dental enamel slabs by immersing the samples in undersaturated acetate buffer (2 mL/mm2 e 6.25 mL/mm2). The lesions were irradiated with blue LED (l=455±20nm), with radiant power of 110 mW, irradiance of 1.4 W/cm2, radiant exposure of 13.8 J/cm2 and exposure time of 10 s. Remineralization was induced by pH-cycling model during 8 days. Cross-sectional hardness and optical coherence tomography (OCT) were used to assess mineral changes after remineralization. Hardness data showed that non-irradiated enamel lesions presented higher mineral content than irradiated ones and this difference was more evident in lesions formed in higher solution volume. The analysis of OCT signal also demonstrated that the mineral content of non-irradiated group was higher than in irradiated one; however, no significant difference was observed. Furthermore, significant differences in OCT sign were detected between sound and demineralized enamel. Based on the results obtained in the present study it can be concluded that blue radiation caused an inhibition of enamel remineralization. The methodology adopted for OCT analysis allowed the quantification of enamel mineral loss; however, the remineralization process could not be evaluated by this technique.

Este trabalho foi desenvolvido com o objetivo de avaliar os efeitos da luz azul na remineralização do esmalte. Adicionalmente foi desenvolvida uma metodologia de análise para a avaliação de alterações minerais do esmalte dental por meio da tomografia por coerência óptica. Lesões foram formadas em amostras de esmalte dental bovino por meio da imersão em solução tampão de acetato subsaturado (2 mL/mm2 e 6,25 mL/mm2) por 32 h. As amostras foram irradiadas com um LED azul com emissão em 455±20 nm, potência de 110 mW, irradiância de 1,4 W/cm2, tempo de irradiação de 10 s e exposição radiante de 13,8 J/cm2. Posteriormente, as amostras foram submetidas à ciclagem de pH durante oito dias à 37 oC para induzir a remineralização. A avaliação do conteúdo mineral foi realizada por meio do teste de dureza seccional e por tomografia por coerência óptica (OCT). Na avaliação por dureza observou-se que as amostras do grupo irradiado apresentaram menor conteúdo mineral que as amostras do grupo não irradiado. A diferença entre os grupos foi mais evidente nas amostras submetidas à formação de lesão em maior volume de solução desmineralizadora. Por meio da técnica de OCT foram observadas diferenças significativas entre o sinal do esmalte hígido e desmineralizado. Após a remineralização, as amostras irradiadas apresentaram menor conteúdo mineral que as não irradiadas; porém, não foram observadas diferenças significativas entre os grupos. Com base nos resultados deste estudo, pode-se concluir que a irradiação com luz azul (l=455nm) promoveu a inibição da remineralização do esmalte dental. A metodologia empregada nas análises por OCT permitiu a avaliação quantitativa da perda mineral no esmalte; porém, este resultado não foi alcançado na avaliação da remineralização. / This study aimed to investigate the effects of blue radiation on dental enamel remineralization. In addition, a methodology of analysis was developed to evaluate alterations of enamel mineral content by optical coherence tomography. Artificial lesions were formed in bovine dental enamel slabs by immersing the samples in undersaturated acetate buffer (2 mL/mm2 e 6.25 mL/mm2). The lesions were irradiated with blue LED (l=455±20nm), with radiant power of 110 mW, irradiance of 1.4 W/cm2, radiant exposure of 13.8 J/cm2 and exposure time of 10 s. Remineralization was induced by pH-cycling model during 8 days. Cross-sectional hardness and optical coherence tomography (OCT) were used to assess mineral changes after remineralization. Hardness data showed that non-irradiated enamel lesions presented higher mineral content than irradiated ones and this difference was more evident in lesions formed in higher solution volume. The analysis of OCT signal also demonstrated that the mineral content of non-irradiated group was higher than in irradiated one; however, no significant difference was observed. Furthermore, significant differences in OCT sign were detected between sound and demineralized enamel. Based on the results obtained in the present study it can be concluded that blue radiation caused an inhibition of enamel remineralization. The methodology adopted for OCT analysis allowed the quantification of enamel mineral loss; however, the remineralization process could not be evaluated by this technique.

La presente investigación tuvo por objetivo identificar los factores asociados a la aparición de DDE en dentición decidua, en el hospital Luis Heysen Inchaústegui, Chiclayo, 2019. El diseño de investigación fue descriptivo, prospectivo, transversal y observacional; para determinar la muestra se tomó de un total de 135 pacientes habiendo seleccionado según criterios de inclusión y exclusión, se encontró 37 niños con DDE, los cuales, con el consentimiento informado firmado por la madre, fueron evaluados en la unidad dental, con luz artificial y un equipo de examen dental. Luego de realizar el análisis estadístico de los datos de manera descriptiva, con (chi-cuadrado, coeficiente de contingencia y gamma) para encontrar y evaluar las relaciones, respecto al DDE se llegó a la conclusión de que los factores asociados en la aparición de DDE, no sería ninguno de los factores posibles citados, sin embargo el análisis descriptivo desarrollado establece que podrían ser, el sexo del bebé, el peso al nacer, el tipo de parto, las infecciones maternas durante la gestación e infecciones en el primer año de vida del bebé; dada las cifras establecidas en cada uno de los casos. Esto es debido a la poca cantidad de datos, que conformaron nuestra muestra, añadida la dificultad para encontrar estos casos y poder estudiarlos, por eso se recurrió a una muestra no probabilística que no es sensible a esta situación. Finalmente se considera al estudio como un importante aporte para los protocolos de prevención en los procesos de gestión y cuidados en los primeros años de vida del bebé.

El objetivo del presente estudio in Vitro fue evaluar la fuerza de adhesión de un sistema adhesivo a la superficie del esmalte blanqueado con peróxido de carbamida al 10% con flúor y sin flúor Se utilizaron 9 terceras molares sanas, las cuales fueron divididas en 3 grupos: control (no blanqueado), grupo I (blanqueado con Opalescence 10%), grupo II (blanqueado con Opalescence PF 10%). Los grupos blanqueados tuvieron un periodo de blanqueamiento de 6horas por día a temperatura 37°C durante 14 días consecutivos y fueron almacenados en saliva artificial. / -- The purpose of this study in vitro was to evaluate the bond strength of adhesive system to the surface of bleached enamel with 10% carbamide peroxide with fluoride and without fluoride. We used nine healthy third molars, which were divided in three groups: Control (unbleached), group I (bleached with 10%Opalescence), group II (bleached with 10%Opalescence PF). Bleached groups had a period of bleaching of 6hours per day at 37°C, during 14 consecutive days and were stored in artificial saliva.

Determina la actividad inhibitoria del extracto etanólico de Theobroma cacao L, sobre el crecimiento y la adherencia in vitro del Streptococcus mutans al esmalte dentario. Evalúa el efecto sobre el crecimiento con el método de difusión en pocillos con los extractos de semilla, de cáscara y controles. Los resultados se expresan con la medida de halos de inhibición. Para el test de adherencia, se expone los cuerpos de esmalte dental, con 2ml de caldo BHI +10% sacarosa +respectivo extracto. En el control positivo no se usa extracto. Se agrega 0.1ml de la suspensión del microorganismo en cada pozo (incubación por 48 horas a 37°C). Luego, los microorganismos adheridos al esmalte son desprendidos, diluidos 1/10, y sembrados en agar Mitis salivaris, para su lectura a las 48h. Los resultados se expresan como UFC/ml. Se observa mayor halo de inhibición y menor conteo de UFC/ml con el uso del extracto de cáscara, seguido por el extracto de semilla, con respecto al grupo control. Concluye que el extracto etanólico de Theobroma cacao L. tiene actividad inhibitoria sobre el crecimiento y adherencia in vitro del Streptococcus mutans al esmalte dentario, siendo mayor el efecto del extracto de cáscara de cacao.

Investiga el manejo odontológico y las posibles opciones de rehabilitación en los casos de hipomineralización incisivo molar. Se reporta clínicamente a un paciente masculino de 8 años 9 meses con diagnóstico sistémico de Comunicación Interauricular (CIA), Retraso Psicomotor Global, Síndrome de Brown, Enfermedad por Reflujo Esofágico (ERGE), TBC Latente; atendido en el INSN-Breña, en el servicio de Odontología de Pacientes Medicamente Comprometidos. Odontológicamente el paciente presenta Hipomineralización en primeras molares y en incisivos centrales inferiores permanentes; debido a la complejidad de las lesiones a restaurar y la poca capacidad del paciente para mantener la apertura bucal por mucho tiempo se opta por rehabilitar al paciente en sala de operaciones, colocándose coronas de acero preformadas en molares más afectados y restaurando con Resina Composite los molares e incisivos menos afectados. En los controles realizados al paciente se puede observar que ha mejorado la calidad de vida, ya que no presenta más sensibilidad dentinaria, tampoco molestias al comer, encontrando a un paciente y sus padres muy satisfechos con los tratamientos realizados, considerando hasta ahora el tratamiento exitoso, tanto clínico como radiográfico. Concluye que la ejecución de medidas preventivas individuales puede posponer el inicio del tratamiento restaurador y reducir la incomodidad del paciente a largo plazo. El diagnóstico precoz permite el seguimiento y la instauración de dichas medidas preventivas tan pronto las superficies afectadas sean accesibles. Las coronas de Acero son una buena opción de tratamiento en dientes muy afectados. / Trabajo académico

Reporta la rehabilitación bucal de un paciente de sexo masculino de 16 años de edad, con diagnóstico de Amelogénesis Imperfecta Tipo I (Hipoplásica), atendido en el Servicio de Pacientes Medicamente Comprometidos del Departamento de Odontología del Instituto Nacional de Salud del Niño. Una vez definido el diagnostico se optó por realizar un plan de tratamiento que incluya las fase educativa, fase preventiva, fase curativa, fase rehabilitadora y la fase de mantenimiento. En la fase de rehabilitación se planificó tratamientos de máxima conservación de estructura dental por lo que se realizó con coronas de resina y acero, mostrado una evolución favorable. / Trabajo académico

Este estudo teve como objetivo verificar a possibilidade de utilizar o esmalte bovino, em teste resistência de união, substituindo o esmalte humano, bem como, analisar a resistência de união, morfologia de interface e padrão de condicionamento de sistemas adesivos autocondicionantes aplicados ao esmalte intacto e asperizado. Foram usados 40 dentes humanos e 40 dentes bovinos. Cada dente foi dividido em quatro regiões, de maneira a permitir a obtenção dos corpos-de-prova de todas as condições experimentais. Três sistemas adesivos autocondicionates; Clearfil Protect Bond (Kuraray Medical inc), Adper Prompt L-Pop (3M-ESPE), i Bond (Heraeus-Kulzer) foram testados, sendo utilizado um sistema de condicionamento total, Excite (Ivoclar-Vivadent), como controle positivo. A resina Tetric Ceram foi utilizada para a confecção dos corpos-de-prova, para resistência de união e amostras de microscopia eletrônica de varredura (MEV). As médias de resistência de união foram avaliadas por análise de variância e Tukey. Não houve diferença estatística, na resistência de união, entre os substratos, embora, as médias em esmalte humano tenham sido mais altas. A interação tripla; sistema Adesivo x Tratamento x Esmalte, também não foi significante, no entanto, manteve-se a tendência dos autocondicionantes de passo único apresentar as menores médias de resistência de união, principalmente no esmalte intacto. Houve diferença estatística para o fator sistema adesivo, sendo que o menor resultado foi obtido com o adesivo i Bond, na interação sistema adesivo x tratamento, a menor média também foi obtida pelo adesivo i Bond, quando aplicado ao esmalte intacto. O fator tratamento foi significante, sendo que, na variável de esmalte asperizado constatou-se a maior média de resistência de união, evidenciando que a asperização da superfície de esmalte, quando um sistema adesivo autocondicionante é aplicado no esmalte, constitui um passo operatório essencial. As imagens de MEV evidenciaram maior porosidade no dente bovino, independente do sistema adesivo utilizado e maior descalcificação do esmalte, tanto asperizado, quanto intacto, para os adesivos Excite e Adper Prompt L-Pop. Em relação à interface observou-se, que a camada de adesivo, no esmalte asperizado, tanto humano, quanto bovino, mostrou-se mais espessa, não importando o tipo de sistema adesivo; autocondicionante ou convencional. Os prismas de esmalte, no substrato bovino, mostraram um arranjo diferenciado, do observado no esmalte humano, porém esta diferença não promoveu alteração na resistência de união, visto que, não houve diferença estatística entre os substratos. Assim na impossibilidade de se obter esmalte humano, para testes de microtração, a utilização do esmalte bovino é viável. / The aim of this study was to verify the possibility in use the bovine enamel, as a substitute to human enamel, in the microtensile bond strength test, as well as analyze the bond strength, interface morphology and etch pattern of the self etching primers (SEP) applied in the cut and uncut, bovine and human, enamel. For this 40 human teeth and 40 bovine teeth were used, each tooth was divided in four halves to obtain all experimental conditions in the same tooth. Three SEP; Clearfil Protect Bond (CPB) (Kuraray Medical Inc), Adper Prompt L-Pop (LP) (3M-ESPE), i Bond (IB) (Heraeus-Kulzer) were tested, using a conventional adhesive system, Excite (EX) (Ivoclar Vivadent), as a positive control. A bulk of composite resin, Tetric Ceram (Ivoclar Vivadent), was build up for the specimens of microtensile test and SEM. In all above trials, some specimens were randomly selected and prepared for SEM. The data collected was submitted for statistical analyze ANOVA and Tukey test. It was possible to verify that there were no statistically differences between the substrate and triple interaction Adhesive Systems x Substrate x Treatment, but in the booth conditions, the SEP, i Bond, showed the lowest means, as same as, all means in bovine enamel were lowest than in human enamel. There were statistically differences between the systems adhesives and for treatment, cut and uncut. For adhesive systems the lowest value was observed for i Bond, in booth substrate and treatment. In the treatment conditions the greater means were observed in the cut enamel, showing that the cutting enamel is essential condition, to improve the bond strength of SEP, applied in the enamel. The SEM images, for etch pattern showed that in the bovine enamel the porosity was more thickness, for all adhesives and cut and uncut treatment. It was possible to verify, trough SEM of morphology interface, that the all adhesives in cut enamel, had adhesive layer more thickness, as and exception was the SEP, I Bond, that showed adhesive layers thinner. The bovine enamel showed a different arrangement for prisms that showed in the human enamel. We conclude that when the use of human enamel, in the microtensile test, is unviable, it is possible to use the bovine enamel as a substrate.

O objetivo deste estudo foi avaliar, in vitro, a influência do refrigerante de limão (Sprite®), do suco à base de soja sabor maçã (Ades®) e do suco de morango (Kapo®), empregadas rotineiramente na alimentação de crianças na microdureza superficial e profunda do esmalte de dentes decíduos em função do tempo de exposição. Foram utilizadas quarenta coroas de incisivos decíduos humanos hígidos, acomodados em bases de acrílico mantendo as superfícies vestibulares expostas. Os conjuntos dente/base de acrílico foram impermeabilizados com esmalte cosmético, deixando exposta uma área de 3 mm de diâmetro na face vestibular, na qual foram realizadas as medidas de microdureza superficial Knoop (50 gf, 10 segundos e 5 endentações). Os espécimes foram divididos aleatoriamente em 4 grupos (n=10), de acordo com as bebidas empregadas (Sprite®, Ades®, Kapo®) e controle (mantidos em saliva artificial). Os ciclos de imersão foram realizados sob agitação, durante 5 minutos, 3 vezes ao dia, com intervalos de 4 horas durante 60 dias. As medidas de microdureza superficial foram realizadas após 7, 15, 30, 45 e 60 dias. Obtidas as medidas superficiais, os espécimes foram cortados no sentido longitudinal, lixados e polidos para a avaliação das medidas de microdureza a 30, 60, 90, 120, 150, 200 e 300?m de profundidade em relação à superfície exposta das bebidas. Os dados da microdureza superficial e profunda foram analisados estatisticamente pelos testes ANOVA e Tukey. Foi realizada a microscopia eletrônica de varredura em 20 coroas de incisivos decíduos humanos hígidos submetidos ao mesmo protocolo de imersão dos espécimes utilizados para a análise de microdureza. Nos resultados da porcentagem de variação de microdureza superficial (%VMS), observou-se que o Sprite® apresentou a maior variação de micro dureza superficial (62,02%), sendo estatisticamente diferente do Kapo®morango (49,05%) do Ades®maçã (40,56%) e da saliva (-11,31%). Houve perda progressiva da microdureza ao longo dos períodos estudados. Os resultados da microdureza em profundidade mostraram que houve diferença estatisticamente significante entre o refrigerante de limão (117,98 KHN), o suco de maçã à base de soja (188,18 KHN) e o suco de morango (157.27 KHN). Apenas na profundidade de 300 ?m é que ocorreu semelhança entre as quatro soluções estudadas. Concluiu-se que todas as bebidas avaliadas alteraram a microdureza do esmalte de dentes decíduos tanto superficialmente quanto em profundidade. A alteração em profundidade foi evidente até 200?m, sendo que o Sprite® alterou o esmalte de maneira mais intensa. Observou-se ainda que a alteração na microdureza do esmalte foi diretamente proporcional ao tempo de exposição a essas bebidas. As soluções deste estudo influenciaram negativamente a dureza do esmalte. / The aim of this study was to assess, in vitro, the influence of a lemon soft drink (Sprite®), an apple soya juice (Ades®) and a strawberry juice (Kapo®) routinely utilized in children\'s diet on the superficial and deep microhardness of primary teeth enamel, as a function of the exposure time. Forty crowns of caries-free human primary incisors were included in acrylic bases, keeping the buccal surfaces exposed. The ensembles tooth/acrylic base were rendered waterproof by coating them with cosmetic nail varnish, leaving exposed a 3-mm area on the buccal surface, in which superficial Knoop microhardness measurements were performed (50 gf, 10 sec and 5 indentations). The specimens were randomly assigned to 4 groups (n=10), according to the beverages employed (Sprite®, Ades®, Kapo®) and the control group (kept in artificial saliva). The immersion cycles were performed under agitation for 5 minutes, 3 times a day, with 4 hours intervals, during a 60-day period. The superficial microhardness measurements were done after 7,15,30,45 and 60 days. Once the superficial measurements were performed, the specimens were longitudinally cut, ground and polished for the deep measurements to be accomplished. Microhardness measurements were done at 30, 60, 90, 120, 150, 200 e 300?m deep from the surface exposed to the beverages. Superficial and deep microhardness data were statistically analyzed using ANOVA and Tukey statistical tests. Scanning electron microscopy was performed in 20 crowns of caries-free human primary incisors submitted to the same imersion regimen as that of specimens utilized for microhardness testing. The results of superficial microhardness variation percentage (%VMS) showed that Sprite® (62, 02%) yielded the greatest microhardness, being statistically different from Kapo® (49, 05%); Ades® (40, 56%) and saliva (-11, 31%). There was a gradual and significant microhardness loss on superficial microhardness in all periods evaluated. The results of deep microhardness showed that there was statistically significant difference between the lemon soft drink (117, 98 KHN), apple soya juice (188, 18 KHN) and the strawberry juice (157.27 KHN). There was similarity between the beverages evaluated only at 300 ?m depth. It may be concluded that all beverages evaluated altered both the superficial and the deep microhardness of enamel of primary teeth. The alteration in deep microhardness was evident up to the 200?m depth. Sprite® affected the enamel more aggressively. It was also observed that the alteration on the enamel microhardness was directly proportional to the time of exposure to the beverages. The beverages of the reported study presented a negative impact on the enamel surface and depth of primary teeth.