Made available in DSpace on 2011-12-27T14:14:37Z (GMT). No. of bitstreams: 2 000429330-0.pdf: 4876127 bytes, checksum: 03e0c09981d2813cd511c4f745b49744 (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / The objective of this study was to evaluate the interface and bond strength of self-adhesives resin cement to dentin pretreated with 11,5% polyacrylic acid. Fifty-six third molars were randomly divided into 7 groups (n=24/group): G1 (control) - Rely X ARC; G2 - RelyX Unicem; G3 - Maxcem Elite; G4 - Set; G5 - polyacrylic acid + Rely X Unicem; G6 - polyacrylic acid + Maxcem Elite; G7 - polyacrylic acid + Set. Resin composite blocks were cemented to flat dentin with a load of 1 kg during 2 minutes, followed by light polymerization. After storage in distilled water at 37ºC for 24 hours, six tooth/resin sets were cut parallel to the long axis of the tooth, in the x and y directions, with a section of about 0. 8 mm2. Twenty-four specimens were obtained to each group, and submitted to microtensile bond strength (μTBS) test in an universal testing machine at 0,5 mm/min crosshead speed. Two sets of each group were sectioned mesio-distal in the center of their crown with a diamond blade. The surfaces were polished by wet sanding with 400, 600 and 1200-grit silicon carbide abrasive paper, followed by polishing with 6, 3, 1 and ¼ μm diamond paste. The samples were demineralized, deproteinized, dried, metalized and observed on a scanning electron microscope at 4. 000x. According to ANOVA and Tukey´s test (a=0,05), the mean ZTBS of RelyX ARC (24. 19 MPa) and RelyX Unicem (23. 12 MPa) associated with polyacrylic acid were not significantly different themselves and were superior to other groups (p<0,05).The ZTBS mean of Maxcem Elite associated with polyacrylic acid (13. 09 MPa) was statistically higher to Maxcem Elite without polyacrylic acid (8. 14 MPa). The RelyX Unicem without polyacrylic acid (10. 23 MPa) did not differ statistically from Maxcem Elite with and without polyacrylic acid. All specimens of Set were lost during the cutting procedure. The hybrid layer was not observed for the self-adhesive resin cements, and resin tags were observed for RelyX Unicem, Maxem Elite and when combined with polyacrylic acid. Pretreatment with 11,5% polyacrylic acid was effective for the bond of RelyX Unicem and Maxcem Elite to dentin. / O objetivo desse estudo foi avaliar a interface e a resistência de união de cimentos resinosos autoadesivos à dentina condicionada com ácido poliacrílico a 11,5%. Cinquenta e seis dentes, terceiros molares, foram divididos aleatoriamente em 7 grupos (n=24/grupo): G1 (controle) - Rely X ARC; G2 - RelyX Unicem; G3 - Maxcem Elite; G4 - Set; G5 - ácido poliacrílico + Rely X Unicem; G6 - ácido poliacrílico + Maxcem Elite; G7 - ácido poliacrílico + Set. Blocos de resina composta foram cimentados sobre dentina plana com carga de 1Kg por 2 minutos, seguido de fotoativação. Após armazenagem em água destilada a 37º C por 24 horas, seis conjuntos dente/resina foram cortados, paralelamente ao longo eixo do dente, nos sentidos x e y, com secção de aproximadamente 0,8 mm2. Foram obtidos 24 corpos de prova para cada grupo, sendo então submetidos ao teste de resistência à microtração (RZt) em máquina de ensaio universal com velocidade de 0,5 mm/min. Dois conjuntos de cada grupo foram seccionados no sentido mésio-distal, no centro de suas coroas, com um disco diamantado de dupla face. As superfícies foram polidas com lixas de carbeto de silício 400, 600 e 1200, seguido de polimento com pastas dimantadas de granulação 6, 3, 1 e ¼ μm. As amostras foram desmineralizadas, desproteinizadas, secadas, metalizadas e observadas em microscópio eletrônico de varredura em aumento de 4. 000 vezes. De acordo com Análise de Variância e teste de Tukey (a=0,05), a média de RZt do RelyX ARC (24,19 MPa) e do RelyX Unicem associado ao ácido poliacrílico (23,12 MPa) não diferiram estatisticamente entre si e foram superiores aos outros grupos (p<0,05). A média de RZt do Maxcem Elite associado ao ácido poliacrílico (13,09 MPa) foi, estatisticamente, superior ao Maxcem Elite sem ácido poliacrílico (8,14 MPa).O RelyX Unicem sem ácido poliacrílico (10,23 MPa) não diferiu, estatisticamente, do Maxcem Elite sem e com ácido poliacrílico. Todos os corpos de prova do Set foram perdidos durante o procedimento de corte. Para os cimentos resinosos autoadesivos não foi observada formação de camada híbrida, havendo a formação de tags de resina para o RelyX Unicem e Maxem Elite quando associados ao ácido poliacrílico. O pré-tratamento com ácido poliacrílico a 11,5% foi efetivo para a união do RelyX Unicem e Maxcem Elite à dentina.

Made available in DSpace on 2011-12-27T14:14:37Z (GMT). No. of bitstreams: 2 000417773-0.pdf: 1138982 bytes, checksum: 03423e2cddaa5a43349be69c0853e615 (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / Given that the majority of osseointegrated implants undergo some type of surface conditioning in order to improve osseoitegration and that in vitro differentiation of mesenchymal cells into osteoblasts is a mastered process that has been used for evaluating a given biomaterial with regard to its osteinductive and osteoconductive capabilities, the present work aims to evaluate the adhesion, proliferation and differentiation of human bone marrow cells on titanium implant surfaces that have or have not been treated by discrete calcium phosphate deposition. Human bone marrow cells obtained from a single donor were cultured in media containing 12 titanium discs of one of the following: the Bonelike® (Biomet 3I, Brazil) with a surface treated by double acid etching; the Osseotite™ (Biomet 3I, USA) with similar surface treatment and the Nanotite™(Biomet 3I, USA). After 14 and 21 days of culture, real time PCR and SEM examinations were performed. From the results we concluded that implant surface roughness allows cell adhesion, differentiation and proliferation, the ALP synthesis is higher in Bonelike® and the presence of calcium phosphate nanoparticles on an implant surface leads to enhanced BGLAP synthesis and cell proliferation. / Os implantes osseointegrados, em sua maioria, possuem algum tipo de condicionamento da sua superfície que visa melhorar a osseointegração. O mecanismo de diferenciação celular in vitro de células mesenquimais em osteoblastos já é bastante conhecido e serve para avaliação das propriedades de osteoindução e osteocondução de biomateriais. O presente estudo tem por objetivo avaliar a adesão, proliferação e diferenciação das células da medula óssea humana em superfícies de implantes de titânio com e sem deposição discreta de fosfato de cálcio. As células foram obtidas a partir da medula óssea de um doador humano. Foram selecionados 12 discos de titânio do tipo Bonelike® (Biomet 3I, Brasil) com superfície tratada por duplo ataque ácido; Osseotite™ (Biomet 3I, USA) com superfície tratada por duplo ataque ácido e Nanotite™ (Biomet 3I, USA). Após 14 e 21 dias de cultura foi realizado PCR em tempo real para avaliação da diferenciação celular e microscopia eletrônica de varredura para avaliação da proliferação e adesão celular aos discos de titânio. Os resultados indicaram que a rugosidade da superfície dos discos de titânio possibilita a adesão, diferenciação e proliferação celular, que a síntese de ALP é maior na superfície Bonelike e que as partículas de fosfato de cálcio demonstraram maior grau de síntese de BGLAP e proliferação celular.

Made available in DSpace on 2011-12-27T14:14:39Z (GMT). No. of bitstreams: 2 000381259-0.pdf: 1714523 bytes, checksum: dac5b4776e73af1f3bdc4f7292a62fe4 (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / Temporomandibular Disorders (TMD) is a collective term embracing muscle and skeletal alterations of multifactorial origin, which involve physical, psychological and social aspects. These conditions have the potential to compromise the comfort and functional health of the stomatognathic system and a great number of treatment modalities have been proposed. The objective of this randomized single-blinded study was to evaluate the effect of gallium/aluminum/arsenide laser therapy (low level laser therapy - LLLT) in the masseter, temporal and lateral pterygoid muscle symptomatology in patients diagnosed with TMD. Thirty-one female patients underwent the Research Diagnostic Criteria for TMD (RDC/TMD) and randomly divided into two groups: Group 1 (n = 16) and Group 2 (n = 15). The therapeutic protocol consisted of six applications on the most painful muscle sites previously determined (04 Joules/cm2; 100 mW; 40 seconds) for two weeks. Pain was assessed by 100 mm visual analogue scales (VAS) at baseline, and at 14, 30 and 90 days after the last (6th) LLLT application. Non-parametric tests, such as the Person’s Chi Square, the Fisher’s Exact test, the Sign test, and Mann-Whitney U test were used for the categorical variables of the RDC/TMD. For the continuous variables (VAS), after the use of the Kolmogorov-Smirnov Single-Sample Normality test, paired t-test, Pearson’s and Spearman’s correlation were used. At the end of 90 days, it could be observed that Group II showed a statiscally significant reduction in both pain at rest (p < 0. 01) and during function (p < 0. 05) when compared to Group I. Therefore, it can be concluded that As/Ga/Al LLLT, in this treatment protocol, was significantly more efficacious than placebo when treating TMD patients, particularly myofascial pain. / As disfunções têmporo-mandibulares (DTM) compreendem alterações músculo-esqueléticas de origem multifatorial, envolvendo aspectos físicos, psicológicos e sociais. Estas condições têm potencial para comprometer o conforto e a saúde funcional dos componentes do sistema estomatognático e várias modalidades terapêuticas têm sido propostas. O objetivo deste estudo randomizado simples-cego foi avaliar o efeito do laser terapêutico Arsenieto de Gálio- Alumínio (AsGaAl) na sintomatologia dolorosa dos músculos masseter, temporal e pterigoideo lateral em pacientes diagnosticados com DTM. Trinta e um pacientes do sexo feminino foram submetidos ao Critério de Diagnóstico de Pesquisa das Desordens Temporomandibulares (Research Diagnostic Criteria/Temporomandibular Disorders) e divididos aleatoriamente em 02 grupos: grupo 1 (placebo n=16) e grupo 2 (teste n=15). O protocolo terapêutico consistiu em 06 aplicações sobre os locais de maior dor muscular previamente determinado (04 Joules/cm2; 100 mW; 40 segundos) durante um período de 02 semanas. A dor foi mensurada por meio de uma escala análoga visual de 100 mm antes do início do tratamento e aos 14, 30 e 90 dias após a 6ª e última aplicação do laser. Para a análise estatística das variáveis categóricas (RDC/DTM) utilizou-se os testes não-paramétricos Chi- Quadrado (Pearson), Exato de Fisher, do Sinal e teste U de Mann-Whitney; para as variáveis contínuas (escala análoga visual - EAV), após a utilização dos testes de normalidade de Kolmogorov-Smirnov (Teste Z), os dados foram submetidos ao Teste “t” Pareado. As variáveis paramétricas foram submetidas ao teste de Correlação de Pearson e as variáveis não-paramétricas ao teste de Correlação de Spearman’s.Ao final, observou-se que o grupo teste apresentou após o período de acompanhamento de noventa dias, uma diminuição da dor facial em repouso e atividade de modo estatisticamente significante quando comparado com o grupo placebo. Portanto, concluímos que o laser AsGaAl, no protocolo terapêutico proposto, foi eficaz na remissão da dor muscular em atividade e em repouso no grupo teste em relação ao grupo placebo, em pacientes com Disfunção Têmporo-Mandibular e Dor Oro-Facial.

Made available in DSpace on 2011-12-27T14:14:40Z (GMT). No. of bitstreams: 2 000422269-0.pdf: 1482550 bytes, checksum: 2ab1328a5dd68b64d8200aabbf0ab2c1 (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / This in vitro study evaluated the combined effect of 10% carbamide peroxide with three toothpastes used during bleaching treatment on microhardness and surface roughness of enamel. Fragments (4mm x 4mm x 2mm) were obtained from 18 human teeth. The initial roughness and microhardness were measured. The fragments were randomly divided into six groups (n=12): G1 - 10% carbamide peroxide (PC10) and brushing with regular toothpaste (R); G2 - PC10 and whitening toothpaste (W); G3 – PC10 and whitening toothpaste with baking soda and peroxide (BS); G4 – Placebo (PLA)+R; G5 (PLA+W); G6 (PLA+BS). The fragments were daily exposed to each treatment agent for six hours and the brushing procedures were performed for seven seconds, with a brushing force of 200g and 250 cycles per minute. The groups were kept in artificial saliva at 37°C until the next cycle of treatment agent and brushing procedures. After 21 days, the final roughness and microhardness measurements of each fragment were obtained. According to paired Student’s t-test, there was a significantly decrease in microhardness for all groups (p<0. 05). The final roughness was statistically higher than the initial roughness only in the group treated with G6 (p=0. 001).According to ANOVA GLM and Bonferroni tests, PLA presented a significantly higher roughness than PC10, and toothpaste BS presented a statistically higher roughness (p<0. 05) than W. Toothpaste R did not differ statistically from W and BS (p>0. 05). For PC10, the toothpastes did not differ among them in relation to microhardness (p>0. 05). According to paired Student’s t-test, toothpastes R and W were statistically different for both treatments. The association of PC10 with toothpastes R, W and BS for 21 days did not significantly alter the enamel surface roughness, but there was a significant decrease in the enamel microhardness. / Foram realizados dois estudos, in vitro e in situ para avaliar a rugosidade e microdureza do esmalte clareado com peróxido de carbamida a 10% (PC10) e escovado com dentifrícios. Fragmentos de esmalte foram obtidos a partir de dentes humanos. A rugosidade e microdureza iniciais foram medidas. Para o estudo in vitro, estes fragmentos foram divididos em seis grupos (n=12): G1 – PC10 e escovado com um dentifrício regular (R); G2 – PC10 escovado com dentifrício clareador (W); G3 – PC10 escovado com dentifrício clareador com bicarbonato de sódio e peróxido de cálcio (BS); G4 – Placebo (PLA) + R; G5 – PLA+W; G6 – PLA+BS. Os fragmentos foram expostos a cada agente de tratamento por 6 horas e escovados com força de 200g por 250 ciclos/minuto durante 7 segundos. Os grupos foram armazenados à 37°C em saliva artificial. Após 21 dias foram feitas medidas finais de rugosidade e microdureza de cada fragmento. Para o estudo in situ, dois grupos de cinco voluntários receberam o PC10 e o PLA por 21 dias em diferentes sequências e em dois períodos distintos, utilizando um estudo crossover 2X3. Foram obtidos 180 fragmentos e distribuídos em 20 dispositivos removíveis intraorais (DRI). Cada DRI recebeu nove fragmentos divididos em três trios, nos quais foram escovados com três dentifrícios: R (Colgate máxima proteção anticáries) no centro do palato; W (Colgate total 12 whiteness gel) e BS (Colgate whitening Oxygen Bubbles) nas regiões direita e esquerda dos pré-molares, respectivamente. Ambos agentes de tratamentos foram aplicados por 8 horas durante a noite. Após as escovações, os voluntários usaram os DRI por, aproximadamente, 16 horas/dia. Para o segundo período (21 dias), novos DRI foram distribuídos e os voluntários receberam o agente de tratamento diferente daquele utilizado no primeiro período.As medidas de rugosidade e microdureza foram medidas antes e após cada período. De acordo com o teste t-Student pareado, in vitro, houve uma diminuição significante da microdureza para todos os grupos (p<0,05) e a rugosidade final foi estatisticamente maior que a final apenas para o G6 (p=0. 001). In situ, a rugosidade final foi estatisticamente maior que a inicial e a microdureza final foi estatisticamente menor que a inicial (p<0,05). De acordo com a ANOVA GLM, apenas os dentifrícios foram significantes (p=0,037) para a rugosidade superficial. No estudo in vitro, o agente PLA apresentou um aumento significativamente maior que o PC10 na microdureza do esmalte, enquanto que para o teste de Bonferroni, o dentifrício BS apresentou uma rugosidade significativamente maior que o W (p<0,05). Em relação a microdureza, com o PC10, os dentifrícios não diferiram entre si. Pode-se concluir, para o estudo in vitro, que a associação do PC10 com dentifrícios R, W e BS por 21 dias não alterou significativamente a rugosidade, mas diminuiu significativamente a microdureza do esmalte. Para o estudo in situ, a associação do peróxido de carbamida a 10% com os dentifrícios BS, W e R causou um aumento significativo na rugosidade e uma diminuição significativa na microdureza superficial do esmalte. O dentifrício BS apresentou a maior rugosidade, seguido por W e R.

Made available in DSpace on 2011-12-27T14:14:40Z (GMT). No. of bitstreams: 2 000428359-0.pdf: 582244 bytes, checksum: c0e24791c0bf94ca1e52e3ad9c02d954 (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / The objectives of this study were to evaluate and to compare rotatory instruments of NiTi from two different commercial brands, where twenty new nickel-titanium endodontic rotatory alloys were taken to the analysis. These alloys were distributed in two groups, in agreement with the manufacturer, being the first composed by 10 K3 alloys (SDS Kerr, Glendora, CA EUA), and the second, by 10 Profile alloys (Maillefer, Ballaiques, Switzerland). The dimensions of the tested alloys are corresponding to the specifications 25. 06 (diameter in the tip equal to 0,25mm, and taper 0, 06). Observations of the alloys were made by electronic microscopy of scintiscan, with analysis of SDE, for characterization of the superficial conditions of the material as provided. The cut surface and the microstructure were also analyzed. After this analysis, the samples were submitted to a test of fatigue for flexing through a system composed by a metallic artificial canal with an angle of curvature of 90 degrees and an electric engine where the contra-angle was connected. The established protocol of speed was of 350 RPM.The alloys were inserted in rotatories movement, until the moment of the fracture. The registration of time was accomplished with a digital timer and the verification of the occurrence of the fracture of the instrument was visual and hearing. The number of necessary cycles for fracture of the alloy was calculated through the relation time and rotations per second until the fracture of each instrument. The twenty recovered fragments were measured (mm) through a digital pachymeter. Based on the observations of this study, it can be verified that the alloys present the same superficial composition and pattern, however, the instruments differed themselves related to the external morphology. Under the experimental condition of the current study, the Profile system presented resistance to cyclical fatigue significantly larger when compared to the K3 system, tested in an abrupt curvature of 90º. The K3 alloy presented average of 547 while Profile presented average of 807. Related to the size of the fragments there was no any relation among the different proposals. / Os objetivos deste estudo foram avaliar e comparar instrumentos endodônticos rotatórios de NiTi de duas marcas comerciais distintas quanto a resistência a fadiga cíclica, microestrutura, morfologia externa, onde vinte limas rotatórias de níquel-titânio novas, foram levadas à análise. Estas limas foram distribuídas em dois grupos, de acordo com o sistema, sendo o primeiro composto de 10 limas K3 (SDS Kerr, Glendora, CA EUA), e o segundo, por 10 limas Profile (Maillefer, Ballaiques, Suiça). As dimensões das limas testadas são correspondentes às especificações 25. 06 (diâmetro na ponta igual a 0,25mm, e conicidade 0,06). Foram feitas observações das limas por microscopia eletrônica de varredura, com análise de EDS, para caracterização das condições superficiais do material como fornecido. A superfície de corte e a microestrutura também foram analisadas. Após esta análise, as amostras foram submetidas a um ensaio de fadiga por flexão através de um sistema composto por um canal artificial metálico com um ângulo de curvatura de 90 graus e um motor elétrico onde o contra-ângulo foi conectado. O protocolo de velocidade estabelecido foi de 350 RPM. As limas foram inseridas em movimento rotatório, até o momento da fratura. O registro de tempo foi realizado com um cronometro digital até o momento da fratura. O número de ciclos necessários para fratura da lima foi calculado através da relação tempo e rotações por segundo até a fratura de cada instrumento.Os vinte fragmentos recuperados foram medidos (mm) através de um paquímetro digital. Com base nas observações deste estudo, pode-se constatar que as limas apresentam a mesma composição superficial e padrão de microestrutura, entretanto, os instrumentos se diferem quanto à morfologia externa. Sob a condição experimental do estudo atual, o sistema Profile apresentou a resistência à fadiga cíclica significativamente maior quando comparada ao do sistema K3, testadas em uma curvatura abrupta de 90º. A lima K3 apresentou média de 547 enquanto a Profile apresentou média de 807. Quanto ao tamanho dos fragmentos não houve qualquer relação entre as diferentes propostas. Pode-se concluir que as limas apresentam a mesma composição superficial e padrão de microestrutura, entretanto se diferem quanto à morfologia externa.

Made available in DSpace on 2011-12-27T14:14:41Z (GMT). No. of bitstreams: 2 000418704-0.pdf: 399268 bytes, checksum: e46093bbe376f77e85de6f280fd10dde (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / Aims: To evaluate the influence of the energy density (light intensity X exposure time) on microhardness, elastic modulus and degree of cristalinity of the following resin composites: ROK (SDI), Filtek Z250 (3M ESPE) Filtek LS (3M ESPE) and Amelogem Plus (Ultradent).Materials and Methods: Disc-shaped specimens were made with the following dimensions: 8mm of diameter x 4mm of height. Each composite was placed in two increments and light cured by a halogen light unit (LCU) with 600mW/cm2 or a LED LCU with 800mW/cm2, using 8 or 16J/cm2 energy density. Sixteen groups were tested. After light-curing, the group matrix/disc was wet-abraded with a silicon carbide paper and polishing paste. The specimens were kept in distilled water at room temperature for 24h, after which they were submitted to the microhardness hardness test using the Fischerscop HV 100 system. The elastic modulus was recorded immediately after the hardness testing in the same sample. The degree of cristalinity was analyzed by the XRD 7000. The data were submitted to the three-way ANOVA and Tukey´s test (α=5%).Results: Both microhardness and elastic modulus of the composite studied were significantly affected by energy density (p<0. 0001). Also, the LED LCU provided higher properties in comparison with halogen LCU (p<0. 001). Filtek LS presented higher pattern of cristalinity in the polymeric chain that the composites based in Bis-GMA, Bis-EMA or UDMA. This composite, though, presented lower elastic modulus and microhardness that the others. / Este estudo avaliou a influência da densidade de energia (intensidade de energia luminosa x tempo de exposição) na microdureza, no módulo de elasticidade e no grau de cristalinidade das resinas compostas Rok (SDI) Filtek Z250 (3M ESPE) Filtek LS (3M ESPE) e Amelogem Plus (Ultradent). Para a confecção dos corpos-de-prova foram utilizadas matrizes de acrílico quadradas com 4mm de espessura e um orifício central de 8mm de diâmetro A resinas foram inseridas em dois incrementos e fotopolimerizadas com aparelho de luz halógena XL 3000 (600mW/cm2) e LED Celalux (800mW/cm2) com 8 e 16J/cm2 de energia luminosa para cada uma das resinas, totalizando 16 grupos. Após a fotoativação o conjunto matriz/disco foi polido com lixas de carbeto de silício umidecidas em água e seguidas de polimento com pasta de óxido de alumínio com 6μm, 3μm, 1μm, 0,25μm. As amostras foram armazenadas em água destilada em temperatura ambiente por 24h. Decorrida esta etapa as amostras foram submetidas aos testes de microdureza e módulo de elasticidade pelo sistema Fischerscop HV 100 e medidas do grau de cristalinidade através de XRD 7000. Os dados foram submetidos aos testes de Shapiro-Wilk , ANOVA e teste de Tukey com nível de confiança de 95%. Os resultados mostraram que houve diferença significativa entre as resinas avaliadas para a microdureza (p<0,01) e o módulo de elasticidade (p<0,01) quando fotoativados com 8 e 16J/cm2. O aparelho fotopolimerizador LED apresentou melhores resultados quando comparado ao aparelho de luz halógena. A resina composta Filtek LS apresentou padrão mais cristalino de cadeia polimérica do que as resinas baseadas em Bis-GMA, Bis-EMA e UDMA, entretanto, a resina com matriz baseada em siloranos apresentou os menores valores para o módulo de elasticidade e microdureza.Conclusão: A densidade de energia assim como a fotopolimerização com aparelhos LED podem afetar significativamente a microdureza e módulo de elasticidade de resinas compostas com diferentes composições de matriz orgânica.

Submitted by Ginamara Lima (ginaj@pucrs.br) on 2012-03-27T18:22:14Z No. of bitstreams: 1 437503.pdf: 3671111 bytes, checksum: fc21218ca251e697145259f86558a4ce (MD5) / Made available in DSpace on 2012-03-27T18:22:14Z (GMT). No. of bitstreams: 1 437503.pdf: 3671111 bytes, checksum: fc21218ca251e697145259f86558a4ce (MD5) / Desde o início da epidemia da AIDS muitos esforços tem sido empregados para definir o valor clínico das manifestações estomatológicas do HIV. Entretanto, poucos estudos nos países em desenvolvimento contemplaram essas enfermidades. O objetivo desta pesquisa foi descrever o perfil epidemiológico de adultos portadores do HIV com lesões bucais associadas e avaliar os fatores de risco para a ocorrência dessas afecções. Com esse fim, um estudo transversal, retrospectivo e descritivoanalítico foi desenvolvido a partir de dados coletados em 534 prontuários médico/odontológicos de pacientes que receberam atendimento em 5 centros de referência na cidade de Porto Alegre, Rio Grande do Sul, Brasil. A análise dos dados foi realizada empregando tabulações cruzadas, teste t pareado e modelos de regressão logística. Cerca de 52% dos pacientes eram homens; 88,2% tinham mais de 30 anos de idade e 78,1% progrediram para AIDS em um período de até 5 anos a partir do diagnóstico inicial. O índice de desemprego na amostra foi de 35% e, significativamente, mais comum no gênero masculino (p<0,001). Aproximadamente 60% dos indivíduos usavam terapia anti-retroviral de alta atividade. A tuberculose foi a doença definidora de AIDS diagnosticada com maior frequência, apresentando percentual de 18,5%. As lesões bucais associadas ao HIV foram observadas em 19,3% dos pacientes no momento do diagnóstico da infecção por esse vírus. A candidíase foi a lesão bucal mais prevalente (50%), tendo predileção pelo gênero feminino (p=0,031). Os fatores de risco vinculados à sua ocorrência foram os graus de imunossupressão moderada (p<0,009) e severa (p<0,001) e alcoolismo (p=0,011).Contagens de CD4+ abaixo de 500 células/mm³ (p=0,029), carga viral acima de 5000 cópias/mm³ (p=0,003) e tabagismo (p=0,005), contribuíram para a maior prevalência de leucoplasia pilosa. O estado avançado da doença por HIV, no momento do diagnóstico, e a rápida progressão para AIDS, requerem a especial atenção dos profissionais da saúde, uma vez que podem ser indicativos de diagnóstico e acesso tardio ao tratamento. Os cirurgiões-dentistas e demais profissionais devem estar alertas para o surgimento dessas manifestações estomatológicas, uma vez que nos sujeitos avaliados neste estudo essas enfermidades foram sinais clínicos sugestivos de deterioração imune e progressão da doença. / Since the beginning of AIDS epidemic many efforts have been employed to define the value of oral cavity lesions as clinical markers of this disease. However, there are fewer reports on oral pathologies from developing countries. The main purpose of this study was to describe the epidemiological characteristics of HIV-positive adults’ carriers of associated oral lesions and evaluate the risk factors for the occurrence of these affections. For that purpose, a cross-sectional, retrospective and descriptive-analytical study was conducted in medical/dental charts of 534 patients at 5 Referral Centers for HIV/AIDS management in Porto Alegre city, Rio Grande do Sul, Brazil. Data analysis consisted of cross-tabulations, binomial t test, and logistic regression models. Nearly 52% of patients were men, 88.2% were older than 30 years and 78.1% progressed to AIDS in less than 5 years after HIV diagnosis. The unemployment index was 35% and was significantly more common among men (p<0.001). Approximately 60% of the patients used highly active antiretroviral therapy. Tuberculosis was the AIDS-defining disease most commonly seen (18.5%).The oral manifestations were seen in 19.3% of patients at the time of HIV diagnosis. Oral candidiasis was the most prevalent lesion in the oral cavity (50%), denoting predilection by the female gender (p=0.031). The risk factors for the occurrence of this affection were moderate (p<0.009) and severe (p<0.001) immunologic impairment and alcoholism (p=0.011). CD4+ counts below 500 cells/mm³ (p=0.029), a viral load above 5000 copies/mm³ (p=0.003) and smoking (p=0.005), contributed for hairy leukoplakya occurrence. The advanced stage of the disease and rapid progression to AIDS observed in this sample requires health professionals’ attention, since they may be indicative of diagnosis and treatment delay. Dentists and other health professionals might be aware to the onset of oral manifestations, since these lesions were helpful markers for the detection of HIV and suggestive clinical signs of immune deterioration and disease progression in the current survey.

Submitted by Ginamara Lima (ginaj@pucrs.br) on 2012-05-04T11:36:30Z No. of bitstreams: 1 438173.pdf: 1856345 bytes, checksum: 88a20c5de7a402c873dcfd4ecbe6460d (MD5) / Made available in DSpace on 2012-05-04T11:36:30Z (GMT). No. of bitstreams: 1 438173.pdf: 1856345 bytes, checksum: 88a20c5de7a402c873dcfd4ecbe6460d (MD5) / INTRODUÇÃO: A tomografia computadorizada do tipo Cone-beam (TCCB) fornece informações detalhadas sobre a qualidade e a quantidade de osso neoformado pela distração osteogênica (DO). Permite mensurar a densidade do osso alongado, por meio da avaliação dos tons de cinza. Desta forma, pode-se realizar uma análise quantitativa da densidade óssea, dimensionando a atenuação dos feixes de raios X pelos tecidos moles nas imagens. OBJETIVOS: Avaliar, por intermédio da TCCB, o osso mandibular neoformado em mandíbulas de coelhos submetidos à DO, sob efeito biomodulatório da irradiação por laser infravermelho AsGaAl (λ=830 nm, 40 mW), aplicado durante a fase de ativação do aparelho distrator. A área da distração é avaliada pelos níveis de cinza das imagens, observando também a influência dos tecidos moles na atenuação dos feixes de raios X. MATERIAIS E MÉTODOS: Dez coelhos foram utilizados (dois grupos experimentais e um grupo controle). Os grupos experimentais foram submetidos à DO e à terapia a laser de baixa potencia (LLLT). Os coelhos do grupo experimental A foram mortos após 11 dias do início da DO e os coelhos do grupo experimental B, mortos após 21 dias do início da DO. Os 10 coelhos foram submetidos a tomografia com tecidos moles e posteriormente dissecados e submetidos a tomografia sem tecidos moles. Assim, foi possível analisar a influência dos tecidos moles em coelhos submetidos à DO na atenuação dos feixes de raios X e, consequentemente, na diminuição dos valores de níveis de cinza observados na imagem tomográfica. RESULTADOS: A presença dos tecidos moles aumenta a atenuação dos feixes de raios X contribuindo na diminuição dos valores de níveis de cinza, observados na imagem do tecido ósseo em 3D, na mandíbula dos 10 coelhos submetidos a tomografia, antes e após a remoção dos tecidos moles. A área das mandíbulas submetidas à distração apresentaram valores superiores de cinza, nos coelhos mortos após 21 dias do início da DO. CONCLUSÕES: Com tomógrafos do tipo Cone-beam, foi possível avaliar a variação da densidade óssea em áreas submetidas à DO. A presença dos tecidos moles contribui na diminuição dos valores de níveis de cinza observados nas imagens do tecido ósseo dos 10 coelhos em 3D. Isto ocorre devido à absorção do feixe de raios X pelos tecidos moles submetidos a tomografia. Também observou-se que a densidade óssea na área da distração, visualizada na tomografia, aumenta proporcionalmente ao período de maturação óssea ocorrido após a fase de ativação da DO, conforme observação dos valores de cinza obtidos. / INTRODUCTION: Cone-beam computed tomography (CBTC) provides detailed information about the amount and quality of new bone formed during distraction osteogenesis (DO). The density of the lengthened bone is measured based on different levels of gray found in the images. The use of CBTC therefore allows to perform a quantitative analysis of bone density and, thus, to measure the level of X-ray attenuation by soft tissues. OBJECTIVES: To assess, via CBTC, newly formed bone in mandibles of rabbits treated with DO under the biomodulating effects of AsGaAl infrared laser radiation (λ=830 nm, 40 mW), applied during the activation phase. The distracted area was assessed based on the gray levels shown on images and observing the influence of soft tissues on X-ray attenuation. MATERIALS AND METHODS: Ten rabbits were used (two experimental groups and one control group). The two experimental groups were treated with DO and low-level laser therapy. Rabbits in experimental group A were killed 11 days after the beginning of DO, and those in experimental group B, after 21 days of DO. CBTC images were obtained from the mandibles of the ten rabbits with soft tissues and subsequently (after dissection) without soft tissues. This comparison allowed to analyze the influence of soft tissues on X-ray attenuation, and consequently on the decrease in gray levels observed in the tomographs of rabbits treated with DO. RESULTS: The presence of soft tissues increased X-ray attenuation, resulting in a decrease in the levels of gray observed in three-dimensional CBCT images of mandibular bone tissue of the rabbits before and after soft tissue removal. The area of the mandibles treated with DO presented higher levels of gray in rabbits killed at 21 days. CONCLUSIONS: CBCT allowed to assess bone density variation in areas treated with DO. The presence of soft tissues contributes to decrease the levels of gray in three-dimensional CBCT bone tissue images of the ten rabbits assessed. This occurs due to the absorption of X-rays by soft tissues studied by tomography. We found that bone density in the area treated with DO, as observed on tomography, increased in direct proportion to the bone maturation period after the activation phase in DO, based on the gray levels observed.

Submitted by Ginamara Lima (ginaj@pucrs.br) on 2012-05-16T12:10:29Z No. of bitstreams: 1 438292.pdf: 353384 bytes, checksum: e966b89cb4618df13c2f46329c3c7c3f (MD5) / Made available in DSpace on 2012-05-16T12:10:29Z (GMT). No. of bitstreams: 1 438292.pdf: 353384 bytes, checksum: e966b89cb4618df13c2f46329c3c7c3f (MD5) / O objetivo desse estudo foi avaliar a influência da vibração ultrassônica na resistência de união de cimentos resinosos autoadesivos à dentina. Vinte e quatro dentes terceiros molares foram divididos aleatoriamente em quatro grupos (n=6/grupo): G1 – RelyX Unicem; G2 – Maxcem Elite; G3 – RelyX Unicem com vibração ultrassônica; G4 – Maxcem Elite com vibração ultrassônica. Blocos de resina composta foram cimentados sobre dentina plana com carga de 500 g por 2 min, seguido de fotoativação nos G1 e G2. Em G3 e G4, a vibração ultrassônica foi aplicada por 20 s sobre o bloco de resina composta, seguido de carga de 500 g por 1 min e 40 s e fotoativação. Após armazenagem em água destilada a 37º C por 24 h, seis conjuntos dente/resina foram cortados paralelamente ao longo eixo do dente, nos sentidos x e y, com secção de aproximadamente 0,8 mm2. Foram obtidos 24 corpos de prova para cada grupo, sendo então submetidos ao teste de resistência à microtração (Rμt) em máquina de ensaio universal com velocidade de 0,5 mm/min. De acordo com Análise de Variância Fatorial, as variáveis tipo de cimento resinoso (p=0,000) e tipo de cimentação (p=0,002) foram significativas. A interação das duas varáveis não foi significativa (p=0,676). De acordo com o teste t-student (α=0,05) a média de Rμt com uso da vibração ultrassônica (13,74 MPa) foi estatisticamente superior sem aplicação da vibração ultrassônica (10,57 MPa)). A média de Rμt do RelyX Unicem (13,95 MPa) foi estatisticamente superior ao Maxcem Elite (10,36 MPa). A vibração ultrassônica aumentou a resistência de união dos cimentos resinosos autoadesivos RelyX Unicem e Maxcem Elite à dentina. / The aim of this study was to evaluate the influence of ultrasonic application on bond strength of self-adhesives resin cements to dentin. Twenty-four third molars were randomly divided into 4 groups (n=6/group): G1 - Rely X Unicem; G2 – Maxcem Elite; G3 – RelyX Unicem and ultrasonic application; G4 – Maxcem Elite and ultrasonic application. Composite resin blocks were luted to flat dentin with a load of 500 g for 2 min, followed by light polymerization in G1 and G2. In G3 and G4, the ultrasonic device was applied for 20 s on the composite resin block, followed by 500 g load for 1 min and 40 s, and light polymerization. After storage in distilled water at 37ºC for 24 h, six tooth/resin sets were cut parallel to the long axis of the tooth, in the x and y directions, with a section of about 0.8 mm2. Twenty-four specimens were obtained to each group, and submitted to microtensile bond strength (μTBS) test in an universal testing machine at 0,5 mm/min crosshead speed. According to two-way ANOVA, type of cement factor (p=0.000) and type of luting factor (o=0.002) were significant. The interaction was not significant (p=0676). According to student-t test (α=0.05), the μTBS mean with ultrasonic application (13.74 MPa) was statistically higher than without this treatment (10.57 MPa). The μTBS mean of RelyX Unicem (13.95 MPa) was statistically higher than Maxcem Elite (10.36 MPa). The ultrasonic application increased the μTBS of the RelyX Unicem and Maxcem Elite to dentin.

Submitted by Ginamara Lima (ginaj@pucrs.br) on 2012-08-08T20:40:07Z No. of bitstreams: 1 440591.pdf: 3736403 bytes, checksum: 8a5e110d9859d4c6d6a19122ed5e0f65 (MD5) / Made available in DSpace on 2012-08-08T20:40:07Z (GMT). No. of bitstreams: 1 440591.pdf: 3736403 bytes, checksum: 8a5e110d9859d4c6d6a19122ed5e0f65 (MD5) / As fraturas tetrapoides do complexo zigomático necessitam de uma exatidão na correção, além de eficiente fixação interna para se obter um bom resultado final. Almejando aprimorar as vantagens e minimizar as desvantagens das técnicas de fixação interna rígida, foi desenvolvido o parafuso neck screw. A estabilidade necessária para a correta fixação vem de um sistema de compressão dinâmica aumentando o contato entre os cotos fraturados. O presente trabalho teve como objetivos avaliar: a fixação e a estabilidade das fraturas do complexo zigomático tipo B proporcionadas pelo parafuso neck screw, aplicado na região da sutura frontozigomática e comparando com uma técnica de microplacas e microparafusos, na região da sutura frontozigomática e no bordo da região orbitária inferior; o conforto ou desconforto pós-operatórios à palpação relatados pelo paciente e o tempo cirúrgico médio empregado. Para avaliar a eficiência do parafuso neck screw, trinta pacientes com fratura tetrapoide de zigoma tiveram realizadas tomografias computadorizadas em cortes axiais e coronais para evidenciação das fraturas e planejamento cirúrgico; os pacientes foram submetidos ao procedimento cirúrgico, com osteossíntese através do parafuso neck screw e a técnica de microplaca e microparafuso na região frontozigomática, com o tempo cirúrgico registrado; após vinte e quatro horas e trinta dias foram submetidos a novo exame tomográfico. Os resultados coletados e mensurados foram submetidos a teste estatístico de Mann Whitney entre as técnicas usadas e teste T para o tempo. O ponto principal desta pesquisa está na proposição de uma técnica para a redução e fixação das fraturas-disjunção do complexo zigomático minimamente invasivo em relação às outras técnicas comparadas na literatura. A técnica com o parafuso neck screw neste trabalho garante estabilidade da fixação pelo acompanhamento tomográfico. A análise da estatística sobre as mensurações se demonstrou altamente significativa. O acompanhamento clínico dos pacientes nos apresentou ausência de assimetria facial, enoftalmo, ou diplopia; o tempo operatório é significativamente reduzido e com a observação da diminuição do desconforto referido pelos pacientes diante da palpação na região frontozigomática, pois o parafuso neck screw tem um alojamento intraósseo. / The tetraploid fractures from the zygomatic complex need accuracy in the correction and an efficient internal fixation for obtaining a good final result. Aiming at improving the advantages and minimizing the disadvantages of the rigid internal techniques, the screw "Neck Screw" was developed. The necessary stability for the correct fixation comes from a dynamic compression sistem increasing the contact between the stumps fractured. This assignment has the objectives to evaluate: the fixation and the stability of the dysjunction-fractures of the zygomatic complex provided by the screw "Neck Screw", applied in the region of the frontozygomatic suture, and to compare with a technique already devoted of micro-plaques and micro-screws applied in the region of the frontozygomatic suture and edge of inferior orbit; the after-operative confort or the disconfort reported by the pacient; the medium medical-surgical time used. To evaluate the efficiency of the screw "Neck Screw", thirty pacients with tetraploid fractures of zygoma had their computerized tomographies done on axial and coronale cuts for evidencing the fractures and for surgical planning. The pacients were subjected to the surgical procedure with osteosynthesis through the "Neck Screw" and the micro-plaque and micro-screw technique in the frontozygomatic region, having the surgical time properly noted. After 24 hours and 30 days, they were subjected to a new tomographic exam. The results gotten and measuremented were subjected to statistical tests of Mann Whitney, among the techniques used, and test T for the time. The importance of this research lies on the proposal of a technique for the reduction and fixation of the disjunction-fractures of the zygomatic complex minimally invasive in relation to the other techniques compared in the literature. The technique with the screw,"Neck Screw", guarantees stability of the fixation through the tomographic follow up. The analysis of the statistic about the measurements was revealed highly significant. The pacients' clinic follow up showed us absense of facial asymmetry, enophthalmos or diplopia. The operating time is significantly reduced and there is decrease of the disconfort reported by the pacients when palpating on the frontzygomatic region, thus the screw,"Neck screw", has an intra-osseous housing.