Currently, the demand for wood-based panels has been growing solidly in European countries. Medium density fibreboard (MDF) manifests the potentialities for outstanding physical and mechanical properties. However, MDF from different fiber sources is normally designed for internal applications due to the poor moisture resistant capability. This study was conducted on acetylated MDF (Medite® MDF Exterior) to evaluate how physical (i.e. density, moisture content, dimensional stability, thickness swelling) and mechanical (i.e. modulus of elasticity, internal bonding strength before and after accelerated aging, bending stiffness and bending strength) properties behave at different relative humidity (i.e. 35 %, 65 % and 85 % RH at constant temperature of 20 ℃) levels. Bending stiffness was measured non-destructively by means of resonance method. The material used for control samples was commercial MDF. The size, quantity, conditioning and test method were followed in accordance with respective standards. The results showed that physical and mechanical properties were less influenced by Medite® MDF Exterior compared to commercial MDF. Medite® MDF Exterior were superior to commercial MDF in moisture resistance. Medite® MDF Exterior had more stable mechanical properties than commercial MDF with the changes of relative humidity.

Uma das alternativas possíveis para substituir os materiais sintéticos na área de embalagem de alimentos é o desenvolvimento de filmes baseados em biopolímeros. Vários estudos têm demostrado o melhoramento nas propriedades de filmes baseados em biopolímeros, devido à utilização de nanopartículas como reforço. No entanto, as melhorias observadas são ainda limitadas e pode-se considerar que isso é devido a problemas de dispersão das nanopartículas em água, especialmente quando se utiliza a técnica tipo casting. Assim, os objetivos deste projeto foram: A) estudar a qualidade da dispersão de nanopartículas de montemorilhonita em água, e B) estudar o efeito dessas dispersões sobre algumas propriedades físicas e funcionais de filmes de gelatina produzidos com elas. As nanopartículas foram dispersas em água na concentração de 1 g MMT/100 g solução, com três dispositivos: homogeneizador mecânico (UT), moinho coloidal (MC) e processador ultrassônico (US). As dispersões foram analisadas para determinação de tamanho das partículas e potencial zeta, e por microscopia eletrônica de varredura e microscopia de força atômica. Os filmes foram produzidos pela técnica de \"casting\", com 5 g de gelatina/100 g de solução filmogênica e 30 g de glicerol/100g de gelatina. A concentração de nanopartículas foi 0, 1, 3, 5 e 7 g de MMT/100g de gelatina. Os filmes de controle e nanocompósitos produzidos com as dispersões de montemorilhonita foram caracterizados para determinação de espessura, umidade, solubilidade, permeabilidade ao vapor de água, propriedades mecânicas por testes de tração e perfuração, cor e opacidade, brilho, microestrutura por microscopia eletrônica de varredura e microscopia de força atômica, transição vítrea por calorimetria diferencial de varredura, difração de raios-X, espectroscopia de infravermelho com transformada de Fourier e ângulo de contato. O potencial zeta e tamanho médio da partícula foi -53, -40, -47 mV e 377, 289, 395 nm, para as dispersões processadas por UT, US e MC, respectivamente. No geral, os filmes reforçados com montemorilhonita, foram 44% menos brilhantes e foram ligeiramente mais hidrofílicos do que os filmes de controle. A tensão na ruptura aumentou de 22 MPa para filmes de controle até 40 MPa, quando a concentração da montemorilhonita foi de até 5 g de MMT/100g de gelatina. A permeabilidade ao vapor de água não variou nos filmes nanocompósitos. O método de dispersão utilizado teve uma forte influência sobre a qualidade das dispersões, afetando o tamanho da partícula e potencial zeta, com efeito evidente sobre as propriedades físicas dos nanocompósitos. A concentração crítica de montemorilhonita como reforço pareceu estar limitada a 5 g de MMT/100 g de gelatina. / One of the possible alternatives to replace synthetic materials in the area of food packaging is the development of films based on biopolymers. Several studies have demonstrated the improvement in properties of films based on biopolymers due to the use of nanoparticles as reinforcement. However, the observed improvements are still limited and it can be considered that this is due to dispersion problems of nanoparticles in water, particularly when using the casting technique. The aim of this project was to study the quality of the dispersion of nanoparticles (montmorillonite) in water, and to analyze the effect of these dispersions on some physical and functional properties of gelatin films. The nanoparticles were dispersed in water (1 g MMT/100 g solution), with three devices: mechanical homogenizer (UT), colloidal mill (MC) and ultrasonic processor (US). The dispersions were analyzed for determination of particle size and zeta potential, and by scanning electron and atomic force microscopies. Films were produced by casting, with 5 g of gelatin/100 g of film-forming solution and 30 g of glycerol/100 g of gelatin. The nanoparticles concentrations were 0, 1, 3, 5 and 7 g of MMT/100g of gelatin. The control and nanocomposite films were characterized for determination of thickness, moisture, water solubility, water vapor permeability, tensile and puncture mechanical properties, color and opacity, brightness, microstructure by scanning electron microscopy and atomic force microscopy, glass transition temperature by differential scanning calorimetry, X-ray diffraction, infrared spectroscopy with Fourier transform and contact angle. The zeta potential and average particle size was -53, -40, -47 mV and 377, 289, 395 nm; for UT, US and MC dispersions, respectively. In general, the films filled with montmorillonite were 44% less glossy and were slightly more hydrophilic than control film. The maximum tensile strength increased from 22 MPa for control film to 40 MPa when the concentration of montmorillonite was up to 5 g of MMT/100g of gelatin. The water vapor permeability did not change in the nanocomposite films. The dispersion method used had a strong influence on the quality of dispersions; it can affect the particle size and zeta potential, with evident effect on the physical properties of nanocomposites. The critical concentration of montmorillonite as reinforcement seemed to be limited to 5 g of MMT/100 g of gelatin maximum tensile strength increased from 22 MPa for control film to 40 MPa when the concentration of montmorillonite was up to 5 g of MMT/100g of gelatin. The water vapor permeability did not change in the nanocomposite films. The dispersion method used had a strong influence on the quality of dispersions; it can affect the particle size and zeta potential, with evident effect on the physical properties of nanocomposites. The critical concentration of montmorillonite as reinforcement seemed to be limited to 5 g of MMT/100 g of gelatin.

Orientador: Itamar Andrioli / Banca: Mara Cristina Pessoa da Cruz / Banca: Marcos Gervásio Pereira / Banca: Roberto Kazuhiko Zito / Banca: José Frederico Centurion / Resumo: O estabelecimento de culturas de cobertura para formação e manutenção dos resíduos culturais na superfície do solo, principalmente nas regiões de cerrado, tem encontrado alguns obstáculos, pois as condições climáticas nestas regiões favorecem a decomposição destes resíduos vegetais. A implantação do plantio direto nestas áreas tem crescido exponencialmente, porém tem sido utilizado como base em dados gerados em outras regiões do País, em outras condições climáticas. O presente estudo teve como objetivo principal estudar as plantas de cobertura mais utilizadas na região, avaliando o tempo de decomposição dos restos culturais, o acúmulo e liberação de nitrogênio por um período de até 320 dias, associando estes dados a produtividade das culturas. Também, fez-se o monitoramento da temperatura e umidade do solo, semanalmente, durante o período de janeiro a junho de 2000 nas profundidades de 0 a 5 e 5 a 10 cm. Após dois anos agrícolas de implantação do experimento, fez-se uma avaliação da influência destas coberturas em algumas propriedades físicas do solo da área. O delineamento experimental utilizado foi de blocos ao acaso, com parcelas subdivididas e quatro repetições. Nas parcelas principais, os tratamentos utilizados constaram de sete tipos de coberturas: milheto (Pennisetum americanum sin. tiphoydes), braquiária (Brachiaria brizantha), sorgo forrageiro (Sorghum bicolor L. Moench), guandu (Cajanus cajan (L.) Millsp), crotalária juncea (Crotalarea juncea) e aveia preta (Avena strigosa Schreb), pousio e área sob sistema de plantio convencional (testemunha). Nas subparcelas, após a dessecação das coberturas, plantou-se milho e soja, sendo estas culturas rotacionadas no segundo ano... (Resumo completo, clicar acesso eletrônico abaixo). / Abstract: The establishment of covering cultures for formation and maintenance of the cultural residues in the soil surface, mainly in the cerrado areas, has been finding some obstacles, because the climatic conditions in these areas favor the decomposition of these vegetable residues. The no tillage system implantation in these areas, has been increasing exponentially, however it has been used as base, the data generated in other areas of the country, in other climatic conditions. The present study had as main objective to study the covering plants more used in this area, evaluating the time of decomposition of cultural remains, the accumulation and liberation of nitrogen for a period up to 320 days, associating these data to the productivity of the cultures. Also, it was made the observation the soil of temperature and humidity, weekly, during the period of January to June 2000, in the depths of 0 - 5 and 5 - 10 cm. After two agricultural years, it was made an evaluation of the influence of the covering plants in some physical soil properties in the area. The experimental design was random blocks, with subdivided plots and four repetitions. The treatments used consisted in eight covering types: pearl millet (Pennisetum americanum sin. tiphoydes), braquiária (Brachiaria brizantha), sorgun (Sorghum bicolor L. Moench), pigeonpea (Cajanus cajan (L.) Millsp), sunn hemp (Crotalárea juncea) and black oat (Avena strigosa Schreb), fallow land, area in conventional system. In the subplots, after the covering plants dessecation, it was planted corn and soybean, and these cultures were rotated in the second year. Among the appraised coverings it was verified that millet and the sunn hemp were the cultures that presented the best score in dry mass production. Nitrogen accumulation and liberation in the appraised periods... (Complete abstract, click eletronic address below). / Doutor

Made available in DSpace on 2014-06-11T19:22:14Z (GMT). No. of bitstreams: 0 Previous issue date: 2008-02-01Bitstream added on 2014-06-13T19:07:29Z : No. of bitstreams: 1 gomes_mrm_me_botfca.pdf: 550230 bytes, checksum: 41e823b5b7173fed49f2418695c6f960 (MD5) / Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) / A cultura da batata requer especial atenção no preparo do solo, sendo necessário descompactar o solo antes do plantio a fim de que se proporcione uma estrutura adequada para permitir o crescimento das raízes e para que não ocorra o acúmulo de água. A estrutura condiciona o arranjo das partículas que, por sua vez, determina a distribuição dos poros. O monitoramento da qualidade do solo é necessário e pode ser realizado mediante avaliação dos seus atributos físicos, que são importantes para a sustentabilidade dos sistemas agrícolas. O emprego da técnica de análise de imagens permite o estudo de amostras de solo não deformadas e a identificação dos constituintes elementares e suas associações. Este trabalho teve por objetivo avaliar e quantificar, por meio da análise de imagens, as modificações na porosidade de um Latossolo Vermelho, no município de Paranapanema, no estado de São Paulo, cultivado com batata sob dois manejos de irrigação. Os tratamentos foram constituídos de: cultivo convencional de batata, em produção agrícola a três anos, irrigado via pivô central (CCP), cultivo convencional de batata, em produção agrícola a três anos, irrigado via canhão (CCC) e, como referência da estrutura do solo, foram utilizadas, também, as áreas de pastagem e mata nativa. Nas áreas de cultivo empregava-se a rotação de culturas com feijão/batata/milho/batata na área CCP e feijão/trigo/milho/batata na área CCC.O delineamento experimental foi o inteiramente casualizado, com três repetições. As amostras de solo foram coletadas na linha da batata, antecedendo a colheita, nos meses de setembro e outubro de 2006. Três amostras deformadas foram retiradas em cada área para análise química do solo. Para avaliação da resistência do solo à penetração, da porosidade e da densidade do solo, foram abertas três trincheiras de 1,00m x 0,50m em cada parcela... / Potato crop requires special attention to soil preparation, there being necessary soil decompactation before sowing, so that there could be a suitable structure to allow root growth and for the water accumulation not to occur. The structure limits the arrangement of the particles that, as well, determines pore distribution. The monitoring of soil quality is necessary and it can be done through the evaluation of its physical attributes, which are important for the sustainability of the crop systems. The use of the technique consisted of image analysis allows the study of undisturbed samples of soil and the identification of the elementary components and their associations. The research had as objective to evaluate and quantify, through image analysis, the modifications in porosity of a Red Latossol in the city of Paranapanema, state of São Paulo, cultivated with potato under two irrigation systems. The treatments consisted of the following: conventional cropping system of potato, in crop production for 3 years, irrigated by a center pivo (CCP); conventional cropping system of potato, in crop production for 3 years, irrigated by a gun sprinkler (CCC), natural pasture and native forest. In the crop areas, rotation crop system was used. The completely randomized design was used, with three replications. The samples of soil were collected in the potato row before harvest, in the months of September and October of 2006. Three disturbed samples were collected from each plot for soil chemical analysis. Three trenches with 1,00m x 0,50m were open in each plot to evaluate soil penetration resistance, porosity and density. For the interpretation of the porosity data, obtained from the thin sections, the program KS 300 Zeiss was used. All data obtained was submitted to the Tukey test at a probability level of 5%, using the SISVAR program...(Complete abstract, click electronic access below)

Este estudo avaliou propriedades físicas de materiais reembasadores para dentaduras após imersão em solução à base de perborato de sódio. Em todos os testes, os materiais, Kooliner e Elite Soft foram divididos nos grupos G1 (controle): imersão em saliva artificial a 37°C e G2 (experimental): imersões diárias em solução à base de perborato de sódio (Corega Tabs) por 5 minutos. Para os testes de sorção, solubilidade, alteração de cor e de dureza, foram obtidos 30 espécimes em forma de disco (15x3mm) de cada material, por meio da técnica direta, a partir da prensagem do material em matriz metálica vazada entre duas placas de vidro. A sorção e solubilidade foram avaliadas após 120 dias de imersão. A alteração de cor foi avaliada imediatamente após o acabamento dos corpos-de-prova e após 30 e 120 dias. A dureza dos materiais foi mensurada inicialmente, após 30 e 60 dias de imersão. O teste de Kruskal-Wallis (P<0,05) indicou que para o material Kooliner, o tipo de imersão (G1=1,43; G2=1,63) não interferiu nos valores de sorção. Quanto ao Elite soft, o perborato de sódio (G1=0,29; G2=0,51) promoveu aumento significativo nos valores de sorção. Comparando os materiais, o Kooliner apresentou médias de sorção significativamente mais altas que o Elite soft, para os dois grupos estudados. Para solubilidade, o teste Anova (P<0,05) a dois fatores de variação indicou diferença significante entre o fator grupo e entre o fator material. O Kooliner (0,168) bem como o grupo 1(0,137) apresentaram as maiores médias de solubilidade em relação ao Elite soft (0,089) e o grupo 2 , respectivamente. Com relação à cor (Anova, P<0,05), os dois materiais sofreram alteração no intervalo de 30 (Kooliner: G1=3,63, G2=2,87; Elite soft: G1=6,27, G2=6,01) e 120 (Kooliner: G1=4,21, G2=3,94; Elite soft: G1=8,54, G2=9,23) dias de imersão. O fator grupo não influenciou nesta propriedade dos materiais. Para a dureza do Kooliner, foi aplicada a análise de variância a dois fatores de variação (grupo: G1=6,63; G2=7,27 e tempo: T0=5,24; T30=7,28; T60=8,34), que indicou diferença somente para o fator tempo. Após a comparação das médias (Tukey=0,87), notou-se aumento significante (P<0,05) da dureza entre todos os tempos avaliados. Os corpos-de-prova de Elite soft do grupo experimental (49,18) apresentaram um aumento (P<0,05) na dureza quando comparado ao grupo controle (48,72). Para o fator tempo, o teste de Tukey (0,76), indicou diferença significante (P<0,05) entre as três médias (T0=46,45; T30=49,63; T60=50,74). O perborato de sódio não influenciou de forma significante nas propriedades avaliadas neste estudo. Dentre os materiais, o Kooliner foi o que apresentou maior estabilidade, porém é um material com características diferentes do Elite soft. O tempo é um fator importantíssimo na alteração das propriedades dos materiais, tendo interferido em todas as variáveis testadas. Estudos com o objetivo de aprimorar as características dos materiais para uma aplicação a longo prazo devem ser ainda realizados, visando a viabilidade de uso dos materiais reembasadores. / The aim of this study was to evaluate the physical properties of denture liners after immersion in a sodium perborate´s solution. In all the tests, both materials, Kooliner and Elite soft, were divided into the groups G1 (control): immersion in artificial saliva at 37°C and G2 (experimental): daily immersions in a sodium perborates´s solution (Corega Tabs) for five minutes. Thirty specimens (diameter of 15 mm and thickness of 3 mm) were obtained for the tests of water sorption, solubility, color change and hardness. Each material was processed according to the manufacturer´s directions in metallic moulds prepared for this purpose and compressed by two glass plates. Water sorption and solubility were evaluated after 120 of immersion. Color change was evaluated after specimens´ finishing, after thirty and sixty days of immersion. Kruskal Wallis (P<0,05) indicated that the immersion in sodium perborate (G1=1,43; G2=1,63) did not interfere in the water sorption values. Sodium perborate promoted significative raise in the Elite soft´s water sorption (G1=0,29; G2=0,51). Comparing the materials, Kooliner had the biggest means in both groups. In the solubility test, ANOVA (P<0,05), using two variation factors, indicated signifficant difference between groups and materials. Kooliner (0,168) and Group 1 (0,137) presented the biggest solubility means when compared with Elite soft (0,089) and Group 2 (0,110). Both materials changed between 30 (Kooliner: G1=3,63, G2=2,87; Elite soft: G1=6,27, G2=6,01) and 120 (Kooliner: G1=4,21, G2=3,94; Elite soft: G1=8,54, G2=9,23) days of immersion in the color test (Anova, P<0,05). To the Kooliner´s hardness, the ANOVA with two variation factors, indicated signifficant differece only for the time of immersion (grupo: G1=6,63; G2=7,27 e tempo: T0=5,24; T30=7,28; T60=8,34). Comparing the means (Tukey=0,87) a signifficant raise (P<0,05) of the hardness was observed between all the periods evaluated. Specimens of the experimental group of Elite soft (49,18) showed a raise (P<0,05) in the hardness when compared to the control group (48,72). The test of Tukey (0,76) indicated significant difference (P<0,05) in the time of immersion between the three means (T0=46,45; T30=49,63; T60=50,74). Sodium perborate did not influence significantly the properties evaluated in this study. Between the materials, Kooliner presented the best stability. But both materials have different compositions and behave in different ways clinically. The period of immersion is a very important factor in the physical properties of the materials; and all of them presented signifficant differences during this period. Studies with the intention of improving the materials´ properties for a long term use should be tried to make viable the use of denture liners.

Para confeccionar próteses faciais e reabilitar aqueles pacientes com perdas anatômicas, são empregados diversos materiais, destacando-se entre estes os flexíveis,devido á semelhança estética que apresentam com a pele humana. O padrão de qualidade dos materiais é liderado por produtos estrangeiros, tornando difícil a obtenção e, por tanto, a aplicação dos mesmos em território nacional. Devido à necessidade de se ter materiais nacionais com qualidade semelhante aos importados, este trabalho mensurou dois materiais, a resina resiliente CLASSIFLEX e o silicone médico ORTHO PAUER, ambos de produção nacional, seguindo as normas da ASTM (American Standard for testing materiais). Foram testadas dureza Shore A, resistência ao rasgamento, resistência a tração e alongamento de ruptura. Os valores obtidos foram analisados estatisticamente e comparados entre sim. Os valores de resistência a tração, resistência ao rasgamento e dureza Shore A, dos materiais testados foram baixos quando comparados com os valores encontrados em outras pesquisas .Os valores de Alongamento de ruptura se encontram dentro dos valores aceitáveis para matérias de uso em reabilitação buco maxilo facial. / To fabricate and create facial prosthesis for those patients with anatomical loss, maxillo facial protesiologist use differet materials. Flexible materials has being used mostly because of their aesthetic similarity with the skin. The standard for quality in prostethic materilas is led by foreign products, making it difficult to obtain and apply these materials in national territory. Due to the necessity of giving new and better materilas the CLASSIFLEX resilient resin and the ORTHO PAUER medical silicone, both of domestic production, were selected to test the fisical properties of: Shore A hardness, elongation, tensile strength and tear strenght. The specimens were made following the parameters indicated by the ASTM and each test was performed. The values obtained were analyzed statistically and compared. The results obtained may conclude that the physical properties of tensile srtrenght, tear strenght and Shore A hardness were low when compared with the results observed in other similar studies. The values obtained from the elongation test shows similarity of other values obtained by past studies.

Orientador: Elias Taylor Durgante Severo / Coorientador: Fred Williams Calogeno / Banca: José Tarcísio da Silva Oliveira / Banca: Claudio Angeli Sansígolo / Resumo: O estudo das propriedades físicas e químicas da madeira possibilita um melhor aproveitamento das suas potencialidades. O aproveitamento da madeira de seringueira Hevea brasiliensis após o declínio da produção de látex tem relevância mundial. Uma parte da madeira da seringueira vem de uma área significativa do fuste submetida ao processo de extração de látex. Esse trabalho tem como objetivo analisar as características químicas e físicas da madeira proveniente da região submetida ao processo de extração de látex e compará-la a madeira originária da região que não sofreu processo de extração de látex. Foram utilizadas árvores de seringueira com 53 anos de idade, submetidas ao processo de extração de látex durante 45 anos ininterruptos. Foram realizadas as seguintes análises químicas: determinação do teor de holocelulose, do teor de lignina e teor de extrativos totais. Foram determinadas as seguintes propriedades físicas: densidade, contração volumétrica, contrações lineares e coeficiente de anisotropia. Não foram encontradas diferenças estatísticas entre as propriedades químicas das duas regiões do fuste analisadas nem entre os diferentes tipos de lenho juvenil e adulto. Em relação às propriedades físicas não foram encontradas diferenças entre as regiões estudadas, mas em relação ao tipo de lenho juvenil e adulto ocorrem diferenças estatísticas entre os coeficientes de contrações lineares e contração volumétrica / Abstract: The study of physical and chemical properties of wood allows a better use of its potential. The use of wood from rubber tree Hevea brasiliensis after the decline of the production of latex has global significance. A portion of the rubber wood is a significant area of the stem submitted to the extraction process latex paper aims to analyze the chemical and physical characteristics of the wood from the region subjected to the process of extracting latex and compares it to wood originally from the region that has not undergone the process of extraction of latex. Rubber trees were used with 53 years old, subject to the latex extraction process for 45 consecutive years. We made the following chemical analysis: determination of holocellulose, lignin content and the content of total extractives. We determined the following properties: density, volumetric shrinkage, linear shrinkage and coefficient of anisotropy. There were no statistical differences between the chemical properties of both the stem region analyzed or between different types of juvenile and adult wood. Regarding the physical properties no differences were found between the regions studied, but in relation to the type of juvenile wood and adult wood statistical difference between the coefficients of linear shrinkage and shrinkage were found / Mestre

O sucesso do tratamento endodôntico a longo prazo depende do preparo químico mecânico e também da obturação dos sistemas de canais radiculares, que tem como objetivo prover o preenchimento de forma tridimensional com um material inerte. Um cimento endodôntico ideal deve ser biocompatível, ter tempo de presa adequado, estabilidade dimensional, união à dentina, baixa solubilidade, fácil manuseio e ser radiopaco. Para estabelecer um padrão nas pesquisas de materiais odontológicos algumas especificações são determinadas pela ISO e ANSI/ADA, onde são determinados os testes a serem realizados para cada tipo de material a ser avaliado. O objetivo desse estudo foi avaliar as propriedades físico-químicas de um novo cimento à base de silicato de cálcio tendo como fonte de comparação um cimento à base de resina epóxi. Para a avaliação do pH e liberação de cálcio, tubos de polietileno de 1mm de diâmetro interno e 10 mm de comprimento foram preenchidos com os cimentos e imersos em 10 ml de água deionizada. Após os períodos experimentais de 1, 24, 72 e 168 horas as amostras foram avaliadas quanto ao pH e a liberação de cálcio em um medidor de pH e espectrofotômetro colorimétrico respectivamente. Na análise da radiopacidade, solubilidade e tempo de presa foram confeccionados anéis com 10mm de diâmetro e 1mm de espessura do cimento; o valor da radiopacidade foi determinado de acordo com a densidade radiográfica (mm Al). Para a solubilidade os espécimes foram imersos em 50ml de água destilada por 7 dias, onde foi aferida a massa inicial (antes da imersão) e a final (após a imersão e desumidificação). A avaliação do tempo de presa foi realizada com agulhas Gilmore de 100g e 456,3g. O escoamento foi realizado com base na ISO 6876:2001. Os dados foram analisados por análise de variância e teste de Tukey (P<0,05). Os resultados encontrados nesse estudo, para valores de pH e Ca- foram significativamente maiores para o cimento Biosealer quando comparados ao AH Plus (P<0,05). Nos testes de escoamento, radiopacidade e tempo de presa o cimento biocerâmico demonstrou valores inferiores ao AH Plus (P<0,05). O Biosealer demonstrou uma alta solubilidade comparativamente ao AH Plus (P<0,05). É lícito concluir que, o cimento Biosealer demonstrou boas propriedades físico-químicas tais como; pH, liberação de cálcio, escoamento, radiopacidade e tempo de presa. Essa nova formulação de cimento endodôntico apresentou uma maior solubilidade do que a prevista na ISO 6876:2012. / The success of long-term endodontic treatments depend on mechanical and chemical preparation, as well as on the root canal fillings, the purpose of which being providing filling in a three-dimensional fashion using inert material. The ideal endodontic cement must be biocompatible, have an appropriate setting time, dimensional stability, dentin bond strength, low solubility, be easy to manipulate and radiopaque. In order to set up a standard for research involving dental materials, some specifications are set forth by ISO and ANSI/ADA, in which the tests to be carried out for each material to be assessed are provided for. The goal of this study is to assess the physical and chemical properties of a new calcium silicate-based cement, to be compared with an epoxy resin-based cement. In order to assess calcium release and pH levels, polyethylene tubes with internal diameter of 1 mm and 10 mm in length have been filled with the cements and immersed in 10 ml of deionized water. After trial periods of 1, 24, 72 and 168 hours, the samples were assessed with regard to their calcium release and pH levels, using a colorimetric spectrophotometer and a pH mete, respectively. In order to assess radiopacity, solubility and setting time, rings with 10 mm in diameter and 1 mm in thickness were manufactured using the cements; the radiopacity levels were calculated in accordance with their radiographic density (mm Al). In order to assess solubility, the items were immersed in 50 ml of distilled water for seven days, with the initial mass (before immersion) and final mass (after immersion and dehumidification) being measured. The setting time assessment was carried out using Gilmore needles weighing 100 g and 456.3 g. Yield test was carried out based on ISO 6876:2001. The data obtained were analyzed through analysis of variance and Tukey test (P<0.05). The results found in this study with regard to pH e Ca- levels were significantly higher for the Biosealer cement, when compared with AH Plus (P<0.05). In the yield, radiopacity and setting time tests, the results for the bioceramic cement were lower when compared with AH Plus (P<0.05). The results for the Biosealer indicated higher solubility levels, when compared with AH Plus (P<0.05). It is conceivable to conclude that the Biosealer has shown good physical-chemical properties, such as pH, calcium release, yield, radiopacity and setting time. This new endodontic cement formulation has shown a higher solubility when compared with the level set forth in ISO 6876:2012.

Objetivo: O objetivo desta pesquisa foi verificar o efeito da interposição de diferentes materiais restauradores indiretos na resistência à flexão em três pontos (RF), microdureza Knoop (MK) e grau de conversão FT-Raman (GC) de um cimento resinoso. Material e métodos: Os materiais restauradores indiretos selecionados para a confecção dos discos (2 mm de espessura e 11 mm de diâmetro) foram: a vitrocerâmica IPS Eris/Ivoclar-Vivadent (E); a cerâmica de infra-estrutura IPS Empress 2/Ivoclar-Vivadent recoberta pela vitrocerâmica IPS Eris/Ivoclar-Vivadent (EE); a resina composta microhíbrida Sinfony/3M ESPE (S); a resina composta microparticulada SR Adoro/Ivoclar-Vivadent (A). Inicialmente, foi determinada a transmitância relativa (TR) destes materiais restauradores através da análise de imagens digitais obtidas por uma câmera CCD e de um espectrômetro de luz visível. Em seguida, os corpos-de-prova (cps, 10 x 2 x 1 mm) do cimento resinoso Nexus 2/SDS Kerr, com (dual) e sem catalisador (fotoativado), foram polimerizados sob os discos de materiais restauradores indiretos utilizando o aparelho de fotoativação de luz halógena OptiluxTM 501/SDS Kerr (QTH) ou o diodo emissor de luz L.E.Demetron 1/SDS Kerr (LED). Os cps também foram fotoativados sem a interposição dos discos, deixando um espaço de zero (E0) e dois (E2) mm entre a ponta do fotoativador e a superfície do cimento. Para avaliação da MK e GC, cada cp foi dividido em quatro zonas: face irradiada - centro (IC); irradiada - borda (IB); não-irradiada - centro (NC); não-irradiada ? borda (NB). Além disso, foi avaliada a emissão espectral dos dois aparelhos de fotoativação com valores de irradiância relativa (%) e absoluta (mW/cm2). Resultados: A espectrometria foi o método mais sensível para detectar diferenças de TR entre os materiais restauradores e detectou que a resina S (3,5%a) transmitiu mais luz e a cerâmica E transmitiu menos luz (1,6%c). A análise de variância mostrou que o cimento dual apresentou médias superiores (P<0,001) de RF (201,3MPa), MK (42,3KHN) e GC (74,8%) em relação ao fotoativado. E, que o QTH (191,5MPaa) promoveu média de RF superior (P<0,001) em relação ao LED (164,4MPab). Em contrapartida, o LED aumentou os valores de MK do cimento em algumas interações e em outras não houve diferença estatística entre os aparelhos. O método FT-Raman apresentou uma menor sensibilidade do que o ensaio de MK para detectar diferenças entre os grupos experimentais. A interposição dos discos de cerâmica reduziu significativamente a RF e MK do cimento fotoativado em relação aos grupos E0 e E2, no entanto, quando foi adicionado o catalisador ao cimento estas reduções não ocorreram. A zona IC (39,6KHNa) dos cps apresentou maiores médias de MK e a zona NB (34,6KHNc) as menores, evidenciando a distribuição não-uniforme da luz sobre o cp. Foi verificado ainda uma correlação positiva entre as médias de GC e MK. Conclusão: A partir dos resultados desta pesquisa concluiu-se que houve uma tendência na qual os materiais restauradores que transmitiram mais luz ao cimento resinoso, principalmente o de pasta única (fotoativado), lhe proporcionou melhores condições para uma reação de polimerização mais eficiente e,consequentemente, propriedades físicas máximas. / Objective: The aim of this study was to verify the effect of interposing different indirect restorative materials on the three-point flexural strength (FS), Knoop microhardness (KHN) and FT-Raman degree of conversion (DC) of a resin cement. Methods: Disks (2-mm thick and 11- mm in diameter) were built using the indirect restorative materials IPS Eris (Ivoclar-Vivadent glass-ceramic, E), IPS Empress 2 (Ivoclar-Vivadent framework ceramic) veneered by IPS Eris (EE), Sinfony (3M ESPE, micro-hybrid composite resin, S) and SR Adoro (Ivoclar-Vivadent microfilled composite resin, A). Initially, their relative transmittance (RT) was determined analyzing digital images obtained by a CCD camera and with visible light spectrometry. Then, bar-shaped specimens (sps, 10 x 2 x 1 mm) of the Nexus 2 resin cement (SDS Kerr) were prepared either with (dual) or without catalyst (light-cured), and photoactivated throught the different restorative materials disks using a halogen light curing unit (QTH, OptiluxTM 501, SDS Kerr) or a light emitting diode (LED, L.E.Demetron 1, SDS Kerr). The sps were also light-cured without interposing the disks, keeping the curing unit light guide either in contact (S0) or 2 mm (S2) from the cement surface. For KHN and DC evaluation, each sp was divided in four regions: irradiated-center (IC), irradiated-edge (IE), non-irradiated-center (NC) and non-irradiated-edge (NE). Light curing unit spectral emissions were obtained with the relative (%) and absolute (mW/cm2) irradiance values. Results: The spetrometry was more capable to detect the RT differences between the restoration materials than the CCD camera and indicated that the S resin (3,5%a) transmitted more light and the E ceramic (1,6%c) transmitted less light. ANOVA revealed higher FS, KHN and DC values for the cement in dual-cure mode compared to light-cure (p<0.001). The QTH (192 MPaa) promoted higher FS than LED (164 MPab). On the other hand, the LED increased the KHN values in some interactions with the EE group and in other interactions there were not statistic differences between the curing units. The FT-Raman method was less sensitive than KHN to detect differences between the experimental groups. The ceramic materials reduced the light-cured cement?s FS and KHN compared to the S0 and S2 groups; however, when the catalyst was added to the cement these reductions did not occurred. The IC regions showed the highest KHN values and the NE, the lowest, indicating the non-uniform distribution of the light. A positive correlation was found between DC and KHN. Conclusion: It was possible to conclude that there was a tendency for the restorative materials which allowed more light transmission to provided better conditions for an efficient polymerization reaction and, consequently, desirable physical properties of the resin cement, more noticeable when used in light-cure mode.

The feed rate at which a defect free friction stir weld can be run (friction stir weldability) on an HSLA steel plate can vary widely between heats that meet the same specified physical properties. Consequently, every time a new heat of HSLA steel is obtained, exploratory welds must be run to determine the proper feed rate for that plate. Previous research suggests that the varying levels of alloying elements related to high temperature physical properties between the different heats causes the observed change in friction stir weldability. Because of this, it was hypothesized that the high temperature physical properties of HSLA steels are related to their friction stir weldability.High temperature physical propeties of HSLA steels are a function of the alloying content of the steel. To determine the relationship between high temperature physical properties and alloying content, eight different heats of HSLA steel with different chemical compositions were obtained. In particular, percent additions of molybdenum, vanadium, niobium, and titanium were varied between the heats in a factorial design. Gleeble compression tests were run on each heat to determine their high temperature properties. Based on these tests, experimental models wereconstructed to estimate the high temperature properties of HSLA steels based on composition and temperature. These models were used to determine the high temperature physical properties of HSLA heats with known friction stir weldability. The high temperature physical properties werecompared to the friction stir weldability of each heat. No correlation was found in this study between the high temperature properties examined and friction stir weldability in HSLA steels.