Made available in DSpace on 2018-08-24T22:53:10Z (GMT). No. of bitstreams: 1 tese_4357_Diss_Jorge_Lacerda.pdf: 16841024 bytes, checksum: 79a45e605faf9ecec242c9848ab8d238 (MD5) Previous issue date: 2010-08-19 / O escoamento da produção de óleo e gás por dutos terrestres (on-shore) e submarinos (off-shore) é um meio econômico, eficiente e seguro de transporte destes insumos entre a unidade de produção (upstream) e os terminais e refinarias (downstream). Após a montagem e o lançamento dos dutos, estes precisam ser preenchidos com fluidos para evitar o colapso da linha sob pressão e avaliar o grau de estanqueidade da mesma. Estes fluidos são normalmente água do mar ou água industrial, aditivada com produtos químicos para prevenir e inibir o processo de corrosão pelo oxigênio ou induzido por microrganismos, durante o período de retenção que pode durar vários meses (período de hibernação). Previamente à entrada em operação, o fluido contido na linha é geralmente liberado no ambiente marinho, razão pela qual o IBAMA demanda estudos de avaliação ecotoxicológica e modelagem da pluma de dispersão para se fazer uma estimativa dos riscos potenciais do fluido sobre a comunidade biológica. A persistência da ecotoxicidade do fluido aliada à extensão da pluma com indícios de ecotoxicidade crônica no corpo receptor são fatores críticos que podem inviabilizar o descarte in situ do efluente. Para reduzir a ecotoxicidade dos fluidos usados em testes hidrostáticos, o uso de menores concentrações de biocida foi tentado com a aplicação da radiação ultravioleta (UV) como técnica de pré-tratamento da água do mar. As composições foram testadas em diferentes condições de temperatura, uso ou não de UV e a presença ou não do agente seqüestrante de oxigênio. O fluido foi avaliado sob parâmetros microbiológicos e de toxicidade a organismos marinhos. Verificou-se que a redução de cerca de 50% na concentração do biocida THPS não prejudica o controle microbiológico quando a água é previamente tratada com radiação UV. Esta melhoria não somente representa uma redução de custos como também uma redução substancial do impacto ambiental quando da liberação dos fluidos no meio ambiente.

Orientador: Jose Augusto Chinellato / Tese (doutorado) - Universidade Estadual de Campinas, Instituto de Fisica "Gleb Wataghin" / Made available in DSpace on 2018-07-21T23:18:43Z (GMT). No. of bitstreams: 1 Biral_AntonioRenatoPerissinotto_D.pdf: 4367746 bytes, checksum: cfd9e75501ffbe76670f0f1ee90d1f1f (MD5) Previous issue date: 1996 / Resumo: O principal objetivo do experimento CLUE (abreviação de "Cerenkov Light Ultraviolet Experiment" ) é a detecção e estudo de chuveiros atmosféricos através da luz Cerenkov emitida pelas suas partículas carregadas. Diferentemente porém de como se costuma trabalhar em astronomia Cerenkov, o experimento CLUE, conforme idealizado, operaria na faixa espectral do ultravioleta médio (1800-2400 Þ ). Esperaria-se desse modo uma efetiva blindagem dos fótons ultravioletas de "fundo", proporcionada principalmente pela absorção ocasionada pelo ozônio atmosférico. Neste trabalho, através do método de Monte-Carlo, são analisadas diversas características do experimento em função do sinal de luz Cerenkov produzido por chuveiros atmosféricos verticais, iniciados seja por gamas, seja por prótons de alta energia (simulados na faixa de Ia 10 TeV). São assim expostas curvas de distribuição lateral dos fótons ultravioletas Cerenkov, obtidas em casos onde foram incluídas ou não algumas das eficiências experimentais do aparato. realizado também um cuidadoso estudo sobre o sinal de luz Cerenkov ultravioleta produzido exclusivamente pelos múons das cascatas atmosf6ricas simuladas. Um estudo referente a energia de limiar do experimento, onde são avaliadas diferentes condições de disparo a partir de uma disposição triangular hipotética de módulos do CLUE, é também apresentado. Por último. diversas considerações referentes aos processos de atenuação da luz ultravioleta na atmosfera, processos de formação de imagem, comparações (num aparato semelhante ao CLUE) entre o sinal de luz Cerenkov produzido tanto no ultravioleta como no visível, e análises comparativas entre os algoritmos de simulação utilizados são também discutidas / Abstract: Not informed. / Doutorado / Física / Doutor em Ciências

Orientador: Edison Bittencourt / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Quimica / Made available in DSpace on 2018-08-03T16:24:31Z (GMT). No. of bitstreams: 1 JovaAguila_Zaida_D.pdf: 3760046 bytes, checksum: cdbf3ed555db78f623deb0ea0f643a97 (MD5) Previous issue date: 2003 / Resumo: Apresenta-se no presente trabalho, o estudo do desenvolvimento de materiais poliméricos com propriedades ópticas e mecânicas controláveis a partir da utilização de modelos de predição de propriedades por contribuição de grupos. O referido estudo é realizado em sistemas poliméricos multicomponentes a partir de uma mistura base de monômeros de estireno e polietilenoglicoldimetacrilatos com a incorporação de monômeros de reticulação derivados do acrílico e monômeros metacrilatos derivados do etileno glicol. Partiu-se de um conjunto restrito de grupos de contribuição que aporta ao sistema compatibilidade entre a resistência ao impacto e resistência térmica, além de alto índice de refração e dureza. Tais propriedades são necessárias para que estes materiais sejam usados na fabricação de lentes oftálmicas. Primeiramente foi realizado o cálculo teórico das propriedades dos polímeros através de predições das propriedades. Posteriormente, realizou-se o cálculo destas propriedades experimentalmente, confeccionando assim, lentes oftálmicas através da polimerização fotoquímica dado a sua simplicidade, baixo custo de operação e otimizando dos tempos de cura, em relação aos processos de termocura, tradicionalmente utilizados pela industria. O material obtido foi caracterizado através da avaliação das propriedades ópticas e mecânicas, tais como medidas de índice de refração, temperatura de transição vítrea, resistência ao impacto e determinação de Dureza superficial Shore D. De forma geral, existe grande compatibilidade entre os resultados teórico e os obtidos experimentalmente, no caso do índice de refração o desvio entre os dados experimentais e os teóricos estão dentro dos erros experimentais da medida, e os resultados de temperatura de transição vítrea apresentaram-se adequados como medida da resistência ao calor. Em todos os casos, as lentes mostram resultados de dureza iguais ou superiores as lentes comerciais. Para a escolha do fotoiniciador mais indicado aos sistemas propostos considerou-se os resultados de um estudo cinético realizados para cada caso / Abstract: A study about the development of polymeric material with controllable optic and mechanical properties using models of prediction of polymers properties for groups contribution, is presented in this work. The study it was carried out in multicompound polymeric systems using a mixture of styrene monomer and polyethyleneglycoldimethacrylates with the addition of the monomer derived from acrylics and methacrylates obtained from the ethylene glycol. These monomers can be polymerized by cross linked or network polymers. A restricted set of groups of contribution were initially used in order to ensure compatibility between impact resistance, thermal resistance, high refractive index and hardness. Those properties are important in lenses production. First the theoretical calculation of polymers was carried through with the use of properties prediction and later the calculation of these properties experimentally by photo cure with ultraviolet radiation. The material was characterized through the evaluation of the optic and mechanical properties, glass transition temperature, refractive index, impact resistance and superficial hardness determination. A method for final properties assessment for this type of system is presented keeping in mind the reactivity ratios of monomers. A comparison between theoretical and experimental data is also presented. Exists great compatibility between the results theoretical and the gotten ones experimentally, in ali the cases equal or superior. This study considers the kinetic of co-polymerisation by free radical of multifunctional monomer and its relation with the final properties of the obtained material. More over it was done a kinetic study for the choice of the photo-initiator to begin for the considered systems / Doutorado / Ciencia e Tecnologia de Materiais / Doutor em Engenharia Química

Orientador: Cláudia Maria Navarro / Resumo: A queilite actínica (QA) é causada pela exposição crônica à radiação ultravioleta (UV), afetando principalmente o lábio de pessoas de pele clara, com 50 anos ou mais, sendo característica a perda da delimitação mucocutânea. A QA mesmo possuindo potencial para malignização ainda não é considerada uma desordem potencialmente maligna oral (DPMO), e isto se deve à falta de estudos com casuísticas consistentes. O objetivo desse estudo foi a caracterização da QA como DPMO mediante estudo do índice de transformação maligna e correlação clinicopatológica. Foram avaliados 182 prontuários de pacientes com QA atendidos no Serviço de Medicina Bucal (SMB) do Departamento de Diagnóstico e Cirurgia, da Faculdade de Odontologia de Araraquara - UNESP, no período de 1990 a 2018. Os dados foram transferidos para um banco de dados do programa Epi Info 7.2.2.6 software aberto. A comparação de dados paramétricos foi realizada por meio do teste Qui - Quadrado e o teste Exato de Fisher, teste T Student e o teste de Mann-Withney. Em testes não paramétricos foi utilizado o teste Anova One way com pós - teste de Tukey. Foi realizado também teste de Regressão categórica linear utilizando o software IBM SPSS Statistics 20, p <0,05 foi considerado significante. Analisando a amostra de 182 pacientes, sendo 71,97% sem carcinoma espinocelular (CEC) e 28,02% com CEC, pode-se traçar o perfil do paciente com QA. Pudemos concluir que as QA acometem principalmente o lábio inferior de homens brancos com mais de 50... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Actinic cheilitis (AC) is caused by chronic exposure to ultraviolet (UV) radiation, affecting mainly the lip of white people aged 50 or older, with loss of mucocutaneous delimitation. The AC even having potential for malignancy it is still not considered a potentially malignant oral disorder (PMOD), and this is due to the lack of studies with consistent sample. The objective of the present study was to characterize the AC as PMOD by studying the index of malignant transformation and clinicopathological correlation. A total of 182 clinical files of patients with AC was attending at the Oral Medicine Service (OMS) of the Department of Diagnosis and Surgery, University of Dentistry of Araraquara - UNESP, in the period 1990 to 2018. The data were transferred to a database of the Epi Info 7.2.2.6 open software program. The parametric data were compared using the Chi - Square test and the Fisher Exact test, Student 's T test and the Mann - Withney test. In non - parametric tests the Anova One way test was used with Tukey post - test. A linear categorical regression test using the IBM SPSS Statistics 20 software was also performed, p <0.05 was considered significant. Analyzing the sample of 182 patients, 71.97% without squamous cell carcinoma (SCC) and 28.02% with SCC, the profile of the patient with AC can be traced. We can conclude that the AC affects mainly the lower lip of white men over 50 years old who suffer chronic exposure to the sun without protection. Although UV radiatio... (Complete abstract click electronic access below) / Mestre

A modificação da superfície de materiais poliméricos demonstra-se extremamente útil em inúmeras áreas em que propriedades superficiais do material (molhabilidade, biocompatibilidade, adesividade, microestrutura, etc.) regem seus usos e aplicações, em setores como na tecnologia de membranas, aplicações medicinais e biotecnológicas e na tecnologia de materiais de recobrimentos. Muitas técnicas de tratamento superficiais já conhecidas apresentam bons resultados reportados na literatura, como descarga em corona, tratamentos com plasma, enxertia por meio químico e tratamentos com UV-VUV/ ozônio. As superfícies de dois polímeros sintéticos (poliestireno e polissulfona) e de um polímero natural (polihidroxibutirato), que inicialmente demonstravam superfícies hidrofóbicas foram modificadas utilizando-se radiação UV em presença de oxigênio ou vapores reativos (ácido acrílico ou trimetoxi propil silano), atribuindo-se características hidrofílicas e superhidrofílicas, sendo que em alguns tratamentos observou-se um processo de fotopolimerização com formação de um filme fino de poliácido acrílico sobre o polímero original. A caracterização das modificações produzidas nas superfícies poliméricas deu-se por técnicas de análise de superfícies (WCA, FTIR-ATR, XPS, NEXAFS, MEV). A utilização da radiação síncrotron monocromática como agente de excitação seletiva foi investigada irradiando-se superfícies de poliestireno sob condições de ultra alto vácuo e posterior exposição à atmosfera de O2. Os resultados demonstram funcionalização seletiva e eficiente de grupos COO e C=O (até 70%) pelo enxerto destes grupos no anel aromático, ocorrendo sobre as camadas mais superficiais do filme, comprovados por análise de XPS e NEXAFS. A funcionalização superficial induzida por radiação eletromagnética (UV ou SR) em presença de gases e ou vapores reativos mostrou excelentes resultados, com vantagens como a grande seletividade química aliada à isenção do emprego de reagentes tóxicos e à simplicidade experimental. / The modification of a polymer surface proves to be extremely useful in several areas in which the surface properties of a material (wettability, biocompatibility, adhesion, microstructure, etc.) controls their uses and applications. Areas such as membrane technology, biotechnology and medical applications and materials and coatings technology depends on surface properties. Many surface treatment techniques well known in the literature report good results, such as corona discharge, plasma treatments, grafting by chemical treatments and UV-VUV / ozone. Surfaces of two synthetic polymers (polystyrene and polysulphone) and one natural polymer (polyhidroxibutirato) were modified by ultraviolet-assisted modification in the presence of reactive Oxygen or vapors (acrylic acid or trimetoxi propil silane). Pristine hydrophobic surfaces were modified to hydrophilic or superhidrofilic. Some treatments led to a process of photo-polymerization with formation of a thin polyacrílic acid film formed on top of the original polymer. Characterization of the treated surfaces was carried out using sensitive surface analysis techniques (WCA, FTIR-ATR, XPS, NEXAFS, and SEM). The use of monochromatic synchrotron radiation for selective excitation was investigated by irradiation of polystyrene films under conditions of ultra high vacuum and subsequent Oxygen exposure to one atmosphere. The results showed efficient functionalization of COO and C = O groups (up to 70%) by grafting the functionalities mainly onto the aromatic rings. XPS and NEXAFS results showed that the grafting occurred on the most top monolayer of the polymers. Surface functionalization induced by electromagnetic radiation (UV or SR) in the presence of reactive gases or vapors showed excellent results. The main advantages are set-up simplicity, no need of toxic reagents and high chemical selectivity when synchrotron radiation is used as excitation source.

Tese (doutorado)—Universidade de Brasília, Instituto de Química, 2004. / Submitted by Tania Milca Carvalho Malheiros (tania@bce.unb.br) on 2009-08-05T12:17:37Z No. of bitstreams: 1 Tese_Tereza_Cristina_Monteiro_Pastore.pdf: 2003113 bytes, checksum: 0064369caee82816989a349b288663a6 (MD5) / Rejected by Tania Milca Carvalho Malheiros(tania@bce.unb.br), reason: on 2009-08-05T12:23:30Z (GMT) / Submitted by Tania Milca Carvalho Malheiros (tania@bce.unb.br) on 2009-08-05T12:25:14Z No. of bitstreams: 1 Tese_Tereza_Cristina_Monteiro_Pastore.pdf: 2003113 bytes, checksum: 0064369caee82816989a349b288663a6 (MD5) / Approved for entry into archive by Guimaraes Jacqueline(jacqueline.guimaraes@bce.unb.br) on 2009-08-06T15:36:20Z (GMT) No. of bitstreams: 1 Tese_Tereza_Cristina_Monteiro_Pastore.pdf: 2003113 bytes, checksum: 0064369caee82816989a349b288663a6 (MD5) / Made available in DSpace on 2009-08-06T15:36:20Z (GMT). No. of bitstreams: 1 Tese_Tereza_Cristina_Monteiro_Pastore.pdf: 2003113 bytes, checksum: 0064369caee82816989a349b288663a6 (MD5) Previous issue date: 2004 / Duas técnicas espectroscópicas de refletância foram usadas para monitorar as modificações causadas por 200 h de irradiação ultravioleta (UV) sobre a superfície das madeiras tropicais: angelim vermelho (Dinizia excelsa Ducke), jatobá (Hymenaea courbaril L. var. courbaril), garapeira (Apuleia molaris Spruce ex Benth) e marupá (Simarouba amara Aubl.). As variações de cor foram mensuradas por espectrocolorimetria (segundo o sistema CIE-L*a*b*) e as modificações estruturais dos componentes principais da madeira – celulose, holocelulose e lignina – foram detectadas por espectrometria de reflectância difusa no infravermelho com transformada de Fourier (DRIFT). Na região do visível, por meio do resultado da diferença entre os espectros Kubelka Munk (KM) da madeira (não-irradiadairradiada), pode-se observar em todas as espécies investigadas o aparecimento de banda forte próxima a 410 nm. Além desta banda, as madeiras de cor escura apresentaram absorções adicionais em outros comprimentos de onda. Pelos parâmetros CIE-L*a*b*, verificou-se que o jatobá deslocou a cor para o vermelho e as outras três espécies para o amarelo. O marupá foi a espécie que sofreu a maior variação de cor e o angelim vermelho foi o menos afetado. Os espectros de diferença KM (DRIFT) mostraram que as bandas associadas à lignina (1600 cm-1 e 1508 cm-1) diminuíram em intensidade, enquanto que a banda associada ao grupo carbonílico (1736 cm-1) aumentou de intensidade com o tratamento UV. Os resultados sugerem que os extrativos interferem no processo de fotodegradação, aumentando a tendência ao amarelecimento e contribuindo com o aumento de intensidade da banda do grupo carbonila. Na região do IR, verificou-se que a celulose também foi degradada pela radiação UV. A holocelulose apresentou tendência muito grande a formar compostos carbonílicos nãoconjugados e a celulose mostrou variação na intensidade da absorção. As quatro madeiras tropicais estudadas não puderam ser classificadas taxonomicamente via DRIFT, adotando-se os critérios de espécies de clima temperado. As duas técnicas de refletância correlacionaramsesignificativamente, indicando que a radiação UV formou produtos cromóforos resultantes da fotodecomposição da lignina, que continham o grupo carbonílico não-conjugado. A presença dos extrativos da madeira pode ser detectada pela espectroscopia FT-Raman, porém esta técnica não se mostrou adequada para monitorar a fotodecomposição. _________________________________________________________________________________________ ABSTRACT / Two reflectance spectroscopic techniques were used to monitor modifications caused by 200 h of ultraviolet (UV) irradiation on the surface of tropical hardwoods species: angelim vermelho (Dinizia excelsa Ducke), jatobá (Hymenaea courbaril L. var. courbaril), garapeira (Apuleia molaris Spruce ex Benth), and marupá (Simarouba amara Aubl.). Colour variations have been evaluated by spectrocolorimetry (according to the CIE-L*a*b* system). Chemical changes of the wood main components – cellulose, lignin and holocellulose – have been detected by Diffuse Reflectance Fourier Transform (DRIFT) spectroscopy in the infrared. The Kubelka Munk (KM) difference spectra (non-irradiated-irradiated) in the visible region, from the woods have shown that all investigated species developped a strong absorption band near 410 nm. Besides this band, darker woods showed addicional absorptions at other wavelengths. The CIE-L*a*b* parameters (∆L, ∆a, and ∆b) have shown that jatobá shifted its color to reddish while the other three species have a tendency to become yellowish. Marupá was the species that suffered major color changes and angelim vermelho was the least affected. In the IR region, the KM difference spectra have shown that bands associated to lignin (1600 and 1508 cm-1) decreased in intensity, while those associated to carbonyl group (1736 cm-1) have increased under UV exposure. The results suggest that the extractives interfere in the photodegradation process, increasing the tendency to yellowing and contributing to the increase of carbonyl band intensity. In the IR region, it was observed that cellulose was also degradeted by UV radiation. Holocellulose presented a very high tendency to produce nonconjugated carbonyl groups, while cellulose showed variation only in the absorption intensity. The four tropical wood species studied did not match the taxonomic classification by DRIFT, adopting the rules developted for temperated wood species. The two reflectance techniques were significantly correlated, indicating that the UV radiation has formed cromophores products resulting of lignin hotodecomposition and that these products contain nonconjugated carbonyl group. The presence of wood extractives was detected by FT-Raman spectroscopy, although this technique has not shown to be appropriated to monitor the photodegradation process.

A modificação da superfície de materiais poliméricos demonstra-se extremamente útil em inúmeras áreas em que propriedades superficiais do material (molhabilidade, biocompatibilidade, adesividade, microestrutura, etc.) regem seus usos e aplicações, em setores como na tecnologia de membranas, aplicações medicinais e biotecnológicas e na tecnologia de materiais de recobrimentos. Muitas técnicas de tratamento superficiais já conhecidas apresentam bons resultados reportados na literatura, como descarga em corona, tratamentos com plasma, enxertia por meio químico e tratamentos com UV-VUV/ ozônio. As superfícies de dois polímeros sintéticos (poliestireno e polissulfona) e de um polímero natural (polihidroxibutirato), que inicialmente demonstravam superfícies hidrofóbicas foram modificadas utilizando-se radiação UV em presença de oxigênio ou vapores reativos (ácido acrílico ou trimetoxi propil silano), atribuindo-se características hidrofílicas e superhidrofílicas, sendo que em alguns tratamentos observou-se um processo de fotopolimerização com formação de um filme fino de poliácido acrílico sobre o polímero original. A caracterização das modificações produzidas nas superfícies poliméricas deu-se por técnicas de análise de superfícies (WCA, FTIR-ATR, XPS, NEXAFS, MEV). A utilização da radiação síncrotron monocromática como agente de excitação seletiva foi investigada irradiando-se superfícies de poliestireno sob condições de ultra alto vácuo e posterior exposição à atmosfera de O2. Os resultados demonstram funcionalização seletiva e eficiente de grupos COO e C=O (até 70%) pelo enxerto destes grupos no anel aromático, ocorrendo sobre as camadas mais superficiais do filme, comprovados por análise de XPS e NEXAFS. A funcionalização superficial induzida por radiação eletromagnética (UV ou SR) em presença de gases e ou vapores reativos mostrou excelentes resultados, com vantagens como a grande seletividade química aliada à isenção do emprego de reagentes tóxicos e à simplicidade experimental. / The modification of a polymer surface proves to be extremely useful in several areas in which the surface properties of a material (wettability, biocompatibility, adhesion, microstructure, etc.) controls their uses and applications. Areas such as membrane technology, biotechnology and medical applications and materials and coatings technology depends on surface properties. Many surface treatment techniques well known in the literature report good results, such as corona discharge, plasma treatments, grafting by chemical treatments and UV-VUV / ozone. Surfaces of two synthetic polymers (polystyrene and polysulphone) and one natural polymer (polyhidroxibutirato) were modified by ultraviolet-assisted modification in the presence of reactive Oxygen or vapors (acrylic acid or trimetoxi propil silane). Pristine hydrophobic surfaces were modified to hydrophilic or superhidrofilic. Some treatments led to a process of photo-polymerization with formation of a thin polyacrílic acid film formed on top of the original polymer. Characterization of the treated surfaces was carried out using sensitive surface analysis techniques (WCA, FTIR-ATR, XPS, NEXAFS, and SEM). The use of monochromatic synchrotron radiation for selective excitation was investigated by irradiation of polystyrene films under conditions of ultra high vacuum and subsequent Oxygen exposure to one atmosphere. The results showed efficient functionalization of COO and C = O groups (up to 70%) by grafting the functionalities mainly onto the aromatic rings. XPS and NEXAFS results showed that the grafting occurred on the most top monolayer of the polymers. Surface functionalization induced by electromagnetic radiation (UV or SR) in the presence of reactive gases or vapors showed excellent results. The main advantages are set-up simplicity, no need of toxic reagents and high chemical selectivity when synchrotron radiation is used as excitation source.

O objetivo desse trabalho é avaliar o efeito fotoprotetor de três espécies de plantas da Antártica - Deschampsia antarctica Desv. , Colobanthus quitensis (Kunth) Bartl. E Polytrichum juniperinum Hedw. Investigou-se a ação do extrato metanólico de cada espécie contra os danos induzidos ao DNA, utilizando a linhagem celular de fibroblasto de pulmão de hamster chinês (células V79) e no molusco Cantareus aspersus utilizando o ensaio cometa em animais alimentados com esses vegetais. O perfil mutagênico e antimutagênco destes extratos também foi avaliado através de linhagens haplóides da levedura Saccharomyces cerevisiae. As concentrações empregadas desses extratos não foram citotóxicas nem mutagênicas em S.cerevisiae. Além disso, o tratamento com todos os extratos melhorou a sobrevivência e diminuiu a taxa de mutagênese induzida por UVC nesse modelo biológico. Os tratamentos empregados diminuíram significativamente os danos ao DNA induzidos pela UVC em células V79, como verificado pelo ensaio cometa. Esses extratos também reduziram a peroxidação lípidica induzida por UVC, mostrando uma clara propriedade antioxidante. Os resultados do ensaio cometa modificado, em células V79, empregando a Endonuclease V, demonstraram uma diminuição na formação de dímeros de ciclobutano piridina após a pré - incubação com estes extratos. O emprego das endonucleases FPG e ENDO III indica um efeito protetor destes extratos contra as lesões oxidativas geradas pelo UVC. Em linhagens de levedura deficientes em fotoliase, o tratamento com os extratos mostrou-se muito menos eficiente na proteção contra os danos citotóxicos da radiação UVC, sugerindo que esta via de reparação do DNA é estimulada por substâncias dos extratos. Em C.aspersus, o tratamento com os vegetais na alimentação dos moluscos, foi capaz de proteger contra os danos induzidos por UVC nas células da hemolinfa. Em conclusão, os extratos de D. antarctica, C. quitensis e P. juniperinum parecem possuir propriedades fotoprotetivas, o que pode ser atribuído a moléculas como flavonóides e carotenóides agindo como moléculas absorventes de UV, antioxidantes e estimulando processos de reparação do DNA. / This study aimed at deepening the knowledge on the photoprotective effects of three Antarctic plant species – Deschampsia antarctica Desv., Colobanthus quitensis (Kunth) Bartl., and Polytrichum juniperinum Hedw. We investigated the protective effect against UV-induced DNA damage in a permanent lung fibroblast cell line derived from Chinese hamsters (V79 cells), and in the snail Cantareus aspersus, using the comet assay. The protective, mutagenic, and antimutagenic profile of these extracts also was evaluated using haploid strains of Saccharomyces cerevisiae. At the concentration range employed, the extracts were not cytotoxic or mutagenic to S.cerevisiae. In addition, the treatment with these extracts enhanced survival, and decreased induced reverse, frameshift, and forward mutations in a dose-response manner in all UV-C doses employed a. In addition, they did not generate DNA strand breaks in V79 cells, and the treatment significantly decreased DNA damage induced by UVC. These extracts significantly decreased UVC-induced lipid peroxidation in V79 cells, showing a clear antioxidant property. Moreover, results of comet assay cells, employing Fpg, EndoIII, and Endo V endonuclease in these cells, demonstrated significant reduction of UVC-induced DNA damage, oxidative damage, and production of cyclobutane pyrimidine dimers after preincubation with these extracts. The treatment with all tested extracts were much less efficient against UVC-induced cytotoxicity in the yeast strain defective in photolyase as compared to the wild type strain, suggesting that this DNA repair pathway is stimulated by substances present in the extracts. In C. aspersus, the treatment was able to protect against UVC-induced damage. In conclusion, D. antarctica, C. quitensis, and P. juniperinum extracts present photoprotective properties, which can be attributed to molecules, such as flavonoids and carotenoids, which act as UV-sorbing molecules and as antioxidants, as well as stimulate DNA-repair processes.

Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro de Ciências Biológicas, Programa de Pós-Graduação em Biologia de Fungos, Algas e Plantas, Florianópolis, 2014. / Made available in DSpace on 2014-08-06T18:07:05Z (GMT). No. of bitstreams: 1 325332.pdf: 840863 bytes, checksum: 84ed65ce94d274796c70aa185e202b27 (MD5) Previous issue date: 2014 / As respostas de fotoaclimatação da macroalga parda Sargassum cymosum foram estudadas para determinar a sua organização ultraestrutural e citoquímica, assim os como seu desempenho e pigmentos fotossintéticos, as respostas bioquímicas, teor de proteínas, poliaminas (PAs), e os níveis de CHN. S cymosum foi cultivada in vitro em três salinidades (30, 35 e 40 ups) e quatro tratamentos de irradiação: controle, PAR+UVA, PAR+UVB e PAR+ UVA+UVB. As plantas controlem foram expostas a 70 µmol fótons m-2s -1, PAR+UVB a 0,35 Wm-2 e PAR+UVA a 0,70 W m-2 ,3 horas por dia durante 7 dias. Nenhum tipo de radiação e salinidade afeitou significativamente a taxa de crescimento. A quantidade de pigmentos em S. cymosum foi significativamente influenciado pela interação dos tratamentos com salinidade e radiação. Comparado ao controle, os tratamentos com radiação UV modificaram os padrões de cinética da curva de fotossíntese / irradiância. Após a exposição à radiação UV, S. cymosum apresentou um aumento da espessura da parede celular e a presença de compostos fenólicos. O número de mitocôndria aumentou, enquanto que o número de cloroplastos apresentou poucas alterações. Embora S. cymosum mostrou insensibilidade às variações da salinidade, pode concluir-se que as amostras tratadas sob quatro regimes de irradiação mostraram alterações estruturais, que foram mais evidentes. Comparado ao controle, os tratamentos com radiação UV mostraram mudanças negativas no teor de proteína, poliaminas e níveis de CHN e perfil metabólico. Pode concluir-se que S. cymosum é insensível às mudanças na salinidade e que amostras tratadas sob quatro regimes de irradiação apresentaram sinais de alteração, porém não foram graves.<br> / Abstract : The photoacclimation responses of the brown macroalga Sargassum cymosum were studied to determine its cytochemical and ultrastructural organization, as well as photosynthetic pigments and performance, biochemical responses, protein content, polyamines, and CHN levels of the brown macroalga. S. cymosum was cultivated in three salinities (30, 35 and 40 psu) under four irradiation treatments: PAR-only, PAR+UVA, PAR+UVB and PAR+UVA+UVB. Plants were exposed to PAR at 70 µmol photons m-2 s-1, PAR+UVB at 0.35 Wm-2 and PAR+UVA at 0.70 W m-2 for 3 h per day during 7 days in vitro. Growth rate was not significantly affected by any type of radiation or salinity. The amount of pigments in S. cymosum was significantly influenced by the interaction of salinity and radiation treatments. Compared to PAR-only, UVR treatments modified the kinetics patterns of the photosynthesis/irradiance curve. After exposure to UVR, S. cymosum increased cell wall thickness and the presence of phenolic compounds. The number of mitochondria increased, while the number of chloroplasts showed few changes. Although S. cymosum showed insensitivity to changes in salinity, it can be concluded that samples treated under four irradiation regimes showed structural changes, which were more evident. Compared to PAR-only, UVR treatments showed negative changes in protein content, polyamines, CHN levels and metabolic profile. It can be concluded that S. cymosum is insensitive to changes in salinity and that samples treated under four irradiation regimes showed signs of alteration, however they were not severe.

Tese (doutorado) - Universidade Federal de Santa Catarina, Centro de Ciências Biológicas, Programa de Pós-Graduação em Biologia Celular e do Desenvolvimento, Florianópolis, 2014. / Made available in DSpace on 2015-02-05T20:13:44Z (GMT). No. of bitstreams: 1 328646.pdf: 3208248 bytes, checksum: 67c80ae89c45fc7d821245f62a795cd4 (MD5) Previous issue date: 2014 / Gelidium floridanum W.R. Taylor é uma alga vermelha de grande importância comercial por ser fonte de ágar com melhor qualidade. Este estudo teve como objetivo ampliar os conhecimentos sobre a germinação de tetrásporos e os efeitos da radiação ultravioleta e do metal pesado cádmio (Cd) nos gametófitos jovens de G. floridanum. Para a análise dos mecanismos reguladores da polarização e germinação, os tetrásporos foram cultivados com brefeldina A (BFA), colchicina e citocalasina, sendo analisados por microscopia de luz (ML), fluorescência e eletrônica de trasmissão (MET). Com a utilização da BFA, a germinação dos esporos não ocorreu, a BFA levou a uma desmontagem das cisternas do Golgi com formação de regiões vesiculares no citoplasma, bloqueando a secreção do Golgi para a formação do tubo germinativo e deposição da parede celular. O tubo germinativo, nas amostras controle, é formado pela incorporação de vesículas derivadas do Golgi, a secreção das vesículas e organização dos corpos de Golgi são processos básicos e essenciais na adesão e formação do tubo. A BFA bloqueou a secreção de proteínas e de polissacarídeos amorfos da matriz, impedindo a germinação dos tetrásporos. Com os inibidores do citoesqueleto, citocalasina e colchicina, a germinação de tetrásporos de G. floridanum também foi afetada. Estes agentes causaram diminuição das taxas de germinação além da malformação dos tubos germinativos e no caso da citocalasina alteração no formato dos cloroplastos. Pode-se sugerir que tanto os microtúbulos quanto os filamentos de actina são reguladores dos processos de polarização e germinação de tetrásporos de G. floridanum. Para os efeitos da radiação ultravioleta, gametófitos jovens de G. floridanum foram cultivados em laboratório e expostos a radiação fotossinteticamente ativa (PAR) de 80µmol fótons m-2 s-1 e PAR+UVA+UVB durante 3 h por dia, por um período de 3 dias. As amostras foram processadas para ML e MET para análise ultraestrutural, bem como análise das taxas de crescimento, teor de pigmentos fotossintéticos, identificação dos carotenóides e avaliação do desempenho fotossintético. PAR + UVA + UVB promoveu aumento da espessura da parede celular, acúmulo de grãos de amido das florídeas no citoplasma e rompimento da organização interna do cloroplasto. As amostras expostas a PAR + UVA + UVB mostraram uma redução na taxa de crescimento de 97%, aumento dos carotenóides, diminuição dos pigmentos fotossintetizantes, em particular, a ficoeritrina e aviiialoficocianina, e consequente diminuição do desempenho fotossintético observados pela redução da taxa de tranporte de elétrons (ETR) e ETRmax. Para os efeitos do Cd, gametófitos jovens foram cultivados durante 7 dias com concentrações de 7,5 e 15 µM do Cd. Após o período experimental, foram realizadas análises de ML, confocal e eletrônica de varredura (MEV), taxas de crescimento, quantificação dos pigmentos fotossintetizantes, carotenóides e a fluorescência da clorofila a. As amostras tratadas apresentaram diminuição das taxas de crescimento, com despigmentação dos talos, redução dos pigmentos fotossintetizantes, resultando num descréscimo da taxa de transporte de elétrons e da autofluorescência dos cloroplastos. Além disso, o Cd aumentou a quantidade de grãos de amido das florídeas e afetou a distribuição do conteúdo proteico no citoplasma. O metal cádmio é altamente tóxico, causando fotoinibição crônica para a espécie. Pode-se concluir que tanto os corpos de Golgi como o citoesqueleto, filamentos de actina e microtúbulos, estão envolvidos nos processos de polarização e formação do tubo germinativo durante a germinaçãos de tetrásporos e, que gametófitos jovens de G. floridanum quando expostos tanto a radiação quanto ao Cd apresentam alterações no metabolismo e na estrutura celular que afetam seu desenvolvimento.<br> / Abstract : Gelidium floridanum W. R. Taylor is a red alga of great commercial importance as a source of high-quality agar. This study aimed to examine the germination of tetraspores and the effects of ultraviolet radiation (UVR) and heavy metal cadmium (Cd) on young gametophytes of G. floridanum. To analyze the regulatory mechanisms of polarization and germination, the tetraspores were cultured with brefeldin A (BFA), colchicine and cytochalasin, followed by analysis under light (LM), fluorescence and transmission electron microscopy (TEM). The use of BFA blocked the secretion of protein and amorphous matrix polysaccharides. It also blocked secretion from Golgi bodies, affecting germ-tube formation, as well as, cell wall deposition, and leading to the disassembly of the Golgi cisternae with regions of vesicular formation in the cytoplasm. These events effectively prevented tetraspore germination. Tetraspore germination was also affected by the use of cytochalasin and colchicine, which are inhibitors of cytoskeleton. These agents caused a decrease in germination rates and, in high concentrations, complete inhibition of germination. In addition, the germ tube becames malformed and, in the case of cytochalasin, the shape of chloroplasts was altered. It can be suggested that both microtubule and actin are regulators of polarization and germination in tetraspores of G. floridanum. Next, to assess the effects of UVR, young gametophytes were cultivated under laboratory conditions and exposed to photosynthetically active radiation (PAR) at 80 µmol photons m-2 s-1 and PAR+UVA +UVB for 3 h per day, during three days. The samples were processed for LM and MET to carry out analyses of ultrastructure, growth rates, and content of photosynthetic pigments, as well as, identify carotenoids and evaluate photosynthetic performance. PAR + UVA + UVB caused an increase in cell wall thickness, accumulation of floridean starch grains and changes in the internal organization of the chloroplast. Samples exposed to PAR + UVA + UVB showed a reduction in growth rate of 97%, increased of carotenoids, decreased photosynthetic pigments, in particular, phycoerythrin and allophycocyanin, and a resulting reduction in photosynthetic performance, as observed by the reduction of transport electron (ETR) and ETRmax. Finally, to test the effects of the Cd, young gametophytes of G floridanum were cultured for 7 days with concentrations of 7.5 and 15µM Cd. After the experimental period, LM, confocal and scanning electron microscopy (SEM) were employed toxanalyze growth rates and quantify the content of photosynthetic pigments, carotenoids and chlorophyll a. The treated samples showed a decrease in growth rates, with depigmentation of the thallus and reduction of photosynthetic pigments, resulting in a decrease in the rate of electron transport and autofluorescence of chloroplasts. Furthermore, exposure to Cd proved to be highly toxic, causing chronic photoinhibition, increasing the amount of starch grains, and altering the distribution of protein content in the cytoplasm. It can be concluded that both the Golgi bodies such as the cytoskeletal actin and microtubules are involved in the processes of polarization and germ tube formation during germination tetraspores and that youngs gametophytes of G. floridanum when exposed to both radiation as to the Cd present alterations in metabolism and cellular structure that affect its development.