Concrete is a material obtained by mixing raw materials such as cement, aggregates and water, and its per capita utilization is only behind water. Due to its large volume of use, it presents itself as a growing generator of waste and waste in civil construction. From the need to minimize these impacts on the environment with the possibility of reuse of concrete residues, transforming them into recycled concrete aggregates (ARGC). These materials are presented with high water absorption capacity and low specific mass. An alternative to improve this feature is the use of accelerated carbonation, which acts through the pores of the mortar adhered to the natural aggregate, producing carbonate elements that reduce the water absorption capacity and increase the specific mass. The objective of this research is to analyze the properties of the carbonated ARGC for concrete application. For this, a chamber was used in which the ARGC were submitted to concentrations of carbon dioxide. From the verification of the impact of carbonation on the samples, analyzed in mineralogical, thermal, microscopic and physical characterization tests, using as determinant impact value of the process, the capacity of absorption and specific mass, it was developed the reproduction of the carbonation parameters In scale for concrete production. They were produced: a reference concrete, with aggregates without carbonation, and their properties were compared with the samples of concrete with carbonated CGA, and analyzed its properties in fresh and hardened state. The ARGC presented, in its non-carbonated form, high absorption and low density, when compared to the natural aggregate, in contrast carbonation modified this picture with the formation of expansive products based on carbonates, which decreased the water absorption capacity and increased The density of carbonated ARGC when compared to untreated ARGC. Carbonation through the chamber proved to be an efficient method in this process, reflecting the behavior of the ARGC, which showed a decrease of 16.5% in the absorption capacity, a 1.53% increase in the specific mass and the formation of carbonates between the pores Of the ARGC. The concretes presented fluid abatement, mechanical strength of 25 MPa at 28 days and a mean carbonation depth of 12 mm. / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / O concreto é um material obtido pela mistura de matérias-primas como cimento, agregados e água, e sua utilização per capita fica atrás somente da água. Devido ao seu grande volume de utilização, apresenta-se como crescente gerador de resíduos e de desperdícios dentro da construção civil. A partir da necessidade de se minimizar estes impactos sobre o meio ambiente com a possibilidade de reutilização dos resíduos de concreto, transformando-os em agregados reciclados graúdos de concreto (ARGC). Estes materiais apresentam-se com alta capacidade de absorção de água e baixa massa específica. Uma alternativa para melhorar esta característica é a utilização da carbonatação acelerada, que age através dos poros da argamassa aderida ao agregado natural, produzindo elementos carbonáticos que reduzem a capacidade de absorção de água e aumentam a massa específica. O objetivo desta pesquisa é analisar as propriedades dos ARGC carbonatados para aplicação em concretos. Para isto foi utilizada uma câmara na qual os ARGC foram submetidos a concentrações de dióxido de carbono. A partir da verificação do impacto da carbonatação nas amostras, analisado em ensaios de caracterização mineralógica, térmicas, microscópicas e físicas, usando como valor de impacto determinante do processo, a capacidade de absorção e massa específica, desenvolveu-se a reprodução dos parâmetros da carbonatação em escala para produção de concretos. Foram produzidos: um concreto de referência, com agregados sem carbonatação, e suas propriedades foram comparadas com as amostras de concreto com ARGC carbonatado, e analisadas suas propriedades no estado fresco e endurecido. O ARGC apresentou, em sua forma não carbonatada, alta absorção e baixa densidade, quando comparados ao agregado natural, em contraponto a carbonatação modificou este quadro com a formação de produtos expansivos a base de carbonatos, que diminuíram a capacidade de absorção de água e aumentaram a densidade do ARGC carbonatado quando comparado ao ARGC sem tratamento. A carbonatação através da câmara mostrou-se um método eficiente neste processo, refletindo no comportamento do ARGC, que apresentou diminuição de 16,5% na capacidade de absorção, 1,53% de aumento na massa específica e a formação de carbonatos entre os poros do ARGC. Os concretos apresentaram abatimento fluido, resistência mecânica de 25 MPa aos 28 dias e uma profundidade de carbonatação média de 12 mm.

Made available in DSpace on 2015-05-14T12:09:34Z (GMT). No. of bitstreams: 1 arquivototal.pdf: 2919741 bytes, checksum: e2646db8015a4181da35e3ee2b1a0e33 (MD5) Previous issue date: 2014-02-21 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / This dissertation is included in area of reuse of solid wastes in paving, with objective to use recycled concrete aggregates and pellet in asphaltic surface course. The aim of the research was to analyze the technical feasibility of asphalt mixtures made with recycled concrete aggregates and pellet, in partial replacement of natural aggregates of the conventional asphalt mix, from tests of physical characterization of aggregates and mechanical performance of asphalt mixtures. The materials used were crushed stone 19 mm, crushed stone 12 mm, crusher dust, recycled concrete aggregate, pellet and 50/70 pen asphalt cement, these materials were obtained from companies in the state of Paraíba. For natural aggregates were performed grading, Los Angeles abrasion, absorption and density. For recycled concrete aggregates were made grading and specific density, and for pellet was carried out grading. One conventional asphaltic mixture were produced containing natural aggregates (crushed stone 19, crushed stone 12, crusher dust) and 50/70 pen asphalt cement, and five asphaltic mixtures were made with partial replacements of crusher dust for recycled concrete aggregates and pellet, in proportions: i) 25% of recycled concrete aggregates; ii) 2% of pellet; iii) 4% of pellet; iv) 23% of recycled concrete aggregates with 2% of pellet, and v) 21% of recycled concrete aggregates with 4% of pellet. The C grading envelope was used and chosen according to DNIT ES 031/2006. The mixtures were performed by the Marshall mix design. The mechanical tests performed were Marshall stability, tensile strength by diametric compression, resilient modulus and Lottman test. The hot asphalt mix containing 75% of natural aggregates, 23% of recycled concrete aggregates and 2% of pellet showed greatest number of parameters in accordance with the technical standards, as a result the best technical viability / Esta dissertação está inserida na problemática de reaproveitamento de resíduos sólidos na pavimentação, buscando o emprego de agregados de resíduos de concreto e pelete em revestimentos asfálticos. O objetivo da pesquisa foi analisar a viabilidade técnica de misturas asfálticas feitas com agregados de resíduos de concreto e pelete, em substituição parcial aos agregados naturais de mistura asfáltica convencional tipo CBUQ, a partir de ensaios de caracterização física dos agregados e de desempenho mecânico das misturas asfálticas. Os materiais empregados foram brita 19, brita 12, pó de pedra, agregados de resíduos de concreto, pelete e CAP 50/70, obtidos de empresas do Estado da Paraíba. Para os agregados naturais foram realizados a granulometria, abrasão Los Angeles, absorção e densidade. Para os agregados de resíduos de concreto foram realizados os ensaios de granulometria e massa específica, e para o pelete foi realizada a granulometria. Seis misturas asfálticas foram realizadas, sendo uma mistura de referência com os agregados naturais (brita 19, brita 12 e pó de pedra) e CAP 50/70; as demais misturas foram feitas com substituições parciais do pó de pedra pelos agregados de resíduos de concreto e pelete, nas proporções: i) 25% de agregados de resíduos de concreto; ii) 2% de pelete; iii) 4% de pelete; iv) 23% de agregados de resíduos de concreto com 2% de pelete, e v) 21% de agregados de resíduos de concreto com 4% de pelete. A faixa granulométrica utilizada foi a faixa C, que foi escolhida com base na norma DNIT 031/2006 ES. As dosagens realizadas foram por meio do método Marshall. Os ensaios mecânicos realizados foram estabilidade Marshall, resistência à tração por compressão diametral, módulo de resiliência e o ensaio Lottman. A mistura asfáltica tipo CBUQ com 75% de agregados naturais, 23% de agregados de resíduos de concreto e 2% de pelete se apresentou com maior número de parâmetros em conformidade com as normas técnicas, o que evidenciou sua maior viabilidade técnica em relação às demais misturas asfálticas modificadas

Many highway and hydraulic structures in North America have been reported to be affected by alkali aggregate reaction (ASR). It is anticipated that most of these structures will be demolished as they approach the end of their service lives. Recycling demolished concrete as aggregates in new concrete is an option that not only reduces the amount of construction demolition waste (CDW) disposed in landfills but also lessens the consumption of non-renewable resources such as natural aggregates. However, the use of recycled concrete aggregate (RCA) in new concrete requires detailed research to make sure that the durability of the recycled material is not compromised, especially if the RCA had been previously affected by ASR. In this research project, coarse recycled concrete aggregate (RCA) is reclaimed and processed from distinct members (i.e. foundation blocks, bridge deck and columns) of an ASR-affected overpass after nearly 50 years of service. RCA concrete mixtures incorporating 50 and 100% replacement are manufactured and stored in conditions enabling further ASR development. Mechanical (i.e. Stiffness Damage Test - SDT) and microscopic (Damage Rating Index - DRI) analyses are performed at a fixed “secondary” induced expansion of 0.12%. Results show that the overall performance of the ASR-affected recycled mixtures depends upon the “past” condition of the RCA particles. Moreover, the DRI was able to capture the “past” and “secondary” induced expansion and damage of affected RCA while the SDT only detected the “secondary” distress development. Lastly, an adapted version of the DRI was proposed to further evaluate the overall damage of recycled concrete along with properly displaying “past” and “secondary” induced distress.

Syftet med studien är att bedöma miljöpåverkan av tre alternativ av väggelement med olika ballastmaterial. Alternativ 1 har 100% krossad återvunnen betong som ballast. Alternativ 2 har ballast av krossat berg. I alternativ 3 består ballasten av naturgrus i fina fraktionerna och krossat berg i grova fraktionerna. Väggelementet i alternativ 3 är en av produkterna som tillverkas av företaget Hedareds Sand och Betong AB (Heda), ett prefabriceringsföretag i Hedared som ligger ca. 17 km utanför Borås. Återvunnen betong har den självklara fördelen att man undviker deponering av betongavfall. Med mindre kostnader och mindre belastning på miljön bidrar detta till hållbar utveckling inom betongindustri. Som metod har livscykelanalys använts. Livscykelanalys är en metod som används för att bedöma miljöpåverkan av en produkt eller en service under hela eller del av sin livstid. När livscykelanalys används för att jämföra olika produkter, vilket är fallet i den här studien, kan man begränsa att studera del av livstiden. I den här studien har man valt att studera de två första skeden av elementens livscykel, dvs anskaffningen av råvaror och transporter av råvaror till anläggningen där elementen tillverkas. Man har antagit att tillverkningsprocessen för alla tre alternativ är samma, varför man exkluderat detta från livscykelanalysen. De kategorier man har valt att undersöka är: klimatpåverkan, förtunning av ozonlagret, försurning, övergödning, skapande av marknära ozon och abiotiska resursutarmning. I studien har två scenario studerats. Det första är att restbetong transporteras från Hedas anläggning till krossanläggning 18 km bort för att sedan transportera ballasten tillbaka till Heda. I det scenariot har det visat sig att alternativ 1 har lägre påverkan än alternativ 3 i alla kategorier. Detta trots att alternativ 3 har färre transportsträckor än alternativ 1. Men det är alternativ 2 som har lägsta påverkan i alla kategorier. En stark orsak är att alternativ 2 har 80 kg mindre cement per kubikmeterelement än de två andra alternativen som har samma recept förutom ballasten. I det andra scenariot antas att krossningen sker vid Hedas anläggning med mobil krossanläggning. Scenariot uppvisar starkt förbättring av alternativ 1 ur miljösynpunkt. Alternativ 2 har i det nya scenariot högre påverkan än alternativ 1 i två av kategorierna (förtunning av ozonlagret +37 % och övergödning +2 %). I de övriga kategorierna är alternativ 2 fortfarande bättre än alternativ 1, även om skillnaderna är små. Alternativ 3 är sämsta för miljön eftersom det har största påverkan i samtliga studerade kategorierna.   I fem av kategorierna är det cementet som dominerar miljöpåverkan. I den sjätte kategorin, förtunning av ozonlagret, är det transporterna som bidrar mest till miljöpåverkan. Sammantaget är påverkan från ballasten förhållandevis mindre avgörande. Därför kan återvunnen betong som ballast till väggelement bli fördelaktig ur miljösynpunkt om den inte medför ökning av andra råvaror framförallt cement för att kompensera eventuella sämre hållfasthet. Samtidigt om logistiken kring återvunnen betong är optimerat så att det inte medför väsentligt fler och längre transportsträckor. / The aim of the study is to assess the environmental impact of three alternatives of walling with different aggregate. Option 1 has 100% crushed recycled concrete aggregate (RCA). Option 2 has aggregate of crushed rock. In option 3, the aggregate consists of natural gravel in the fine fractions and crushed rock in the rough fractions. The wall element in option 3 is one of the products manufactured by the company Hedareds Sand and Betong AB (Heda), a prefabrication company in the Hedared which is located about 17 km outside Borås. RCA has the obvious advantage of avoiding landfilling of concrete waste. With less costs and less burden on the environment contributes to sustainable development in the concrete industry.   Life cycle assessment has been used as a method. Life cycle assessment is a method used to assess the environmental impact of a product or service throughout or part of its lifetime. When life cycle analysis is used to compare different products, as is the case in this study, it can be limited to study part of the lifetime. This study has chosen to study the first two phases of the life cycle of the elements, i.e. the acquisition of raw materials and the transportation of raw materials to the plant where the elements are produced. It has been assumed that the manufacturing process for all three alternatives is the same, which is why it was excluded from the life cycle assessment. The categories chosen to investigate are: Global warming, ozone depletion, acidification, eutrophication, photochemical oxidation and abiotic depletion.   In the study, two scenarios have been studied. The first is that the concrete waste is transported from Hedas plant to crushing plant 18 km away and then transport the ballast back to Heda. In this scenario, option 1 has been shown to have a lower impact than option 3 in all categories. This is even though option 3 has fewer transport distances than option 1. But it's option 2 that has the lowest impact in all categories. A strong cause is that option 2 has 80 kg less cement per cubic meter element than the two other options which have the same recipe except for the aggregate. In the second scenario, it is assumed that the crushing takes place at Hedas plant with mobile crushing plant. The scenario shows a strong improvement in option 1 from an environmental point of view. In the new scenario, option 2 has a higher impact than option 1 in two of the categories (ozone depletion + 37% and eutrophication + 2%). In the other categories, option 2 is still better than option 1, although the differences are small. Option 3 is the worst for the environment as it has the greatest impact in all the studied categories.  In five of the categories, it is the cement that dominates the environmental impact. In the sixth category, the ozone depletion, it is the transport that contributes most to environmental impact. Overall, the influence of the ballast is relatively less decisive. Therefore, RCA to walling can be beneficial from an environmental point of view if it does not lead to an increase in other raw materials above all cement to compensate for any weaker strength. At the same time if the logistics of recycled concrete is optimized so that it does not involve significantly more and longer transport distances.

Submitted by Ricardo Cedraz Duque Moliterno (ricardo.moliterno@uefs.br) on 2017-02-02T00:09:36Z No. of bitstreams: 1 CONCRETO COM AGREGADO GRAU?DO RECICLADO DE CONCRETO_DOSAGEM E PRODUC?A?O.pdf: 3147518 bytes, checksum: 5fc02389f0e0978e3636005417e03f9e (MD5) / Made available in DSpace on 2017-02-02T00:09:36Z (GMT). No. of bitstreams: 1 CONCRETO COM AGREGADO GRAU?DO RECICLADO DE CONCRETO_DOSAGEM E PRODUC?A?O.pdf: 3147518 bytes, checksum: 5fc02389f0e0978e3636005417e03f9e (MD5) Previous issue date: 2016-08-04 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior - CAPES / A proper mix design and production must be done in order to increase the use of recycled concrete. The type of recycled aggregate (RA) used, the best replacement content, the best sequence and mixing time and the best way to evaluate the workability are some of the features that must be considered. Thus, this work was done to evaluate the mix design and production of concrete with concrete recycled coarse aggregate (RCA), using as a measure of workability the flow test in Graff?s table. Two levels of recycled coarse aggregate (20 and 40%), two levels of flow, for plastic and fluid mixtures, (350 and 400mm), and two mix design methods (IPT/EPUSP and ABCP) were evaluated on the concrete compressive strength, at 7 and 28 days of age. The results pointed out that the IPT/EPUSP mix design method was more suitable for recycled concrete. The flow test in Graff?s table, as a measure of workability, and the two stage mixture approach presented to be more suitable for the mix design and production of recycled concrete. Also, in this study, the concrete RCA content evaluated did not influence the compressive strength of concrete produced. So, it is completely feasible to use up to 40% replacement of NCA by concrete RCA. / Para ampliar o uso de concretos reciclados deve-se estabelecer a sua dosagem e produ??o considerando aspectos relacionados com o tipo de agregado reciclado (AR) utilizado, o melhor teor de AR, a melhor sequ?ncia e tempo de mistura e a melhor forma de avaliar a trabalhabilidade desses concretos. Assim, este trabalho foi desenvolvido com o objetivo de avaliar a dosagem e produ??o de concretos com ARs de concreto, usando como medida de trabalhabilidade o ensaio de espalhamento na mesa de Graff. Os teores de aplica??o do agregado gra?do reciclado(AGR) foram 20 e 40%. Foram avaliados dois n?veis de espalhamento (350 e 400mm) e dois m?todos de dosagem (IPT/EPUSP e ABCP). Os concretos foram avaliados ainda quanto a resist?ncia ? compress?o axial, aos 7 e 28 dias, e os resultados obtidos foram tratados estatisticamente atrav?s da an?lise de vari?ncia(ANOVA). Os resultados mostraram que o m?todo de dosagem do IPT/EPUSP apresentou-se mais adequado para a dosagem de concretos reciclados. O ensaio de espalhamento na mesa de Graff, como medida da trabalhabilidade, e o m?todo de mistura em duas etapas apresentaram-se adequados para a dosagem e produ??o de concretos reciclados. Nesse estudo, o teor de AGR avaliado n?o influenciou a resist?ncia ? compress?o dos concretos produzidos, sendo plenamente vi?vel o uso de at? 40% do agregado gra?do reciclado de concreto.

Submitted by Maicon Juliano Schmidt (maicons) on 2015-04-09T19:46:05Z No. of bitstreams: 1 Rafaela Gava Padovan.pdf: 7081051 bytes, checksum: 9e1501c4f4ebed520c7882be21164038 (MD5) / Made available in DSpace on 2015-04-09T19:46:05Z (GMT). No. of bitstreams: 1 Rafaela Gava Padovan.pdf: 7081051 bytes, checksum: 9e1501c4f4ebed520c7882be21164038 (MD5) Previous issue date: 2013-09-05 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / FINEP - Financiadora de Estudos e Projetos / Os agregados reciclados de concreto, de um modo geral, apresentam elevada absorção de água, em função da sua maior porosidade. Esta absorção resulta em alterações no teor de água das misturas, e têm implicação direta sobre as propriedades microestruturais dos materiais à base de cimento, não sendo diferente com o agregado reciclado. Contudo, tais alterações ainda são pouco conhecidas nestes materiais. Esta pesquisa possui o objetivo de determinar a influência do processo de pré-molhagem do agregado no comportamento de concretos desenvolvidos através da incorporação de agregado graúdo reciclado de concreto (AGRC) em substituição ao agregado graúdo natural (AGN). O teor de substituição do AGRC em relação ao AGN utilizado foi de 50% em relação ao volume do concreto. Previamente à utilização do AGRC, foi realizada uma pré-molhagem do material com percentuais na ordem de 40, 60, 80 e 100% da água relativa à absorção total do resíduo. Foram adotadas relações água/cimento iniciais de 0,45; 0,55 e 0,65. O abatimento foi fixado em 100 ± 20 mm, realizando-se uma compensação de água da mistura no teor necessário para atingir este abatimento. Num segundo grupo, a menor quantidade de água utilizada na produção dos concretos sem aditivo foi adotada para a produção dos mesmos concretos, com percentuais de pré-molhagem de 40, 60 e 80%, utilizando-se aditivo superplastificante ao invés de água para que fosse atingido o abatimento fixado. Verificou-se a influência da pré-molhagem do AGRC sobre as propriedades do concreto fresco, através da determinação da consistência ao longo do tempo; e do concreto endurecido, através da resistência à compressão e absorção de água por capilaridade dos concretos, e a alteração de porosidade de amostras de argamassa extraídas dos concretos frescos após diferentes tempos de contato com o agregado reciclado. Os resultados obtidos indicam que a trabalhabilidade e a resistência a compressão dos concretos com AGRC são pouco influenciadas pelo teor de pré-molhagem, enquanto que a permeabilidade a água e o teor de vazios existente na argamassa da mistura sofrem influencia significativa: nos concretos com AGRC sem aditivo, há pequenas variações de permeabilidade e porosidade, sendo que o teor de pré-molhagem de 80% resulta em concretos menos porosos. Entretanto, nos concretos com AGRC e aditivo superplastificante, o menor teor de pré-molhagem testado (40%) se revela a melhor opção, pois a água de mistura é absorvida pelos poros vazios do agregado reciclado, o que diminui a porosidade da argamassa, e consequentemente a capilaridade do concreto. / Recycled aggregates have high water absorption properties due to its high porosity. It changes the water content of the mixtures, and has implications on the microstructural properties of cement-based materials as those who uses recycled aggregate; however, little is known about these materials. This research has the objective of determining the influence of aggregate pre-wetting in new concrete made with recycled coarse aggregate concrete (RCAC) replacing natural aggregate. The substitution ratio of natural coarse aggregate (NCA) in relation to RCAC was 50% relative to the volume of the concrete. Prior to employing RCAC, it was pre-wetted with pre-wetting levels of 40, 60, 80 and 100% of the total water absorption of the residue. Water to cement ratios were initially determined to be 0.45, 0.55 and 0.65. The slump was set at 100 ± 20 mm, performing a compensation on the water content of the mixture required to get this slump. In a second group, the smallest amount of water used in the concrete’s production without additive was set with saturation levels of 40, 60 and 80%, using a superplasticizer instead of water to achieve the required slump. The recycled concrete produced was found to influence the pre-wetting RCAC on the properties of fresh concrete, through determination of consistency over time, compressive strength and durability and water absorption by capillarity. Mortar samples were obtained from the extraction of recycled concrete. These samples were analyzed for porosity. The results indicate that the workability and the compressive strength of concretes with AGRC are little influenced by the amount of pre-wetting, while the water permeability and the void content of the mixture existing in the mortar suffer significant influence: in the concrete with no additive AGRC there are small variations in porosity and permeability, and in the amount of pre-wetting results in 80% less porous concrete. However, in concrete with AGRC and superplasticizer, the lowest level of pre-wetting tested (40%) proves the best option, because the mixing water is absorbed by the empty pores of recycled aggregate, which reduces the porosity of the mortar, and consequently the capillarity of hard concrete.

Submitted by JOSIANE SANTOS DE OLIVEIRA (josianeso) on 2018-04-18T16:00:57Z No. of bitstreams: 1 Tatiane Isabel Hentges_.pdf: 11562616 bytes, checksum: 76c15f0e9ee280811a91bbb6d05b0494 (MD5) / Made available in DSpace on 2018-04-18T16:00:57Z (GMT). No. of bitstreams: 1 Tatiane Isabel Hentges_.pdf: 11562616 bytes, checksum: 76c15f0e9ee280811a91bbb6d05b0494 (MD5) Previous issue date: 2018-03-15 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / PROSUP - Programa de Suporte à Pós-Gradução de Instituições de Ensino Particulares / Pesquisas vêm desenvolvendo formas de mitigar os efeitos da absorção de água de agregados graúdos reciclados quando inseridos em novas misturas de concreto, de forma que as características mecânicas e de durabilidade desses agregados e dos concretos que o empregam sejam melhoradas. Destacam-se, nesse sentido, a carbonatação e a impregnação em solução de pozolanas. Este trabalho teve como objetivo avaliar o tratamento do agregado graúdo reciclado de concreto através da carbonatação e da impregnação de microfinos de cerâmica vermelha (MCV), para emprego em misturas de concreto. Para avaliação do tratamento do AGRC foi executada absorção de água dos agregados, abatimento ao longo do tempo e resistividade elétrica dos concretos no estado fresco, além de resistência à compressão e absorção de água por capilaridade no estado endurecido. Foi, ainda, realizada análise por microscópio eletrônico de varredura dos agregados e da zona de transição com novas argamassas. Por último, foi realizada análise da redução nas gerações de gás carbônico devido ao uso de AGRCs e à carbonatação. Como resultados, tem-se a redução da absorção de água dos agregados, verificada também pela resistividade elétrica no estado fresco. O abatimento ao longo do tempo não apresentou diferenças significativas com a alteração no tipo de agregado utilizado. As propriedades mecânicas dos concretos contendo AGRC tratado com MCV são comparáveis às de concretos contendo apenas agregados naturais e os concretos contendo AGRC carbonatados não reduzem significativamente as resistências. A absorção de água por capilaridade foi reduzida ao empregar concretos com agregados carbonatados e aumentou para os concretos com AGRC tratado com MCV, de forma similar a outros trabalhos que empregaram pozolanas. Analisando-se as emissões de CO2 isoladamente por parte dos agregados reciclados, verifica-se a redução de 40% com o emprego desses e de 49% com a carbonatação dos mesmos. Por outro lado, quando verificada a ecoeficiência das emissões por MPa considerando o consumo de cimento, essa diferença é reduzida de forma que as emissões relativas se apresentam com valores similares. / Research has been developing ways to mitigate water absorption effects from recycled concrete aggregates use in new concrete mixtures, so that the mechanical and durability characteristics of these aggregates and the concretes that use it are improved. In this sense, the carbonation and impregnation in solution of pozzolans are highlighted. This study aimed to evaluate the treatment of coarse recycled concrete aggregate (CRCA) by carbonation and impregnation of red ceramic microfines (RCM) powder for use in concrete mixtures. To evaluate the treatment of the CRCA, water absorption of the aggregates, reduction over time and electrical resistivity of the concretes in the fresh state were performed, as well as compressive strength and water absorption by capillarity in the hardened state. It was also carried out by scanning electron microscope of the aggregates and the transition zone with new mortars. It was also performed by analysis of scanning electron microscope aggregates and the transition zone with new mortar. Finally, was conducted analysis of the reduction in the generation of carbon dioxide from the use of CRCAs and carbonation. As results, there is a reduction in the water absorption of the aggregates, also verified by the electrical resistivity in the fresh state. The slump loss did not present significant differences by changes on aggregate type used. The mechanical properties of the concrete containing CRCA treated by RCM are comparable to those of concrete containing only natural aggregates, and the concrete containing carbonated CRCAs do not significantly reduce the strengths. The capillary water absorption was reduced when using concrete with carbonate aggregates and increased for concrete with CRCA treated with RCW, in a similar way to other works that used pozolanas. Analyzing CO2 emissions alone from the recycled aggregates, the reduction of 40% is achieved using these and 49% by the carbonation of them. On the other hand, when the eco-efficiency of the emissions per MPa is verified considering the cement consumption, this difference is reduced so that the relative emissions present themselves with similar values.

Submitted by Fabricia Fialho Reginato (fabriciar) on 2015-06-27T00:47:04Z No. of bitstreams: 1 MarianaBattisti.pdf: 4940838 bytes, checksum: da6b432c65c732aae6b2315e828e6836 (MD5) / Made available in DSpace on 2015-06-27T00:47:04Z (GMT). No. of bitstreams: 1 MarianaBattisti.pdf: 4940838 bytes, checksum: da6b432c65c732aae6b2315e828e6836 (MD5) Previous issue date: 2013-03-27 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / FAPERGS - Fundação de Amparo à Pesquisa do Estado do Rio Grande do Sul / FINEP - Financiadora de Estudos e Projetos / O concreto é o material de construção mais empregado no mundo, consumindo grandes volumes de recursos naturais não renováveis, além da obtenção de matérias primas para sua produção causar grandes impactos ambientais. Deficiências do concreto relativas às propriedades de durabilidade podem diminuir a vida útil das estruturas, gerando resíduos precocemente, ou então necessitando de intervenções não previstas. A incorporação de agregados reciclados de concreto na produção de concreto vem sendo proposto como substituição parcial do agregado natural. No entanto, seu emprego pode aumentar a porosidade do concreto e diminuir sua durabilidade. A utilização de cinza de casca de arroz pode trazer melhorias nas propriedades dos concretos, principalmente quando se refere à penetração de íons cloreto e às propriedades mecânicas. O objetivo deste trabalho é avaliar a influência da cinza de casca de arroz na penetração de íons cloreto em concretos com agregado reciclado de concreto. Foram produzidos concretos com 0; 25 e 50% de agregado reciclado em substituição ao agregado natural; 0; 10 e 20% de substituição de cimento por cinza de casca de arroz; e relações água/aglomerante iguais a 0,42, 0,53 e 0,64. A resistência à compressão foi analisada aos 7, 28, 63 e 91 dias. Os ensaios de durabilidade englobaram os ensaios de absorção de água por capilaridade e dois métodos acelerados de penetração de íons cloretos: ASTM C1202 e NT Build 492, comumente empregados em pesquisas científicas. Os resultados mostram, em média, que a cinza de casca de arroz trouxe benefícios ao concreto com agregado reciclado de concreto em todas as propriedades estudadas. O comportamento observado pode ser atribuído a uma possível interação entre o agregado reciclado e o emprego da cinza de casca de arroz, em decorrência de uma reação pozolânica da cinza com produtos de hidratação da pasta do agregado reciclado e a um efeito microfíler da mesma nos poros deste agregado. O melhor desempenho foi obtido com concreto produzido com 50% de agregado reciclado de concreto e 20% de cinza de casca de arroz, com um aumento médio da resistência à penetração de íons cloreto de 91% pela ASTM C1202 e 64% pelo NT Build 492, em relação aos concretos de mesmo teor de agregado reciclado e sem cinza de casca de arroz. / The durability of building materials is emphasized when it searches to maintain the useful life of the construction design or extend it. Corrosion reinforcement in concrete is among one major problem that affects the constructions throughout the world. Chloride ion is one of the agents that can induce the corrosion reinforcement in concrete. For this reason, research about the durability of construction materials in severe environments gained space in the scientific community. The use of recycled concrete aggregate as replacement of natural aggregate has been studied to solve the question about non-renewable raw materials. But, these recycled waste as aggregate can increase the concrete porosity and reduce its durability. The rice husk ash has been employed as supplementary material in Portland cement concrete to get a more sustainable concrete and improve its durability, mainly related to chloride ingress. The aim of this research was to study the influence of rice husk ash on the chloride penetration in concrete made with recycled concrete aggregate. The natural coarse aggregates were replaced by recycled concrete aggregates in amounts of 0; 25 and 50%. The rice husk ash was employed as replacement of Portland cement in 0; 10 and 20%. Three water/binder ratios were used in concrete production: 0.42, 0.53 and 0.64. The compressive strength tests were conducted at 7, 28, 63 and 91 days age. The concrete resistance to chloride ingress was tested by the ASTM C1202 test method and by the NT Build 492 test method. The results of all studied properties showed that the use of rice husk ash can improve the concrete resistance against chloride ingress in concrete made with recycled concrete aggregate. This behavior can be attributed to the reduction of the porosity of recycled concrete aggregate due to interaction of rice husk ash with the calcium hydroxide of this aggregate as well as due to micro filler effect. The best performance was obtained in concrete with 50% of recycled concrete aggregate and 20% of rice husk ash. The resistance against chloride ingress in relation to the same concrete without rice husk ash was increased 91% in average when tested by ASTM C1202, and 64% when tested by NT Build 492.

Submitted by Silvana Teresinha Dornelles Studzinski (sstudzinski) on 2016-02-05T12:26:48Z No. of bitstreams: 1 JOÃO RAFAEL SEVERO NOGUEIRA_ .pdf: 2326836 bytes, checksum: feff4e1efd0b8efb7dec079f29659d53 (MD5) / Made available in DSpace on 2016-02-05T12:26:48Z (GMT). No. of bitstreams: 1 JOÃO RAFAEL SEVERO NOGUEIRA_ .pdf: 2326836 bytes, checksum: feff4e1efd0b8efb7dec079f29659d53 (MD5) Previous issue date: 2015-06-19 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / FAPERGS - Fundação de Amparo à Pesquisa do Estado do Rio Grande do Sul / A reciclagem dos resíduos de construção e demolição (RCD) classe A é incentivada e a viabilidade do seu emprego como agregado alternativo em concretos e argamassas já vem sendo estudada por diversos autores. A fração de concreto do RCD é indicada como a mais viável para o emprego como agregado na produção de concretos, pois apresentam propriedades mecânicas mais elevadas que outras frações do RCD classe A, e características próximas à matriz na qual são inseridos. Porém, apresentam-se mais porosos e possuem propriedades mecânicas inferiores aos agregados convencionais. A porosidade do agregado de concreto reciclado influencia na sua absorção de água, o que geralmente altera a demanda de água da nova mistura, podendo desta forma, trazer prejuízos ao novo concreto, principalmente no estado fresco e na durabilidade. Muitas pesquisas têm incorporado o Agregado Graúdo Reciclado de Concreto (AGRC) ao concreto no início da mistura, o que faz com que o mesmo tenha maior tempo para absorver a água de amassamento durante o preparo e manipulação, trazendo prejuízos a consistência do concreto. Um dos métodos para mitigar este efeito é o seu emprego saturado ou parcialmente saturado com água, o que introduz uma etapa prévia de preparação do AGRC na produção do concreto. A presente pesquisa tem por objetivo comparar dois diferentes métodos de incorporação do AGRC na mistura de concreto, com o intuito de mitigar os efeitos da sua maior absorção de água. Alternativamente ao método tradicional, foi avaliada neste estudo a incorporação do AGRC seco ao final da mistura. Para avaliar estes concretos, foram realizados os ensaios de abatimento de tronco de cone (slump), resistividade elétrica no estado fresco, resistência à compressão, absorção de água por capilaridade e resistividade elétrica no estado endurecido. A consistência do concreto sofre menos influência do AGRC quando ele é incorporado no final da mistura. No entanto, a resistividade no estado fresco não aponta diferenças significativas entre os dois métodos. Já no estado endurecido, percebe-se que, por absorver água de amassamento, e com isso reduzir a relação a/c efetiva, a incorporação do AGRC na primeira etapa da mistura traz resultados de resistência à compressão, em alguns traços, superiores ao concreto de referência. / The recycled concrete aggregate (RCA) have been widely studied and the results have been showed that its employ in partial replacement can be feasible. This recycled aggregate is more viable to use in concrete than those recycled from mixed construction and demolition waste. However, the RCA has a higher porosity than natural aggregate and sometimes their mechanical resistance is less than the new concrete resistance. The higher porosity leads the RCA to absorb the mixing water of new concrete and to reduce the concrete slump. To avoid these problems the consequences are an increase on the water demand and on the cement consumption, in order to maintain the water/binder ratio. There are some ways to mitigate these problems like as to add water to the mixture, use the RCA pre saturated, cover the RCA surface with resins, use carbonated RCA. Some researchers proposed different concrete mix methods to produce concrete with RCA with some good results. The aim of this research is to evaluate two methods of mixing concrete with recycled concrete aggregate and their influence in fresh and hardened concrete properties. Usually the RCA is added to the mixture in the same time as the natural aggregate. This practice put the RCA in contact with the fresh mixing for a large period time and lead to absorb a higher amount of water. In consequence, there is a great loss in concrete slump, but this can bring an increment in the concrete resistance. In alternative, this work proposed the adding of RCA in the end of the mixture, evaluating the influence of the two methods the properties of fresh concrete and hardened concrete. The loss in concrete slump is lower when the RCA is introduced at the end of the mixture. However there is no significant difference in the electrical resistivity of fresh concrete. For hardened concrete, the best results were from concretes where the RCA was added at the end of the mixture.

Submitted by Silvana Teresinha Dornelles Studzinski (sstudzinski) on 2016-02-29T15:46:40Z No. of bitstreams: 1 Jeferson Alcantara Alves Sentena_.pdf: 9477344 bytes, checksum: b6b4ffd8def394ec6203badce4e2dd85 (MD5) / Made available in DSpace on 2016-02-29T15:46:40Z (GMT). No. of bitstreams: 1 Jeferson Alcantara Alves Sentena_.pdf: 9477344 bytes, checksum: b6b4ffd8def394ec6203badce4e2dd85 (MD5) Previous issue date: 2015-09-28 / CNPQ – Conselho Nacional de Desenvolvimento Científico e Tecnológico / FINEP - Financiadora de Estudos e Projetos / FAPERGS – Fundação de Amparo à Pesquisa do Estado do Rio Grande do Sul / A construção civil tem apresentado um grande crescimento nesta última década. Junto à construção, cresce a demanda por matéria prima e há um aumento da geração de resíduos nos canteiros de obras e em indústrias ligadas ao setor. Segundo o Ministério de Minas e Energias (MME) no ano de 2008, a estimativa de produção de areia chegou a 279 milhões de toneladas e estima-se que em 2030 possa chegar a 1,276 bilhões de toneladas. O uso de resíduos de construção e demolição para a produção de argamassas de revestimento pode trazer benefícios econômicos e ambientais, no entanto, sua utilização somente é possível se o revestimento for durável, suportando as ações ambientais. O presente estudo consiste no desenvolvimento, aplicação e comparação entre dois métodos de ensaio de ciclagem térmica. O primeiro se baseia na NBR 15575-4:2013, que estabelece um método para a avaliação da durabilidade de componentes de vedação em edifícios, utilizando caixas térmicas irradiantes, que consiste na exposição unilateral da alvenaria revestida a ciclos de aquecimento e resfriamento simultâneo à molhagem do revestimento. Utilizando-se esse método, também foram submetidos a exposição térmica prismas de cada argamassa, nas dimensões de 40x40x160 mm. No segundo método, o sistema revestido é totalmente exposto a variações de temperaturas, permanecendo em uma câmara climática que executa repetidos ciclos de aquecimento e resfriamento. As argamassas utilizadas foram produzidas no traço 1:1:6 em volume (cimento, cal e areia) utilizando-se cimento CP II F-32, cal CH-I em pasta, areia de rio e fíler produzido a partir de agregado reciclado de concreto (ARC), adicionado nos teores de 2; 4,5; 7 e 9,5% em relação à massa da areia, e aplicadas sobre substrato de cerâmica vermelha. A primeira atividade do programa experimental consistiu no desenvolvimento dos métodos para a realização da ciclagem térmica e em sua avaliação. Posteriormente, foram produzidas as argamassas e revestimentos, e realizadas as ciclagens térmicas. O método que utiliza uma câmara climática para a ciclagem térmica demonstrou menor potencial de degradação das argamassas; o método das caixas térmicas demonstrou maior eficiência no envelhecimento acelerado dos revestimentos e prismas de argamassas. A exposição à ciclagem térmica resultou em expressiva perda das propriedades das argamassas testadas na forma de prisma, em todos os teores de adição de fíler de ARC. A ciclagem dos revestimentos de argamassa aplicados sobre substrato cerâmico apresentou menor degradação que os prismas, sendo que os dois revestimentos com baixo teor de adição (2 e 4,5% de fíler) apresentaram maior degradação nas argamassas e os demais revestimentos (com 7 e 9,5% de fíler) apresentaram as menores resistências de aderência à tração. / Construction industry has shown a significant growth this past decade. With it, grows the demand for raw materials and there is a generation of waste at construction sites and in industries linked to the sector. According to the Ministery of Mines and Energy (MME) in 2008, sand production reached an estimated 279 million tonnes and it is estimated that in 2030 its production can reach 1.276 billion tons. The use of construction and demolition waste for the production of coating mortars can bring economic and environmental benefits, but its use is only possible if the coating is durable, supporting environmental actions. This study is the development, application and comparison between two thermal cycling test methods. The first method is based on the NBR 15575-4:2013 standard, uses radiant boxes and consists in unilateral exposure of masonry coated to simultaneous cycles of heating and cooling under wetting. This method were also underwent to thermal exposure 3 prisms of each mortar, in the dimensions of 40x40x160 mm. In the second method, the coated system is fully exposed to temperature variations and remains in a climatic chamber that performs repeated heating and cooling cycles. The mortars used and applied to ceramic substrates have been produced in a proportion of 1: 1: 6 by volume (cement, lime and sand) using Brazilian cement CP II F-32, CH-I lime putty, river sand and filler produced from recycled concrete aggregate (RCA), in compositions with varying content (2, 4.5; 7 and 9.5%) relative to the mass of sand. The first activity of the experimental program was the development of the methods for performing thermal cycling and in their assessment. Mortars and coatings were produced, and then was performed thermal cycling. The method using a climatic chamber for thermal cycling has showed lower efficiency for the degradation of mortar; the method that uses radiant thermal boxes has demonstrated greater efficiency in the accelerated aging of the coatings. The thermal cycling exposure resulted in a significant loss of properties of the prisms, in all addition levels of ARC’s filler. The thermal cycling in mortar applied on the ceramic substrate showed less degradation than the prisms, and the two coatings with a low content of filler (2% and 4.5%) showed higher degradation in mortars while other coatings (with 7 and 9.5% of filler) had the lowest coating bond strength.