Este estudo avalia a resistência de união à microtração de dois cimentos resinosos (RelyXTM U200 - 3M/ESPE e RelyXTM ARC - 3M/ESPE), na fixação de restauração cerâmica, em função do tipo de tratamento ao substrato dentinário: G1, sem tratamento (cimento autoadesivo RelyX U200); G2, sistema adesivo autocondicionante de dois passos (ClearfilTM SE Bond, Kuraray /RelyXTM ARC); e G3, sistema adesivo convencional de três passos (AdperTM ScotchbondTM Multi- Purpose, 3M/ESPE /RelyXTM ARC). Trinta dentes bovinos foram selecionados, limpos e armazenados em solução neutra de timol a 0,1% a 37oC, sendo divididos aleatoriamente em três grupos experimentais (n=10). O esmalte da face vestibular foi desgastado para expor a superfície dentinária com área de 8 mm x 8 mm e submetido, em seguida, a planificação com lixas de carbeto de silício no 180, 320 e 600. Trinta blocos cerâmicos de dissilicato de lítio, IPS e-max - Ivoclar Vivadent, medindo 8 mm x 8 mm x 2 mm, foram confeccionados e suas superfícies de cimentação jateadas com partículas de óxido de alumínio (50μm). Previamente à cimentação, todos os blocos cerâmicos tiveram suas superfícies internas condicionadas com ácido fluorídrico e foram aplicados agentes silano. Os tratamentos em dentina e os procedimentos de cimentação seguiram as normas dos fabricantes correspondentes para cada grupo. Decorridas 24 horas da cimentação, os conjuntos dente/cimento/cerâmica foram seccionados em forma de vigas, com área aproximada de 1 mm2, adaptados à máquina universal de ensaios (INSTRON) para realização do teste de microtração, utilizando-se a célula de carga de 500N com velocidade de 0,5 mm/minuto. Os valores médios de resistência à microtração (MPa) encontrados foram: G1 (16,16 ± 7,16), G2 (27,92 ± 6,17) e G3 (25,06 ± 6,09). Os dados foram submetidos à análise de variância e ao teste de Tukey em nível de significância de 5%. O cimento resinoso autoadesivo RelyXTM U200 apresentou menor potencial de resistência de união com diferença estatística significante, quando comparado ao cimento resinoso convencional RelyXTM ARC e tratamento prévio com os adesivos convencional de três passos e autocondicionante de dois passos. Entretanto, a associação do cimento RelyXTM ARC tanto ao sistema adesivo convencional quanto ao acondicionante apresentou valores médios similares de resistência de união aos substratos dentinário e cerâmico. Dentre os tipos de fratura, após o teste de microtração, o cimento RelyXTM U200 demonstrou maior ocorrência de falhas do tipo adesiva em dentina (AD), com menor interação adesiva junto à dentina. A associação do sistema adesivo convencional ao cimento resinoso convencional evidenciou menor ocorrência de fraturas AD e maior ocorrência junto à cerâmica, quando comparada à associação do sistema adesivo autocondicionante ao cimento resinoso convencional, apesar de os resultados de resistência de união demonstrarem similaridade de valores e estatística. / This study evaluates the microtensile bond strength of two resin cements (RelyXTM U200 - 3M/ESPE and RelyXTM ARC - 3M/ESPE), in the retention of ceramic restorations according to the treatment type of the dentin substrate; G1: no treatment (RelyX U200 self-adhesive cement); G2: two-step self-etch adhesives (ClearfilTM SE Bond, Kuraray /RelyXTM ARC); and G3: three-step etch and rinse adhesives (AdperTM ScotchbondTM Multi-Purpose, 3M/ESPE /RelyXTM ARC). Thirty bovine teeth were selected, cleaned and stored in a neutral 0,1% thymol solution at 37oC, divided randomly into three experimental groups (n=10). The facial surface enamel was scaled in order to expose an area of 8mm x 8mm of the dentin surface, and subsequently planed with no 180, 320 and 600 silico n carbide sandpaper. Thirty lithium disilicate ceramic blocks, IPS e-max Ivoclar Vivadent, measuring 8mm x 8mm x 2mm were made and their surfaces sandblasted with aluminum oxide particles (50μm). Before cementation, the internal surfaces of all the ceramic blocks were conditioned with hydrofluoric acid and silanized. The dentin treatments and the cementation procedures followed the manufacturers norms for each group. Twentyfour hours after cementation, the tooth/cement/ceramic blocks were sectioned into beam-like structures, each with an approximate area of 1mm2, adapted to the universal testing machine (INSTRON) in order to test microtensile strength, with the load cell set at 500N, at a speed of 0.5mm/min. The mean values found for microtensile strength (MPa) were: G1 (16,16 ± 7,16), G2 (27,92 ± 6,17) and G3 (25,06 ± 6,09). The data were submitted to analysis of variance and to Tukeys test, with a 5% significance level. The self-adhesive resin cement RelyXTM U200 presented the lowest potential bond strength, with a statistically significant difference when compared to the conventional resin cement RelyXTM ARC and prior treatment with three-step etch and rinse adhesives and two-step self-etch adhesives. However the association of the RelyXTM ARC cement, both with the conventional adhesive system and with the self-etch adhesives produced similar mean values for bond strength in the dentin and ceramic substrates. Among the types of fracture, following the test for microtensile strength, the RelyXTM U200 cement presented the highest incidence of faults of the dentin adhesive (DA) type, and the lowest adhesive interaction with the dentin. The association of the conventional adhesive system with conventional resin cement presented a lower incidence of DA fractures and a higher incidence along the ceramics, when compared to the association of the self-etch adhesive system and conventional resin cement, despite the similarity in the numbers and statistics of the bond strength results.

Os cimentos resinosos têm sido largamente utilizados em odontologia restauradora com a finalidade de reter o pino intra-radicular e dissipar tensões entre este e a raiz. Entretanto, o grau de conversão alcançado pelos mesmos influencia suas propriedades mecânicas, biocompatibilidade e degradação pela água e pelos ácidos bucais. Testes de microdureza podem ser aplicados para estimar o grau de conversão de compósitos, uma vez que apresentam boa correlação com a espectroscopia infravermelha. Este trabalho objetivou analisar a microdureza de quatro cimentos resinosos de polimerização dual utilizados na cimentação de pinos de fibra de vidro, nos períodos inicial, após 24 horas de imersão em etanol a 75% e após 3 meses de armazenamento em água, e testar a hipótese de que não há diferença entre a microdureza dos terços cervical, médio e apical na linha de cimento. Quarenta incisivos bovinos tratados endodonticamente foram distribuídos em quatro grupos para a cimentação de pinos Fibrekor® (Jeneric/Pentron) de 1mm de diâmetro, sendo: Grupo 1 - Panavia F 2.0 (Kuraray Medical Inc.), Grupo 2 - Variolink (Ivoclar), Grupo 3 - Rely X Unicem (3M ESPE) e Grupo 4 - Duolink (Bisco). Após a cimentação, as raízes foram divididas em 2 subgrupos, sendo 5 seccionadas após 7 dias para análise da microdureza inicial e 5 mantidas íntegras em água deionizada por 3 meses, para avaliação da microdureza final no microdurômetro Shimadzu HMV (Japan). Após a mensuração inicial, as raízes seccionadas eram armazenadas a 37º C por 24h em 10mL de solução de etanol a 75%, e reavaliadas. Foram identificadas diferenças estatisticamente significativas entre cimentos, terços e períodos (inicial ou após 24h de imersão em etanol a 75%), bem como interações entre cimento/terços e cimento/períodos de avaliação. O cimento Panavia exibiu os valores de microdureza inicial significativamente superiores, sem diferença estatística entre os demais cimentos. Os valores de microdureza inicial por terços não seguiram um padrão homogêneo; os cimentos Variolink e Duolink exibiram valores de microdureza significativamente superiores no terço cervical, sem diferença significativa entre os terços para os demais cimentos. A imersão em etanol reduziu significativamente a média dos valores de dureza para todos os cimentos; o comportamento por terços variou em função do material. O armazenamento em água por 3 meses não exerceu influência sobre a dureza da maioria dos cimentos, com exceção do Unicem, que exibiu aumento significativo dos valores de dureza após esse período. Portanto, a hipótese proposta neste estudo foi rejeitada. / Resin cements have been largely used in dentistry for retaining intraradicular posts and to minimize tension between them. However, the degree of conversion influences mechanical properties, biocompatibility and susceptibility of water and acid degradation of these polymers. Hardness tests are used to estimate the degree of conversion of composites, as it shows good correlation with infrared spectroscopy. The aim of this study was to evaluate the microhardness of four resin cements used for fiber posts cementation at the nitial period, 24h-immersion in a 75% ethanol solution and after 3-month water storage. Forty bovine incisives were endodontically treated and restored with 1mm diameter Fibrekor® posts (Jeneric/Pentron), being: Group 1 - Panavia F 2.0 (Kuraray Medical Inc.), Group 2 - Variolink (Ivoclar), Group 3 - Rely X Unicem (3M ESPE) and Group 4 - Duolink (Bisco). After cementation, each group was divided in two subgroups: 5 roots were sectioned 7 days after cementation for initial hardness measurement and 5 roots were immersed in deionized water for 3 months for final hardness measurements using Shimadzu Micro Hardness Tester (HMV, Japan). After the initial measurements, the sectioned roots were immersed in 10mL 75% ethanol solution for 24h at 37ºC, and tested again. Differences in hardness values have been detected among resin cements, radicular thirds and periods (initial or 24h-immersion in a 75% ethanol solution). Data also revealed significant interaction to cement/third and cement/period of evaluation. Panavia showed higher hardness values, with no statistical differences among the other cements. It was not verified a homogeneous pattern regarding radicular third; Variolink and Duolink exhibited higher hardness values for the cervical third, without differences among radicular thirds for the other cements. Hardness values decreased after ethanol immersion for all resin cements and the hardness according to radicular thirds varied among the materials. The hardness of tested resin cement showed no influence after 3-month water storage, except for Unicem as it showed an increase in Knoop hardness after this period. Therefore, the null hypotesis proposed was rejected.

Atualmente, existem cimentos resinosos que dispensam o uso prévio de sistemas adesivos (autoadesivos) e aliam as vantagens dos cimentos resinosos às dos cimentos não resinosos, sendo recomendados para todas as restaurações indiretas, inclusive a cimentação de pinos intrarradiculares. Devido à falta de conhecimento do comportamento desses cimentos perante as diferentes técnicas de manipulação e aplicação, o objetivo deste trabalho foi avaliar a força de retenção de 3 cimentos autoadesivos, quando empregados na cimentação de pinos intrarradiculares de fibra de vidro. Para isso, foram selecionados 45 caninos humanos, divididos aleatoriamente em três grupos (N=15) diferenciados pelos cimentos: Grupo I - BisCem (Bisco), Grupo II - Breeze (Pentron Clinical Technologies, LLC) e Grupo III Maxcem (Kerr). Esses grupos foram divididos em três subgrupos, variando a técnica de aplicação e de manipulação: Subgrupo A - Ponta automisturadora/Ponta aplicadora, Subgrupo B - Espatulação/Lentulo, Subgrupo C - Espatulação/Centrix. O teste de push-out foi realizado com uma velocidade de 1 mm/min, e a força de retenção foi expressa em Mega Pascal (MPa). O cimento Breeze apresentou os maiores resultados médios para os subgrupos A, B e C (12,27 ± 3,19 Mpa; 13,65 ± 2,51 MPa; 13,64 ± 3,65 MPa), quando comparados aos cimentos Biscem (7,25 ± 2,37 MPa; 13,37 ± 1,80 MPa; 9,48 ± 2,38 MPa), e Maxcem Elite (7,87 ± 1,12 MPa; 7,21 ± 1,43 MPa; 9,89 ± 1,43 MPa. Somente para o cimento Biscem houve diferença estatística significante entre seus subgrupos. Assim, pôde-se concluir que, de acordo com os resultados deste estudo, a técnica de aplicação e manipulação pode influenciar na resistência retentiva, dependendo do cimento autoadesivo utilizado. / Currently, there are resin cements that do not require prior use of adhesive systems (self-adhesive), and combine the advantages of resin cements with that of non-resin cements, and are recommended for all indirect restorations, including intraradicular cementation. Due to the lack of understanding about the behavior of these cements in the presence of the different handling and application techniques, the objective was to evaluate the retention strength of 3 self-adhesive cements, when used in cementing intra-radicular fiberglass posts. For this, 45 human canines were selected and divided randomly into three groups (N = 15) for different cements: roup I - Bisco (Bisco), Group II - Breeze (Pentron Clinical Technologies, LLC) and Group III - Maxcem (Kerr). These groups were divided into three sub-groups by varying the application and handling technique: Sub-group A - Automix/Point tip applicator, Sub-group B - Handmix/ Lentulo, Sub-group C Handmix/ Centrix. The test of push-out was performed with a speed of 1 mm / min, and the retention strength was expressed in Mega Pascal (MPa). The Breeze cement, showed the highest average for sub-groups A, B and C (12.27 ± 3.19 MPa, 13.65 ± 2.5 MPa, 13.64 ± 3.65 MPa)when compared to the Biscem cement (7.25 ± 2.37 MPa, 13.37 ± 1.80 MPa, 9.48 ± 2.38 MPa), and Maxcem Elite (7.87 ± 1.12 MPa, 7.21 ± 1 , 43 MPa, 9.89 ± 1.43 MPa. Only for the Biscem cement was there statistically significant difference between the sub-groups. Thus, one can conclude that according to the results of this study, the application and handling technique may influence the retentive strength depending on the self-adhesive cement used.

As restaurações indiretas em sistemas totalmente cerâmicos desenvolveram-se visando à obtenção de próteses com melhor capacidade de mimetismo do dente natural. Além das propriedades óticas, essas restaurações devem ter adesão ao substrato de suporte, de modo a promover a união entre a cerâmica, o esmalte e a dentina, formando um corpo único, permitindo a transferência de tensões da restauração para a estrutura dental. Alguns fatores como: composição, espessura, opacidade e a cor do material cerâmico podem interferir na passagem de luz e, consequentemente, diminuir o grau de conversão do cimento, limitando o alcance de suas propriedades mecânicas e prejudicando o desempenho clínico. Dessa forma, este trabalho teve por objetivo avaliar a influência de diferentes níveis de opacidade da infraestrutura do dissilicato de lítio na polimerização de um cimento resinoso dual. Foram utilizados quatro discos de cerâmica (IPS e.max Press, IvoclarVivadent, Schaan, Liechtenstein), um para cada opacidade da infraestrutura (HT, LT, MO e HO) recobertas por sua respectiva cerâmica de cobertura (IPS e.max ceram na cor A3), e um grupo de cimento sem a cerâmica interposta (grupo-controle). Para cada grupo foram polimerizados 15 corpos de prova de cimento resinoso (Variolink II, Ivoclar Vivadent, Schaan, Liechtenstein). Foi mensurado o grau de conversão do cimento com o teste de microdureza knoop. Cada corpo de prova foi avaliado imediatamente após a polimerização e após sete dias. Foram feitas cinco endentações para cada tempo e obtida uma média de cada corpo de prova. O grupo com disco de maior opacidade (HO) apresentou o menor valor de microdureza (9,48 ± 0,36) no tempo inicial. O maior valor de microdureza foi o do grupo-controle após 07 dias (38,51 ± 1,05). Os grupos com disco LT e MO apresentaram comportamento igual nos dois tempos, não havendo diferença entre eles. O maior valor de microdureza com o uso de discos cerâmicos foi o do grupo HT após 07dias (29,53 ± 1,81), o qual apresentou valor próximo do controle inicial, porém estatisticamente diferente. Conclui-se que o nível de opacidade da infraestrutura do dissilicato de lítio pode influenciar no grau de polimerização de um cimento resinoso dual. / The indirect restorations in totally ceramic systems have been developed in order to obtain prostheses with improved ability to mimicry of the natural tooth. In addition to optical properties, these restorations must have adhesion to the supporting substrate so as to promote the bonding between the ceramic, enamel and dentin, forming a single body, allowing the transfer of stresses to the structure of the dental restoration. Some factors such as composition, thickness, opacity and color of the ceramic material can interfere with the transmission of light and, consequently, decrease the degree of conversion of the cement, impairing their mechanical properties and impairing clinical performance. Thus, this study aimed to evaluate the influence of different opacity levels of lithium disilicate infrastructure in the polymerization of a dual resin cement. Four ceramic discs were used (IPS e.max Press, Ivoclar Vivadent, Schaan, Liechtenstein), one for each opacity infrastructure (HT, LT, MO and HO) covered by their respective veneering ceramic (IPS e.max ceram in color A3) and a group of ceramic cement without an intermediary (control group). For each group there were 15 specimens (n=15) (Variolink II, Ivoclar Vivadent, Schaan, Liechtenstein). The degree of conversion of the cement was measured with the Knoop microhardness test. Each specimen was evaluated immediately after polymerization and after seven days. Five indentations were made for each time and obtained an average of each specimen. The group with the largest disk opacity (ho) had the lowest microhardness value (9.488 ± 0.364) at baseline. The control group showed the highest microhardness the after 07 days (38.517 ± 1.055). Groups with LT and MO disk behaved the same on both days, with no difference between them. The highest microhardness using ceramic disc was in the HT group after 07dias (29.530 ± 1.812). It was concluded that the lithium disilicate infrastructure level of opacity influence the degree of polymerization of a dual resin cement.

O objetivo desta pesquisa foi avaliar a transmitância de diferentes tipos e cores de cerâmicas e seus efeitos no grau de conversão (GC) de dois tipos de cimentos resinosos com modo de polimerização dual. Foram confeccionadas 60 pastilhas com a cerâmica IPS e.max (Ivoclar Vivadent, Schaan, Liechtenstein) e divididas em 3 grupos: LT, MO e Z, com 20 pastilhas cada um. Nos grupos LT e MO, as pastilhas foram confeccionadas com a cerâmica de dissilicato de lítio de baixa translucidez (LT - low transluscency) e de média opacidade (MO - medium opacity), respectivamente. No grupo Z, as pastilhas foram confeccionadas em zircônia. Cada grupo foi subdividido em 5 subgrupos (n=4), de acordo com a cor da cerâmica: A2; A3,5; B2; C2; D3. No grupo LT, as pastilhas foram prensadas nas cores anteriormente citadas e, nos grupos MO e Z, as pastilhas foram, inicialmente, confeccionadas para simular infraestruturas e, posteriormente, receberem aplicação de cerâmica de revestimento IPS e.max Ceram (Ivoclar Vivadent, Schaan, Liechtenstein) nas mesmas cores. O espectrofotômetro UV 1800 Shimadzu foi utilizado para medir a transmitância de cada espécime de cerâmica (2,0 mm de espessura). Para medir o GC, espécimes dos cimentos resinosos Variolink II (Ivoclar Vivadent, Schaan, Liechtenstein) e Rely X U200 (3M ESPE, St. Paul, MN, USA), com espessura de 100 μm, foram fotopolimerizados sob os discos de cerâmica por 40 s. Espécimes dos cimentos fotoativados sem a interposição da cerâmica foram usados como grupo controle. A polimerização dos cimentos foi avaliada através da espectrometria no infravermelho com transformada de Fourier (FTIR) empregando o método de reflexão atenuada total (ATR) imediatamente após a fotopolimerização. Os resultados foram submetidos aos testes ANOVA a 1 critério e Teste de Tukey (α=5%). Os valores de transmitância foram inferiores a 1%, sendo que as do grupo LT apresentaram, em geral, os maiores valores de transmitância, seguidos dos grupos MO e Z. O GC do cimento Variolink II não sofreu influência da interposição da pastilha de cerâmica. Para o cimento Rely X U200, a interposição de alguns tipos/cores de cerâmica (LT A3,5; MO A2; MO A3,5 e Z A3,5) diminuíram o GC em relação ao grupo controle. Concluiu-se que os valores de transmitância e GC foram influenciados pelos tipos/cores de cerâmica. Entretanto, somente o grupo formado pela cerâmica de dissilicato de lítio LT, usando o Rely X U200, apresentou correlação negativa entre transmitância e GC. / The aim of the present study was to evaluate the transmittance of different ceramic types and shades and their effects on the degree of conversion (DC) of two dual-cure resin cements. Sixty discs were fabricated with IPS e.max ceramic (Ivoclar Vivadent, Schaan, Liechtenstein) and divided into three groups (n= 20 in each group): LT, MO and Z. For LT and MO groups discs were fabricated with low translucency (LT) and medium opacity (MO) lithium disilicate ceramic, respectively. Discs from Z group were manufactured of zirconia. Each group was divided into five subgroups (n = 4), according to the ceramic shade: A2; A3,5; B2; C2; D3. In the LT group, specimens were heat-pressed in shades cited above and in the MO and Z groups, the discs were initially fabricated as core materials and then veneered with veneer ceramic (IPS e.max Ceram, Ivoclar Vivadent, Schaan, Liechtenstein) in the same shades. A spectrophotometer UV-1800 Shimadzu was used to determine the transmittance percentage of each ceramic specimen (2.0-mm-thick). For DC measurements, the resin cements (Variolink II - Ivoclar Vivadent, Schaan, Liechtenstein and Rely X U200 - 3M ESPE, St. Paul, MN, USA) specimens (thickness: 100 μm) were photocured under the ceramic discs (2.0-mm-thick) for 40 s. Specimens photocured without the ceramics discs were used as control group. ATR/FTIR spectrometry was used to evaluated the extent of polymerization for all cement specimens immediately after photocuring. The results were submitted to one-way ANOVA and Tukey test (α=5%). The transmittance percentage was less than 1% and the LT group had the highest transmittance values, followed by MO and Z groups. The %DC of Variolink II cement was not influenced by the ceramic disc interposition. For Rely X U200 cement, the interposition of some ceramics types/shades (LT A3,5, MO A2, MO A3,5 and Z A3,5) significantly decreased the %DC compared to control group. It was concluded that the transmittance values and %DC were influenced by the ceramics types/shades. However, only the LT group, using the Rely X U200, showed a negative correlation between transmittance and %DC.

Este trabalho teve como objetivo avaliar a microdureza de dois cimentos resinosos de polimerização dual (RelyX U100®, 3M-ESPE e Panavia F 2.0®, Kuraray), empregados na cimentação de pinos de fibra de vidro (Fibrekor-Jeneric® Pentron) variando o modo de polimerização em químico, fotoativação imediata ou tardia após 5min através de luz halógena, avaliando também o efeito do armazenamento em água deionizada por três meses. Este trabalho testou as seguintes hipóteses nulas: não há diferença nos valores de microdureza entre os cimentos, modo de polimerização, efeito do armazenamento e entre os terços radiculares. Sessenta raízes de incisivos bovinos, com 16mm de comprimento cérvico-apical, tiveram seus condutos obturados e, posteriormente, preparados para cimentação do pino intracanal. Os espécimes foram divididos em 6 grupos (n = 10), cada um subdividido em 2 subgrupos com 5 espécimes para cada cimento. Os pinos foram cimentados de acordo com o protocolo descrito por cada fabricante. No grupo A1, os espécimes foram mantidos em ambiente à prova de luz para que ocorresse apenas a polimerização química. No grupo B1, os espécimes foram cimentados e submetidos à fotoativação imediata, e, no grupo C1, realizou-se a fotoativação após 5 minutos. As raízes foram seccionadas longitudinalmente, para que a linha de cimento pudesse ser exposta e os testes de microdureza realizados. Após 7 dias, as médias de microdureza (± desvio padrão) foram obtidas, para os terços cervical, médio e apical, respectivamente: A1 (Panavia) - 41,25 ±3,38 / 38,17±1,74 / 35,63±1,73; A1 (U100) - 59,43±4,32 / 52,14±3,00 / 50,27±4,13; B1 (Panavia) - 75,29±4,84 / 60,36±6,76 / 48,97±3,33; B1 (U100) 62,41±6,83 / 53,99±4,74 / 49,04±2,20; C1 (Panavia) - 70,22±93 / 61,00±4,48 / 56,46±7,51; C1 (U100) - 62,40±6,66 / 53,69±2,00 / 51,54±2,18. Para os grupos armazenados em água, os valores médios de microdureza (± desvio padrão) obtidos nos 3 grupos, químico (grupo A2), fotoativado imediatamente (grupo B2) e fotoativado tardiamente (grupo C2), nos terços cervical, médio e apical, respectivamente, foram: A2 (Panavia) - 37,17±1,38 / 35,01±0,74 / 34,10±2,37; A2 (U100) - 52,39±2,00 / 52,13±3,01 / 51,06±1,48; B2 (Panavia) - 63,01±2,17 / 55,94±2,10 / 48,55±1,62; B2 (U100) - 58,81±2,34 / 55,19±1,42 / 55,71±3,17; C2 (Panavia) - 56,99±1,21 / 51,29±1,81 / 48,29±3,00; C2 (U100) - 59,02±2,04 / 57,05±2,04 / 54,95±1,05. Os resultados foram submetidos ao teste ANOVA a 4 critérios (cimento, modo de polimerização, armazenamento e terços), que detectou diferenças estatísticas entre os grupos, e o teste de Tukey foi aplicado para comparações individuais. Os resultados mostraram que: a fotoativação com luz halógena promoveu um aumento significativo nos valores de microdureza para o cimento Panavia; o armaz namento em água por três meses reduziu os valores de microdureza para a maioria dos grupos, sendo que o cimento o U100 apresentou menor variação de dureza quando comparado ao Panavia; os terços que receberam maior intensidade de luz halógena tiveram maior aumento de microdureza para ambos os cimentos, especialmente para o cimento Panavia. Conclui-se, portanto, que as hipóteses de nulidade propostas foram rejeitadas. / The objective of this study was to evaluate the microhardness of two dual cure resin cements (RelyX - U100®, 3M-ESPE and Panavia F 2.0®, Kuraray), used for fiberglass posts (Fibrekor ® - Jeneric Pentron) cementation. Chemical cure and a halogen immediate and late light cure source were compared, and the effect of storage in deionized water for three months was also evaluated. This study tested the following null hypotheses: there is no difference between the microhardness values for each dual cure resin cement, cure source type, storage time, or root thirds. Sixty bovine incisor roots 16mm long had their roots restored and then prepared for post cementation. The specimens were divided into 6 groups (n = 10), and each group was subdivided into 2 subgroups with 5 specimens for each cement. The posts were cemented according to manufacturers instructions. In group A1, the specimens were kept in a light-proof environment to ensure only a chemical cure. In group B1, the specimens were restored and subjected to immediate light curing, and in group C1, light curing was performed after 5 minutes. The roots were longitudinally sectioned to expose the cement line and perform microhardness tests. After 7 days, the average microhardness (± standard deviation) values were obtained for the cervical, medium and apical thirds, respectively: A1 (Panavia ) - 41,25±3,38 / 38,17±1,74 / 35,63±1,73; A1 (U100) - 59,43±4,32 / 52,14±3,00 / 50,27±4,13; B1 (Panavia) - 75,29±4,84 / 60,36±6,76 / 48,97±3,33; B1 (U100) - 62,41±6,83 / 53,99±4,74 / 49,04±2,20; C1 (Panavia) - 70,22±1,93 / 61,00±4,48 / 56,46±7,51; C1 (U100) - 62,40±6,66 / 53,69±2,00 / 51,54±2,18. For the 3 groups stored in deionized water (chemical [group A2], immediate light curing [group B2] and late light curing [group C2]), the average microhardness values (± standard deviation) obtained for the cervical, medium and apical thirds, respectively were: A2 (Panavia) - 37,17±1,38 / 35,01±0,74 / 34,10±2,37; A2 (U100) - 52,39±2,00 / 52,13±3,01 / 51,06±1,48; B2 (Panavia) - 63,01±2,17 / 55,94±2,10 / 48,55±1,62; B2 (U100) - 58,81±2,34 / 55,19±1,42 / 55,71±3,17; C2 (Panavia) - 56,99±1,21 / 51,29±1,81 / 48,29±3,00; C2 (U100) - 59,02±2,04 / 57,05±2,04 / 54,95±1,05. ANOVA testing was used to detect statistical differences among the 4 criteria (cements, cure mode, storage and thirds) and the Tukey test was used for individual comparisons. The results showed that the halogen light cure promoted a significant increase in microhardness values for Panavia cement; storage in water for three months reduced microhardness values for most of the groups, although U100 resulted in less microhardness variation compared to Panavia; the thirds that received a higher intensity of halogen light had a higher increase in the average values of microhardness for both cements, especially for Panavia. Therefore, the null hypotheses proposed in this work were rejected.

A perda de adesao e uma falha comum reportada para os pinos reforçados por fibra e usualmente ocorre ao longo da interface adesiva entre a dentina radicular e o cimento resinoso. A espessura de cimento resinoso ideal para preservar a continuidade da interface adesiva cimento-dentina e aumentar a retencao do pino e desconhecida. O objetivo deste estudo foi avaliar a influencia da espessura do cimento na integridade e na resistencia adesiva de dois cimentos resinosos empregados para a cimentacao de pinos reforcados por fibra. Trinta incisivos laterais superiores humanos com comprimentos radiculares semelhantes foram selecionados, secionados na juncao cimento-esmalte e tratados endodonticamente. As raizes foram aleatoriamente divididas em seis grupos (n=5), e os condutos radiculares foram preparados a uma profundidade de 8 mm usando uma das três brocas com diametro diferente: Broca Largo n 3 para o grupo controle (L3 1 mm); Broca Largo nℵ 4 (L4 - 1,25 mm) e Broca Largo nℵ 5 (L5 1,5 mm) para os grupos experimentais. Pinos de resina reforcados por fibra de vidro (Fibrekor post, Jeneric Pentron), 1 mm de diametro, foram cimentados aos condutos radiculares utilizando o cimento resinoso dual (Duolink, Bisco) ou o cimento resinoso autopolimerizavel (C&B Cement, Bisco). A porcao de cada especime contendo os pinos reforcados por fibra foi secionada transversalmente em tres secoes (cervical, media e apical) de 2 mm de espessura utilizando um disco diamantado em maquina de corte seriado sob refrigeracao com agua. As secoes foram polidas, limpas ultrassonicamente e duplicadas com polivinil siloxano. Replicas em resina epoxica das secoes foram obtidas para a mensuracao da espessura do cimento e da integridade adesiva na interface cimento-dentina por meio de MEV. As secoes foram armazenadas em solucao fisiologica a 37o C por uma semana e, entao, submetidas ao teste push-out em uma maquina de ensaio universal a velocidade de 0,5 mm/min-1, e a forca maxima requerida para deslocar cada pino foi registrada (N). Os dados foram analisados usando ANOVA a um criterio, teste de Tukey e teste t de Student (α=0,05). A correlacao entre a integridade adesiva, a resistencia adesiva e a espessura do cimento tambem foi determinada pelo coeficiente de Pearson (α=0,05). A comparacao multipla entre as condicoes experimentais para cada cimento revelou que os valores medios de integridade adesiva (%) e de resistencia adesiva (MPa) dos pinos reforcados por fibra cimentados com o cimento resinoso Duolink foram significantemente maiores no grupo controle (L3: 61,79 ± 18,06 e 11,32 ± 4,66) do que no grupo experimental com camada de cimento muito espessa (L5: 38,91 ± 5,75 e 4,68 ± 2,16) (p=0,018 e p=0,035), respectivamente. Embora nao tenha sido observada diferenca significante na integridade adesiva entre as diferentes espessuras de cimento avaliadas para o cimento resinoso C&B Cement (p>0,05), o grupo com camada de cimento muito espessa (L5: 10,67 ± 4,59) foi significantemente mais retentivo do que o grupo controle (L3: 4,01 ± 0,76) (p=0,014). A comparacao entre cimentos para cada condicao experimental mostrou que o cimento resinoso Duolink foi mais retentivo do que o cimento resinoso C&B Cement no grupo controle (11,32 ± 4,66 e 4,01 ± 0,76, p=0,008), ao passo que o cimento resinoso C&B Cement foi mais retentivo do que o cimento resinoso Duolink em L5 (4,68 ± 2,19 e 10,67 ± 4,59, p=0,030), respectivamente. Somente a comparação entre o grupo experimental L4 e os outros grupos nao foi significante para ambos os cimentos resinosos e testes realizados. O aumento da espessura do cimento diminuiu significantemente a integridade adesiva (r=-0,5901; p=0,021) e a resistência adesiva (r=-0,5387; p=0,038) para o cimento resinoso Duolink. A integridade adesiva correlacionou-se positivamente com a resistencia adesiva para esse tipo de cimento resinoso (r=0,6855; p=0,005). Diferentemente, nao foi encontrada correlação significante entre a espessura do cimento e a integridade adesiva (r=0,153; p=0,586) e nem entre a integridade adesiva e a resistencia adesiva (r=0,2969; p=0,283) registradas para C&B Cement. Contudo, o aumento da espessura deste tipo de cimento resinoso aumentou significantemente a retencao do pino (r=0,6576; p=0,008). Os dados sugeriram que a espessura da camada dos cimentos resinosos influenciou a integridade adesiva e a resistencia adesiva dos pinos de resina reforcados por fibra. Para o cimento resinoso Duolink selecionado, os maiores valores de integridade adesiva e de resistencia adesiva foram obtidos quando a camada mais fina de cimento foi testada (L3). Contudo, o cimento resinoso C&B Cement apresentou maior retencao quando a espessura da camada de cimento aumentou muito (L5), embora a espessura do cimento nao tenha desempenhado um papel importante na integridade adesiva da interface cimento-dentina para esse cimento resinoso. / Debonding is the most common cause of failure reported for glass fiberreinforced composite posts and occurs frequently along the adhesive interface between the resin cement and the root dentin. The ideal thickness of the resin cement to preserve the continuity along the cement-dentin interface and to increase the retention of the post is unknown. The purpose of this study was to evaluate the influence of the thickness of the resin cement on the bond integrity and strength of two resin cements used for glass fiber-reinforced composite posts cementation. 30 human maxillary incisors with similar root dimensions were selected, sectioned at the amelocemental junction and endodontically treated. The roots were randomly divided into six groups (n=5), and the post spaces were prepared 8 mm deep using one of the three burs with different diameters: Largo bur nℵ 3 for the control group (L3 1- mm); Largo bur nℵ 4 (L4 1,25-mm) e Largo bur nℵ 5 (L5 1,5-mm) for the experimental groups. Fiber-reinforced composite posts (Fibrekor post, Jeneric Pentron), 1-mm diameter, were cemented to post spaces by using the dual-cure (Duolink, Bisco) or self-cure system (C&B Cement, Bisco). The portion of each specimen that contained the bonded fiber post was sectioned into three 2-mm thick serial slices (cervical, middle, apical) with the Isomet saw under water cooling. The slices were polished and ultrasonicated in deionized water. Polyvinyl siloxane impressions of the observable surfaces were taken and the surfaces replicated with epoxy resin for measuring of the thickness of the resin cement and the bond integrity by using MEV. The slices were stored in physiologic solution at 37o C for one week, and then submitted to the push-out test at a crosshead speed of 0.5 mm/min-1. The maximum force required to dislocate each post was registered (N). Data were analyzed by one-way ANOVA, Tukey test and t test (α=0,05). The correlation between bond integrity, bond strength and thickness of the resin cement was also determined by correlation test (α=0,05). The multiple comparison test between the experimental conditions for each resin cement showed that the mean values of bond integrity (%) and strength (MPa) of the fiber posts cemented with Duolink were significantly higher at the control group (L3: 61.79 ± 18.06 and 11.32 ± 4.66) than those obtained for the experimental groups with the thicker layer cement (L5: 38.91 ± 5.75 and 4.68 ± 2.16) (p=0.018 and p=0.035), respectively. Although there was no significant difference on the bond integrity between the different thicknesses evaluated for C&B Cement (p>0.05), the group with thicker layer (L5: 10.67 ± 4.59) was significantly more retentive than the control group (L3: 4.01 ± 0.76) (p=0.014). The comparison between cements for each experimental condition has showed that Duolink was more retentive than C&B Cement at the control group (11.32 ± 4,66 and 4.01 ± 0,76, p=0.008), whereas C&B Cement was more retentive than Duolink at L5 group (4.68 ± 2.19 and 10.67 ± 4.59, p=0.030), respectively. Only the comparison between the L4 experimental group and the others groups was not significant for both resin cements and tests conducted. The increase of the thickness of the cement significantly reduced the bond integrity (r=-0.5901; p=0.021) and strength (r=-0,5387; p=0.038) for Duolink. Bond integrity positively correlated with bond strength for this type of resin cement (r=0.6855; p=0.005). On the other hand, there was no significant correlation between the thickness of the cement and the bond integrity (r=0.153; p=0.586) and neither between the bond integrity and strength (r=0.2969; p=0.283) registered for C&B Cement. However, the increase of the thickness of this type of resin cement has significantly increased the retention of the post (r=0.6576; p=0.008). Data suggested that the thickness of resin cements affected both the bond integrity and strength of fiber posts. For the Duolink resin cement selected, the higher values of bond integrity and strength were obtained when the thinner layer was tested (L3). However, C&B Cement has showed higher retention when the thickness of the cement increased excessively (L5), though the thickness of the cement has not played a role on the bond integrity of the cement-dentin interface for this resin cement.

Objetivo: O objetivo desta pesquisa foi verificar o efeito da interposição de diferentes materiais restauradores indiretos na resistência à flexão em três pontos (RF), microdureza Knoop (MK) e grau de conversão FT-Raman (GC) de um cimento resinoso. Material e métodos: Os materiais restauradores indiretos selecionados para a confecção dos discos (2 mm de espessura e 11 mm de diâmetro) foram: a vitrocerâmica IPS Eris/Ivoclar-Vivadent (E); a cerâmica de infra-estrutura IPS Empress 2/Ivoclar-Vivadent recoberta pela vitrocerâmica IPS Eris/Ivoclar-Vivadent (EE); a resina composta microhíbrida Sinfony/3M ESPE (S); a resina composta microparticulada SR Adoro/Ivoclar-Vivadent (A). Inicialmente, foi determinada a transmitância relativa (TR) destes materiais restauradores através da análise de imagens digitais obtidas por uma câmera CCD e de um espectrômetro de luz visível. Em seguida, os corpos-de-prova (cps, 10 x 2 x 1 mm) do cimento resinoso Nexus 2/SDS Kerr, com (dual) e sem catalisador (fotoativado), foram polimerizados sob os discos de materiais restauradores indiretos utilizando o aparelho de fotoativação de luz halógena OptiluxTM 501/SDS Kerr (QTH) ou o diodo emissor de luz L.E.Demetron 1/SDS Kerr (LED). Os cps também foram fotoativados sem a interposição dos discos, deixando um espaço de zero (E0) e dois (E2) mm entre a ponta do fotoativador e a superfície do cimento. Para avaliação da MK e GC, cada cp foi dividido em quatro zonas: face irradiada - centro (IC); irradiada - borda (IB); não-irradiada - centro (NC); não-irradiada ? borda (NB). Além disso, foi avaliada a emissão espectral dos dois aparelhos de fotoativação com valores de irradiância relativa (%) e absoluta (mW/cm2). Resultados: A espectrometria foi o método mais sensível para detectar diferenças de TR entre os materiais restauradores e detectou que a resina S (3,5%a) transmitiu mais luz e a cerâmica E transmitiu menos luz (1,6%c). A análise de variância mostrou que o cimento dual apresentou médias superiores (P<0,001) de RF (201,3MPa), MK (42,3KHN) e GC (74,8%) em relação ao fotoativado. E, que o QTH (191,5MPaa) promoveu média de RF superior (P<0,001) em relação ao LED (164,4MPab). Em contrapartida, o LED aumentou os valores de MK do cimento em algumas interações e em outras não houve diferença estatística entre os aparelhos. O método FT-Raman apresentou uma menor sensibilidade do que o ensaio de MK para detectar diferenças entre os grupos experimentais. A interposição dos discos de cerâmica reduziu significativamente a RF e MK do cimento fotoativado em relação aos grupos E0 e E2, no entanto, quando foi adicionado o catalisador ao cimento estas reduções não ocorreram. A zona IC (39,6KHNa) dos cps apresentou maiores médias de MK e a zona NB (34,6KHNc) as menores, evidenciando a distribuição não-uniforme da luz sobre o cp. Foi verificado ainda uma correlação positiva entre as médias de GC e MK. Conclusão: A partir dos resultados desta pesquisa concluiu-se que houve uma tendência na qual os materiais restauradores que transmitiram mais luz ao cimento resinoso, principalmente o de pasta única (fotoativado), lhe proporcionou melhores condições para uma reação de polimerização mais eficiente e,consequentemente, propriedades físicas máximas. / Objective: The aim of this study was to verify the effect of interposing different indirect restorative materials on the three-point flexural strength (FS), Knoop microhardness (KHN) and FT-Raman degree of conversion (DC) of a resin cement. Methods: Disks (2-mm thick and 11- mm in diameter) were built using the indirect restorative materials IPS Eris (Ivoclar-Vivadent glass-ceramic, E), IPS Empress 2 (Ivoclar-Vivadent framework ceramic) veneered by IPS Eris (EE), Sinfony (3M ESPE, micro-hybrid composite resin, S) and SR Adoro (Ivoclar-Vivadent microfilled composite resin, A). Initially, their relative transmittance (RT) was determined analyzing digital images obtained by a CCD camera and with visible light spectrometry. Then, bar-shaped specimens (sps, 10 x 2 x 1 mm) of the Nexus 2 resin cement (SDS Kerr) were prepared either with (dual) or without catalyst (light-cured), and photoactivated throught the different restorative materials disks using a halogen light curing unit (QTH, OptiluxTM 501, SDS Kerr) or a light emitting diode (LED, L.E.Demetron 1, SDS Kerr). The sps were also light-cured without interposing the disks, keeping the curing unit light guide either in contact (S0) or 2 mm (S2) from the cement surface. For KHN and DC evaluation, each sp was divided in four regions: irradiated-center (IC), irradiated-edge (IE), non-irradiated-center (NC) and non-irradiated-edge (NE). Light curing unit spectral emissions were obtained with the relative (%) and absolute (mW/cm2) irradiance values. Results: The spetrometry was more capable to detect the RT differences between the restoration materials than the CCD camera and indicated that the S resin (3,5%a) transmitted more light and the E ceramic (1,6%c) transmitted less light. ANOVA revealed higher FS, KHN and DC values for the cement in dual-cure mode compared to light-cure (p<0.001). The QTH (192 MPaa) promoted higher FS than LED (164 MPab). On the other hand, the LED increased the KHN values in some interactions with the EE group and in other interactions there were not statistic differences between the curing units. The FT-Raman method was less sensitive than KHN to detect differences between the experimental groups. The ceramic materials reduced the light-cured cement?s FS and KHN compared to the S0 and S2 groups; however, when the catalyst was added to the cement these reductions did not occurred. The IC regions showed the highest KHN values and the NE, the lowest, indicating the non-uniform distribution of the light. A positive correlation was found between DC and KHN. Conclusion: It was possible to conclude that there was a tendency for the restorative materials which allowed more light transmission to provided better conditions for an efficient polymerization reaction and, consequently, desirable physical properties of the resin cement, more noticeable when used in light-cure mode.

Orientador: Lourenço Correr Sobrinho / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-12T10:14:46Z (GMT). No. of bitstreams: 1 Komori_PaulaCarolinadePaiva_D.pdf: 603004 bytes, checksum: 11e75b4ee3e84d165caa74d684ffbe94 (MD5) Previous issue date: 2008 / Resumo: Os cimentos resinosos têm sido amplamente utilizados devido à capacidade de união ao dente e a prótese fixa e ao sucesso estético. Os cimentos resinosos apresentam ativação química, física ou dupla ativação. Para esses cimentos, quanto maior o grau de polimerização melhores serão suas propriedades. Entretanto, em diversas situações clínicas a polimerização é afetada pela distância da ponta da unidade fotoativadora em relação ao cimento, pela presença de restaurações indiretas ou estrutura dentária. Assim, este estudo avaliou a polimerização de um cimento resinoso de dupla ativação RelyX ARC (RLX), sob diferentes condições. No primeiro estudo para simular uma restauração indireta foram confeccionados discos com 1,4mm de espessura e 8mm de diâmetro das cerâmicas Empress 2 (EMP) e Empress Esthetic (EST), Duceram Plus (DUC) e resina composta Z250 (Z250). Amostras do RLX com 0,8mm de espessura e 5mm de diâmetro, foram fotoativadas diretamente e indiretamente sob o anteparo, com os aparelhos de fotoativação com lâmpada halógena (QTH - 800mW/cm2) e por diodo emissor de luz (LED - 1100mW/cm2). A potência (mW) das fontes de luz foram medidas com um potenciômetro (Ophir) e o espectro da luz emitida foi registrado com espectrômetro (USB 2000), com e sem a presença do anteparo. No segundo estudo as amostras do cimento foram fotoativadas diretamente com QTH ou LED, recebendo diferentes densidades de energia (10, 20, e 30J/cm2). O grau de polimerização do RLX foi mensurado com a porcentagem do grau de conversão pelo método FT-Raman (CD) e dureza Knoop (KHN). Os resultados obtidos CD (%) e KHN foram submetidos à Análise de Variância e teste de Tukey (5%). De acordo com os resultados destes estudos foi possível concluir que o CD e a KHN podem ser influenciadas pelo tipo de aparelho fotoativador, densidade de energia, assim como, pela presença de restaurações indiretas. / Abstract: The resin cements have been widely used because it provide link between prosthesis and tooth structure and esthetic success. Resin cements are available in chemical-cured, light-cured or dual-cured mode. For this type of cements higher polymerization reflects in improvement on properties. However in many clinical situations polymerization is affected by indirect restoration, tooth or distance of light-curing unit tip to cement. This study evaluated the polymerization of dual-cured resin cement RelyX ARC (RLX) in different simulated clinical conditions. The first study simulated indirect restoration with disks of 1.4mm in thickness and 8mm in diameter of Empress 2 (EMP), Empress Esthetic (EST), Duceram Plus (DUC) ceramics, and resin composite Z250 (Z250). Specimens of RLX with 0.8mm in thickness and 5mm in diameter were light-cured directly and indirectly through restorative materials with quartz-tungsten-halogen (QTH 800mW/cm2) or light-emitting diode (LED 1100mW/cm2). The output power energy (mW) emitted by each light-curing unit was measured with the digital power meter (Ophir) and the spectral output emitted by each unit was registered using a spectrometer (USB 2000), directly and through the disks. In the second study, RLX specimens were lightcured directly with QTH or LED with 10, 20 e 30J/cm2 energy densities. The degree of polymerization achieved by RLX was analyzed by conversion degree (CD) using a FT-Raman Spectrometer and Knoop hardness test (KHN). Data of CD (%) and Knoop hardness (KHN) were submitted to Analysis of Variance and to Tukey's test (5%). According to the results of these studies were unable to conclude that CD and KHN can be influenced by the lightcuring units, light energy density and also by the presence of indirect restorations. / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários

Submitted by Renata Lopes (renatasil82@gmail.com) on 2018-08-22T14:32:57Z No. of bitstreams: 1 weronicajaernevaysilveiramitterhofer.pdf: 1391105 bytes, checksum: 52aca5cc80e8e9f8351f73c962b70c2e (MD5) / Approved for entry into archive by Adriana Oliveira (adriana.oliveira@ufjf.edu.br) on 2018-08-23T12:17:06Z (GMT) No. of bitstreams: 1 weronicajaernevaysilveiramitterhofer.pdf: 1391105 bytes, checksum: 52aca5cc80e8e9f8351f73c962b70c2e (MD5) / Made available in DSpace on 2018-08-23T12:17:06Z (GMT). No. of bitstreams: 1 weronicajaernevaysilveiramitterhofer.pdf: 1391105 bytes, checksum: 52aca5cc80e8e9f8351f73c962b70c2e (MD5) Previous issue date: 2017-12-07 / PROQUALI (UFJF) / Hipótese de estudo: No presente estudo foi hipotetizado que os diferentes protocolos de cimentação adesiva de pinos de fibra de vidro, não afetariam os valores de resistência de união a dentina radicular nas diferentes profundidades do canal radicular. Objetivo: Neste estudo ex vivo foi avaliada a resistência da união por push out de cimentos resinosos na fixação de pinos de fibra de vidro nos terços cervical, médio e apical da raiz dentária. Método: Foram usadas cinquenta raízes bovinas no comprimento de 18mm, que foram tratadas endodonticamente e, sem seguida os condutos foram preparados para fixação de pinos de fibra de vidro por meio de diferentes cimentos resinosos. Os sistemas de cimentação testados foram: ED Primer/Panavia F (Kuraray), Single Bond Multipurpose Plus - SBMP (3M ESPE)/RelyX ARC (3M ESPE), Single Bond Universal - SBU (3M ESPE)/RelyX Ultimate - ULT (3M ESPE), SBMP (3M ESPE)/RelyX Ultimate (3M ESPE), RelyX U200 (3M ESPE). As raízes foram seccionadas para obtenção de fatias com 1mm de espessura dos terços cervical, médio e apical de cada raiz. A mensuração da resistência de união dos diferentes terços foi obtida pelo ensaio de push out (máquina de ensaio Universal EZ-S, Shimadzu). O padrão de fratura foi analisado usando um estereomicroscópio (MZ75; Leica Microsystems, Heerbrugg, Suíça) com aumento de 40x para observar o modo de falha. Sendo classificados em: (1) falha adesiva entre o cimento resinoso e a dentina radicular, (2) falha adesiva entre o cimento resinoso e o pino de fibra de vidro, (3) falha coesiva no cimento resinoso, (4) falha coesiva na dentina radicular e (5) falha mista (envolvendo mais de um padrão anteriormente descrito). Os dados obtidos foram analisados estatisticamente pelo teste ANOVA e teste de Tukey, com nível de significância de 5%. Resultados: Os resultados demonstraram que sistemas de cimentação SBU/ULT e SBMP/ULT apresentaram os maiores valores de resistência de união comparado aos demais grupos experimentais, sem diferença significante entre si. Menores valores de resistência de união foram observados para os demais grupos, também sem diferença entre os mesmos. O terço cervical mostrou a maior resistência de união comparado aos terços médio e apical, os quais não apresentaram diferença significante entre si. Conclusão: o sistema SBU/ULT produz resistência adesiva superior aos demais sistemas testados, exceto SBMP/ULT, com vantagem de reduzidos passos clínicos e, consequentemente menor sensibilidade da técnica adesiva. / Study hypothesis: The hypothesis in the present study was that the different protocols cementation of glass fiberglass would not affect the values of bond strength to root dentin at the different depths of the root canal. Aim: In this ex vivo study was evaluated the bond strength of resin cement fixed by fiber posts in the cervical, medium and apical roots thirds. Method: Fifty bovine incisors roots in length 18mm were prepared to lute fiber posts with different protocols of cementation. The luting agents tested: ED Primer/Panavia F (Kuraray), Scotchbond Multipurpose Plus (3M ESPE)/RelyX ARC (3M ESPE), Single Bond Universal - SBU(3M ESPE)/RelyX Ultimate - ULT (3M ESPE), Scotchbond Multipurpose Plus - SBMP (3M ESPE)/RelyX Ultimate (3M ESPE), RelyX U200 (3M ESPE). The roots were sectioned to obtain 1mm thick slices of the cervical, middle and apical thirds of each root. The bond strength was evaluated with a push-out test (universal testing machine EZ-S, Shimadzu). Data were statistically analyzed by ANOVA and Tukey’s test with a significance level of 5%. Results: The results showed that SBU/ULT and SBMP/ULT cementation systems had the highest bond strength values compared to the other experimental groups, with no significant difference between them. Lower values of bond strength were observed for the other groups, also with no difference between them. The cervical third showed the highest bond strength compared to the middle and apical thirds, which did not present significant difference between them. Conclusion: the SBU/ULT system produces superior adhesive resistance to the other systems tested, except SBMP/ULT, with the advantage of reduced clinical steps and consequently lower sensitivity of the adhesive technique.