Orientadores: Luis Alexandre M. S. Paulillo, Jaime Aparecido Cury / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T18:00:18Z (GMT). No. of bitstreams: 1 Mendonca_CarlotaCristinaLeite_D.pdf: 1552031 bytes, checksum: 27cf0ef67462150273284dc1c4caabbe (MD5) Previous issue date: 2002 / Resumo: O objetivo desta pesquisa foi avaliar a deposição superficial de placa bacteriana in situ sobre dois materiais estéticos indiretos, apresentando 2 texturas superficiais - lisa e rugosa - na presença ou não de sacarose. Assim, foram testadas a cerâmica Duceram LFC e a resina composta laboratorial Solidex. Para a avaliação do acúmulo de placa bacteriana foram selecionados 12 voluntários, para os quais foram confeccionados dispositivos palatinos em acrílico, onde foram fixados 4 corpos de prova correspondentes aos grupos experimentais: (1) Cerâmica lisa (glaze); (2) Cerâmica rugosa (desgaste com ponta diamamtada); (3) Resina composta indireta lisa (polimerizada em contato com a tira matriz) e (4) Resina composta rugosa (desgaste com ponta diamamtada). Os voluntários utilizaram a placa palatina 3 dias por semana, durante 8 semanas, divididas em 2 fases distintas: com sacarose e sem sacarose, 4 semanas para cada fase. Em uma etapa, metade dos voluntários realizou imersões do aparelho em sacarose a 20%, 8 vezes ao dia e a outra metade realizou as imersões em água. Na 2a etapa, esta situação foi invertida. No 4o dia, a placa formada sobre cada corpo de prova foi extraída em NaOH 1,0M e quantificada em espectrofotômetro. Os resultados obtidos apresentaram efeito estatístico significativo para os fatores material e superfície, e não significativo para o fator sacarose. Entre os materiais estudados, a cerâmica com superfície lisa, grupo (1) apresentou as menores médias em relação ao acúmulo de placa dental, sem diferença estatística para o grupo (2). As maiores médias foram obtidas pelo grupo (4), que apresentou diferença estatística significativa em relação aos demais grupos experimentais / Abstract: The aim of this study was to evaluate in situ the plaque retention on indirect aesthetic restorative materials presenting rough or smooth surfaces, after sucrose exposuring or not. Duceram LFC ceramic and Indirect composite resin Solidex were tested. Twelve subjects were request and asked to wear palatal appliances containing four samples corresponding the four experimental groups: (1) Ceramic (glaze); (2) Rough ceramic (finishing with diamond bur); (3) Indirect composite resin (polimerized in contact with Mylar Strips) and (4) Rough indirect composite resin (finishing with diamond bur). The experimental period was three days per week, divided into two distinct phases, during eight weeks: with or without sucrose exposuring. Each phase corresponds four weeks. Either the appliances were immersed eight times a day into 20% sucrose solution, to induce plaque formation or into water. The quantity of dental plaque formed on samples was extracted with Sodium Hidroxide solution 1,0 M and analysed by spectrophotometer. The results presented statistical main variances for the factors material and surface, and no significance for the fator sucrose. Among the studied samples, the ceramic blocks with smooth surface, group (1) showed the smalest mean considering plaque retention, no statistical diference was observed to group (2). In the other side, Group (4) presented larger amounts of dental plaque acumulation differing statistically from the other groups / Doutorado / Dentística / Doutor em Clínica Odontológica

Orientador: Simonides Consani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-17T16:31:27Z (GMT). No. of bitstreams: 1 Fugolin_AnaPaulaPiovezan_M.pdf: 7087256 bytes, checksum: 828f5aed76c8ac133d37deb6cf423e11 (MD5) Previous issue date: 2011 / Resumo: O objetivo neste estudo foi investigar a influência de diferentes irradiâncias e de energia emitida pelo fotoativador na dureza Knoop, grau de conversão e contração de polimerização de compósitos odontológicos com diferentes partículas de carga. Anéis de latão de 12 mm de diâmetro externo, 8 mm de diâmetro interno e 2 mm altura foram preenchidos com os compósitos Filtek Supreme XT® (ESPE 3M) e Charisma® (Heraeus Kulzer), ambos na cor A2. O aparelho utilizado foi o LED Bluephase G2 (Ivoclar-Vivadent), com tempo de fotoativação de 20 s e irradiância conforme o protocolo: grupos A e D- 300 mW/cm²; grupos B e E- 650 mW/cm² e grupos C e F- 1200mW/cm², sendo n = 5. Depois da polimerização, cada conjunto (matriz e amostra) foi submetido aos procedimentos de acabamento e polimento com lixas de carboneto de silício. A armazenagem foi em estufa a 37ºC por 24 horas, dispostos em recipiente a seco e no escuro. Após armazenagem, as superfícies de topo e base das amostras foram submetidas ao teste de dureza Knoop em durômetro, onde foram efetuadas 5 penetrações em cada região, com carga de 50 gf por 5 s. As amostras submetidas ao ensaio de dureza Knoop foram analisadas em microscopia eletrônica de varredura para verificar o nível de adaptação material-matriz. Por meio do programa UTHSCSA ImageTool foi mensurada a largura das fendas. Para avaliar o grau de conversão outras amostras foram confeccionadas, as quais foram avaliadas pelo FTIR com ATR. Os dados foram submetidos à ANOVA múltiplos fatores e teste de Tukey (5%). Os resultados mostraram que: A dureza Knoop do Filtek Supreme XT foi significativamente maior que do Charisma, independente do local e irradiância. Independente do material e local, as irradiâncias de 1200 mW/cm² e 650 mW/cm² mostraram valores de dureza estatisticamente similares, sendo ambas significativamente maiores aos de 300 mW/cm². Para Charisma houve diferença estatística significante entre topo e base nas irradiâncias de 300 mW/cm² e 650 mW/cm². No Filtek Supreme XT houve diferença estatística significante entre topo e base somente na irradiância de 300 mW/cm². Independente do local e irradiância, o grau de conversão do Charisma foi estatisticamente maior que do Filtek Supreme XT, exceto na irradiância de 650 mW/cm², onde os valores foram estatisticamente similares. No Charisma, a irradiância de 1200 mW/cm² proporcionou grau de conversão significativamente maior que 300 mW/cm² e 650 mW/cm², ambos similares entre si. No Filtek Supreme XT, a irradiância de 1200 mW/cm² proporcionou valor significativamente maior, 300 W/cm² menor e 650 mW/cm² valor intermediário. Independente da irradiância, para Filtek Supreme XT não houve diferença entre topo e base. Para Charisma, 300 mW/cm² e 650 mW/cm² apresentaram diferença estatística significante entre topo e base, sendo que em 1200 mW/cm² não houve diferença estatística significante. Independente da irradiância, a contração do Charisma foi significativamente maior que do Filtek Supreme XT. Independente do material, a contração promovida pelas irradiâncias foi similar. Os resultados deste estudo mostraram que a irradiância influenciou na dureza Knoop e no grau de conversão, não causando efeito na contração dos compósitos. / Abstract: The aim of this study was to investigate the influence of both energy and power density (of different levels) emitted by light curing unit in the Knoop hardness, conversion degree and polymerization shrinkage of dental composites with different types of filler particles. Brass rings of 12mm outside diameter, 8mm internal diameter and 2mm height were filled with the composites Filtek Supreme XT® (3M ESPE) and Charisma (Heraeus Kulzer), both color A2. The light curing unit Bluephase G2 LED (Ivoclar-Vivadent) was used for 20s with irradiance according to the protocol; groups A and D ¿ 300 mW/cm², groups B and E ¿ 650 mW/cm² and groups C and F ¿ 1200 mW/cm². After polymerization, the sets (matrix and sample) were finished and polished with silicon carbide sandpaper and stored for 24 hours at 37°C in dark and dry container. After his period the specimens were evaluated for their hardness in an indenter, where top and bottom surfaces were submitted to five penetrations, with a load of 50gf for 5 s. Scanning electron microscopy (SEM) of these samples was carried out to check the gap between composite and matrix and the extent of crack were measured using the program UTHSCSA ImageTool. FTIR with ATR techniques assessed the degree of conversion of new samples. The data were analyzed by multiple factors ANOVA and Tukey test (p ? 0.05). In the results Filtek Supreme XT showed hardness values significantly higher than those of Charisma, regardless the location and the irradiance. At irradiances of 1200 mW/cm² and 650 mW/cm² showed hardness values statistically similar and significantly higher at 300 mW/cm², regardless the material and the location. Charisma showed a statistically significant difference between top and bottom in the irradiances 300 mW/cm² and 650 mW/cm². Filtek Supreme XT showed significant difference between top and bottom only in the irradiance of 300 mW/cm². The results for degree of conversion showed that, regardless the location and irradiance, Charisma had statistically higher values than Filtek Supreme XT, except for the irradiance of 650 mW/cm², where the values of the composites were statistically similar. At the power density of 1200 mW/cm², Charisma achieved values significantly higher than 650 mW/cm² and 300 mW/cm². At the power density of 1200 mW/cm² Filtek Supreme XT showed the highest conversion values, while at 300 mW/cm² showed the lowest values, and at 650 mW/cm² intermediate values were found. Regardless the irradiance, Filtek Supreme XT showed no difference between top and bottom. Charisma, at 300 mW/cm² and at 650 mW/cm² showed statistically significant difference between top and bottom, and at 1200 mW/cm² the difference was not statistically significant. Charisma showed significantly higher values of contraction than Filtek Supreme XT, regardless the irradiance. Regardless the material, no statistical difference was found for values of contraction for the evaluated irradiances. The findings of this study showed that the power density influenced the hardness and the degree of conversion, but not the contraction. / Mestrado / Materiais Dentarios / Mestre em Materiais Dentários

Propôs-se avaliar a influência de diferentes fontes de luz fotoativadoras na micromorfologia e na resistência de união adesiva de restaurações de resina composta. Selecionaram-se terceiros molares hígidos que receberam preparos cavitários classe I (6,0 mm x 4,5 mm; 2,5 mm profundidade). A resina composta (Filtek Z250 - RC) foi inserida em incremento único após a aplicação e polimerização do sistema adesivo (Adper Single Bond - SB). Os materiais restauradores foram fotoativados com os seguintes aparelhos: XL 3000 (QTH: 540 mW/cm2); Elipar FreeLight 2 (LED: 750 mW/cm2) e Arc Light IIM (PAC: 2.130 mW/cm2). Nove grupos experimentais foram avaliados de acordo com as combinações de fonte de luz para fotoativar SB/RC: QTH/QTH; QTH/LED; QTH/PAC; LED/LED; LED/QTH; LED/PAC; PAC/PAC; PAC/QTH; PAC/LED. Para a análise da micromorfologia foi utilizada microscopia de fluorescência (Laser de Fóton Duplo), sendo que um corante fluorescente vermelho (Rodamina B) foi adicionado ao sistema adesivo. Além disso, utilizou-se uma solução de corante fluorescente verde (Dextran- Fluoresceína), que foi aplicada na câmara pulpar durante 4 horas, para que se difundisse em direção à interface. Os dentes foram então lavados, incluídos, seccionados e analisados microscopicamente. Os parâmetros analisados foram: espessura da camada de adesivo, espessura e qualidade da camada híbrida, micropermeabilidade, qualidade e habilidade de selamento dos tags de resina e, ainda, localização e extensão de fendas. Para o teste de resistência adesiva, os dentes foram restaurados, de acordo com as combinações de fonte de luz, e armazenados por 24 horas a 37 °C. Em seguida os dentes foram seccionados e submetidos ao teste de microtração. Realizou-se ainda a análise dos parâmetros de cinética de conversão de monômeros (conversão total, taxa máxima de conversão, conversão na máxima taxa, tempo em que ocorreu a máxima taxa e relação conversão na máxima taxa/conversão total) em um espectrofotômetro de raios infravermelho, ao qual foram aplicados os mesmos materiais restauradores que foram polimerizados com as diferentes fontes de luz. Para as avaliações qualitativas foi realizado o teste estatístico Kruskal-Wallis e o teste de Dunnet para comparações múltiplas (&#945; = 0,05). Para as avaliações quantitativas foi realizada análise de variância e teste de Tukey para comparações múltiplas (&#945; = 0,05). Da análise dos resultados, observou-se que as fontes de luz utilizadas influenciaram nos parâmetros de cinética de conversão de monômeros. De forma geral, ocorreu uma relação inversa entre a conversão total e a densidade de potência quando se polimerizou o sistema adesivo. Na resina composta base, houve uma relação direta. Para ambos os materiais houve uma maior taxa máxima de conversão, em um menor tempo, proporcional à densidade de potência dos aparelhos. Quanto aos parâmetros de micromorfologia, não se observou diferença siginificante entre os grupos experimentais em relação à espessura e qualidade de camada híbrida. Em relação à espessura da camada de adesivo, observaram-se maiores espessuras quando o sistema adesivo foi polimerizado com o PAC. Para a micropermeabilidade, também não se observou diferença entre os grupos. Também, não se observou diferença siginificante em relação à qualidade e habilidade de selamento dos tags de resina. Em relação à presença de fendas, quando o PAC polimerizou o sistema adesivo, menores porcentagens de piores escores e menores extensões de fendas foram observadas. A combinação PAC/QTH apresentou valores significantemente maiores de resistência adesiva e LED/QTH, as menores. A espessura da camada de adesivo, localização de fendas e resistência adesiva foram significantemente influenciados pela fonte de luz que polimerizou o sistema adesivo, sendo que, quando o PAC foi utilizado, melhores resultados foram observados. As combinações de mesma fonte de luz apresentaram, de forma geral, resultados similares. As diferentes fontes de luz fotoativadoras influenciam na resistência de união adesiva e em alguns parâmetros da micromorfologia da interface de restaurações de resina composta. / The purpose of the present in vitro study was to evaluate the effect of different light-curing sources on interfacial micromorphology and on bond strength of resin composite restorations. Class I preparations (6.0 mm long, 4.5 mm wide, 2.5 mm deep) were made in extracted human third molars, after abrading cusps, following university approved HAC guidelines. Restorations were placed in bulk, using a dentin bonding agent (DBA) / resin composite (RC): Adper Single Bond / Filtek Z250. Restoratives were light-cured as follows: XL 3000 (QTH: 540 mW/cm2); Elipar FreeLight2 (LED: 750 mW/cm2); Arc Light II (PAC: 2,130 mW/cm2). Nine experimental groups were developed from the different light combinations with respect to curing the DBA/COMP: QTH/QTH; QTH/LED; QTH/PAC; LED/LED; LED/QTH; LED/PAC; PAC/PAC; PAC/QTH; PAC/LED. Fluorescing agent (Rhodamine B) was added to the DBA, highlighting the bonded interface and surrounding structures. A different colored dye (FTIC-Dextran) was placed in the pulp chamber for 3 hours, allowing time to diffuse toward the different-colored interface. The teeth were then embedded, sectioned, and microscopically analyzed using fluorescence microscopy (Two-Photon Laser) at 40x magnification. Micromorphology quantitative and qualitative evaluations were: quality and thickness of hybrid layer; micropermeability test, adhesive layer thickness; quality and sealing ability of resin tags; location and extension of gaps. For bond strength test, the same experimental groups were obtained. After restorative procedures, the teeth were stored in distilled water for 24 h at 37 °C. After this time period, resin layers were added to the restoration surface (providing same dentin/resin length), and then sectioned and subjected to microtensile test in a universal testing machine. Kinetics conversion parameters were also evaluated in an FT-IR spectrophotometer (total conversion, maximum rate of cure, time when maximum rate occurred, conversion at maximum rate, conversion at maximum rate/ total conversion ratio). The same restorative materials were applied to the ATR device, attached to the spectrophotometer, and then polymerized according to manufacturer’s instructions. Data was statistically analyzed as mentioned below. Statistical analyses revealed that different light sources influenced the kinetics conversion (one-way ANOVA, p< 0,05). It was found an inverse relation between power density and monomer conversion when polymerizing DBA. For resin composite (bottom), there was a positive relation between power density and total conversion. High intensity, broad banded PAC light produced higher maximum rate of cure (in %/s), in shorter times. In terms of micromorphology, no significant difference was found in terms of quality and thickness of hybrid layer (two-way ANOVA, p> 0.05). No significant difference was noted for in quality and in sealing ability of tags (Kruskal Wallis, p> 0.05). QTH/QTH presented higher percentages of best scores for both parameters. Adhesive layers were found to be significantly thicker when PAC light was used to polymerize DBA. Even thought it was also found no significance in micropermeability scores (Kruskal Wallis, p> 0.05), it was found higher percentage of best scores for control QTH/QTH. Photo-polymerizing DBA using PAC produced lower incidence of gap formation, irrespective of RC curing source. Combination PAC/QTH presented significantly higher bond strength and LED/QTH, the lower (two-way ANOVA, Dunnet’s pos-hoc test, p< 0.05). Part of interfacial micromorphology parameters and bond strength were more dependent on the photo-polymerization source used for dentin-bonding agent than for resin composite. Photo- polymerizing DBA using PAC produced best results for adhesive thickness, gap location, and bond strength. Although QTH/QTH, LED/LED, and PAC/PAC combinations produced similar general results, it was found inherent characteristics when analysing tested parameters. Different light curing units influence bond strength and some parameters of micromorphology.

Avaliou-se a resistência adesiva ao cisalhamento de uma resina composta contaminada por saliva, com adição de novo incremento do mesmo material. 40 corpos-de-prova de uma resina composta nano-híbrida, confeccionados em uma matriz de resina epóxica, foram divididos em quatro grupos, cada um recebendo um tratamento de superfície. Em um dos grupos, a superfície não foi contaminada (Grupo 1 - controle). Para a confecção do segundo segmento do corpo-de-prova, utilizou-se uma matriz de Teflon de 3,5mm de diâmetro por 3,0mm de altura. Nos demais grupos, a superfície da resina composta foi contaminada com saliva e seca com ar comprimido, sendo os tratamentos estabelecidos da seguinte forma: Grupo 2 - resina composta inserida e polimerizada sobre a superfície contaminada; Grupo 3 - condicionamento com ácido fosfórico a 35%, aplicação de adesivo e inserção de resina composta; Grupo 4 - asperização com ponta diamantada, condicionamento com ácido fosfórico a 35%, aplicação de adesivo e inserção de resina composta. Após a confecção, os espécimes foram armazenados em água a 37oC durante 24h, sendo em seguida montados em uma máquina universal de ensaios para realização dos testes de resistência ao cisalhamento. Os resultados foram submetidos à análise de variância a um critério e ao teste de Tukey para comparação entre os grupos. Não houve diferença entre os grupos 3, 4 e controle (p < 0,05). A contaminação da superfície da resina com saliva (Grupo 2) diminuiu significativamente a resistência de união (p < 0,05). A análise em MEV dos espécimes do grupo 2 demonstrou a ocorrência de fraturas na interface adesiva em quase todos os corpos-de-prova (80%). Fraturas coesivas da resina inserida na matriz de resina epóxica puderam ser observadas em todos os espécimes dos Grupos 3 e 4. O método que emprega limpeza superficial com ácido e aplicação de um sistema adesivo demonstrou ser efetivo na recuperação da resistência adesiva a valores semelhantes à resistência coesiva do material / Shear bond strength between the contaminated composite resin surface and a new increment of the same material was analysed. Forty specimens of a nanohybrid composite, were divided into four groups. Each group received a surface treatment. In one of the groups, there was no surface contamination (Group 1 - control). The new increment of composite resin was inserted by placing a Teflon matrix (3.5mm height, 3mm diameter) over the already polymerized composite surface. For the other groups, the polymerized composite surface was contaminated with saliva and dried with air. Surface treatments were performed in the following way: Group 2 - new increment was inserted and polymerized directly on the contaminated surface; Group 3 - contaminated surface was treated with 35% phosphoric acid etching and adhesive was applied prior to the insertion of the new increment; Group 4 - diamond bur roughening, 35% phosphoric acid etching, adhesive application and insertion of the new composite increment. Specimens were stored in water at 37oC for 24h. After this period, specimens were mounted in a universal testing machine for the shear bond strength tests. Results were submitted to one way anova and Tukey test multiple comparison. No significant differences were detected between Groups 3, 4 and control (p < 0.05). Saliva contamination of resin surface (Group 2) significantly reduced shear bond strength (p < 0.05). SEM analysis in Group 2 demonstrated fractures at the interface in 80% of the specimens. Cohesive fractures in first increment of resin composite was observed in all specimens in Groups 3 and 4. Decontamination of resin surface with phosphoric acid followed by adhesive application, was an effective method to improve shear strength, reaching similar numbers to the cohesive resistance of the material

Este estudo teve a finalidade de verificar influência de diferentes tipos de pinos intra-radiculares sobre a resistência à fratura de um material restaurador coronário, utilizando o teste de tração diametral. Foram confeccionados 70 corpos de prova divididos em 7 grupos: G1. Compósito (Tetric Ceram – Ivoclar/Vivadent) (Grupo Controle); G2. Compósito e pino VectrisPost (Ivoclar/Vivadent); G3. Compósito e pino Fiber-Post (Jeneric/Pentron); G4. Compósito e pino Æstheti-Plus (Bisco); G5. Compósito e pino Light-Post (Bisco); G6. Compósito e pino Dentorama (Svenska) e G7. Compósito e pino ParaPost (Còltene/Whaledent). Todos os grupos foram submetidos ao ensaio de tração diametral em uma máquina de ensaios Instron, modelo 8501, até a fratura. A média dos grupos em MPa foi: G 1- 49,64 (3,36); G 2- 29,77 (3,36); G 3- 31,9 (2,39); G 4- 28,92 (2,20); G 5- 34,26 (3,37); G 6-33,45 (2,46) e G 7- 27,90 (2,40). A análise estatística dos dados nos permitiu concluir que: os pinos utilizados não reforçaram a resina composta; os pinos Light-Post, Dentorama e Fiber-Post apresentaram os melhores valores de adesividade ao material de reconstrução coronária e que o pino metálico ParaPost apresentou o menor valor de adesão à resina de reconstrução coronal. / The purpose of this study was to determine the influence of different types of posts on the fracture strength of a resin composite core material using the diametral tensile strength test. Seven groups of specimens were prepared each with 10 cylindrical specimens made of one composite material (Tetric Ceram, IvoclarVivadent) as follows: Group 1- Control group of composite only specimens; Group 2-Composite and VectrisPost (IvoclarVivadent); Group 3- Composite and Fiber-Post (Jeneric/Pentron); Group 4- Composite and Æstheti-Plus post (Bisco); Group 5- Composite and Light-Post (Bisco); Group 6- Composite and Dentorama post (Svenska) and group 7- Composite and ParaPost (Coltene/Whaledent). Following storage specimens were subjected to compressive loading in an Instron testing machine (model 8501) until failure occurred. Means and standard deviations of diametral tensile strengths in MPa were: Group 1- 49,64 (3,36); Group 2- 29,77 (3,36); Group 3- 31,9 (2,39); Group 4- 28,92 (2,20); Group 5- 34,26 (3,37); Group 6- 33,45 (2,46) and Group 7- 27,90 (2,40). Statistical analysis revealed significant differences in mean diametral tensile strengths among the groups. It is concluded that the use of posts did not reinforce the composite resin cores. Among the post/core groups Light-Post, Dentorama post and Fiber-Post resulted in the highest values of tensile strength while ParaPost resulted in the lowest value of tensile strength.

Foram analisadas in vitro a dureza superficial, a contração de polimerização e a rugosidade de 29 resinas compostas. Foram confeccionados 3 corpos-de-prova para cada material, com fotopolimerização por 80 segundos; após mais 5 minutos, determinou-se a dureza superficial Rockwell 30T; os espécimes foram então armazenados em água desionizada, a 37ºC, durante 168 horas, quando nova leitura da dureza foi realizada. Para avaliação da contração de polimerização, foram confeccionados 5 corpos-deprova para cada material; cada resina era inserida em uma matriz metálica, com uma cavidade em forma de “meia cana", cujas paredes das extremidades planas eram paralelas entre si, com fotopolimerização por 40 segundos; após 10 minutos, removia-se a amostra da matriz, cujo comprimento era medido para se estabelecer a contração inicial ocorrida; os espécimes eram então armazenados em estufa a 37ºC, durante 168 horas (1 semana), quando nova medida era tomada, para se determinar a contração final da resina. Os mesmos corpos-de-prova usados nos testes de dureza, após desgaste com lixas de papel até a de n.º 1.500, foram analisados num rugosímetro. Estatisticamente, todas as resinas mostraram aumento da dureza e da contração de polimerização, da medição imediata para a com 168 horas. Em termos globais, as que apresentaram os melhores resultados, analisando-se as três características simultaneamente, foram a Z-100 e a P-60, enquanto as com o pior desempenho foram a Solitaire e a Helioprogress. / In vitro surface hardness, polimerization shrinkage and roughness of 29 composite resins were stablished. For each material, it were made 3 specimens, photocured by 80 seconds; 5 minutes later, Rockwell 30T surface hardness was determined; the specimens were then imersed in deionized water, at 37ºC by 168 hours, when a new evaluation of hardness was effectued. In evaluating polymerization shrinkage, 5 specimens were made for each material; each resin was inserted in a metallic matrix, in which there was a cavitiy with the shape of a hemi-cilinder, whose flat surfaces were paralel between itself, com photopolimerization for 40 seconds; 10 minutes later, the lenght was measured to determine the inicial shrinkage; specimes were then stored in a stove, at 37ºC for 168 hours, when a new length measuring was effectued to determine the final shrinkage. The same specimens used for hardness were abraded with sand paper (till 1,500 mesh) and evaluated for roughness with a rugosimeter. All resins showed an increase in hardness and in polymerization shrinkage, since the inicial evaluation to that effectued 168 hours later. In a global way, by a simultaneous analysis of the 3 characteristics, the best results were presented by Z-100 and P-60; Solitaire and Helioprogress had the worst performance.

O objetivo deste estudo foi avaliar o efeito do bisel na infiltração marginal em restaurações de resina composta em cavidades Classe IV sem e com bisel em todo ângulo cavossuperficial, submetidas à ciclagem térmica e mecânica. Foram preparadas nas mesmas dimensões, variando na ausência ou presença de bisel, 30 cavidades de Classe IV em incisivos inferiores de bovinos. No grupo 1 não foi realizado bisel e no grupo 2 o bisel foi realizado com uma extensão aproximada de 1,0 mm ao redor de todo o ângulo cavossuperficial. As cavidades foram restauradas com o mesmo sistema adesivo e resina composta Single Bond Z-250 (3M). Após a restauração foi executado um acabamento inicial com lâminas de bisturi. Em seguida, os dentes foram armazenados em água deionizada a uma temperatura de 37ºC durante sete dias. No sétimo dia foi realizada a complementação do acabamento e polimento. Os grupos foram submetidos à ciclagem térmica com o tempo de imersão de 30 segundos em cada banho, a uma temperatura de 5 ºC e 55ºC, por 500 ciclos. Logo após, os corpos-de-prova foram submetidos à ciclagem mecânica, utilizando a máquina universal de ensaio EMIC programada para executar um carregamento e descarregamento axial de compressão na face lingual de cada dente restaurado. Inicialmente, foi aplicada uma carga ascendente de 1 a 10 kgf e descendente de 10 a 1 kgf durante 30 segundos, perfazendo um total de 100 ciclos para cada corpo-de-prova. Durante este ensaio, a porção coronária dos dentes ficou submersa em fucsina básica a 0,5 %. Após o término da ciclagem mecânica, os corpos-de-prova permaneceram por mais 24 horas mergulhados na mesma solução e, em seguida, foram lavados em água corrente por 12 horas. Cada dente foi seccionado em fatias transversais de aproximadamente 1,0 mm, sendo selecionada a fatia que apresentou maior grau de infiltração. Para avaliação da infiltração marginal foi utilizado um programa de análise de imagens, Image Tools, no qual foi medida a extensão da penetração do corante em milímetros. Os valores em milímetros da extensão de penetração do corante foram para os grupos 1 e 2; sendo 1,02 mm e 0,0 mm respectivamente. Aplicando o teste estatístico, verificou-se que houve diferença estatisticamente significante (p < 0,05) entre os valores de infiltração do grupo 1 (ausência de bisel) com os do grupo 2 (presença de bisel). Concluiu-se que a presença do bisel diminui significativamente a infiltração marginal nas restaurações de Classe IV, restaurações estas confeccionadas com o sistema restaurador adesivo e resina composta. / The purpose of this study was to evaluate the effect of bevel in the microleakage in restorations of composite resin, in cavities Class IV with bevel and without bevel around all the cavosurface margins, submitted to a thermal and mechanical cycled. The same dimensions was prepared, varying in the bevel presence or absence, thirty cavites of Class IV bovine teeth. Thereby, in group 1 the bevel was not done and in group 2 the bevel of 1 mm length was done around all the cavosurface margins. The cavities was restored with Single Bond / Z-250 (3 M). After restored, all restorations were finished with a scalpel. Afterwards, they were stored in deionize water at 37º C for seven days followed by the polishing procedures. All the groups were submitted to thermocycling 500 times between 5 ºC and 55 ºC, in a 30 seconds dwell time. For the mechanical cycled test, it was used the EMIC machine which was programmed to execute an axial load of 10 kgf, during 30 seconds in the lingual surface of the restorations. During the mechanical cycled test, the crown of the teeth remained submerse in a 0,5% basic fuchsin, and continued submerse until 24 hours had been completed. After that, the teeth were left 12 hours in the running water, followed by the section. Each tooth was parted in transversal sections with approximately 1,0 mm and the section with the higher amount of dye penetration was selected. It was used a program (Image Tool) to make possible an analysis of the images, to determined the dye penetration in milimeters. Through the results it is clearly that, there was a significant statistic difference (p < 0,05) between group 1 (absence of bevel) and group 2 (presence of bevel), which had 1,02 mm and 0,0 mm averages of dye penetration respectively. It was concluded that the procedure of bevel execution reduce expressively the microleakage around the margins of the restorations.

Orientador: Aldo Eloizo Job / Banca: Clodoaldo Saron / Banca: Elidiane Cipriano Rangel / Banca: Deuber Lincon da Silva Agostini / Banca: Maria Odila Hilario Cioffi / O Programa de Pós Graduação em Ciência e Tecnologia de Materiais, PosMat, tem caráter institucional e integra as atividades de pesquisa em materiais de diversos campi / Resumo: O presente trabalho teve por objetivo o desenvolvimento de compósitos poliméricos através da mistura de resíduo de couro (RC), a ser utilizado como carga, com elastômeros termoplásticos obtidos por meio da compatibilização de polietileno de baixa densidade (PEBD) com borracha natural (BN) obtida a partir do látex de seringueira (clone de Hevera Brasiliensis), juntamente com agentes de cura, visando à vulcanização da BN, para que desta forma se obtivesse melhores propriedades do material. As amostras foram produzidas em um Reômetro de Torque (HAAKE, utilizando rotores tipo roller. Após o processo de reometria, as amostras foram termoprensadas para que ocorresse a vulcanização da fase elastomérica e moldagem dos corpos de prova. Os TPEs e os compósitos foram caracterizados por meio de análises mecânicas, morfológicas, estruturais e térmicas. Diante dos resultados obtidos, pretende-se direcionar o novo material para aplicações tecnológicas a fim de ser utilizado na fabricação peças de automóveis, engrenagens, entre outros. Com este novo material visa-se também direcionar uma aplicação ao resíduo de couro bovino, que é um material abundante e indesejável gerado na industrialização do couro, que pode causar sérios danos ambientais devido ao crono presente em sua estrutura / Abstract: This work aimed at the development of polymr composites by mixing leather waste (RC), to use as filler, with thermoplastic elastomers obtained by the compatibility of low density polyethylene (LDPE) with natural rubber (NR) obtained latex form the rubber tree (NR) obtained latex from the rubber three (Hevea brasileiensis clone), together with curing agents, vulcanizing order to BN, for which thereby obtain the best properties of the material. The samples were produced on a HAAKE torque rheometer using roller type rotors. After the processes of rheometer, samples were pressed to occur term vulcanization of the elastomeric phase and molding of speciments. The TPEs and composites were characterized by means of mechanical, morphological, structural and thermal analysis. Based on these results, we intend to drive new material for technological applications to be used in manufacturing automobile parts, gears, among others. With this new material also pretends to direct an application to the reside of bovide leather, which is an abundant and undersirable material generated in the manufacturing of leather, which can cause serious environmental damage due to the chromium present in its structure / Doutor

Orientador: João Neudenir Arioli Filho / Banca: Ana Carolina Pero Vizoto / Banca: Raphael Freitas de Souza / Resumo: O propósito do presente estudo foi avaliar a resistência à fratura de coroas provisórias implanto - suportadas unitárias imediatas anteriores confeccionadas com facetas de resina acrílica e resina composta após diferentes tratamentos superficiais. Para isto 64 coroas provisórias implanto-suportadas foram confeccionadas e divididas 8 grupos experimentais (n=8), de acordo com o material de confecção, resina acrílica(RA) no grupo 1 ou resina composta(RC) nos grupos 2 a 8, e, tratamentos superficiais realizados na faceta: 1- sem tratamento, 2- sem tratamento, 3- metilmetacrilato(MM), 4- primer para metal(PM), 5- sistema adesivo(SA), 6- jateamento com óxido de alumínio(Al3O2)+MM, 7- Al3O2+PM e 8- Al3O2+SA . Os espécimes foram submetidos a 1x104 ciclos térmicos variando entre duas temperaturas (5ºC e 55 ºC) e posteriormente ao ensaio de resistência à fratura, com carga aplicada com velocidade de 0,5 mm/ min até a ocorrência de falha. Quando os valores de carga máxima para fratura foram analisados, o grupo 1 (controle) obteve os maiores valores (332 N média e ± 67 desvio padrão). Comparados ao controle, os grupos 2, 3, 4, 6 e 7 se mostraram estatisticamente diferentes (P < 0.05), com valores de carga máxima para fratura inferiores ao controle. Por outro lado os grupos 5 e 8 foram semelhantes e não demonstraram diferença estatística quando comparados com o controle (P > 0.05). A partir da análise dos dados, de acordo com a metodologia utilizada, pode-se concluir que o tratamento com sistema adesivo é uma boa opção para uso clínico, aumentando a resistência das coroas provisórias implanto-suportadas confeccionadas com resina acrílica e resina composta. / Abstract: The purpose of this study was to evaluate the fracture resistance of the immediate implant-supported provisional crown prepared with denture tooth and composite resin, after different surface treatments. Sixty-four screw-retained implant-supported provisional crown were divided into 8 groups (n= 8) according to the crown material, acrylic resin(AR) group1 or composite resin(CR) groups 2 to 8 and surface treatment performed: 1- no surface treatment, and 2- no surface treatment, 3- methyl methacrylate(MM), 4- metal primer(MP), 5- bonding system(BS) 6- alumina air abrasion (Al3O2) +MM, 7- Al3O2+MP and 8- Al3O2+BS. Specimens were subjected to 1x104 thermal cycles at two temperatures (5ºC and 55 ºC) and after that was performed the static mechanical test with a crosshead speed of 0.5 mm/ min until the sample fracture. When the maximum load to failure was analyzed the group 1 (control) had the highest values (332 N ± 67 mean and standard deviation). Compared to the control, groups 2, 3, 4, 6 and 7 were statistically different (P <0.05), with lower values of maximum than the control. Moreover the 5 and 8 groups were similar and showed no statistical difference when compared with the control (p> 0.05). From the analysis of the data in accordance with the methodology used, it can be concluded that the treatment with bonding system is a good option for clinical use, increasing the resistance of implant-supported provisional crowns made with acrylic resin and composite resin. / Mestre

Orientador: Marcelo Ferrarezi de Andrade / Coorientador: Alessandra Nara de Souza Rastelli / Banca: Simone Xavier Silva Costa / Banca: Hugo Henriques Alvim / Banca: Andrea Abi Rached Dantas / Banca: Edson Alves de Campos / Resumo: O objetivo deste trabalho foi avaliar diferentes propriedades de resinas compostas comerciais e uma resina composta experimental contendo dióxido de zircônia, por meio de 3 estudos: (1): avaliar a fluorescência por meio de imagens conjugadas ao processamento digital e estabilidade de cor após 24 horas de imersão em saliva artificial e envelhecimento acelerado em câmara ultravioleta (UV), (2): avaliar o grau de conversão (GC%) por meio de espectroscopia por FTIR e (3): avaliar sorpção de água por meio de imersão em saliva artificial nos períodos de 1, 3, 14, 21, 30 e 60 dias. Para os três estudos, corpos-de-prova para cada resina foram confeccionados em matriz metálica circular com dimensões específicas para cada teste. Para fotoativação, um LED Celalux® (Voco, 776 mW/cm²) foi utilizado por 40 segundos. No primeiro estudo, cinco dentes caninos foram utilizados como referência para análise da fluorescência e oito corpos-de-prova para cada resina composta (n=48) foram confeccionados. A análise digital da fluorescência foi realizada com auxílio de câmara CCD conectada a computador, sob iluminação com LED UV. Foram coletadas 16 imagens para cada corpo-de-prova, e estas foram processadas matematicamente, quantificando a intensidade de fluorescência em escala de cinza. Na estabilidade de cor, oito corpos-de-prova para cada resina (n=48) foram submetidos ao envelhecimento artificial, inicialmente por meio de imersão em saliva por 24 horas e depois em câmara ultra-violeta (UV). As mensurações foram obtidas por meio de colorímetro (Minolta, CM 2600 d, Japão), as quais foram registradas no próprio display do equipamento e transferidos a microcomputador mediante um software específico que registrou os valores de cor de acordo com o Sistema CIE- L*a*b*. Os dados para fluorescência e estabilidade de cor foram... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The aim of this study was to evaluate different properties of commercial and experimental composites resins through three studies: (1): to evaluate the fluorescence by digital images and color stability after 24 hours immersion in artificial saliva and accelerated aging in the UV chamber, (2) to evaluate the degree of conversion (DC%) by means of FTIR spectroscopy, and (3): to evaluate water sorption by immersion in artificial saliva at 1, 3, 14, 21, 30 and 60 days. For the three studies, specimens were made in a circular metallic mold with specific dimensions for each test. For photoactivation, a LED Celalux ® (Voco, 776 mW / cm²) was used for 40 seconds. In the first study, five anterior teeth were used to fluorescence analysis and eight specimens (n=48) were made. The digital fluorescence analysis was performed using a CCD camera (LG) connected to a computer and using a UV LED. For each specimen, 16 images were captured and the mean values were also obtained, which were then converted into gray intensity scale values. For color stability, eight specimens for each composite resin were subjected to artificial aging, initially through immersion in artificial saliva for 24 hours, and in an ultra-violet (UV) chamber. The color measurements were taken with a Minolta colorimeter (CM 2600d, Japan), which were registered in their own display equipment and transferred to a microcomputer through a specific software, which recorded the color values according to the CIE-L * a * b *. Data for fluorescence and color stability were submitted to Analysis of Variance (ANOVA) followed by Tukey's test (α=5%). For the second study, the degree of conversion (DC%) was evaluated. Five specimens (n=25) were pressed with KBr and analyzed by FTIR spectrophotometer (Nexus-470). The data for the DC% were statistically analyzed by Welch's correction and complemented... (Complete abstract click electronic access below) / Doutor