Made available in DSpace on 2017-07-10T14:57:32Z (GMT). No. of bitstreams: 1 HELOUISE_ RIGHI.pdf: 781690 bytes, checksum: e73794e76d42164775e107e6f2160613 (MD5) Previous issue date: 2016-03-02 / With the ample craving for teeth whitening, it is fundamental the production of increasingly clearer materials and also a good color stability, before the possible degradation which are exposed. The camphorquinone (CQ) is the photo initiator most widely applied on the dental composite, but it has the yellow coloration and suffers darkening when exposed to ultraviolet light (UV), endangering the maintenance of the esthetics harmony. The goal of this study was to evaluate in vitro the effect of the photo initiator Phenylpropanodione, singly or in association with the CQ, about the color stability of the resinous photoactive cement and its bond adhesive resistence, by microshear. The null hypotheses are: i) the photo initiator PPD does not interfere with the color changing of the resin cement, after the photoaging motivated by prolonged exposure to UV light; and ii) the photo initiator PPD does not interfere with the resistance of the adhesive bond of resin cement to the ceramic. Four resinous cements where used, which one of them was commercial (RelyX Venner, 3M/ESPE) and three experimental, differing each other's photo initiator's concentration. For the color analysis, ceramic discs were cemented above the bovine dentine, simulating the indirect restorations (n=8), being exposed to 120 h of UV, and tested about the color alterations which were measured applying the CIELab scale, by spectrophotometer of reflectance. The obtained datas were verified about the normal distribution, for then being submited to ANOVA and to the complementary test Tukey, all with 5% significance. The results of color analysis do not statistically significant difference to E of 4 cements studied neither to L , a and b . For the Union of Resistance of all cements studied showed statistically significant differences among themselves, with the highest for commercial cement RelyX Venner® (29.07 MPa), followed by cement with CQ (21.74 MPa) , and cement CQ + PPD (19.09 MPa); and the lowest result was obtained with the cement using only the PPD as photoinitiator (13.99 MPa) . Therefore to the parameters studied in this work, the PDD was not advantageous as photoinitiator resin cements, because made low bond strength value ceramics and not demonstrated superiority as for color stability . / Com o amplo anseio pelo branqueamento dental, é fundamental a produção de materiais cada vez mais claros e que também possuam boa estabilidade de cor, ante às possiveis degradações a que ficam expostos. A Canforoquinona (CQ) é o fotoiniciador mais amplamente empregado nos compósitos odontológicos, porém tem coloração amarelada e sofre escurecimento ao ser exposta à luz ultra violeta (UV), comprometendo a manutenção da harmonia estética. O objetivo deste estudo foi avaliar in vitro o efeito do fotoiniciador Phenilpropanodiona (PPD), isoladamente ou em associação com a CQ, sobre a estabilidade de cor de cimentos resinosos fotoativados, e sua resistência de união adesiva à cerâmica, por teste de microcisalhamento. As hipóteses nulas testadas são: i) o fotoiniciador PPD não interfere na alteração de cor de cimentos resinosos, após o foto envelhecimento provocado por exposição prolongada a luz UV; e ii) o fotoiniciador PPD não interfere na resistência da união adesiva de cimentos resinosos à cerâmica. Foram utilizados 4 cimentos resinosos, sendo um comercial (RelyX Venner®) e 3 experimentais, diferindo entre si quanto ao tipo e concentração dos fotoiniciadores. Para a análise de cor, foram cimentados discos cerâmicos sobre dentina bovina, simulando restaurações indiretas (n=8), sendo expostos a 120 h de UV, e testados quanto às alterações de cor, que foram mensuradas empregando a escala CIELab, por meio de espectrofotômetro de reflectância. Os dados obtidos foram verificados quanto a distribuição normal, para então serem submetidos a ANOVA e ao teste complementar Tukey, todos com significância de 5%. Os resultados do teste de cor não apresentam diferença estatisticamente significante para o E dos 4 cimentos estudados, nem tampouco para L, a e b. Para a resistência de união, todos os cimentos estudados apresentaram diferenças estatisticamente significantes entre si, com o maior resultado para o cimento comercial RelyX Venner® (29,07 Mpa), seguido pelo cimento com CQ (21,74 Mpa), e então pelo cimento de CQ+PPD (19,09 Mpa); e o menor resultado foi obtido com o cimento utilizando apenas o PPD como fotoiniciador (13,99 Mpa). Portanto, para os parâmetros estudados neste trabalho, o PDD não se mostrou vantajoso como fotoiniciador de cimentos resinosos, já que apresentou baixo valor de resistência de união à cerâmica e não demonstrou superioridade quanto à estabilidade de cor.

Submitted by Automação e Estatística (sst@bczm.ufrn.br) on 2018-06-05T22:51:01Z No. of bitstreams: 1 ArethaHeitorVerissimo_DISSERT.pdf: 2407174 bytes, checksum: 2f467cd23d57f1f11aebbf13a2edb1cb (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2018-06-12T21:16:53Z (GMT) No. of bitstreams: 1 ArethaHeitorVerissimo_DISSERT.pdf: 2407174 bytes, checksum: 2f467cd23d57f1f11aebbf13a2edb1cb (MD5) / Made available in DSpace on 2018-06-12T21:16:53Z (GMT). No. of bitstreams: 1 ArethaHeitorVerissimo_DISSERT.pdf: 2407174 bytes, checksum: 2f467cd23d57f1f11aebbf13a2edb1cb (MD5) Previous issue date: 2018-03-20 / Introdução: Novos blocos CAD/CAM de materiais restauradores resinosos, híbridos e cerâmicos têm sido desenvolvidos recentemente. Entretanto, a literatura ainda não tem um protocolo de reparo para esses materiais frente a uma fratura coesiva do material restaurador. Objetivo: Avaliar a influência do tratamento de superfície (ponta diamantada, jateamento com Al2O3, COJET, e ácido hidrofluorídrico) e do envelhecimento in situ na resistência de união ao cisalhamento de blocos CAD/CAM (LU: Lava Ultimate/3M, VE: Vita Enamic/VITA e VS: VITA Suprinity/VITA) à resina composta. Metodologia: 390 blocos (6 x 5 x 2,5mm) foram confeccionados, sendo 130 de cada material restaurador. Foram utilizadas 300 amostras para o teste de resistência de união ao cisalhamento, as outras amostras foram utilizadas para análises extras. Cinquenta amostras de cada material restaurador foram incrustados em próteses totais em uso, e após período de 60 dias (envelhecimento in situ), as 150 amostras envelhecidas e 150 não envelhecidas foram divididas aleatoriamente (N=30/n=10) de acordo com o tratamento realizado: 1.Ponta diamantada + Single Bond Universal (SUB); 2.Ponta diamantada + silano + adesivo convencional; 3.Ácido fluorídrico 10% + silano + adesivo convencional; 4.COJET + silano + adesivo convencional; 5.Jateamento com óxido de alumínio Al2O2 + silano + adesivo convencional. Em seguida, foram construídos cilindros de resina composta Z350 (3M ESPE) (: 2,37mm, altura: 2mm) na superfície dos blocos. Posteriormente, os 300 corpos de prova foram então submetidos à termociclagem (10.000 ciclos, 50 /550C) e em seguida ao ensaio de cisalhamento (50kgf, 0,5mm/min). Após fratura, a análise de falha foi realizada em estereomicroscópio (20X). Amostras adicionais confeccionadas de cada material restaurador foram utilizadas para as análises de microdureza Vickers e Rugosidade (n=10) mesmas amostras para os dois testes; análise da viabilidade celular fúngica (n=10); análise em microscopia eletrônica de varredura (MEV) dos tratamentos superficiais e análise de EDS (n=10) para caracterização dos materiais, mesmas amostras para os dois testes. Os dados de resistência ao cisalhamento (MPa), análise da viabilidade celular (UFC/mL) e microdureza (HV) foram analisados estatisticamente por ANOVA e teste de Tukey (5%). Aos demais testes foram realizadas análises descritivas qualitativas. Resultados: A resistência de união foi afetada pela exposição ao envelhecimento in situ para os materiais LU e VS (p=0,0001), foi observado no LU maior resistência de união para o grupo Ponta diamantada + Single Bond Universal (SUB) envelhecido (14,67MPa), para o VE o grupo HF envelhecido (17,10MPa) apresentou maior resistência de união, e o VS o grupo HF sem envelhecimento (14,27MPa) apresentou maior resistência de união (p=0,0001). A falha adesiva apresentou maior prevalência em todos os tipos de bloco CAD/CAM (LU: 78%, VE: 61%, VS: 98%). O Vita Suprinity (734,31HV) exibiu a maior dureza Vikers e o Lava Ultimate (137,34HV) a menor (p=0,0001). A análise de viabilidade celular demonstrou não haver diferença entre a adesão fúngica nos três materiais (p=0,9064). Relativa à análise das superfícies tratadas (MEV) e rugosidade observou-se que os jateamentos e asperização com ponta diamantada apresentaram uma maior alteração nas superfícies de todos os materiais; a análise de EDS demonstrou que os tratamentos de superfície alteram a composição química superficial dos materiais. Conclusão: O envelhecimento in situ altera a resistência de união dos materiais LU e VS. O tratamento de superfície mais eficaz para o LU foi asperização com ponta diamantada+SBU, para os VE e VS o condicionamento com HF. O VS apresentou maior dureza Vickers. Os tratamentos de superfície promovem alterações superficiais de topografia e rugosidade de todos os materiais testados, as maiores rugosidades por material foram LU: COJET, VE: Al2O3 e VS: Ponta diamantada, lém de alterar a composição química superficial nos materiais. / Introduction: New CAD/CAM blocks of resin, hybrid and ceramic restorative materials have been recently developed. However, the literature does not yet have a repair protocol for these materials against a cohesive fracture of the restorative material. Purpose: To determine the influence of surface treatment (diamond burs, abrasive jet Al2O3, COJET, and hydrofluoric acid) and in situ aging on CAD/CAM shear bond strength (LU:Lava Ultimate / 3M, VE: Vita Enamic / VITA and VS:VITA Suprinity / VITA) to the composite resin. Methodology: 390 blocks (6 x 5 x 2.5mm) were made, 130 of each restorative material. 300 samples were used for the shear bond strength test, the other samples were used for extra analysis. Fifty samples of each restorative material were embedded in total dentures in use, and after a period of 60 days (aging in situ), the 150 aged and 150 unripe samples were randomly divided (N = 30 / n = 10) according to treatment carried out: 1. Diamond burs + Single Bond Universal (SUB); 2. Diamond burs + silane + conventional adhesive; 3. Hydrofluoric acid 10% + silane + conventional adhesive; 4. COJET + silane + conventional adhesive; 5. abrasive jet aluminum oxide Al2O3 + silane + conventional adhesive. Then, Z350 (3M ESPE) composite resin cylinders (: 2.37mm, height: 2mm) were built on the surface of the blocks. Subsequently, the 300 specimens were then subjected to thermocycling (10,000 cycles, 50 / 550C) and then to the shear test (50kgf, 0.5mm / min). After fracture, the failure analysis was performed in stereomicroscope (20X). Additional samples of each restorative material were used for the Vickers microhardness and Roughness (n = 10) analyzes for the two tests; analysis of fungal cell viability (n = 10); scanning electron microscopy (SEM) analysis of the surface treatments and EDS analysis (n = 10) for characterization of the same materials for the two tests. The shear strength (MPa), cell viability (UFC / mL) and microhardness (HV) data were analyzed statistically by ANOVA and Tukey's test (5%). The other tests were qualitative descriptive analyzes. Results: The bond strength was affected by the in situ aging exposure for the LU and VS materials (p = 0.0001), the highest bond strength for the diamond burs group + Single Bond Universal (SUB) was observed in the LU (14.67MPa), for the VE the aged HF group (17.10MPa) presented higher union strength, and the VS the HF group without aging (14.27MPa) had higher union strength (p = 0.0001). The adhesive failure presented a higher prevalence in all types of CAD/CAM block (LU: 78%, VE: 61%, VS: 98%). The Vita Suprinity (734.31HV) exhibited the highest Vikers hardness and Lava Ultimate (137.34HV) the lowest (p = 0.0001). Cell viability analysis showed no difference between fungal adhesion in the three materials (p = 0.9064). Regarding the analysis of the treated surfaces (SEM) and roughness, it was observed that the blasting and diamond burs asperisation showed a greater change in the surfaces of all the materials; the EDS analysis demonstrated that surface treatments alter the surface chemical composition of the materials. Conclusion: In situ aging changes the bond strength of LU and VS materials. The most effective surface treatment for LU was diamond burs grinding + SBU, for VS and VS the conditioning with HF. The VS presented greater Vickers hardness. The surface treatments promoted surface changes of topography and roughness of all the materials tested, the largest roughness per material were LU: COJET, VE: Al2O3 and VS: Diamond burs, besides altering the superficial chemical composition in the materials.

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / The evaluation of the performance of adhesive systems in enamel and dentin of primay teeth is justified by the differences in composition and micromorphology of these compared to permanent teeth. The difficulty of obtaining primary teeth in conditions to be included in laboratory studies causes other substrates to be used as substitutes. The objective of this study was to evaluate the bond strength of adhesive systems to the enamel and dentin of human and bovine primary teeth, in order to answer the research question: can bovine primary teeth replace humans in bond strength studies? 56 sound primary molars and 56 primary bovine incisors were randomly distributed into eight groups (n = 7) for each substrate. Composite resin cylinders (0.72 mm²) were built on the substrates after application of adhesive systems (Single Bond Universal, self etching and acid etching, Clearfil SE Bond and Adper Single Bond Plus) and the specimens submitted to the 24 hour micro-shear test. The values of bond strength (MPa) were submitted to two-way analysis of variance and Tukey's test (α = 0.05). A specimen of each type of tooth was prepared for scanning electron micrograph (SEM) and spectroscopy of Energy dispersive X-rays (ESD). The enamel bond strength values were not significantly influenced (p = 0.97) by tooth type. However the adhesive system interaction vs tooth type was (p = 0.04). In dentin, lower bond strength values (p = 0.03) were obtained for bovine teeth. No significant differences were found for the interaction between adhesive system and tooth type (p = 0.84).When analyzed the adhesive system factor in enamel and dentin, regardless of the factor tooth type, statistically significant difference was found in both substrates. In enamel, the Universal Single Bond adhesive system in the previous acid conditioning strategy presented the same performance as its Single Bond Plus control, since the self-etching strategy was not enough to match its Clearfil SE Bond control. In dentin the adhesive systems presented the same behavior, except for the Single Bond Plus adhesive system that obtained the lowest values of bond strength. For the Universal Single Bond adhesive system the use strategy did not influence the results in both substrates. Bovine and human enamel showed a similar structure of enamel prisms and Ca and P concentration. In dentin, a lower tubular density and Ca and P concentration is obtained in primary bovine teeth. In view of the differences found in the dentin substrate, the replacement of primary human teeth by primary bovine teeth in bond strength studies is only valid when the substrate of interest is the enamel. / A avaliação do desempenho de sistemas adesivos em esmalte e dentina de dentes decíduos é justificada pelas diferenças na composição e micromorfologia destes comparadas a de dentes permanentes. A dificuldade de obtenção de dentes decíduos em condições para serem incluídos em estudos laboratoriais faz com que outros substratos sejam utilizados como substitutos. O objetivo desse estudo foi avaliar a resistência de união (RU) de sistemas adesivos ao esmalte e a dentina de dentes decíduos humanos e bovinos, a fim de responder a questão de pesquisa: dentes decíduos bovinos podem substituir os humanos em estudos de adesão? 56 molares deciduos hígidos e 56 incisivos bovinos decíduos foram distribuídos aleatoriamente em oito grupos (n = 7) para cada substrato. Cilindros de resina composta (0,72 mm²) foram construídos sobre os substratos após a aplicação dos sistemas adesivos (Single Bond Universal, estratégias autocondicionante e condicionamento ácido, Clearfil SE Bond e Adper Single Bond Plus) e os espécimes submetidos ao ensaio de microcisalhamento após 24 horas. Análise de Os valores de RU (MPa) foram submetidos a análise de variância de dois fatores e Teste de Tukey (α= 0,05).Um espécime de cada tipo de dente foi preparado para microscopia eletrônica de varredura (MEV) e espectroscopia de raios X por dispersão em energia (EDS). Os valores de RU ao esmalte não foram influenciados signficativamente (p=0,97) pelo tipo de dente. No entanto a interação sistema adesivo vs tipo de dente foi (p=0,04). Em dentina, valores de RU inferiores (p=0.03) foram obtidos para os dentes bovinos. Não foram encontradas diferenças significativamente significantes para a interação sistema adesivo vs tipo de dente (p=0,84). Quando analisado o fator sistema adesivo em esmalte e dentina, independentemente do fator tipo de dente diferença estatisticamente significante foi encontrada em ambos os substratos. Em esmalte o sistema adesivo Single Bond universal na estartégia de condicionamento ácido prévio apresentou o mesmo desempenho do seu controle Single Bond Plus, já a estratégia autocondicionante não foi suficiente para se igualar ao seu controle Clearfil SE Bond. Em dentina os sistemas adesivos apresentaram o mesmo comportamento, com exceção do sistema adesivo Single Bond Plus que obteve os menores valores de resistência de união. Para o sistema adesivo Single Bond Universal a estratégia de uso não influenciou nos resultados em ambos os susbtratos. O esmalte bovino e humano mostrou estrutura semelhante de prismas de esmalte e concentração de Ca e P. Em dentina, uma menor densidade tubular e concentração de Ca e P é obtida nos dentes bovinos decíduos. Diante das diferenças encontradas no substrato dentinário, a substituição de dentes humanos decíduos por bovinos decíduos em estudos de resistência de união só é válida quando o substrato de interesse for o esmalte.

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / O objetivo deste estudo foi avaliar a resistência de união a microtração de cimentos resinosos autoadesivos a cerâmicas de zircônia policristalina. Dezoito blocos cerâmicos de zircônia 3Y-TZP (9 LAVA e 9 LAVA Plus) foram jateados com partículas de 50 m de Al2O3por 20 s com pressão de 28 psi a uma distância de 10 mm. Os blocos cerâmicos foram duplicados em resina composta (Point 4, Kerr) por moldagem com silicone. Os blocos de resina composta foram cimentados à superfície jateada da zircônia usando três diferentes cimentos resinosos autoadesivos: (1) RelyX Unicem 2 (3M ESPE); (2) SmartCem 2 (Dentsply); (3) Speedcem (Ivoclar Vivadent). Após 24 h imersos em água destilada a 37oC, os blocos cimentados foram cortados em palitos para testes de microtração,com área da interface adesiva de 1 mm2 0,2 mm, e tensionados até a fratura. Os resultados foram analisados pelo teste de análise de variância de dois fatores e pelo teste de comparações múltiplas LSD (&#945;=0.05). As amostras fraturadas foram analisadas com microscopia eletrônica de varredura (MEV) e o modo de falha foi registrado. A topografia das superfícies cerâmicas antes e após o jateamento foi comparada por microscopia de força atômica (AFM). A resistência de união do cimento Speedcem à zircônia foi estatisticamente superior àquela reportada pelos cimentos RelyX Unicem 2 e SmartCem 2, independentemente da cerâmica usada (p<0,05). O fator cerâmica não teve influência estatística na resistência de união. A interação entre os dois fatores se mostrou significativa (p<0,05). O modo de fratura associado ao SmartCem 2 foi quase exclusivamente adesiva, enquanto oRelyX Unicem 2e o Speedcem exibiram um maior percentual de falhas mistas. Não foram observadas falhas coesivas. O AFM não revelou diferença no padrão de topografia de superfície entre as duas cerâmicas antes ou após o jateamento. Concluiu-se que o cimento Speedcem foi superior na adesão a cerâmicas de zircônia policristalina. / The aim of this study was to evaluate the microtensile bond strength of self-adhesive resin cements to polycrystalline zirconia. Eighteen 3Y-TZP ceramic blocks (9 LAVA and 9 LAVA Plus) were sandblasted with 50 m Al2O3 powder for 20 s with a pressure of 28 psi at a working distance of 10 mm. The ceramic blocks were duplicated in composite resin (Point 4, Kerr) using a silicon mold. Composite blocks were bonded to sandblasted zirconia using different self-adhesive resin cements: (1) RelyX Unicem 2 (3M ESPE); (2) SmartCem 2 (Dentsply); (3) Speedcem (Ivoclar Vivadent). After 24 h immersed in distilled water at 37oC the bonded specimens were cut into microtensile bond sticks of 1 mm2 0,2 mminterface areaand loaded in tension until failure. Data were analyzed by two-way ANOVA and LSDtest for multiple comparisons (&#945;=0.05). The fractured surfaces were observed using a scanning electron microscope (SEM) and the failure mode was recorded. Surface topography of the sandblasted and the as sintered zirconia materials were analyzed under an atomic force microscope (AFM).Bond strength of Speedcem cement to zirconia was significantly higher than that of RelyX Unicem 2 and SmartCem 2, irrespective of the ceramic used (p<0,05). Bond strength was not significantly influenced by the ceramic factor. Interactions were significant (p<0,05). The mode of failure of SmartCem 2 was almost exclusively adhesive, while RelyX Unicem 2 and Speedcem exhibited a good percentage of mixed fractures. No cohesive fractures were observed. AFM did not reveal differences in the topography pattern of the two ceramics before or after sandblasting. It was concluded that Speedcem presented superior adhesion to polycrystalline zirconia ceramics.

Submitted by RAFAELA ANDRADE DE VASCONCELOS null (rafaela-vasconcelos@hotmail.com) on 2016-04-27T21:04:50Z No. of bitstreams: 1 vasconcelos_ra_dr_sjc.pdf: 1223725 bytes, checksum: f212f1adab3c030b4b7089bfeacaf463 (MD5) / Approved for entry into archive by Juliano Benedito Ferreira (julianoferreira@reitoria.unesp.br) on 2016-04-27T21:10:57Z (GMT) No. of bitstreams: 1 vasconcelos_ra_dr_sjc.pdf: 1223725 bytes, checksum: f212f1adab3c030b4b7089bfeacaf463 (MD5) / Made available in DSpace on 2016-04-27T21:10:57Z (GMT). No. of bitstreams: 1 vasconcelos_ra_dr_sjc.pdf: 1223725 bytes, checksum: f212f1adab3c030b4b7089bfeacaf463 (MD5) Previous issue date: 2016-03-18 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O propósito deste estudo foi avaliar, in vitro, a influência de remanescente de materiais obturadores endodônticos, após desobturação e preparo para pino, sobre a resistência de união adesiva de pinos de fibra de vidro cimentados. Foram utilizados 60 dentes humanos unirradiculados sem coroa. As raízes foram preparadas pela técnica coroa-ápice com sistema Reciproc. Para obturação, as raízes foram divididas em grupos (n = 10) de acordo com o cimento endodôntico utilizado: SO= sem obturação; GP=guta percha sem cimento; AHP= guta-percha + AHPlus; SLP= guta-percha + Sealapex; IRT= guta-percha + iRoot SP; e ERZ= guta-percha + EndoRez. As raízes foram obturadas pela técnica do cone único. A cimentação dos pinos de fibra de vidro Rebilda n.12 foi realizada com sistema adesivo futurabond DC e cimento Rebilda DC em 10 mm do comprimento da raiz. Após esse período, as raízes foram seccionadas obtendo-se discos de 2 mm de espessura em cada terço da raiz (3 discos por raiz) que foram submetidos ao teste de push out, análise por meio de uma lupa estereoscópica (40x) para identificação através de scores da presença de remanescente de material obturador na luz do canal e avaliação por espectroscopia de energia dispersiva (EDS) para identificação de remanescente de componentes químicos do cimento endodôntico presentes nos túbulos dentinários. Os dados obtidos foram analisados estatisticamente pelos testes de Kruskal Wallis, Qui Quadrado e teste de Anova e Tukey, todos com nível de significância de 5%. Não houve diferença estatística para a resistência adesiva entre os cimentos na região cervical (p = 0,49), media (p = 0,28) e apical (p = 0,09). Os grupos SLP e ERZ apresentaram menos remanescente de material obturador nas regiões cervical (p = 0,045) e apical (p = 0,006). Significantes diferenças de remanescentes de componentes químicos foram observadas na região apical dos grupos AHP, IRT e SLP. Conclui-se que os materiais endodônticos não influenciaram na resistência de união adesiva de pinos de fibra de vidro. / The purpose of this study was to evaluate the influence of remnants endodontic filling material in root canal on the bond strength of fiberglass posts cemented. Sixty single-rooted human teeth were used.Crowns were removed. The roots were prepared by crown-down technique with Reciproc system. For fillings, the roots were divided (n = 10) according to the sealer used: SO- without fillings; GP-gutta-percha without sealer; AHP- gutta-percha + AHPlus; SLP- gutta-percha + Sealapex; IRT-gutta-percha + iRoot SP; ERZ-and gutta-percha + EndoRez. Single cone obturation technique was used. After root canal fillings, the teeth were kept in an oven 37 0C for 7 days. Cementing fiberglass posts Rebilda n.12 was performed with fiber adhesive system Futurabond DC and cement Rebilda DC in 10 mm of root length, getting stored in an oven at 37 0C for 48 h. After this period, roots were sectioned obtaining 1 disc of 2 mm thickness in each third of the root (3 discs per root), this discs were underwent to push out test, analyzed by means of a stereomicroscope (40x) to identify the presence of remnants of filling material in the lumen of the canal, and then evaluated by energy dispersive spectroscopy (EDS) for identification of chemical components remnants sealer present in the dentinal tubules. Datas were analyzed with Kruskal-Wallis test, Chi square test, and also Anova and Tukey test, 5% of significance. There were no significant differences in push-out bond strengths among the different groups in the coronal (p = 0.49), middle (p = 0.28) or apical third (p = 0.09). Sealeapex and EndoRez groups showed significantly less remnants of filling material at coronal (p = 0.045) and apical levels (p = 0.006).Significant differences of chemical components remnants were found in AHP, IRT and SLP groups on apical third. It is concluded that residual endodontic filling material does not influence on the bond strength of fiberglass.

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The root canal preparation for placement of endodontical posts, more than in coronary preparations, produces smear layer rich in remains of dentine, filling materials and microorganisms, which may decrease the penetration and action of the adhesives, as well it favors the infection recidivation. This study investigated the effect of root canal disinfection on bond strength of glass fiber posts (White Post DC) cemented with two adhesive cements at cervical, middle and apical root. Sixty roots were randomly divided into six groups (n = 10) in accordance with the cleaning technique: water (control), 5% sodium hypochlorite and sodium hypochlorite 5% + ultrasonic agitation; and the strategies of cementation: etching with phosphoric acid 37% (Condac, FGM) +_Adper Single Bond 2 adhesive resin + RelyX ARC adhesive resin cement conventional or self-adhesive resin cementRelyX U100 (3M ESPE). After fiber posts cementation and core build-up with composite resin Z350 (3M ESPE), the reconstructed teeth were subjected to 1,000,000 cycles of mechanical fatigue (ER 11000, manufacturer, city, state, country). The specimens were then sectioned into slices of 2.0 mm thickness with a cutting machine (Labcut 1010, Extec, city, state, country) for the push-out test (EMIC City, PR, Brazil). The results were analyzed statistically (three-way ANOVA and Tukey´s test). Cleaning methods did not interfere on the bond strength in the groups with conventional cement and there was no difference between the thirds in the control groups and sodium hypochlorite, but in groups that used sodium hypochlorite associated with ultrasonic agitation, the cervical third provided significantly higher bond strength. In groups associated with the self-adhesive cement the bond strength was higher in the control group in all thirds; in the sodium hypochlorite group, the bond strength was greater in the apical third. However, there was no significant difference between the thirds in the control groups and sodium hypochlorite associated with ultrasonic agitation. The selfadhesive cement has provided higher bond strength than the conventional in all groups. In this study, the use of sodium hypochlorite reduced the bond strength for the self-adhesive cement. / O preparo do canal protético para colocação de pinos, mais do que em preparos coronários, produz smear layer rica em restos de dentina, materiais obturadores e microorganismos, que podem diminuir a penetração e a ação dos adesivos, bem como favorece a recidiva de processos infecciosos. Este estudo investigou o efeito da desinfecção dos canais protéticos na resistência adesiva de pinos de fibra de vidro (White Post DC, FGM, Joinvile, SC, Brasil) cimentados com 2 cimentos adesivos nos terços cervical, médio e apical da raiz. Sessenta raízes foram aleatoriamente divididas em 6 grupos (n=10) conforme a técnica de limpeza: água (controle); hipoclorito de sódio 5% e hipoclorito de sódio 5% + ultrassom; e a estratégia de cimentação: condicionamento com ácido fosfórico 37% (Condac, FGM) + sistema adesivo Adper Single Bond 2 (3M ESPE, St Paul, MN, EUA) + cimento adesivo convencional RelyX ARC ou cimento resinoso auto-adesivo RelyX U100 (3M ESPE). Após a cimentação dos pinos de fibra e a reconstrução do núcleo coronário com resina composta Z350 (3M ESPE), os dentes reconstruídos foram submetidos a 1.000.000 de ciclos de fadiga mecânica (ER 11000, ERIOS, São Paulo, SP, Brasil). Os espécimes foram, então, seccionados em fatias de 2,0 mm de espessura em uma máquina de corte (Labcut 1010, Extec Corp., Enfield, CT, USA) para o teste de push-out (EMIC Equipamentos e Sistemas Ltda./ São José dos Pinhais-PR, Brasil). Os resultados foram analisados estatisticamente (Análise de variância de 3 fatores e Tukey). Os métodos de limpeza não interferiram sobre a resistência adesiva nos grupos com o cimento convencional; não houve diferença entre os terços nos grupos controle e hipoclorito de sódio, mas nos grupos que usaram hipoclorito de sódio associado a ultrassom o terço cervical proporcionou resistência adesiva significativamente maior. Nos grupos associados com o cimento autoadesivo a resistência adesiva foi maior no grupo controle, em todos os terços; no grupo hipoclorito de sódio, a resistência adesiva foi maior no terço apical. Entretanto, não houve diferença entre os terços nos grupos controle e hipoclorito de sódio associados ao ultrassom. O cimento autoadesivo proporcionou resistência de união maior que o convencional em todos os grupos. Neste estudo, a utilização do hipoclorito de sódio diminuiu a resistência de união para o sistema autoadesivo.

The aim of this study was to evaluate the effect of dentin pretreatment with chlorhexidine and sodium hypochlorite in the bond strength of adhesive systems. Seventy-two sound human third molars were divided in 12 groups according to the adhesive system (Single Bond 2 - SB2, Clearfil SE Bond - SE, Single Bond Universal - SBU ) pretreatment (control, 2% chlorhexidine and hypochlorite sodium 10% ) and strategies ( self-etching or total etching ). The adhesive protocols followed the recommendation of the respective manufacturers and resin restorations were made of 5mm. After restoration, the teeth were stored in distilled water for 24 hours and sectioned to obtain specimens with interface area of 1.0 mm². Then, the specimens were subjected to microtensile testing in a universal testing machine until its failure. The results of the test microtensile bond strength were recorded in Mpa. Mean and standard deviation were calculated for each of the experimental groups. The mean bond strengths were subjected to analysis of variance (ANOVA) and differences between groups were assessed by Tukey test. For all analyzes the significance level was 5%. Analysis of variance showed that treatment surface factor exerted significant influence on the values of bond strength. The use of sodium hypochlorite to 10 % reduced the values of bond strength when compared to other treatments for all adhesive systems and should not be considered as a pretreatment of dentin. / O objetivo deste estudo foi avaliar o efeito de pré-tratamentos dentinários com clorexedina e hipoclorito de sódio, na resistência de união de sistemas adesivos. Setenta e dois terceiros molares humanos hígidos foram alocados em quatro grupos experimentais de acordo com o sistema adesivo (Single Bond 2 SB2, Clearfil SE Bond SE, Single Bond Universal - SBU) pré-tratamento (controle, Clorexedina 2% e Hipoclorito de Sódio 10%) e estratégias de uso (autocondicionante ou condicionamento ácido total). Os protocolos adesivos seguiram recomendação dos respectivos fabricantes e restaurações de resina de 5mm foram confeccionadas. Após restaurados, os dentes foram armazenados em água destilada durante 24h e seccionados para obtenção dos espécimes com área na interface de 1,0 mm² . Em seguida, os espécimes foram submetidos ao ensaio de microtração em máquina de ensaios universais até a ruptura. Os resultados de resistência adesiva ao ensaio de microtração foram registrados em MPa e elaboradas médias e desvios padrão para cada um dos grupos experimentais. As médias de resistência adesiva foram submetidas à análise de variância (ANOVA) e as diferenças entre os grupos foram submetidas ao teste de Tukey. Para todas as análises, o nível de significância considerado foi de 5%. A análise de variância mostrou que o fator tratamento de superfície exerceu influência significante nos valores de resistência de união. A aplicação de hipoclorito de Sódio a 10% reduziu os valores de resistência de união quando comparados aos tratamentos controle e clorexedina para todos os sistemas adesivos testados, não devendo portanto ser considerado como um pré-tratamento em dentina.

O objetivo deste estudo foi avaliar a resistência de união à dentina da obturação de canais radiculares com cimentos à base de resina epóxica e de metacrilato, por meio do dispositivo material testing stage (MTS) acoplado ao microtomógrafo (&mu;CT), bem como avaliar qualitativamente a ruptura da massa obturadora por meio de imagens de &mu;CT. Além disso, foram utilizados o método de elementos finitos 3D e microscopia confocal de varredura a laser (MCVL) para verificar, respectivamente, a distribuição de tensões e presença de gaps na interface de união. Raízes de caninos superiores com 17 mm de comprimento foram submetidas ao preparo biomecânico com instrumentos rotatórios de níquel titânio, sob irrigação constante com NaOCl 1% e irrigação final com EDTA 17%. Os canais foram obturados pela técnica da condensação lateral com cones de guta percha e os cimentos: AH Plus, Epiphany SE ou RealSeal XT. As raízes foram armazenadas (100% de umidade, 37°C) por três vezes o tempo de endurecimento do cimento utilizado. Após este período, as raízes foram seccionadas para obtenção de dois slices (2 mm) de cada terço radicular. Um slices de cada terço foi submetido ao teste de push-out através de dispositivo mecânico MTS acoplado ao &mu;CT SkyScan 1174 (50kV, 80mA). Após o escaneamento inicial do slices, com resolução isotrópica de 13 &mu;m, filtro de 0.5 mm de Al e 360º de rotação, o teste mecânico foi iniciado até que ocorresse o deslocamento do material. Novo escaneamento foi realizado com os mesmos parâmetros iniciais, que determinou regiões de ruptura da massa obturadora em secções axiais. Os tipos de falhas foram avaliados por MCVL e classificadas em: adesivas, coesivas e mistas. Modelos 3D de elementos finitos foram gerados para os terços cervical, médio e apical, a partir de imagens de &mu;CT. No segundo slices de cada terço radicular, foi aferido o percentual de gaps do material obturador às paredes do canal radicular, por meio de MCVL e do programa OLS 4000. Os dados foram analisados por testes estatísticos paramétricos e não paramétricos (p<0,05). O cimento AH Plus [1,89 (1,01/2,39) MPa] apresentou maior resistência de união à dentina (p<0,001) quando comparado aos cimentos Epiphany SE [0,36 (0,29/0,44) MPa] e RealSeal XT [0,43 (0,32/0,54) MPa]. Para os cimentos AH Plus e RealSeal XT, os terços cervical e médio apresentaram maior resistência de união à dentina que o terço apical (p<0,001). As rupturas ocorreram nas margens da massa obturadora para o cimento AH Plus, enquanto os cimentos Epiphany SE e RealSeal XT tiveram este tipo de ruptura, bem como na própria massa obturadora. No cimento AH Plus, a interface de união mostrou maior concentração de tensões, que foram distribuídas principalmente na massa obturadora para os cimentos Epiphany SE e RealSeal XT. Houve predominância de falhas adesivas e mistas em todos os cimentos. Em relação ao percentual de gaps, o cimento AH Plus apresentou as menores médias (11,14% ± 4,03), com diferença estatisticamente significante (p<0,05) dos cimentos Epiphany SE (55,39% ± 13,46) e RealSeal XT (62,50% ± 6,72). O cimento à base de resina epóxica (AH Plus) apresentou a maior resistência de união à dentina e teve comportamento diferente em relação aos outros cimentos, quanto à ruptura da massa obturadora e distribuição de tensão interfacial. Além disso, o cimento AH Plus apresentou o menor percentual de gaps entre o material obturador e as paredes do canal radicular / The aim of this study was to evaluate the bond strength of epoxy resin- and methacrylate-based sealers to root dentin, using the material testing stage (MTS) coupled to a micro-computed tomography (&mu;CT) device and to qualitatively assess the root-filling mass rupture by &mu;CT images. Additional analyses were conducted using the 3D element finite method and confocal laser scanning microscopy (CLSM) to verify, respectively, the stress distribution and percentage of gaps on dentin filling material interfaces. Maxillary canine roots measuring 17 mm were subjected to biomechanical preparation with nickel-titanium rotary instruments under constant irrigation with 1% NaOCl and final irrigation with 17% EDTA. Canals were filled by the lateral condensation technique with gutta-percha cones and the following sealers: AH Plus, Epiphany SE or RealSeal XT. The roots were stored (100% humidity, 37 °C) for a period three times longer than the setting time required for each sealer and then sectioned transversally to obtain two 2-mm-thick slices from each root third. One slice of each third was subjected to the push-out test using the MTS coupled to the SkyScan 1174 &mu;CT (50 kV, 80 mA) with 13 &mu;m isotropic resolution, 0.5 mm Al filter and 360° rotation. After the initial scanning of the slice, the mechanical test was performed until material dislodgement occurred. A new scanning was performed using the same initial parameters. The axial sections obtained were used for qualitative evaluation of the root-filling mass rupture. Failure modes were assessed by CLSM and classified as adhesive, cohesive or mixed. 3D &mu;CT based finite element models were generated from cervical, middle and apical root thirds to simulate the push-out test. The second slice of each root third was used to assess the percentage of gaps between the filling material and the root canal walls, using CLSM with the aid of the OLS 4000 software. The data were analyzed by parametric and non-parametric tests (p<0.05). AH Plus presented higher bond strength [1.89 (1.01/2.39) MPa] to dentin (p<0.001) than Epiphany SE [0.36 (0.29/0.44) MPa] and RealSeal XT [0.43 (0.32/0.54) MPa]. For AH Plus and RealSeal XT sealers, the cervical and middle thirds showed higher bond strength to dentin than the apical third (p <0.001). The ruptures occurred in the margins of the root filling mass for AH Plus, while Epiphany SE and RealSeal XT had this type of rupture as well as in the root filling mass itself. AH Plus showed stress concentration on bond interface, while in Epiphany SE and RealSeal XT the stress was mainly distributed on the root-filling mass. Adhesive and mixed failures were the predominant fracture modes in all sealers. Regarding the percentage of gaps between the filling material and the root canal walls, AH Plus presented the lowest means (11.14%±4.03), differing significantly (p<0.05) from Epiphany SE (55.39%±13.46) and RealSeal XT (62.50%±6.72) sealers. The epoxy resin-based sealer (AH Plus) presented the highest bond strength to dentin, which had different behavior from other sealers regarding root-filling mass rupture and interfacial stress distribution. Moreover, AH Plus resulted in the lowest percentage of gaps between the material and the root canal walls

Made available in DSpace on 2014-06-11T19:27:47Z (GMT). No. of bitstreams: 0 Previous issue date: 2005-02-28Bitstream added on 2014-06-13T20:17:11Z : No. of bitstreams: 1 sanabe_me_me_arafo.pdf: 801888 bytes, checksum: c29d9fba1c2e1a1219458d7df6abd318 (MD5) / Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) / O presente estudo teve como objetivo investigar o efeito da redução do tempo de condicionamento da dentina decídua na resistência de união imediata de um sistema convencional e um autocondicionante, e na degradação da união resina-dentina após 6 meses de armazenagem em água. Foram utilizados quarenta e oito molares decíduos hígidos foram aleatoriamente divididos em 4 grupos (n=12) de acordo com o sistema adesivo (Adper Single Bond e Clearfil SE Bond) e o tempo de condicionamento da dentina (como recomendado pelo fabricante e metade desse tempo). Desta forma, o sistema Single Bond foi aplicado sobre a dentina condicionada com ácido fosfórico a 35% por 15 ou 7 segundos, enquanto que o sistema Clearfil SE Bond foi aplicado à dentina condicionada com SE Primer por 20 ou 10 segundos. Em seguida, coroas em resina composta foram reconstruídas incrementalmente e os dentes foram mantidos hidratados em estufa à 37o C por 24 horas. Dez dentes de cada grupo foram utilizados para o ensaio mecânico de microtração. Os demais foram preparados para análise da interface adesiva em MEV. Espécimes em forma de pilar de secção transversal quadrangular (0,49 mm2) foram obtidos e divididos de acordo com a condição de armazenagem, 24 horas em água (controle), 6 meses em água e 6 meses em óleo. Os espécimes foram tracionados a velocidade de 0,5 mm/min em máquina de ensaios mecânicos e as fraturas classificadas em adesiva, coesiva em dentina, coesiva em resina ou mista. Os dados foram analisados estatisticamente pela análise de variância e testes complementares de comparação múltipla, considerando-se o nível de significância de 5%. Após 24 horas de armazenagem, os sistemas adesivos apresentaram valores de resistência de união comparáveis estatisticamente, não influenciados pela redução do tempo de condicionamento ácido... . / To evaluate the effect of reducing the acid etching of primary dentin on the immediate bond strength of a conventional and a self-etching primer system, and on the degradation of the resin-dentin bonds after 6 months aging. Forty-eight sound primary molars were randomly divided into 4 groups of investigation (n=12) according to the adhesive system (Adper Single Bond and Clearfil SE Bond) and the period of acid etching (as recommended by the manufacturers and half of this time). Single Bond was applied to dentin after 35% phosphoric acid etching for 15 seconds or 7 seconds, whereas Clearfil SE Bond was applied to dentin after the application of SE Primer for 20 seconds or 10 seconds. Following the adhesive systems, composite resin crowns were incrementally built-up and the teeth were stored in water at 37o C for 24 hours. Specimens with a cross-sectional area of 0,49 mm2 were produced from each one of the teeth (10 teeth per group) and further divided according to the storage condition, 24 hours in water, 6 months in water and 6 months in mineral oil, when they were tested under tension until failure in a machine operating at a cross-head speed of 0.5 mm/min. After the microtensile test, the failures were classified as adhesive, cohesive in dentin, cohesive in resin or mixed. The two remaining teeth per group were prepared to SEM evaluation of the interfaces. Two-way analysis of variance and multiple comparison testes were applied at a significance level of 5%. When bond strength was evaluated after 24 hours storage in water there was no significant difference between the adhesive systems, irrespective of the periods of acid etching. For Single Bond, water storage for 6 months in water significantly reduced bond strength, especially when the dentin was phosphoric acid conditioned for 15 seconds (36.7% reduction). For Clearfil SE Bond... (Complete abstract, click electronic address below).

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Purpose: To evaluate the effect of different hydrofluoric (HF) acid concentrations in the contact angle and in the durability of bond strength between feldspathic ceramic and resin cement, as well as the impact on the roughness and flexural strength of this ceramic. Materials and Methods: Twenty-five ceramic blocks (VitaBlocks Mark II) (12 x 10 x 2.4 mm) were produced for contact angle analysis, 40 ceramic blocks (12 x 10 x 4 mm) for microtensile bond strength (MTBS), and 150 ceramic barshaped specimens (14 x 4 x 1.2 mm) to evaluate the roughness and flexural strength. Specimens were randomly divided into 5 groups, excluding the control group for MTBS: SC (control) - no ceramic surface treatment; etching with HF acid 1% (HF1), 3% (HF3), 5% (HF5) and 10% (HF10) for 60. The contact angle measurements were performed on a Goniometer and the MTBS test in a universal testing machine. All bar-shaped specimens were analyzed in a profilometry and loaded to failure using a 3-point bending test. Data were submitted to statistical analysis. Results: SC had the highest contact angle (61.4°± 5°), whereas HF10 showed the lowest value (17.5° ± 4°). In dry conditions, different HF acid concentrations promoted similar bond strength statistically (14.2 to 15.7 MPa) (p<0.05), but when the specimens were aged, only the bond from the HF1 group decreased statistically (14.5 to 10.2 MPa). All groups produced significantly rougher surfaces than the control group (SC) (p<0.05). However, the mean flexural strength values were not statistically different among the etched groups (106.47 to 102.02 MPa). Conclusion: In terms of adhesion, the tested ceramic can be etched with HF acid in concentrations of 3%, 5% and 10%. Different acid concentrations did not affect the flexural strength of the tested ceramic. Acid etching appear to have a weakening effect on the ceramic surface, if compared to the untreated group. / Objetivo: Avaliar o efeito de diferentes concentrações de ácido fluorídrico (HF) no ângulo de contato e na durabilidade da resistência adesiva entre uma cerâmica feldspática e um cimento resinoso, bem como o impacto sobre a rugosidade e resistência à flexão desta cerâmica. Materiais e Métodos: Vinte e cinco blocos cerâmicos (VitaBlocks Mark II) (12 x 10 x 2.4 mm) foram produzidos para a análise do ângulo de contato, 40 blocos cerâmicos (12 x 10 x 4 mm) para resistência de união à microtração (MTBS) e 150 espécimes em forma de barra de cerâmica (14 x 4 x 1,2 mm) para avaliar rugosidade e resistência à flexão. Os espécimes foram divididos aleatoriamente em 5 grupos, excluindo o grupo controle para MTBS: SC (controle) - sem tratamento da superfície cerâmica; condicionamento com ácido HF 1% (HF1), 3% (HF3), 5% (HF5) ou 10% (HF10) por 60 s. As medidas de ângulo de contato foram realizadas no Goniômetro e o teste MTBS em uma máquina de ensaio universal, sendo metade dos espécimes de cada bloco testados imediatamente e a outra metade submetida à armazenagem/termociclagem. Todas as amostras em forma de barra foram analisadas em um rugosímetro e carregadas até a falha usando um teste de flexão de três pontos. Os dados foram submetidos à análise estatística. Resultados: SC obteve o maior ângulo de contato (61,4° ± 5°), enquanto que HF10 apresentou o menor valor (17,5° ± 4°). Em condições secas, diferentes concentrações de ácido HF promoveram resistências adesivas estatisticamente semelhantes (14,2-15,7 MPa) (p<0,05), mas quando os espécimes foram envelhecidos, apenas a adesão do grupo HF1 reduziu estatisticamente (14,5-10,2 MPa). Todos os grupos produziram superfícies significativamente mais rugosas do que o grupo controle (SC) (p<0,05). No entanto, os valores médios de resistência à flexão não foram estatisticamente diferentes entre os grupos condicionados (106,47- 102,02 MPa). Conclusão: Em termos de adesão, a cerâmica testada pode ser condicionada com ácido HF em concentrações de 3%, 5% ou 10%. As diferentes concentrações de ácido não afetaram a resistência à flexão da cerâmica testada. O condicionamento ácido parece ter um efeito de enfraquecimento sobre a superfície cerâmica, se comparado com o grupo não tratado.