Given the routine use of polishing and finishing systems in Restorative Dentistry, the search for better outcomes of these materials, it is essential to optimize the results. Thus, this study aimed to evaluate in vitro the effect of polishing finishing and polishing systems on surface roughness of composite resin. Specimens were made for each group (n = 10), totaling 80 specimens. Randomly distributed among the eight selected polishing systems. The polishing systems were employed after the stabilize the polishing and metallographic specimens was followed according to the manufacturer's instructions. The specimens were stored for 24 hours in aqueous solution (room temperature) underwent evaluation of roughness on rugosimeter, and surface roughness as groups were compared using ANOVA, followed by post-hoc Tukey test at a significance level 5%, with p = 0.05. Was no statistical difference between finishing and polishing systems evaluated. The finishing and polishing systems produce different patterns on the surface roughness of the composite, and the rotating disc systems based on superior results obtained with smaller surface roughness measurements. / Tendo em vista o uso rotineiro dos sistemas de polimento e acabamento na Odontologia Restauradora, a busca por melhores resultados destes materiais, é essencial a fim de otimizar os resultados. Assim, este estudo teve como objetivo avaliar in vitro, o efeito de polimento de sistemas de acabamento e polimento na rugosidade superficial de resina composta. Foram confeccionados corpos de prova para cada grupo (n=10), totalizando 80 espécimes. Distribuídos aleatoriamente entre os 8 sistemas de polimento selecionados. Os sistemas de polimento foram empregados após a regularização dos espécimes em politriz metalográfica e foi seguido conforme as instruções do fabricante. Os espécimes foram armazenados por 24 horas em solução aquosa, (temperatura ambiente) submetidos a avaliação de rugosidade no rugosímetro, e os grupos foram comparados quanto a rugosidade superficial por meio de ANOVA, seguido de teste de Post-Hoc de Tukey ao nível de significância de 5%, com p≤0,05. Houve diferença estatística entre os sistemas de acabamento e polimento avaliados. Os sistemas de acabamento e polimento produzem diferentes padrões de rugosidade na superfície da resina composta, sendo que os sistemas baseados em discos rotatórios obtiveram resultados superiores, com menores medidas de rugosidade superficial.

Made available in DSpace on 2014-06-11T19:24:47Z (GMT). No. of bitstreams: 0 Previous issue date: 2005-02-17Bitstream added on 2014-06-13T19:06:29Z : No. of bitstreams: 1 zhu_nxj_me_bauru.pdf: 4158261 bytes, checksum: bafc2c29b13e8c6fb309c4a1b184788a (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Atualmente tem-se verificado crescente demanda por processos de fabricação capazes de produzir peças sob estreitas faixas de tolerâncias dimensionais e geométricas. Dentre os processos utilizados para conferir acabamento superficial e correção de forma destacam-se a retificação e a lapidação. Porém, muitas peças mostram-se suscetíveis ao calor gerado pela retificação, como no caso da deformação de peças delgadas ou então naquelas peças passíveis de mudanças microestruturais, recorrendo-se nestes casos à lapidação que, por sua vez, é um processo de difícil seleção de parâmetros. Neste trabalho é iniciado o desenvolvimento de um processo híbrido capaz de aliar algumas importantes características da retificação e da lapidação, no qual do primeiro é usado a operação de dressagem e do segundo o movimento cinemático. Dessa forma dotou-se uma... / Lately, one can verify that there has been a growing demand for manufacturing processes capable of producing workpieces under tight dimensional and geometric tolerance rangers. Among the processes used to assure surface finish and shape correction to the part, grinding and lapping arise as the most used. However, many parts show themselves sensitive to the heat generated during the grinding process, as in the case of thin ones, or those susceptible to micro-structural changes. On these cases, one can use lapping, even though being a more difficult parameter selection process. In these studies, the development of a hybrid process capable of binding some important grinding and lapping features is initiated; the dressing operation, for the case of grinding and, for the case of lapping, the cinematic movement... (Complete abstract click electronic access below)

Submitted by EDUARDO LUIZ DE GODOI null (eduardo.luiz.godoi@gmail.com) on 2018-02-16T12:51:52Z No. of bitstreams: 1 Dissertação Eduardo Luiz de Godoi.pdf: 3930737 bytes, checksum: 3a40c9358ea11d0b9adc83902c1bbafe (MD5) / Approved for entry into archive by Maria Marlene Zaniboni null (zaniboni@bauru.unesp.br) on 2018-02-16T17:50:07Z (GMT) No. of bitstreams: 1 godoi_el_me_bauru.pdf: 3930737 bytes, checksum: 3a40c9358ea11d0b9adc83902c1bbafe (MD5) / Made available in DSpace on 2018-02-16T17:50:07Z (GMT). No. of bitstreams: 1 godoi_el_me_bauru.pdf: 3930737 bytes, checksum: 3a40c9358ea11d0b9adc83902c1bbafe (MD5) Previous issue date: 2017-12-18 / A operação de roleteamento é realizada com o intuito de diminuir a rugosidade e melhorar as propriedades mecânicas da peça, como o aumento da dureza e da resistência à fadiga. O processo se dá sem remoção de material, por meio de trabalho a frio, no qual a ferramenta promove o escoamento do material dos picos para o preenchimento dos vales na superfície da peça de trabalho. Esta operação envolve deformação plástica com consequente introdução de tensão residual de compressão nas camadas subsuperficiais da peça. No entanto, as forças de contato envolvidas no processo podem ser excessivamente altas ao ponto de produzir desvios de forma afetando a qualidade superficial da peça acabada. Para minimizar estes problemas, encontram-se pesquisas que utilizam um feixe de laser para o aquecimento localizado da peça na região imediatamente anterior ao contato da ferramenta. Porém, por questões de custo e espaço físico em torno da máquina, este método tem seu uso restrito. A fim de tornar o roleteamento a quente mais viável, neste trabalho é proposto o uso de resistência elétrica em cerâmica, de baixo custo, a qual emite radiação infravermelha como fonte de calor. Para medir a eficiência da técnica proposta foram realizadas operações de roleteamento convencional e comparadas com a condição a quente empregando uma liga aeronáutica inconel 718. Foram analisadas importantes variáveis de saída do processo relacionadas com a qualidade superficial, como a rugosidade, microdureza, tensão residual e circularidade, quando utilizados diferentes parâmetros de entrada, como força de contato, rotação da peça e número de passes. Os resultados demonstraram que a rugosidade (parâmetros Ra e Rt) dos corpos de prova roleteados apresentou uma redução de aproximadamente 20% sem auxilio e 23% com auxílio de radiação infravermelha em relação ao valor observado antes da operação, ao passo que a dureza superficial apresentou elevação de cerca de 20% sem auxilio e 35 % com auxílio de radiação infravermelha em comparação ao componente torneado. A tensão residual registrada na superfície dos corpos de prova passou a ser tensão residual de compressão e atingiu camadas subsuperficiais após roleteamento a quente e os valores de desvio de circularidades diminuíram. / The burnishing operation is performed in order to reduce roughness and improve the mechanical properties of the part, such as increased hardness and fatigue resistance. The process takes place without material removal by means of cold working, in which the tool promotes the flow of the material from the peaks to fill the valleys on the surface of the workpiece. This operation involves plastic deformation with consequent introduction of residual compressive stress in the subsurface layers of the part. However, the forces involved in the process may be excessively high to the extent of producing shape deviations affecting the surface quality of the finished workpiece. To minimize these problems, there are researches that use a laser beam for localized heating of the part in the region immediately prior to the tool contact. However, for reasons of cost and physical space around the machine, this method has its restricted use. In order to make hot rolling more feasible, in this work the use of low cost electric ceramic resistance is proposed, which emits infrared radiation as a source of heat. To measure the efficiency of the proposed technique, conventional burnishing operations will be performed and compared to the hot condition using an aeronautical alloy 718 Inconel. Important process output variables related to surface quality, such as roughness, micro hardness, residual stress and circularity, when using different input parameters, such as force, part rotation and number of passes. The results showed that the roughness (Ra and Rt parameters) of the test specimens showed a reduction of approximately 20% without aid and 23% with the aid of infrared radiation in relation to the value observed before the operation, whereas the surface hardness presented increase of about 20% without assistance and 35% with the aid of infrared radiation in comparison to the turned component. The residual stress recorded on the surface of the specimens increased and reached subsurface layers after hot burnishing, the values of deviation of circularities decreased.

Este trabalho discute as alterações micro-estruturais superficiais nos aços usinados por torneamento duro. Uma estrutura não aceita metalurgicamente, chamada de Camada Branca (\"White Layer\" - WL), é freqüentemente encontrada na superfície torneada. A presença desta camada branca depende dos parâmetros do processo de corte, especialmente do desgaste da ferramenta e da velocidade do corte. A formação da camada branca foi investigada no presente trabalho na face plana inferior de um anel de rolamento fabricada com o aço DIN 100Cr6, usinada por torneamento duro no estado temperado e revenido (dureza 60HRC). A profundidade foi medida usando as técnicas padrões metalográficas. As propriedades mecânicas da camada superficial (módulo de rigidez, E, e microdureza Vickers, HV) foram estimadas pelo método de microidentação instrumentada em uma amostra isenta da camada branca e em duas outras amostras, com camadas brancas de diferentes espessuras (respectivamente 7 e 12 mm de espessura). De acordo com a literatura a profundidade da camada branca aumenta de acordo com o desgaste da aresta da ferramenta. Este por sua vez aumenta com a velocidade de corte, mas atinge a saturação. Em outras palavras, a profundidade de corte tem pouco efeito sobre a profundidade da camada branca; porém aumentando o avanço da ferramenta de corte ocorre o aparecimento da mesma. Os presentes resultados confirmam um efeito do avanço da ferramenta sobre a espessura da WL, tal que quanto menor o avanço, maior é a espessura, porém não confirmam o efeito do desgaste da ferramenta. A formação desta camada é discutida no contexto da sua influência sobre a rugosidade das peças. / This work deals with the microstructural changes in the surface of steels machined by hard turning. A non-acceptable microstructure, called White Layer - WL, is usually found in the hard turned surface. The presence of the white layer depends on hard turning parameters, especially on the wear of the machining tool and cutting speed. The formation of the white layer was investigated in the present work by hard turning the inferior face of a roller-bearing ring fabricated with DIN 100Cr6 steel quenched and tempered (60 HRC hardness). The depth of the WL was measured by standard metallographic procedures. The mechanical properties (stiffness modulus, E, and Vickers hardness) of the surface layer were measured by intrumented indentation in three samples: one with no WL, and two containing a WL of respectively 7 and 12 mm. According to the literature the depth of the WL increases with the wear of the machining tool. This increased with cutting speed, but reaches saturation. The presentresults confirm an effect of tool advance upon the depth of the WL, such that decreasing the advance leads to an increase in its depth, but an effect of tool wear could not be recognized. The formation of the WL is discussed in the context of its effect on surface roughness.

[pt] O conhecimento da concentração de tensões provocada pelas bordas de corpos que interagem e do efeito das rugosidades sobre as tensões de contato é de grande importância para o projeto de elementos de máquinas que tenham no contato a sua principal causa de falhas. Estas ocorrem normalmente por fadiga superficial (tais como em rolamentos e engrenagens) e também em aplicações onde estão envolvidos atrito, desgaste superficial e contato elétrico. Neste trabalho, procurou-se estudar a influência da rugosidade nestas distribuições de tensões. O método da fotoelasticidade foi utilizado para análise dos campos de tensões provocados pelo contato de corpos rugosos. As situações envolvendo o contato de superfícies cilíndricas rugosas com o plano liso foram preferidas em virtude das facilidades apresentadas para confecção dos modelos. Primeiramente, realizou-se um estudo de similitude para definir os termos adimensionais considerando as variáveis físicas relevantes às tensões de contato. Posteriormente, comprovou-se que estes termos são adequados através de ensaios fotoelásticos. Nestes ensaios foram variadas as dimensões dos corpos de prova, sua rugosidade e materiais. Foram utilizados diversos materiais, tais como vidro, resinas epoxi e poliester e acrílico. Também foram realizados testes onde materiais metálicos foram submetidos à contato com materiais birrefringentes. Os resultados experimentais fotoelásticos mostraram que a rugosidade superficial provoca grandes reduções sobre a tensão cisalhante máxima e sobre a pressão de contato. Constatou-se que a rugosidade provoca um aumento de largura de contato entre cilindros, aumentando desta forma a área de contato. Os resultados foram apresentados segundo gráficos que oferecem ao projeto de componentes cilíndricos, meios para que se possa conhecer a influência da rugosidade nas tensões de contato e determinar os limites para os quais a teoria de Hertz pode ser aplicada a estas situações, sem implicar em resultados demasiadamente conservativos. Finalmente, os experimentos fotoelásticos com cilindros também forneceram uma comprovação experimental para a teoria de Lo sobre o contato de cilindros rugosos. / [en] The knowlegeof the stress concentration generated by the edge of contacting bodies and the effect of roughness on the contact stresses are of great importance to the design of machine elements which have in the contact stresses their principal sources of failures. These failures usually occur due to surface fatigue (as in bearings and gears) and in applications where friction, wear and eletric contact are present. In this thesis the influence of roughness on the contact stress distribution is studied. The method of 2D photoelasticity is employed to analyse stress distributions fields generated by the contact of rough surfaces of cylindrical bodies. At first, a similitude study was carried out to define the dimensionless parameters which would be important for the problem of contact stresses. It was shown that these parameters were adequate by means of photoelastic experiments, where the dimensions of the models, their roughness and the materials were varied. Different materials were utilized, such as glass, epoxy, polyester resins and flexiglass. Experiments were carried out with contacting cylinders of metals (steel and aluminum) and birrefringent materials. The photoelastic experimental results showed that surface roughness causes great reduction on the maximum shear stress and on the maximum contact pressure. It was verified that roughness causes an increase in the width of contact of cylinders and also an increase in the contact area. The results are furnished in plots that help the design of cylindrical components by presenting the influence of roughness on the contact stresses and the limits for the application of Hertz theory. Finally, the photoelastic experiments gave an experimental validation to the theory of Lo for the contact of rough cylinders.

Tese de mestrado integrado. Engenharia Mecânica. Faculdade de Engenharia. Universidade do Porto. 2012

Orientador: Paulo Roberto de Aguiar / Banca: Carlos Elias da Silva Junior / Banca:m Eduardo Carlos Bianchi / Resumo: O processo de retificação confere à peça o acabamento final, minimizando as irregularidades superficiais através de interações entre os grãos abrasivos de uma ferramenta (rebolo) e peça retificada. O desgaste do rebolo devido ao atrito entre o rebolo e a peça retificada torna a ferramenta inadequada para nova utilização, sendo necessária a realização do processo de dressagem do rebolo para remoção e ou avivamento dos grãos gastos de sua superfície de corte, de forma e deixá-lo em condições para novo uso. O presente trabalho tem como objetivo classificar a condição do rebolo durante a operação de dressagem utilizando o sinal de emissão acústica (EA) e estatísticas derivadas desse sinal, por meio de redes neurais artificiais. Nos experimentos realizados usou-se um rebolo de óxido de alumínio instalado em uma retificadora plana, um sistema de aquisição de sinais e um dressador de ponta única de diamante. O processamento digital de sinais foi obtido através do software MATLAB. Os ensaios foram realizados com diferentes graus de recobrimento e profundidade de dressagem. A partir dos dados obtidos de EA puro, calculou-se o valor médio quadrático (RMS), bem como mais duas estatísticas, as quais já foram empregadas com sucesso em trabalhos de detecção de queima, no processo de retificação. Essas estatísticas também se mostraram bons indicadores para o monitoramento da operação de dressagem. Uma rede neural perceptron multicamadas (MLP) foi utilizada com o algoritmo de aprendizado Levenberg-Marquardt, cujas entradas foram as duas estatísticas mencionadas e o valor RMS de EA. Os resultados mostram que o método empregado foi capaz de classificar as condições do rebolo no processo de dressagem, identificando o rebolo como "afiado" (com capacidade de corte) e rebolo "se afiação" (com perda de capacidade de corte), viabilizando a redução do tempo e custo dessa operação e minimizando a remoção excessiva / Abstract: The grinding process gives the piece a final finish by minimizing surface irregularities through interactions between the abrasive grains of a tool (wheel) and the part to be ground. The wear of the grinding wheel due to excessive friction between the grinding wheel and ground workpiece makes the tool unsuitable for further use; it is imperative the accomplishment of the process of dressing the grinding wheel to remove or resharpen the worn grains of its surface in order to make if suitable for use again. The present study aims to classify the condition of the grinding wheel during operation using acoustic emission (AE) signal and statistics derived from this sinal through artificial neural networks. In the experiments an aluminum oxide grinding wheel installed to a surface grinding machine was used along with a data acquisition system and a single point diamond dresser. The digital processing of these data was obtained using the MATLAB software. Tests were performed with different overlap ratio and depth of cut. The root mean square value of the AE signal as well as two other statistics were obtained from the raw acoustic emission signal, which have been successfully used in grinding burn detection. These statistics were also good indicators for monitoring the dressing operation. A multilayer perceptron neural network (MLP) was used with the learning algorithm Levenberg-Marquardt, whose inputs were the statistics previously mentioned and dressing conditions. The results show that the method used was able to classify the conditions of the grinding wheel in the process of dressing, identifying the wheel as sharp (cutting capacity) and dull (with loss of cutting capacity), enabling the reduction of time and cost of operation and minimizing the excessive removal of the wheel abrasive material / Mestre

O presente estudo avaliou a influência do hipoclorito de sódio a 1% e 2,5% na qualidade do acabamento superficial e na resistência à corrosão de duas limas endodônticas: Race® e Hyflex® através de ensaio eletroquímico de polarização potenciodinâmica cíclica (EPPC) e imagens obtidas por microscopia eletrônica de varredura (MEV). Para o EPPC foram utilizados vinte limas de cada marca comercial (#25, conicidade 0.04 e 25 mm de comprimento). Dez dos vinte instrumentos foram individualmente fixados pelo cabo a uma ponta de fio de cobre 0,12 mm de 20 cm de comprimento e posicionado no interior de uma célula eletroquímica com 500 mL de solução de hipoclorito de sódio (NaClO) 1% (Fórmula&Ação) à temperatura ambiente controlada em 23 ºC (±2) até cobrir a parte ativa do instrumento. Os registros foram feitos com o potenciostato da PAR modelo 273A. O ensaio foi repetido nos mesmos padrões para as outras dez limas da mesma marca comercial com o NaClO 2,5%. Além do EPPC, as limas foram submetidas a exames e análises em MEV antes e depois do teste de corrosão para a obtenção de fotomicrografias dos 3 (três) mm finais de cada lima com o intuito de estabelecer parâmetros para a avaliação final. Das fotomicrografias obtidas, 72 foram escolhidas, inseridas no Power Point sem legenda original de identificação, numeradas aleatoriamente para avaliação e projetadas num monitor para 06 avaliadores orientados e calibrados. Os dados obtidos foram tabulados e submetidos aos testes estatísticos pertinentes (Friedman, Wilcoxon e Mann-Whitney). A lima Hyflex® apresentou uma quantidade maior de alterações superficiais (ranhuras, manchas e materiais depositados) antes e depois do ensaio sendo mais suscetível à corrosão. Race® apresentou uma superfície mais polida e regular. Em relação a concentração do NaClO, percebeu-se que os defeitos presentes se tornavam mais evidentes para a concentração maior (2,5%). Nas duas concentrações os itens que apresentaram diferença significativa foram bordas, ranhuras, microcavidades, rebarbas e material depositado. Concluiuse que o acabamento superficial e a concentração da solução de NaClO influenciam a resistência à corrosão dos instrumentos de NiTi. A lima Race® apresentou menor corrosão e melhor acabamento de superfície do que a lima Hyflex® nas condições experimentais testadas. / The present paper evaluated the influence of 1% and 2.5% sodium hypochlorite in the quality of the surface finishing and resistance to corrosion of two endodontic files: Race® and Hyflex® by electrochemical test of cyclic power dynamics polarization (EPPC) and images obtained by scanning electronic microscopy (SEM). Twenty files of each commercial brand (#25, 0.04 taper and 25 mm length) were used in EPPC. Ten from the twenty instruments were individually fixed by the handle to a copper wire tip (0.12 mm diameter and 20 cm length) and placed in the interior of an electrochemical cell with 500 mL sodium hypochlorite solution (NaCIO) 1% (Fórmula e Ação) at the environment temperature controlled in 23ºC (±2) until covering the active part of the instrument. Recordings were made with a PAR potentiostat model 273A. The test was repeated in the same pattern to the other ten files from the same commercial brand with NaClO 2.5%. Besides EPPC, the files were submitted to the scanning electronic microscopy (SEM) test before and after the corrosion test to obtain photomicrographs of the final 3 mm of each file in order to establish the parameters for final evaluation. From the obtained photomicrographs, 72 were chosen and inserted in the Power Point without the original identification legend, randomly numbered for evaluation and projected on the screen to the 06 guided and calibrated evaluators. Data obtained were tabbed and submitted to the relevant statistical tests (Friedman, Wilcoxon and Mann-Whitney). The Hyflex® file showed a higher amount of surface alterations (grooves, stains and deposited materials) before and after the test, being more susceptible to corrosion. Race® showed a more polished and regular surface. As to the NaClO concentration, it was seen that the present defects became more evident in the higher concentration (2.5%). In the two concentrations, the items that presented significant differences were edges, grooves, micro cavities, margins and deposited materials. Conclusion was that surface finishing and the concentration of the NaClO solution influenced the resistance to corrosion of NiTi instruments. The Race® file showed the least corrosion and the best surface finishing compared to the Hyflex® file under the tested experimental conditions.

Neste trabalho são apresentados os principais conceitos relacionados às pinturas texturizadas. Foram propostas diretrizes mínimas para especificação e recebimento de pinturas texturizadas acrílicas em substratos de argamassa para fachadas de edifícios. Para o estabelecimento das diretrizes foram evidenciadas as práticas adotadas através de estudos de casos e foi realizado um estudo experimental para desenvolvimento dos principais critérios de aceitação propostos. Considera-se que a especificação técnica é o ponto de partida para assegurar que as pinturas texturizadas acrílicas atendam o uso previsto. / In this work the main concepts related to textured coatings are presented. The minimal directives are proposed for specification and act of receiving of acrylic textured coatings in renderings for buildings frontages. For the establishment of the directives the practices adopted through studies of cases had been evidenced and an experimental study was carried through for development of the main considered accepted criteria. It is considered that the technical specification is the starting point to assure that the acrylic textured coatings take care of the foreseen use.

O objetivo desse trabalho foi verificar a influência do procedimento de acabamento e polimento das restaurações de resina composta na resistência adesiva à dentina, através de testes de microtração, assim como, analisar em microscopia eletrônica de varredura a interface dente/restauração no nível do ângulo cavo-superficial. Terceiros molares humanos extraídos e hígidos foram utilizados nesse estudo, após aprovação pelo Comitê de Ética em Pesquisa da FOB-USP. Os dentes foram restaurados com sistema adesivo Solobond M (VOCO) e resina composta Grandio (VOCO) e distribuídos nos seguintes grupos: G1 (controle) - sem acabamento e polimento, G2 - acabamento e polimento imediato, G3 - sem acabamento e polimento e armazenado por sete dias e G4 - acabamento e polimento após sete diasem estufa a 37ºC. Palitos com dimensões de 1mm x 1mm foram obtidos e submetidos a uma força de tração em uma máquina de ensaios universal EMIC à velocidade de 0.5mm/min. Para a análise em microscopia eletrônica de varredura, 20 terceiros molares receberam quatro preparos cavitários com 1mm de diâmetro e 3mm de altura que foram restaurados com o mesmo sistema restaurador utilizado para os testes de resistência adesiva e distribuídos nos mesmos grupos descritos acima. Após a obtenção dos espécimes de cada grupo, os dentes foram metalizados e analisados na interface dente/restauração em microscopia eletrônica de varredura por três examinadores. As médias de resistência adesiva (MPa) e respectivos desvios-padrão foram: G1 - 23,05 (8,62); G2 - 17,34 (6,11); G3 - 21,64 (7,63) e G4 - 18,12 (6,51). Os valores de resistência adesiva submetidos à Anova a um critério e teste de Fisher permitiram concluir que o procedimento de acabamento e polimento das restaurações de resina composta diminuiu significativamente a resistência adesiva à dentina. O teste de Kruskal-Wallis aplicado aos escores obtidos da análise das fendas no ângulo cavo-superficial permitiu determinar que o acabamento e polimento da resina composta não interfere na formação de fendas. / The objective of this study was to verify the influence of finishing and polishing procedures on dentin bond strength of resin composite, and at the interface tooth/restoration using MEV. Recently extracted human third molars were utilized in this study, after approved by ethics and search committee at FOB-USP. The teeth were restored with Solobond M (VOCO) adhesive system and resin composite Grandio (VOCO) and randomized in the follow groups: G1 (control) - no polishing and finishing, G2 - immediate polishing and finishing procedures, G3 - no polishing and finishing and stored for seven days e G4 - polishing and finishing procedures after seven days under water at 37oC. Sticks 1mm x 1mm were obtained and the bonds were then stressed to failure by microtensile forces in a EMIC universal testing machine at a crosshead speed of 0.5 mm/min. Twenty human third molars were prepared with four cavities with 1mm diameter and 3mm height and restored with the same restoration system used for the microtensile tests and were distributed at the same groups and the interface tooth/restoration was analyzed in MEV by three examinators. The means of bond strength (MPa) and respective standard deviation were: G1 - 23.05 (8.62); G2 - 17.34 (6.11); G3 - 21.64 (7.63) e G4 - 18.12 (6.51). The data were analyzed by One-Way Anova and e Fisher´s test. It was possible to conclude that the finishing and polishing procedures of resin composite decrease significantly the bond strength to dentin of the composite restorations. The Kruskal- Wallis test aplicated to gap scores at the tooth/restoration interface allows to determinate that the finishing and polishing procedures of resin composite do not interfere in gap formation.