In the thesis CuPc thin films were investigated by (in situ) SE and RAS, which are employed to determine the out-of-plane and in-plane optical anisotropy and molecular orientation, respectively. CuPc is a promising candidate of organic semiconductors used in organic field effect transistors, organic light emitting diodes and organic solar cells. Vicinal Si(111) substrates are interesting due to the in-plane anisotropy caused by the steps and terraces on the surface. The strength of in-plane anisotropy of vicinal Si(111) is dependent on the offcut angle. The influence of offcut angle on out-of-plane and in-plane molecular orientation in CuPc thin films is explored. The in situ investigation of CuPc films suggests that structural changes occur during film growth. In addition, two different surface modification layers were utilized to examine the effect on CuPc molecular orientation: OTS monolayer with upright standing molecules and PTCDA layers with flat lying molecules. Metal-organic interface plays an important role in organic electronic devices. In-CuPc is chosen to be an example system investigated employing in situ SE and RAS. When In was thermally evaporated onto CuPc film, In atoms firstly diffuse into the CuPc film underneath and then aggregate to form clusters on top. Hafnium dioxide (HfO2) is currently a hot topic to replace the conventionally used SiO2 as gate dielectrics in order to minimize leakage current when further scaling down microelectronic devices. Since HfO2 films are often crystalline, in order to obtain amorphous films which are beneficial to minimize leakage current, aluminum oxide (Al2O3) (k value: 9) which stays amorphous at much higher temperatures are combined to overcome this difficulty. Two series of ultra-thin samples were deposited by atomic layer deposition: mixed layers HfxAl1-xOz and bilayers HfO2 on Al2O3. Optical constants and bandgap are determined using SE in the energy range of 0.7-10 eV. It is found that the (effective) optical bandgap of both mixed layer and bilayer structures can be tuned by the film composition. Aging effect of high-k films was observed after storage of samples in air for two months, which is attributed to further oxidation of the dielectric films caused by the oxygen diffusion from ambient air to high-k films. / In dieser Arbeit werden dünne Schichten aus Kupferphthalozyanin (CuPc) mittels spektroskopischer (in-situ) Ellipsometrie (SE) und (in-situ) Reflektions-Anisotropie-Spektroskopie (RAS) untersucht, um die optische Anisotropie in einer Ebene parallel und senkrecht zur Schichtoberfläche und die molekulare Orientierung zu bestimmen. CuPc ist ein aussichtsreicher Kandidat als organischer Halbleiter in organischen Feldeffekt-Transistoren, organischen Leuchtdioden und organischen Solarzellen. Vizinale Si(111)-Substrate sind wegen der Anisotropie in der Substratebene interessant, die durch die Treppen und Terrassen auf der Oberfläche verursacht wird. Die Stärke der Anisotropie der vizinalen Si(111)-Oberfläche ist vom Schnittwinkel (Offcut) abhängig. Es wird der Einfluss des Offcut-Winkels auf die molekulare Orientierung in dünnen CuPc-Schichten parallel und senkrecht zur Substratoberfläche untersucht. Die in-situ Untersuchungen von CuPc-Schichten weisen darauf hin, dass strukturelle Veränderungen beim Wachstum auftreten. Darüber hinaus wurden zwei unterschiedliche Oberflächenmodifizierungsschichten, um deren Wirkung auf die molekulare Orientierung von CuPc zu untersuchen, verwendet: eine OTS-Monoschicht mit aufrecht stehenden Molekülen und PTCDA-Schichten mit flach liegenden Molekülen. Metall-organische Grenzflächen spielen eine wichtige Rolle in organischen elektronischen Bauelementen. In-CuPc wird als Beispiel für ein Metall-organisches System durch in-situ SE und RAS untersucht. Wenn In thermisch auf eine CuPc-Schicht aufgedampft wird, diffundieren In-Atome zunächst in die darunterliegende CuPc-Schicht und bilden dann Cluster auf der Schicht. Hafniumdioxid (HfO2) ist ein heißer Kandidat für das Ersetzen des herkömmlich als Gate-Dielektrikum verwendeten SiO2 mit dem Ziel, die Leckströme bei der weiteren Verkleinerung mikroelektronischer Bauelemente zu minimieren. Um amorphe Schichten, die vorteilhaft zur Minimierung der Leckströme sind, zu erhalten, werden die HfO2-Schichten, die oft kristallin sind, mit Aluminiumoxid (Al2O3) (k-Wert: 9) kombiniert, das bei wesentlich höheren Temperaturen amorph bleibt. Zwei Serien von ultra-dünnen Proben wurden durch Atomlagenabscheidung hergestellt: Mischschichten HfxAl1-xOz und Doppelschichten HfO2 auf Al2O3. Die optischen Konstanten und Bandlücken wurden mittels SE im Energiebereich von 0,7 bis 10 eV bestimmt. Es hat sich gezeigt, dass die (effektive) Bandlücke der Misch- und Doppelschichten durch die Komposition abgestimmt werden kann. Nach Lagerung der High-k-Schichten für zwei Monate an Luft konnte ein Alterungseffekt beobachtet werden. Dieser wird auf die weitere Oxidation der dielektrischen Schichten, die durch Sauerstoffdiffusion aus der Umgebungsluft in die High-k-Schichten ermöglicht wird, zurückgeführt.

In dieser Arbeit wurde die atomare Struktur von Si(100)- und Ge(100)-Oberflächen untersucht, die mit metallorganischer chemischer Gasphasenabscheidung (MOCVD) für anschließende Heteroepitaxie von III-V-Halbleitern präpariert wurden. An der III-V/IV Grenzfläche werden atomare Doppelstufen auf der Substratoberfläche benötigt, um Antiphasenunordnung in den III-V-Schichten zu vermeiden. Die MOCVD-Prozessgasumgebung beeinflusst die Domänen- und Stufenbildung der Si- und Ge(100)-Oberfläche sehr stark. Deswegen wurden in situ Reflexions-Anisotropie-Spektroskopie (RAS) und Ultrahochvakuum-(UHV)-basierte oberflächensensitive Messmethoden verwendet, um die verschiedenen Oberflächen zu charakterisieren. In situ RAS ermöglicht die Identifizierung der Oberflächenstruktur und somit Kontrolle über die Oberflächenpräparation, insbesondere der Domänenbildung auf Si- und Ge(100). Beide Oberflächen wechselwirken stark mit dem H2-Prozessgas, was zu Monohydrid-Bedeckung während der Präparation führt und sogar zu Si-Abtrag während Präparation unter hohem H2-Druck. Die Erzeugung von Leerstellen auf den Terrassen bewirkt eine kinetisch bedingte Oberflächenstruktur, basierend auf Diffusion von Leerstellen und Atomen. Dadurch kommt es zu ungewöhnlichen DA-Doppelstufen auf verkippten Si(100)-Substraten während auf exakten Substraten ein schichtweiser Abtrag stattfindet. Unter niedrigem H2-Druck bildet sich eine energetisch bedingte Domänen- und Stufenstruktur. Während das H2-Prozessgas keinen direkten Einfluss auf die Stufen- und Domänenbildung von verkippten Ge(100)-Oberflächen zeigt, ist der Einfluss von Gruppe-V-Elemente entscheidend. Die As-terminierten Ge(100)-Oberflächen bilden eindomänige Oberflächen unterschiedlicher Dimerorientierung und Stufenstruktur abhängig von Temperatur und As-Quelle. Angebot von P an Ge(100)-Oberflächen durch Heizen in Tertiärbutylphosphin führt zu einer ungeordneten, P-terminierten Ge(100)-Oberfläche, die instabiler als die Ge(100):As-Oberfläche ist. / In this work, the atomic surface structure of Si(100) and Ge(100) surfaces prepared in metalorganic chemical vapor phase deposition (MOCVD) ambient was studied with regard to subsequent heteroepitaxy of III-V semiconductors. At the III-V/IV interface, double-layer steps on the substrate surface are required to avoid anti-phase disorder in the epitaxial film. The MOCVD process gas ambient strongly influences the domain and step formation of Si and Ge(100) surfaces. Therefore, in situ reflection anisotropy spectroscopy (RAS) and ultra-high vacuum-based (UHV) surface sensitive methods were applied to investigate the different surfaces. In situ RAS enabled identification of the surface structure and the crucial process steps, leading to complete control of Si and Ge(100) surface preparation. Both surfaces strongly interact with H2 process gas which leads to monohydride termination of the surfaces during preparation and Si removal during processing in high H2 pressure ambient. The generation of vacancies on the terraces induces a kinetically driven surface structure based on diffusion of vacancies and Si atoms leading to an energetically unexpected step structure on vicinal Si(100) substrates with DA-type double-layer steps, whereas Si layer-by-layer removal occurs on substrates with large terraces. Processing in low H2 pressure ambient leads to an energetically driven step and domain structure. In contrast, H2-annealed vicinal Ge(100) surfaces show no direct influence of the H2 ambient on the step structure. At the Ge(100) surface, group-V elements strongly influence step and domain formation. Ge(100):As surfaces form single domain surfaces with different majority domain and significantly different step structures depending on temperature and As source, respectively. In contrast, exposure to P by annealing in tertiarybutylphosphine leads to a very disordered P-terminated vicinal Ge(100) surface which is less stable compared to the Ge(100):As surfaces.

Diese Arbeit untersucht das Aufwachsen von dünnen GaP-Schichten auf Si(100)-Oberflächen mittels metallorganischer Gasphasenabscheidung (MOVPE) und die damit verbundene Entstehung von Antiphasendomänen (APDs). Die Vermessung der Si(100)-Substratoberfläche, der III-V/Si(100)-Grenzfläche und der abgeschiedenen GaP-Filme mit oberflächenempfindlichen Messverfahren dient der Etablierung APD-freier III-V-Heteroepitaxie auf Si(100). Die Präparation reiner Si(100)-Oberflächen frei von Sauerstoff in der MOVPE-Umgebung konnte durch Röntgenphotoelektronenspektroskopie (XPS) belegt werden. Vorwiegend doppelgestufte Substrate wurden sowohl auf 0.1°, 2° als auch 6° fehlorientierten Substraten erzielt. Im Widerspruch zu etablierten Ergebnissen im Ultrahochvakuum richteten sich die Dimere auf 0.1° und 2° Proben senkrecht zu den Doppelstufenkanten aus, vermutlich durch den Einfluss des Wasserstoffs in der MOVPE. Infrarotspektroskopie (FTIR) belegte eine Monohydridterminierung infolge der Präparation, während in-situ Reflexions-Anisotropie-Spectroskopie (RAS) zeigte, dass diese bei höheren Prozesstemperaturen nicht vorliegt. Für die GaP-Heteroepitaxie auf diesen Substraten wurde ein optisches in-situ Messverfahren für die quantitative Bestimmung des APD-Gehaltes entwickelt, welches auf dem eingehenden Verständnis der Rekonstruktionen von GaP(100), der assozierten RAS-Signaturen und dem mit Rastertunnelmikroskopie (STM) und Beugung niedrigenergetischer Elektronen (LEED) etablierten mikroskopischen Verständnis der Oberflächen beruht. Die APD-Quantifizierung mittels RAS wurde durch empirische Korrektur von Interferenzeffekten und optische Modellrechnungen, die auch Rückschlüsse auf die Grenzflächenanisotropie erlauben, deutlich verbessert. Der Abgleich mit unterschiedlichsten Mikroskopiemethoden, basierend auf niedrigenergetischen Elektronen (LEEM), Elektronentransmission (TEM) und Rasterkraftverfahren (AFM) bestätigt die erzielten Ergebnisse. / The present work investigates the growth of thin, pseudomorphic GaP films by metalorganic vapor phase epitaxy (MOVPE) on Si(100) surfaces by a variety of surface-sensitive methods and pays with specific attention to the substrate induced anti-phase disorder in this lattice matched model system for III-V/Si(100) heteroepitaxy. Thorough X-ray photoelectron spectroscopy investigations verified the preparation of clean Si(100) surfaces free of oxygen in the MOVPE ambient. Predominantly double-layer stepped Si(100) surfaces were obtained for 0.1°, 2°, and 6° misoriented substrates. In contrast to results established in ultra-high vacuum (UHV), double-layer steps with dimers oriented perpendicular to their edges were observed, which was attributed to the presence of hydrogen as a process gas in the MOVPE environment. A monohydride termination of Si(100) was determined after substrate preparation by Fourier-transform infrared spectroscopy (FTIR), while reflectance anisotropy spectroscopy (RAS) showed the absence of hydrogen termination at higher temperatures. Optical in situ spectroscopy was established as a method for the quantitative evaluation of anti-phase disorder in GaP heteroepitaxy based on a detailed understanding of the GaP(100) surface reconstructions, of the development of the corresponding RAS signatures, and of the associated surface structure studied by scanning tunneling microscopy (STM) and low-energy electron diffraction (LEED). The in situ RAS quantification was greatly improved by empirical correction of thin film interference and optical model calculations, which also enable extraction of the GaP/Si(100) interface anisotropy. The characterization was supported by benchmarking to atomic force microscopy (AFM) and transmission electron microscopy (TEM) results as well as to low energy electron microscopy (LEEM), which was used for surface sensitive visualization of anti-phase domains on a mesoscopic length scale.