This paper examines the styles, shapes, and chemical composition, and ceramic fabric of Minoan Barbotine Ware. During the Middle Minoan period, Barbotine Ware exemplifies the creative ingenuity of the Minoan potter. The vessels’ elaborate decorative motifs play an integral part in the development of Minoan pottery. Barbotine Ware remains an ill-defined tradition. This paper will analyze the styles and shapes of Barbotine Ware vessels, as well as provide a chemical and petrographic study of Barbotine Ware from Kommos. The ultimate goal is to provide a thorough study of all aspects of the Ware in the hopes that future scholars may better understand its place within Minoan pottery and appreciate how it exemplifies the spirit of experimentation during the Middle Bronze Age on Crete. / Art History

Les superalliages base nickel sont couramment utilisés dans les parties chaudes des turbines aéronautiques et de production d'énergie. Les températures employées, supérieures à 900°C, nécessitent de concevoir des revêtements protecteurs pour lutter contre les phénomènes d'oxydation. Les revêtements couramment utilisés, composés pour la plupart de la phase β-NiAl, permettent de retarder les phénomènes de dégradation en développant une couche d'alumine. Dans les sections les plus chaudes, une barrière thermique composée de céramique, associée à un système de refroidissement interne complètent le dispositif de protection en permettant d'abaisser la température effective au niveau du substrat métallique.Ces revêtements sont cependant onéreux et utilisent de nombreux produits polluants. Les travaux de cette thèse, qui s'inscrivent dans le cadre du projet européen Particoat, se proposent d'élaborer un système barrière thermique en une seule étape reposant sur l'application d'une barbotine à base aqueuse comprenant des microparticules d'aluminium, suivi d'un traitement thermique approprié. L'aluminium contenu dans les sphères devient liquide puis réagit avec le substrat pour former une couche d'intermétallique riche en aluminium par diffusion à l'état solide. Simultanément les coquilles des sphères s'oxydent pour former une structure mousse en surface du substrat qui va conférer au système son isolation thermique. La cohésion des deux parties est assurée par l'oxyde thermique qui se forme à la surface du revêtement inter métallique. Les mécanismes mis en jeu lors des différentes étapes, ont été étudiés sur un substrat modèle, le nickel, ainsi que sur trois superalliages industriels (René N5, PWA 1483 et CM-247). Les revêtements ainsi élaborés ont été testés en condition d'oxydation isotherme et cyclique entre 900 et1100°c pour le nickel et entre 1000 et 1100°C pour les superalliages revêtus. L'ensemble montre une bonne résistance du système barrière thermique élaboré par barbotine.

Devant l’augmentation constante de la demande énergétique mondiale, la protection des installations électriques contre les effets de la foudre ou des instabilités du réseau nécessite des équipements toujours plus performants et adaptés. La technologie céramique apporte une solution à ce problème grâce à des dipôles à base d’oxyde de zinc possédant des propriétés électriques non linéaires se traduisant par une décroissance de leur résistance à mesure que la tension augmente. La tendance actuelle dictée par des défis technico-économiques et les nouvelles normes européennes conduit à réduire le poids et les dimensions de ces dipôles ou varistances : L’objectif et les principaux résultats de cette thèse sont : 1- Transfert à l’échelle pilote (100kg) de varistances miniaturisées à très haute tenue énergétique pouvant supporter plus de 300J.cm-3 en onde rectangulaire de courant de 800A en conformité avec la norme CEI 600 99-4 de 2006 [Classe III 10kA-5kV] 2- Pour atteindre les objectifs, il a été nécessaire d’abaisser les tensions d’écrêtage de 3%±0.2%. Ce fléchissement est apparemment modeste mais il est associé à une augmentation de la densité de courant traversant la céramique de plus de 30% / With the constant increase of world energy demand, the protection of electrical installations against the effects of lightning or network's instabilities, requires equipment more powerful and adapted. Ceramic technology brings a solution to this problem thanks to zinc oxide dipoles having nonlinear electric properties resulting in a decrease of their resistance as the tension increases. The current trend driven by technico-economic challenges and new European standards results in reducing the weight and dimensions of these dipoles or varistors: The objective and the principal results of this thesis are: 1- Transfer on the semi-industrial scale (100kg) of miniaturized varistors with very high energy capability being able to support more 300J.cm-3 in rectangular wave of current of 800A in conformity with standard CEI 600 99-4 of 2006 [Class III 10kA-5kV] 2- To achieve these goals, it was necessary to lower the clamping voltage of 3%±0.2%. This bending is apparently modest but it is associated with an increase of current density crossing the ceramics of more than 30%

En raison de leur bonne résistance mécanique à haute température, les superalliages base nickel sont employés dans les turbines aéronautiques et de production d’énergie. Ils doivent alors être capables de résister aux phénomènes d’oxydation « sèche » intervenant entre 900 et 1500°C. Ces matériaux sont donc protégés par des revêtements à base d’aluminure de nickel (β-NiAl). De plus, dans les sections les plus chaudes des turbines (T>1050°C), une barrière thermique (BT) est ajoutée afin de diminuer l’impact de la température sur le substrat. Dans le cadre du projet de recherche Européen « PARTICOAT », le travail décrit dans cette thèse a porté sur l’élaboration d’un système complet de revêtements protecteurs (BC+BT) à l’aide d’un procédé en une seule étape, à partir d’une barbotine obtenue par dispersion de microparticules d’Al dans une base aqueuse, milieu susceptible de satisfaire aux directives environnementales européennes. Des caractérisations rhéologique et physico-chimique ont montré la stabilité de la barbotine jusqu’à sept jours. Après dépôt de cette dernière par pulvérisation, un traitement thermique adapté a conduit, via la formation intermédiaire d’Al liquide, à l’obtention d’un revêtement d’aluminure de nickel (β-NiAl) comparable à ceux obtenus par les procédés industriels actuels. L’oxydation des particules d’Al permet la formation simultanée d’une « mousse » d’alumine (concept PARTICOAT) superficielle. Après validation des mécanismes réactionnels mis en jeu sur un substrat modèle de nickel pur, l’extrapolation du procédé à différents superalliages base nickel (René N5 (SX), CM-247 (DS), PWA-1483 (SX) et IN-738LC (EQ)) a donné des revêtements présentant différentes compositions et microstructures. Un intérêt particulier a alors été porté sur l’étude de l’influence des éléments d’alliage (Cr, Ta, Ti) et de leur ségrégation au sein du revêtement. Le comportement à haute température des échantillons revêtus a pu être évalué à l’aide de tests d’oxydation isotherme (1000h sous air entre 900 et 1100°C). Il a ainsi été montré que les phénomènes d’oxydation et d’interdiffusion régissent les mécanismes de dégradation. Par ailleurs, l’électrodéposition de cérine préalablement à l’application du procédé de revêtement PARTICOAT a permis de limiter fortement les phénomènes d’interdiffusion et de stabiliser la couche d’aluminure de nickel. / Because of their good mechanical resistance at high temperature, Ni-based superalloys are used for aero-engine and land-based turbines but undergo “dry” oxidation between 900 and 1500°C. These materials are thus coated with nickel-aluminide coatings (BC). An additional thermal barrier coating (TBC) is generally applied in the hottest sections of the turbines (T>1050°C) to lower the impact of the temperature on the substrate. In the framework of the European research programme “PARTICOAT”, this PhD work was focused on the growth mechanisms of a full protective coating system (BC+TBC) in a single step process, using a water-based slurry containing a dispersion of Al micro-particles to satisfy the European environmental directives. The rheological and physico-chemical characterizations showed the slurry stability up to seven days. After depositing the latter by air spraying, a tailored thermal treatment resulted in a nickel-aluminide coating (β-NiAl) similar to the conventional industrial ones but through an intermediate Al liquid phase stage. Simultaneously, the oxidation of the Al micro-particles brought aboutthe formation of a top alumina “foam” (PARTICOAT concept). After a validation step of the mechanisms involved in pure Ni substrate, the extrapolation of the process to several Ni-based superalloys (René N5 (SX), CM-247 (DS), PWA- 1483 (SX) and IN-738LC (EQ)) revealed different coating compositions and microstructures. A particular attention was therefore paid onto the effect of alloying elements (Cr, Ta, Ti) as well as their segregation in the coating. The high temperature behaviour of the coated samples has been studied through isothermal oxidation (1000h in air between 900 and 1100°C) and showed that the oxidation and interdiffusion phenomena ruled the degradation mechanisms. Besides, the electrodeposition of ceria before the application of the PARTICOAT coating allowed to strongly limit interdiffusion phenomena and stabilized the nickel aluminide coating.

Les superalliages base nickel sont couramment utilisés dans les parties chaudes des turbines aéronautiques et de production d’énergie. Les températures employées, supérieures à 900°C, nécessitent de concevoir des revêtements protecteurs pour lutter contre les phénomènes d’oxydation. Les revêtements couramment utilisés, composés pour la plupart de la phase β-NiAl, permettent de retarder les phénomènes de dégradation en développant une couche d’alumine. Dans les sections les plus chaudes, une barrière thermique composée de céramique, associée à un système de refroidissement interne complètent le dispositif de protection en permettant d’abaisser la température effective au niveau du substrat métallique.Ces revêtements sont cependant onéreux et utilisent de nombreux produits polluants. Les travaux de cette thèse, qui s’inscrivent dans le cadre du projet européen Particoat, se proposent d’élaborer un système barrière thermique en une seule étape reposant sur l’application d’une barbotine à base aqueuse comprenant des microparticules d’aluminium, suivi d’un traitement thermique approprié. L’aluminium contenu dans les sphères devient liquide puis réagit avec le substrat pour former une couche d’intermétallique riche en aluminium par diffusion à l’état solide. Simultanément les coquilles des sphères s’oxydent pour former une structure mousse en surface du substrat qui va conférer au système son isolation thermique. La cohésion des deux parties est assurée par l’oxyde thermique qui se forme à la surface du revêtement inter métallique. Les mécanismes mis en jeu lors des différentes étapes, ont été étudiés sur un substrat modèle, le nickel, ainsi que sur trois superalliages industriels (René N5, PWA 1483 et CM-247). Les revêtements ainsi élaborés ont été testés en condition d’oxydation isotherme et cyclique entre 900 et1100°c pour le nickel et entre 1000 et 1100°C pour les superalliages revêtus. L’ensemble montre une bonne résistance du système barrière thermique élaboré par barbotine. / Nickel superalloys are commonly used in the high temperature sections of aero- and land-based turbines blades. Protection of these materials by coatings is required to improve their resistance to oxidation beyond 900°C. The conventional process consists of a β-NiAl, which allows to form a protective alumina scale with alow oxidation kinetic. In the hottest parts of the turbine, a ceramic is used as a thermal barrier coating in addition to an internal cooling system in order to diminish the temperature seen at the metallic substrate surface. However, these existing methods are expensive, long and pollutant. Thus, this PhD thesis aims at producing a new thermal barrier system in one step, in the frame of the European project Particoat. Its concept is to apply on the substrate an aqueous slurry containing aluminum microparticles. Then, during an appropriate heat treatment the metallic particles sinter and oxidize completely resulting in a quasi-foam structure made of alumina hollow spheres (TBC). Simultaneously, the diffusion of the Al into the substrate creates a bond coat below the TBC. This coating formation is studied on model alloy (pure nickel) and on three different superalloys (René N5, PWA-1483 and CM-247). The pure nickel coated system is tested during isothermal and cyclic oxidation between 900°C and 1100°C whereas the degradation of the superalloys is realized upon cyclic oxidation at 1000°C and 1100°C. The overall results show a good resistance of this new thermal barrier system, enlightened by an industrial aluminide coatings comparison.

L'excès de réactivité neutronique dans les centrales nucléaires est compensé par des sys-tèmes actifs de contrôle du réacteur : acide borique et barres de contrôle. L'apport d'antiréactivité peut se faire passivement avec des poisons consommables, c'est-à-dire des absorbants de neutrons, en particulier avec du gadolinium (Gd). Dans le cadre d'une augmentation de l'enrichissement en U²³⁵ et de réduction de l'utilisation d'acide borique, cette thèse a pour objectif d'optimiser la distribution du ga-dolinium dans des céramiques d'UO₂ afin d'obtenir un apport optimisé d'antiréactivité dans un Réacteur à Eau sous Pression. Dans ce sens, le travail est orienté à trouver des nouveaux matériaux riches en gadoli-nium. Le diagramme de phase U-O-Gd a donc été exploré dans le domaine des fortes teneurs en Gd. Deux phases cubiques ont été trouvées et caractérisées : les phases C1 et C2. En vue d'une application industrielle, la phase C1 a été retenue comme candidate pour l'ajout du Gd dans les pastilles d'UO₂. La distribution optimale de cette phase C1 dans les assemblages de combustible nucléaire a été étudiée avec le code de calcul neutronique APOLLO2.8. Des études paramétriques ont été réalisées. Ces études neutroniques ont aboutit à un concept performant de pas-tille empoisonnée. Finalement, des pastilles prototype ont été fabriquées en laboratoire suivant ce concept. L'ensemble des résultats obtenus montre qu'un concept de pastille avec un dépôt super-ficiel neutrophage de phase C1 est une manière d'apporter de l'antiréactivité de manière optimisée dans le cadre de cycles longs. Ceci pourrait potentiellement être appliquée à l'échelle industrielle. Un brevet a été déposé en ce sens.