Dissertação (mestrado) - Universidade Federal de Santa Catarina. Centro Tecnologico / Made available in DSpace on 2016-01-08T16:10:41Z (GMT). No. of bitstreams: 1 83538.pdf: 2778171 bytes, checksum: 8b9dbcd52cc329f9fdecd94fbe76b245 (MD5) Previous issue date: 1988 / No Sul do Estado de Santa Catarina encontram-se concentradas algumas das micro e pequenas empresas dedicadas à produção de elementos cerâmicos estruturais, normalmente de cor vermelha, utilizando as argilas encontradas na região. Com base nos dados colhidos em entrevistas diretas com empresários e em visitas realizadas às indústrias de uma amostra do Vale do Rio Urussanga, são estabelecidos, sempre que possível, de forma quantitativa os parâmetros principais que caracterizam a situação daquela fatia do ramo produtivo da cerâmica. A partir dos parâmetros obtidos e de dados adicionais colhidos junto a outros participantes indiretos do setor, realizam-se as análises do sistema industrial e a estratégia das quais se depreende a fragilidade em que se encontra aquele grupo de unidades produtivas, bem como apontam-se as causas para este fato. Na conclusão do estudo sugere-se a reunião dos empresários, de forma associativa, formando um corpo mais resistente para o enfrentamento das instabilidades a que se encontram submetidos.

Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnologico / Made available in DSpace on 2016-01-08T22:26:22Z (GMT). No. of bitstreams: 1 108495.pdf: 18631914 bytes, checksum: b5432dfe69086048bc267434c5e75200 (MD5) Previous issue date: 1997 / As operações classificadas como usinagem a verde de cerâmica são aquelas que ocorrem após a compactação inicial do corpo cerâmico, até aquelas anteriores à sinterização total da peça. A usinagem a verde é uma solução para contornar as dificuldades encontradas na usinagem de materiais cerâmicos sinterizados, onde os altos custos de usinagem são responsáveis pela maior parte dos custos de produção. As propriedades que tornam os materiais cerâmicos avançados atrativos, como por exemplo a dureza e a estabilidade a altas temperaturas e sob condições corrosivas, excluem a maioria das técnicas tradicionais de usinagem. Neste trabalho é apresentada uma tecnologia inovadora de corte de corpos cerâmicos de alumina verde com uma nova ferramenta, o fio diamantado com movimento alternante. É mostrada a viabilidade técnica do recorte de componentes de geometria complexa e analisado o limite tecnológico do processo para cortes retilíneos com movimento de avanço automatizado da peça para diversas espessuras de fio e corpos de alumina pré-sinterizados a diferentes temperaturas, variando-se a altura da peça e as velocidades de corte e de avanço.

Tese (doutorado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2016 / Made available in DSpace on 2016-09-20T04:43:14Z (GMT). No. of bitstreams: 1 340519.pdf: 20067846 bytes, checksum: 217bd22919cc06cb7bc6895571a11ab0 (MD5) Previous issue date: 2016 / O objetivo deste estudo foi avaliar a influência do desenho do preparo de restaurações cerâmicas do tipo faceta na integridade marginal imediata e após 5 anos de envelhecimento simulado, em diferentes regiões do dente. Material e métodos. Foram selecionados 30 dentes pré-molares superiores humanos hígidos e divididos aleatoriamente em 3 grupos (n=10), de acordo com o desenho do preparo da restauração cerâmica: G1: faceta total com preparo (Convencional); G2: faceta total sem preparo (Lente de Contato); G3: faceta parcial sem preparo (Fragmento). Os preparos do G1 foram controlados por meio de guias de silicone (vertical e horizontal, 0,5 mm redução axial vestibular). Os dentes foram incluídos em resina de poliestireno com simulação do ligamento periodontal. Trinta restaurações cerâmicas de dissilicato de lítio foram produzidas utilizando tecnologia CAD/CAM com espessura padronizada 0,5 mm e espaço interno 100 µm. As restaurações cerâmicas foram cimentadas adesivamente e envelhecidas com ciclagem termo-mecânica (CTM) (1.200,000 ciclos mastigatórios; 50 N; 2 Hz; e 6.000 ciclos térmicos 5o / 55o C, 2 min cada ciclo) para simular 5 anos de serviço clínico. Os espécimes foram escaneados por microtomografia computadorizada por raios-X (Micro-CT) para análise 3D da adaptação marginal (µm) em três regiões (cervical, proximal, oclusal) antes e após a CTM. Os dados foram analisados estatisticamente pelo ANOVA de 2 fatores, seguido pelo teste de Tukey (?? = 5%). Resultados. Os resultados de adaptação marginal (µm) e desvio padrão antes a CTM para as regiões cervical, oclusal e proximal, respectivamente foram: G1 (51,5 ± 9,4; 51,5 ± 21,8; 59,7 ± 12,9), G2 (45,3 ± 9,7; 65,1 ± 11,8; 52,0 ± 7,0), G3 (55,0 ± 9,5; 84,8 ± 52,1; 48,0 ± 3,7). Após a CTM: G1 20 (105,0 ± 28,2; 120,6 ± 34,0; 65,0 ± 10,8), G2 (103,5 ± 22,7; 127,3 ± 45,4; 61,9 ± 7,6), G3 (101,9 ± 6,5; 167,5 ± 37,6; 58,5 ± 4,4). Houve maior aumento da fenda marginal para o grupo G3 na região oclusal após a CTM, acima do limite aceitável clinicamente (120 µm). A fenda marginal na região proximal foi estatisticamente menor para todos os grupos após a CTM. Conclusões. O desenho do preparo para facetas cerâmicas influenciou significativamente na formação de fendas marginais após 5 anos de envelhecimento simulado. As facetas convencionais e lentes de contato apresentaram significativamente menor aumento das fendas marginais quando comparadas aos fragmentos na região oclusal, que obtiveram resultados acima do limite aceitável clinicamente. A região proximal foi a região mais estável. <br> / Abstract : The purpose of this study was to evaluate the influence of the preparation design for ceramic veneers on the immediate marginal integrity and after 5 years of simulated aging, in different regions of the tooth. Material and methods. Thirty freshly sound human superior premolars were selected and randomly divided into 3 groups (n = 10), according to the preparation design of the ceramic veneer restoration: G1/Conventional: total veneer with preparation; G2/Contact Lens: total veneer without preparation; G3/Fragment: partial veneer without preparation. The preparations for the group Conventional were controlled by means of silicone guides (vertical and horizontal, 0.5 mm buccal axial reduction). The teeth were embedded in polystyrene resin with periodontal ligament simulation. Thirty lithium disilicate ceramic restorations were produced using CAD/CAM technology with standard thickness (0.5 mm) and internal space (100 µm). Ceramic restorations were adhesively cemented and the specimens were aged with a proven thermomechanical cycling protocol (TMC) (1200000 chewing cycles, 50 N, 2 Hz, and 6000 thermal cycles, 5/55 ° C, 2 min per cycle) to simulate five years of clinical service. All specimens were scanned by micro-computed tomography (micro-CT) for 3D analysis of the marginal adaptation (µm) in three areas (cervical, proximal, occlusal) before and after the TMC. The means were calculated and data were statistically analyzed by ANOVA two factors, followed by Tukey test (a = 5%). Results. The results of marginal fit (µm) and standard deviation before TMC for cervical, 22 occlusal and proximal regions respectively were: Conventional (51.5 ± 9.4, 51.5 ± 21.8, 59.7 ± 12.9) Contact Lens (45.3 ± 9.7, 65.1 ± 11.8, 52.0 ± 7.0), Fragment (55.0 ± 9.5, 84.8 ± 52.1; 48.0 ± 3.7). After the TMC: Conventional (105.0 ± 28.2, 120.6 ± 34.0, 65.0 ± 10.8) Contact Lens (103.5 ± 22.7, 127.3 ± 45 4; 61.9 ± 7.6), Fragment (101.9 ± 6.5, 167.5 ± 37.6, 58.5 ± 4.4). The variation before and after the TMC: Conventional (53.5 ± 29.2, 69.1 ± 53.6, 5.3 ± 5.0), Contact Lens (58.2 ± 28.2; 62 2 ± 43.4, 9.9 ± 3.7), Fragment (46.9 ± 3.0, 82.7 ± 45.8, 10.5 ± 2.5). There was a significantly greater increase in marginal gap for the group Fragment in the occlusal region after the TMC, above the clinically acceptable limit of 120 µm (p < 0.05). The marginal gap in the proximal region was significantly lower for all groups after the TMC (p < 0.05). Conclusions. The preparation design for ceramic veneers significantly influenced the marginal gaps formation after 5 years of simulated aging. Conventional and contact lens veneers presented a significantly lower increase in marginal gaps compared to fragments in the occlusal region, which revealed results above the clinically acceptable limit. The proximal region was the most stable region.

Made available in DSpace on 2014-06-11T19:35:02Z (GMT). No. of bitstreams: 0 Previous issue date: 2012-08-02Bitstream added on 2014-06-13T19:05:08Z : No. of bitstreams: 1 macedo_vc_dr_sjc.pdf: 1078267 bytes, checksum: eb074f00cda8aebeaed5f9a49ae91eac (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / As cerâmicas são indicadas para coroas livres de metal, pois alcançaram resistência suficiente para resistir às cargas funcionais. O objetivo neste estudo foi avaliar a resistência à flexão de barras cerâmicas, após diferentes tempos de condicionamento com ácido fluorídrico, e diferentes protocolos de envelhecimento. Foram confeccionadas 500 barras cerâmicas com dimensões de 16 mm x 4 mm x 2 mm, sendo 250 para cada tipo de cerâmica. As barras foram lixadas e polidas e distribuídas em 5 grandes grupos com 50 amostras cada e foram condicionadas com ácido fluorídrico a 10%, variando os tempos de condicionamento entre 20, 30, 40, 60 e 90 segundos. Posteriormente, foi aplicado o agente silano e uma camada fina de cimento resinoso dual. Foram então subdivididas em 5 diferentes meios de envelhecimento: termociclagem, ciclagem mecânica, ciclagem termomecânica, ciclagem intra-bucal e controle. Após os ciclos, as amostras foram submetidas ao teste de resistência à flexão, em uma máquina de ensaio universal EMIC, com velocidade de 1mm/min. Os valores médios forma submetidos a análise estatística ANOVA 2 fatores e comparação de Tukey 5%. Para a cerâmica feldspática tanto o grupo controle quanto o grupo submetido à ciclagem termomecânica apresentaram valores mais homogêneos em relação ao tempo de condicionamento. No grupo submetido à ciclagem mecânica, houve um aumento da resistência quando condicionado por 90 segundos. No grupo ciclado termicamente houve uma queda nos valores de resistência quando condicionados por 40 segundos, e no grupo intra-bucal, uma queda quando condicionados por 60 segundos. Uma expressiva diferença foi encontrada entre os grupos condicionados por 40 e 60 segundos, ambos submetidos à ciclagem intra-bucal. Para a cerâmica de dissilicato de lítio o maior valor... / Ceramics can be indicated for metal free crowns, since they have reached sufficient strength to withstand functional loads. The objective of this study was to evaluate the flexural strength of feldspathic bars and lithium disilicate, after different times of etching with hydrofluoric acid, and different protocols of aging. Five hundred bars (16 mm x 4 mm x 2 mm) were prepared, 250 for each type of ceramic. The bars were grounded, polished and distributed in 5 groups of 50 samples each and were etched with 10% hydrofluoric acid, varying the conditioning time (20, 30, 40, 60 and 90 seconds). Subsequently, the silane agent was applied followed by a thin layer of dual resin cement. Samples were then divided into five different ways of aging: thermal cycling, mechanical cycling, thermomechanical cycling, intra-oral cycling and control. After the cycles, the samples were subjected to flexural strength testing in a universal testing machine (EMIC), at a speed of 1 mm / min. Mean values were submitted to two-way ANOVA and Tukey test (α =5%). Both feldspathic ceramic control group and the group submitted to thermomechanical cycling showed more homogeneity regarding the conditioning time. In the group submitted to mechanical loading, there was an increase in the resistance when conditioning for 90 seconds. The thermally cycled group presented decrease in the strength values when conditioned for 40 seconds, and the intra-oral group, a decrease when conditioned for 60 seconds. The most significant difference was found between the groups conditioned for 40 and 60 seconds, both when submitted to intra-oral cycling. For lithium disilicate ceramic, the highest value of flexural strength was obtained in the control group, conditioned for 90 seconds. The lower values of flexural strength were found in groups submitted to intra-oral... (Complete abstract click electronic access below)

Este trabalho avalia o efeito da adição de diferentes resíduos, todos de baixa granulometria e gerados não muito distantes de empresas fabricantes de produtos de cerâmica vermelha, quando incorporados a argilas para processamento cerâmico tradicional. Foram utilizadas argilas da região de Sangão e Forquilhinha (Santa Catarina), bem como os seguintes resíduos: resíduo siderúrgico da produção de aço em forno elétrico (pó de aciaria), resíduo de atomizador de uma indústria de revestimentos cerâmicos e resíduo do polimento de grês porcelanato. Após a caracterização das matérias-primas, foram formuladas massas cerâmicas na relação argila/resíduo de 5:1 para cada resíduo. E, como padrão de comparação, utilizou-se a formulação apenas com argilas. As massas cerâmicas foram conformadas por prensagem e submetidas à queima em forno elétrico tipo mufla nas seguintes temperaturas 800, 900, 950, 1000 e 1100oC. Os corpos cerâmicos assim obtidos foram caracterizados segundo suas propriedades físicas (retração linear e absorção de água – curva de gresificação) e mecânicas (resistência mecânica à flexão a quatro pontos). Além disso, os corpos cerâmicos fabricados, utilizando pó de aciaria (resíduo perigoso segundo a ABNT), foram avaliados segundo as normas NBR 10005 e NBR 10006, quanto ao seu aspecto ambiental. Os resultados mostraram a viabilidade do uso destes resíduos na fabricação de produtos cerâmicos. As propriedades finais e a cor de queima (entre marrom claro e marrom escuro) variaram de acordo com a natureza do resíduo e temperatura de queima. A formulação testada com pó de atomizador de industria cerâmica apresentou em todas as temperaturas ensaiadas os maiores incrementos de resistência mecânica em relação às formulações testadas, sendo que à temperatura de 1100oC, a formulação com pó de aciaria apresentou desempenho similar, porém com menor absorção de água e maior retração linear. Nestas condições, os corpos cerâmicos com pó de aciaria mostraram-se inertes quanto ao aspecto ambiental de acordo com as normas Brasileiras.

Orientador: José de lós Santos Guerra / Banca: Devaney Ribeiro do Carmo / Banca: Michel Venet Zambrano / Resumo: O presente trabalho tem como objetivo a síntese de cerâmicas ferroelétricas do sistema titanato e zirconato de chumbo modificado com lantânio, considerando a ocorrência de vacâncias nos sítios A ( e B ( da estrutura perovskita, através das fórmulas químicas estequiométricas ( ) e , respectivamente, onde x representa a fração molar de lantânio, com valores de 0,02; 0,04; 0,06; 0,08; 0,10 e 0,12 e y = 0,70 (representando a razão de Zr/Ti=70/30). Os pós-utilizados para a conformação das cerâmicas foram sintetizados pelo método convencional de Reação do Estado Sólido (RES), também conhecido por mistura convencional de óxidos ou método cerâmico tradicional. A calcinação foi realizada a 900°C por 2 horas. Amostras cerâmicas em forma de pastilhas foram obtidas mediante prensagens uniaxial e isostática, seguido pelo processo de sinterização à temperatura de 1250°C durante 2 horas, em atmosfera rica em chumbo. Para obter a temperatura dos eventos térmicos foi utilizada a técnica de Análise Térmica Diferencial (DTA). A formação das fases ferroelétricas desejadas foi verificada por Difração de Raios-X (DRX), realizada à temperatura ambiente nas amostras em forma de pó-calcinado e posteriormente nas pastilhas cerâmicas sinterizadas. Para algumas composições uma pequena concentração de PbO sem reagir foi observada. Amostras cerâmicas com densidades maiores que 88,5% foram obtidas. Utilizou-se a técnica de Microscopia Eletrônica de Varredura (MEV) para investigar as características microestruturais das cerâmicas, revelando um tamanho médio dos grãos em escala micrométrica (m) para todas as composições estudadas. A microanálise por Energia Dispersiva de Raios-X (EDX) confirmou a composição desejada em todos os casos. As propriedades dielétricas foram investigadas em uma ampla faixa de frequência e temperatura, a fim de se obter a temperatura de Curie ... / Abstract: The objective of the present work was related to the synthesis of lanthanum modified lead zirconate titanate ferroelectric ceramics, considering the occurrence of vacancies at the A-site ( or B-site ( of the perovskite structure, through the stoichiometric chemical formulas ( ) and , respectively, where x is the molar fraction of lanthanum with values of 0.02, 0.04, 0.06, 0.08, 0.10 and 0.12, and y = 0.70 (representing the Zr/Ti=70/30 ratio). The method used for the synthesis of the samples was the Solid State Reaction (SSR), well known as the conventional oxide mixture or ceramic method. The calcination process was performed at 900° C for 2h. Pellets-shaped ceramics samples were obtained from uniaxial and isostatic pressing, followed by the sintering process at a temperature of 1250°C, during 2h, under lead atmosphere containing, being that for some compositions low concentration of PbO was observed. For determining the temperature of thermal events was used technique called Differential Thermal Analysis (DTA). The formation of the desired ferroelectric phases was confirmed by X-ray Diffraction (XRD), room at temperature, performed on the calcined powder and the sintered ceramic samples. The Scanning Electron Microscopy (SEM) technique was used to investigate the microstructure of the ceramics, revealing an average grains size on m scale. The EDS microanalysis confirmed the desired composition. The dielectric properties were investigated in a wide frequency range and temperature in order to obtain the Curie temperature (TC) and verify the dielectric character of the studied system. The obtained results have been discussed and compared according to the theories described in the current literature / Mestre

A moldagem por injeção em baixa pressão (MIBP) é uma técnica que já vem sendo empregada na produção de peças cerâmicas com formas e geometrias complexas. A composição e a homogeneidade da mistura de ligantes orgânicos e pós cerâmicos, são fatores determinantes que devem ser controlados para minimizar a formação de imperfeições no processamento do feedstock2 para MIBP. Defeitos típicos de processamento por MIBP, como bolhas de ar e aglomerados, geram gradientes de densidade nas misturas, que após conformadas, possuem poucas possibilidades de remoção. Essas imperfeições comprometem o desempenho dos produtos obtidos por essa técnica. Sendo assim, este trabalho tem por objetivo avaliar a influência que variáveis de processo, tais como o tipo de misturador, o uso ou não de vácuo durante o processamento e o tempo de mistura, exercem na densidade aparente das amostras a verde. Também foi analisada a influência que a distribuição do tamanho de partículas, os modificadores de superfície e o percentual de cera de carnaúba exercem no comportamento reológico dessas misturas. Para tanto, usou-se alumina submicrométrica (como recebida ou desaglomerada), foi adicionada a uma mistura fundida de ligantes (a base de parafina, ceras e aditivos) e processada em dois tipos diferentes de misturadores, com e sem o auxílio de vácuo. Além disso, foram preparadas misturas variando-se a composição, trocando o modificador de superfície utilizado ou alterando o percentual de cera de carnaúba presente no veículo orgânico (V.O.). Foi observada a presença de aglomerados na alumina como recebida, possivelmente gerados durante a etapa de calcinação. Também foi observado que o tipo de misturador e a aplicação ou não de vácuo durante a etapa final do processamento tem grande influência na densidade das amostras a verde, bem como na viscosidade do feedstock para a injeção. Além disso, observou-se que a composição com dois modificadores de superfície (ácido oleico e ácido esteárico) apresenta viscosidade menor do que quando se usa um único agente modificador de superfície. Finalmente, foi observado que a adição de cera de carnaúba diminui exponencialmente a viscosidade das amostras a verde, abrindo assim a possibilidade de aumentar o percentual de sólidos ou diminuir o tempo de processamento, o que pode auxiliar na redução de custos na produção de peças cerâmicas utilizando o método de moldagem por injeção em baixa pressão. / Submitted by Marcelo Teixeira (mvteixeira@ucs.br) on 2014-06-24T11:41:34Z No. of bitstreams: 1 Dissertacao Pedro Antonio Ourique.pdf: 3076704 bytes, checksum: 94abb2518ac1b55ce6f8e3359d025a97 (MD5) / Made available in DSpace on 2014-06-24T11:41:34Z (GMT). No. of bitstreams: 1 Dissertacao Pedro Antonio Ourique.pdf: 3076704 bytes, checksum: 94abb2518ac1b55ce6f8e3359d025a97 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Low-pressure injection molding (LPIM) is a technique that has been used in the production of ceramic parts with complex shapes and geometries. The composition and homogeneity of the mixture of ceramic powder and organic binders are determining factors that must be controlled to minimize the defect formation in LPIM parts. Typical defects generated in LPIM processing, such as bubbles and agglomerates, form density gradients in the mixtures, that after molded, have a low probability of removal. These imperfections compromise the performance of the products obtained by this technique. Therefore, this work aims to evaluate the influence of process variables (such as mixers, the use or not of vacuum during the processing and mixing time), on the apparent density of green samples. It was also evaluated the influence of particle size distribution, the surface active agents and the percentage of carnauba wax on the rheological behavior of these mixtures. For that, purpose submicrometric alumina (as received and deagglomerated), was added to a molten binder mixture (based on paraffin wax and additives) and processed in two different mixers, with and without vacuum assistance. Furthermore, mixtures were prepared varying the composition, changing the surface active agent used or modifying the percentage of carnauba wax presents in the organic vehicle (O.V.). It was observed the presence of alumina agglomerates in the powder as received, possibly generated during the calcination step. It was also observed that the kind of the mixer and the application or not of vacuum during the final stage of process has a great influence on the density of green samples, as well as in the viscosity of feedstock for injection. Furthermore, it was observed that the mixture with two surface active agents (oleic acid and stearic acid) presents lower viscosity than only one surface active agent. Finally, the addition of carnauba wax reduces exponentially the viscosity of feedstock, allowing the possibility to increase the percentage of solids or reduce the time of processing, which can help in the production cost reduction of ceramic parts using the low-pressure injection molding method.

Resumo: Neste trabalho, apresenta-se uma rota alternativa para produção de cerâmicas de mulita (3Al2O3.2SiO2), a partir da mistura de pós de alumina (Al2O3) e sílica (SiO2), para uma possível aplicação em um dispositivo de perfuração de rochas por jato supersônico quente (thermal spallation). Os pós precursores foram utilizados de dois modos diferentes: no primeiro com tamanho micrométrico, tal como fornecido pelos fabricantes; no segundo, a alumina foi moída e misturada separadamente com ácido silícico e aerosil nanométricos, ambos usados como fontes de sílica. O processo consistiu basicamente na mistura a úmido dos pós, secagem, prensagem e sinterização. Além do tamanho das partículas dos pós, foi avaliada a influência da pressão de prensagem (40 a 300 MPa), dos aditivos de sinterização (MgO, CaO e Y2O3), do meio de dispersão (água e álcool), da calcinação dos pós, da temperatura (1600 e 1650 ºC) e do tempo (1 e 3h) de sinterização. As cerâmicas obtidas foram caracterizadas de acordo com a contração, perda de massa, porosidade e densidade aparente e resistência à flexão. A microestrutura foi caracterizada por meio da microscopia óptica e microscopia eletrônica de varredura (MEV), e complementada com difração de raios X. Os resultados obtidos mostram que cerâmicas de mulita para aplicações comerciais, que requerem resistência mecânica até aproximadamente 207 MPa, podem ser obtidas utilizando pós de alumina moída e aerosil 380, com 1 % de CaO, homogeneizadas com álcool, calcinadas a 600 ºC, prensadas com 160 MPa (ou mais), pré-sinterizadas a 1000 ºC por 1h e sinterizadas a 1650 ºC por 1h. Estas cerâmicas demonstram também, grande potencial para uso em queimadores para fornos e tubeiras para thermal spallation. / Abstract: The present study was made in order to obtain an alternative process to produce mullite ceramic (3Al2O3.2SiO2), from powder mixture of alumina (Al2O3) and silica (SiO2), for a possible use in a device for rock drilling hot supersonic jet (thermal spallation). The precursors powders were employed in two different ways: the first powder, in micrometric size, was used as supplied by the manufacturer; the second, milled alumina was alternated with silicic acid and nanometric aerosil®, both used as silica sources. The ceramic processing consisted basically of four steps: mixture of humid powders, drying, pressing and sintering. Besides the powder particle size, it was also evaluated the influence of the pressing (40 to 300 MPa), the sintering additives (MgO, CaO and Y2O3), the middle of dispersion (water and alcohol), the powder calcination and the time (1 and 3h) and sintering temperature (1600 and 1650 ºC). The obtained ceramics were characterized according to the contraction, mass loss, porosity, densification and resistance to flexing. The microstructure was analyzed by light microscopy, scanning electron microscopy (SEM) besides X-ray diffraction. The obtained results show that mullite ceramic for commercial applications requiring mechanical resistance up to about approximately 207 MPa, it can be obtained using milled alumina powder and aerosil 380® with 1 % CaO, homogenized with alcohol, calcined in 600 ºC, pressed with 160 MPa (or more), pre-sintered to 1000 ºC for 1h and sintered to 1650 ºC for 1h. These ceramic also show, great potential to be used in burners for ovens and nozzles for thermal spallation. / Orientador: Elson de Campos / Coorientador: Demétrio Bastos Netto / Banca: Rogério Pinto Mota / Banca: Eduardo Bellini Ferreira / Banca: Francisco Cristovâo Lourenço de Melo / Banca: Gilmar Patrocínio Thim / Doutor

Orientador: Cesar Rogério Pucci / Co-orientador: Rodrigo Máximo de Araujo / Banca: Antonio Marcio Resende do Carmo / Banca: Maria Filomena Rocha Lima Huhtala / Resumo: O objetivo deste estudo foi avaliar o efeito de diferentes tratamentos de superfície na resistência de união entre a cerâmica de di-silicato de lítio IPS e.max Press (IvoclarVivadent, Liechtenstein) e o cimento resinoso Variolink II (Ivoclar Vivadent, Liechtenstein) quando submetidos a teste de tração. Para isso 330 bases tronco-cônicas de cerâmica de di-silicato de lítio foram aleatoriamente divididas em 11 grupos de acordo com o tratamento a ser realizado: C - grupo controle; J - Jateamento com óxido de alumínio (50 μm); JAr - Jateamento com óxido de alumínio (30 μm) e secagem do silano com ar quente; GEr - Revestimento da superfície com grafite e tratamento com laser Er:YAG(200 mJ de intensidade de energia e 10 Hz de frequência); GErAr - Revestimento da superfície com grafite, tratamento com laser Er:YAG (200 mJ de intensidade de energia e 10 Hz de frequência) e secagem do silano com ar quente; Er - Tratamento com laser Er:YAG (200 mJ de intensidade de energia e 10 Hz de freqüência); ErAr - Tratamento com laser Er:YAG (200 mJ de intensidade de energia e 10 Hz de frequência) e secagem do silano com ar quente; GNd - revestimento da superfície com grafite e tratamento com laser Nd:YAG (120 mJ de intensidade de energia e 15 Hz de frequência); GNdAr - Revestimento da superfície com grafite, tratamento com laser Nd:YAG (120 mJ de intensidade de energia e 15 Hz de frequência) e secagem do silano com ar quente; Nd - Tratamento com laser Nd:YAG (120 mJ de intensidade de energia e 15 Hz de frequência); NdAr - Tratamento com laser Nd:YAG (120 mJ de intensidade de energia e 15 Hz de frequência) e secagem do silano com ar quente. O cimento resinoso que uniu os espécimes foi fotoativado por 40 segundos utilizando o aparelho LED (Radii cal-SDI). Então, foi realizada a ciclagem termomecânica com carga de 60N, 1.000 ciclos termicos e 24000 mecânicos e o ensaio ... / Abstract: The aim of this study was to evaluate the bond strength afforded by different surface treatments on IPS e.max Press ceramic united to Variolink II (both Ivoclar-Vivadent, Liechtenstein), when subjected to tensile test. 330 ceramic bases were divided into 11 groups in accordance with the surface treatment performed: C - control group J - aluminum oxide sandblast, JAraluminum oxide sandblast and silane hot air dry, GEr - surface coating with graphite and treatment with Er: YAG laser (200 mJ of energy intensity and frequency 10 Hz), GErAr - surface coating with graphite, treatment with Er: YAG laser (200 mJ of energy intensity and 10 Hz frequency) and silane hot air dry; Er - treatment with Er: YAG laser (200 mJ of energy intensity and frequency 10 Hz) ErAr - treatment with Er: YAG laser (200 mJ intensity energy and 10 Hz frequency) and silane hot air dry; GNd - coating the surface with graphite and treatment with Nd: YAG laser (120 mJ of energy and intensity of frequency 15 Hz); GNdAr - coating the surface with graphite , treatment with Nd: YAG laser (120 mJ of energy intensity and 15 Hz frequency) and silane hot air dry; Nd - treatment with Nd: YAG laser (120 mJ of energy intensity and frequency 15 Hz); NdAr - treatment with Nd: YAG laser (120 mJ of energy and intensity of frequency 15 Hz) and silane hot air dry. The resin cement that unite the specimens was cured for 40 seconds using the LED cure equipment (Radii-cal SDI). Then they were termomechanical cycled (60N, 1,000 thermical cycles and 24000 mechanical) and were submitted to the tensile test in a universal testing machine EMIC-2000. Data were tested for Dunnet ( α = 5 % ) and 3 ANOVA Way . The Er group showed higher tensile strength greater than the control group and the other groups, while the NdG group presented results of bond strength lower than the control group and the other surface treatments. The other groups did... / Mestre

Orientador: Osmir Batista de Oliveira Junior / Banca: Paulo Francisco Cesar / Banca: Luis Geraldo Vaz / Resumo: O objetivo deste trabalho foi avaliar a resistência à flexão de cerâmicas de zircônia estabilizada por ítrio em função de marca comercial e espessura. A resistência à flexão (MPa) foi testada pelo método uniaxial de 3 pontos, conforme Norma ISO 6872/2005 em Máquina de Ensaios Universal EMIC DL 2000, usando célula de carga de 5kN, velocidade de 0,5 mm/min. e suporte com 20 mm de distância entre os apoios. Foram testados 2 sistemas cerâmicos de zircônia parcialmente estabilizada por ítrio (Y-TZP) ZirCAD© - Ivoclar Vivadente e LavaTM Framework - 3MESPE e 2 espessuras (norma ISO: 2,00 mm e uso clinico: 0,7 mm): ZC_2; ZC_0,7; LV_2 e LV_0,7. ANOVA one way e post Hoc de Bonferroni foram utilizados com significância para p<0,05. Não houve diferença estatisticamente significativa entre as médias de resistência a flexão entre ZC_2 (Média = 673,62 e dp = 129,95), ZC_0,7 (Média = 533,63 e dp = 129,84), LV_2 (Média = 593,56 e dp = 122,78) e LV_0,7 (Média = 673,02 e dp = 81,36). Conclusão: Os sistemas cerâmicos Y=TZP ZirCAD e Lava apresentam resistência a flexão (MPa) semelhantes independente da espessura. Espessuras de 0,7 mm podem ser utilizadas nos testes de resistência a flexão para melhor simular as situações de uso clinico dos sistemas cerâmicos Y-TZP / Abstract: The objective of this study was to evaluate the flexural strength of ceramics by Yttrium stabilized zirconia as a function of thickness and trademark. Flexural strength (MPa) was tested by the method of three uniaxial points, in accordance with ISO 6872/2005. The Universal Testing Machine EMIC DL 2000, using a 5 kN load cell, crosshead speed of 0.5 mm / min. and holder with 20 mm distance between supports was used. We tested 2 systems ceramic zirconia partially stabilized by yttrium (Y-TZP) ZirCAD © - Ivoclar Vivadente and LavaTM Framework - 3MESPE and 2 thicknesses (ISO: 2.00 mm and clinical use: 0.7 mm): ZC_2; ZC_0 7; LV_2 and LV_0, 7. One-way ANOVA and post hoc Bonferroni was used with significance for p <0.05. There was no statistically significant difference between the mean flexural strength between ZC_2 (Mean = 673.62 and SD = 129.95), ZC_0, 7 (mean = 533.63 and SD = 129.84), LV_2 (Average = 593 , 56 and SD = 122.78) and LV_0, 7 (mean = 673.02 and SD = 81.36). Conclusion: Y-TZP ceramic systems ZirCAD and Lava have flexural strength (MPa) similar independent of the thickness. Thickness of 0.7 mm can be used in tests of flexural strength for better simulate the clinical conditions of use of Y-TZP ceramic systems / Mestre