Submitted by Daniella Sodre (daniella.sodre@ufpe.br) on 2015-03-04T16:32:32Z No. of bitstreams: 2 dissertacao marcio.pdf: 1723641 bytes, checksum: 60ffd3141bc44ba48bdc4ac5eb11188a (MD5) license_rdf: 1232 bytes, checksum: 66e71c371cc565284e70f40736c94386 (MD5) / Made available in DSpace on 2015-03-04T16:32:32Z (GMT). No. of bitstreams: 2 dissertacao marcio.pdf: 1723641 bytes, checksum: 60ffd3141bc44ba48bdc4ac5eb11188a (MD5) license_rdf: 1232 bytes, checksum: 66e71c371cc565284e70f40736c94386 (MD5) Previous issue date: 2012-02-24 / FACEPE / Esse trabalho avaliou a incorporação em argamassas de revestimento de cinzas de topo e cinzas de base, provenientes da queima de lenha de Algaroba nas lavanderias do arranjo produtivo local (APL) de confecções da região agreste pernambucano-Brasil. As cinzas foram coletadas em uma lavanderia de médio porte representativa da região, peneiradas em malha 200, avaliadas quanto as suas características físico-químicas e adicionadas em argamassa do tipo emboço, com traço 1:2:9 (cimento, cal, areia), comum nas construções da região de Caruaru-Pernambuco-Brasil. Na produção das formulações, para cada uma das cinzas, foi mantida a mesma relação água/cimento e mesma faixa de consistência para todas as argamassas, gerando formulações com adição de 10, 20, 30 e 40% em relação à massa de cimento. As formulações com adição foram comparadas com uma argamassa padrão (sem adição), utilizando a metodologia para caracterização de argamassas descrita pela ABNT. Os resultados indicaram que argamassas com adição de cinzas, quando comparadas com a argamassa padrão, apresentaram, no estado fresco, capacidade de retenção de água e densidade semelhantes, e no estado endurecido, índice de vazios, resistência mecânica, absorção de água e resistência potencial de aderência à tração sem alterações significativas. A manutenção das características das argamassas com a adição é atribuída à ação do efeito filler, que contribuiu para uma maior compacidade do sistema compensando os efeitos negativos da adição. Foi verificado, ainda, que argamassas com adição de cinzas de topo e cinzas de base apresentaram resultados equivalentes. O sucesso dos resultados gera a possibilidade de estudos futuros envolvendo a substituição parcial do cimento por cinzas de algaroba, o que significa redução de custos para a obtenção de argamassas com resistências mecânicas semelhantes à argamassa padrão, além de contribuir para a sustentabilidade ambiental minimizando o descarte aleatório desses resíduos.

Os experimentos de adsorção descontínuos foram realizados para remover azul de metileno de solução aquosa usando zeólitas sintetizadas a partir de cinza leve de carvão como adsorvente. Os estudos foram conduzidos para avaliar os efeitos do tempo de contato, concentração inicial do corante, parâmetros de ativação hidrotérmica, composição da cinza leve, quantidade do adsorvente, pH e temperatura sobre a adsorção. Um tempo de contato de aproximadamente 10 minutos foi suficiente para a adsorção do corante alcançar o equilíbrio. Os dados de equilíbrio foram analisados usando as isotermas de Langmuir e Freundlich e os resultados se ajustaram melhor à equação da isoterma de Freundlich. A eficiência de adsorção estava entre 72 a 98% sob as condições estudadas. O valor da constante de Freundlich para a capacidade de adsorção (KF) do azul de metileno no adsorvente foi 0,738 (mg/g) (L/mg)1/n. Os dados de adsorção foram ajustados aos modelos cinéticos de pseudoprimeira- ordem de Lagergren e pseudo-segunda-ordem e seguiram as cinéticas de pseudosegunda- ordem. As constantes de velocidade foram estimadas em diferentes concentrações iniciais. O mecanismo do processo de adsorção encontrado mostrou-se complexo, consistindo de adsorção superficial e difusão intrapartícula. Os parâmetros termodinâmicos foram avaliados indicando que o processo de adsorção do azul de metileno sobre a zeólita é espontâneo e exotérmico. / Batch sorption experiments were carried out to remove methylene blue from its aqueous solutions using zeolites synthesized from coal fly ash as an adsorbent. The studies were conducted to evaluate the effects of contact time, initial dye concentration, hydrothermal activation parameters, composition of fly ash, quantity of adsorbent, pH and temperature on adsorption. Nearly 10 min of contact time are found to be sufficient for the adsorption of dye to reach equilibrium. Equilibrium data have been analyzed using Langmuir and Freundlich isotherms and the results were found to be well represented by the Freundlich isotherm equation. The adsorption efficiency was between 72 and 98% under the conditions studied. The value of the Freundlich constant for adsorption capacity (KF) of methylene blue on the adsorbent was 0.738 (mg/g) (L/mg)1/n. Adsorption data were fitted to both Lagergren first-order and pseudo-secondorder kinetic models and the data were found to follow pseudo-second-order kinetics. Rate constants at different initial concentrations were estimated. The adsorption process mechanism was found to be complex, consisting of both surface adsorption and intraparticle diffusion. Thermodynamic parameters were evaluated indicating that adsorption process for methylene blue onto zeolite is spontaneous and exothermic.

Os experimentos de adsorção descontínuos foram realizados para remover azul de metileno de solução aquosa usando zeólitas sintetizadas a partir de cinza leve de carvão como adsorvente. Os estudos foram conduzidos para avaliar os efeitos do tempo de contato, concentração inicial do corante, parâmetros de ativação hidrotérmica, composição da cinza leve, quantidade do adsorvente, pH e temperatura sobre a adsorção. Um tempo de contato de aproximadamente 10 minutos foi suficiente para a adsorção do corante alcançar o equilíbrio. Os dados de equilíbrio foram analisados usando as isotermas de Langmuir e Freundlich e os resultados se ajustaram melhor à equação da isoterma de Freundlich. A eficiência de adsorção estava entre 72 a 98% sob as condições estudadas. O valor da constante de Freundlich para a capacidade de adsorção (KF) do azul de metileno no adsorvente foi 0,738 (mg/g) (L/mg)1/n. Os dados de adsorção foram ajustados aos modelos cinéticos de pseudoprimeira- ordem de Lagergren e pseudo-segunda-ordem e seguiram as cinéticas de pseudosegunda- ordem. As constantes de velocidade foram estimadas em diferentes concentrações iniciais. O mecanismo do processo de adsorção encontrado mostrou-se complexo, consistindo de adsorção superficial e difusão intrapartícula. Os parâmetros termodinâmicos foram avaliados indicando que o processo de adsorção do azul de metileno sobre a zeólita é espontâneo e exotérmico. / Batch sorption experiments were carried out to remove methylene blue from its aqueous solutions using zeolites synthesized from coal fly ash as an adsorbent. The studies were conducted to evaluate the effects of contact time, initial dye concentration, hydrothermal activation parameters, composition of fly ash, quantity of adsorbent, pH and temperature on adsorption. Nearly 10 min of contact time are found to be sufficient for the adsorption of dye to reach equilibrium. Equilibrium data have been analyzed using Langmuir and Freundlich isotherms and the results were found to be well represented by the Freundlich isotherm equation. The adsorption efficiency was between 72 and 98% under the conditions studied. The value of the Freundlich constant for adsorption capacity (KF) of methylene blue on the adsorbent was 0.738 (mg/g) (L/mg)1/n. Adsorption data were fitted to both Lagergren first-order and pseudo-secondorder kinetic models and the data were found to follow pseudo-second-order kinetics. Rate constants at different initial concentrations were estimated. The adsorption process mechanism was found to be complex, consisting of both surface adsorption and intraparticle diffusion. Thermodynamic parameters were evaluated indicating that adsorption process for methylene blue onto zeolite is spontaneous and exothermic.

As indústrias de papel e celulose geram enormes quantidades de cinzas de caldeira todos os anos. A disposição final dessas cinzas em aterros costumava ser prática comum, porém a sua utilização em solos florestais e agrícolas merece consideração devido ao seu potencial de corrigir a acidez e de fertilizar os solos, minimizando assim a pressão sobre sua forma de descarte no ambiente. No entanto, o uso desse resíduo pode afetar diretamente a dinâmica de pesticidas no solo, além de adicionar metais pesados. Desta forma, o presente trabalho avaliou o efeito de três cinzas de biomassa florestal (C-1, C-11 e C-27) na fertilidade e na sorção do herbicida imazetapir em três solos com atributos físico-químicos distintos (RQd, LVd e LVAd). Além das três cinzas, calcário e o controle compuseram os tratamentos, os quais foram incubados por três meses. Posteriormente, estudos de sorção do herbicida imazetapir foram realizados nos diferentes tratamentos. As cinzas C-11 e C-27 aumentarem o valor do pH dos solos e os teores de macroelementos, mas reduziram os teores de microelementos catiônicos. A C-1 mostrou ser boa fonte de K para os solos. Nenhuma cinza mostrou-se limitante quanto ao teor de metais pesados. De forma geral, o imazetapir apresentou baixo potencial de sorção nos solos e seus respectivos tratamentos (Kd < 1,8 L kg-1). A C-11 e a C-27 reduziram enquanto que a C-1 aumentou o potencial de sorção do imazetapir nos solos, o que foi devido às alterações nos valores de pH do solo. A sorção foi ligeiramente maior no solo com maiores teores de argila e carbono orgânico (LVd), enquanto a dessorção foi maior no solo de teores intermediários (LVAd). Houve histerese em todos os solos, sugerindo irreversibilidade de parte do herbicida sorvido. / The pulp and paper industries generate huge amounts of wood ash every year. The ashes disposals in landfills used to be a common practice, but their use in agricultural and forest soils deserves special attention due to their potential to neutralize acidity and to fertilize soils, thus decreasing pressure about their environmental disposal. However, the use of this residue may directly impact the dynamic of pesticides as well as add heavy metals to the soils. Therefore, this study evaluated the effects of three wood ashes (C-1 , C-11, and C-27 ) in the fertility and sorption of imazethapyr in three soils (RQd, LVd, LVAd), with contrasting physical-chemical attributes. Besides the ashes, lime and control treatments were added, all of them incubated for three months. Afterwards, batch sorption isotherms for imazethapyr were performed for all treatments. The C-11 and C-27 enhanced soil-pH and macroelement contents, but decreased cationic microelement contents. The C-1 was a good source of K to the soils. There is little risk of contamination by heavy metals. Overall, imazethapyr sorption was low in all soils and their respective treatments (Kd < 1,8 L kg-1). The C-11 and the C-27 decreased whereas C-1 enhanced sorption of imazethapyr to the soils, most likely due to changes in soil-pH. Sorption was slightly higher in the soil with higher clay and organic carbon contents (LVd) whereas desorption was higher in the soil with intermediate values (LVAd). There was hysteresis, suggesting irreversibility during sorption/desorption processes.

As indústrias de papel e celulose geram enormes quantidades de cinzas de caldeira todos os anos. A disposição final dessas cinzas em aterros costumava ser prática comum, porém a sua utilização em solos florestais e agrícolas merece consideração devido ao seu potencial de corrigir a acidez e de fertilizar os solos, minimizando assim a pressão sobre sua forma de descarte no ambiente. No entanto, o uso desse resíduo pode afetar diretamente a dinâmica de pesticidas no solo, além de adicionar metais pesados. Desta forma, o presente trabalho avaliou o efeito de três cinzas de biomassa florestal (C-1, C-11 e C-27) na fertilidade e na sorção do herbicida imazetapir em três solos com atributos físico-químicos distintos (RQd, LVd e LVAd). Além das três cinzas, calcário e o controle compuseram os tratamentos, os quais foram incubados por três meses. Posteriormente, estudos de sorção do herbicida imazetapir foram realizados nos diferentes tratamentos. As cinzas C-11 e C-27 aumentarem o valor do pH dos solos e os teores de macroelementos, mas reduziram os teores de microelementos catiônicos. A C-1 mostrou ser boa fonte de K para os solos. Nenhuma cinza mostrou-se limitante quanto ao teor de metais pesados. De forma geral, o imazetapir apresentou baixo potencial de sorção nos solos e seus respectivos tratamentos (Kd < 1,8 L kg-1). A C-11 e a C-27 reduziram enquanto que a C-1 aumentou o potencial de sorção do imazetapir nos solos, o que foi devido às alterações nos valores de pH do solo. A sorção foi ligeiramente maior no solo com maiores teores de argila e carbono orgânico (LVd), enquanto a dessorção foi maior no solo de teores intermediários (LVAd). Houve histerese em todos os solos, sugerindo irreversibilidade de parte do herbicida sorvido. / The pulp and paper industries generate huge amounts of wood ash every year. The ashes disposals in landfills used to be a common practice, but their use in agricultural and forest soils deserves special attention due to their potential to neutralize acidity and to fertilize soils, thus decreasing pressure about their environmental disposal. However, the use of this residue may directly impact the dynamic of pesticides as well as add heavy metals to the soils. Therefore, this study evaluated the effects of three wood ashes (C-1 , C-11, and C-27 ) in the fertility and sorption of imazethapyr in three soils (RQd, LVd, LVAd), with contrasting physical-chemical attributes. Besides the ashes, lime and control treatments were added, all of them incubated for three months. Afterwards, batch sorption isotherms for imazethapyr were performed for all treatments. The C-11 and C-27 enhanced soil-pH and macroelement contents, but decreased cationic microelement contents. The C-1 was a good source of K to the soils. There is little risk of contamination by heavy metals. Overall, imazethapyr sorption was low in all soils and their respective treatments (Kd < 1,8 L kg-1). The C-11 and the C-27 decreased whereas C-1 enhanced sorption of imazethapyr to the soils, most likely due to changes in soil-pH. Sorption was slightly higher in the soil with higher clay and organic carbon contents (LVd) whereas desorption was higher in the soil with intermediate values (LVAd). There was hysteresis, suggesting irreversibility during sorption/desorption processes.

Submitted by Setor de Tratamento da Informa??o - BC/PUCRS (tede2@pucrs.br) on 2016-11-17T16:56:45Z No. of bitstreams: 1 DIS_BARBARA_MEIER_DA_COSTA_COMPLETO.pdf: 2683221 bytes, checksum: 7df1d25c854004887ae73f23ab2e40ca (MD5) / Made available in DSpace on 2016-11-17T16:56:45Z (GMT). No. of bitstreams: 1 DIS_BARBARA_MEIER_DA_COSTA_COMPLETO.pdf: 2683221 bytes, checksum: 7df1d25c854004887ae73f23ab2e40ca (MD5) Previous issue date: 2016-08-30 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior - CAPES / The coal fly ash (CFA) is one of the main waste generated during the burning of fossil fuel. The annual global production of CFA is about 800 million tons and is increasing more and more. While a portion is recycled and reused in the construction area, much is still destined to landfills. This study aims to synthesize zeolites in two different scales employing for both CFA arising Thermoelectric Complex Jorge Lacerda, SC, in order to use them in carbon dioxide adsorption (CO2). For synthesis of zeolite was used hydrothermal process in two steps. The first step consisted mainly in the extraction of Si and Al contained in the CFA. The second step was to add an external source of Al in alkaline solution to hit the molar ratio and formation of zeolite of interest. The parameters time, temperature, Si/Al ratio and the reaction medium bench scale has been optimized for the scaling (5 times) was performed. The zeolitic material obtained was characterized using SEM-FEG, XRD, BET and NMR indicates the presence of zeolites X (major phase) and A. Under the conditions used was obtained on a smaller scale a mass of 5.5 g of zeolites of interest while with large scale it was possible to obtain a value of 7 times greater. Tests for adsorption/desorption of CO2 in the zeolitic material was pelleted using bentonite and PVA. The material was efficient in capture and CO2 adsorption selectivity both with He mixture (inert gas), as in admixture with other gases (CH4 and CO). Obtained CO2 adsorption capacities of 0.47 and 0.92 mmol.g-1 with the individual standard in a mixture of He, and with synthetic standard (CO, CH4 and CO2, balance in N2 ), respectively. The adsorbent material produced showed good regeneration, and easily to desorb the adsorbed CO2 both with and without heating, for three cycles of adsorption/desorption tested. The results of this study indicated that the synthesized zeolitic product (X and A) from CFA, has potential use for the adsorption of CO2 at different conditions. / As cinzas leves de carv?o (CLC) s?o um dos principais res?duos gerados durante a queima desse combust?vel f?ssil. A gera??o global anual de CLC ? de cerca de 800 milh?es de toneladas e vem aumentando cada vez mais. Apesar de uma parte ser reciclada e reutilizada na ?rea de constru??o civil, boa parte ainda ? destinada a aterros sanit?rios. O presente trabalho visa sintetizar ze?litas em duas diferentes escalas empregando-se para tanto CLC oriundas do Complexo Termoel?trico Jorge Lacerda, SC, com o intuito de utiliz?-las na adsor??o de di?xido de carbono (CO2). Para s?ntese da ze?lita foi utilizado o processo hidrot?rmico em duas etapas. A primeira etapa consistiu basicamente na extra??o de Si e Al contidos na CLC. A segunda consistiu em adicionar uma fonte externa de Al em solu??o alcalina para acerto da raz?o molar e forma??o da ze?lita de interesse. Os par?metros tempo, temperatura, raz?o Si/Al e meio reacional da escala de bancada foram otimizados para que o aumento de escala (5 vezes) fosse realizado. O material zeol?tico obtido foi caracterizado com o uso de MEV-FEG, DRX, RMN e BET indicando a presen?a de zeolitas X (fase majorit?ria) e A. Sob as condi??es utilizadas obteve-se em escala menor uma massa de 5,5 g da ze?lita de interesse, enquanto com escala maior foi poss?vel obter um valor 7 vezes maior. Para os testes de adsor??o/dessor??o de CO2 nos materiais zeol?ticos, estas foram transformadas em pelotas utilizando bentonita e ?lcool polivin?lico (PVA). O material se mostrou eficiente na captura e seletividade de adsor??o de CO2 tanto em mistura com He (g?s inerte), quanto em mistura com outros gases (CH4 e CO;) a temperatura de 30oC e press?o total de 1 atm. Obteve-se capacidades de adsor??o de CO2 de 0,47 mmol.g-1 e 0,92 mmol.g-1 com o padr?o individual em mistura de He e com padr?o sint?tico (CO, CH4 e CO2, balan?o em N2), respectivamente. O material adsorvente produzido demonstrou boa regenera??o, tendo facilidade para dessorver o CO2 adsorvido tanto com e sem calor, para os tr?s ciclos de adsor??o/dessor??o testados. Os resultados deste estudo indicaram que o produto ze?litico sintetizado (X e A) a partir de CLC, tem potencialidade de uso para a adsor??o de CO2 em diferentes condi??es.

A baixa disponibilidade do ácido fítico para os animais não ruminantes tem incrementado as pesquisas quanto ao uso da enzima fitase. Pesquisas têm sido realizadas com a adição de fitase em rações para frangos de corte e têm demonstrado resultados favoráveis sobre o aproveitamento do fósforo e a digestibilidade de nutrientes como aminoácidos e proteína. Para se avaliar os efeitos do fornecimento de rações contendo níveis reduzidos de proteína bruta e fósforo disponível com adição da enzima fitase sobre o desempenho, excretas e parâmetros ósseos em frangos de corte no período de 1 a 21 dias de idade foram utilizados 504 pintos de corte, machos, de linhagem comercial de frangos de corte, de 1 dia de idade, distribuídos em 12 tratamentos com seis repetições cada. O delineamento foi em blocos casualizados e os tratamentos foram organizados de acordo com um esquema fatorial 2x2x3: dois níveis de fósforo disponível, dois níveis de fitase e três níveis de proteína bruta. Houve um aumento do peso das aves que receberam dietas contendo a enzima fitase embora não tenha afetado a conversão alimentar. O consumo não foi afetado pelos níveis de proteína bruta quando ocorreu a suplementação com fitase. A porcentagem de fósforo nas excretas diminuiu com o nível intermediário de proteína bruta (20,5%) com a adição de fitase (1,15 vs. 1,03%). A proteína bruta excretada foi reduzida com a suplementação de fitase (33,36 vs. 31,83%). A enzima fitase atua de forma significativa na dieta à base de milho e farelo de soja com baixos níveis de proteína bruta e fósforo disponível para frangos de corte. / The low phytic acid availability to nonruminant animals has increased the researches about the phytase enzyme use. Researches have been realized with phytase addition in broiler diets and they demonstrated favorable results on phosphorus utilization and nutrients digestibility as amino acids and protein. To evaluate the effects of feeding low levels of crude protein and available phosphorus diets supplemented with phytase on performance, feces and bone parameters on broiler chickens over a 21 days period, it was used 504 (five hundred four) 1 day old male chicks, of a commercial broiler line, distributed in 12 treatments, with 6 replicates per treatment. The experimental design was casually blocked and treatments were organized in a 2x2x3 factorial arrangement: two phosphorus levels, two phytase inclusion levels and three protein levels. Body weight gain (BWG) was observed in birds fed diets with phytase supplementation although it hasn\'t affected the feed conversion ratio (FCR). Feed intake (FI) wasn\'t affected by the low protein levels with added phytase. Phosphorus percentage in excretion decreased with the intermediary protein level (20.5%) when phytase was added (1.15 vs 1.03%). Crude protein excreted was lower with phytase supplementation (33.36 vs 31.83%). Phytase enzyme acts in a significant way on broilers fed a corn-soybean diet with low levels of crude protein and available phosphorus.

Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Química / Made available in DSpace on 2013-03-04T19:06:43Z (GMT). No. of bitstreams: 1 305251.pdf: 2194737 bytes, checksum: 86889321953a12f8401a6c0eda9604a3 (MD5) / A presente pesquisa concentrou-se no estudo e desenvolvimento de um material com propriedades cimentícias. Trata-se de um polímero inorgânico, formado pela ativação de aluminossilicatos (Al2O3.SiO2) amorfos, que reagem em um meio fortemente alcalino, chamado geopolímero. Como matéria-prima foram utilizadas cinzas pesadas, resíduo da queima de carvão mineral (Termoelétrica do Sul do Brasil), como fonte de aluminossilicatos; e o meio alcalino foi hidróxido de sódio (NaOH) e silicato de sódio (Na2SiO3), utilizados como ativadores. As cinzas pesadas cristalizam-se parcialmente durante a queima e perdem parte de seu estado amorfo, devido a isso suas propriedades reativas para combinar quimicamente durante a polimerização são reduzidas. Para aumentar as propriedades reativas da cinza pesada foi adicionado metacaulim, processado a partir de resíduos da indústria de papel. Os resíduos sólidos e as amostras geopoliméricas passaram por caracterização e, as principais análises envolvidas no processo, foram: fluorescência de raios X (FRX), difração de raios X (DRX), microscopia eletrônica de varredura (MEV), espectrometria no infravermelho com transformada de Fourier (FTIR), análise termogravimétrica (TGA) e a análise térmica diferencial (DTA). Também foram realizados ensaios de resistência à compressão nas amostras geopoliméricas para avaliar o grau de polimerização, uma vez que, quanto mais polimerizada estiver a estrutura, maior será a resistência. Com 24 horas de cura as pastas geopoliméricas atingiram resistências à compressão de até 10 megapascais (MPa) e, com 90 dias de cura, aproximadamente, 25 MPa. Os melhores resultados foram obtidos com amostras ativadas com 15 mols/l de NaOH na mistura com silicato de sódio e nas proporções de 2:1 entre a cinza pesada e o metacaulim. Os resultados obtidos através das análises de caracterização das amostras foram satisfatórios e demonstraram que os resíduos de cinza pesada e metacaulim, quando ativados com hidróxido de sódio e silicato de sódio, são uma alternativa viável para a produção de materiais geopoliméricos. / This research concentrated on the study and development a material with cementitious properties. It is an inorganic polymer formed by the activation of aluminosilicates (Al2O3.SiO2) amorphous, which reacts in a strongly alkaline medium, called geopolymer. As raw material were used bottom ash residue from burning mineral coal (Thermoelectric South of Brazil) the alkaline medium were sodium hydroxide (NaOH) and sodium silicate (Na2SiO3), used as activators. Because the bottom ash partially crystallizes during burning and loses its amorphous state, its reactive properties to combine chemically during polymerization are reduced. For o increase the bottom ash reactive properties, metakaolin synthesized from paper industry waste was added. The solid waste and the geopolymeric samples passed for characterization and main analysis involved in the process, were: X-ray fluorescence (XRF), X-ray Diffraction (XRD), scanning electron microscope (SEM), Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), differential thermal analysis (DTA). Were also conducted of compressive strength tests geopolymer sample, to measure the degree of polymerization, since the more polymerized structure, the more will resistance. With 24 hours of curing folders geopoliméricas reached compressive strengths of up to 10 megapascals (MPa) and with 90 days of curing approximately, 25 MPa. The best results were obtained in samples activated with 15 mol / l NaOH in a mixture with sodium silicate and the proportion of 2:1 between the ash and metakaolin. The results obtained of analysis characterization were satisfactory, demonstrating that waste bottom ash and metakaolin activated with sodium hydroxide and sodium silicate are viable alternative to production of geopolymer materials.

Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico. Programa de Pós-graduação em Ciência e Engenharia de Materiais / Made available in DSpace on 2013-07-16T00:37:59Z (GMT). No. of bitstreams: 1 222080.pdf: 13292877 bytes, checksum: d5a534f49f03e538736333a1b7ef898f (MD5) / As cinzas pesadas de carvão mineral são subprodutos originados da combustão do carvão mineral em usinas termelétricas. As características físicas, químicas e mineralógicas das cinzas pesadas são compatíveis com várias matérias-primas utilizadas nas indústrias cerâmicas de revestimento, o que indica uma possibilidade de substituição parcial ou integral destas matérias-primas por este subproduto. A metodologia de superfícies de resposta aplicada à técnica de planejamento de experimentos tem sido muito utilizada em várias áreas da ciência e tecnologia. A consideração importante é que uma determinada propriedade depende das proporções dos componentes que constituem um material. Os materiais cerâmicos têm suas propriedades definidas pela composição química e microestrutura que apresentam. A quantificação das fases amorfas e cristalinas é uma etapa fundamental na determinação da estrutura, propriedades e aplicações de um material cerâmico. Dentro deste contexto, este trabalho tem como objetivo o desenvolvimento de materiais cerâmicos com adição de cinzas pesadas de carvão mineral, visando à utilização industrial deste subproduto como matéria-prima de baixo custo e alto valor agregado, adaptável aos processos de fabricação de revestimentos cerâmicos. Busca-se a aplicação da metodologia de delineamento de misturas para a formulação das massas cerâmicas; e a determinação quantitativa das fases amorfas e cristalinas dos materais desenvolvidos utilizando a técnica de difração de raios X, através dos métodos propostos por Rietveld (1969) e Ruland (1961). Para a formulação das massas cerâmicas utilizou-se o planejamento experimental {3,3}, originando dez formulações dos três componentes (dois diferentes tipos de argilas e cinza pesada de carvão mineral). Foram realizados ensaios tecnológicos nos corpos-de-prova a seco e após a sinterização. A análise estatística mostrou que todos os modelos de regressão obtidos relativos às propriedades físicas dos materiais cerâmicos são significantes, não apresentam falta de ajuste e que os erros são aleatórios, com média tendendo a zero e variância praticamente constante. A metodologia proposta de utilização do método de Rietveld para a quantificação relativa das fases cristalinas em conjunto com o método de Ruland utilizado para determinação da cristalinidade dos materiais, mostrou-se bastante adequada e eficiente. Os materiais cerâmicos sinterizados, desenvolvidos com adição de cinzas pesadas de carvão mineral, apresentaram valores mais adequados de retração linear, densidade aparente, absorção de água e módulo de resistência à flexão, comparados com um material cerâmico industrial padrão desenvolvido com a utilização de matérias-primas convencionais.

Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico. Programa de Pós-Graduação em Engenharia Civil. / Made available in DSpace on 2012-10-21T01:02:55Z (GMT). No. of bitstreams: 1 196522.pdf: 1667187 bytes, checksum: 08850f6836f7d7fc66fa6efe7b7b375e (MD5) / O aproveitamento de resíduos sólidos industriais representa uma alternativa benéfica tanto para as indústrias geradoras quanto para a construção civil. A cinza pesada do carvão mineral, resultante dos processos de queima deste produto nas usinas termelétricas, é um subproduto conhecido e abundante, porém pouco explorado. Desta