Made available in DSpace on 2014-12-17T14:58:07Z (GMT). No. of bitstreams: 1 SistanleyJLB_DISSERT.pdf: 3362424 bytes, checksum: 30d67bc0b13dba47c7002133ab1bb63d (MD5) Previous issue date: 2011-06-20 / This research presents an approach to the addition of curau? fibers and licuri fibers in a polypropylene resin matrix, such as an alternative proposal to reinforce the polymeric composites. Fiber content of 0 %, 5 %, 10 %, and 20% were analyzed for verification of their mechanical properties comparing them, inclusive with the properties of polypropylene. The grainulated biocomposites had been prepared in an extrusora. The test bodies had been molded by injection and submitted to the mechanical essays uniaxial traction, flexion on three points, impact, in addition to thermal tests (HDT). These biocomposites had been also subjected the essay physicist-chemistry index of fluidity (IF). It was observed that the biocomposites of PP with 20% curau?, obtained bigger increase in the modulus of elasticity and a bigger reduction in the resistance to the impact. In the mechanical behavior, for all the biocomposites, these were increases in values of the limit of drainage and tension of rupture, when tested by uniaxial traction, as they added the fibers. Another important point was the increase of the resistance the flexion. It was also noted that the addition of fibers reduced the thermal degradation of the mixture natural fibers / polypropylene. / Esta pesquisa apresenta uma abordagem da adi??o de fibras de licuri e curau? em uma matriz de resina de polipropileno, essa como uma proposta alternativa de refor?o aos comp?sitos polim?ricos. Teores de fibras de 0 %, 5 %, 10 %, e 20 % foram analisados para verifica??o de suas propriedades mec?nicas comparando-as, inclusive com as propriedades do polipropileno. Os biocomp?sitos granulados foram preparados em uma extrusora. Os corpos de prova foram moldados por inje??o e submetidos aos ensaios mec?nicos de tra??o uniaxial, flex?o em tr?s pontos, impacto, al?m de ensaios t?rmicos (HDT). Estes biocomp?sitos tamb?m foram submetidos a ensaio f?sico-qu?mico de ?ndice de fluidez (IF). Observou-se que os biocomp?sitos de PP com 20% curau? obteve maior aumento no m?dulo de elasticidade, e uma maior diminui??o na resist?ncia ao impacto. No comportamento mec?nico, para todos os biocomp?sitos, houve acr?scimos nos valores do limite de escoamento e tens?o de ruptura quando ensaiados por tra??o uniaxial, ? medida que se adicionavam as fibras. Outro ponto importante foi o aumento da resist?ncia ? flex?o. Verificou-se tamb?m que a adi??o de fibras reduziu a degrada??o t?rmica da mistura fibras naturais / polipropileno.

Made available in DSpace on 2014-12-17T14:58:09Z (GMT). No. of bitstreams: 1 HallyjusADB_DISSERT.pdf: 2542860 bytes, checksum: a76cbfa6200b38f0f8ff5811d0315d59 (MD5) Previous issue date: 2011-02-18 / Composite materials have a wide application in various sectors, such as the medical field in the manufacture of prostheses, in automotive and aerospace. Thus it is essential to the development of new composite and a better understanding in the face of various loading conditions and service. Several structural elements are manufactured in the presence of geometric discontinuity (notch, hole, etc ) in their longitudinal sections and/or cross-cutting, and these affect the mechanical response of these elements. The objective is to study the mechanical response of laminated polymer matrix hybrid composites reinforced with glass fiber/jute in a uniaxial tensile test. The mechanical response takes in account both the influence of the presence of a geometric discontinuity (semicircular notches) and the orientation of fibers in the layers (anisotropy). The semicircular notches are located in longitudinal section (with a reduction in cross section) of the same. In this analysis, the anisotropy is characterized by types of configurations (with different orientations of fibers in the outer layers). A comparative study of mechanical properties with and without the presence of notches is developed. Both configurations consist of four layers of woven jute fiber bidirectional and a central layer of bidirectional woven glass fibers. In addition to the mechanical properties was also studied the characteristics of the fracture developed in each composite laminate. The results showed that in the comparative study, the anisotropy and the presence of semicircular notches directly influences the mechanical behavior of laminates composites, mainly in reducing the tensile strength, and well as the final characteristics of the fracture / Os materiais comp?sitos t?m uma ampla aplica??o nos mais variados setores, como por exemplo, na ?rea m?dica na confec??o de pr?teses, na ind?stria automotiva e no setor aeroespacial. Assim ? essencial o desenvolvimento de novos comp?sitos e uma melhor compreens?o frente ?s mais diversas condi??es de carga e servi?o. V?rios elementos estruturais s?o fabricados na presen?a de descontinuidade geom?trica (entalhe, furo etc.) em suas se??es longitudinais e/ou transversais, e essas prejudicam a resposta mec?nica desses elementos. O objetivo do trabalho ? estudar a resposta mec?nica de laminados comp?sitos h?bridos de matriz polim?rica refor?ado com fibras de vidro/juta em um ensaio de tra??o uniaxial. A resposta mec?nica leva em conta tanto a influ?ncia da presen?a de uma descontinuidade geom?trica (entalhes semicirculares) quanto da orienta??o das fibras nas camadas (anisotropia). Os entalhes semicirculares est?o localizados na se??o longitudinal (com redu??o da se??o transversal) dos mesmos. Nessa an?lise, a anisotropia ? caracterizada por dois tipos de configura??es (com diferentes orienta??es das fibras nas camadas externas). Um estudo comparativo das propriedades mec?nicas com e sem a presen?a dos entalhes ? desenvolvido. As duas configura??es consistem de quatro camadas de tecidos bidirecionais de fibras de juta e uma camada central de tecido bidirecional de fibras de vidro. Al?m das propriedades mec?nicas, tamb?m foi estudada as caracter?sticas da fratura desenvolvidas em cada laminado comp?sito. Os resultados mostraram que, no estudo comparativo, a anisotropia e a presen?a dos entalhes semicirculares influi diretamente no comportamento mec?nico dos laminados comp?sitos, principalmente na redu??o da resist?ncia ? tra??o, e bem como na caracter?stica final da fratura

Made available in DSpace on 2014-12-17T14:58:13Z (GMT). No. of bitstreams: 1 AlcioneOG_DISSERT.pdf: 4986234 bytes, checksum: d81c2eeeb91a55690b1f5b9671a9a5e3 (MD5) Previous issue date: 2011-08-26 / Use of natural fibres as a reinforcement material in the manufacture of composites show a series of advantages: availability, biodegradability, low weight and regeneration in relation to synthetic fibres, thus justifying its utilization. In the present research work, composites were developed with chicken feathers (KF), using unsaturated polyester resin as matrix, for diversified applications, mainly in the furniture/timber industry.At present, in Brazil the chicken feathers are used as part of the animal feed, even though this material possesses low aggregated value. The chicken feathers are hollow, light and resistant. After washing with water at room temperature, a part of the chicken feathers were treated with 2% NaOH. Composites were manufactured using treated and untreated chicken feathers with unsaturated orthothalic polyester resin and 1% peroxide as catalyser, obtained in the commerce. Samples with size 150x25x3 mm for mechanical tests were cut by laser in the composite plate. Mechanical analyses were carried out in the Laborat?rio de Metais e Ensaios Mec?nicos UFRN. All the analyses were in accordance with ASTM standards. SEM analyses were also carried out on the samples.In the analyses of the results obtained, it was observed that the composites made with untreated chicken feathers showed better results (Traction 11.406 MPa and 9.107 MPa Bending 34.947 and 20.918 MPa for samples with and without treatment respectively) compared to the composite with treated feathers. Very low values of the water absorption results, evidenced the impermeability characteristic of the feathers. From the SEM images, the structure, fracture and the fibre/matrix adsorption can be evidenced. In the flammability test, it was observed that despite the feathers having sulfur as a constituent, natural inhibitor of flame, no burning support of the composites, because the manufacturing process of the composite / O uso de fibras naturais como refor?o em comp?sitos apresenta uma s?rie de vantagens: abund?ncia, biodegradabilidade, baixo peso e regenerabilidade em rela??o ?s fibras sint?ticas, justificando sua utiliza??o. Na presente pesquisa foram desenvolvidos comp?sitos com penas de frango (KF), utilizando resina de poli?ster n?o-saturado como matriz. Atualmente, no Brasil, as penas de frango s?o utilizadas como parte de ra??o animal, por?m este produto possui um baixo valor agregado. As penas s?o um material oco, leve e resistente. Ap?s a lavagem com ?gua em temperatura ambiente uma parte das penas foi tratada com 2% de NaOH. Foram fabricados dois comp?sitos, um com as penas tratadas e outro sem tratamento, usando o processo de molde fechado por compress?o, utilizando a resina de poli?ster ortoft?lica e 1% de per?xido MEK (per?xido de metil etil cetona) como iniciador, adquiridos no com?rcio local. As amostras com 150x25x3 mm de tamanho para os ensaios mec?nicos foram cortadas a laser na placa do comp?sito. Os ensaios de tra??o e flex?o em tr?s pontos foram realizados no Laborat?rio de Metais e Ensaios Mec?nicos - UFRN. Todas as an?lises estavam de acordo com as normas da ASTM. As amostras resultantes dos ensaios mec?nicas foram avaliadas no MEV. Com base nas observa??es dos resultados nos ensaios mec?nicos, (Tra??o 11,2 Mpa e 8,3 Mpa; Flex?o 34,9 Mpa e 22,9 MPa para as amostras sem e com tratamento respectivamente) observou-se que os comp?sitos refor?ados com as penas sem tratamento apresentaram um melhor comportamento quando foram expostos a carregamentos tanto de tra??o quanto de flex?o. O ensaio de absor??o evidenciou nos valores de absor??o de ?gua, uma das caracter?sticas da prote?na existente nas penas, a queratina, a sua capaciade de impermiabiliza??o a ?gua. Nas imagens do MEV foi poss?vel verificar a estrutura da pena, as regi?es de ruptura do comp?sito e a ades?o fibra/matriz. No ensaio de inflamabilidade, observou-se que apesar das penas terem como constituinte o enxofre, inibidor natural de chama, n?o houve a susten??o da queima nos comp?sitos, devido o processo de fabrica??o do comp?sito

Made available in DSpace on 2014-12-17T14:58:13Z (GMT). No. of bitstreams: 1 FlavioASL_DISSERT.pdf: 2460649 bytes, checksum: bed5dd26e82ea61d687c6641214ac014 (MD5) Previous issue date: 2012-04-27 / Space Science was built using a composite made of plaster, EPS, shredded tires, cement and water. Studies were conducted to thermal and mechanical resistance. Inside the mold EPS plates were placed in order to obtain a higher thermal resistance on the wall constructed, as well as to give it an end environmentally friendly in view of both the tire and the EPS occupy a large space in landfills and year need to be degraded when released into the environment. Compression tests were performed according to ABNT blocks to seal, measurements of the temperature variation in the external and internal walls using a laser thermometer and check the temperature of the indoor environment using a thermocouple attached to a digital thermometer. The experiments demonstrated the heat provided by the composite values from the temperature difference between the internal and external surfaces on the walls, reaching levels of 12.4 ? C and room temperature in the interior space of the Science of 33.3 ? C, remaining within the zone thermal comfort for hot climate countries. It was also demonstrated the proper mechanical strength of such a composite for sealing walls. The proposed use of the composite can contribute to reducing the extreme housing shortage in our country, producing popular homes at low cost and with little time to work / Foi constru?do o Espa?o Ci?ncia utilizando um comp?sito constitu?do de gesso, EPS, pneu triturado, cimento e ?gua. Foram realizados estudos de resist?ncias t?rmica e mec?nica. No interior do molde foram colocadas placas de EPS com o intuito de se obter uma maior resist?ncia t?rmica nas paredes constru?das, como tamb?m dar-lhe um fim ecologicamente correto, tendo em vista que tanto o pneu quanto o EPS ocupam grande espa?o em aterros sanit?rios e necessitam de anos para serem degradados quando lan?ados ao meio ambiente. Foram realizados ensaios de compress?o segundo as normas da ABNT para blocos de veda??o, medi??es da varia??o de temperatura nas paredes externas e internas utilizando um term?metro a laser e verifica??o da temperatura do ambiente interno utilizando um termopar acoplado a um term?metro digital. Os experimentos t?rmicos demonstraram os valores proporcionados pelo comp?sito a partir da diferen?a de temperatura entre as superf?cies internas e externas nas paredes, alcan?ando n?veis de 12,4?C e temperatura ambiente no interior do espa?o ci?ncia, de 33,3 ?C ficando dentro da zona de conforto t?rmico para pa?ses de clima quente. Demonstrou-se tamb?m apropriada resist?ncia mec?nica de tal comp?sito para paredes de veda??o. A utiliza??o do comp?sito proposto pode contribuir para a diminui??o do extremo d?ficit habitacional do nosso pa?s, produzindo resid?ncias populares a baixo custo e com pequeno tempo de obra

Made available in DSpace on 2014-12-17T14:58:14Z (GMT). No. of bitstreams: 1 JoaoPMS_DISSERT.pdf: 2368005 bytes, checksum: d7875a294c5267dc99db89f3b20a7106 (MD5) Previous issue date: 2012-03-14 / In the present work, three composites with distinct reinforcements (polyester, modal e polyester + modal), all if a unsaturated orthophthalic polyester resin as matrix were used, in order to conduct a comparative study by mechanical tests and water absorption. The fibre mats were prepared in a mat preparatory by immersion developed in the Textile Engineering Laboratory. The composites were manufactured using a closed mould process by compression using an unsaturated orthophthalic polyester resin as matrix and 1% MEK (methyl ethyl ketone peroxide) as an initiator. In each composite twelve samples with the dimensions of 150x25x3 mm were cut randomly for the mechanical analysis (tension x extension, three points bending and water absorption and Scanning Electron Micsroscopy). The mechanical tests were carried out in the Laborat?rio de Metais e Ensaios Mec?nicos UFRN . All the analyses were carried out according to the ASTM norms. The resultant samples from the mechanical analysis were subjected for the Scanning Electron Microscopy analysis. Based on the results obtained, it was observed that the reinforced composite with two fibres (modal + polyester) presented better results in comparison to the other two composites both in the tension/extension as well on the three point bending tests. In the water absorption test, it was possible to observe an equilibrium in the water absorption by the modal and polyester composite, due to the union of the two fibres. In the SEM images, the regions of rupture in the composites as well as the adsorption between the fiber and the matrix could be observed / No presente trabalho foram fabricados tr?s comp?sitos com refor?os distintos (poli?ster, modal e poli?ster + modal), todos com uma matriz de resina de poli?ster ortofit?lico n?o saturado, com o objetivo de realizar um estudo comparativo atrav?s de ensaios mec?nicos e absor??o d ?gua. As mantas de fibras foram preparadas num preparador de manta por imers?o desenvolvido no Laborat?rio de Engenharia T?xtil da UFRN. Os comp?sitos foram fabricados usando o processo de molde fechado por compress?o, utilizando a resina de poli?ster ortoft?lica e 1% de per?xido MEK (per?xido de metil etil cetona) como iniciador. Em cada comp?sito foram cortadas doze amostras aleatoriamente, com as dimens?es 150x25x3 mm, para avalia??o atrav?s de ensaios mec?nicos (resist?ncia ? tra??o e ? flex?o, absor??o d agua e microscopia eletr?nica de varredura). Os ensaios de tra??o e flex?o em tr?s pontos foram realizados no Laborat?rio de Metais e Ensaios Mec?nicos - UFRN. Todas as an?lises estavam de acordo com as normas da ASTM. As amostras resultantes dos ensaios mec?nicas foram avaliadas no MEV. Com base nos resultados dos ensaios mec?nicos, observou-se que o comp?sito refor?ado com as duas fibras em conjunto (poli?ster+modal) apresentou um melhor comportamento quando foram expostos a carregamentos tanto de tra??o quanto de flex?o. No ensaio de absor??o d agua foi poss?vel observar um equilibribio na absor??o de umidade do comp?sito com modal e poli?ster, devido a uni?o das duas fibras. Nas imagens do MEV foi poss?vel ver as regi?es de ruptura do comp?sito e a ades?o entre a fibra e a matriz

Made available in DSpace on 2014-12-17T14:58:15Z (GMT). No. of bitstreams: 1 JoseHBL_DISSERT_PARCIAL.pdf: 2505963 bytes, checksum: 1b82ec8a8147b2b7e13d0af6880855f0 (MD5) Previous issue date: 2012-05-02 / Conselho Nacional de Desenvolvimento Cient?fico e Tecnol?gico / Materials denominated technical textiles can be defined as structures designed and developed with function to fulfill specific functional requirements of various industrial sectors as are the cases of the automotive and aerospace industries. In this aspect the technical textiles are distinguished from conventional textile materials, in which the aesthetic and of comfort needs are of primordial importance. Based on these considerations, the subject of this dissertation was established having as its main focus the study of development of textile structures from aramid and glass fibers and acting in order to develop the manufacture of composite materials that combine properties of two different structures, manufactured in an identical operation, where each structure contributes to improving the properties of the resulting composite material. Therefore were created in laboratory scale, textile structures with low weight and different composition: aramid (100%), glass (100%) and aramid /glass (65/35%), in order to use them as a reinforcing element in composite materials with polyester matrix. These composites were tested in tension and its fracture surface, evaluated by MEV. Based on the analysis of mechanical properties of the developed composites, the efficiency of the structures prepared as reinforcing element were testified by reason of that the resistance values of the composites are far superior to the polyester matrix. It was also observed that hybridization in tissue structure was efficient, since the best results obtained were for hybrid composites, where strength to the rupture was similar to the steel 1020, reaching values on the order of 340 MPa / Os materiais denominados t?xteis t?cnicos podem ser definidos como estruturas projetadas e desenvolvidas com a fun??o de atender a requisitos funcionais espec?ficos de diversos setores da ind?stria, caso da ind?stria automotiva e aeroespacial. Nesse aspecto, distinguem-se dos materiais t?xteis convencionais, nos quais as necessidades est?ticas e de conforto t?m import?ncia primordial. Com base nessas considera??es, o tema dessa disserta??o foi estabelecido tendo como enfoque principal o estudo do desenvolvimento de estruturas t?xteis a partir de fibras de aramida e de vidro, atuando no sentido de elaborar a fabrica??o de materiais comp?sitos que combinem propriedades de duas estruturas diferentes, fabricadas em uma mesma opera??o, onde cada estrutura contribui para melhoria das propriedades do material comp?sito resultante. Para tanto foram desenvolvidas em escala laboratorial estruturas t?xteis de baixa gramatura e composi??o diferenciada de aramida (100%), vidro (100%) e aramida/vidro (65/35%) para utiliza??o como elemento refor?ante em comp?sitos com matriz de poli?ster. Os comp?sitos produzidos foram ensaiados em tra??o e sua superf?cie de fratura avaliada por MEV. Com base nas analises das propriedades mec?nicas dos comp?sitos desenvolvidos, observou-se a efici?ncia das estruturas ou elaboradas como elemento refor?ante tendo em vista que os valores de resist?ncia dos comp?sitos foram muito superiores ? matriz de poli?ster. Tamb?m foi observado que a hibridiza??o na estrutura dos tecidos foi eficiente, uma vez que os melhores resultados obtidos foram para os comp?sitos h?bridos, onde a resist?ncia na ruptura foi semelhante ? do a?o 1020, atingindo valores na ordem de 340 MPa

Made available in DSpace on 2014-12-17T14:58:19Z (GMT). No. of bitstreams: 1 EduardoCBC_DISSERT.pdf: 1858317 bytes, checksum: de7993f7a4a27b8a08342ddc43175aff (MD5) Previous issue date: 2012-12-14 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / The aim of this study is to create an artificial neural network (ANN) capable of modeling the transverse elasticity modulus (E2) of unidirectional composites. To that end, we used a dataset divided into two parts, one for training and the other for ANN testing. Three types of architectures from different networks were developed, one with only two inputs, one with three inputs and the third with mixed architecture combining an ANN with a model developed by Halpin-Tsai. After algorithm training, the results demonstrate that the use of ANNs is quite promising, given that when they were compared with those of the Halp?n-Tsai mathematical model, higher correlation coefficient values and lower root mean square values were observed / Este trabalho tem como principal objetivo a cria??o de uma arquitetura de rede neural artificial (RNA) capaz de modelar o m?dulo de elasticidade transversal (E2) de comp?sitos unidirecionais. Para tanto, se fez necess?rio o uso de um conjunto de dados que foi dividido em duas partes, uma parte sendo utilizada para o treinamento e a outra para teste das RNA. Para este trabalho se desenvolveu tr?s tipos de arquiteturas de rede diferentes uma delas possuindo somente duas entradas, a outra tr?s entradas e a ?ltima foi uma arquitetura mista que combina uma RNA com um modelo desenvolvido por Halpin-Tsai. Ap?s o treinamento dos algoritmos, os resultados demonstram que o uso de RNAs se mostra bastante promissor, j? que quando esses resultados foram comparados com o modelo matem?tico de Halpin-Tsai, apresentaram maiores valores de coeficiente de correla??o e menores valores de erro m?dio quadr?tico

Made available in DSpace on 2014-12-17T14:58:19Z (GMT). No. of bitstreams: 1 CamilaCS_DISSERT.pdf: 2789090 bytes, checksum: 9ef229c63f260457515e8c401747ce25 (MD5) Previous issue date: 2012-08-10 / Conselho Nacional de Desenvolvimento Cient?fico e Tecnol?gico / This study aims to evaluate the mechanical properties of polymer matrix composites reinforced with sisal fabric bidirectional tissue (Agave sisalana,) and E-glass fibers, containing the following configuration: a polymer matrix hybrid composite (Polyester Resin orthophalic) reinforced with three (3) layers of glass fibers and alternating-2 (two) layers of bidirectional sisal fabric, and finally a composite of polymer matrix reinforced with five (5) layers of glass fiber mat-type E. For this purpose as first step, the preparation of by sisal, since they are not on the market. The composites were made by manual lamination (Hand lay-up) and evaluated for tensile properties and three point bending both in the dry, and wet conditions aswele as immersed in oil. Macroscopic and microscopic characteristics of the materialsweve awalysed, after the completion of the mechanical tests. After the studies, it was proven that the sisal fiber decreases the tensile stiffness of the material above 50% for both situations studied the tensile strength of the material decreases by approximately 40% for the cases mentioned, and when compared to the specific strength stiffness values drop to 14.6% and 29.02% respectively for the dry state only. Constants for bending the values were are to approximately 50% to 25% for strength and stiffness of the material for the cases dry, wet and immersed in oil. Under the influence of tension fluids do not interfere in the stiffness of the material for the bending tests, the same does not occur with the resistance, and these values are modified only in the cases stiffness and flexural strength / Este trabalho tem como objetivo avaliar as propriedades mec?nicas de comp?sitos de matriz polim?rica refor?ados com tecidos bidirecionais de sisal (Agave Sisalana,) e fibras de vidro E, contendo estes materiais a seguinte configura??o: um comp?sito h?brido de matriz polim?rica (Resina Poli?ster Ortoft?lica) refor?ado com 3 (tr?s) camadas de fibras de vidro e intercalando as 2 (duas) camadas de tecido bidirecional de sisal, e por fim um comp?sito de matriz polim?rica refor?ado com 5 (cinco) camadas de manta de fibras de vidro do tipo E. Para tanto teve se como primeira etapa a confec??o dos tecidos de sisal, j? que estes n?o se encontram no mercado. Os comp?sitos foram confeccionados de acordo com o processo de lamina??o manual (Hand lay-up) e avaliadas as propriedades de tra??o uniaxial e flex?o em tr?s pontos do material tanto em estado seco, como para o material imerso em ?gua destilada e imerso em petr?leo e as caracter?sticas macrosc?picas e microsc?picas dos materiais ap?s a realiza??o dos ensaios mec?nicos, t5amb?m j? realizados. Ap?s a realiza??o dos estudos foi observado que a fibra de sisal diminui a rigidez do material ? tra??o acima de 50 % para ambas as situa??es estudadas, a resist?ncia ? tra??o do material diminui em aproximadamente 40% para os casos citados, sendo que quando comparado ? resist?ncia e rigidez especificas esses valores caem para 14,6% e 29,02 % respectivamente s? para o estado seco. Quando observados as constantes para flex?o esses valores passam a serem de aproximadamente 50 % para a resist?ncia e 25% para a rigidez do material para os casos secos, ?mido e imerso em petr?leo

Made available in DSpace on 2014-12-17T14:58:20Z (GMT). No. of bitstreams: 1 AlanJLM_DISSERT.pdf: 1835050 bytes, checksum: 47bf4fbd76665d11995bd7eb5bd3522a (MD5) Previous issue date: 2013-07-23 / Materials known as technical textiles can be defined as structures designed and developed to meet specific functional requirements of various industry sectors, which is the case in automotive and aerospace industries, and other specific applications. Therefore, the purpose of this work presents the development and manufacture of polymer composite with isophthalic polyester resin. The reinforcement of the composite structure is a technical textile fabric made from high performance fibers, aramid (Kevlar 49) and glass fiber E. The fabrics are manufactured by the same method, with the aim of improving the tensile strength of the resulting polymer composite material. The fabrics, we developed some low grammage technical textile structures in laboratory scale and differentiated-composition type aramid (100%), hybrid 1 aramid fiber / glass (65/35%) and hybrid 2 aramid fiber / glass (85/15% ) for use as a reinforcing element in composite materials with unsaturated isophthalic polyester matrix. The polymer composites produced were tested in uniaxial tensile fracture surface and it?s evaluated by SEM. The purpose of this work characterize the performance of polymer composites prepared, identifying changes and based on resistance to strain corresponding to the mechanical behavior. The objectives are to verify the capability of using this reinforcement structure, along with the use of high performance fibers and resin in terms of workability and mechanical strength; verify the adherence of the fiber to the matrix and the fracture surface by electron microscopy scanning and determination of tensile strength by tensile test. The results indicate that, in a comparative study to the response of uniaxial tensile test for tensile strength of the composites and the efficiency of the low percentage of reinforcement element, being a technical textile fabric structure that features characteristic of lightness and low weight added in polymer composites / Os materiais denominados de tecidos t?cnicos podem ser definidos como estruturas projetadas e desenvolvidas com a fun??o de atender a requisitos funcionais espec?ficos de diversos setores da ind?stria com aplica??es espec?ficas. Nesse sentido, este trabalho apresenta o desenvolvimento e a fabrica??o de comp?sito polim?rico com resina poli?ster isoft?lico. O refor?o do comp?sito ? uma estrutura de tecido t?xtil t?cnico confeccionado com fibras de alto desempenho de aramida (Kevlar 49) e fibra de vidro E. Os tecidos s?o fabricados pelo mesmo m?todo, com o objetivo do aprimorar a resist?ncia a tra??o do material comp?sito polim?rico resultante. Os tecidos, foram desenvolvidos em escala laboratorial com baixa gramatura e composi??o diferenciada de aramida (100%), h?brido 1 fibra de aramida/vidro (65/35%) e h?brido 2 fibra de aramida/vidro (85/15%) para utiliza??o como elemento refor?ante em comp?sitos com matriz de poli?ster insaturada isoft?lico. Os comp?sitos polim?ricos produzidos foram ensaiados em tra??o uniaxial e sua superf?cie de fratura avaliada por MEV. A proposta do trabalho ? caracterizar o desempenho dos comp?sitos polim?ricos elaborados, identificando as altera??es e baseando-se na resist?ncia ao ensaio de tra??o correspondente a comportamento mec?nico. Os objetivos s?o verificar a potencialidade da utiliza??o desta estrutura de refor?o, juntamente com a utiliza??o das fibras de alto desempenho e a resina, em termos de trabalhabilidade e resist?ncia mec?nica; verificar a ader?ncia da fibra ? matriz e a superf?cie de fratura atrav?s de microscopia eletr?nica de varredura e determina??o de resist?ncia ? ruptura por ensaio de tra??o. Os resultados indicam que, em um estudo comparativo para a resposta dos ensaios mec?nicos de tra??o uniaxial h? resist?ncia ? ruptura dos comp?sitos e a efici?ncia da baixa porcentagem do elemento de refor?o, sendo uma estrutura de tecido t?xtil t?cnico que apresenta caracter?stica de leveza e baixa gramatura adicionada nos comp?sitos polim?ricos

Made available in DSpace on 2014-12-17T14:58:24Z (GMT). No. of bitstreams: 1 AlvaroCPG_DISSERT.pdf: 5603649 bytes, checksum: a174104255aac25a9810c32081bc2cd1 (MD5) Previous issue date: 2014-04-11 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / Thermal insulation is used to protect the heated or cooled surfaces by the low thermal conductivity materials. The rigid ricin polyurethane foams (PURM) are used for thermal insulation and depend on the type and concentration of blowing agent. Obtaining PURM occurs by the use of polyol, silicone, catalyst and blowing agent are pre -mixed, reacting with the isocyanate. The glass is reusable, returnable and recyclable heat insulating material, whose time of heat dissipation determines the degree of relaxation of its structure; and viscosity determines the conditions for fusion, operating temperatures, annealing, etc. The production of PURM composites with waste glass powder (PV) represents economical and renewable actions of manufacturing of thermal insulating materials. Based on these aspects, the study aimed to produce and characterize the PURM composites with PV, whose the mass percentages were 5, 10, 20, 30, 40 and 50 wt%. PURM was obtained commercially, while the PV was recycled from the tailings of the stoning process of a glassmaking; when the refining process was applied to obtain micrometer particles. The PURM + PV composites were studied taking into account the standard sample of pure PURM and the influence of the percentage of PV in this PURM matrix. The results of the chemical, physical and morphological characterization were discussed taking into account the difference in the microstructural morphology of the PURM+PV composites and the pure PURM, as well the results of the physicochemical, mechanical e thermophysical tests by values obtained of density, hardness, compressive strength, specific heat, thermal conductivity and diffusivity. In general, the structure of pure PURM showed large, elongated and regular pores, while PURM+PV composites showed irregular, small and rounded pores with shapeless cells. This may have contributed to reducing their mechanical strength, especially for PURM - PV50. The hardness and density were found to have a proportional relationship with the PV content on PURM matrix. The specific heat, thermal diffusivity and thermal conductivity showed proportional relationship to each other. So, this has been realized that the increasing the PV content on PURM matrix resulted in the rise of diffusivity and thermal conductivity and the decrease of the specific heat. However, the values obtained by the PURM composites were similar the values of pure PURM, mainly the PURM-PV5 and PURM-PV10. Therefore, these composites can be applied like thermal insulator; furthermore, their use could reduce the production costs and to preserve the environment / O isolamento t?rmico ? empregado na prote??o de superf?cies aquecidas ou resfriadas atrav?s de materiais de baixa condutividade t?rmica. As espumas r?gidas de poliuretano de mamona (PURM) s?o utilizadas para o isolamento t?rmico e dependem do tipo e da concentra??o do agente de expans?o. O vidro ? um material isolante t?rmico reutiliz?vel, retorn?vel e recicl?vel, cujo tempo de dissipa??o do calor determina o grau de relaxa??o da sua estrutura e a viscosidade determina as condi??es de fus?o, temperaturas de trabalho, recozimento, etc. A produ??o de comp?sitos de PURM com rejeito de p? de vidro (PV) representa a??es econ?micas e renov?veis de fabrica??o de materiais isolantes t?rmicos. Baseado nestes aspectos, o trabalho objetivou a produ??o e caracteriza??o de comp?sitos de PURM com PV 5, 10, 20, 30, 40 e 50 % em massa. A PURM foi obtida comercialmente, enquanto que o PV foi reaproveitado do rejeito do processo de lapida??o de uma ind?stria vidreira, cujo processo de refino foi utilizado para se obter part?culas microm?tricas. Os comp?sitos de PURM + PV foram estudados levando-se em considera??o o padr?o de refer?ncia PURM pura e a influ?ncia do percentual de PV desta matriz. Os resultados das caracteriza??es qu?micas, f?sicas e morfol?gicas foram apresentadas e discutidas levando-se em considera??o a diferen?a na morfologia estrutural dos comp?sitos do PURM e da PURM pura e os valores obtidos nos ensaios de massa espec?fica, dureza, resist?ncia ? compress?o, condutividade t?rmica, calor espec?fico e difusividade t?rmica. Em geral, a estrutura da PURM pura apresentou poros regulares alongados e grandes, enquanto que os comp?sitos de PURM + PV apresentaram poros irregulares, pequenos e arredondados com presen?a de c?lulas disformes, o que p?de ter contribu?do na redu??o de sua resist?ncia mec?nica, principalmente para a PURM-PV50. A dureza e a massa espec?fica revelaram ter uma rela??o proporcional com o teor de PV na matriz de PURM. O calor espec?fico, condutividade e difusividade t?rmica apresentaram rela??es proporcionais entre si. Assim, foi percebido que o aumento do teor de PV na matriz de PURM proporcionou um aumento da difusividade t?rmica e da condutividade t?rmica e a diminui??o do calor espec?fico. Contudo, os valores apresentados pelos comp?sitos de PURM foram similares aos valores da PURM pura, principalmente os comp?sitos PURM-PV5 e PURM-PV10. Portanto, estes comp?sitos podem ser aplicados como isolantes t?rmicos, al?m disto, o seu uso poderia reduzir os custos de fabrica??o e preservar o meio ambiente