<p>Aim and Objectives: To assess the effect of bleaching on the marginal integrity of Class V composite resin restorations. To determine the effect of a 6% hydrogen peroxide over the counter and a 38% hydrogen peroxide in-office vital bleaching treatment products on the microleakage of Class V composite restorations.</p>

Made available in DSpace on 2014-06-11T19:23:29Z (GMT). No. of bitstreams: 0 Previous issue date: 2006-09-22Bitstream added on 2014-06-13T19:09:19Z : No. of bitstreams: 1 ulhoa_mpm_me_bauru.pdf: 4701106 bytes, checksum: 92fca12bc8517cc3f9df59893cd0503c (MD5) / Secretaria de Educação do Estado de São Paulo / A Humanidade, ao buscar as melhoras nas suas condições de vida, vem desenvolvendo materiais capazes de reparar e melhorar imperfeições naturais e acidentais. Encontra nas resinas compostas, constantemente utilizadas por dentistas, uma maneira de reparar imperfeições e perdas de materiais dentários no ser humano. A escolha de resinas compostas em substituição aos antigos materiais de restauração, como o amálgama, se dá pelo fato de serem fáceis de preparar, apresentarem menor desgaste, serem praticamente imperceptíveis após sua aplicação devido à grande quantidade de cores fornecidas pelos fabricantes. Porém não apresentam desgaste semelhante ao do esmalte dentário, sendo necessária substituição com o passar do tempo, devido ao desgaste abrasivo. Dentre os vários fatores determinantes do processo de desgaste abrasivo, encontram-se, genericamente, as características da própria resina e do preparo cavitário, assim como da restauração confeccionada e das condições das agressões a que ela for submetida. Para fazer a medição da resistência ao desgaste abrasivo, utilizou-se o método do disco retificado aperfeiçoado para Odontologia (COELHO, 1991; BIANCHI et al., 2002). É utilizado um banco de ensaios onde um disco dinâmico revestido com porcelana desgasta um disco estático revetido com a resina polimerizada em um tempo pré-estabelecido... / Humanity, when searching for a better life conditions, is developing materials capable to repair and to improve natural and accidental imperfections. It finds in composite resins, constantly used for dentists, a way to repair imperfections and losses of human dental material. The composed resin choice in substituion to the old restoration materials, as the amalgamates, it is for the fact of being easy to prepare, to present less wear, to be practically invisible after its application due to great amount of colors supplied for the manufacturers. However they do not show similar wear as the dental enamel, being necessary the substitution after a while, due to the abrasive wear. Among some determinative factors of the process of abrasive wear, there are, generically, the characteristics of the resin and the cavitary preparation, as well as the confectioned restoration and the conditions of the aggressions that it is submitted. To make the measurement of the resistance to the abrasive wear, the method of the rectified circular surface improved for odontology was used (COELHO, 1991; BIANCHI et al., 2002). A Test bench is used where a dynamic circular surface covered with porcelain consumes a static circular surface covered with the polymerized resin in a pre-established time... (Complete abstract, click electronic address below)

Resumo: O presente estudo teve por objetivo avaliar o efeito do gel de peróxido de hidrogênio a 20% e 35% na alteração de cor, opacidade e fluorescência de materiais restauradores estéticos. Foram confeccionados 210 espécimes com 3mm de diâmetro e 2mm de espessura, sendo 30 de cada tipo de resina composta (Amaris, Admira, Estelite, Esthet X, Venus, Z350 e GrandioSO). Os espécimes foram armazenados em água deionizada por 24 horas. Na seqüência os mesmos foram polidos com lixa d'água #4000. Realizou-se então a primeira medição de cor, opacidade e fluorescência por um aparelho espectrofotômetro com iluminante padrão D65. Em seguida, cada grupo de 30 corpos de prova foi dividido em três subgrupos (n=10) de acordo com o tratamento clareador; utilizando-se o gel clareador peróxido de hidrogênio a 20% e 35%. Foram feitas quatro aplicações do gel clareador de 30 minutos cada, totalizando duas horas.O grupo controle não recebeu nenhum tipo de tratamento, permanecendo imerso em água deionizada por todo período do experimento. Após a ação dos géis, realizou-se a segunda medição da cor, opacidade e fluorescência. Os dados obtidos foram submetidos à análise estatística pelos testes ANOVA e Tukey ao nível de significância de 5%. Os resultados da ANOVA a dois fatores para o parâmetro ΔE mostram haver diferença estatística significante apenas para o fator concentração (p=0,00). O tratamento com o gel clareador a 35% provocou um resultado com uma média de variação de cor estatisticamente maior com relação aos demais grupos. Quanto à opacidade não houve diferença estatística significativa para nenhum fator. A fluorescência foi influenciada pela concentração do peróxido de hidrogênio (p=0,0016) e pelo tipo de resina (p=0,000), não havendo diferença entre as concentrações de 20% e 35%. A resina que mais sofreu alteração da fluorescência dos materiais... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: This study evaluate the effect of 20% and 35% hydrogen peroxide on color, opacity and fluorescence of seven composities resins: Amaris, Admira, Estelite Sigma, Esthet X, Venus, Z350 e GrandioSO. 30 specimes, of each material, were prepared and than they recived bleaching treatment. A control group was stored in water (n=10). Color and spectral distribution of the materials were measured according to the CIELAB color scale, before and after bleaching treatment. The color and the Opacity parameter (OP) of specimens was measured after polymerization on a reflection spectrophotometer under the illuminant D65 over white and black backgrounds. UV component of the illuminant was included and excluded to calculate the fluorescence spectrum (FP). Differences and changes in optical properties (color, opacity parameter and fluorescence parameter) were analyzed using ANOVA and Tukey test, with significance set at p < 0.05. The range of color values (delta E*) was significantly influenced by concentration of hydrogen peroxide (p=0.00). The range of OP values was not influenced by material (p=0.14) or bleaching agent (p=0.38). And the range of FP values was significantly influenced by concentration of hydrogen peroxide (p=0.0016) and also by material (p=0.00). It is demonstrated that opacity of resin composites did not change after 20% and 35% hydrogen peroxide treatment. But color and fluorescence changed significantly after these treatments / Orientador: Carlos Rocha Gomes Torres / Coorientador: Alessandra Bühler Borges / Banca: Cláudio A. Talge Carvalho / Banca: Sérgio Eduardo de Paiva Gonçalves / Banca: Ricardo Amore / Banca: Claudio Hideki Kubo / Doutor

Orientador: Eduardo Carlos Bianchi / Banca: Cesar Antunes de Freitas / Banca: Paulo Noronha Lisboa Filho / O Programa de Pós-Graduação em Ciência e Tecnologia de Materiais, PosMat, tem caráter institucional e integra as atividades de pesquisa em materiais de diversos campi da Unesp / Resumo: A Humanidade, ao buscar as melhoras nas suas condições de vida, vem desenvolvendo materiais capazes de reparar e melhorar imperfeições naturais e acidentais. Encontra nas resinas compostas, constantemente utilizadas por dentistas, uma maneira de reparar imperfeições e perdas de materiais dentários no ser humano. A escolha de resinas compostas em substituição aos antigos materiais de restauração, como o amálgama, se dá pelo fato de serem fáceis de preparar, apresentarem menor desgaste, serem praticamente imperceptíveis após sua aplicação devido à grande quantidade de cores fornecidas pelos fabricantes. Porém não apresentam desgaste semelhante ao do esmalte dentário, sendo necessária substituição com o passar do tempo, devido ao desgaste abrasivo. Dentre os vários fatores determinantes do processo de desgaste abrasivo, encontram-se, genericamente, as características da própria resina e do preparo cavitário, assim como da restauração confeccionada e das condições das agressões a que ela for submetida. Para fazer a medição da resistência ao desgaste abrasivo, utilizou-se o método do disco retificado aperfeiçoado para Odontologia (COELHO, 1991; BIANCHI et al., 2002). É utilizado um banco de ensaios onde um disco dinâmico revestido com porcelana desgasta um disco estático revetido com a resina polimerizada em um tempo pré-estabelecido... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Humanity, when searching for a better life conditions, is developing materials capable to repair and to improve natural and accidental imperfections. It finds in composite resins, constantly used for dentists, a way to repair imperfections and losses of human dental material. The composed resin choice in substituion to the old restoration materials, as the amalgamates, it is for the fact of being easy to prepare, to present less wear, to be practically invisible after its application due to great amount of colors supplied for the manufacturers. However they do not show similar wear as the dental enamel, being necessary the substitution after a while, due to the abrasive wear. Among some determinative factors of the process of abrasive wear, there are, generically, the characteristics of the resin and the cavitary preparation, as well as the confectioned restoration and the conditions of the aggressions that it is submitted. To make the measurement of the resistance to the abrasive wear, the method of the rectified circular surface improved for odontology was used (COELHO, 1991; BIANCHI et al., 2002). A Test bench is used where a dynamic circular surface covered with porcelain consumes a static circular surface covered with the polymerized resin in a pre-established time... (Complete abstract, click electronic address below) / Mestre

Introdução: Existe no mercado odontológico muitos instrumentos rotatórios para serem utilizados no polimento final de uma restauração adesiva. Como são muitas as opções, e um mesmo fabricante tem mais de um tipo de instrumento rotatório para realizar a finalização da restauração, não se estabelece uma conduta única que determine qual o instrumento utilizar para resinas compostas que contenham nanopartículas. Objetivo: Avaliar, in vitro, o efeito de dois diferentes sistemas de polimento, baseados em um e multi etapas, sobre a qualidade e rugosidade da superfície de duas resinas com nanopartículas. Materiais e métodos: As amostras foram confeccionadas com resina nanoparticulada Filtek Z 350 XT (3M ESPE) e nanohíbrida Tetric N Ceran (Ivoclar Vivadent ). As amostras foram confeccionadas em moldes cilíndricos medindo 3 mm X 6 mm. Um único operador executou todos os procedimentos. Cada grupo foi composto por 20 amostras: 1) ZXT-Controle (sem polimento); 2)TNC-Controle (sem polimento); 3) ZXT+ Sof-Lex (seqüência Laranja – fina e superfina); 4) ZXT+ Optrapol; 5) TNC+ Optrapol ; 6) TNC+ Sof- Lex (seqüência Laranja – fina e superfina ). A rugosidade de superfície foi avaliada com rugosímetro (Ra), MEV e AFM. Estatística: Para análise das médias de rugosidade Ra (μm), os dados foram submetidos aos testes de normalidade de ANOVA, ao nível de significância de 5%. Uma vez verificada a distribuição normal dos resultados, estes foram submetidos à análise de variância, seguida pelo teste de Tukey com nível de significância de 5%. Resultados: As análises qualitativas e quantitativas mostraram que as resinas polidas com Optrapol apresentaram maior rugosidade superficial e o polimento com Sof-Lex não mostrou diferença estatística entre as resinas testadas. A menor rugosidade foi obtida com os grupos controle, sem diferença estatística entre as resinas. Conclusão: Optrapol promove maior rugosidade nas resinas testadas, e ZXT apresentou maior rugosidade. O polimento com Soft-Lex não mostrou diferenças estatisticamente significantes entre as resinas testadas. A rugosidade superficial das resinas foi menor com TNC, quando comparado com Optrapol. A menor rugosidade de superfície obtida foi pelo grupo controle. / Introduction: There are many tools on the market dental rotary for use in polishing of a restoration adhesive. As there are many choices, and the same manufacturer have more than one type of rotary apparatus of restoration, does not establish a single conduit to determine which tool to use composites containing nanoparticles. Objective: To evaluate, in vitro, the effect of two different polishing systems, based on a multi steps and on the quality and surface roughness of two composites nanoparticles. Materials and methods: The samples were prepared with nanofilled material resin Filtek Z 350 XT (3M ESPE) and nanohíbrid Tetric N Ceran (Ivoclar Vivadent). The samples were made in cylindrical molds measuring 3 mm X 6 mm. A single operator executed all procedures. Each group consisted of 20 samples: 1) ZXT-control (without polishing); TNC-2) control (without polishing); 3) ZXT Sof-Lex (Orange – fine and Superfine); 4) ZXT Optrapol; 5) TNC Optrapol; 6) TNC Sof-Lex (Orange – fine and Superfine). The surface roughness was assessed with porfilometry (Ra), SEM and AFM. Statistical analyses: For analysis of mean roughness Ra (um), the data were tested for normality of ANOVA, at a significance level of 5%. Once verified the normal distribution of the results, they were subjected to analysis of variance followed by Tukey's test with a significance level of 5%. Results: The qualitative and quantitative analyzes showed that resins polished with Optrapol showed higher surface roughness and polishing with Sof-Lex showed no statistical difference between the resins tested. The lowest roughness was obtained with the control group, with no statistical difference between the resins. Conclusion: Optrapol promotes greater roughness in the resins tested, and ZXT showed higher roughness. Polishing with Soft-Lex showed no statistically significant differences between the tested resins. The surface roughness of the resins with TNC was lower when compared with Optrapol. The lowest surface roughness was obtained by the control group.

Conselho Nacional de Desenvolvimento Científico e Tecnológico / O objetivo deste trabalho foi avaliar o efeito de um diodo emissor de luz (LED) Smart Lite PS (Dentsply) e da lâmpada halógena convencional Curing Light XL 3000 (3M) na efetividade de polimerização do compômero Dyract Ap (Dentsply) e da resina composta TPH Spectrum (Dentsply) por meio de testes de microdureza Knoop, resistência à compressão e resistência flexural e caracterização dos materiais. Foram confeccionadas 100 amostras e divididas em 12 grupos de acordo com o teste aplicado, a luz de polimerização e o material utilizado. A lâmpada halógena convencional selecionada, Curing Light XL 3000 (3M), tinha intensidade de 470mW/cm2 e comprimento de onda entre 400 e 510nm; o LED Smart Lite PS (Dentsply) tinha intensidade de 950mW/cm2 e comprimento de onda entre 450 e 490nm. O tempo de fotopolimerização para cada incremento com 2mm de espessura foi de 40 s. para a lâmpada halógena convencional e 10 s. para o LED. Para os testes de microdureza Knoop foram confeccionadas 20 amostras numa matriz cilíndrica com 8,0mm de diâmetro e 2,0mm de altura. As leituras da microdureza foram realizadas nas superfícies superiores e inferiores das amostras utilizando um microdurômetro Micromet 2003, com uma carga de 50 gf por 15 s. Para o teste de resistência à compressão foram confeccionadas 40 amostras numa matriz cilíndrica com 4,0mm de diâmetro e 8,0mm de altura. A resistência foi medida na máquina de teste universal de ensaios Emic DL 10.000 com uma célula de carga 500Kgf e velocidade de carregamento de 0,5 mm/min. Para o teste de resistência flexural foram construídas 40 amostras numa matriz em forma de caixa com 25,0mm de comprimento, 2,0mm de altura e 2,0mm de largura. A resistência foi medida na máquina de teste universal de ensaios Emic DL 10.000 com uma célula de carga 50Kgf e velocidade de carregamento de 0,5 mm/min. Cada material foi caracterizado pela termogravimetria, espectrometria no infravermelho, espectrometria de ressonância magnética nuclear, teor de cinzas, fluorescência de raios-X e microscopia eletrônica de varredura. Os resultados foram tratados por ANOVA e teste de SNK (p<0,05). Os resultados de microdureza Knoop, resistência à compressão e resistência flexural providos pela luz halógena foram melhores que os dos LED. A resina composta apresentou melhor performance que o compômero em todos os testes. / The goal of this work was to evaluate the effects of the blue light emitting diodes (LEDs) Smart Lite PS (Dentsply) and the conventional halogen lamp Curing Light XL 3000 (3M) on the polymerization effectiveness of the Dyract Ap compomer (Dentsply) and the TPH Spectrum composite resin (Dentsply) by the Knoop microhardness, compressive strength, flexural strength and material characterization tests. A hundred samples were prepared and divided into 12 groups according to the test applied, the polymerization light and the material. The conventional halogen lamp light had power of 470mW/cm and wavelength between 400 and 510nm; the LED light had power of 950mW/cm and wavelength between 450 and 490nm. The polymerization time for each material 2mm buildup was 40 seconds for the conventional halogen lamp and 10 seconds for LED. For the Knoop microhardness tests the 20 samples were cylinder shaped, 8mm diameter and 2mm height. The hardness was read in the upper and lower side of the samples by a micrometer (Micromet 2003), with 50 gf for 15 seconds. For the compressive strength test the 40 samples were cylinder shaped, 4mm diameter and 8mm height. The strength was measured in an universal testing machine Emic DL 10.000 with 500Kgf and cross-head speed of 0,5 mm/min. For the flexural strength test the 40 samples were box shaped, 25mm length, 2mm width and 2mm height. The strength was measured in an universal testing machine Emic DL 10.000 machine with 50Kgf and cross-head speed of 0,5 mm/min. Each material was characterized by Thermogravimetry, FT-IR analysis, Nuclear Magnetic Resonance, Ash Content Test, X-Ray Fluorescence and Scanning Electron Microscopy. The results were treated by ANOVA and SNK tests (p<0,05). The Knoop microhardness, compressive strength and flexural strength results provided by the halogen light lamp were better than the LED ones. The composite resin performed better than the compomer in all mechanical tests.

Submitted by LETÍCIA CARVALHO COUTINHO COSTA PEROTE (leticiaccc@gmail.com) on 2016-04-08T17:53:49Z No. of bitstreams: 1 Tese biblioteca finalizada.pdf: 4785988 bytes, checksum: 99777155681f63934c41a2cacd0892f3 (MD5) / Approved for entry into archive by Ana Paula Grisoto (grisotoana@reitoria.unesp.br) on 2016-04-11T17:17:19Z (GMT) No. of bitstreams: 1 perote_lccc_dr_sjc.pdf: 4785988 bytes, checksum: 99777155681f63934c41a2cacd0892f3 (MD5) / Made available in DSpace on 2016-04-11T17:17:20Z (GMT). No. of bitstreams: 1 perote_lccc_dr_sjc.pdf: 4785988 bytes, checksum: 99777155681f63934c41a2cacd0892f3 (MD5) Previous issue date: 2016-02-17 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O objetivo deste estudo foi avaliar a influência de soluções de clorexidina e de própolis e da simulação de pressão pulpar na resistência de união entre resina e dentina. Para isto, foram obtidos segmentos coronários de 120 dentes humanos. Metade das amostras foram conectadas a um dispositivo de simulação de pressão pulpar, cuja altura foi ajustada para 15 cm de água. Foi realizado condicionamento com ácido fosfórico 37% por 15 s, lavagem e secagem com papel absorvente. Em seguida, foram divididas em 3 grupos, de acordo com a solução aplicada por 30 s: GC(Grupo Controle – nenhuma solução), CLX (Digluconato de Clorexidina 0,2%), PA (Extrato de própolis aquoso). Aplicou-se o adesivo (Single Bond Universal) e resina composta (Filtek Z250) em todos as amostras. Os grupos foram subdivididos de acordo com o tipo de envelhecimento: I (Corte Imediato), C (15000 ciclos térmicos). As amostras foram cortadas em palitos e submetidas ao teste de microtração. Os dados obtidos de resistência de união (MPa) foram submetidos ao teste de ANOVA 3 fatores. Para o fator Solução, não foi encontrada diferença estatisticamente significante entre os grupos (p=0,46), mas sim para os fatores Pressão Pulpar (p=0,00) e Envelhecimento (p=0,00), além das interações entre os fatores Solução e Pressão Pulpar (p= 0,00), Pressão Pulpar e Envelhecimento (p=0,00) e entre os três fatores (p=0,03). Os resultados do teste de Tukey para o fator Pressão Pulpar foram: CPP (com pressão pulpar): 29,19a, SPP (sem pressão pulpar): 32,98b; e para o fator Envelhecimento foram: C (ciclados): 28,12a, I (imediato): 34,05b. Concluiu-se que as soluções de clorexidina e de própolis não interferiram na resistência de união; e que a simulação de pressão pulpar e a termociclagem diminuíram os valores de resistência de união da resina à dentina. / This study aimed to assess the influence of chlorhexidine and propolis solutions and simulated pulpal pressure on the bond strength between resin and dentin. To do so, crown segments of 120 human teeth were obtained. Half of the samples were connected to a pulp pressure simulation device, adjusted to 15 cm H2O. Conditioning was accomplished with 37% phosphoric acid for 15 seconds, washing and drying with absorbing paper. Then, samples were split into 3 groups, according to the solution applied for 30 s: GC (Control group – no solution), CLX (Chlorhexidine digluconate 0.2%), PA (Aqueous propolis extract). Single Bond Universal adhesive and composite resin (Filtek Z250) were applied in all samples. Groups were subdivided according to the aging process: I (Immediate cut) and T (15000 thermal cycles). Samples were cut into beams and went through microtensile bonding tests. Bond strength data (MPa) were analyzed by three-way ANOVA. For the factor Solution, there was no statistically significant difference among the groups (p = 0.46), but was found difference for the factors Pulpal Pressure (p=0.00), Aging (p=0.00), and interaction between Solution and Pulpal Pressure (p=0.00), Pulpal Pressure and Aging (p=0.00) and between the 3 factors (p=0.03). The results from Tukey’s test for Pulpal Pressure factor were: SPP (simulated pulpal pressure): 29,19a, NPP (no pulpal pressure): 32,98b; and for the factor Aging were: T (thermal cycling): 28,12a, I (immediate): 34,05b. It was concluded that chlorhexidine and propolis solutions have not interfered in the bond strength; but simulated pulpal pressure and termal cycling reduced the dentin bond strength.

Made available in DSpace on 2014-06-11T19:31:25Z (GMT). No. of bitstreams: 0 Previous issue date: 2010-07-16Bitstream added on 2014-06-13T19:20:21Z : No. of bitstreams: 1 rocha_dm_dr_sjc.pdf: 501808 bytes, checksum: d965f3ab0fb785017ed14a552084fe08 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / A proposta desse estudo foi avaliar a deflexão cuspídea e a resistência à fratura de pré-molares, com e sem tratamento endodôntico, restaurados com diferentes técnicas e materiais restauradores. Para tal foram utilizados 60 pré-molares hígidos, extraídos por motivos ortodônticos que foram divididos em 6 grupos. Seis dentes foram mantidos hígidos, formando o grupo controle positivo (C POS), outros 6 receberam preparos tipo MOD e não receberam procedimentos restauradores formando o Grupo controle negativo (C NEG). Os demais 48 dentes foram divididos em 4 grupos de 12 dentes que foram restaurados de acordo com cada grupo. No grupo RC os dentes foram restaurados diretamente com resina composta, os demais grupos receberam tratamento endodôntico. No grupo CIV, os dentes tiveram as suas câmaras pulpares preenchidas com cimento de ionômero de vidro e posteriormente restauradas com resina composta, no grupo PM os dentes receberam pinos metálicos e foram restaurados com resina composta e por fim, os dentes do grupo PF receberam pinos de fibra de vidro e foram restaurados diretamente com resina composta. Os corpos-de-prova foram então submetidos a um ensaio não destrutivo de compressão a fim de se realizar a medição de deflexão das cúspides dos dentes de cada grupo e posteriormente, realizou-se o ensaio destrutivo a fim de registrar as medidas de resistência à fratura de cada grupo envolvido. Podem-se perceber diferenças estatisticamente significantes entre os grupos experimentais e os grupos controle, tanto para a deflexão das cúspides (CNEG: 81,0 με; CPOS: 5,20 με; RC: 17,73 με; CIV: 17,63 με; PF: 20,61 με; PM: 24,29 με) quanto para os valores de resistência à fratura (CNEG: 5,212 Kgf; CPOS: 128,22 Kgf; RC: 48,89 Kgf; CIV: 18,41 Kgf; PF: 29,81 Kgf; PM: 37,51 Kgf). Entre os grupos experimentais podem-se notar diferenças estatisticamente significantes... / The aim of this study was to evaluate de cuspal deflection and the fracture resistance of pre-molars, with and without endodontic therapy, using different restorative techniques and materials. Sixty sound teeth, extracted by orthodontic reasons were divided in 6 groups. Six teeth remained unprepared and formed the positive control group, other 6 teeth were MOD prepared and remained unrestored forming the negative control group. The remaining 48 teeth were divided in 4 groups with 12 teeth each and were restored following the groups. The RC group teeth were directly restored with composite resins. The other 3 groups received endodontic therapy. At the CIV group, the pulpal chambers of the endodontic treated teeth were fulfilled with glass ionomer cements an then directly restored with composite resin, the PM group teeth were restored with a metallic post and then directly restored with composite resin, in the PF group were used a fiber glass post and then direct composite restoration. The specimens was submitted first to non-destructive compression test due to cuspal deflection measurements, and then submitted to a destructive compression test to evaluate the fracture resistance of the specimens. Statistical differences were perceived when the experimental groups were compared to the control groups thus cuspal deflection (CNEG: 81,0 με; CPOS: 5,20 με; RC: 17,73 με; CIV: 17,63 με; PF: 20,61 με; PM: 24,29 με) and fracture resistance (CNEG: 5,212 Kgf; CPOS: 128,22 Kgf; RC: 48,89 Kgf; CIV: 18,41 Kgf; PF: 29,81 Kgf; PM: 37,51 Kgf). Differences between the experimental groups were verified both cuspal deflection, with a better performance of the RC and the CIV groups. The PM group showed the highest values of cuspal deflection. Concerning fracture resistance, the highest values were presented by the RC and CIV groups and the worst performance presented... (Complete abstract click electronic access below)

Made available in DSpace on 2014-06-11T19:31:25Z (GMT). No. of bitstreams: 0 Previous issue date: 2010-12-04Bitstream added on 2014-06-13T20:41:40Z : No. of bitstreams: 1 ribeiro_cf_dr_sjc.pdf: 502886 bytes, checksum: a75a349193855697ddf0f761652c4229 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O presente estudo teve por objetivo avaliar o efeito do gel de peróxido de hidrogênio a 20% e 35% na alteração de cor, opacidade e fluorescência de materiais restauradores estéticos. Foram confeccionados 210 espécimes com 3mm de diâmetro e 2mm de espessura, sendo 30 de cada tipo de resina composta (Amaris, Admira, Estelite, Esthet X, Venus, Z350 e GrandioSO). Os espécimes foram armazenados em água deionizada por 24 horas. Na seqüência os mesmos foram polidos com lixa d’água #4000. Realizou-se então a primeira medição de cor, opacidade e fluorescência por um aparelho espectrofotômetro com iluminante padrão D65. Em seguida, cada grupo de 30 corpos de prova foi dividido em três subgrupos (n=10) de acordo com o tratamento clareador; utilizando-se o gel clareador peróxido de hidrogênio a 20% e 35%. Foram feitas quatro aplicações do gel clareador de 30 minutos cada, totalizando duas horas.O grupo controle não recebeu nenhum tipo de tratamento, permanecendo imerso em água deionizada por todo período do experimento. Após a ação dos géis, realizou-se a segunda medição da cor, opacidade e fluorescência. Os dados obtidos foram submetidos à análise estatística pelos testes ANOVA e Tukey ao nível de significância de 5%. Os resultados da ANOVA a dois fatores para o parâmetro ΔE mostram haver diferença estatística significante apenas para o fator concentração (p=0,00). O tratamento com o gel clareador a 35% provocou um resultado com uma média de variação de cor estatisticamente maior com relação aos demais grupos. Quanto à opacidade não houve diferença estatística significativa para nenhum fator. A fluorescência foi influenciada pela concentração do peróxido de hidrogênio (p=0,0016) e pelo tipo de resina (p=0,000), não havendo diferença entre as concentrações de 20% e 35%. A resina que mais sofreu alteração da fluorescência dos materiais... / This study evaluate the effect of 20% and 35% hydrogen peroxide on color, opacity and fluorescence of seven composities resins: Amaris, Admira, Estelite Sigma, Esthet X, Venus, Z350 e GrandioSO. 30 specimes, of each material, were prepared and than they recived bleaching treatment. A control group was stored in water (n=10). Color and spectral distribution of the materials were measured according to the CIELAB color scale, before and after bleaching treatment. The color and the Opacity parameter (OP) of specimens was measured after polymerization on a reflection spectrophotometer under the illuminant D65 over white and black backgrounds. UV component of the illuminant was included and excluded to calculate the fluorescence spectrum (FP). Differences and changes in optical properties (color, opacity parameter and fluorescence parameter) were analyzed using ANOVA and Tukey test, with significance set at p < 0.05. The range of color values (delta E*) was significantly influenced by concentration of hydrogen peroxide (p=0.00). The range of OP values was not influenced by material (p=0.14) or bleaching agent (p=0.38). And the range of FP values was significantly influenced by concentration of hydrogen peroxide (p=0.0016) and also by material (p=0.00). It is demonstrated that opacity of resin composites did not change after 20% and 35% hydrogen peroxide treatment. But color and fluorescence changed significantly after these treatments

Made available in DSpace on 2014-06-11T19:31:27Z (GMT). No. of bitstreams: 0 Previous issue date: 2003-11-10Bitstream added on 2014-06-13T20:41:47Z : No. of bitstreams: 1 mazur_rf_dr_arafo.pdf: 2691655 bytes, checksum: aa6766566238765dc0a1f4d5cb633eda (MD5) / O objetivo deste trabalho foi realizar, in vitro, avaliação da resistência de adesiva pelo teste de microtração de dez sistemas adesivos diferentes. Os sistemas adesivos One Up Bond F - Tokuyama, Clearfil SE Bond - Kuraray, Adper Prompt L-Pop, Single Bond - 3M/ESPE, One Step - Bisco, One Step Plus - Bisco, Prime&Bond NT - Dentsply, Excite - Vivadent, Scotchbond Multi - Uso - 3M/ESPE e All Bond 2 - Bisco. Para a realização do teste foram utilizados quarenta dentes molares hígidos, sendo que destes dentes dez foram utilizados para a microscopia eletrônica de varredura. Para a realização do teste de microtração os dentes foram cortados na superfície oclusal com disco diamantado e posteriormente foram desgastados com discos de lixa. Posteriormente as amostras foram restauradas com os respectivos sistemas adesivos e resina composta Z-100 com tempo de polimerização de 40 segundos cada incremento. Após vinte e quatro horas de armazenagem em temperatura de 37ºC os dentes foram seccionados com disco diamantado com finalidade de obter palitos com área de 1,0 +- 0,2 mm2. Após o corte os palitos foram armazenados em temperatura de 37ºC por vinte e quatro horas e em seguida foram levados para a máquina de ensaio universal EMIC 500 DL onde os palitos foram tracionados com velocidade de 1 mm/min. Os resultados foram analisados pelo através dos testes de normalidade de Lilliefors e de homogeneidade de variância de Bartlett. Quando alguns dos pressupostos não se verificaram, utilizou-se o teste não paramétrico de Kruskal - Wallis. Os resultados obtidos foram em ordem decrescente de 36,73 +- 10,52 para o sistema adesivo One Up Bond F, seguido do sistema de três etapas All Bond 2 com 34,29 +- 12,63 para o sistema adesivo One Step Plus foi de 33,18 +- 11,33 para o sistema Adper Prompt L-Pop de 31,76 +- 11,3, sistema One Step de 29,02 +- 11,28, para o... . / The aim of this study was to analyze the bond strength of ten adhesive systems: One Up Bond F - Tokuyama (OU); Adper Prompt L-Pop - 3M-ESPE (AP); Clearfil SE Bond - Kuraray CO. (SE); Prime Bond NT - Caulk-Dentsply (NT); Single Bond - 3M-ESPE (SB); One Step - Bisco (OS); One Step Plus - Bisco (OP); Excite - Vivadent (EX); Scotchbond Multi - Purpose (SMP) e All Bond 2 - Bisco (AB). Methods: Forty freshly extracted human teeth were transversely wetcut using a diamond disk in order to expose the occlusal dentin surface. Then the adhesive systems were applied according to the manufacturer's instruction. The teeth were restored with composite resin Z-100 (3M) and stored in distilled water at 37ºC for 24 hours. A slow-speed diamond disk was used to prepare microtensile test specimens, with a bonded area of 1,00 +- 0,2 mm2. Each group was composed of thirty sticks, which were stored in distilled water at 37ºC for 24 hours. The sticks were bonded on a universal testing machine at a cross head speed of 1 mm/min. The following results demonstrate values microtensile bond strengths in MPa. Data were statistically analyzed by Kruskal-Wallis Test (p<-0.05). The bond strength values were 36,73 +- 10,52 for One Up Bond F, 34,29 +- 12,63 for All Bond 2, 33,18 +- 11,33 for One Step Plus, 31,76 +- 11,3 for Adper Prompt L-Pop, 29,02 +- 11,28 for One Step, 28,82 +- 14,74 for Single Bond, 28,08 +- 12,09 for Clearfil SE Bond, 26,31 +- 9,02 for Scotchbond Multi - Purpose, 21,35 +- 10,22 for Prime&Bond NT and 19,52 +- 10,08 for Excite. Ten teeth were analysed by SEM and all of them showed resin into the dentin tubules. Most of fractures were adhesive in the composite/teeth interface. One up bond F (OU) resulted in higher bond strength when compared to all the other systems tested and Excite resulted in lower bond strength. Self-etching systems were not statistically... (Complete abstract, click electronic address below).