Submitted by Marco Antônio de Ramos Chagas (mchagas@ufv.br) on 2018-07-12T12:02:47Z No. of bitstreams: 1 texto completo.pdf: 9092047 bytes, checksum: 974ae7db880ee66c1f42778fd4204373 (MD5) / Made available in DSpace on 2018-07-12T12:02:47Z (GMT). No. of bitstreams: 1 texto completo.pdf: 9092047 bytes, checksum: 974ae7db880ee66c1f42778fd4204373 (MD5) Previous issue date: 2018-04-16 / Fundação de Amparo à Pesquisa do Estado de Minas Gerais / O amadurecimento de Ostwald é um processo de crescimento controlado por difusão onde partículas maiores crescem em detrimento da diminuição, e eventualmente do desaparecimento, de partículas menores. Nesse processo ocorre o aumento do raio médio e a diminuição do número total de partículas. A descrição teórica desse fenômeno é dada pela teoria LSW, que descreve o crescimento de partículas em soluções sólidas supersaturadas. Há um grande número de trabalhos teóricos e experimentais sobre o amadurecimento de Ostwald, todavia existe uma carência de trabalhos experimentais com bolhas de gás em escala macroscópica (10-100μm). Com isso, fica evidente a necessidade de realizar um estudo experimental preciso da atuação do amadurecimento de Ostwald em bolhas de gás em líquido. Os resultados foram obtidos a partir do processamento de imagens geradas por videomicroscopia óptica. É apresentado os resultados da evolução temporal do raio médio das bolhas R(t), do número de bolhas N (t), da fração volumétrica ocupado pelas bolhas φ(t) e das distribuições de tamanhos f (R, t) para três frentes de experimento com bolhas de gás em um fluido: fluido em repouso, fluido sob fluxo macroscópico e fluido em repouso com adição de surfactante. Confrontando os resultados com as previsões teóricas verificou-se que o raio médio pode, em algumas condições, se comportar de acordo com a lei de crescimento segundo a teoria LSW (R ∼ t1/3 ), mas que na maioria dos casos a evolução é a mais lenta do que o previsto. O número de bolhas N(t) decai mais devagar do que o previsto pela teoria (N (t) ∼ t-¹). Há uma discussão sobre o sistema estar em um regime transiente, migrando para o regime de validade dos modelos teóricos, e sobre a teoria LSW não ser suficiente para descrever um sistema real de bolhas de gás. Todas as etapas foram realizadas no Laboratório de Microfluídica e Fluidos Complexos, coordenado pelo professor Alvaro Vianna N. C. Teixeira, utilizando-se dos recursos do mesmo e do Departamento de Física da UFV, como programas apropriado para processamento de imagens, microscópio óptico, câmera integrada ao computador, mesa de deslocamento dentre outros. / Ostwald ripening is a diffusion-controlled growth process where larger particles grow at the expense of the shrinking, and eventual disappearance, of smaller particles. In this process the mean radius increases and the total number of particles decreases. The theoretical description of this phenomenon is given by the LSW theory, which describes the growth of particles in supersaturated solid solutions. There is a large number of theoretical and experimental works about the of Ostwald ripening, however there is a lack of experimental works with gas bubbles on a macroscopic scale (10-100μm). Thus, it is evident the need to carry out a precise experimental study of the performance of Ostwald ripening of gas bubbles in liquid. The results were obtained by image processing generated by optical videomicroscopy. It is shown the results of the temporal ̄ evolution of the average bubble radius R(t), the number of bubbles N (t), the volume fraction occupied by the bubbles φ(t) and the size distributions f (R, t) for three types of experiment with gas bubbles in a fluid: resting fluid, fluid under macroscopic flow and resting fluid with addition of surfactant. Comparing the results with the theoretical predictions, it has been found that the average radius can, under some conditions, behave according to the growth law predicted ̄ ∼ t 1/3 ), but that in most cases the evolution is slower than expected. by the LSW theory ( R The number of bubbles N (t) decreases more slowly than predicted by the theory (N (t) ∼ t −1 ). There is a discussion about the system being in a transient regime, migrating to the validity regime of the theoretical models, and about the LSW theory not being enough to describe a real system of gas bubbles. All steps were carried out in the Microfluidics and Complex Fluids Laboratory, led by professor Alvaro Vianna N.C. Teixeira, using either the resources or those of and the Department of Physics at UFV, as appropriate softwares for image processing, optical microscope, integrated camera to computer, displacement table etc.

A classe de óxidos contendo nióbio (Nb) ou tântalo (Ta) e possuindo estrutura AB2O6 (A = Mg, Zn, Ca e B = Nb, Ta) do tipo columbita ou trirutilo, tem sido investigada devido a sua potencialidade para ressonadores na freqüência de microondas (GHz), os quais podem ser usados em sistemas de comunicação móvel e satélite, tais como telefones celulares e sistemas de comunicação pessoal. Preparamos corpos cerâmicos densos pelo método convencional de mistura de óxidos e reação no estado sólido. A rota de processamento e condições ótimas de sinterização foram desenvolvidas para as cerâmicas de MgTa2O6 (MT), ZnTa2O6 (ZT), MgNb2O6 (MN) e ZnNb2O6 (ZN). Temperaturas de sinterização a 1300°C para os niobatos e 1400°C para os tantalatos, para tempos de patamar de 8 horas, promoveram alta densificação atingindo-se densidades relativas maiores que 98% em todos os casos. Na caracterização dielétrica das cerâmicas de ZT e MT, por meio de medidas de impedância nas faixas de freqüência de 24MHz a 1,5GHz, determinamos as constantes dielétricas com valores de ε´=32 para o MT e ε´=36,5 para o ZT; resultados similares aos melhores existentes na literatura. Na fase monocristalina, estes materiais possuem potencialidades para aplicação em geração, transmissão, detecção e conversão de sinais ópticos em uma larga faixa de comprimentos de onda e níveis de potência. Fibras de CaTa2O6 puderam ser eficientemente obtidas pela técnica de Laser Heated Pedestal Growth (LHPG) e a dopagem desses compostos com íons terras raras de Nd3+ e Er3+foi uma alternativa para a obtenção de um material laser ativo. O estudo de fibras dos compostos do tipo ATa2O6 como meio laser ativo, não tem sido devidamente explorado. Resultados de espectroscopia óptica com fibras de CaTa2O6 dopadas com íon de Nd+3revelaram ser um novo material laser ativo para ser bombeado com laser de diodo. / The c1ass of oxides containing the elements niobium or tantalum with AB2O6 (A= Mg e Zn; B= Nb e Ta) structure of the type columbite or trirutilo, has been investigated due to their potentialities for applications in dielectric resonators at microwave frequencies (GHz), which can be used for mobile and satellite communications, as in cell phones and personal communication systems. We have prepared dense ceramic bodies by conventional method of oxides mixture followed by solid state reaction. The experimental route and sintering conditions were developed for the MgTa2O6 (MT), ZnTa2O6 (ZT), MgNb2O6 (MN) and ZnNb2O6 (ZN) ceramics. It was observed that sintering under temperatures of 1300°C for the niobates, and 1400°C for the tantalates, for 8 hours, promoted densities higher than 98% for all ceramic bodies. Impedance spectroscopy was used for the dielectric characterization of MT and ZT ceramics in the frequency range of 24MHz to 1.5GHz and the values of dielectric constant are ε´=32 and ε´ =36.5 respectively. These results are comparable to the best results found in the literature. Moreover, it is also shown that while in the single crystal form, these materials might be used for the generation, transmission, detection, and conversion of optical signals, over a broad range of wavelengths and power levels. Undoped or doped (Nd3+ or Er3+) CaTa2O6 (CT) single crystal fibers were efficiently obtained by the laser−heated pedestal growth (LHPG) technique. The doped samples were characterized from the structural and spectroscopic points of view, aiming to investigate them as potential candidates for compact laser active media, which can be pumped by low cost diode lasers. Although the study of ATa2O6 single crystal fibers for this purpose hasn\'t been much explored yet, the results obtained for CaTa2O6: Nd+3 fibers are very promising.

Utilizando o método de crescimento de cristais por solução aquosa preparamos grandes monocristais de sulfato de triglicina (TGS). Os resultados obtidos na caracterização dos monocristais garantiram uma alta qualidade óptica e estrutural, pré-requisitos básicos para o futuro desenvolvimento de detetores de radiação infravermelha. Também, são apresentados os resultados de responsividade de voltagem, tempo de resposta e resposta espectral de um protótipo de detetor construído com os monocristais. Considerações gerais sobre a teoria de crescimento de cristais são apresentadas juntamente com uma revisão bibliográfica dos principais resultados sobre a dependência da velocidade linear de crescimento com a supersaturação relativa para três direções cristalográficas. Além disso, uma abordagem sobre a velocidade média de crescimento de um dos experimentos é efetuada para exemplificar um dos mecanismos que atuam no crescimento por solução. Devido ao interesse do DFCM (Departamento de Física e Ciência dos Materiais) e de alguns grupos de pesquisa do país foram crescidos outros monocristais, como dihidrogênio fosfato de potássio (KDP) e de TGS dopados. / We prepared large single crystals of triglycine sulphate (TGS) using method of crystal growth from aqueous solution. Results obtained by the characterization of single crystals showed a high optical and structural quality, basic properties for the future development of infrared radiation detectores. Voltage responsivity, time and espectral responses of a detector prototype built with single crystals are presented. General considerations about crystal growth theory are presented with bibliographical review of principal result on dependence of the linear growth rate with relative supersaturation respecting three crystallographical directions. An approach on growth rate is realized with one of the experiments, showing one of the mechanisms acting in the growing from solution. Due to DFCM (Departamento de Física e Ciência dos Materiais) and some research groups in country interests another single crystals were growed, potassium dihydrogen phosphate (KDP) and toped TGS.

Neste trabalho de tese é apresentado um estudo sistemático do crescimento e das propriedades magnéticas e estruturais dos compostos semicondutores magnéticos diluídos (SMD) Zn1-xMnxIn2Se4. Amostras monocristalinas com concentrações de Mn $0leqslant xleqslant 1.00$ foram obtidas pela técnica de transporte químico em fase vapor (CVT). Através de técnicas de difração de raios-X (padrões de pó e diagramas de Laue), estudou-se a evolução da estrutura desde a fase romboédrica do MnIn2Se4, até a fase tetraédrica do ZnIn2Se4. Observou-se a existência de uma fase pura romboédrica para $xgeqslant 0.87$, uma fase pura tetragonal para$xleqslant 0.25$ e uma mistura destas duas fases para x entre 0.67 e 0.35. Espectros de ressonância paramagnética eletrônica (EPR) foram obtidos em temperaturas T desde 4 K até 300 K, para diversas concentrações de Mn. Todos os espectros têm o pico de absorção principal centrado em g=2. A largura pico a pico da linha de ressonância, $deltaHpp$, decresce com o aumento da concentração de manganês e com o aumento da temperatura. Este comportamento está intimamente relacionado com a interação de troca entre os íons magnéticos. A partir de análises da dependência de $deltaHpp$ com a temperatura se extraíram estimativas para a temperatura de Curie-Weiss, $ heta$ e para a temperatura de congelamento Tf das fases de vidro de spin. Medidas da susceptibilidade magnética em modo DC foram realizadas para temperaturas $2Kleqslant Tleqslant 300K$. Dos dados de alta temperatura (T>100 K), resultaram estimativas para o parâmetro $ heta$, bem como para a concentração x de Mn. Os valores de $ heta$ obtidos destas medidas concordam bem com os obtidos de EPR e foram utilizados para estimar as constantes de troca antiferromagnéticas nos dois extremos de concentração da série. Nas amostras com alta concentração de Mn, $xgeqslant 0.67$, irreversibilidades características de uma transição para uma fase de vidro de spin foram observadas em temperaturas abaixo de 4K. Para melhor caracterizar estas transições, medidas da susceptibilidade AC e DC para diversas freqüências e campos magnéticos foram realizadas em temperaturas entre 2 e 20 K. A susceptibilidade DC em baixos campos mostra picos agudos em Tf ~ 2.5, 3.0 e 3.5 K, respectivamente para as amostras com x=0,67; 0,87 e 1,00. Nas três amostras, observa-se irreversibilidade entre medidas com esfriamento na ausência de campo (ZFC) e em presença de campo (FC). Evidência de um verdadeiro fenômeno de transição de fase é fornecida pelo crescimento da susceptibilidade não linear, $chiNL$, próximo de Tf.. Análises de escala estáticas de $chiNL$ e análises de escala dinâmicas desenvolvidas a partir de dados da susceptibilidade AC resultaram em expoentes críticos consistentes com os obtidos em outros vidros de spin com interação de curto alcance. / This work reports a systematic study on the crystal growth and magnetic and structural properties of the diluted magnetic semiconductors (SMD) Zn1-xMnxIn2Se4. Crystals with Mn concentrations $0leqslant xleqslant 1.00$ were grown by chemical vapour transport (CVT). Through x-ray powder diffraction patterns and Laue diagrams of single crystal we studied the transformation from the layered rhombohedral structure of MnIn2Se4 to the tetragonal structure of ZnIn2Se4. We observe the presence of a purely rhombohedral phase for $xgeqslant 0.87$, a purely tetragonal phase for $xleqslant 0.25$ and a two-phase mixture for x between 0.67 and 0.35. Electron Paramagnetic Resonance (EPR) spectroscopy has been performed in the temperature range 4.2 K to 300 K for various concentrations of Mn. All the spectra had the main absorption peak centered at g=2. The resonance peak-to-peak line width, ÄHpp, decreases with increasing concentration of manganese and with increasing temperature. This behavior is intimately related with the exchange interaction between magnetic ions. The analysis of the temperature dependence of ÄHpp resulted in estimates for the Curie-Weiss temperature $ heta$ and for the freezing temperature Tf of the spin glass phase. The DC magnetic susceptibility has been investigated in the range between $2Kleqslant Tleqslant 300K$. The high temperature data (T>100 K) gave estimates for the parameter $ heta$, as well as for the concentration x of Mn. The values of $ heta$ obtained in this way are in good agreement with those obtained from EPR and were used to estimate the antiferromagnetic exchange constants for the two extremes of concentration of the system. For the samples with high concentration of Mn, $xgeqslant 0.67$, irreversibilities characteristic of a spin glass transition have been observed at temperatures below 4K. To better characterize this transition, AC and DC susceptibility measurements for different frequencies and magnetic fields were made in the temperature range between 2 and 20 K. The low field AC susceptibility displayed sharp peaks at Tf ~2.5, 3.0 and 3.5 K for samples with x= 0.67, 0.87 and 1.00, respectively. Irreversibility between zero field cooled (ZFC) and field cooled (FC) DC measurements was observed in the three samples. Evidence of a true phase transition phenomenon is given by the steep increase of the nonlinear susceptibility $chiNL$ when approaching Tf from above. Static scaling analysis of $chiNL$ and dynamic scaling analysis of the AC susceptibility data have been carried out, which yielded critical exponents consistent with those obtained in other spin-glasses with short-range interactions.

O presente trabalho descreve o procedimento experimental do método de purificação do sal de Triiodeto de Bismuto (BiI3), visando uma futura aplicação destes em cristais semicondutores, como detector de radiação à temperatura ambiente. A técnica de Bridgman Vertical Repetido foi aplicada para a purificação e crescimento de BiI3, baseada na teoria da fusão e o fenômeno de nucleação do material. Uma ampola preenchida com sal de BiI3, na quantidade máxima de 25% do seu volume interno, foi posicionada no interior do forno de Bridgman Vertical e verticalmente deslocada à uma velocidade de 2 milímetros por hora dentro do forno programado obedecendo um perfil térmico e gradiente de temperatura, com uma temperatura máxima de 530°C, estabelecidos neste trabalho. A redução de impurezas no BiI3, para cada purificação, foi analisada por Análise por Ativação Neutrônica Instrumental (AANI), para a verificação da eficiência do técnica de purificação estabelecida neste trabalho, para impurezas de metais traço, presente na matéria prima do cristal Foi demonstrado que a técnica de Bridgman Repetido é eficiente para a redução da concentração de diversas impurezas, como Ag, As, Br, Cr, K, Mo, Na, e Sb. As estruturas cristalinas nos cristais purificados duas e três vezes apresentou similaridade com o padrão do BiI3. No entanto, para o sal de partida e cristal purificado somente uma vez foi observado a contribuição de intensidade BiOI (Oxido de Iodeto de Bismuto) similar ao padrão observada no seu difratograma. É conhecido que detectores semicondutores fabricados a partir de cristais com alta pureza exibem uma melhora significativa no seu desempenho, comparado com os cristais produzidos com cristais de baixa pureza. / This study describes the experimental procedure of a BiI3 purification method powder, aiming a future application of these semiconductor crystals as room temperature radiation detector. The Repeated Vertical Bridgman Technique was applied for the purification, based on the melting and nucleation phenomena. An ampoule filled with a maximum of 25% by volume of BiI3 powder was mounted into the Bridgman furnace and vertically moved at a speed of 2 millimeters per hour, inside the furnace with programmed thermal gradient and temperature profile, at a temperature maximum of 530ºC. The reduction of the impurities in the BiI3, each purification, was analysed by Instrumental Neutron Activation Analysis (INAA), in order to evaluate the efficiency of the purification technique established in this work, for trace metal impurities. It was demonstrated that the Repeated Bridgman is effective to reduce the concentration of many impurities in BiI3, such as Ag, As, Br, Cr, K, Mo, Na and Sb. The crystalline structure of the BiI3 crystal purified twice and third times was similar to the BiI3 pattern. However, for BiI3 powder and purified once an intensity contribution of the BiOI was observed in the diffractograms. It is known that semiconductor detectors fabricated from high purity crystal exhibit significant improvement in their performance compared to those produced from low purity crystals.

Neste trabalho estudamos as propriedades ópticas não lineares de aminoácidos utilizando pulsos de laser com duração de femtossegundos. O índice de refração não linear (n2) da L-alanina, L-prolina, L-serina, L-treonina e L-arginina em solução aquosa foram determinados. Foi também estudada a influência do pH na magnitude de n2 dos aminoácidos em solução. Paralelamente, determinamos a dispersão de n2 em cristais de L-treonina nos três eixos principais, x, y e z. Os aminoácidos têm despertado grande interesse devido as suas boas propriedades ópticas de segunda ordem. Todavia, suas propriedades ópticas de terceira ordem ainda não haviam sido estabelecidas. Além disso, implementamos a técnica de espalhamento hiper-Rayleigh para determinar a primeira hiperpolarizabilidade (P) de moléculas orgânicas, onde uma mudança foi introduzida para permitir medidas mais rápidas e com melhor precisão. Foram encontrados os valores de P de algumas porfirinas e corantes orgânicos. / In this work we have studied nonlinear optical properties of amino acids using femtosecond laser pulses. The nonlinear index of refraction (nz) of L-alanine, L-proline, L-serine, L-threonine and L-arginine in aqueous solution have been determined. Also, the influence of pH in the magnitude of nz of amino acids in solution has been studied. Besides, we have determined the n;, dispersion in the three main axis, x, y and z, in L-threonine crystals. The amino acids have attracted a great deal of attention due to their good second-order optical properties. However, their third-order optical properties had not been established yet. Furthermore, we have implemented the hyper-Rayleigh scattering technique to determine the first hyperpolarizability (P) of organic molecules, leading to fast and more precise measurements. It was found the P value of some porphyrins and organic dyes.

Neste trabalho descreve-se o estudo do estabelecimento de uma técnica para o crescimento e preparo de cristais de HgI2, com o intuito de utilizá-los como detectores semicondutores de radiação que operam a temperatura ambiente. Três métodos de crescimento de cristais foram estudados no desenvolvimento deste trabalho: (1) Transporte Físico de Vapor (Physical Vapor Transport PVT), (2) Solução Saturada de HgI2 empregando dois solventes distintos; Dimetil Sulfóxido (DMSO) (a) e acetona (b) e (3) método de Bridgman. A fim de avaliar os cristais de HgI2 desenvolvidos pelos três métodos, medidas sistemáticas foram realizadas para determinar a estrutura, o plano de orientação, a estequiometria, a morfologia da superfície e as impurezas do cristal. A influência destas propriedades físico-químicas sobre os cristais desenvolvidos foi avaliada em termos de desempenho como detector de radiação. Os difratogramas indicaram que os cristais estão orientados preferencialmente planos (001) e (101) com estrutura tetragonal para todos os cristais desenvolvidos. No entanto, a morfologia com menor nível de deformação foi observada para o cristal obtido pela técnica de PVT. Uma uniformidade na camada de superfície do cristal de PVT foi observada, enquanto na superfície do cristal de DMSO podem ser nitidamente encontradas incrustações de elementos distintos ao cristal. A melhor resposta de radiação foi encontrada para os cristais crescidos pela PVT. Significativa melhora no desempenho do detector de radiação de HgI2 foi encontrada, purificando o cristal por meio de dois crescimentos sucessivos, pela técnica de PVT. / In this work, the establishment of a technique for HgI growth and preparation of crystals, for use as room temperature radiation semiconductor detectors is described. Three methods of crystal growth were studied while developing this work: (1) Physical Vapor Transport (PVT); (2) Saturated Solution of HgI2, using two different solvents; (a) dimethyl sulfoxide (DMSO) and (b) acetone, and (3) the Bridgman method. In order to evaluate the obtained crystals by the three methods, systematic measurements were carried out for determining the stoichiometry, structure, orientation, surface morphology and impurity of the crystal. The influence of these physical chemical properties on the crystals development was studied, evaluating their performance as radiation detectors. The X-ray diffractograms indicated that the crystals were, preferentially, oriented in the (001) e (101) directions with tetragonal structure for all crystals. Nevertheless, morphology with a smaller deformation level was observed for the crystal obtained by the PVT technique, comparing to other methods. Uniformity on the surface layer of the PVT crystal was detected, while clear incrustations of elements distinct from the crystal could be viewed on the DMSO crystal surface. The best results as to radiation response were found for the crystal grown by physical vapor transport. Significant improvement in the HgIz2 radiation detector performance was achieved for purer crystals, growing the crystal twice by PVT technique.

Neste trabalho nós crescemos e caracterizamos oticamente cristais de L-treonina e L-lisina-HCl. Esses materiais pertencem a uma família de cristais orgânicos que tem demonstrado potencial para uso como dispositivos ópticos não lineares. Os cristais foram crescidos em solução aquosa pelos métodos de evaporação lenta do solvente e abaixamento controlado da temperatura. Realizamos medidas de óptica linear, índices de refração e a absorção óptica, e de óptica não linear, a geração de segundo harmônico (GSH). Essa nova classe de materiais não linear é de fácil crescimento e apresentam uma boa qualidade óptica e propriedades não lineares comparáveis as dos cristais de KDP. / In this work we grew and optically characterized L-threonine and L-lysine-HCL crystals. These materials belong to a family of organic crystals that have a potential application in nonlinear optical devices. The crystals were grown in aqueous solution by slow solvent evaporation and controlled cooling techniques. We characterized the linear and nonlinear optical properties of these materials, for exarnple, the index of refi-action, optical absorption and second harmonic generation (SHG). This new class of nonlinear medium is easy to grow and present good optical quality and nonlinear properties comparable to KDP crystals.

Este trabalho teve como objetivo estudar detalhadamente as propriedades do vapor gerado pela ablação de um alvo sólido de tungstênio por um laser de Cu-HBr, tais como: densidade de átomos, neutros ou ionizados, e a distribuição de velocidades destas mesmas espécies, e obter informações sobre mecanismos de redução das cargas elétricas, de gotículas e de aglomerados no vapor com o objetivo de se obter um jato de vapor monoatômico e neutro, para aplicação de crescimento de filmes finos e espectroscopia de fotoionização. Foram desenvolvidas e testadas três técnicas de monitoramento da pluma de vapor: sensores de PVDF, sondas de Langmuir e ion-gauge. Destas, as duas primeiras se mostraram simples e eficazes para a determinação da distribuição de velocidade de jatos monoatômicos, com a obtenção de parâmetros como temperatura translacional e velocidade de deriva da pluma.

Nesse trabalho é reportado o crescimento de filmes finos de dióxido de titânio (TiO2) por duas técnicas assistidas a plasma chamadas magnetron sputtering convencional (MSC) e magnetron sputtering catodo oco (MSCO). O dióxido de titânio foi crescido sobre substratos de silício, variando alguns parâmetros de plasma como, por exemplo, a distância axial (z0) e a concentração de oxigênio na mistura Ar+O2. As amostras foram caracterizadas por perfilometria, microscopia de força atômica (MFA) e difração de raios-X (DRX). Não obstante, foi realizado diagnóstico das descargas através de métodos como características elétricas corrente-tensão (I×V), sonda simples de Langmuir e espectroscopia de emissão ótica (EEO). Os resultados dessas técnicas foram comparados com os parâmetros provenientes da caracterização dos filmes depositados, de modo a conhecer a interação plasma-superfície. Como uma forma de complementação das análises, foi realizada a comparação de parâmetros como razão de deposição (Rd) com o parâmetro geométrico PCI (probabilidade de coleção de íons). Os resultados mostraram que todos os filmes produzidos são cristalinos, cujas estruturas são altamente dependentes do sistema de deposição, i.e., da energia e da reatividade da descarga.