An improved knowledge of wood material behavior in hot-pressing environments can provide the benefit of an increased understanding of material properties during the manufacture of wood-based composites as well as insight into the development of new processes and products which manipulate the viscoelastic nature of wood. Two specific areas where additional knowledge is needed are: the high temperature equilibrium moisture content (EMC) behavior and the moisture dependent softening behavior. EMC data was collected and desorption isotherms were generated for mature and juvenile wood of aspen, loblolly pine and yellow-poplar at 50 and 160°C. High temperature EMC behavior was found to be distinct from that at lower temperatures, and considerable differences between the isotherms for juvenile and mature wood were detected. Substantial thermal degradation was observed during desorption at 160 °C and found to be strongly influenced by relative humidity. The thermal softening behavior of wood was evaluated using dielectric thermal analysis (DETA) at moisture levels from 0 to 20 percent. Coincident in situ relaxations of hemicellulose and amorphous cellulose in the range of 20 to 200 °C were observed and found to exhibit the characteristics of a secondary (glass) transition. The moisture dependence of this transition was characterized, and differences in the observed Tg were detected between juvenile and mature wood. Time-temperature superposition was also shown to be applicable to the wood-water system. / Ph. D.

Percent Moisture Content (MC %) of wood is defined to be the weight of the moisture in the wood divided by the weight of the dry wood times 100%. Equilibrium Moisture Content (EMC), moisture content at environmental equilibrium is a very important metric affecting the performance of wood in many applications. For best performance in many applications, the goal is to maintain this value between 6% and 8%. EMC value is a function of the temperature and the relative humidity of the surrounding air of wood. It is very important to maintain this value while processing, storing or finishing the wood. This thesis develops a special purpose sensor and processor system to be implemented as a small hand-held device used to sense, calculate and display the value of EMC of wood depending on surrounding environmental conditions. Wood processing industry personnel would use the hand-held EMC calculating and display device to prevent many potential problems that can show significant affect on the performance of wood. The design of the EMC device requires the use of sensors to obtain the required inputs of temperature and relative humidity. In this thesis various market available sensors are compared and appropriate sensor is chosen for the design. The calculation of EMC requires many arithmetic operations with stringent precision requirements. Various arithmetic algorithms and systems are compared in terms of meeting required arithmetic functionality, precision requirements, and silicon implementation area and gate count, and a suitable choice is made. The resulting processor organization and design is coded in VHDL using the Xilinx ISE 6.2.03i tool set. The design is synthesized, validated via VHDL virtual prototype simulation, and implemented to a Xilinx Spartan2E FPGA for experimental hardware prototype testing and evaluation. It is tested over various ranges of temperature and relative humidity. Comparison of experimentally calculated EMC values with the theoretical values of EMC derived for corresponding temperature and relative humidity points resulted in validation of the EMC processor architecture, functional performance and arithmetic precision requirements.

Além da secagem convencional, a aplicação de tratamentos térmicos a altas temperaturas é um dos processos mais empregados para potencializar a estabilidade da madeira, porém necessitam de estrutura e equipamentos próprios. Diante disto, a proposta desta pesquisa fundamenta-se no estudo da aplicação de tratamentos estabilizadores para redução da higroscopicidade do material madeira, mediante temperaturas mais brandas (abaixo de 150°C) e que permitam a aplicação prática em equipamentos de secagem utilizados na indústria nacional. O objetivo geral deste trabalho foi avaliar os efeitos dos tratamentos estabilizadores nas propriedades físicas e componentes químicos da madeira para sua viabilização prática. O trabalho consistiu em duas etapas, na primeira: foram utilizadas três espécies de folhosas: Cedrinho (Erisma uncinatum), Tachi preto (Tachigali myrmecophyla) e Itaúba amarela (Mezilaurus itauba), foi realizada a caracterização anatômica das espécies utilizando Microscopia Ótica e Microscopia Eletrônica de Varredura (MEV), e análise da composição química e propriedades físicas. As amostras destinadas aos tratamentos estabilizadores, inicialmente, foram secas em estufa convencional e em seguida passaram pelos tratamentos estabilizadores em autoclave a 90°C (24 e 96h) e 120°C (2h e 8h). Em seguida, foram realizados os condicionamentos higroscópicos (adsorção e dessorção) nas umidades relativas de 30, 60 e 90% para avaliação do potencial higroscópico e das variações dimensionais. Na segunda etapa, a partir dos resultados obtidos na primeira etapa, foi possível aplicar o tratamento propriamente dito, o piloto em escala industrial, utilizando uma estufa de secagem convencional (90°C por 24 horas); e em escala laboratorial (90°C por 24 e 96 horas), em uma câmara de climatização simulando um secador convencional. Para o tratamento piloto, foi levado em consideração a disponibilidade de matéria prima da empresa e tendo como foco o trabalho concomitante entre laboratório e aplicação industrial, a espécie utilizada foi o Cumarú (Dipterix sp), uma vez que essa espécie é considerada pela indústria como uma das mais problemáticas e, portanto, uma das espécies prioritárias para receber um tratamento que contribua para reduzir a variação dimensional após secagem. Os principais resultados permitiram observar que os tratamentos estabilizadores na forma em que foram aplicados na presente pesquisa, não causaram alterações na composição química na madeira das espécies e quando realizados em ambiente com alta umidade relativa, não apresentam redução significativa da higroscopicidade e da variação dimensional na maioria dos condicionamentos. Com aplicação do tratamento piloto foi possível observar que com o controle da umidade relativa do ar, tanto no início quanto no final do processo, é possível reduzir o potencial higroscópico da madeira mediante aplicação de tratamentos estabilizadores. / Besides conventional drying, the application of heat treatment at high temperatures is one of the processes employed to improve the stability of wood, however they require its own structure and equipment. Therefore, the purpose of this research is based on the application of the stabilizers treatments studies of wood material hygroscopicity reduction, using low temperatures (below 150°C) and that allows practical application in drying equipment used in the domestic industry. The aim of this study was to evaluate the effects of stabilizing treatments on the physical properties and chemical components of wood for its practical feasibility. The research was comprised for two steps, the first: a total of three species of hardwoods had been used: Cedrinho (Erisma uncinatum), Tachi preto (Tachigali myrmecophyla) e Itaúba amarela (Mezilaurus itauba). The characterization of this three species was made by anatomical description, using Optical Microscope and Scanning Electron Microscopy (SEM), the chemical composition analysis and the physical properties. Samples of the stabilizing treatment, initially, were dried in a conventional kiln dryer and then the stabilizing treatment was applied in an autoclave at 90°C (24 e 96h) e 120°C (2h e 8h). Next, the hygroscopic conditioning were conducted (adsorption and desorption) in relative humidity (RH) of 30, 60 and 90% for evaluation of hygroscopic potential and dimensional changes. In the second stage, from the results obtained in the first step, it was possible to apply the treatment itself, the industrial scale pilot, using a conventional kiln dryer (90°C for 24 hours); and laboratory scale (90°C for 24 and 96 hours) in a climate chamber simulating a conventional dryer. For the pilot treatment, the availability of raw materials in the company was taken into account and focusing on the concurrent work between laboratory and industrial application, the selected specie was Cumarú (Dipterix sp), considered by the industry as one of the most problematic and, therefore a priority species to receive a treatment that can help to reduce the dimensional change after drying. The main results allowed to observe that the stabilizing treatments in the way that were applied in this study, did not cause changes in the chemical composition and when performed in an environment with high relative humidity, show no significant reduction of hygroscopicity and dimensional variation in most of conditionings. From the implementation of pilot treatment was observed that adopting the control of relative humidity, both in the beginning and the end of the process, is possible to reduce hygroscopic potential of wood by applying stabilizers treatments.

Made available in DSpace on 2016-12-23T14:37:35Z (GMT). No. of bitstreams: 1 lucelio lovatti.pdf: 1248502 bytes, checksum: c196251467613db326908ba81532337a (MD5) Previous issue date: 2008-03-26 / This research had as general objective to obtain information regarding commercialization and physical properties of the sawn wood marketed in the South area of the Esp?rito Santo State. Seventeen wood deposits were visited and collected samples, as well as applied a questionnaire for obtaining of the information. Through the anatomy of the log forty species being marketed as sawn coming mainly of the Amazonia area were identified. Regarding the collected general information, it can highlight, there are no one use of technical specifications established by entities of normalization, so much for the dimensioning of the pieces as for the quality in relation to defects and problems with the drying of the wood, which are commonly marketed green. The behavior hygroscopic in several conditions of relative humidity of the air and the relationships between retratibility and the moisture content of the wood for the main species was studied. The wood used in the study concerning of the behavior hygroscopic and of the retratibility are deriving from the trade of the area and also of the Laborat?rio de Ci?ncias da Madeira (LCM) of the Departamento de Engenharia Florestal of the Univercidade Federal do Esp?rito Santo. For the sorption curves it was observed that each species possesses own a characteristic that means a differentiated behavior among the wood in the several conditions of relative humidity of the air. In relation to the retratibility with the variation in the moisture content of the samples the shrinkages volumetric, radial and tangential not vary exponentially with the loss of water by wood. / A presente pesquisa teve como objetivo geral obter informa??es referentes ? comercializa??o e propriedades f?sicas das madeiras serradas comercializadas na regi?o Sul do Estado do Esp?rito Santo. Foram visitadas dezessete madeireiras e coletadas amostras, bem como aplicado um question?rio para obten??o das informa??es. Atrav?s da anatomia do lenho, foram identificadas quarenta esp?cies sendo comercializadas na forma serrada, provenientes principalmente da regi?o Amaz?nica. Referente ?s informa??es gerais coletadas, se pode destacar, o n?o uso de especifica??es t?cnicas estabelecidas por entidades normalizadoras, tanto para o dimensionamento das pe?as quanto para a qualidade em rela??o a defeitos e problemas com a secagem das madeiras, as quais s?o comumente comercializadas verdes. Para as principais esp?cies, estudou-se o comportamento higrosc?pico em diversas condi??es de umidade relativa do ar e as rela??es entre retratibilidade e o teor de umidade da madeira. As madeiras utilizadas no estudo acerca do comportamento higrosc?pico e da retratibilidade s?o provenientes do com?rcio da regi?o e tamb?m do Laborat?rio de Ci?ncia da Madeira (LCM) do Departamento de Engenharia Florestal da Universidade Federal do Esp?rito Santo. Para as curvas de sor??o, observou-se que cada esp?cie possui caracter?sticas pr?prias, o que significa um comportamento diferenciado entre as madeiras nas diversas condi??es de umidade relativa do ar. Em rela??o ? retratibilidade com a varia??o no teor de umidade das amostras, observou-se que as contra??es volum?trica, radial e tangencial, n?o variam exponencialmente com a perda de ?gua pela madeira.

Além da secagem convencional, a aplicação de tratamentos térmicos a altas temperaturas é um dos processos mais empregados para potencializar a estabilidade da madeira, porém necessitam de estrutura e equipamentos próprios. Diante disto, a proposta desta pesquisa fundamenta-se no estudo da aplicação de tratamentos estabilizadores para redução da higroscopicidade do material madeira, mediante temperaturas mais brandas (abaixo de 150°C) e que permitam a aplicação prática em equipamentos de secagem utilizados na indústria nacional. O objetivo geral deste trabalho foi avaliar os efeitos dos tratamentos estabilizadores nas propriedades físicas e componentes químicos da madeira para sua viabilização prática. O trabalho consistiu em duas etapas, na primeira: foram utilizadas três espécies de folhosas: Cedrinho (Erisma uncinatum), Tachi preto (Tachigali myrmecophyla) e Itaúba amarela (Mezilaurus itauba), foi realizada a caracterização anatômica das espécies utilizando Microscopia Ótica e Microscopia Eletrônica de Varredura (MEV), e análise da composição química e propriedades físicas. As amostras destinadas aos tratamentos estabilizadores, inicialmente, foram secas em estufa convencional e em seguida passaram pelos tratamentos estabilizadores em autoclave a 90°C (24 e 96h) e 120°C (2h e 8h). Em seguida, foram realizados os condicionamentos higroscópicos (adsorção e dessorção) nas umidades relativas de 30, 60 e 90% para avaliação do potencial higroscópico e das variações dimensionais. Na segunda etapa, a partir dos resultados obtidos na primeira etapa, foi possível aplicar o tratamento propriamente dito, o piloto em escala industrial, utilizando uma estufa de secagem convencional (90°C por 24 horas); e em escala laboratorial (90°C por 24 e 96 horas), em uma câmara de climatização simulando um secador convencional. Para o tratamento piloto, foi levado em consideração a disponibilidade de matéria prima da empresa e tendo como foco o trabalho concomitante entre laboratório e aplicação industrial, a espécie utilizada foi o Cumarú (Dipterix sp), uma vez que essa espécie é considerada pela indústria como uma das mais problemáticas e, portanto, uma das espécies prioritárias para receber um tratamento que contribua para reduzir a variação dimensional após secagem. Os principais resultados permitiram observar que os tratamentos estabilizadores na forma em que foram aplicados na presente pesquisa, não causaram alterações na composição química na madeira das espécies e quando realizados em ambiente com alta umidade relativa, não apresentam redução significativa da higroscopicidade e da variação dimensional na maioria dos condicionamentos. Com aplicação do tratamento piloto foi possível observar que com o controle da umidade relativa do ar, tanto no início quanto no final do processo, é possível reduzir o potencial higroscópico da madeira mediante aplicação de tratamentos estabilizadores. / Besides conventional drying, the application of heat treatment at high temperatures is one of the processes employed to improve the stability of wood, however they require its own structure and equipment. Therefore, the purpose of this research is based on the application of the stabilizers treatments studies of wood material hygroscopicity reduction, using low temperatures (below 150°C) and that allows practical application in drying equipment used in the domestic industry. The aim of this study was to evaluate the effects of stabilizing treatments on the physical properties and chemical components of wood for its practical feasibility. The research was comprised for two steps, the first: a total of three species of hardwoods had been used: Cedrinho (Erisma uncinatum), Tachi preto (Tachigali myrmecophyla) e Itaúba amarela (Mezilaurus itauba). The characterization of this three species was made by anatomical description, using Optical Microscope and Scanning Electron Microscopy (SEM), the chemical composition analysis and the physical properties. Samples of the stabilizing treatment, initially, were dried in a conventional kiln dryer and then the stabilizing treatment was applied in an autoclave at 90°C (24 e 96h) e 120°C (2h e 8h). Next, the hygroscopic conditioning were conducted (adsorption and desorption) in relative humidity (RH) of 30, 60 and 90% for evaluation of hygroscopic potential and dimensional changes. In the second stage, from the results obtained in the first step, it was possible to apply the treatment itself, the industrial scale pilot, using a conventional kiln dryer (90°C for 24 hours); and laboratory scale (90°C for 24 and 96 hours) in a climate chamber simulating a conventional dryer. For the pilot treatment, the availability of raw materials in the company was taken into account and focusing on the concurrent work between laboratory and industrial application, the selected specie was Cumarú (Dipterix sp), considered by the industry as one of the most problematic and, therefore a priority species to receive a treatment that can help to reduce the dimensional change after drying. The main results allowed to observe that the stabilizing treatments in the way that were applied in this study, did not cause changes in the chemical composition and when performed in an environment with high relative humidity, show no significant reduction of hygroscopicity and dimensional variation in most of conditionings. From the implementation of pilot treatment was observed that adopting the control of relative humidity, both in the beginning and the end of the process, is possible to reduce hygroscopic potential of wood by applying stabilizers treatments.

Orientador: Sylvio Luis Honorio / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Agricola / Made available in DSpace on 2018-08-08T08:41:42Z (GMT). No. of bitstreams: 1 Portugal_EdilbertoPrinci_D.pdf: 3108115 bytes, checksum: 834974ae808b2dc8cae3ca812f9976ba (MD5) Previous issue date: 2006 / Resumo: A Stevia rebaudiana, um arbusto que tem na produção de esteviosídeos seu principal produto de interesse, foi objeto deste trabalho. Considerando sua cadeia produtiva, existem lacunas que necessitam pesquisas, tanto no aspecto agronômico, como o emprego de espécies fúngicas micorrízicas, quanto procedimentos pós-colheita, dos quais a secagem é um dos fatores. O presente trabalho teve como objetivos, identificar uma espécie de fungo micorrízico arbuscular eficiente e sua relação com o desenvolvimento e concentração de esteviosídeos em plantas de estévia, cultivadas em campo, hidroponia e aeroponia, selecionar substrato adequado para o desenvolvimento da colonização micorrízica, avaliar sistemas de secagem no teor de esteviosídeos e determinar as isotermas de sorção da estévia. Para seleção de fungo micorrízico foram testadas sete espécies, sendo cinco de um banco de culturas e duas isoladas da própria cultura da estévia. O ensaio foi conduzido em casa de vegetação em vasos com solo esterilizado e cinco repetições. Foram determinados a massa seca total da parte aérea e de folhas, teor e quantidade acumulada de esteviosídeos nas folhas e colonização micorrízica. Para seleção de substratos, foram testados nove produtos comerciais, utilizando-se como planta indicadora uma gramínea (Brachiaria humidicola) e como parâmetro avaliado a taxa de colonização fúngica no sistema radicular. Plantas de estévia inoculadas ou não com o fungo micorrízico Glomus intraradices foram cultivadas em três sistemas distintos, campo, aeroponia e hidroponia. Foram realizadas três colheitas em épocas distintas e determinada a massa da matéria seca total da parte aérea e de folhas, teor e acúmulo de esteviosídeos nas folhas e colonização micorrízica. Foram testados três processos de secagem, ao sol, secador a gás e estufa elétrica com circulação forçada de ar, à temperatura de 45oC. Os processos foram avaliados em função do teor de esteviosídeos nas folhas. A determinação da umidade de equilíbrio nas folhas de estévia foi realizada nas temperaturas de 30 e 45oC e, as isotermas de sorção foram tratadas com os modelos matemáticos de BET, BET linear, Peleg, GAB, Halsey, Langmuir, Oswin, Henderson e Chung e Pfost. A espécie Glomus intraradices foi a mais eficiente para o desenvolvimento da estévia e acumulação de esteviosídeos. O substrato Rendmax Citrus sem adubação propiciou as melhores condições para a colonização micorrízica nas raízes da gramínea. Dentre os sistemas de cultivo estudados a hidroponia mostrou-se o menos eficiente para o cultivo de estévia. Em aeroponia obteve-se maior produtividade em termos de matéria seca da parte aérea, enquanto no campo maior quantidade acumulada de esteviosídeos. Não se observou diferença entre a secagem na estufa e no secador para qualquer das épocas de colheita. O teor de esteviosídeos nas folhas de plantas secadas ao sol foi sempre inferior, com perda de até 20% em relação aos outros dois sistemas. Os modelos que apresentaram melhor ajuste, nas temperaturas de 30 e 45oC, foram GAB e HALSEY. O modelo BET LINEAR também mostrou bom ajuste, mas somente para a temperatura de 45oC / Abstract: Stevia rebaudiana, a shrub mostly interesting for its production of steviosides, was the object of this work. In regard to its productive chain, further researches must be done, not only in agronomical aspects, but also in the utilization of mycorrhizal fungal species, as well as in the post-harvest processes, namely the drying one. The present work aimed at the identification of an efficient arbuscular mycorrhizal fungal species and its influence in the development and concentration of steviosides in stevia plants grown in hydroponic and aeroponic systems; to select an adequate substrate for the development of mycorrhizal fungi; to evaluate drying systems in steviosides rates and to determine stevia?s isotherms of sorption. For the mycorrhizal fungi selection seven species were tested, five from a germplasm bank and two were isolated from their own stevia culture. Five assays in pots with sterilized soil were carried out in a greenhouse. The total dry mass of the aerial parts and of the leaves, the rate and accumulated quantity of steviosides in the leaves as well as the mycorrhizal colonization were determined. Nine commercial substrates were tested for the rate of colonization of the root system of an indicating gramineous plant (Brachiaria humidicola). Stevia plants that were inoculated (or not) with the mycorrhizal fungus Glomus intraradices were cultivated in three different growing systems, field, aeroponic and hydroponic. Three harvests were carried out in different periods and the total dry mass of the branch and leaves sections, contents and accumulated steviosides in the leaves and mycorrhizal colonization were determined. Three processes for drying leaves were tested: by sunlight, gas dryer and electrical stove with forced air circulation, at 45oC. The processes were evaluated in relation to the steviosides rate of the leaves. The equilibrium moisture content for stevia leaves was done at 30oC and 45oC, while the isotherms of sorption were tested for the best fit by mathematical models of BET, BET linear, Peleg, Gab, Halsey, Langmuir, Oswin, Henderson and Chung and Pfost. The Glomus intraradices species was the most efficient for the stevia development and accumulation of steviosides. The Rendmax Citrus substrate without manure rendered the best conditions for the mycorrhizal colonization in the gramineous roots. Among the growing systems studied, hydroponics turned out to be the least efficient for stevia cultivation. Aeroponics brought the highest production in terms of dry mass from the aerial parts, while in the field a larger accumulated quantity of steviosides was obtained. No difference was observed between the stove and gas drying processes at any of the harvesting periods. The steviosides rate from the leaves dried by sunlight was always inferior, coming to a loss of 20% in relation to the others. The best fit models were GAB and HALSEY. The BET LINEAR fitted by 45ºC / Doutorado / Tecnologia Pós-Colheita / Doutor em Engenharia Agrícola

No description available.

Submitted by LILIAN FACHIN LEONARDO BETIOL null (lilianfacleo@hotmail.com) on 2016-12-04T18:12:23Z No. of bitstreams: 1 Tese - Formatada (1) Corrigida.pdf: 1975637 bytes, checksum: a2ca74a2f726452b217e860e0c11c866 (MD5) / Approved for entry into archive by Felipe Augusto Arakaki (arakaki@reitoria.unesp.br) on 2016-12-06T13:52:01Z (GMT) No. of bitstreams: 1 betiol_lfl_me_sjrp.pdf: 1975637 bytes, checksum: a2ca74a2f726452b217e860e0c11c866 (MD5) / Made available in DSpace on 2016-12-06T13:52:01Z (GMT). No. of bitstreams: 1 betiol_lfl_me_sjrp.pdf: 1975637 bytes, checksum: a2ca74a2f726452b217e860e0c11c866 (MD5) Previous issue date: 2016-11-21 / As isotermas de sorção tornaram-se importantes para prever o comportamento da cinética de secagem e as condições de armazenamento de resíduos da indústria alimentícia. O conhecimento de tal propriedade é útil para projetar equipamentos ou operações para fins de armazenamento ou processamento. O bagaço quando é apenas descartado, representa um desperdício de matéria prima, de compostos orgânicos com categoria bioquímica definida (proteínas, açúcares, ceras, graxas, resinas), que poderia ser aproveitada. Dentro deste contexto, a presente pesquisa teve como objetivo caracterizar quimicamente o bagaço de mandioca e fazer a determinação experimental das isotermas de sorção destes resíduos da indústria de fécula, além de calcular a entalpia e entropia, temperatura media harmônica e calor isostérico de adsorção. Para isso, o teor de umidade de equilíbrio nas isotermas de sorção, de bagaço de mandioca, foi determinado utilizando o método gravimétrico estático nas temperaturas de 20 a 80 °C. Modelos teóricos e empíricos foram usados para representar os valores experimentais das isotermas de sorção, sendo que o modelo de GAB foi o que apresentou os melhores ajustes. Utilizando o modelo de GAB foi possível determinar o calor isostérico de adsorção como função do teor de umidade. A teoria da compensação foi confirmada pela relação linear entre entalpia e entropia. Maiores valores de temperatura isocinética do que a temperatura harmônica reforçam a teoria da compensação e sugeriram que a adsorção de água pelo bagaço de mandioca é considerado um processo conduzido pela entalpia. / The sorption isotherms become important to predict the drying kinetics behavior and waste storage conditions of the food industry. The knowledge of such property is useful for designing equipment or operations for storage or processing. The bagasse is only when discarded, is a waste of raw materials, organic compounds with defined biochemical category (proteins, sugars, waxes, greases, resins), which could be harnessed. Within this context, this study aimed to chemically characterize the Cassava Bagasse and make the experimental determination of the sorption isotherms of these starch industry waste and calculates the enthalpy and entropy, harmonic average temperature and isosteric heat of adsorption. For this, the equilibrium moisture content in the sorption isotherms of cassava bagasse was determined using the gravimetric static method in temperatures 20-80 ° C. Theoretical and empirical models were used to represent the experimental values of sorption isotherms, and the GAB model was the one that presented the best fit. Using the GAB model was possible to determine the isosteric heat of adsorption and moisture content of the function. The theory of compensation was confirmed by the linear relationship between enthalpy and entropy. Isokinetic higher temperature values than the harmonic temperature reinforce the theory of compensation and suggested that the adsorption of water by mancioca bagasse and considered one of enthalpy driven process.

This thesis deals with massive wooden buildings especially with regard to the current approach to their design, assessment and approval. In this thesis are shown future possibilities of development of traditional wooden buildings with regard to current thermal technical requirements. Theoretical considerations are then compared with measurements which were performed on massive wooden wall samples.

This paper deals with the determination of the capillary pore-size distribution (CPSD) and equilibrium moisture content (EMC) of untreated and thermally modified (TM) Norway spruce [Picea abies (L.) Karst.] by means of the pressure plate technique (PPT). Desorption experiments were conducted at very high values of relative humidity (RH) in the range between 99.2% and 100%. The thermal modification of spruce results in an alteration of the CPSD, owing to the formation of intercellular cracks in the middle lamella, as a result of cell-wall compression. The desorption curves for both untreated and TM spruce show an extremely upward bend at 99.97% RH. This step reflects an EMC of 38.1% for untreated spruce and 33.8% for TM spruce. None of the samples shrunk during the PPT measurements. Following desorption experiments at 97.4% RH, all samples shrunk. This step reflects an EMC of 27.9% for untreated spruce and 21.7% for TM spruce.