Spelling suggestions: "subject:"isoladamente""
11 |
Determinação do Grau de Polimerização Em Papel Isolante Através da Espectroscopia No Infravermelho Próximo e Calibração MultivariadaSANTOS, Edmilson Oliveira dos 23 April 2012 (has links)
Submitted by Eduarda Figueiredo (eduarda.ffigueiredo@ufpe.br) on 2015-03-10T19:13:46Z
No. of bitstreams: 2
license_rdf: 1232 bytes, checksum: 66e71c371cc565284e70f40736c94386 (MD5)
Dissertacao_Correcoes_Banca_ok.pdf: 2816599 bytes, checksum: c4a961acbc8da039ba84e8bd7534bd87 (MD5) / Made available in DSpace on 2015-03-10T19:13:46Z (GMT). No. of bitstreams: 2
license_rdf: 1232 bytes, checksum: 66e71c371cc565284e70f40736c94386 (MD5)
Dissertacao_Correcoes_Banca_ok.pdf: 2816599 bytes, checksum: c4a961acbc8da039ba84e8bd7534bd87 (MD5)
Previous issue date: 2012-04-23 / CAPES / Transformadores de potência são equipamentos importantes na rede elétrica,
tanto para a distribuição quanto para o uso. O principal sistema isolante em
transformadores elétricos consiste de um papel (isolante sólido) impregnado com
óleo mineral. O envelhecimento e a degradação do isolante sólido determina a vida
útil do transformador. À medida que o papel isolante perde as suas propriedades
mecânicas, torna-se vulnerável à ruptura quando o equipamento é submetido à
esforços devido a curtos-circuitos. O papel isolante é composto por longas fibras de
celulose. O comprimento médio das moléculas de celulose pode ser estimado por
seu grau de polimerização (GP), que determina o número médio de unidades de
glicose para cada cadeia de celulose. No Brasil, a determinação do GP é realizada
de acordo com a Norma ABNT NBR 8148 (equivalente à ASTM D 4243), a qual
envolve um procedimento demorado, destrutivo, e exige uma grande quantidade de
amostra necessária para realizar ensaios repetitivos e atingir resultados confiáveis.
Um método alternativo e simples para determinar o grau de polimerização (GP) de
papéis isolantes de transformadores elétricos, utilizando espectroscopia no
infravermelho próximo (NIR), foi desenvolvido para reduzir os custos e o tempo de
análise do método convencional. Setenta e cinco amostras de papel tipos kraft,
crepe e papelão, em diferentes estágios de degradação (GP variando entre 200 e
900 unidades) foram coletados em transformadores durante um período de três
anos. O conjunto de amostras foi analisado de acordo com o método convencional e
os espectros foram obtidos por reflectância difusa, utilizando a faixa espectral entre
1260 e 2500 nm. Algumas estratégias de pré-processamento dos dados espectrais
foram avaliadas e os melhores resultados foram obtidos com os espectros derivados
(algoritmo Savitzky-Golay utilizando uma janela de 23 pontos). A espectroscopia
NIR, combinada com o método de regressão por mínimos quadrados parciais (PLS)
mostrou-se uma técnica simples e rápida para determinar o GP dos papéis. O erro
de previsão de 83, obtido após a validação externa, é aceitável para a avaliação da
vida útil remanescente do papel isolante.
|
12 |
Estudo teórico de característica elétrica de contato schottky não íntimo metal-isolante amorfo e estrutura metal-isolante-metal / Theoric study of electrical of Schottky contact from metal-insulator-metal and metal-amorphous insulators structuresMarta Bueno de Moraes 01 September 1989 (has links)
No presente trabalho foi desenvolvida uma teoria de característica elétrica da estrutura metal-isolante-metal considerando uma camada fina de óxido entre o metal e o isolante, sendo o óxido um outro isolante de banda de energia proibida mais larga. Foi considerada uma distribuição energética uniforme de estados de impurezas à interface óxido-isolante. Estudamos a distribuição real do potencial na região de carga espacial usando a equação de Poisson. Através desta distribuição obtemos a relação entre o potencial de contato e a carga positiva na região de depleção e assim a característica capacitância-voltagem da estrutura. Este tipo de característica é útil para se calcular as características corrente em função do potencial e corrente em função do tempo para um dado potencial e deste modo é importante para o entendimento das estruturas MIM e MOIM. / In this work we have developed a theory of electric characteristic of the metal-oxide-insulator-metal structure, considering a thin film of oxide between metal and insulator; the oxide is another insulator of wider forbidden energy gap. A uniform energy distribution of impurity states at the oxide-insulator interface was considered. W e have studied the actual distribution of potential in the region of spatial charge using the Poisson equation. With this distribution we obtain the relation between the contact potential and the charge in the depletion region and then the characteristic potential - capacitance of t his structure. This type of characteristic is useful to calculate the characteristic current - potential, and current-time at a given potential . In this manner it is important to the understanding of MIM and MOIM structures.
|
13 |
Estrutura atômica e eletrônica em niquelatos (TRNiO3) através de espectroscopia de níveis profundosPiamonteze, Cinthia 18 March 2004 (has links)
Orientador: Helio C. N. Tolentino / Tese (doutorado) - Universidade Estadual de Campinas, Instituto de Fisica Gleb Wataghin / Made available in DSpace on 2018-08-03T19:43:00Z (GMT). No. of bitstreams: 1
Piamonteze_Cinthia_D.pdf: 4154285 bytes, checksum: 82d97aed8eb9e53d3bae6e0cb0a40eb5 (MD5)
Previous issue date: 2004 / Resumo: Neste trabalho de tese estudamos a estrutura atômica e eletrônica de sistemas de perovskitas de Ni com terras-raras (TRNiO3) utilizando a espectroscopia de absorção de níveis profundos. A fonte de luz síncrotron foi explorada na região de raios X moles para o estudo das bordas LIII e LII do Ni, e na região de raios X duros para o estudo da borda K do Ni e LIII dos terras raras. A propriedade mais notável nesses sistemas é a ocorrência de uma transição metal-isolante ao variarmos a temperatura da amostra. Essa tem-peratura de transição depende do íon terra-rara, e aumenta ao reduzirmos o tamanho do mesmo. Esses sistemas possuem uma estrutura perovskita distorcida, onde os octaedros NiO6 giram para preencher o espaço em torno do íon terra-rara. Quanto menor o íon, maior a distorção. Observamos assim uma estreita correlação entre a distorção da rede e a transição metal-isolante.Para sistemas com TR variando desde Pr ao Gd foi encontrada uma estrutura cristalográfica de simetria ortorômbica, onde o Ni ocupa um sítio simétrico.Baseado nisto, um primeiro modelo proposto sugeria que a transição seria devido ao estreitamento da banda formada pelos orbitais hibridizados Ni-3d e O-2p, quando o ângulo Ni-O-Ni diminui. No entanto, modificações na temperatura de transição metal-isolante pela substituição isotópica do O mostraram que o acoplamento elétron-fônon deveria ser importante. De fato, para sistemas com íons TR menores (de Ho a Lu) foi encontrada uma distorção monoclínica na fase isolante desses sistemas. Em tal estrutura o Ni ocupa sítios distintos com distâncias Ni-O diferentes. Um ordenamento de cargas nesses sítios distintos explica a fase isolante, bem como o ordenamento antiferromagnético observado para alguns dos compostos. Nossos resultados mostram que essas duas distâncias Ni-O coexistem para todos os sistemas, independentemente da estrutura cristalográfica de longo alcance, e em ambas fases eletrônicas. O sítio maior, de fraca hibridização, é o responsável pela localização eletrônica e coexiste com uma matriz condutora de forte hibridização. A transição metal isolante é explicada pelas modificações na proporção entre esses dois sítios. Dentro deste contexto, um forte acoplamento dos elétrons de condução com a rede é esperado, bem como a supressão da fase isolante sob pressão / Abstract: In this work, we studied the atomic and electronic structure of Ni perovskite systems (TRNiO3, TR=rare earth) using core level absorption spectroscopy. The synchrotron light source was exploited in the soft X-ray range to study Ni LIII and LII edges and in the hard X-ray range to study Ni K edge and rare earths LIII edges. The most remarkable property in these systems is a metal to insulator transition with temperature. This transition temperature depends on the rare-earth ion, increasing its value as the rare earth size is re-duced. These systems have a distorted perovskite structure, where the Ni O6octahedra rotate to fill the empty space left around the rare-earth ion. The smaller the ion, the larger the distortion. This indicates a straight correlation between the net distortion and the metal-insulator transition. For systems with TR varying from Pr to Gd it was found a crystallographic structure with orthorhombic symmetry, where Ni occupies a very symmetric site. Based on these results, it was proposed a model suggesting that the bandwidth would decrease due to a smaller hybridization between Ni3d and O2p bands caused by a decrease at the Ni-O-Ni angle. However, modifications in the transition temperature by the O isotope substitution, showed that the electron-phonon coupling plays an important role. Indeed, for systems with smaller TR ions (from Ho to Lu) it was found a monoclinic distortion in the insulating phase. In such structure Ni occupies two different sites with different Ni-O distances. A charge ordering associated to these different sites explains the insulating phase, as well as the antiferromagnetic ordering observed for some systems. Our results show that these two Ni-O distances coexist in all systems, inde-pendent of its long range crystallographic structure, and in both electronic phases. The site with longer Ni-O distance, which is weakly hybridized, is the responsible for the electronic localization and it is immersed in a con-ducting matrix with stronger hybridization. The metal-insulator transition is explained by the modifications in the proportion between these two Ni sites. In this context, a strong electron-phonon coupling is expected, as well as the suppression of the insulating phase under pressure / Doutorado / Física / Doutor em Ciências
|
14 |
Subcoberturas: aplicação de isolantes térmicos em sistemas de coberturas / not availableConsuelo Carletto 20 May 2005 (has links)
Este trabalho tem como foco principal apresentar os resultados e as contribuições da pesquisa experimental comparativa de subcoberturas em sistemas de cobertura. Para tal fim foram utilizados quatro protótipos localizados no canteiro experimental do CRHEA - EESC em São Carlos, São Paulo. Os protótipos foram construídos da mesma forma e com os mesmos materiais: tijolo comum, laje cerâmica recapeada com concreto; cobertos com telhas de fibrocimento e submetidos às mesmas excitações de clima ao ar livre. A análise foi feita aplicando um curto intervalo de clima, com respaldo teórico da climatologia dinâmica. Um dos protótipos serviu como testemunho e não recebeu a instalação de nenhuma subcobertura. Os outros três receberam cada um, respectivamente, subcobertura de foil (isolante por reflexão, ou barreira de radiação), lã de rocha (isolante convencional, condutividade térmica k) e de caixas cartonadas Tetra Pak, um resíduo, como isolante por reflexão e câmara de ar, já que foram utilizadas fechadas e uma ao lado da outra. Foram monitoradas as temperaturas superficiais da telha e da laje e, das temperaturas de bulbo seco no ático e na parte interna dos protótipos a 1,10 m de altura. As medidas de aquisições de dados foram feitas através de CR10X Campbell Scientific automático com medições em 30 segundos, armazenados e totalizados em 30 minutos, o que resultou em valores de clima ao livre e em recinto fechado muito precisos. / Thermal comfort achievement can be done by using thermal reflexive barriers, meaning energy savings and avoiding health problems of air conditioning. It can also be done by using building construction waste materials as Tetra Pak boxes, a low cost reflexive insulation, and applying an industrial \"foil\" which the same effect on reducing indoor air temperatures. In the same way traditional thermal insulation materials were used on this research as the mineral wool (conventional insulation material, thermal conductivity - k values). The analysis was made applying short intervals of climate such as recommended by the dynamic climatic approach. The use of foil insulation can be justified because of its behavior as a reflective barrier and because it has a lot of acceptation; mineral wool (mineral source with low k insulation values) for being a traditional kind of thermal insulation and the Tetra Pak box, because it is a reflective insulation and also because of its waste recycle usage characteristic. The research shows the insulation thermal efficiency applied on three kinds of fiber asbestos cover system, which makes the indoor air temperatures inside of comfort zones values, as intended to expose by graphics, made by real time and automatic experimental measurements. The measurements of data acquisitions were made by automatic CR10X Campbell Scientific Inc., 30 seconds scanner and totalized storage as 30 minutes average intervals. This means a very accurate result of values of outdoor and indoor climate translated by indoor and out door air temperatures.
|
15 |
Localização de Anderson e transição metal-isolante em filmes de Pb1-xEuxTe do tipo p / Anderson Localization and Metal-Insulator Transition in p - type Filmes of Pb1-xEuxTePeres, Marcelos Lima 20 May 2008 (has links)
Neste trabalho, realizamos o estudo da transição metal-isolante e da localização de Anderson na liga de Pb1-xEuxTe do tipo p para x variando de 0 até 0.1. As propriedades de transporte nessa liga (mobilidade, concentração de portadores e resistividade elétrica) foram obtidas utilizando o método de caracterização elétrica por efeito Hall entre as temperaturas de 300 K e 10 K. Nessa região de temperatura, foi possível observar uma transição metal-isolante para x > 0.05. Verificamos que a transição é do tipo Anderson e ocorre devido à desordem presente na liga. Para baixas temperaturas (T < 10 K) e em amostras com x > 0.01, verificamos a presença de magnetorresistência positiva e negativa aplicando campos magnéticos de até 11T. Nas amostras metálicas, a presença de magnetorresistência negativa é causada pelo efeito conhecido como localização de Anderson (efeito de interferência quântica construtiva entre as funções de onda) e a presença de magnetorresistência positiva é causada, principalmente, pelo acoplamento spin-órbita, e é chamada de antilocalização. Nas amostras isolantes, a magnetorresistência negativa é originada pelo efeito Zeeman enquanto que a magnetoresistência positiva é causada pela redução do comprimento de localização. Assim, os valores positivos e negativos da magnetoresistência têm origens diferentes dependendo do regime de condução (metálicoou isolante). Por esse motivo, o estudo dos resultados experimentais apresentados nesse trabalho foi dividido em duas partes: uma parte que trata as amostras metálicas (região de desordem fraca) e outra parte para as amostras isolantes (região de desordem forte). A partir dessa divisão, e utilizando os modelos teóricos disponíveis na literatura, foi possível fazer uma análise das medidas experimentais de magnetotransporte. Como resultado, identificamos os principais mecanismos de interação (espalhamento inelástico, efeito Zeeman, acoplamento spin-órbita, etc.) que interferem no transporte e nos efeitos de localização e antilocalização. / In this work, we investigated Anderson localization and the metal-insulator transition in p-type films of Pb1-xEuxTe for x varying from 0 up to 0.1. The transport properties of this alloy (mobility, carrier concentration and electrical resistivity) were obtained using the Hall method of electrical caracterization for temperatures ranging from 300 K down to 10 K. In this temperature range, it was possible to observe a metal-insulator transition for x > 0:05. The transition is of the Anderson type and is due to the disorder present in the alloy. For low temperatures (T < 10 K) and for samples with x > 0.01, we observed positive and negative magnetoresistance for magnetic fields up to 11 T. For metallic samples, the negative magnetoresistance originates from Andersons localization (constructive quantum interference effect between the wave functions) while positive magnetoresistence is caused, mainly, by the spin-orbit scattering, and it is called antilocalization. For insulating samples, negative magnetoresistance is originated from the Zeeman effect while positive magnetoresistance is caused by the localization length reduction. Therefore, positive and negative magnetoresistance values have different origins depending on the conduction regime (metallic or insulating). For this reason, our experimental investigation, presented in this work, was separated into two parts: the first one treats the metallic samples (weak-disorder regime) and the other treats the insulating samples (strong-disorder regime). From this division, and using available theoretical models, it was possible to analyze the magnetotransport experimental measurements. As a result, we identify the main interaction mechanisms (inelastic scattering, Zeeman effect, spin-orbit coupling, etc.) that interfere on the transport and localization and antilocalization effects.
|
16 |
Painéis de partículas de saco de cimento e embalagem longa vida aplicados como forro em protótipos de aviários / Particleborads of cement bag and long-life packaging applied as lining in avian prototypesCravo, Julio Cesar Machado 03 March 2016 (has links)
No presente trabalho, considerou o estudo do potencial de utilização de sacos de cimento e embalagens de longa vida com o intuito de agregar valor a esses resíduos, mediante a fabricação de painéis de partículas para uso como forro em protótipos de galpões avícolas. Para fabricação desse material foi utilizado sacos de cimento descartados nas obras civis, embalagens longa vida residuais e resina poliuretana bicomponente à base de óleo de mamona. O estudo foi dividido em quatro etapas: 1) Caracterização da matéria-prima (sacos de cimento); 2) Efeito da densidade e teor de resina nas propriedades físicas, mecânicas e térmicas de painéis de partículas de saco de cimento; 3) Avaliação do desempenho de embalagens longa vida e verniz como revestimentos dos painéis selecionados na etapa anterior; 4) Determinação do desempenho térmico de protótipos de aviários executados em escala reduzida e distorcida com forro de painel de saco de cimento e embalagem longa vida. Os resultados obtidos indicaram: Em razão do painel com 0,6 g.cm-3 e 12% de resina ter apresentado melhor desempenho nas propriedades investigadas, essa combinação foi selecionada para avaliar o desempenho do material (físicas, mecânicas e térmicas) quando revestido com embalagens longa vida, adotando a testemunha e o verniz como um revestimento comparativo. Dentre os revestimentos avaliados, os painéis com embalagens de longa vida, foram superiores aos revestidos com verniz, quando comparados as suas propriedades físicas, mecânicas e térmicas. Dessa maneira, painéis com 0,6 g.cm-3 e 12% de resina revestidos embalagens longa vida, foram testados como forro quanto ao desempenho térmico (primavera, verão, outono e inverno) em protótipos em escala reduzida e distorcida, mediante a determinação de índices de conforto térmico (Entalpia e IAPfc) para aves de corte. A associação do forro sob o protótipo permitiu reduzir a temperatura interna do ar e dos índices de conforto térmico na primavera, verão e outono, enquanto que no inverno não foi constatado eficácia do material. Dentre as estações estudadas, o verão e a primavera, demonstraram serem as épocas mais críticas para criação de aves corte em instalações avícolas que apresentem características semelhantes aos protótipos experimentais. / In this study, the study of the potential use of cement bags and long-life packaging is considered in order to add value to this waste, by manufacturing particleboards as insulating panels in poultry house facilities. For the production of this material cement bags discarded in civil works, long-life packaging discarded by consumers and two-component polyurethane resin based on castor oil base were used. The study was structured in four steps: 1) Characterization of the raw material (cement bags), 2) Effect of the density and the level of resin on the physical, mechanical and thermal properties of cement particles bag panels, 3) Evaluation of long-life packaging and varnish as a coating of selected panels in precedent step and 4) Evaluation of thermal performance of poultry prototypes in reduced and distorted scale with the long-life packaging as a coating material. The cement bags were disintegrated and transformed into particles with the 8% of moisture content. Subsequently, these particles were mixed with bicomponent polyurethane based on castor oil resin and taken into a planetary mixer (MT120) in order to homogenize the mixture of the particles with the resin. Panels were made for three different densities (0.4, 0.5 and 0.6 g.cm-3) with two resin levels (12 and 15%) and their physical, mechanical and thermal properties were evaluated. Because the panel with 0.6 g.cm-3 and 12% resin have shown a better performance in the investigated properties, this combination has been selected to evaluate the performance of the material (physical, mechanical and thermal) when coated with long-life packaging, adopting the control and the varnish as a comparative coating. Among the evaluated coatings, panels with long-life packaging, presented higher performance than those coated with varnish regarding their physical, mechanical and thermal properties. Thus, the combination of 0.6 g.cm-3 and 12% resin coated long-life packages were tested as lining according the thermal performance (spring, summer, autumn and winter) in prototypes and small-distorted scale by determining thermal comfort indices (Enthalpy and IAPfc) for broilers. The association of lining under the prototype reduced indoor air temperature and thermal comfort indices in spring, summer and autumn, while during the winter no effectiveness of the material was observed. Among the studied seasons, the spring and summer, proved to be the most critical time for cut birds breeding in poultry houses that have characteristics similar to experimental prototypes.
|
17 |
Estudo da transição metal-isolante em óxidos de terra-rara e níquel / Study of metal-insulator transition in rare-earth oxides and nickel.Escote, Marcia Tsuyama 06 February 2002 (has links)
Esta tese apresenta um estudo sistemático da síntese e das propriedades físicas de amostras policristalinas de Nd IND. 1-X R IND. X NiO IND. 3; R = Sm, Eu, 0 < OU = X < OU = 1. Estes materiais apresentam uma transição de fase metal-isolante MI em temperaturas 200 < OU = T IND. MI < OU = 400 K. Amostras foram produzidas a partir do método de precursores sol-gel, sinterizadas a 1000 GRAUSC e sob pressões de O IND. 2 de até 80 bar. O estudo da influência da substituição de R POT. 3+ na matriz de NdNiO IND. 3 foi realizado a partir das caracterizações através de medidas de difração de raios-X DRX, difração de neutrons como função da temperatura DRN, transporte elétrico ro(T), transporte térmico capa(T), coeficiente Seebeck S(T), calorimetria diferencial e susceptibilidade magnética qui(T). Os resultados de DRX revelaram que as amostras são monofásicas e cristalizam-se na estrutura perivskita distorcida ortorrombicamente, grupo espacial Pbnm. As medidas de DRN realizadas nas amostras de Nd IND. 1-XEu IND. X NiO IND. 3 mostraram a evolução dos parâmetros de rede e do volume da cela unitária V como função da temperatura. Estas caracterizações revelaram que, em T DA ORDEM DE T IND. MI, ocorre uma expansão em V, assim como um aumento do ângulo de ligação Ni-O e uma diminuição do ângulo de \"superexchange\" teta. Medidas de ro(T) revelam a ocorrência da transição MI em um amplo intervalo de temperatura 200 < OU = T IND. MI 400 K. Através destas medidas verificou-se também a presença de histerese térmica ocorre decresce continuamente com o aumento de x, até anular-se em x > 0,5 e em x > 0,35 para R=Sm e Eu, respectivamente. Este resultado foi confirmado através das medidas de capa(T) e S(T). Além disso, verificou-se a importância da contribuição da rede na capa(T). As medidas de S(T) indicam que os portadores de carga são elétrons e que a densidade de ) estados no nível de Fermi N(E IND. F) foi estimada ser da ordem de 10 POT. 23 (eVcm POT. 3) POT. -1. Os valores de T IND. MI e a presença ou não de histerese térmica foram verificados através das medidas de DSC. Um estudo foi feito para verificar qual a maneira mais precisa de subtrair a contribuição dos íons terras-raras nas medidas de susceptibilidade magnética qui(T) dos compostos Nd IND. 1-X R IND. X NiO IND. 3. Após estas correções foi possível verificar o ordenamento magnético da sub-rede do Ni POT. 3+ na região de temperatura T IND. n DA ORDEM DE 200 K para as amostras com x < 0,4 e x < 0,25 para R=Sm e Eu, respectivamente. Ajustes lineares feitos em qui(T) acima de temperaturas T > 200 K revelaram valores de momentos magnéticos efetivos müeff variando de 1,7 a 1,8 mü IND. B o que está em concordância com o valor esperado de müeff DA ORDEM DE 1,76 mü IND. B do íon livre de Ni POT. 3+. Adicionalmente, uma separação precisa do termo independente da susceptibilidade magnética foi efetuada e a susceptibilidade de Pauli dos materiais foi encontrada. Foi possível então obter uma estimativa da densidade de estados no nível de Fermi N(E IND. F), que gerou valores similares aos obtidos via medidas do coeficiente Seebeck. Entretanto, o comportamento de qui(T) corrigido abaixo de T IND. n revelou características de um antiferromagnetismo não convencional devido a um aumento monotônico de qui(T) com o decréscimo da temperatura e a presença de irreversibilidade nas curvas resfriadas a campo magnético zero ZFC e do refinamento de estrutura estimou-se que a valência no Ni nas amostras de Nd IND. 1-X R IND. X NiO IND. 3 DA ORDEM DE 3. Estimativas grosseiras da largura de bando W do O 2ro e da energia de transferência de carga delta para a série de compostos Nd IND. 1-X R IND. X NiO IND. 3 revelaram valores compatíveis com aqueles ) encontrados na literatura. De maneira geral, as caracterizações das propriedades estruturais, de transporte e magnéticas sugerem que os compostos Nd IND. 1-X R IND. X NiO IND. 3 podem ser classificados como sistemas onde correlações eletrônicas e flutuações dessas correlações ocorrem. Foram discutidas algumas limitações acerca da aplicabilidade dos modelos vigentes para a explicação da transição metal-isolante nos niquelatos aqui estudados. / This work reports a systematic study on the synthesis and general physical properties of polycrystalline samples of Nd IND. 1-X R IND. X NiO IND. 3; R = Sm, Eu, 0 < OU = X < OU = 1. These compounds exhibit a metal-insulator MI phase transition in a broad range of temperature 200 < OU = T IND. MI < OU = 400 K. The samples were prepared through sol-gel precursors and sintered at extreme conditions: high temperatures 1000 GRAUSC and under oxygen pressures up to 80 bar. These samples were characterized by several techniques including X-ray powder diffraction XRD, neutron diffraction as a function of temperature NRD, electrical resistivity ro(T), thermal conductivity capa(T), Seebeck coefficient S(T), differential scanning calorimetry DSC, and magnetic susceptibility qui(T). The results of XRD revealed that all samples are single phase and crystallize in an orthorhombic structure, space group Pbnm. The NRD data, combined with the Rietveld analysis, indicated small changes in the lattice parameters a, b, and c and in the volume V of the unit cell T DA ORDEM DE T IND. MI. Such a small change in these parameters is accompained by either a little decrease of the superexchange angle teta and a small expansion of the Ni-O bond-length. The ro(T) data exhibit interesting features such as: (1) a metallic-like behavior of ro(T) at high temperatures; (2) a huge increase of the magnitude of ro(T) at T DA ORDEM DE T IND. MI; and (3) a thermal hysteresis occurring just below T DA ORDEM DE T IND. MI in a temperature interval as large as 100K. Such a thermal hysteresis is characteristic of a first order MI transition and was found to vanish with increasing substitution of x. This strongly suggests that increasing x modify the character of this transition to second order. Thermal properties were carried out and confirmed the change of this MI transition with increasing x. In addition, an analysis of the capa(T) data indicate that phonons are the major thermal carriers in these nickelates. Also, the Seebeck coefficient S(T) data revealed features of a conventional metal at higher temperatures with electrons as carriers. An accurate analysis of the S(T) data based on simple band structure arguments indicate a density of states at the Fermi level of 10 POT. 23 (eVcm POT. 3) POT. -1 and energy gaps in the insulating regime close to 20 meV. The character of the first order transition in lightly substituted samples at T DA ORDEM DE T IND. MI was also inferred from the DSC data. The S(T) data confirmed the occurrence of the metal-insulator transition and the already observed change from first to second order character with increasing x. The magnetic susceptibility ípsilon(T) data have been precisely corrected by a systematic subtraction of the R POT.3+-ion contribution of the measured qui(T). Linear adjusts of the corrected curves above 150K where found to fit the Curie-Weiss law with effective magnetic moment of mü IND. EFF ~ 1.76 mü IND. B, which is close to the free-ion value of mü IND. EFF ~ 1.76 mü IND. B (Ni POT. 3+). These results indicate that the Ni POT. 3+ array displays an antiferromagnetic ordering below a well-defined temperature T IND. N, which is close to T IND.MI for Nd IND. 1-X R IND. X NiO IND. 3 and lightly substituted samples. However, the evolution of the susceptibility of the Ni POT. 3+ array displays features which are fingerprints of unconventional antiferromagnetic state. These features, observed mostly below T IND. N, include a field independent irreversibility of qui(T) and a systematic increase of qui(T) with decreasing temperature, resembling that of a paramagnet. An analysis of the electronic contribution to ípsilon(T) resulted in a density of states at the Fermi level close to the one estimated from the S(T) data. These results are discussed within the context of recent experimental results and theories employed to explain the origin of the metal-insulator transition in these nickelates.
|
18 |
Análise do enxofre corrosivo em óleo mineral isolante e remoção do dibenzil dissulfeto com nanotubos de carbono baseados em matriz metálicaSARAIVA, Augusto Cesar Fonseca 07 May 2012 (has links)
Submitted by Edisangela Bastos (edisangela@ufpa.br) on 2014-01-13T19:07:46Z
No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Tese_AnaliseEnxofreCorrosivo.pdf: 5261345 bytes, checksum: d394934b8edcf92029d079a04f821905 (MD5) / Approved for entry into archive by Ana Rosa Silva(arosa@ufpa.br) on 2014-01-14T16:03:22Z (GMT) No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Tese_AnaliseEnxofreCorrosivo.pdf: 5261345 bytes, checksum: d394934b8edcf92029d079a04f821905 (MD5) / Made available in DSpace on 2014-01-14T16:03:22Z (GMT). No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Tese_AnaliseEnxofreCorrosivo.pdf: 5261345 bytes, checksum: d394934b8edcf92029d079a04f821905 (MD5)
Previous issue date: 2012 / Falhas inesperadas em transformadores levaram a identificação da formação de
sulfeto de cobre, depositado sobre os condutores, avaliando-se da presença
qualitativa de enxofre corrosivo resultando na alteração da norma brasileira ABNT
NBR 10505, que avalia a presença de enxofre corrosivo em óleo mineral, alterando-se
o tempo e a temperatura de ensaio para 150 °C por 48 horas. Realizando-se a
especiação química de compostos organosulfurados via cromatografia gasosa
acoplada a espectrometria de massas, onde foram encontrados 13 compostos
sulfurados no óleo Nynas e 9 compostos no óleo da Petrobras, sendo o dibenzil
dissulfeto (DBDS) o de maior concentração, encontrado apenas no óleo Nynas. Para
realizar a determinação da presença do DBDS em óleo mineral isolante foi
desenvolvido um método através de cromatografia gasosa acoplada a
espectrometria de massas, e por este método foi possível quantificar o teor de
DBDS em amostras de OMI oriundas de transformadores de potência. Foi avaliado o
processo de passivação do cobre por benzotriazol e tolutriazol, utilizados como
aditivos anticorrosivos no núcleo dos equipamentos elétricos, verificando-se que o
efeito da adição agente de passivação torna-se ineficaz com o passar do tempo. A
solução para a remoção de DBDS em óleo mineral foi a utilização de nanotubo de
carbono baseado em matriz metálica (NTC/Al) como agente de remoção do DBDS.
Verificou-se que o agente de adsorção foi capaz de efetuar a remoção total do
DBDS do OMI até um volume de 4000 mL de óleo contaminado com DBDS. / Unexpected failures in transformers led to the identification of copper sulphide
formation, deposited on the conductors. The qualitative presence evaluation of
corrosive sulfur in insulating mineral oil, led to a change in the Brazilian standards
ABNT NBR 10505, which assesses the presence of corrosive sulfur in mineral oil,
change in the time and test temperature to 150 °C / 48 hours. Performing the
chemical speciation of organosulfur compounds (by gas chromatography coupled to
mass spectrometry), were found 13 compounds in the Nynas oil and 9 compounds in
the Petrobras oil. DBDS, which was found only in the Nynas oil, and it was the
compound with the highest concentration. To perform the determination of the
presence of DBDS in insulating mineral oil, a method by gas chromatography
coupled to mass spectrometry was developed, and it was possible to quantify the
amount of DBDS in insulating mineral oil samples derived from the power
transformer. The passivation process by tolutriazol and benzotriazol, used as
anticorrosive additives in the core of electrical equipament, was evaluated; after a
while the effect of the addition of passivating agent becomes ineffective with time.
The solution for the remotionl of DBDS from mineral oil was realized by using carbon
nanotube reinforced by metallic matrix as agent to remove the DBDS. It was found
that the adsorption agent was able to realize the complete DBDS remotion from
insulating mineral oil up to a volume of 4000 mL (oil contaminated with DBD).
|
19 |
Localização de Anderson e transição metal-isolante em filmes de Pb1-xEuxTe do tipo p / Anderson Localization and Metal-Insulator Transition in p - type Filmes of Pb1-xEuxTeMarcelos Lima Peres 20 May 2008 (has links)
Neste trabalho, realizamos o estudo da transição metal-isolante e da localização de Anderson na liga de Pb1-xEuxTe do tipo p para x variando de 0 até 0.1. As propriedades de transporte nessa liga (mobilidade, concentração de portadores e resistividade elétrica) foram obtidas utilizando o método de caracterização elétrica por efeito Hall entre as temperaturas de 300 K e 10 K. Nessa região de temperatura, foi possível observar uma transição metal-isolante para x > 0.05. Verificamos que a transição é do tipo Anderson e ocorre devido à desordem presente na liga. Para baixas temperaturas (T < 10 K) e em amostras com x > 0.01, verificamos a presença de magnetorresistência positiva e negativa aplicando campos magnéticos de até 11T. Nas amostras metálicas, a presença de magnetorresistência negativa é causada pelo efeito conhecido como localização de Anderson (efeito de interferência quântica construtiva entre as funções de onda) e a presença de magnetorresistência positiva é causada, principalmente, pelo acoplamento spin-órbita, e é chamada de antilocalização. Nas amostras isolantes, a magnetorresistência negativa é originada pelo efeito Zeeman enquanto que a magnetoresistência positiva é causada pela redução do comprimento de localização. Assim, os valores positivos e negativos da magnetoresistência têm origens diferentes dependendo do regime de condução (metálicoou isolante). Por esse motivo, o estudo dos resultados experimentais apresentados nesse trabalho foi dividido em duas partes: uma parte que trata as amostras metálicas (região de desordem fraca) e outra parte para as amostras isolantes (região de desordem forte). A partir dessa divisão, e utilizando os modelos teóricos disponíveis na literatura, foi possível fazer uma análise das medidas experimentais de magnetotransporte. Como resultado, identificamos os principais mecanismos de interação (espalhamento inelástico, efeito Zeeman, acoplamento spin-órbita, etc.) que interferem no transporte e nos efeitos de localização e antilocalização. / In this work, we investigated Anderson localization and the metal-insulator transition in p-type films of Pb1-xEuxTe for x varying from 0 up to 0.1. The transport properties of this alloy (mobility, carrier concentration and electrical resistivity) were obtained using the Hall method of electrical caracterization for temperatures ranging from 300 K down to 10 K. In this temperature range, it was possible to observe a metal-insulator transition for x > 0:05. The transition is of the Anderson type and is due to the disorder present in the alloy. For low temperatures (T < 10 K) and for samples with x > 0.01, we observed positive and negative magnetoresistance for magnetic fields up to 11 T. For metallic samples, the negative magnetoresistance originates from Andersons localization (constructive quantum interference effect between the wave functions) while positive magnetoresistence is caused, mainly, by the spin-orbit scattering, and it is called antilocalization. For insulating samples, negative magnetoresistance is originated from the Zeeman effect while positive magnetoresistance is caused by the localization length reduction. Therefore, positive and negative magnetoresistance values have different origins depending on the conduction regime (metallic or insulating). For this reason, our experimental investigation, presented in this work, was separated into two parts: the first one treats the metallic samples (weak-disorder regime) and the other treats the insulating samples (strong-disorder regime). From this division, and using available theoretical models, it was possible to analyze the magnetotransport experimental measurements. As a result, we identify the main interaction mechanisms (inelastic scattering, Zeeman effect, spin-orbit coupling, etc.) that interfere on the transport and localization and antilocalization effects.
|
20 |
Avaliação da estabilidade a oxidação de óleo vegetal de crambe (Crambe abyssinica Hochst) como fluido isolante / Evaluation of oxidation stability of vegetable oil from crambe (Crambe abyssinica Hochst) how insulating fluid, with different strengths and percentages of antioxidantsPrimieri, Cornélio 24 February 2012 (has links)
Made available in DSpace on 2017-07-10T15:14:43Z (GMT). No. of bitstreams: 1
Cornelio Primieri.pdf: 3721204 bytes, checksum: 8dabdaaf2812e1f80bfd5bfcd26f1dd1 (MD5)
Previous issue date: 2012-02-24 / This research aimed overall assessment of a new plant insulating fluid, using
as raw vegetable oil culture of crambe (Crambe abyssinica Hochst). Specific
objectives were to evaluate the oxidation stability of crambe oil with various types of
typical antioxidants used in edible vegetable oils available in the domestic market,
aiming at a new plant insulating fluid, using a raw vegetable oil that does not
compete with human food chain / animal. The experiment was conducted at the
Research Laboratory of Oil Chemistry of College Assis Gurgacz-FAG. In the
municipality of Cascavel / PR, a Latitude 24 º 56 'South, Longitude 53 º 30' W and
altitude of 682 m in the period from September to December 2011. The methodology
used was called Rancimat equipment, a device which simulates the two main
parameters that affect the oxidation stability of greases matters, which are the action
of high temperatures and the presence of oxygen, which presents results as an
induction period which is represented by periods in hours. From the data collected
during testing of the samples prepared using the Rancimat temperatures of 110 ° C
and 130 ° C, an average was calculated for each typ e of antioxidant, as well as their
concentrations and mixtures. The survey results showed that the sample that showed
the best oxidation stability at 110 ° C was obtaine d from the use of antioxidant TBHQ
in a concentration of 0.3% m / m (52.96 h). The worst case was the DBPC 0.1% m /
m (6.72 h). At temperatures of 130 ° C, the best re sult was TBHQ 0.3% m / m (12.67
h) and DBPC worst case was 0.1% m / m (0.61 h). Thus, we conclude that to obtain
a new fluid-based insulation plant crambe is feasible to use the antioxidant TBHQ,
with a concentration of 0.3% m / m. / A presente pesquisa teve como objetivo geral a avaliação de um novo fluído
vegetal isolante, utilizando como matéria prima o óleo vegetal da cultura do crambe
(Crambe abyssinica Hochst). Como objetivo específico a avaliação da estabilidade à
oxidação do óleo de crambe com diversos tipos de antioxidantes típicos utilizados
em óleos vegetais comestíveis disponíveis no mercado nacional, visando um novo
fluído vegetal isolante, utilizando matéria prima um óleo vegetal que não compete
com a cadeia alimentar humana/animal. O experimento foi conduzido no Laboratório
de Pesquisas em Óleo Química da Faculdade Assis Gurgacz-FAG, no município de
Cascavel/PR, a uma Latitude 24º56 Sul, Longitude de 53º30 Oeste e altitude de
682 m, no período de setembro a dezembro de 2011. A metodologia utilizada foi a
do equipamento denominado de Rancimat, equipamento este que simula os dois
principais parâmetros que afetam a estabilidade a oxidação das matérias graxas,
que são a ação das temperaturas elevadas e a presença de oxigênio, o que
apresenta como resultados um período de indução que é representado por períodos
em horas. A partir dos dados coletados nos ensaios das amostras elaborados no
Rancimat utilizando temperaturas de 110ºC e 130ºC, foi calculada uma média para
cada tipo de antioxidante, bem como suas concentrações e misturas. Os resultados
da pesquisa demonstraram que a amostra que apresentou a melhor estabilidade a
oxidação a 110ºC foi obtida do uso do antioxidante TBHQ com uma concentração de
0,3% m/m (52,96 h). O pior caso foi o DBPC a 0,1% m/m (6,72 h). Para
temperaturas de 130ºC, o melhor resultado foi o TBHQ a 0,3% m/m (12,67 h) e o
pior caso foi o DBPC a 0,1% m/m (0,61 h). Deste modo, conclui-se que para obter-se
um novo fluído vegetal isolante a base de crambe é viável a utilização do
antioxidante TBHQ, com uma concentração de 0,3% m/m.
|
Page generated in 0.0492 seconds