Orientador: Lourenço Correr Sobrinho / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-28T12:03:18Z (GMT). No. of bitstreams: 1 Francisco_MauroUriarte_M.pdf: 3424806 bytes, checksum: 47006e8306842cdbe7b0a44693ea0974 (MD5) Previous issue date: 2000 / Resumo: O propósito deste estudo foi investigar a influência da escovação mecânica na rugosidade de superfície dos materiais restauradores Artglass (Kulzer), Targis (Ivoclar) e Sculpture (Jeneric/Pentron). Oito amostras com 7mm de diâmetro por 2,5 mm de espessura foram confeccionadas para cada material. O Artglass foi polimerizado no forno Uni-XS por 180 segundos, o Targis foi polimerizado no aparelho Targis Power por 25 minutos e o Scuípture foi polimerizado por 10 minutos com o aparelho Cure Lite. Todas as amostras foram armazenadas em água destilada a 37° C, por 24 horas. Em seguida quatro amostras de cada material receberam acabamento e polimento e outras quatro serviram como controle. A rugosidade foi verificada com o aparelho Surf-corder (SE 1700), antes e após as amostras serem submetidas a 30.000 ciclos numa máquina de escovação Equilabor, usando escova dental (Kolynos) e dentifrício (Sorriso). Foram feitas três leituras em cada amostra, totalizando 72 leituras. Os resultados foram submetidos à análise de variância e ao teste de Tukey (5%) e indicaram que: 1- Para as amostras sem polimento, antes da escovação, a rugosidade do Targis (0,535 um) foi superior em relação ao Sculpture (0,190 um). Nenhuma diferença estatística foi observada quando o Targis foi comparado com o Artglass (0,330 um) e o Artglass com o Sculpture. Após a escovação, nenhuma diferença estatística foi observada entre o Targis (0,945 um), Artglass (0,597 um) e Sculpture (0,810 um); 2 - Para as amostras com polimento não houve diferença estatística entre os materiais Targis, Artglass e Sculpture, antes (0,627 um; 0,551 um; 0,535 um) e após a escovação (0,283 um; 0,344 um; 0,122 um); e, 3 -Os resultados indicaram que a escovação promoveu aumento na rugosidade de superfície nas amostras sem polimento e redução nas amostras com polimento / Abstract: The purpose of this study was to investigate the influence of mechanic brushing on surface roughness restorative materials of Artglass (Kulzer), Targis (Ivoclar) and Sculpture (Jeneric/Pentron). Eight samples with 7 mm in diameter and 2.5 mm in thickness were made for each material. The Artglass was cured in an Unix-XR oven for 180 seconds, the Targis was cured in a curing unit Targis Power for 25 minutes and Sculpture was cured for 10 minutes with Cure Lite unit. All samples were stored in distilled water at 37° C, for 24 hours. After four samples of each material received finishing and polishing treatment and four (control) without treatment. Roughness was verified using Surf-corder (SE 1700), before and after the specimens had been submitted to 30,000 cycling in an Equilabor brushing machine, using toothbrush (Kolynos) and toothpaste (Sorriso). Afterwards, the rougness were verified.The results were submitted to variance analysis and Tukey's test (5%) and indicated that: 1 - For the samples without polishing before toothbrushing the roughness for Targis (0.535 urn) was significantly stronger than Sculpture (0.190 |jm). No difference was found when Targis was compared with Artglass (0.330 urn) and when Artglass was compared with Sculpture. No difference was found after toothbrushing Targis (0.945 urn), Artglass (0.597 urn) and Sculpture (0.810 urn); 2 - For the samples with polishing , no difference was found among Targis, Artglass and Sculpture with polishing, before (0.627 urn; 0.551 urn; 0.535 urn) and after toothbrushing (0.283 urn; 0.344 urn; 0.122 urn). The results indicated that the mechanic brushing showed increased on surface roughness for the specimens without polishing and reduction for specimens with polishing / Mestrado / Materiais Dentarios / Mestre em Odontologia

Orientadores: Luis Alexandre Maffei Sartini Paulillo, Jaime Aparecido Cury / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-28T13:35:56Z (GMT). No. of bitstreams: 1 LeiteJunior_FernaoHeliodeCampos_M.pdf: 2155162 bytes, checksum: d525fc2dae861b16e55d38f823d30624 (MD5) Previous issue date: 2001 / Mestrado

Orientador: Mario Fernando de Goes / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-12T22:02:48Z (GMT). No. of bitstreams: 1 DiHipolito_Vinicius_D.pdf: 13253510 bytes, checksum: 5d98b51afd2b05e1bdb39a32ec2f39ce (MD5) Previous issue date: 2009 / Resumo: O objetivo deste estudo foi avaliar o efeito de partículas inorgânicas incorporadas em adesivos sobre a resistência de união (RU) e morfologia da interação com a dentina. O esmalte oclusal de molares humanos foi removido e cada dente seccionado em quatro partes, com o auxílio de disco dupla face de diamante, montado em baixa rotação. A dentina média exposta dos dentes foi regularizada com lixa granulação 600. Todas as superfícies de dentina foram condicionadas (ácido fosfórico 35% - 15s) e cada quarto do dente tratado com um dos seguintes adesivos: Adper Single Bond (SB-3M/ESPE - sem carga), Adper Single Bond 2 (SB2-3M/ESPE - silica coloidal, 5nm Ø), Prime & Bond NT (NTDentsply - silica coloidal, 7-40nm Ø) e OptiBond Solo (OS-Kerr Corp - aluminoborosilicate de bário, 400nm Ø). Um bloco de resina composta (Filtek Z350 3M/ESPE) foi construído sobre cada superfície tratada. Após armazenagem por 24horas em água destilada, cada conjunto dente/restauração foi seccionado nos eixos X e Y para obter espécimes em forma de palito, contendo 1mm2 de área de secção transversal. A RU foi determinada em máquina de ensaio universal (Instron 4411), a uma velocidade de 0,5mm/min. Os valores de RU foram submetidos à ANOVA e teste Tukey (?=0,05), e os padrões de fratura classificados em quatro categorias: Tipo I - fratura coesiva no adesivo, Tipo II - fratura coesiva na dentina, Tipo III - fratura coesiva na camada híbrida, Tipo IV - fratura mista: coesiva no adesivo e na camada híbrida. Vinte oito dentes adicionais foram usados para a análise morfológica em Microscopia Eletrônica de Varredura (MEV - 16 dentes) e Microscopia Eletrônica de Transmissão (TEM - 12 dentes). As superfícies de 32 discos de dentina (1,5mm de espessura) foram tratadas com cada um dos adesivos e unidas, aos pares, usando uma resina de baixa viscosidade (Filtek Flow - 3M/ESPE), para análise em SEM/EDX. Seções ultrafinas de dentina (90nm de espessura) foram obtidas de 12 dentes para o exame em TEM. O adesivo SB2 apresentou RU significativamente maior [Média (MPa) ± SD] - (42,64±11,4) que o SB (34,6±7,6), NT (28,5±7,0) e OS (33,3±5,6). Houve predominância do padrão defratura tipo IV para todos os adesivos. O SB2 revelou a mais baixa incidência do padrão de fratura tipo III. As análises em SEM/EDX e TEM mostraram uma distribuição homogênea das nanopartículas (silica) em toda a extensão da camada híbrida formada pelo SB2. Partículas inorgânicas apresentaram-se aglomeradas na embocadura dos túbulos dentinários e na porção superior da camada híbrida dos adesivos OS e NT. A presença de nanopartículas entre os espaços interfibrilares da camada híbrida formada pelo SB2 exerceu influência sobre a propriedade mecânica de resistência da união à dentina. / Abstract: The aim of this study was to evaluate the effect of fillers incorporated to adhesives on bond strength (µTB) and interfacial morphology of dentin. Oclusal enamel of 5 human molars was removed and each tooth was sectioned in four parts using a low-speed saw. The medium dentin exposed was ground with Sic (600 grit). All dentin surfaces were etched (35% phosphoric acid - 15s) and each part of the tooth treated with one of the following adhesives: Adper Single Bond (SB-3M/ESPE - unfilled); Adper Single Bond 2 (SB2-3M/ESPE - colloidal silica, 5nm Ø); Prime & Bond NT (NT-Dentsply - colloidal silica, 7-40nm Ø) and OptiBond Solo (OS-Kerr Corp - barium aluminoborosilicate, 400nm Ø). Blocks of resin-based composite (Filtek Z350 - 3M/ESPE) were built on the adhesive surfaces. After 24 hour water storage, each part of the tooth was sectioned in X and Y directions to obtain 1mm2 cross-sectional area sticks. µTB were determined with an Instron at cross-speed of 0.5mm/min. µTB values were submitted to ANOVA and Tukey test (a=0,05). The fracture pattern was classified in: Type I- total cohesive failure in adhesive resin, Type II - total cohesive failure in dentin, Type III - total cohesive failure in the hybrid layer, Type IV - cohesive failure in adhesive resin and in the hybrid layer .Twenty eight additional teeth were used for interfacial morphological analyzes by SEM (16 teeth) and TEM (12 teeth). The surfaces of 32 dentine discs (1.5mm thick) were treated with each of the adhesives and bonded to form discpairs using a flowable resin composite (Filtek Flow -3M/ESPE) for SEM/EDX analysis. Dentin sections (90nm thick) were obtained from 12 teeth for TEM interface examination. The SB2 had significantly higher µTB values [Mean (MPa) ± SD] - (42.6±11.4) than SB (34.6±7.6), NT (28.5±7) and OS (33.33±5.64). There was prevalence of type IV failure pattern for all the adhesives and the SB2 revealed the lowest incidence of type III failure pattern. The SEM/EDX and TEM analysis showed the homogeneous distribution of nanofillers (silica) into interfibrillar spaces of the hybrid layer formed by SB2. Fillers were concentrated around patent tubular orifices and at the upper part of the hybrid zone for OS and NT adhesives. The presence of nanofillers within interfibrilar spaces suggests its importance in the improvement of the tensile bond strength at the dentin-resin interface. / Doutorado / Doutor em Materiais Dentários

Orientador: Marcelo Giannini / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-13T02:32:05Z (GMT). No. of bitstreams: 1 Aguiar_ThaianeRodrigues_M.pdf: 2081066 bytes, checksum: 7befb03bacdaacad5af000ab6fe79fb2 (MD5) Previous issue date: 2009 / Resumo: A utilização de materiais que possibilitam alcançar excelência em estética, associada à redução do número de etapas presentes no protocolo de cimentação adesiva, tem destacado o interesse dos profissionais quanto ao uso dos cimentos resinosos autoadesivos. Com o recente advento destes materiais, contempla-se a necessidade em conhecer suas propriedades físicas e químicas, assim como o mecanismo de união ao substrato dental. Diante disso, este estudo teve como objetivo avaliar a influência do modo de polimerização (dupla polimerização e ativação química) de 4 cimentos resinosos sendo 3 cimentos resinosos autoadesivos (RelyX Unicem (RX), 3M ESPE, Seefeld, Alemanha; BisCem (BC), Bisco Inc., Schuamburg, IL, EUA e G-Cem (GC), GC Corp., Tóquio, Japão) e 1 cimento resinoso convencional (Panavia F 2.0 (PF), Kuraray Medical Inc., Kurashiki, Japão) quanto ao grau de conversão, resistência flexural biaxial e resistência de união à dentina. Para o ensaio de microtração, superfícies dentinárias de terceiros molares humanos foram utilizados e o padrão de fratura foi analisado em Microscopia Eletrônica de Varredura, enquanto, para os outros testes, os espécimes foram preparados a partir dos próprios cimentos resinosos com dimensões padronizadas e definidas de acordo com o ensaio aplicado. Para o estudo do grau de conversão, também foi avaliado o comportamento dos cimentos resinosos em função do tempo (5, 10 e 15 minutos), observou-se diferença estatística entre o tempo de avaliação e o modo de polimerização. A dupla polimerização aumentou os valores médios de grau de conversão para o RX e o BC; entretanto, o PF não demonstrou diferença significativa. Em relação ao tempo de avaliação, o melhor comportamento quanto ao grau de conversão foi observado 15 minutos após a manipulação dos cimentos avaliados com exceção do BC quimicamente ativado, que não demonstrou diferença estatística entre o período de 5 e 10 minutos. Para o cimento autoadesivo G-Cem, o cálculo do grau de conversão foi inviabilizado, pois não foi observado o anel aromático de carbono na leitura inicial do monômero. No ensaio de resistência flexural biaxial notou-se que a fotoativação aumentou os valores médios do módulo de flexão e da resistência à flexão; contudo, o cimento resinoso autoadesivo BC sempre apresentou os menores valores médios. O ensaio de microtração demonstrou o aumento da resistência de união dos materiais PF e GC quando fotoativados; os cimentos RX e BC não foram influenciados pelo modo de polimerização, porém, quando quimicamente ativados, o PF e RX apresentaram as maiores médias, sendo RX semelhante ao GC. O padrão de fratura apresentou predominância da falha adesiva entre dentina e cimento resinoso exceto para o grupo RX quimicamente ativado e GC fotoativado, seguido por falhas mistas envolvendo fraturas adesivas e coesivas no cimento resinoso. Conclui-se que a fotoativação dos cimentos resinosos de dupla polimerização empregados demonstrou melhores resultados na avaliação do grau de conversão, na resistência flexural biaxial e na resistência de união; entretanto, o melhor desempenho de alguns sistemas pode estar relacionado às características químicas inerentes ao material. / Abstract: The use of materials that enable excellence in esthetics, coupled with a reduction in the number of steps in the adhesive luting protocol, have aroused the interest of professionals in the use of self-adhesive resin luting. As these materials have appeared only recently, it is necessary to study the physical and chemical properties as well as the mechanism of bonding to dental substrate. Thus, the purpose of this study was to evaluate the effect of curing mode (dual and self-polymerizing) of four resin cements, of which three were self-adhesive resin cements (RelyX Unicem (RX), 3M ESPE, Seefeld, Germany; BisCem (BC), Bisco Inc., Schuamburg, IL, USA e G-Cem (GC), GC Corp., Tokyo, Japan) and one convenctional resin cement (Panavia F 2.0 (PF), Kuraray Medical Inc., Kurashiki, Japan) with regard to the degree of conversion, biaxial flexural strength and bond strength to dentin. For microtensile bond test, occlusal dentin surfaces of third human molars were used and the fractured surfaces of tested specimens were examined by scanning electron microscopy. In other tests, resin cement specimens of standard dimensions were prepared in accordance with each test applied. To study the degree of conversion, the behavior of resin cements was observed with regard to evaluation time (5, 10 and 15 minutes) and statistical difference was observed for the time of evaluation and curing mode. The mean values for RX and BC were increased when the resin cement was dual-polymerizing; however, PF showed no significant differences. With regard to the time of evaluation, the highest degree of conversion was observed 15 minutes after the cement was manipulated for all the groups evaluated, except when BC was auto-polymerized after 5 and 10 minutes. For the resin cement G-Cem it was not possible to calculate the degree of conversion, because no aromatic carbon ring was shown during the initial measurement of the monomer. For biaxial flexural strength, dual-polymerizing of the resin cement produced higher flexural modulus and strength; however, the resin cement BC always showed the lowest values. The tensile bond strength showed higher bond strength for PF and GC when light polymerized. The resin cements RX and BC were not influenced by the polymerization mode. However, when the systems were self-polymerizing, PF and RX showed the best results and RX was similar to GC. The failure pattern presented a predominance of adhesive failures between dentin and resin cement, except when RX was self-polymerized and G-Cem light polymerized, followed by mixed fractures, involving adhesive failure and cohesive fractures of the resin cement. It was concluded that light activation of the dual-polymerized resin cements used, showed highest degrees of conversion, biaxial flexural strength and microtensile bond strength. However, the better performance of some cementing systems may be associated with the chemical characteristics inherent to the material. / Mestrado / Dentística / Mestre em Clínica Odontológica

Orientador: Simonides Consani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-09T01:37:40Z (GMT). No. of bitstreams: 1 Mendes_WilsonBatista_D.pdf: 2328628 bytes, checksum: 84a6ebc2ccc7f57c27c8ec896e555096 (MD5) Previous issue date: 2007 / Resumo: O propósito deste estudo foi verificar a resistência à fratura da Porcelana pura e da cerâmica de cobertura sobre casquete de três sistemas cerâmicos (metalocerâmica, In Ceram e IPS Empress 2) após ciclagem mecânica, utilizando ensaio de carregamento com carga de compressão. As coroas foram fixadas nos preparos feitos em dentes bovinos, com cimento de ionômero de vidro modificado por resina composta ou cimento resinoso, seguindo as recomendações dos fabricantes. Após inclusão das raízes em tubos de PVC contendo resina acrílica, os preparos em forma de tronco de cone foram feitos com pontas diamantadas, em torno mecânico. Na linha marginal dos preparos foram confeccionados entalhes chanfrados, objetivando a padronização do posicionamento dos casquetes sobre o término marginal, em forma de ombro arredondado com 0,8mm de largura e paredes convergentes em 8 graus. Quinze casquetes foram confeccionados para cada um dos sistemas cerâmicos, exceto para a cerâmica pura, nos quais a aplicação da cerâmica de estratificação foi feita com auxílio de um dispositivo para padronizar a anatomia oclusal do dente. Após aplicação do glaze, a cimentação foi realizada com carga estática de 4kgf, por 1 minuto. Para simular o contato oclusal entre coroa e ponta da haste do dispositivo de carga, foram confeccionadas pontas-ativas metálicas com anatomia oclusal, de forma a não atingir o fundo da fossa e manter o paralelismo da haste. Após armazenagem em água destilada a 37ºC por 24 horas, os corpos-de-prova foram submetidos a 60.000 ciclos, com carga de 35N e 2Hz, imersos em água destilada. O teste de resistência à fratura foi efetuado numa máquina Instron, com velocidade de 0,5mm/minuto. Os resultados foram submetidos à análise de variância para experimentos aleatórios com fator único (fratura após fadiga). Os resultados mostraram diferenças significativas entre os diferentes sistemas cerâmicos, em nível de 95% de probabilidade. O teste de Tukey (5%) mostrou que os valores de resistência à fratura após fadiga mecânica foram com diferença estatisticamente significativa quando o sistema IPS Empress 2 foi comparado com o In Ceram. Os valores entre Porcelana pura e In Ceram foram sem diferença estatística, sendo que a Metalocerâmica não diferiu estatisticamente dos demais sistemas / Abstract: The purpose of this study was to verify the fracture strength of coverage ceramics in relation to four ceramics systems (metalporcelain, pure porcelain, In Ceram and IPS Empress 2), utilizing compressive load trial after dynamic cycle. The crowns were fixed in complete crown preparations made in bovine teeth, with glass-ionomer cement modified by composite resin or resinous cement, following the manufacturer¿s recommendations. The teeth were embedded by root in PVC tubes comprising acrylic resin, and the crown was made with diamond points in mechanic lathe. In the marginal preparation line was made a bevel cut, with the objective of standardize the cap¿s placement upon the marginal line, in rounded shoulder with 0,8mm in width and convergent walls in 8 degrees. Fifteen copings were produced for each ceramic system, with exception for all ceramic, in which the stratification ceramic application was performed with aid of a device to standardize the occlusal tooth anatomy. After glaze application, the crown cementation was realized with 4kgf static load, for 1 minute. To simulate the occlusal contact between opposite crowns, the loading device surface was made according to the tooth occlusal anatomy. After water storage at 37°C for 24 hours, the specimens were submitted to 60,000 dynamic cycles (35N load and 2Hz) immersed in water. The fracture strength test was accomplished in an Instron machine with a crosshead speed of 0,5mm/minute. Collected data were submitted to one-way ANOVA analyzing the fracture after fatigue factor. The results showed statistically significant difference among different ceramic systems at confidence level of 95%. Tukey¿s test showed that the fracture strength values after fatigue were statistically different when IPS Empress 2 system was compared with In Ceram. The values between pure ceramic and In Ceram were with no statistically significant difference, whereas the metalceramic was with no statistically significant difference when compared to other systems / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários

Orientador: Giselle Maria Marchi Baron / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-09T18:39:20Z (GMT). No. of bitstreams: 1 Voltarelli_FernandaRegina_M.pdf: 2059410 bytes, checksum: 22cefbd92cd0c4d2a5e932fba114a277 (MD5) Previous issue date: 2007 / Resumo: O objetivo deste estudo foi avaliar o efeito do tipo de fonte de luz (Halógena/HAL, Diodos Emissores de Luz/LED, Laser de Argônio/LAS e Arco de Plasma/PAC) e dos meios de envelhecimento sobre a microdureza das superfícies de topo e base de cilindros de resina composta com 4mm de altura. Para este estudo foram confeccionados 200 corpos de prova em resina composta Filtek Z250 (3M ESPE) a partir de matrizes metálicas bipartidas cilíndricas (5mm de diâmetro e 4mm de altura), divididos, aleatoriamente, em 20 grupos (n=10) de acordo com a fonte de luz e o envelhecimento empregado (Ciclagem Mecânica/CM, Ciclagem Térmica/CT, Estocagem/E, CM+CT e CM+CT+E), onde a ciclagem térmica consistiu em 1000 ciclos, com banhos de 60s a temperaturas variando entre 5 ± 2 °C e 55 ± 2°C; a ciclagem mecânica, em 200000 ciclos com 2Hz de freqüência e carga vertical de 75N e, a estocagem, em armazenamento em solução tamponada de Hank pelo período de 1 ano. O teste de microdureza Knoop (25g; 20s) foi realizado nas superfícies de base e topo de cada corpo de prova antes e após os envelhecimentos. A análise estatística (ANOVA One-way; ANOVA em esquema de parcelas subdividades; Tukey, ?=5%; Teste para dados pareados) observou interação significativa entre os aparelhos, entre os aparelhos e os envelhecimentos e entre os tempos avaliados. Tanto para base como para o topo, antes dos envelhecimentos, PAC obteve menores valores de microdureza Knoop quando comparado à HAL. Na superfície de topo, depois dos procedimentos de envelhecimento, PAC e LAS também apresentaram valores de microdureza inferiores quando comparados à HAL. Os menores valores de dureza, dentre os procedimentos de envelhecimentos testados, foram obtidos pelos corpos de prova submetidos à estocagem (CM+CT+E e E). Na superfície de base, para PAC não houve diferença entre os envelhecimentos, enquanto para HAL, LED e LAS, CM+CT+E e E obtiveram menores valores de microdureza Knoop. Quando procedimentos de CM, CT e CM+CT foram realizados, PAC obteve valores de dureza inferiores, enquanto para CM+CT+E e E não houve diferença entre as fontes de luz utilizadas. Assim, podemos concluir que a qualidade do polímero formado pelo PAC pode ter reduzido os valores de microdureza knoop obtidos tanto na base como no topo antes dos envelhecimentos e no topo, juntamente com o LAS, depois dos envelhecimentos. Dessa forma, podemos notar que HAL ainda demonstra adequada polimerização das resinas compostas. Além disso, podemos concluir que todos os procedimentos de envelhecimento influenciaram adversamente as amostras confeccionadas com PAC, e que os procedimentos de estocagem (CM+CT+E e E) foram os procedimentos de envelhecimento que mais afetaram os valores de microdureza Knoop, apresentando-se prejudiciais para todas as fontes de luz / Abstract: The aim of this study was to evaluate the effect of the light-curing devices (Halogen/HAL, Light Emitting Diodes/LED, Argon Laser/LAS and Plasma Arc/PAC) and aging procedures on the microhardness of bottom and top surfaces of resin composite cylinders with 4mm height, submitted to thermal and mechanical cycles, and one year storage. For this study 200 specimens of Filtek Z250 (3M ESPE) were prepared from metallic molds, and randomly allocated in 20 groups (n=10) according to the light source and the aging procedure employed (Mechanical Cycling/CM, Thermal Cycling/CT, Storage/E, CM+CT and CM+CT+E). The thermal cycling consisted of 1000 cycles (5±2C/55±2C)oo, the mechanical cycling in 200000 cycles (75N/2Hz), and the storage procedure in one year of storage in Hank solution. The microhardness test on bottom and top surfaces (25g/20s) was performed before and after the aging process. The statistical analysis (repeated measures of variance analysis and non parametric test) showed significant interaction between the devices, between the devices and the aging process, and also between the evaluated times. For base and top surfaces, before the aging procedures, PAC demonstrated reduced polymerization effectiveness when compared to HAL. In the top surface, after the aging procedures, PAC and LAS had also presented reduced polymerization effectiveness when compared to HAL. The lower hardness values, among the aging procedures tested, had been showed by the specimens submitted to storage (CM+CT+E and E). In the base surface, PAC did not presented differences between the aging procedures, while for HAL, LED and LAS, CM+CT+E and E had reduced the microhardness values. When CM, CT and CM+CT had been performed, PAC showed reduced polymerization effectiveness, while for CM+CT+E and E there was no difference between the light sources. Thus, we can conclude that the quality of the polymer formed by PAC reduced the microhardness values on the base and top surfaces before the aging process, and in the top surface after the aging procedures. It should be noted that HAL still demonstrate an adequate polymerization of resin composite. Moreover, we can conclude that all the aging procedures had been harmful for the samples confectioned with PAC, and that the storage procedures (CM+CT+E e E) were the aging procedures that had affected more the Knoop microhardness values, presenting themselves as harmful for all the light sources / Mestrado / Dentística / Mestre em Clínica Odontológica

Para avaliar o efeito de diferentes tratamentos superficiais sobre a resistência ao cisalhamento da união entre uma liga metálica (Co-Cr-Mo - Remanium CD) e um cimento resinoso (Rely XTM) e analisar o tipo de fratura durante a separação dos espécimes, quarenta pares de discos metálicos foram fundidos, regularizados e polidos, submetidos a quatro ciclos térmicos (vácuo, 960ºC, 8 minutos) e divididos aleatoriamente em quatro grupos. Cada grupo recebeu um tipo de tratamento: Grupo PSP: Polimento com lixa d'água Nº 600; Grupo PCP: Polimento com lixa 600 e aplicação do condicionador metálico Alloy Primer (Kuraray); Grupo JSP: Jato de óxido de alumínio (100 m, 75lib/pol2) e Grupo JCP: Jato de óxido de alumínio (100 m, 75lib/pol2) e aplicação do Alloy Primer. Os grupos foram cimentados e armazenados em água deionizada a 37ºC por 36 horas e separados em ensaio de cisalhamento. Os maiores valores foram produzidos pelos grupos jateados (JSP, JCP), independentemente da aplicação do primer; o Alloy Primer aumentou a retentividade entre o cimento Rely X e a superfície polida da liga de Co-Cr-Mo, entretanto sua força de união não superou a alcançada através do jateamento; todos os espécimes apresentaram falha adesiva na interface testada. / To evaluate the effect of different surface treatments on shear bond strength between a metallic alloy (Co-Cr-Mo - Remanium CD) and a resin cement (Rely XTM) and to evaluate the mode of fracture after testing, forty couples of metallic-alloy disks were melted, regularized, polished, submitted to four thermal cycles at 960ºC and divided casually in four groups. Each group received a type of different treatment: Group PSP: Polishing with sandpaper 600; Group PCP: Polishing with sandpaper 600 and application of a metallic Primer; Group JSP: Sandblaster with 100 m aluminum oxide; Group JCP: Sandblaster with 100 m aluminum oxide and application of a metallic Primer. The groups were cemented and stored in distilled water at 37ºC for 36 hours and submitted to shear strength test. The highest values were obtained by the sandblasted groups (JSP, JCP), independently of the primer application; the Alloy Primer increased the retention between the Rely X cement and the polished surface of the Co-Cr-Mo alloy, however its bond strength was not greater than that obtained by sandblasting; all of the specimens showed adhesive failures within the tested interface.

O objetivo deste trabalho foi avaliar a infiltração marginal de restaurações cervicais em função do fator de configuração cavitária (FC) e de quatro materiais restauradores estéticos. Cavidades convencionais com FC=5, e em forma de “pires” com FC<5 foram realizadas, respectivamente, nas faces distais e mesiais de 60 prémolares recém-extraídos. Para a primeira cavidade, utilizou-se uma ponta diamantada troncocônica com dimensões especiais (2,9 mm x 2,5 mm (base menor) x 1,5 mm de profundidade). A cavidade em forma de “pires” apresentou dimensões proporcionais ao diâmetro da ponta diamantada esférica n.3018 (2,9 mm) e, também, com profundidade de 1,5 mm, sendo que as margens das cavidades localizaram-se em esmalte e cemento/dentina. Os seguintes grupos foram estabelecidos: G1 (Z100/Single Bond-3M), G2 (Freedom/Stae–SDI), G3 (Vitremer/Primer–3M) e G4 (Durafill/Durafill Bond-Kulzer). Os sistemas restauradores foram aplicados conforme as orientações de cada fabricante. A termociclagem dos espécimes compreendeu 10 ciclos/dia nas temperaturas de 37ºC, 5ºC e 55ºC, com permanência de 1,5 minuto. Esses procedimentos foram repetidos pelo período de sete dias, totalizando 70 ciclos, sendo que no último dia a ciclagem foi feita em solução aquosa tamponada de azul de metileno a 2%. Em seguida os espécimes foram seccionados, fotografados em estereomicroscópio, com aumento de 16X, e depois avaliados por dois examinadores pela projeção das fotografias. Os valores foram submetidos à análise de Kruskal-Wallis a um critério, Dunn; Wilcoxon; e Friedman, Student-Newman-Keuls. As médias dos escores de infiltração observados na cavidade convencional e naquela em forma de “pires” foram, respectivamente: G1- 0,66 / 0,46; G2- 0,92 / 0,69; G3- 1,8 / 1,86; G4- 3,54 / 2,3. Portanto, o fator de configuração cavitária não exerceu, de maneira geral, influência significativa para os diferentes sistemas restauradores. Com exceção do sistema Durafill/Durafill Bond, que apresentou os maiores graus de infiltração marginal, os demais materiais comportaram-se de forma semelhante. / The aim of this work was to evaluate the cervical restorations marginal leakage in regard with the cavity configuration factor (CF) and four esthetic restorative materials. Conventional cervical cavities with CF=5 and other "Saucer"- like cavities with CF<5, were carried out on the distal and mesial surfaces, in 60 freshly extracted premolars. For the first cavity, a trunk-conic diamond bur with special dimensions (2.9mm x 2.5 mm x 1.5mm) was used. The "Saucer"-like cavity had dimensions proportional to the diamond bur diameter #3018 (2.9 mm), and the depth determined in 1.5 mm. The cavities margins were set either in cement/dentin or enamel. Some groups were established: G1 (Z100/Single Bond-3M), G2 (Freedom/Stae-SDI), G3 (Vitremer/Primer-3M) and G4 (Durafill/Durafill Bond). These restorative systems were used according to their manufacters' directions. The specimens were submitted to 10 cycles/day at the temperatures 37ºC, 5ºC and 55ºC, exposing the teeth to 1.5 minutes. Seven thermocyclings (7 days) were performed, totalizing 70 cycles, but at the last one, the thermocycling was done in 2% buffered methylene blue aqueous solution. The specimens were thereafter sectioned, photographed under a stereomicroscope at 16X magnification, and the obtained photographs were assessed by two trained examiners. The results were evaluated through the Kruskal-Wallis one way analysis, Dunn's multiple comparisons method; Wilcoxon; and Friedman, Student-Newman-Keuls methods. The means scores of the marginal leakage concerning the conventional cavity and the "Saucer"-like cavity, were respectively: G1- 0.66 / 0.46; G2- 0.92 / 0.69; G3- 1.8 / 1.86; G4- 3.54 / 2.3. Hence, the cavity configuration factor didn’t have, at all, a significant influence to the different restorative materials. Except for the Durafill/Durafill Bond system, that presented the greatest degrees of marginal leakage, the other restorative materials had the same behavior.

O objetivo deste trabalho foi avaliar a estabilidade dimensional das siliconas de condensação pesada e leve para moldagem odontológica, quando imersas em solução desinfetante por 10 e 20 minutos, relacionando a importância da biossegurança no manuseio destes materiais. Os materiais de moldagem testados foram: Optosil Confort e Xantopren VL Plus; e as soluções desinfetantes foram o hipoclorito de sódio a 1% (Solução de Milton) e o glutaraldeído a 2% (Glutaron II). Impressões foram obtidas através de moldeiras perfuradas de aço inoxidável, de acordo com a especificação n.º 19 da ADA, perfazendo um total de 50 moldagens, que foram executadas pela técnica em passo único, de acordo com as especificações do fabricante. Para assegurar a completa polimerização o material foi removido após 7 minutos e submetido à imersão nas soluções desinfetantes nos tempos determinados, sendo um grupo controle representado por moldes sem imersão. Depois de removidos das soluções, os corpos de prova foram lavados em água corrente por 15 segundos, secos e medidos 3 vezes cada para registro da média, usando um microscópio óptico, com precisão de 0,001 mm. A análise de variância a dois critérios, com nível de significância de 5%, mostrou que as diferenças nas dimensões lineares da silicona testada não são estatisticamente significantes (p>0,05) após sua imersão em solução de hipoclorito de sódio a 1% e glutaraldeído a 2% até 20 minutos. Os resultados indicaram que a combinação testada de material de moldagem e solução desinfetante pode seguramente ser empregada na clínica odontológica para o controle de infecção e segurança da equipe de saúde bucal. / The purpose of this study was to evaluate the dimensional stability of condensation silicone rubber heavy and light body after immersion in disinfectant solution for 10 or 20 minutes. The impression materials were Optosil Confort e Xantopren VL Plus and the disinfectants solutions were 1% sodium hypochlorite and 2% glutaraldehyde. Impressions were made on a perforated stainless steel tray, according to the American Dental Association specification No. 19, performed a total of 50 samples. The double mixing method (one time, two viscosities) was used. Impressions were removed from the roulette block after 7 minutes to ensure complete polymerization and then immersed in the solutions. Impressions with no treatment composed the control group. After these steps, impressions were taken out the solution and rinsed in running water and air dried. Three dimensional measurements were calculated, using an optic microscope graduated at 0,001 mm. The two- way ANOVA indicated no differences (p>0.05) for any combination between variables. The results have shown that the solution studied can be safety used to disinfect condensation silicon in clinical prosthodontic procedures.

Avaliou-se a resistência ao cisalhamento da união metalocerâmica, de três diferentes sistemas cerâmicos de uso odontológico (Ceramco, Noritake e Vita VMK-68) aplicados sobre uma liga de paládio-prata (Pors-on 4), utilizando-se para isto, forças de compressão. Utilizando-se a metodologia descrita por CHONG; BEECH; CHEM19, modificada por BATISTA7, foram confeccionados 30 padrões metálicos divididos em três grupos de dez espécimes, sob os quais foi aplicada a cerâmica. Para a confecção dos corpos de prova, aplicação da cerâmica e realização dos testes de cisalhamento, utilizou-se uma matriz de aço inoxidável, em formato cilíndrico, com uma perfuração central de tamanho predeterminado, obtendo-se assim, corpos de prova padronizados. Após a fundição os padrões metálicos foram jateados com óxido de alumínio 50µm e levados ao forno sem vácuo a 980ºC por dez minutos para a oxidação prévia. Recolocados novamente no interior da matriz, receberam duas camadas de cerâmica opaca e duas camadas de cerâmica de corpo. Em seguida foram realizados os testes de resistência ao cisalhamento em uma máquina de tração e compressão, utilizando-se uma célula de carga de 100Kgf e velocidade de 0,5mm/min. As médias dos valores de resistência de união obtidas foram de 28,212MPa para o sistema Ceramco, 28,963MPa para o Noritake e 24,110MPa para o Vita VMK-68. Quando submetidos à análise de variância a um critério, não foram observadas diferenças estatisticamente significantes, o que nos levou à conclusão de que todos os sistemas possuem uma características de união metalocerâmica satisfatórias quando utilizados em conjunto com a liga selecionada. Além disso, os resultados são semelhantes aos descritos na literatura e se encontram além das forças necessárias para provocar a falha dos mesmos. / The purpose of this study was to evaluate the bond strength of a palladium-silver alloy (Pors-on 4) to three ceramic systems (Ceramco, Noritake and Vita VMK-68) using shear forces at the metal-ceramic interface. The method used for the tests was that developed by CHONG, BEECH e CHEM19, modified by BATISTA7. A stainless steel cylindric matrix was used for preparation of the metal patterns, application of ceramic and to perform the shear tests. Thirty specimens were prepared consisting of a palladium-silver alloy cylinder with two layers of opaque porcelain covered by two layers of body porcelain. The shear tests were perfomed in a universal testing machine using a load cell of 100kgf at a cross head speed of 0,5mm/min. The mean shear strength values for the three ceramic systems were: 28.212MPa (Ceramco), 28.963MPa (Noritake) and 24.110MPa Vita VMK-68). No statistically significant diferences were found among the groups what led us to conclude that the three ceramic systems are suitable for use in combination with the selected alloy.