121 |
GaN:Gd - Ein verdünnter magnetischer Halbleiter? / GaN:Gd - A dilute magnetic semiconductor?Röver, Martin 18 October 2010 (has links)
No description available.
|
122 |
In situ- und online-Raman-Spektroskopie zur Analyse von Halbleiterheterostrukturen aus ZnSxSe1-x und Gruppe-III-NitridenSchneider, Andreas 31 May 2001 (has links)
In situ and online Raman spectroscopy - also known as Raman monitoring - offers the excellent opportunity among other possibilities for the evaluation of Raman spectra to investigate semiconductor layers during their growth without any interruption. Not only the surface properties of such layers can be studied, also simultaneously the substrate and the interface layer/substrate can be analysed.
This study presents the analysis of growth processes of ZnS/sub x/Se/sub(1-x)/ and GaN layers as well the investigation of nitrogen doped ZnSe:N. Molecular beam epitaxy (MBE) was used for the fabrication of these layers. The analysis of the Raman spectra was focused on the chemical composition of the semiconductor material, the stress in layer and substrate, the incorporation of extraneous atoms like nitrogen radicals into a crystal, the doping and structural order of the semiconductor and as well on the crystalline and amorphous phase of the material. Additionally to the MBE growth processes, the temperature induced resonant Raman scattering of ZnS/sub x/Se/sub(1-x)/ and ZnSe:N and also the desorption, adsorption and phase transition of a-As, a-Se and Sb were studied. Further investigations were undertaken on the nitridation of GaAs(100) by means of a nitrogen plasma generated in an rf-plasma source.
The properties and changes of the semiconductor layers and the substrate depending on the layer thickness during growth are evaluated. The results are compared with theoretical models (e.g. spatial correlation model and modified random-element-isodisplacement (MREI) model). / In situ- und online-Raman-Spektroskopie oder auch Raman-Monitoring genannt bietet unter anderem die ausgezeichnete Möglichkeit, das Wachstum von Halbleiterschichten ohne Unterbrechung zu verfolgen. Dabei können nicht nur die Oberflächeneigenschaften untersucht werden, sondern es können gleichzeitig auch Informationen über das Substrat und über die Grenzfläche Schicht/Substrat gemacht werden.
In der vorliegenden Arbeit wurden die Wachstumsprozesse von ZnS/sub x/Se/sub(1-x)/- und GaN-Schichten sowie des stickstoffdotierten ZnSe:N untersucht. Zur Schichtherstellung wurde die Molekularstrahlepitaxie (MBE) verwendet. Das Hauptaugenmerk wurde dabei auf die chemische Zusammensetzung der Halbleitermaterialien, Verspannungen von Schicht und Substrat, auf den Einbau von Fremdatomen wie Stickstoffradikale in ein Kristall, die Dotierung und die strukturelle Ordnung der Halbleiter sowie deren kristalline und amorphe Phase gerichtet. Neben den MBE-Wachstumsprozessen wurden temperaturinduzierte resonante Raman-Streuung an ZnS/sub x/Se/sub(1-x)/ und ZnSe:N sowie Desorptions-, Adsorptions- und Phasenübergänge von a-As, a-Se und Sb studiert. Die Nitridierung von GaAs(100) mittels eines Stickstoffplasmas aus einer rf-Quelle wurde ebenso untersucht.
Die Eigenschaften und Veränderungen der Halbleiterschichten und der Substrate während des Wachstums werden in Abhängigkeit von der Schichtdicke dargelegt. Die Ergebnisse werden mit entsprechenden theoretischen Modellen (z.B. Spatial-Correlation-Modell und Modified Random-Element-Isodisplacement (MREI)-Modell) verglichen.
|
123 |
Entwurf, Herstellung und Charakterisierung von GaN/AlGaN/GaN High Electron Mobility Transistoren für Leistungsanwendungen im GHz-BereichWächtler, Thomas 28 December 2005 (has links)
High Electron Mobility Transistoren (HEMTs),
basierend auf
dem Materialsystem GaN/AlGaN/GaN, wurden entworfen,
hergestellt und elektrisch charakterisiert.
Für das Maskendesign kam das CAD-Programm LasiCAD
zum Einsatz. Das Design umfasste bis zu sechs
Lithographieebenen.
Die Herstellung der Bauelemente geschah unter
Reinraumbedingungen und unter Nutzung einer
vorhandenen Technologie für Transistoren mit
kleiner Gate-Peripherie (Doppelgate-Transistoren),
die teilweise optimiert wurde. Daneben wurden
Prozesse zur Herstellung von Multifinger-HEMTs
entwickelt, wobei die Metallisierung der
Drainkontakte mittels Electroplating von Gold
vorgenommen wurde.
Zur elektrischen Charakterisierung der
Bauelemente wurden sowohl
Gleichstromcharakteristiken,
d.h. die Ausgangskennlinienfelder und
Verläufe der Steilheit, als auch das
Großsignalverhalten für cw-Betrieb bei 2 GHz
gemessen. Dabei zeigten die Transistoren
eine auf die Gatebreite bezogene
Ausgangsleistungsdichte
von mehr als 8 W/mm
und eine Effizienz größer als 40%,
einhergehend mit vernachlässigbarer
Drainstromdispersion der unpassivierten
Bauelemente.
|
124 |
Electronic Coupling Effects and Charge Transfer between Organic Molecules and Metal SurfacesForker, Roman 12 January 2010 (has links)
We employ a variant of optical absorption spectroscopy, namely in situ differential reflectance spectroscopy (DRS), for an analysis of the structure-properties relations of thin epitaxial organic films. Clear correlations between the spectra and the differently intense coupling to the respective substrates are found. While rather broad and almost structureless spectra are obtained for a quaterrylene (QT) monolayer on Au(111), the spectral shape resembles that of isolated molecules when QT is grown on graphite. We even achieve an efficient electronic decoupling from the subjacent Au(111) by inserting an atomically thin organic spacer layer consisting of hexa-peri-hexabenzocoronene (HBC) with a noticeably dissimilar electronic behavior. These observations are further consolidated by a systematic variation of the metal substrate (Au, Ag, and Al), ranging from inert to rather reactive. For this purpose, 3,4,9,10-perylenetetracarboxylic dianhydride (PTCDA) is chosen to ensure comparability of the molecular film structures on the different metals, and also because its electronic alignment on various metal surfaces has previously been studied with great intensity. We present evidence for ionized PTCDA at several interfaces and propose the charge transfer to be related to the electronic level alignment governed by interface dipole formation on the respective metals. / Zur Analyse der Struktur-Eigenschafts-Beziehungen dünner, epitaktischer Molekülfilme wird in situ differentielle Reflexionsspektroskopie (DRS) als Variante der optischen Absorptionsspektroskopie verwendet. Klare Zusammenhänge zwischen den Spektren und der unterschiedlich starken Kopplung zum jeweiligen Substrat werden gefunden. Während man breite und beinahe unstrukturierte Spektren für eine Quaterrylen (QT) Monolage auf Au(111) erhält, ist die spektrale Form von auf Graphit abgeschiedenem QT ähnlich der isolierter Moleküle. Durch Einfügen einer atomar dünnen organischen Zwischenschicht bestehend aus Hexa-peri-hexabenzocoronen (HBC) mit einem deutlich unterschiedlichen elektronischen Verhalten gelingt sogar eine effiziente elektronische Entkopplung vom darunter liegenden Au(111). Diese Ergebnisse werden durch systematische Variation der Metallsubstrate (Au, Ag und Al), welche von inert bis sehr reaktiv reichen, untermauert. Zu diesem Zweck wird 3,4,9,10-Perylentetracarbonsäuredianhydrid (PTCDA) gewählt, um Vergleichbarkeit der molekularen Filmstrukturen zu gewährleisten, und weil dessen elektronische Anordnung auf verschiedenen Metalloberflächen bereits eingehend untersucht worden ist. Wir weisen ionisiertes PTCDA an einigen dieser Grenzflächen nach und schlagen vor, dass der Ladungsübergang mit der elektronischen Niveauanpassung zusammenhängt, welche mit der Ausbildung von Grenzflächendipolen auf den entsprechenden Metallen einhergeht.
|
125 |
In-situ study of Ga2O3 thermal expansion and epitaxy by synchrotron based x-ray diffraction and reflection high-energy electron diffractionCheng, Zongzhe 26 August 2019 (has links)
Diese Arbeit präsentiert eine umfassende in-situ Studie zur thermischen Ausdehnung von β-Ga2O3 im Temperaturbereich von Raumtemperatur (RT) bis 1200 K sowie zum Wachstum dünner Ga2O3 Schichten durch plasmaunterstützte Molekularstrahlepitaxie (MBE). Hierfür kamen synchrotron-basierte hochauflösende Röntgenbeugung (HRXRD) sowie die Beugung hochenergetischer Elektronen bei Reflexion (RHEED) zum Einsatz. Die dadurch erhaltenen Resultate gestatten detaillierte quantitative Aussagen zu den Ausdehnungskoeffizienten (CTE) von β-Ga2O3 und ein tieferes Verständnis des Wachstumsprozesses von Ga2O3 sowohl im Rahmen der Homo- als auch der Heteroepitaxie. / This thesis presents a comprehensive in-situ study on the thermal expansion of beta-Ga2O3 from room temperature (RT) to 1200 K, and the thin film growth of Ga2O3 as carried out by oxygen plasma assisted molecular beam epitaxy (MBE) using synchrotron-based high-resolution x-ray diffraction (HRXRD) and reflection high-energy electron diffraction (RHEED). The obtained results provide a quantitative analysis on the coefficients of thermal expansion (CTE) of beta-Ga2O3, and a deeper understanding in the growth process of Ga2O3 in both homoepitaxy and heteroepitaxy.
|
126 |
Novel Methods for Controlled Self-Catalyzed Growth of GaAs Nanowires and GaAs/AlxGa1-xAs Axial Nanowire Heterostructures on Si Substrates by Molecular Beam EpitaxyTauchnitz, Tina 12 March 2020 (has links)
GaAs-based nanowires are attractive building blocks for the development of future (opto)electronic devices owing to their excellent intrinsic material properties, such as the direct band gap and high electron mobility. A pre-requisite for the implementation of novel functionalities on a single Si chip is the monolithic integration of the nanowires on the well-established Si complementary-metal-oxide-semiconductor (CMOS) platform with precise control of the nanowire growth process.
The self-catalyzed (Ga-assisted) growth of GaAs nanowires on Si(111) substrates using molecular beam epitaxy has offered the possibility to obtain vertical nanowires with predominant zinc blende structure, while potential contamination by external catalysts like Au is eliminated. Although the growth mechanism is fairly well understood, control of the nucleation stage, the nanowire number density and the crystal structure has been proven rather challenging. Moreover, conventional growth processes are typically performed at relatively high substrate temperatures in the range of 560-630 °C, which limit their application to the industrial Si platform.
This thesis provides two original methods in order to tackle the aforementioned challenges in the conventional growth processes. In the first part of this thesis, a simple surface modification procedure (SMP) for the in situ preparation of native-SiOx/Si(111) substrates has been developed. Using a pre-growth treatment of the substrates with Ga droplets and two annealing cycles, the SMP enables highly synchronized nucleation of all nanowires on their substrate and thus, the growth of exceptionally uniform GaAs nanowire ensembles with sub-Poissonian length distributions. Moreover, the nanowire number density can be tuned within three orders of magnitude and independent of the nanowire dimensions without prior ex situ patterning of the substrate. This work delivers a fundamental understanding of the nucleation kinetics of Ga droplets on native-SiOx and their interaction with SiOx, and confirms theoretical predictions about the so-called nucleation antibunching, the temporal anti-correlation of consecutive nucleation events.
In the second part of this thesis, an alternative method called droplet-confined alternate-pulsed epitaxy (DCAPE) for the self-catalyzed growth of GaAs nanowires and GaAs/AlxGa1-xAs axial nanowire heterostructures has been developed. DCAPE enables nanowire growth at unconventional, low temperatures in the range of 450-550 °C and is compatible with the standard Si-CMOS platform. The novel growth approach allows one to precisely control the crystal structure of the nanowires and, thus, to produce defect-free pure zinc blende GaAs-based nanowires. The strength of DCAPE is further highlighted by the controlled growth of GaAs/AlxGa1-xAs axial quantum well nanowires with abrupt interfaces and tunable thickness and Al-content of the AlxGa1-xAs sections. The GaAs/AlxGa1-xAs axial nanowire heterostructures are interesting for applications as single photon emitters with tunable emission wavelength, when they are overgrown with thick lattice-mismatched InxAl1-xAs layers in a core-shell fashion. All results presented in this thesis contribute to paving the way for a successful monolithic integration of
highly uniform GaAs-based nanowires with controlled number density, dimensions and crystal structure on the mature Si platform. / GaAs-basierte Nanodrähte sind attraktive Bausteine für die Entwicklung von zukünftigen (opto)elektronischen Bauelementen dank ihrer exzellenten intrinsischen Materialeigenschaften wie zum Beispiel die direkte Bandlücke und die hohe Elektronenbeweglichkeit. Eine Voraussetzung für die Realisierung neuer Funktionalitäten auf einem einzelnen Si Chip ist die monolithische Integration
der Nanodrähte auf der etablierten Si-Metall-Oxid-Halbleiter-Plattform (CMOS) mit
präziser Kontrolle des Wachstumsprozesses der Nanodrähte.
Das selbstkatalytische (Ga-unterstützte) Wachstum von GaAs Nanodrähten auf Si(111)-Substrat mittels Molekularstrahlepitaxie bietet die Möglichkeit vertikale Nanodrähte mit vorwiegend Zinkblende-Struktur herzustellen, während die potentielle Verunreinigung der Nanodrähte und des Substrats durch externe Katalysatoren wie Au vermieden wird. Obwohl der Wachstumsmechanismus gut verstanden ist, erweist sich die Kontrolle der Nukleationsphase, Anzahldichte und Kristallstruktur der Nanodrähte als sehr schwierig. Darüber hinaus sind relativ hohe Temperaturen im Bereich von 560-630 °C in konventionellen Wachstumsprozessen notwendig, die deren Anwendung auf der industriellen Si Plattform begrenzen.
Die vorliegende Arbeit liefert zwei originelle Methoden um die bestehenden Herausforderungen in konventionellen Wachstumsprozessen zu bewältigen. Im ersten Teil dieser Arbeit wurde eine einfache Prozedur, bezeichnet als surface modification procedure (SMP), für die in situ Vorbehandlung von nativem-SiOx/Si(111)-Substrat entwickelt. Die Substratvorbehandlung mit Ga-Tröpfchen und zwei Hochtemperaturschritten vor dem Wachstumsprozess ermöglicht eine synchronisierte Nukleation aller Nanodrähte auf ihrem Substrat und folglich das Wachstum von sehr gleichförmigen GaAs Nanodraht-Ensembles mit einer sub-Poisson Verteilung der Nanodrahtlängen. Des Weiteren kann die Anzahldichte der Nanodrähte unabhängig von deren Abmessungen und ohne ex situ Vorstrukturierung des Substrats über drei Größenordnungen eingestellt werden. Diese Arbeit liefert außerdem ein grundlegendes Verständnis zur Nukleationskinetik von Ga-Tröpfchen auf nativem-SiOx und deren Wechselwirkung mit SiOx und bestätigt theoretische Voraussagen zum sogenannten Nukleations-Antibunching, dem Auftreten einer zeitlichen Anti-Korrelation aufeinanderfolgender Nukleationsereignisse.
Im zweiten Teil dieser Arbeit wurde eine alternative Methode, bezeichnet als droplet-confined alternate-pulsed epitaxy (DCAPE), für das selbstkatalytische Wachstum von GaAs Nanodrähten und GaAs/AlxGa1-xAs axialen Nanodraht-Heterostrukturen entwickelt. DCAPE ermöglicht das Nanodrahtwachstum bei unkonventionell geringeren Temperaturen im Bereich von 450-550 °C und ist vollständig kompatibel mit der Standard-Si-CMOS-Plattform. Der neue Wachstumsansatz erlaubt eine präzise Kontrolle der Kristallstruktur der Nanodrähte und folglich das Wachstum
von defektfreien Nanodrähten mit phasenreiner Zinkblende-Struktur. Die Stärke der DCAPE Methode wird des Weiteren durch das kontrollierte Wachstum von GaAs/AlxGa1-xAs axialen Quantentopf-Nanodrähten mit abrupten Grenzflächen und einstellbarer Dicke und Al-Anteil der AlxGa1-xAs-Segmente aufgezeigt. Die GaAs/AlxGa1-xAs axialen Nanodraht-Heterostrukturen sind interessant für den Einsatz als Einzelphotonen-Emitter mit einstellbarer Emissionswellenlänge, wenn diese mit gitterfehlangepassten InxAl1-xAs-Schichten in einer Kern-Hülle-Konfiguration überwachsen werden. Alle Ergebnisse dieser Arbeit tragen dazu bei, den Weg für eine erfolgreiche monolithische Integration von sehr gleichförmigen GaAs-basierten Nanodrähten mit kontrollierbarer Anzahldichte, Abmessungen und Kristallstruktur auf der industriell etablierten Si-Plattform zu ebnen.
|
127 |
From 2D CoCrPt:SiO2 films with perpendicular magnetic anisotropy to 3D nanocones — A step towards bit patterned media —Ball, David Klaus 02 July 2013 (has links) (PDF)
Due to the ever-increasing worldwide consumption of memory for digital information, new technologies for higher capacity and faster data storage systems have been the focus of research and development. A step towards achieving higher data storage densities or magnetic recording media is the concept of bit patterned media, where the magnetic recording layer is divided up into magnetically isolated bit units. This approach is one of the most promising technologies for increasing data storage densities and could be implemented by nanostructuring the wafer. Therefore, the fabrication of the appropriate nanostructures on a small scale and then be able to manufacture these structures on an industrial scale is one of the problems where science and industry are working on a solution. In addition, the answer to the open question about the influence that patterning on the nano length scale has on the magnetic properties is of great interest.
The main goal of this thesis is to answer the open question, which magnetic properties can be tailored by a modification of the surface texture on the nanometre length scale. For this purpose the following properties: anisotropy, remanence, coercivity, switching field distribution, saturation magnetisation, Gilbert damping, and inhomogeneous linebroadening were compared between planar two dimensional thin ferromagnetic films and three dimensional magnetic structures. In addition, the influences of the tailored morphology on the intergranular or the exchange coupling between the structures, which is called interdot exchange coupling, was investigated. For the ferromagnetic thin films, the focus of the investigations was on the granular CoCrPt:SiO2 and [Co/Pd] layer, which currently are the state-of-the-art material for magnetic data storage media. These materials are characterised by their high coercivity and high perpendicular anisotropy, which has a low spatial distribution in the preferred direction of magnetisation.
In this work the pre-structured GaSb(001) substrate with self-assembled periodic nanocone structures at the surface are used. The preparation by ion beam erosion of these structures is simple, fast, and highly reproducible and therefore this method is particularly beneficial for fundamental research. To compare the 2D thin films with the 3D magnetic structures, besides the pre-structured specimen, planar samples were also fabricated. The first sample series prepared was coated by Py. Due to the fact that the magnetic properties of this material are well-known, it was also possible to do some OOMMF simulations in addition to the VNA-FMR and MOKE measurements.
Afterwards two planar samples with CoCrPt and CoCrPt:SiO2 were prepared. The planar CoCrPt:SiO2 samples were Co+ ion implanted to study the influence of such irradiation on the intergranular and interdot exchange coupling, switching field distribution, and in particular on the spin dynamics. Moreover, both samples were measured by TRMOKE in order to obtain information about the spin dynamics.
Subsequently, the perpendicular storage media materials CoCrPt:SiO2 and [Co/Pd] were deposited on a prestructured GaSb(001) nanocone substrate surface. These sample series were measured by MOKE, SQUID, and vector-VSM. The measurements demonstrate the influence of the periodicity and height of the nanocones on the intergranular and interdot exchange coupling. They also show the reorientation of the magnetisation with respect to the curvature of the substrate template and furthermore, the morphology-induced influences on the magnetic domains.
From the comparison between the results for the planar and the pre-structured samples, a decrease of the interdot exchange coupling was observed, which scales together with the periodicity of the nanocone pattern. In addition, it was shown that for all samples with thin magnetic films on nanocones,the magnetisation aligns along the curvature of the underlying nanocone structure. For Py on nanocones, planar granular CoCrPt:SiO2, and planar granular CoCrPt, measurements by VNA-FMR and TRMOKE could be carried out, which yielded information about the spin dynamics. The results obtained for both of the planar sample are comparable to values from the literature for the Gilbert damping. The results for the Py samples showed that the commonly used 2D model resonance condition is, in case of a 3D magnetic structure, no longer valid due to the alignment of the magnetisation along the underlying substrate structure and therefore an new model has to be derived. / Aufgrund des weltweiten, immer weiter steigenden Bedarfs an Speicherplatz von digitalen Information, sind neue Technologien für größere und schnellere Speichermedien im Fokus von Forschung und Entwicklung. Ein Schritt hin zu einer höheren Speicherdichte in der magnetischen Datenspeicherung ist dabei das sogenannte Konzept der ”Bit patterned media”, das definierte Informationseinheiten auf regelmäßig angeordneten Nanostrukturen beschreibt. Dieser Ansatz ist einer der derzeit vielversprechendsten Optionen die Speicherdichte zu erhöhen. Dabei ist die Herstellung der benötigten Nanostrukturen und deren Skalierung hin zu makroskopischen Dimensionen eines der Probleme an deren Lösung die Wissenschaft und Industrie derzeit
arbeitet. Desweiteren ist die Antwort auf die noch offene Frage nach der Beeinflussung der nanoskaligen Strukturen auf die magnetischen Eigenschaften von großem Interesse.
Das Hauptziel in dieser Arbeit ist es, einen Beitrag zur Beantwortung der Frage, welche magnetischen Eigenschaften sich durch eine Veränderung der Oberflächenstruktur im Nanometerbereich beeinflussen lassen, zu leisten. Hierzu wurden die folgenden Eigenschaften, wie zum Beispiel die Anisotropie, Remanenz,Koerzitivität, Schaltfeldverteilung, Sättigungsmagnetisierung, Gilbertdämpfung und inhomogene Linienverbreiterung von planaren zweidimensionalen dünnen ferromagnetische Schichten mit denen von dreidimensionalen magnetischen Strukturen verglichen. Zusätzlich wurde der Einfluss der angegpassten Morphologie auf die intergranularen- beziehungsweise auf die zwischen den Strukturen wirkende (interdot) Austauschkopplung untersucht. Der Hauptaugenmerk bei den ferromagnetisch dünnen Schichten lag dabei auf den granularen CoCrPt:SiO2 und [Co/Pd] Filmen, die heutzutage ein Standardmaterial für die magnetischen Speichermedien darstellen. Diese Materialien zeichnen sich durch eine hohe Koerzivität und senkrechte Anisotropie, mit geringer räumlicher Verteilung der Vorzugsrichtung der Magnetisierung, aus.
Die hier vorgestellten vorstrukturierten GaSb(001) Substrate mit selbstordnenden periodischen Nanokegeln auf der Oberfläche, sind mittels Ionenstrahlerosion einfach, schnell und sehr gut reproduzierbar herzustellen. Deshalb ist diese Methode besonders für die Grundlagenforschung von Vorteil. Um einen Vergleich zwischen 2D Filmen und 3D Strukturen ziehen zu können, wurden neben den vorstrukturierten Substraten auch planare Proben beschichtet. Eine erste Versuchsreihe wurde mit einem dünnen Py Film präpariert. Da dessen magnetische Eigenschaften wohlbekannt sind, konnten neben den Untersuchungen mit VNA-FMR und MOKE auch einige OOMF Simulationen erstellt werden.
Danach wurden zwei Proben mit planarem CoCrPt beziehungsweise CoCrPt:SiO2 untersucht. Bei den planaren CoCrPt:SiO2 Proben wurden außerdem noch Co+ Ionen implantiert, um deren Auswirkungen auf die intergranulare Austauschkopplung, Schaltfeldverteilung und besonders auf die Spindynamik zu bestimmen. Bei beiden Probensystemen konnte zusätzlich die Spindynamik mittels zeitaufgelöstem MOKE gemessen werden.
Im Anschluss wurden die beiden senkrechten Speichermedien CoCrPt:SiO2 and [Co/Pd] auf Substraten mit Nanokegeln vorstrukturierten GaSb(001) Oberflächen abgeschieden. Diese Proben wurden mit MFM, MOKE, SQUID und Vektor-VSM vermessen. Aus den Messungen konnnten dann die Einflüsse auf die intergranulare- beziehungsweise interdot Austauschkopplung in Abhängigkeit von der Periodizität und Höhe der Nanokegel bestimmt werden, sowie die Umorientierung der Magnetisierung bezüglich der Substratkrümmung und den Morphologie induzierten Einfluss auf die magnetischen Domänen.
Anhand der Vergleiche zwischen den Messungen der planaren und den vorstrukturierten Proben konnte eine Verringerung der Austauschkopplung zwischen den Strukturen gezeigt werden, die mit der Nanokegelstrukturperiodizität skaliert. Außerdem wurde in allen dünnen magnetischen Filmen auf Nanokegeln gezeigt, dass die Magnetisierung sich in Abhängigkeit der darunterliegenden Struktur ausrichtet. Bei den Py auf Nanokegeln, den planaren CoCrPt und dem planaren CoCrPt:SiO2 Proben konnten außerdem mit VNA-FMR und TRMOKE Informationen bezüglich der Spindynamik gemessen werden. Die erzielten Ergebnisse, der beiden planaren Proben, sind vergleichbar mit denen, aus der Literatur bekannten Werten, für die Gilbertdämpfung. Darüber hinaus wurde durch die Messungen an den Py Proben gezeigt, dass die Theorie, des bisher genutzten 2D Modells, nicht mehr gültig ist, da sich die Magnetisierung entlang der Substratstruktur ausrichtet, und deshalb ein neues Model aufgestellt werden muss.
|
128 |
From 2D CoCrPt:SiO2 films with perpendicular magnetic anisotropy to 3D nanocones — A step towards bit patterned media —Ball, David Klaus 19 April 2013 (has links)
Due to the ever-increasing worldwide consumption of memory for digital information, new technologies for higher capacity and faster data storage systems have been the focus of research and development. A step towards achieving higher data storage densities or magnetic recording media is the concept of bit patterned media, where the magnetic recording layer is divided up into magnetically isolated bit units. This approach is one of the most promising technologies for increasing data storage densities and could be implemented by nanostructuring the wafer. Therefore, the fabrication of the appropriate nanostructures on a small scale and then be able to manufacture these structures on an industrial scale is one of the problems where science and industry are working on a solution. In addition, the answer to the open question about the influence that patterning on the nano length scale has on the magnetic properties is of great interest.
The main goal of this thesis is to answer the open question, which magnetic properties can be tailored by a modification of the surface texture on the nanometre length scale. For this purpose the following properties: anisotropy, remanence, coercivity, switching field distribution, saturation magnetisation, Gilbert damping, and inhomogeneous linebroadening were compared between planar two dimensional thin ferromagnetic films and three dimensional magnetic structures. In addition, the influences of the tailored morphology on the intergranular or the exchange coupling between the structures, which is called interdot exchange coupling, was investigated. For the ferromagnetic thin films, the focus of the investigations was on the granular CoCrPt:SiO2 and [Co/Pd] layer, which currently are the state-of-the-art material for magnetic data storage media. These materials are characterised by their high coercivity and high perpendicular anisotropy, which has a low spatial distribution in the preferred direction of magnetisation.
In this work the pre-structured GaSb(001) substrate with self-assembled periodic nanocone structures at the surface are used. The preparation by ion beam erosion of these structures is simple, fast, and highly reproducible and therefore this method is particularly beneficial for fundamental research. To compare the 2D thin films with the 3D magnetic structures, besides the pre-structured specimen, planar samples were also fabricated. The first sample series prepared was coated by Py. Due to the fact that the magnetic properties of this material are well-known, it was also possible to do some OOMMF simulations in addition to the VNA-FMR and MOKE measurements.
Afterwards two planar samples with CoCrPt and CoCrPt:SiO2 were prepared. The planar CoCrPt:SiO2 samples were Co+ ion implanted to study the influence of such irradiation on the intergranular and interdot exchange coupling, switching field distribution, and in particular on the spin dynamics. Moreover, both samples were measured by TRMOKE in order to obtain information about the spin dynamics.
Subsequently, the perpendicular storage media materials CoCrPt:SiO2 and [Co/Pd] were deposited on a prestructured GaSb(001) nanocone substrate surface. These sample series were measured by MOKE, SQUID, and vector-VSM. The measurements demonstrate the influence of the periodicity and height of the nanocones on the intergranular and interdot exchange coupling. They also show the reorientation of the magnetisation with respect to the curvature of the substrate template and furthermore, the morphology-induced influences on the magnetic domains.
From the comparison between the results for the planar and the pre-structured samples, a decrease of the interdot exchange coupling was observed, which scales together with the periodicity of the nanocone pattern. In addition, it was shown that for all samples with thin magnetic films on nanocones,the magnetisation aligns along the curvature of the underlying nanocone structure. For Py on nanocones, planar granular CoCrPt:SiO2, and planar granular CoCrPt, measurements by VNA-FMR and TRMOKE could be carried out, which yielded information about the spin dynamics. The results obtained for both of the planar sample are comparable to values from the literature for the Gilbert damping. The results for the Py samples showed that the commonly used 2D model resonance condition is, in case of a 3D magnetic structure, no longer valid due to the alignment of the magnetisation along the underlying substrate structure and therefore an new model has to be derived. / Aufgrund des weltweiten, immer weiter steigenden Bedarfs an Speicherplatz von digitalen Information, sind neue Technologien für größere und schnellere Speichermedien im Fokus von Forschung und Entwicklung. Ein Schritt hin zu einer höheren Speicherdichte in der magnetischen Datenspeicherung ist dabei das sogenannte Konzept der ”Bit patterned media”, das definierte Informationseinheiten auf regelmäßig angeordneten Nanostrukturen beschreibt. Dieser Ansatz ist einer der derzeit vielversprechendsten Optionen die Speicherdichte zu erhöhen. Dabei ist die Herstellung der benötigten Nanostrukturen und deren Skalierung hin zu makroskopischen Dimensionen eines der Probleme an deren Lösung die Wissenschaft und Industrie derzeit
arbeitet. Desweiteren ist die Antwort auf die noch offene Frage nach der Beeinflussung der nanoskaligen Strukturen auf die magnetischen Eigenschaften von großem Interesse.
Das Hauptziel in dieser Arbeit ist es, einen Beitrag zur Beantwortung der Frage, welche magnetischen Eigenschaften sich durch eine Veränderung der Oberflächenstruktur im Nanometerbereich beeinflussen lassen, zu leisten. Hierzu wurden die folgenden Eigenschaften, wie zum Beispiel die Anisotropie, Remanenz,Koerzitivität, Schaltfeldverteilung, Sättigungsmagnetisierung, Gilbertdämpfung und inhomogene Linienverbreiterung von planaren zweidimensionalen dünnen ferromagnetische Schichten mit denen von dreidimensionalen magnetischen Strukturen verglichen. Zusätzlich wurde der Einfluss der angegpassten Morphologie auf die intergranularen- beziehungsweise auf die zwischen den Strukturen wirkende (interdot) Austauschkopplung untersucht. Der Hauptaugenmerk bei den ferromagnetisch dünnen Schichten lag dabei auf den granularen CoCrPt:SiO2 und [Co/Pd] Filmen, die heutzutage ein Standardmaterial für die magnetischen Speichermedien darstellen. Diese Materialien zeichnen sich durch eine hohe Koerzivität und senkrechte Anisotropie, mit geringer räumlicher Verteilung der Vorzugsrichtung der Magnetisierung, aus.
Die hier vorgestellten vorstrukturierten GaSb(001) Substrate mit selbstordnenden periodischen Nanokegeln auf der Oberfläche, sind mittels Ionenstrahlerosion einfach, schnell und sehr gut reproduzierbar herzustellen. Deshalb ist diese Methode besonders für die Grundlagenforschung von Vorteil. Um einen Vergleich zwischen 2D Filmen und 3D Strukturen ziehen zu können, wurden neben den vorstrukturierten Substraten auch planare Proben beschichtet. Eine erste Versuchsreihe wurde mit einem dünnen Py Film präpariert. Da dessen magnetische Eigenschaften wohlbekannt sind, konnten neben den Untersuchungen mit VNA-FMR und MOKE auch einige OOMF Simulationen erstellt werden.
Danach wurden zwei Proben mit planarem CoCrPt beziehungsweise CoCrPt:SiO2 untersucht. Bei den planaren CoCrPt:SiO2 Proben wurden außerdem noch Co+ Ionen implantiert, um deren Auswirkungen auf die intergranulare Austauschkopplung, Schaltfeldverteilung und besonders auf die Spindynamik zu bestimmen. Bei beiden Probensystemen konnte zusätzlich die Spindynamik mittels zeitaufgelöstem MOKE gemessen werden.
Im Anschluss wurden die beiden senkrechten Speichermedien CoCrPt:SiO2 and [Co/Pd] auf Substraten mit Nanokegeln vorstrukturierten GaSb(001) Oberflächen abgeschieden. Diese Proben wurden mit MFM, MOKE, SQUID und Vektor-VSM vermessen. Aus den Messungen konnnten dann die Einflüsse auf die intergranulare- beziehungsweise interdot Austauschkopplung in Abhängigkeit von der Periodizität und Höhe der Nanokegel bestimmt werden, sowie die Umorientierung der Magnetisierung bezüglich der Substratkrümmung und den Morphologie induzierten Einfluss auf die magnetischen Domänen.
Anhand der Vergleiche zwischen den Messungen der planaren und den vorstrukturierten Proben konnte eine Verringerung der Austauschkopplung zwischen den Strukturen gezeigt werden, die mit der Nanokegelstrukturperiodizität skaliert. Außerdem wurde in allen dünnen magnetischen Filmen auf Nanokegeln gezeigt, dass die Magnetisierung sich in Abhängigkeit der darunterliegenden Struktur ausrichtet. Bei den Py auf Nanokegeln, den planaren CoCrPt und dem planaren CoCrPt:SiO2 Proben konnten außerdem mit VNA-FMR und TRMOKE Informationen bezüglich der Spindynamik gemessen werden. Die erzielten Ergebnisse, der beiden planaren Proben, sind vergleichbar mit denen, aus der Literatur bekannten Werten, für die Gilbertdämpfung. Darüber hinaus wurde durch die Messungen an den Py Proben gezeigt, dass die Theorie, des bisher genutzten 2D Modells, nicht mehr gültig ist, da sich die Magnetisierung entlang der Substratstruktur ausrichtet, und deshalb ein neues Model aufgestellt werden muss.
|
129 |
Ferromagnetic thin films of Fe and Fe 3 Si on low-symmetric GaAs(113)A substratesMuduli, Pranaba Kishor 24 April 2006 (has links)
In dieser Arbeit werden das Wachstum mittels Molekularstrahlepitaxie und die Eigenschaften der Ferromagneten Fe und Fe_3Si auf niedrig-symmetirschen GaAs(113)A-Substraten studiert. Drei wichtige Aspekte werden untersucht: (i) Wachstum und strukturelle Charakterisierung, (ii) magnetische Eigenschaften und (iii) Magnetotransporteigenschaften der Fe und Fe_3Si Schichten auf GaAs(113)A-Substraten. Das Wachstum der Fe- und Fe_3Si-Schichten wurde bei einer Wachstumstemperatur von = bzw. 250 °C optimiert. Bei diesen Wachstumstemperaturen zeigen die Schichten eine hohe Kristallperfektion und glatte Grenz- und Oberflächen analog zu [001]-orientierten Schichten. Weiterhin wurde die Stabilität der Fe_(3+x)Si_(1-x) Phase über einen weiten Kompositionsbereich innerhalb der Fe_3Si-Stoichiometry demonstriert. Die Abhängigkeit der magnetischen Anisotropie innerhalb der Schichtebene von der Schichtdicke weist zwei Bereiche auf: einen Beresich mit dominanter uniaxialer Anisotropie für Fe-Schichten = 70 MLs. Weiterhin wird eine magnetische Anisotropie senkrecht zur Schichtebene in sehr dünnen Schichten gefunden. Der Grenzflächenbeitrag sowohl der uniaxialen als auch der senkrechten Anisotropiekonstanten, die aus der Dickenabhängigkeit bestimmt wurden, sind unabhängig von der [113]-Orientierung und eine inhärente Eigenschaft der Fe/GaAs-Grenzfläche. Die anisotrope Bindungskonfiguration zwischen den Fe und den As- oder Ga-Atomen an der Grenzfläche wird als Ursache für die uniaxiale magnetische Anisotropie betrachtet. Die magnetische Anisotropie der Fe_3Si-Schichten auf GaAs(113)A-Substraten zeigt ein komplexe Abhängigkeit von der Wachstumsbedingungen und der Komposition der Schichten. In den Magnetotransportuntersuchungen tritt sowohl in Fe(113)- als auch in Fe_3Si(113)-Schichten eine antisymmetrische Komponente (ASC) im planaren Hall-Effekt (PHE) auf. Ein phänomenologisches Modell, dass auf der Kristallsymmetrie basiert, liefert ein gute Beschreibung sowohl der ASC im PHE als auch des symmetrischen, anisotropen Magnetowiderstandes. Das Modell zeigt, dass die beobachtete ASC als Hall-Effekt zweiter Ordnung beschreiben werden kann. / In this work, the molecular-beam epitaxial growth and properties of ferromagnets, namely Fe and Fe_3Si are studied on low-symmetric GaAs(113)A substrates. Three important aspects are investigated: (i) growth and structural characterization, (ii) magnetic properties, and (iii) magnetotransport properties of Fe and Fe_3Si films on GaAs(113)A substrates. The growth of Fe and Fe_3Si films is optimized at growth temperatures of 0 and 250 degree Celsius, respectively, where the layers exhibit high crystal quality and a smooth interface/surface similar to the [001]-oriented films. The stability of Fe_(3+x)Si_(1-x) phase over a range of composition around the Fe_3Si stoichiometry is also demonstrated. The evolution of the in-plane magnetic anisotropy with film thickness exhibits two regions: a uniaxial magnetic anisotropy (UMA) for Fe film thicknesses = 70 MLs. The existence of an out-of-plane perpendicular magnetic anisotropy is also detected in ultrathin Fe films. The interfacial contribution of both the uniaxial and the perpendicular anisotropy constants, derived from the thickness-dependent study, are found to be independent of the [113] orientation and are hence an inherent property of the Fe/GaAs interface. The origin of the UMA is attributed to anisotropic bonding between Fe and As or Ga at the interface, similarly to Fe/GaAs(001). The magnetic anisotropy in Fe_3Si on GaAs(113)A exhibits a complex dependence on the growth conditions and composition. Magnetotransport measurements of both Fe(113) and Fe_3Si(113) films shows the striking appearance of an antisymmetric component (ASC) in the planar Hall effect (PHE). A phenomenological model based on the symmetry of the crystal provides a good explanation to both the ASC in the PHE as well as the symmetric anisotropic magnetoresistance. The model shows that the observed ASC component can be ascribed to a second-order Hall effect.
|