Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico. Programa de Pós-Graduação em Engenharia Civil / Made available in DSpace on 2012-10-21T04:22:19Z (GMT). No. of bitstreams: 0

Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico. Programa de Pós-Graduação em Engenharia Mecânica. / Made available in DSpace on 2012-10-21T11:14:41Z (GMT). No. of bitstreams: 1 229663.pdf: 4936213 bytes, checksum: fb1d37f31d7e3b1a0bdf2b007ba4a0ff (MD5) / Neste trabalho são apresentados dois modelos para análise plana de materiais em regime elasto-plástico. Um modelo é chamado de plasticidade J2 baseado na teoria de vonMises com dano isotrópico para análise do comportamento plástico de metais, e o outro modelo, chamado de "Cap" Suave, é baseado nas teorias de Drucker-Prager e Mohr-Coulomb para análise do comportamento de solos. Todas análises e conceitos desenvolvidos são averiguados no âmbito de carregamentos monotônicos. No modelo J2 pode-se avaliar com maior rigor o fenômeno plástico que ocorre nos metais. Dessa forma, torna-se possível avaliar o comportamento material e estrutural de componentes mecânicos que sofrem efeitos de concentração de tensão devidos a: alterações em sua geometria, alterações nas propriedades elásticas ou cargas concentradas. Além do mais, nesse modelo é também implementada uma teoria capaz de analisar o fenômeno do dano, que permite identificar valores de tensões de ruptura do material. A teoria de dano utilizada é fundamentada dentro do enfoque da termodinâmica dos processos irreversíveis e foi desenvolvida basicamente por Lemaitre (1992). No modelo de "Cap" Suave o objetivo principal é avaliar o comportamento de solos, tais como: areias, siltes e argilas. O interesse nesse tipo de avaliação é importante na elaboração de projetos de fundações em geral, principalmente para se estimar capacidades de carga de fundações rasas e na análise de estabilidade de taludes. A resolução dos problemas formulados comesses modelos de plasticidade é incremental, e utiliza um algoritmo da classe de mapeamento de retorno para integrar as equações elasto-plásticas. Como o problema torna-se não linear devido a decomposição aditiva da deformação - problemas de pequena deformação -, faz-se uso também do método de Newton-Raphson para solução do conjunto de equações não lineares locais e globais. Na discretização do domínio sólido o método de elementos finitos é utilizado com um elemento finito quadrático triangular de 6 nós. São mostrados alguns exemplos em estados planos de tensão, deformação e axissimétrico para validação dos modelos plásticos: " Para o modelo J2 com dano isotrópico, exemplos como: placa com furo (EPT), placa em flexão (EPD) e eixo cilídrico chanfrado (Axis). " Para o "Cap"Suave são apresentadas fundações rasas em sapata rígida (EPD) e em sapata rígida circular (Axis), contemplando solos arenosos à argilosos.

Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico. Programa de Pós-Graduação em Engenharia Civil. / Made available in DSpace on 2012-10-21T13:54:11Z (GMT). No. of bitstreams: 1 207429.pdf: 2535632 bytes, checksum: 69ac83398fb4fc69a05e3cc357d87331 (MD5)

Tese (doutorado) - Universidade Federal de Santa Catarina, Centro de Ciências Físicas e Matemáticas. Programa de Pós-Graduação em Física. / Made available in DSpace on 2012-10-21T18:18:03Z (GMT). No. of bitstreams: 1 207726.pdf: 3525171 bytes, checksum: e6dbf258853a53ea14f7a66fa361e8e7 (MD5) / Este trabalho, desenvolvido na maior parte no Laboratório de Filmes Finos e Superfícies (LFFS), teve como objetivo principal a preparação e caracterização de ligas amorfas de CoP eletrodepositadas. O trabalho consiste de proposta inserida no cenário atual de pesquisas, aliando o estudo dos conceitos básicos da física com desenvolvimento de novos materiais e métodos de produção compatíveis com o mercado de novas tecnologias. Durante o trabalho foram produzidos filmes amorfos de CoP, por eletrodeposição, utilizando diferentes tipos de substratos: lâminas de Si (100) do tipo-n com ou sem uma camada tampão de CuNi; lâminas ou fios de Cu; e ainda camadas de Au/Cr e Cu/Au/Cr depositadas sobre vidro. A caracterização estrutural, morfológica e magnética das ligas foi realizada através de diferentes técnicas experimentais, sendo estas, difração de raios X, microscopia eletrônica de varredura, espectroscopia por espalhamento de energia (EDS) e de retroespalhamento Rutherford (RBS), magnetometria de gradiente de força e de efeito Kerr magneto-ótico, e ainda medidas de magnetoimpedância gigante (GMI). A topografia foi estudada através de imagens obtidas por microscopia de ponta de prova e cálculo da rugosidade superficial.

Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico. Programa de Pós-Graduação em Engenharia Civil. / Made available in DSpace on 2012-10-20T15:39:19Z (GMT). No. of bitstreams: 1 221523.pdf: 2848087 bytes, checksum: 8b5db4205171611315a2ab31260cab27 (MD5) / Com a crescente escassez das peças de madeira maciça de grandes dimensões, a utilização de madeira reconstituída é uma tendência atual, e, dentro deste contexto, as chapas de lascas orientadas, conhecidas por OSB (Oriented Strand Board), destacam-se pelas suas características mecânicas e preço competitivo, podendo ser utilizadas em diversas aplicações na construção civil, tais como: fechamento de paredes, contrapiso, forro de cobertura, vigas I, fôrmas para concreto armado, reforço de estruturas, bem como na fabricação de móveis. Apesar da sua utilização estar amplamente difundida na maioria dos países do hemisfério norte, ainda é um material novo no Brasil, uma vez que a produção de chapas OSB no país é recente. Sendo assim, é de fundamental importância a avaliação do comportamento deste material quando empregado em componentes estruturais. Neste trabalho, estudou-se o comportamento de vigas I submetidas a ensaio de flexão a 4 pontos, considerando a alma em OSB e as mesas em Pinus maciço. Paralelamente à análise experimental realizou-se a modelagem das vigas pelo Método de Elementos Finitos analisadas através do programa SAP2000, utilizando-se elementos sólidos de 8 nós, e uma análise teórica através do método da homogeneização da seção. Ao final do trabalho comparam-se os resultados obtidos a partir das análises experimental, numérica e teórica e são extraídas algumas conclusões e recomendações para trabalhos futuros.

Tese (doutorado) - Universidade Federal de Santa Catarina, Centro de Ciênicas Físicas e Matemáticas. Programa de Pós-Graduação em Química. / Made available in DSpace on 2012-10-19T03:08:59Z (GMT). No. of bitstreams: 0Bitstream added on 2014-09-25T20:31:09Z : No. of bitstreams: 1 184724.pdf: 2199939 bytes, checksum: 2f5d65a47993529117b6cdd6b8b23245 (MD5) / Quatro poliamidas foram sintetizadas por policondensação homogênea em 1,4-dioxano a partir do ácido 1,1'-ferrocenilmetanoico e etilenodiamina, 1,6-hexanodiamina, dietilenotriamina e trietilenotetramina. O tempo e temperatura de reação foram diferentes e específicos. Os resultados obtidos por este método, foram comparados com os das policondensações em m-xileno a partir do 1,1'-bis(clorocarbonil)ferroceno nas mesmas condições reacionais, e com policondensação heterogênea em benzeno-água a 25 °C. Os produtos isolados foram caracterizados por FTIR, RMN 1H e análise elementar de CHN. As policondensações homogêneas apresentaram melhores rendimentos de reação, particularmente para as reações com Fc(COOH)2 em 1,4-dioxano. As propriedades térmicas e mecanismo de decomposição dos derivados de ferroceno e poliamidas foram investigados através de técnicas termoanalíticas (DSC e TG/DTG) e FTIR. Os resultados mostraram temperaturas de fusão das poliamidas próximas a 200 °C. Para os precursores de reação, as curvas TG/DTG e os valores de Ea (faixa de 50-215 kJ mol-1) mostraram claramente que a estabilidade térmica obedece a ordem: Fc<FcCOOH<Fc(COOH)2. Para as poliamidas estudadas os valores de Ea na faixa de 50-400 kJ mol-1 sugerem mecanismos de decomposição do tipo randômico. O aquecimento das poliamidas a 350 °C por 1 hora, levou a uma completa decomposição das amostras com a formação de Fe2O3, independendo da atmosfera utilizada.

Made available in DSpace on 2014-06-11T19:32:50Z (GMT). No. of bitstreams: 0 Previous issue date: 2012-10-03Bitstream added on 2014-06-13T21:04:59Z : No. of bitstreams: 1 faria_mcm_dr_guara.pdf: 2691005 bytes, checksum: a507bf57757d62ae4ad112e4aeb41c2e (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Durante o século XX os materiais compósitos estruturais receberam especial atenção dos pesquisadores, o que levou a uma rápida evolução tecnológica acarretando uma intensa procura e posterior obtenção de materiais com características mecânicas cada vez mais elevadas, principalmente no que diz respeito ao módulo de elasticidade e a resistência mecânica. Dessa forma, os materiais tradicionalmente aplicados em engenharia aeroespacial, como o aço e o alumínio entre outros, vêm sendo substituídos por uma nova classe de materiais denominada materiais compósitos, em particular os de matrizes poliméricas reforçadas com fibras contínuas, em resposta à impossibilidade de aumento de resistência e tenacidade nos materiais homogêneos associado a redução de massa específica. Entretanto, devido às aeronaves operarem em uma grande variedade de condições ambientais tais como: ar frio e seco, em condições quentes e úmidas e diferentes gradientes de temperatura, estas condições adversas sempre devem ser consideradas na utilização de materiais aeronáuticos. Portanto, torna-se extremamente importante a avaliação da resistência às intempéries por parte dos materiais a serem selecionados para aplicações estruturais, principalmente em estruturas primárias. Dentro desse contexto, o objetivo do presente trabalho foi avaliar a influência da temperatura e umidade em laminados de aplicação aeronáutica (PPS/fibras de carbono e epóxi/fibras de carbono), a partir da exposição desses materiais a ambientes agressivos (câmaras higrotérmica, de ciclagem térmica e de choque térmico) e, posteriormente, estudar a degradação das suas propriedades mecânicas por meio de ensaios de tração, compressão e cisalhamento interlaminar e das suas propriedades térmicas utilizando-se das técnicas de... / During the 20th century the structural composites received special attention of the researchers leading to the very fast technological development of such materials. This way, occurred the preparation of materials with good mechanical properties, mainly concerning high mechanical strength and stiffness. So, the materials usually applied in aeronautical engineering, as steel and aluminium among others, have been substituted by a new class of materials, named composite materials, particularly polymeric matrix reinforced with continuous fibers answering the difficulty in increasing of mechanical strength and toughness in the homogeneous materials. Therefore, because the aircraft are always operating under different environment conditions such as dry and cold air, warm and wet conditions and large cyclical variations of temperature, these conditions have to be taken into consideration in the utilization of the aeronautical materials. However, it is extremely important the evaluation of the resistance of the materials to the intemperate weather to be selected for structural applications, mainly as primary structures. In this context the aim of this work was the evaluation the influence of intemperate weather in the laminates of aeronautical application (PPS/carbon fiber and epoxy/carbon fiber), submitting these materials to aggressive environment and study the degradation of their mechanical properties by tensile, compression and interlaminar shear tests as well as thermal properties by DMA and TMA. From these found results, it was observed that for PPS/carbon fiber laminates no one used conditioning generate significant differences in the glass transition temperature nor on the mechanical performance of its composite, qualifying this laminate for aeronautical application when its necessary this kind of requirements... (Complete abstract click electronic access below)

Made available in DSpace on 2014-06-11T19:32:50Z (GMT). No. of bitstreams: 0 Previous issue date: 2008-10-10Bitstream added on 2014-06-13T19:03:29Z : No. of bitstreams: 1 marins_em_dr_guara_prot.pdf: 7283473 bytes, checksum: 080948824f946973e97d101c513ae685 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Armas de fogo têm sido usadas em periódo dificeis da história, nos quais conflitos entre países têm ocorrido, ou no cotidiano cada vez amis violento das grandes cidades. Neste sentido, a blindagem de veículos, aeronaves e de pessoas é uma necessidade cada vez maior. Das cerâmicas utilizadas para esse fim, o carbeto de silício tem um excelente desempenho devido à alta dureza e baixa densidade. O objetivo desse trabalho é otimizar a manufatura de cerâmicas de carbeto de silício feitas de matéria prima nacional, caracterizá-las tanto quanto comparar suas características com aquelas de material importado, visando sua aplicação em blindagem balística pessoal ou de veículos leves. a fim de proporcionar independência tecnológica nessa área. Foram confeccionadas cerâmicas de carbeto de dilício de dois tipos de pós: um nacional Microservice e importado - H. C. Starck. As cerâmicas foram conformadas por prensagem uniaxial, seguida de prensagem isostática e sinterização com fase líquida, utilzando YAG como aditivo de sinterização. A caracterização das cerâmicas foir formada por: ensaios de flexão por quatro pontos, medidas de densidade, testes de dureza e ceramografia. As cerâmicas confeccionadas com o SiC H. C, Starck apresentaram maior densidade e maior resistência mecânica do que as demais. Enquanto que, as amostras nas quais o SIC da Microservice associado a 10% de YAG como aditivo foi usado, demostraram a mais alta homogeneidade e valores de resistência mecânica e dureza os mais próximos aos valores daquelas feitas com matéria-prima importada. Esses resultados mostram que é possível usar cerâmicas feitas com o SIC nacional para propósitos de blindagem balística. / Firearms have beem used either in hard periods of history, in which conflicts between countries have occurred, or in the everyday life of the large cities, wich are more and more violent. Thus, the protection of vehicles, aircraft and people is an increasing need. Among ceramics used for this purpose, silicon carbide has an excellent performane due to its high hardness and low density. The goal of this work is to optimize the manufacture of the silicon carbide ceramics made from Brazilian raw-materials, characteriza them as well as to compares their characteristics with those form imported raw-material, aiming their application in personnel or in light vehicles armor to provide technological independence in this field. Silicon carbide ceramics were made of two kinds of powders: Brazilian - Microservice and importe - H. C. Starck. The ceramics were shaped by uniaxial pressing, followed by isostatic pressing, and liquid phase sintering using YAG as an sintering additive. The characterization of the ceramics was consisted of the four-point flexural tests, measurements of density, hardness testsm and ceramography. The ceramics made of SIC H.C. Starck presentes higher density and higher mechanical resistance than the others. While the samples of ceramicsm in wich the SIC of Microservice and a 10-percent of YAG as an additive was used, presented the highest homogeneity and mechanical resistance and hardness values closets to the values from those made of importes raw-materials. These results show it is possible to use ceramics, made of Brazilian sources for ballistica armor purposes.

Made available in DSpace on 2014-06-11T19:32:50Z (GMT). No. of bitstreams: 0 Previous issue date: 2010-12-15Bitstream added on 2014-06-13T20:24:13Z : No. of bitstreams: 1 mazur_rl_dr_guara.pdf: 5349444 bytes, checksum: 5546ed3e05f9b04e6ef0e88215a4b018 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Os compósitos poliméricos avançados têm sido utilizados como materiais estruturais de elevado desempenho em aplicações aeroespaciais nos últimos 40 anos. No entanto, esses materiais podem apresentar problemas quando expostos à umidade, temperatura, radiação ultravioleta e variação térmica, podendo ocorrer sinergia entre os principais mecanismos de degradação. Entre os compósitos termoplásticos, o laminado processado a partir de fibras de carbono/PEKK (poli(éter-cetona-cetona)) mostra excelente balanço de propriedades, incluindo elevada temperatura de transição vítrea, elevados valores de resistência, rigidez e tenacidade à fratura, baixa absorção de umidade e boa resistência ambiental. O objetivo do presente trabalho é avaliar a influência dos parâmetros de processamento na obtenção do compósito de fibra de carbono/PEKK, via moldagem por compressão a quente, assim como, estudar a influência de diferentes condicionamentos ambientais, como efeito higrotérmico, radiação ultravioleta (UV) e ciclagem térmica nos comportamentos viscoelástico e mecânico do compósito. Neste trabalho, os efeitos da degradação ambiental sobre as propriedades mecânicas e viscoelásticas foram avaliadas por meio de ensaios de compressão, de cisalhamento interlaminar, DMA e vibração livre. O processamento dos compósitos por moldagem por compressão a quente mostrou-se adequado necessitando, porém, da otimização de alguns parâmetros. As análises viscoelásticas das amostras submetidas ao condicionamento por radiação UV mostram que as temperaturas de transição vítrea das amostras não condicionadas e condicionadas encontram-se relativamente próximas (~157°C a 162°C), mas o módulo de armazenamento apresenta uma acentuada degradação, evidenciando o efeito deletério da radiação UV na rigidez do compósito estudado / Advanced polymeric composites have been introduced as structural materials for high performance aerospace applications over the last 40 years. However, these materials can present problems when exposed to moisture, temperature, ultraviolet (UV) radiation and thermal cycling, besides it may occur the synergy among the main degradation mechanisms. Among the thermoplastic composite materials, carbon fiber reinforced PEKK (poly(etherketone- ketone)) laminates have shown excellent balance of properties, including high glass transition temperature, high strength, stiffness and fracture toughness values, low moisture absorption and good environmental resistance. The aim of the present work is to evaluate the influence of the processing parameters on the carbon fiber/PEKK composites manufacturing, by hot compression molding, and also the influence of different environmental conditionings as hygrothermal, ultraviolet (UV) radiation and thermal cycling effects on viscoelastic and mechanical behaviors. In this work, the effects of environmental degradation on mechanical and viscoelastic properties were studied by compression, interlaminar shear strengths, DMA and free vibration tests. Hot compression molding showed good to produce the thermoplastic composite, but it need be optimised. The viscoelastic tests of the samples submitted to the UV radiation effects show the glass transition temperatures of non-conditioning and conditioning specimens are near (~157°C to 162°C) when compared between then. On the other hand, the storage modulus presents a significant degradation emphasising the deleterious effect of the UV conditioning on the studied composite stiffness

Resumo: 0 Faxinal, objeto deste estudo, é um sistema de produção camponês tradicional e secular, característico da região Centro-Sul do Paraná, onde coexistem o uso comum e privado da terra. Nele ocorre a integração de três componentes: a) criação extensiva de animais em áreas comuns denominadas criadouro comunitário; b) policultura alimentar de subsistência e comercialização; c) extração florestal de baixo impacto. Em 1997, através do Decreto n 0 3446/97, o Governo do Paraná reconheceu formalmente a existência do Faxinai e criou as Áreas Especiais de Uso Regulamentado - ARESUR, para categorizá-los. Assim, os municípios que possuem Faxinais em seu território adquiriram o direito de receber, pela lei do ICMS Ecológico, um maior percentual na distribuição dos recursos do ICMS que são repassados pelo Estado. O decreto determina que os Faxinais deverão receber um tratamento diferenciado, com avaliação anual, sendo que para cada um deverá ser definido um escore de qualidade. Este trabalho objetivou, através de Métodos Estatísticos Multivariados, criar um critério para hierarquizar os faxinais, visando ao ICMS Ecológico, melhorando a compreensão do sistema e das transformações em curso, além de identificar e propor ações que proporcionem melhoria das condições de vida nos Faxinais. O estudo foi realizado em 20 Faxinais distribuídos em 4 municípios inscritos para receber os recursos: Boa Ventura de São Roque, Irati, Prudentópolis e Rebouças. Após a coleta de dados em campo mediante questionário, foram selecionadas 80 variáveis, que vieram a compor a matriz de dados. Foi, então, aplicada a técnica de Análise Fatorial, através da qual foram obtidos 17 fatores comuns, que explicaram 87,38% da variação total. A partir deles obtiveram-se, por regressão, os valores dos escores de cada faxinai em cada um dos 17 fatores e o escore final médio por Faxinai, ponderado pela importância de cada fator. Os escores finais obtidos definiram a hierarquia dos faxinais. Para atender as exigências do Instituto Ambiental do Paraná, que determina que os escores devem assumir valores entre "0" e "2", a escala dos mesmos foi padronizada. Os faxinais hierarquizados foram caracterizados considerando os fatores comuns e a matriz de dados originais. Com os resultados obtidos foi possível atingir os objetivos propostos, comprovando a eficiência do método escolhido.