Made available in DSpace on 2014-06-11T19:28:57Z (GMT). No. of bitstreams: 0 Previous issue date: 2005-12-15Bitstream added on 2014-06-13T20:18:38Z : No. of bitstreams: 1 mazaro_jvq_me_araca.pdf: 2035782 bytes, checksum: e67d1a0017e9c678266d158062acc962 (MD5) / Universidade Estadual Paulista (UNESP) / A relação existente entre os métodos de processamento das resinas acrílicas e a espessura de resina das bases de dentaduras, bem como a associação com o tamanho e forma do arco maxilar, tem sido um assunto bastante discutido no que diz respeito à possíveis alterações no posicionamento dos dentes e selamento posterior de próteses totais maxilares. Sendo assim, o propósito desse trabalho foi avaliar a movimentação dentária que ocorre durante o processamento de próteses totais maxilares com três diferentes espessuras de base, frente a dois métodos de inclusão e submetidas à polimerização por microondas. Quarenta e duas (42) amostras foram aleatoriamente divididas em 6 grupos de 7 amostras cada, respeitando, evidentemente, a espessura da base (1,25 mm - 2,50 mm - 3,75 mm) e o tipo de revestimento em mufla (silicone e gesso pedra). Pontos foram demarcados sobre os dentes artificiais para permitir a mensuração das R ee ssum o amostras através do software AutoCad. A diferença das médias dos segmentos entre o modelo encerado e demuflado de cada grupo foi submetida à analise de variância (ANOVA) e teste de Tukey. De acordo com os resultados obtidos pode-se concluir que: todas as técnicas de processamento juntamente com as diferentes espessuras de base de prótese total avaliadas apresentaram alteração na posição dos dentes artificiais após o processamento. A técnica de inclusão com barreira de silicone foi a que apresentou as maiores alterações dimensionais, independentemente da espessura. Na análise dos segmentos, houve uma maior alteração dos segmentos A/B/C (Triângulo maior) com relação aos segmentos D/E/F (Triângulo menor). Independente do tipo de inclusão, não houve diferença estatística entre as espessuras das bases (p<0,059), entretanto, analisando o comportamento de alteração, as prótese totais com bases mais finas apresentaram maior... . / The existent relationship between the methods of processing of the acrylic resins and the thickness of dentures bases resin, as well as the association with the size and form of the maxillary arch, it has been a subject quite discussed with regard to possible alterations in the teeth positioning and maxillary complete denture postdamming. So that, the aim of the study was to evaluate the dental movement that it happens during the processing of maxillary complete dentures with three base thickness different, front of two inclusion methods and submitted to the microwaves polymerization. Forty two (42) samples were randomly divided in 6 groups of 7 samples each, respecting, evidently, the base thickness (1,25 mm - 2,50 mm - 3,75 mm) and the type in flask investment (silicone and plaster stone). Points were demarcated on the artificial teeth to allow the measurement of the samples through the AutoCad software. The averages difference of the segments between the Ab ss tt rr a cc tt waxed model and deflasked of each group was submitted to it analysis of variance (ANOVA á=0,05) and Tukey test. In agreement with the obtained results it can be conclusion that: all the processing techniques together with the different thickness of complete denture base evaluated, presented alteration in the artificial teeth positionig after the processing. The silicone flasking technique was that presented the largest dimensional alterations, independently of the thickness. In the segments analysis, there was a larger alteration of the segments A/B/C (larger Triangle) regarding the segments D/E/F (smaller Triangle). Independent of the flasking type, there was not difference statistics among the thickness of the bases (p <0,059), however, analyzing the alteration behavior, thinner bases presented larger movement in the position of the artificial teeth than thicken base that complete denture them. The completed... (Complete abstract, click electronic address below).

Resumo: A energia por microondas tem sido recomendada para desinfetar próteses totais. Entretanto, os ciclos de desinfecção podem afetar a estabilidade dimensional das bases de próteses. Assim, o objetivo deste estudo clínico foi avaliar o efeito de dois protocolos de desinfecção por microondas na estabilidade dimensional de próteses totais, analisando a estabilidade dimensional linear, o percentual de força oclusal obtido a partir dos contatos oclusais cêntricos e as ocorrências clínicas. Foram confeccionadas próteses totais para quarenta pacientes totalmente edêntulos. Todas as próteses foram prensadas com a resina Lucitone 550. Após a colocação, aguardou-se 30 dias para submeter as próteses às condições experimentais como a seguir: Grupo 1 (G1)- 20 pacientes tiveram as próteses maxilares submetidas a desinfecção por microondas (650 W / 3 minutos), uma vez por semana, durante 4 semanas. Grupo 2 (G2)- 20 pacientes tiveram as próteses maxilares submetidas a desinfecção por microondas (650 W / 3 minutos), três vezes por semana, durante 4 semanas. Para avaliar a estabilidade dimensional linear, mensurações foram realizadas entre quatro pontos de referência (primeiros pré-molares e segundos molares bilateralmente) antes da primeira desinfecção por microondas (baseline) e após cada semana de desinfecção. Um software foi utilizado para mensurar as distâncias entre os pontos de referência a partir de fotografias padronizadas. As dimensões médiolateral e anteroposterior e a área foram calculadas. Os dados foram analisados pelos testes ANOVA two-way, Tukey e t-Student (_=0,05). O sistema T-Scan III foi utilizado para avaliar o percentual de força oclusal obtido a partir dos contatos oclusais cêntricos. Os contatos oclusais cêntricos foram capturados, antes da primeira desinfecção por microondas (baseline) e após cada semana de desinfecção, por meio... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Microwave energy has been recommended for disinfecting complete dentures. However, the microwave disinfection cycles may affect the dimensional stability of denture bases. Therefore, the purpose of this clinical study was to evaluate the effect of two microwave disinfection protocols on the dimensional stability of complete dentures, analyzing the linear dimensional stability, the percent occlusal force obtained from centric occlusal contacts and the clinical events. Complete dentures were constructed for forty totally edentulous patients. All dentures were conventionally processed with heat-polymerized acrylic resin (Lucitone 550). After insertion of complete dentures, it was expected 30 days to submit the dentures to the experimental conditions as follows: Group 1 (G1)- 20 patients had the maxillary complete dentures submitted to microwave disinfection (650 W/ 3 minutes), once a week, for four weeks. Group 2 (G2)- 20 patients had the maxillary complete dentures submitted to microwave disinfection (650 W/ 3 minutes), three times a week, for four weeks. To evaluate the linear dimensional stability, measurements were taken across four reference points (first premolars and second molars bilaterally) before of first microwave disinfection (baseline) and after each week of disinfection. Software was used to measure distances between reference points from standardized photographs. Mediolateral and anteroposterior dimensions and area between reference points were calculated. The dimensional data obtained were analyzed using two-way ANOVA, Tukey test and t test (_ = .05). To evaluate the percent occlusal force obtained from centric occlusal contacts, the T-Scan III system was used. The centric occlusal contacts were measured, before of first microwave disinfection (baseline) and after each week of disinfection, using pressure-sensitive sheets and studied in T-Scan software. The occlusal data... (Complete abstract click electronic access below) / Orientador: Eunice Teresinha Giampaolo / Coorientador: Marco Antonio Compagnoni / Banca: Raphael Freitas de Souza / Banca: Claudia Helena Lovato da Silva / Banca: Ana Claudia Pavarina / Banca: João Neudenir Arioli Filho / Doutor

Neste trabalho, objetivou-se avaliar as propriedades físicas e microbiológicas de resinas acrílicas a base de polimetilmetacrilato após a incorporação de sal de diacetato de clorexidina (CDA) às mesmas. Para tal, foram confeccionados corpos de prova (CDPs) com as resinas VIPI COR e Duralay, sem e com incorporação de 0,5%; 1,0% e 2,0% de CDA, totalizando 8 grupos. A cromatografia líquida foi utilizada para mensurar a liberação de CDA pelas resinas acrílicas, e ainda, mensurar sua lixiviação de monômeros residuais.Para isso, os CDPs foram armazenados individualmente em placas para cultura celular de 24 poços contendo 1 ml de água destilada estéril em cada poço. Após tempo de armazenagem de 2 horas, 7 dias, 14 dias, 21 dias e 28 dias, a 37oC, a solução foi retirada e a liberação de clorexidina ou monômeros residuais foi avaliada utilizando-se HPLC associado a espectrometria ultravioleta. A atividade antifúngica para C. albicans foi avaliada utilizando teste de difusão em ágar, no qual os CDPs foram colocados em placas de BHI previamente inoculadas com C. albicans, com medição do halo de inibição após 48 horas de incubação a 37C. A análise do grau de conversão das resinas se deu através da técnica de espectroscopia de infravermelho transformada de Fourier FTIR utilizando-se uma amostra de resina não polimerizada de cada grupo e realizados 4 scans de absorbância. Para a mensuração da sorção de água por parte das resinas contendo CDA, foram confeccionados 10 corpos de prova para cada grupo, que foram posicionados em suporte dentro de dessecador a 37C para remoção de umidade intrínseca (m1) e depois imersos em 100 ml de água deionizada por 7 dias a 37C, tendo a água trocada diariamente. Após este intervalo, os corpos foram secos para obter a nova massa da resina (m2). As massas obtidas foram incluídas em fórmula matemática para obtenção do grau de sorção. Após obtenção dos resultados, quando comparou-se o halo inibição entre os grupos testados e de mesma marca, apenas as análises entre grupo CDA 2% x grupo CDA 1% e entre CDA 1% x CDA 0,5% não apresentaram diferenças significantes. Quanto a liberação de CDA, a análise de variância demonstrou que dois dos três fatores avaliados (concentração do fármaco e tempo de armazenagem) alteram de maneira significativa a taxa de liberação da clorexidina (p<0,0001), entretanto a marca do material pareceu não influenciar de maneira significativa na liberação do fármaco. Quanto ao grau de conversão, os valores obtidos não foram significantes e apresentou-se menor apenas nos grupos com CDA 2% . Para ambas a sorção de água aumentou conforme a incorporação do sal cresceu e houve aumento significativo nas concentrações de 1.0% e 2.0%. Podemos concluir que a incorporação da clorexidina às resinas a base de PMMA: é capaz de inibir o crescimento de C. albicans; não alterou o grau de conversão das resinas testadas; não altera a liberação de monômeros residuais; e, altera a sorção de água das resinas acrílicas a base de PMMA quando concentrações maiores de CDA são adicionadas. / This work aimed to evaluate physical and microbiological properties of PMMA acrylic resins after incorporating chlorhexidine diacetate salt (CDA) to them . For that, specimens ( CDPs ) were made with resins VIPI COR and Duralay , with and without incorporation of 0.5 % , 1.0 % and 2.0 % of CDA , totaling 8 groups . The liquid chromatography was used to measure the release of CDA by acrylic resins , and also to measure leaching of residual monomers . For that, CDPs were stored individually in cell culture plates to 24 well containing 1 ml of sterile distilled water in each well. Storage time after 2 hours , 7 days, 14 days, 21 days and 28 days at 37 C , the solution was removed and release of residual monomers or chlorhexidine was evaluated by using ultraviolet spectrometry combined with HPLC. The antifungal activity to C. albicans was evaluated using the agar diffusion method , in which the CDPs were placed on BHI plates inoculated with C. albicans with measuring the zone of inhibition after 48 hours incubation at 37 C. The analysis of the resins conversion degree is given by infrared spectroscopy Fourier transform - FTIR using an uncured resin sample in each group and 4 scans performed absorbance . For the measurement of resins containing CDA s water sorption, 10 specimens were prepared for each group , which were placed in support within desiccator 37 C to remove intrinsic ( m1 ) and then immersed moisture in 100 ml deionized water for 7 days at 37 C , and the water was changed daily. After this interval , the specimens were dried to obtain the new resins weight ( m2 ) . The masses obtained were included in the mathematical formula for the degree of sorption. After obtaining results, when compared the inhibition halo between the tested groups and the same brand , only the analyzes between group CDA2 % x CDA 1 % group and from CDA 1 % x CDA0.5 %,showed no significant differences . About the release of CDA , analysis of variance showed that two of the three factors assessed ( drug concentration and storage time ) significantly change the rate of release of chlorhexidine ( p < 0.0001 ) , however the material mark seemed not significantly influence the drug release . About the conversion degree , the values were not significant and were minor only in groups with CDA 2 % . For both water sorption increased with the incorporation of salt grew and there was significant increase in concentrations of 1.0 % and 2.0 % . We conclude that the incorporation of chlorhexidine to the PMMA based resin : is able to inhibit the growth of C. Albicans ; did not alter the degree of conversion of the resins tested , does not alter the release of residual monomers , and changes the water sorption of the base PMMA acrylic resins when CDA concentrations are incorporated.

Neste trabalho, objetivou-se avaliar as propriedades físicas e microbiológicas de resinas acrílicas a base de polimetilmetacrilato após a incorporação de sal de diacetato de clorexidina (CDA) às mesmas. Para tal, foram confeccionados corpos de prova (CDPs) com as resinas VIPI COR e Duralay, sem e com incorporação de 0,5%; 1,0% e 2,0% de CDA, totalizando 8 grupos. A cromatografia líquida foi utilizada para mensurar a liberação de CDA pelas resinas acrílicas, e ainda, mensurar sua lixiviação de monômeros residuais.Para isso, os CDPs foram armazenados individualmente em placas para cultura celular de 24 poços contendo 1 ml de água destilada estéril em cada poço. Após tempo de armazenagem de 2 horas, 7 dias, 14 dias, 21 dias e 28 dias, a 37oC, a solução foi retirada e a liberação de clorexidina ou monômeros residuais foi avaliada utilizando-se HPLC associado a espectrometria ultravioleta. A atividade antifúngica para C. albicans foi avaliada utilizando teste de difusão em ágar, no qual os CDPs foram colocados em placas de BHI previamente inoculadas com C. albicans, com medição do halo de inibição após 48 horas de incubação a 37C. A análise do grau de conversão das resinas se deu através da técnica de espectroscopia de infravermelho transformada de Fourier FTIR utilizando-se uma amostra de resina não polimerizada de cada grupo e realizados 4 scans de absorbância. Para a mensuração da sorção de água por parte das resinas contendo CDA, foram confeccionados 10 corpos de prova para cada grupo, que foram posicionados em suporte dentro de dessecador a 37C para remoção de umidade intrínseca (m1) e depois imersos em 100 ml de água deionizada por 7 dias a 37C, tendo a água trocada diariamente. Após este intervalo, os corpos foram secos para obter a nova massa da resina (m2). As massas obtidas foram incluídas em fórmula matemática para obtenção do grau de sorção. Após obtenção dos resultados, quando comparou-se o halo inibição entre os grupos testados e de mesma marca, apenas as análises entre grupo CDA 2% x grupo CDA 1% e entre CDA 1% x CDA 0,5% não apresentaram diferenças significantes. Quanto a liberação de CDA, a análise de variância demonstrou que dois dos três fatores avaliados (concentração do fármaco e tempo de armazenagem) alteram de maneira significativa a taxa de liberação da clorexidina (p<0,0001), entretanto a marca do material pareceu não influenciar de maneira significativa na liberação do fármaco. Quanto ao grau de conversão, os valores obtidos não foram significantes e apresentou-se menor apenas nos grupos com CDA 2% . Para ambas a sorção de água aumentou conforme a incorporação do sal cresceu e houve aumento significativo nas concentrações de 1.0% e 2.0%. Podemos concluir que a incorporação da clorexidina às resinas a base de PMMA: é capaz de inibir o crescimento de C. albicans; não alterou o grau de conversão das resinas testadas; não altera a liberação de monômeros residuais; e, altera a sorção de água das resinas acrílicas a base de PMMA quando concentrações maiores de CDA são adicionadas. / This work aimed to evaluate physical and microbiological properties of PMMA acrylic resins after incorporating chlorhexidine diacetate salt (CDA) to them . For that, specimens ( CDPs ) were made with resins VIPI COR and Duralay , with and without incorporation of 0.5 % , 1.0 % and 2.0 % of CDA , totaling 8 groups . The liquid chromatography was used to measure the release of CDA by acrylic resins , and also to measure leaching of residual monomers . For that, CDPs were stored individually in cell culture plates to 24 well containing 1 ml of sterile distilled water in each well. Storage time after 2 hours , 7 days, 14 days, 21 days and 28 days at 37 C , the solution was removed and release of residual monomers or chlorhexidine was evaluated by using ultraviolet spectrometry combined with HPLC. The antifungal activity to C. albicans was evaluated using the agar diffusion method , in which the CDPs were placed on BHI plates inoculated with C. albicans with measuring the zone of inhibition after 48 hours incubation at 37 C. The analysis of the resins conversion degree is given by infrared spectroscopy Fourier transform - FTIR using an uncured resin sample in each group and 4 scans performed absorbance . For the measurement of resins containing CDA s water sorption, 10 specimens were prepared for each group , which were placed in support within desiccator 37 C to remove intrinsic ( m1 ) and then immersed moisture in 100 ml deionized water for 7 days at 37 C , and the water was changed daily. After this interval , the specimens were dried to obtain the new resins weight ( m2 ) . The masses obtained were included in the mathematical formula for the degree of sorption. After obtaining results, when compared the inhibition halo between the tested groups and the same brand , only the analyzes between group CDA2 % x CDA 1 % group and from CDA 1 % x CDA0.5 %,showed no significant differences . About the release of CDA , analysis of variance showed that two of the three factors assessed ( drug concentration and storage time ) significantly change the rate of release of chlorhexidine ( p < 0.0001 ) , however the material mark seemed not significantly influence the drug release . About the conversion degree , the values were not significant and were minor only in groups with CDA 2 % . For both water sorption increased with the incorporation of salt grew and there was significant increase in concentrations of 1.0 % and 2.0 % . We conclude that the incorporation of chlorhexidine to the PMMA based resin : is able to inhibit the growth of C. Albicans ; did not alter the degree of conversion of the resins tested , does not alter the release of residual monomers , and changes the water sorption of the base PMMA acrylic resins when CDA concentrations are incorporated.

Orientador: Celia Marisa Rizzatti Barbosa / Tese (doutorado) - Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-28T03:15:46Z (GMT). No. of bitstreams: 1 Zanetti_GlaucoRangel_D.pdf: 4522575 bytes, checksum: 4717fe0797e79a21a39c9cbeebb8ac1d (MD5) Previous issue date: 2000 / Resumo: Este estudo avaliou a influência do material de inclusão (gesso tipo 11 Herodent@ "G", silicone por condensação laboratorial Zetalabor@ "Z"), e da configuração da porção distal da grade metálica (com apoio "C" e sem apoio "s" sobre o modelo), nas alterações horizontais (esquerda "HE" e direita "HD") e verticais (esquerda "VE" e direita "VD") , entre as porções distais de estruturas metálicas de prõteses parciais removíveis (PPR's) e seus respectivos modelos durante o processamento das bases em resina acrílica. Foram utilizados modelos simulando uma arcada inferior parcialmente desdentada classe I de Kennedy. Quarenta amostras padronizadas foram divididas em quatro grupos. As bases foram processadas com uma resina polimerizada por energia de microondas (Onda-Cryl@). Os dados foram submetidos à análise de variância e as médias, ao teste de Tukey (p<O,O5). Os resultados das médias das alterações em milímetros, nos grupos GC (HE=0,2043; HD=0,1610; VE=0,0599; VD=0,0599), GS (HE=O,1888; HD=0,1156; VE=0,2063; VD=O,2420), ZC (HE=0,1796; HD=0,2025; VE=O,0717; VD=0,1396), ZS (HE=0,2043; HD=0,O746; VE=O,2143; VD=0,2880) indicaram que: na VE e VD, G não diferiu de Z, mas C apresentou alterações significativamente menores que S; na HE os grupos não diferiram estatisticamente entre si; na HD não houve diferença significativa entre (ZC e GC), (GC e GS), (GS e ZS) e as alterações foram progressivamente maiores em ZS, GS, GC e ZC / Abstract: This study evaluated the effect of two types of investment material ("G", type 11 dental stone, Herodent@; "Z", condensation silicone, Zetalabor@) and two types of design of the distal portion of the metallic framework ("S", with support in the model; "N", without support in the model) in the horizontal ("H L", left; "HR", right) and vertical ('VL", left; 'VR", right) distance changes between the distal portion of the metallic framework and their respective models during processing of the acrylic bases. A lower Kennedy Class I model was used. Forty standardized RPD's were prepared and equally divided into 4 groups. The RPD's bases were processed using a microwave-cured acrylic resin (OndaCryl@). Data was submitted to a "Tukey's Studentized" test (p<O.O5). The results of the means alterations in millimeters, in the groups GS (HL=O.2043; HR=O.1610; VL=O.O599; VR=O.O599), GN (HL=O.1888; HR=O.1156; VL=O.2063; VR=O.2420), ZS (HL=O.1796; HR=O.2025; VL=O.O717; VR=O.1396), ZN (HL=O.2043; HR=O.O746; VL=O.2143; VR=O.2880) showed that for VL and VR measurements, G and Z were not different, and S showed statistical lower changes than N. There was not difference of HL among groups. Considering HR, there was no statistical difference between groups for each following pair: ZS-GS, GS-GN and GN-ZN. Changes were crescent in the order ZN, GN, GS and ZS / Doutorado / Protese Dental / Doutor em Clínica Odontológica

No / To determine whether Hartmann-Shack wavefront sensing detects differences in optical performance in vivo between poly(methyl methacrylate) (PMMA) and foldable acrylic intraocular lenses (IOLs) and between clear corneal and scleral tunnel incisions and whether optical differences are manifested as differences in visual performance. SETTING: Department of Optometry, University of Bradford, West Yorkshire, United Kingdom. METHODS: This study comprised 74 subjects; 17 were phakic with no ocular pathology, 20 had implantation of a Pharmacia 722C PMMA IOL through a scleral tunnel, 21 had implantation of an Alcon AcrySof IOL through a scleral tunnel, and 16 had implantation of an AcrySof IOL through a corneal incision. Visual acuity and contrast sensitivity testing, ocular optical quality measurement using Hartmann-Shack wavefront sensing, and corneal surface measurement with a videokeratoscope were performed in all cases. RESULTS: There were significant differences between groups in the total root-mean-square (RMS) wavefront aberration over a 6.0 mm pupil (F=3.91; degrees of freedom=3,70; P<.05) mediated at the 4th-order RMS, specifically spherical and tetrafoil aberrations. The PMMA-scleral group had the least aberrations and the AcrySof-corneal group the most. For a 3.5 mm diameter pupil, the total higher-order RMS wavefront aberration was not significantly different between the groups (P>.05). There were no differences between groups in corneal shape, visual acuity, or contrast sensitivity. CONCLUSIONS: Implantation of the spherical PMMA IOL led to a slight reduction in total wavefront aberration compared to phakic eyes. AcrySof IOLs induced more aberrations, especially spherical aberration. Corneal-based incisions for IOL implantation compounded this increase. Studies of the optical performance of IOLs in vivo should use wavefront sensing as the main outcome measure rather than visual measures, which are readily confounded by multiple factors.

As restaurações provisórias no tratamento reabilitador oral são de suma importância. Por isso é preocupante que os materiais utilizados para a execução das mesmas sejam críticos com relação à sua resistência e longevidade, principalmente, quando estas são executadas em tratamentos prolongados e/ou em espaços desdentados extensos. O objetivo deste trabalho foi avaliar em 4 grupos reforçados, compostos por 9 espécimes cada um, a resistência e o modo de fratura, de uma resina acrílica poli(metilmetacrilato) auto-polimerizável (Dencor® - Clássico®, São Paulo, SP, Brasil) utilizada para restaurações provisórias quando reforçada com fibras de vidro (Fibrante® e Interlig® - Angelus®, Londrina, PR, Brasil), fibras de aramida (Kevlar® - Du Pont®, USA) y fio ortodôntico &#x2205; 0, 7mm. E um grupo controle sem nenhum tipo de reforço, com a mesma quantidade de corpos de prova. A análise dos resultados (ANOVA, p < 0,05), para o teste de resistência, mostrou haver diferença estatística entre os grupos. O teste de Tukey encontrou que os grupos reforçados, aqueles que alcançaram maior média de resistência à fratura foram os que utilizaram a fibra de vidro trançada pré-impregnada com resina composta foto-polimerizável, Interlig® (1083 N); a fibra de vidro unidirecional préimpregnada com dimetacrilato de glicol, Fibrante® (1022 N) e a fibra de poli(aramida) unidirecional sem pré-impregnação, Kevlar® 29, aumentando em 26%, 22% e 17%, respectivamente, esta resistência em relação ao grupo controle (800 N), não havendo diferença estatística significante entre eles. O grupo reforçado com fio de aço com &#x2205; 0,7 mm (871 N) apareceu em seguida com uma resistência somente 8% maior e semelhante àquela apresentada pelo grupo controle sem reforço. A análise das fraturas concorreu com a elaboração de um novo sistema de classificação dividindo-as em quatro tipos: Ausente, Parcial, Total Não Separada e Total Separada. As fraturas dos espécimes reforçados foram consideradas mais favoráveis ocorrendo, predominantemente, os tipos Ausente e Parcial. / Provisional restorations are of ultimate importance in the oral rehabilitation treatment. Thus, clinicians have to bear in mind that materials used for their fabrication are critical due to its longevity and strength, when these are done for longterm therapy and/or large edentulous spaces. The aim of this work was to evaluate the flexural resistance and fracture mode of an auto-cure polymethylmetacrilate resin (Dencor® - Classico® , Sao Paulo, SP, Brasil) used for provisional restorations and reinforced with four materials. Samples were divided in four groups of nine each, as the following: glass fiber (Fibrante® and Interlig® Angelus®, Londrina, PR, Brasil), aramide fibers (Kevlar® Du Pont®, USA), and orthodontic wire &#x2205; 0,7mm. one group whitout reinforcement served as control. Data was submitted to statistical analysis with one-way ANOVA (p<.05) test. Results showed statistically significant difference among the groups. Tukeys test showed that glass-fiber Interlig® exhibited the greatest value of flexural strength (1083 N); followed by unidirectional glycol dimetacrylate glass-fiber Fibrante® (1022 N) and aramid fiber Kevlar® (966 N). These values represent 26%, 22% and 17% in relation to the control group (800 N), being non statistically significant difference observed among them. The group with &#x2205; 0,7mm orthodontic wire (871 N) had a resistance only 8% higher and similar of that of control group without reinforcement. Fracture analysis was conducted by the following scale: absence, partial, complete without separation, and complete with separation. Fracture modes observed on reinforced samples were considered more favorable, with types absent and partial seeing more frequently.

O custo elevado na fabricação de peças pela tecnologia da Manufatura Aditiva (AM) impulsionou, nos últimos anos, várias pesquisas visando ao desenvolvimento de novos equipamentos e novos materiais. Neste contexto, uma resina fotossensível, desenvolvida anteriormente com componentes disponíveis no mercado nacional pelo grupo de pesquisa ao qual este trabalho está inserido, apresentou baixas propriedades mecânicas e alta contração do material quando comparada aos materiais disponíveis no mercado. Assim, uma alternativa para melhorar essas propriedades é a obtenção de nanocompósitos. Estes compreendem uma nova classe de materiais, em que substâncias inorgânicas de dimensões nanométricas, tais como argilas e outros argilominerais, são finamente dispersas dentro de uma matriz polimérica. Dessa forma, o presente estudo tem por objetivo preparar e caracterizar um nanocompósito fotossensível de acrílico/argila curado por exposição à radiação UV-C, com propriedades mecânicas de tração, flexão e dureza, e contrações adequadas para aplicação em processo de AM. Para tanto, a formulação original, composta pelos monômeros Trimetilpropano Triacrilato (TMPTA®) e Ácido Metacrilato Modificado (Ebecryl 171®), oligômero Amina Acrilada (Ebecryl 7100®), Co-iniciador Benzofenona 99% (Additol BP®) e o fotoiniciador Additol LX®, foi testada com o acréscimo das argilas Cloisite 20® e a BN-CT nas concentrações de 0,5%, 1,0% e 1,5% (m/m) da massa total. Após o preparo dessas formulações obtidas pela dispersão 1 (agitação magnética) e 2 (agitação magnética e ultrassom), foram preparados corpos de prova pelo princípio de adição sucessiva de camadas pela AM. A caracterização foi realizada através da análise da contração, ensaios de resistência à tração, flexão e dureza, microscopia eletrônica de varredura (MEV), difração de raios X(DRX), termogravimetria (TG) e viscosidade. O empenamento do material apresentou uma melhora média de 18,27% com argila Cloisite 20® e de 11,30% com a argila BN-CT. Os resultados dos ensaios de tração, flexão e dureza não apresentaram aumentos significativos nas propriedades mecânicas. O MEV não apresentou nenhuma delaminação entre as camadas após a realização do teste de flexão. A análise de DRX não apresentou pico de difração, sugerindo a formação de nanocompósito com estrutura intercalada e/ou esfoliada para todas as formulações com argila. O ensaio de TG mostrou que a adição de argila nas formulações não apresentou melhoras significativas na estabilidade térmica do nanocompósito. Também a viscosidade não apresentou melhoras à temperatura de 25°C, mas apresentou uma redução significativa da viscosidade a 35°C. Apesar dos resultados não muito promissores em termos de resistência mecânica, as formulações com argila podem ser empregadas na AM, considerando essas limitações. / The high cost in manufacturing parts for the of Additive Manufacturing technology (AM) boosted in recent years several studies aiming the development of new equipment and new materials. With this in mind, a photosensitive resin previously developed by the research group to which this work is inserted with components available in the domestic market, presented low mechanical properties and high shrinkage of the material compared to the materials available on the market. One alternative for improving these properties is to obtain nanocomposites. They comprise a new class of materials in which inorganic substances of nanometric dimensions, such as clays and other minerals, are finely dispersed within a polymeric matrix. Thus, this study aims to prepare and characterize a photosensitive acrylic / clay nanocomposite cured by exposure to UV-C radiation, with mechanical properties of tensile, bending and hardness, and shrinkage propers for use in AM process. Therefore, the original formulation, composed of trimethylolpropane triacrylate (TMPTA®) and Acid Methacrylate Modified (Ebecryl 171®)monomers, Amina acrylated (Ebecryl 7100®)oligomer, Co-initiator Benzophenone 99% (Additol BP®) and the photoinitiator Additol LX® was tested with the addition of the clays Cloisite 20® and BN-CT in concentrations of 0.5%, 1.0% and 1.5% (w/w) of total weight. After preparing these formulations, obtained by dispersion 1 (magnetic stirring) and 2 (magnetic stirring and ultrasound), it was prepared specimens by the principle of adding successive layers by AM. The characterization was perform by shrinkage analysis, tensile strength, bending and hardness tests, scanning electron microscopy (SEM), X-ray diffraction (XRD), thermogravimetry (TG) and viscosity. The warpage of the material showed an average improvement of 18.27% with the Cloisite 20® clay and 11.30% with the BN-CT clay. The results of the tensile, flexural and hardness testing did not show significant increases in mechanical properties. The SEM showed no delamination between the layers after the bending test was performed. The XRD analysis showed no diffraction peak, suggesting the formation of nanocomposite with intercalated and / or exfoliated structure for all formulations with clay. The TG test showed that the addition of clay in the formulations presented no significant improvements in thermal stability of the nanocomposite. The viscosity showed no improvement at a temperature of 25 °C, but showed a significant reduction in viscosity at 35 °C. Although not very promising results in terms of mechanical strength, the formulations with clay can be used in the AM considering these limitations.

O custo elevado na fabricação de peças pela tecnologia da Manufatura Aditiva (AM) impulsionou, nos últimos anos, várias pesquisas visando ao desenvolvimento de novos equipamentos e novos materiais. Neste contexto, uma resina fotossensível, desenvolvida anteriormente com componentes disponíveis no mercado nacional pelo grupo de pesquisa ao qual este trabalho está inserido, apresentou baixas propriedades mecânicas e alta contração do material quando comparada aos materiais disponíveis no mercado. Assim, uma alternativa para melhorar essas propriedades é a obtenção de nanocompósitos. Estes compreendem uma nova classe de materiais, em que substâncias inorgânicas de dimensões nanométricas, tais como argilas e outros argilominerais, são finamente dispersas dentro de uma matriz polimérica. Dessa forma, o presente estudo tem por objetivo preparar e caracterizar um nanocompósito fotossensível de acrílico/argila curado por exposição à radiação UV-C, com propriedades mecânicas de tração, flexão e dureza, e contrações adequadas para aplicação em processo de AM. Para tanto, a formulação original, composta pelos monômeros Trimetilpropano Triacrilato (TMPTA®) e Ácido Metacrilato Modificado (Ebecryl 171®), oligômero Amina Acrilada (Ebecryl 7100®), Co-iniciador Benzofenona 99% (Additol BP®) e o fotoiniciador Additol LX®, foi testada com o acréscimo das argilas Cloisite 20® e a BN-CT nas concentrações de 0,5%, 1,0% e 1,5% (m/m) da massa total. Após o preparo dessas formulações obtidas pela dispersão 1 (agitação magnética) e 2 (agitação magnética e ultrassom), foram preparados corpos de prova pelo princípio de adição sucessiva de camadas pela AM. A caracterização foi realizada através da análise da contração, ensaios de resistência à tração, flexão e dureza, microscopia eletrônica de varredura (MEV), difração de raios X(DRX), termogravimetria (TG) e viscosidade. O empenamento do material apresentou uma melhora média de 18,27% com argila Cloisite 20® e de 11,30% com a argila BN-CT. Os resultados dos ensaios de tração, flexão e dureza não apresentaram aumentos significativos nas propriedades mecânicas. O MEV não apresentou nenhuma delaminação entre as camadas após a realização do teste de flexão. A análise de DRX não apresentou pico de difração, sugerindo a formação de nanocompósito com estrutura intercalada e/ou esfoliada para todas as formulações com argila. O ensaio de TG mostrou que a adição de argila nas formulações não apresentou melhoras significativas na estabilidade térmica do nanocompósito. Também a viscosidade não apresentou melhoras à temperatura de 25°C, mas apresentou uma redução significativa da viscosidade a 35°C. Apesar dos resultados não muito promissores em termos de resistência mecânica, as formulações com argila podem ser empregadas na AM, considerando essas limitações. / The high cost in manufacturing parts for the of Additive Manufacturing technology (AM) boosted in recent years several studies aiming the development of new equipment and new materials. With this in mind, a photosensitive resin previously developed by the research group to which this work is inserted with components available in the domestic market, presented low mechanical properties and high shrinkage of the material compared to the materials available on the market. One alternative for improving these properties is to obtain nanocomposites. They comprise a new class of materials in which inorganic substances of nanometric dimensions, such as clays and other minerals, are finely dispersed within a polymeric matrix. Thus, this study aims to prepare and characterize a photosensitive acrylic / clay nanocomposite cured by exposure to UV-C radiation, with mechanical properties of tensile, bending and hardness, and shrinkage propers for use in AM process. Therefore, the original formulation, composed of trimethylolpropane triacrylate (TMPTA®) and Acid Methacrylate Modified (Ebecryl 171®)monomers, Amina acrylated (Ebecryl 7100®)oligomer, Co-initiator Benzophenone 99% (Additol BP®) and the photoinitiator Additol LX® was tested with the addition of the clays Cloisite 20® and BN-CT in concentrations of 0.5%, 1.0% and 1.5% (w/w) of total weight. After preparing these formulations, obtained by dispersion 1 (magnetic stirring) and 2 (magnetic stirring and ultrasound), it was prepared specimens by the principle of adding successive layers by AM. The characterization was perform by shrinkage analysis, tensile strength, bending and hardness tests, scanning electron microscopy (SEM), X-ray diffraction (XRD), thermogravimetry (TG) and viscosity. The warpage of the material showed an average improvement of 18.27% with the Cloisite 20® clay and 11.30% with the BN-CT clay. The results of the tensile, flexural and hardness testing did not show significant increases in mechanical properties. The SEM showed no delamination between the layers after the bending test was performed. The XRD analysis showed no diffraction peak, suggesting the formation of nanocomposite with intercalated and / or exfoliated structure for all formulations with clay. The TG test showed that the addition of clay in the formulations presented no significant improvements in thermal stability of the nanocomposite. The viscosity showed no improvement at a temperature of 25 °C, but showed a significant reduction in viscosity at 35 °C. Although not very promising results in terms of mechanical strength, the formulations with clay can be used in the AM considering these limitations.

As restaurações provisórias no tratamento reabilitador oral são de suma importância. Por isso é preocupante que os materiais utilizados para a execução das mesmas sejam críticos com relação à sua resistência e longevidade, principalmente, quando estas são executadas em tratamentos prolongados e/ou em espaços desdentados extensos. O objetivo deste trabalho foi avaliar em 4 grupos reforçados, compostos por 9 espécimes cada um, a resistência e o modo de fratura, de uma resina acrílica poli(metilmetacrilato) auto-polimerizável (Dencor® - Clássico®, São Paulo, SP, Brasil) utilizada para restaurações provisórias quando reforçada com fibras de vidro (Fibrante® e Interlig® - Angelus®, Londrina, PR, Brasil), fibras de aramida (Kevlar® - Du Pont®, USA) y fio ortodôntico &#x2205; 0, 7mm. E um grupo controle sem nenhum tipo de reforço, com a mesma quantidade de corpos de prova. A análise dos resultados (ANOVA, p < 0,05), para o teste de resistência, mostrou haver diferença estatística entre os grupos. O teste de Tukey encontrou que os grupos reforçados, aqueles que alcançaram maior média de resistência à fratura foram os que utilizaram a fibra de vidro trançada pré-impregnada com resina composta foto-polimerizável, Interlig® (1083 N); a fibra de vidro unidirecional préimpregnada com dimetacrilato de glicol, Fibrante® (1022 N) e a fibra de poli(aramida) unidirecional sem pré-impregnação, Kevlar® 29, aumentando em 26%, 22% e 17%, respectivamente, esta resistência em relação ao grupo controle (800 N), não havendo diferença estatística significante entre eles. O grupo reforçado com fio de aço com &#x2205; 0,7 mm (871 N) apareceu em seguida com uma resistência somente 8% maior e semelhante àquela apresentada pelo grupo controle sem reforço. A análise das fraturas concorreu com a elaboração de um novo sistema de classificação dividindo-as em quatro tipos: Ausente, Parcial, Total Não Separada e Total Separada. As fraturas dos espécimes reforçados foram consideradas mais favoráveis ocorrendo, predominantemente, os tipos Ausente e Parcial. / Provisional restorations are of ultimate importance in the oral rehabilitation treatment. Thus, clinicians have to bear in mind that materials used for their fabrication are critical due to its longevity and strength, when these are done for longterm therapy and/or large edentulous spaces. The aim of this work was to evaluate the flexural resistance and fracture mode of an auto-cure polymethylmetacrilate resin (Dencor® - Classico® , Sao Paulo, SP, Brasil) used for provisional restorations and reinforced with four materials. Samples were divided in four groups of nine each, as the following: glass fiber (Fibrante® and Interlig® Angelus®, Londrina, PR, Brasil), aramide fibers (Kevlar® Du Pont®, USA), and orthodontic wire &#x2205; 0,7mm. one group whitout reinforcement served as control. Data was submitted to statistical analysis with one-way ANOVA (p<.05) test. Results showed statistically significant difference among the groups. Tukeys test showed that glass-fiber Interlig® exhibited the greatest value of flexural strength (1083 N); followed by unidirectional glycol dimetacrylate glass-fiber Fibrante® (1022 N) and aramid fiber Kevlar® (966 N). These values represent 26%, 22% and 17% in relation to the control group (800 N), being non statistically significant difference observed among them. The group with &#x2205; 0,7mm orthodontic wire (871 N) had a resistance only 8% higher and similar of that of control group without reinforcement. Fracture analysis was conducted by the following scale: absence, partial, complete without separation, and complete with separation. Fracture modes observed on reinforced samples were considered more favorable, with types absent and partial seeing more frequently.