Made available in DSpace on 2014-12-17T14:58:16Z (GMT). No. of bitstreams: 1 RudsonSL_DISSERT.pdf: 2711682 bytes, checksum: 322c3d4fe0f471064164ab72367f6ce8 (MD5) Previous issue date: 2012-09-14 / Due to the increasing need to promote the use of resources that support the environment and the clean industry, the science has developed in the area of natural resource use as well as enhanced use of the renewable energy sources. Considering also the great need for clean water and wide availability of salt or brackish water, added to the great solar energy potential in northeastern of the Brazil, it was developed a solar distiller whose main difference is its system of pre-solar heating also. From experimental adjustments, the system was developed by the use of a cylindrical solar concentrator coupled to a conventional distiller. The system is designed such that attempt to facilitate the process termination trap to ensure constant movement of the fluid mass and thus enable higher temperatures to the system and thus fetch a higher amount of distillate collected. In a stage of the experiment were used a forced circulation to try to further increase the amount of energy exchange system. To develop the study were set up four settings for comparison in which one was only distiller simple as basic parameter, the second proposed configuration were with the coupling of the concentration triggered manually every 30 minutes to monitor the sun, the third configuration occurred with automatic triggering of a timer, and the fourth configuration was also used a pumping system that tried to improve the circulation of the fluid. With the comparative analysis of the results showed a gain in the amount of distillate system, especially in the forced model / Devido ? crescente necessidade de promover o uso de recursos que favore?am o ambiente e a ind?stria limpa, a ci?ncia tem desenvolvido-se na ?rea da utiliza??o de recursos naturais visando uma melhor utiliza??o de fontes de energias renov?veis. Tendo em vista tamb?m a grande necessidade de ?gua pot?vel e a grande disponibilidade de ?gua salgada ou salobra, agregado ao grande potencial energ?tico solar da regi?o nordeste do Brasil, foi desenvolvido um destilador solar cuja principal diferen?a ? o seu sistema de pr?aquecimento tamb?m solar. A partir de adapta??es experimentais, o sistema foi desenvolvido atrav?s da utiliza??o de um concentrador solar cil?ndrico acoplado a um destilador convencional para promover troca de calor consider?vel e ac?mulo de energia. O sistema foi desenvolvido de tal maneira que tente favorecer o processo de termossif?o para garantir o movimento constante da massa de fluido, e assim permitir temperaturas mais elevadas para o sistema e, consequentemente, buscar uma maior quantidade de destilado recolhido. Em uma das fases do experimento buscou-se uma circula??o for?ada para tentar aumentar mais a quantidade de troca de energia do sistema. Para o desenvolvimento do trabalho montou-se quatro configura??es de compara??o em que uma teve apenas o destilador simples como par?metro b?sico, a segunda configura??o prop?s o acoplamento do concentrador acionado manualmente a cada 30 minutos para o acompanhamento do sol, a terceira configura??o ocorreu com o acionamento autom?tico por um temporizador, e na quarta configura??o usouse tamb?m um sistema de bombeamento que tentasse melhorar a circula??o do fluido. Com a an?lise comparativa dos resultados observou-se um ganho da quantidade de destilado do sistema, principalmente no modelo com circula??o for?ada

Made available in DSpace on 2014-12-17T14:58:20Z (GMT). No. of bitstreams: 1 LuandaKOR_DISSERT.pdf: 4300124 bytes, checksum: 469607cbcb40b12cb19598ea2781bdff (MD5) Previous issue date: 2013-07-24 / The lubricants found in the market are of mineral or synthetic origin and harm to humans and the environment, mainly due to their improper discard. Therefore industries are seeking to develop products that cause less environmental impact, so to decrease mainly, operator aggression the Cutting Fluids became an emulsion of oil / water or water / oil. However, the emulsion was not considered the most suitable solution for environmental question, therefore the search for biodegradable lubricants and which no are toxic continues and so vegetable oils are seen, again, as a basis for the production of lubricants. The biggest problem with these oils is their oxidative instability that is intensified when working at high temperatures. The process transesterification decreases the oxidation, however changes some physical and chemical properties. Therefore soybean oil after the transesterification process was subjected to tests of density, dynamic viscosity, kinematic viscosity which is calculated from two parameters mentioned, flash point and acidity. Besides the physico-chemical test the soybean oil was subjected to a dynamic test in a tribometer adapted from a table vise, whose induced wear was the adhesive and ultimately was used as cutting fluid in a process of turning in two different materials, steel 1045 and cast iron. This latter test presented results below the mineral cutting fluid which it was compared in all tests, already in other experiments the result was satisfactory and other experiments not, so that chemical additives can be added to the oil analyzed to try equate all parameters and so formulate a biolubrificante not toxic to apply in machining processes of metalworking industry / Os lubrificantes encontrados no mercado s?o de origem mineral ou sint?tico e agridem ao homem e ao meio ambiente, principalmente, devido ao seu descarte inadequado, por isso as ind?strias est?o buscando desenvolver produtos que causem um menor impacto ambiental. Para diminuir a agress?o ao operador, principalmente, os Fluidos de Corte passaram a formar uma emuls?o ?leo/?gua ou ?gua/?leo. No entanto a emuls?o n?o foi tida como a solu??o mais adequada para a quest?o ambiental, portanto a busca por lubrificantes biodegrad?veis e que n?o sejam t?xicos continua e assim os ?leos vegetais est?o sendo vistos, novamente, como base para a produ??o de lubrificantes. O maior problema desses ?leos ? sua instabilidade oxidativa que ? intensificada ao trabalhar em altas temperaturas. O processo de transesterifica??o diminui a oxida??o, no entanto altera algumas propriedades f?sico-qu?micas. Portanto o ?leo de Soja ap?s o processo de transesterifica??o foi submetido aos ensaios de densidade, viscosidade din?mica (cuja viscosidade cinem?tica foi calculada a partir dos dois par?metros citados); ponto de fulgor e acidez. Al?m dos ensaios f?sico-qu?micos, o ?ster de soja foi submetido a um ensaio din?mico em um trib?metro adaptado de um torno de bancada cujo desgaste induzido foi o adesivo e por ?ltimo foi usado como fluido de corte em um processo de torneamento em dois materiais distintos, A?o1045 e Ferro Fundido. Esse ?ltimo ensaio apresentou resultados inferiores ao fluido de corte mineral o qual foi comparado em todos os ensaios, j? nos outros ensaios alguns o resultado era satisfat?rio em outros n?o de modo que aditivos qu?micos podem ser adicionados ao ?leo analisado para tentar equacionar todos os par?metros e assim formular um biolubrificante n?o t?xico para aplicar nos processos de usinagem da ind?stria metal-mec?nica

Made available in DSpace on 2014-12-17T14:58:23Z (GMT). No. of bitstreams: 1 RubensCA_DISSERT3.pdf: 2459942 bytes, checksum: f001281d5b69338e66d3fe7b5d544a25 (MD5) Previous issue date: 2013-08-09 / Os pol?meros biodegrad?veis, como o poli?cido l?ctico (PLA) apesar de consolidado nos campos farmac?uticos, m?dico e biom?dico como biomateriais ?teis para aplica??es variadas, por?m, depende da necessidade de funcionalizar a sua superf?cie estudando suas propriedades tais como hidrofilidade e hidrofobicidade favorecendo a intera??o do pol?mero com os materiais de aplica??o farmac?utica, m?dica e biom?dica. Este trabalho tem como objetivo produzir um material com caracter?sticas diferentes em cada um de seus lados, sendo um lado hidrof?lico e o outro hidrof?bico. O substrato t?xtil utilizado neste estudo foi um tecido de malha de composi??o 100% PLA que ? biodegrad?vel e biocompat?vel, o que possibilita sua aplica??o na ?rea biom?dica. Para modifica??o superficial foi utilizado o tratamento a plasma de baixa press?o. A t?cnica de modifica??o de superf?cie por plasma foi escolhida por ser uma tecnologia limpa, anticorrosiva e n?o t?xica ao contrario de muitos processos qu?micos convencionais utilizados na ind?stria t?xtil, al?m disso, n?o afeta as propriedades de massa do substrato. Neste estudo, um lado da superf?cie do substrato foi tratado com plasma oxig?nio, arg?nio e nitrog?nio, para o trabalho de melhoria da hidrofilidade da superf?cie e metano para a hidrofobicidade da amostra. A espectroscopia de emiss?o ?tica (OEE) foi utilizada para fazer o diagn?stico das esp?cies do plasma durante o tratamento. Ap?s o tratamento a plasma as amostras foram caracterizadas por medidas de ?ngulo de contato, microscopia eletr?nica de varredura (MEV), Espectroscopia de fotoel?trons de raios-X (XPS), Infravermelho com Transformada de Fourier (FTIR) de reflex?o total atenuada (ATR), medidas da ?rea de espalhamento do l?quido e arraste vertical. Onde foi caracterizado o aumento e diminui??o da molhabilidade das amostras tratadas por plasma bem como as vari?veis que contribu?ram para tal efeito. O tratamento das amostras de PLA com O2 + CH4 apresenta comportamento hidrof?lico no lado tratado com O2, apresentando aumento de rugosidade e grupos funcionais e no lado tratado com CH4, apresentando a forma??o de um filme polim?rico formado sobre a superf?cie da amostra. O tratamento com N2 + CH4 apresenta comportamento hidrof?bico, por?m com varia??es no fluxo do CH4 tem-se um controle da molhabilidade na superf?cie das amostras, podendo ir de hidrof?bico a hidrof?lico, neste tratamento as amostras apresentaram pequenas diferen?as de molhabilidade entre os lados tratados com plasma de N2 e com plasma de CH4

Made available in DSpace on 2014-12-17T14:58:23Z (GMT). No. of bitstreams: 1 ErissonADL_DISSERT.pdf: 1589862 bytes, checksum: 6b02f85f6525d125a48a0c38ad306945 (MD5) Previous issue date: 2013-08-09 / O gradiente t?rmico da superf?cie para o interior do s?lido depende da taxa de colis?es das part?culas e da condutividade t?rmica do material utilizado. Quando um s?lido ? imerso em plasma, a transfer?ncia de energia ocorre por radia??o e colis?es das part?culas sobre a superf?cie do material. Dependendo da taxa de colis?es das particulas e da condutividade t?rmica do s?lido existir?o gradientes t?rmicos da superf?cie para o interior das amostras, ocorrendo picos t?rmicos na superficie, ou seja, o aquecimento pontual nas regi?es de colis?es. A fim de estudar esse efeito, amostras de a?o r?pido AISI M35 cujos valores de dureza s?o fortemente sens?veis ? temperatura de revenimento, foram utilizadas como micro sensores t?rmicos. Amostras foram temperadas em forno resistivo e, em seguida, parte das mesmas foram revenidas em forno resistivo e a outra parte em plasma. A partir do gr?fico da dureza (Hv) em fun??o da temperatura (T) das amostras revenidas em forno resistivo foi poss?vel obter uma fun??o Hv(T) para determina??o indireta do perfil t?rmico das amostras tratadas em plasma. As amostras foram revenidas em plasma utilizando temperatura de refer?ncia igual a 550 oC. Em seguida foi obtido o perfil de dureza dessas amostras ao longo da se??o transversal e, subsequentemente, o perfil de temperatura. Verificou-se que amostras tratadas em plasma, ao contr?rio daquelas tratadas em forno resistivo, apresentaram gradiente de temperatura da superf?cie para o n?cleo. Al?m disso, verificou-se que as amostras tratadas em configura??o planar apresentaram gradientes t?rmicos inferiores ?quelas tratadas em configura??o c?todo oco, variando de 20 a 120 ?C, respectivamente

Made available in DSpace on 2014-12-17T14:58:24Z (GMT). No. of bitstreams: 1 AngelicaGSL_DISSERT.pdf: 1633829 bytes, checksum: a49da749db1c036dad950f4eca7e9db7 (MD5) Previous issue date: 2011-02-28 / The segment of the structural ceramics industry is one of the most important to the economy of Rio Grande do Norte. The supply chain makes a total of 206 companies that are distributed in 39 counties, concentrated in three regional centers: Serid? Apodi / Assu and great Natal. The ceramic industry in the state is around 80 million pieces per month, with 50,186 million of these tiles, which makes the Rio Grande do Norte one of the largest manufacturers of product in the Country. Different ceramic products can be manufactured by mixing two or more clays and accessory minerals. Mixtures acquire characteristics and form what is called the ceramic body. Refractory masses have a high melting point and thermal shock support. Its composition contains refractory clays with a little iron oxide and material fluxes. A line of semi-refractory ceramic products that stands out for its high added value are the bricks in ivory or red, used in building barbecues, fireplaces, wood stoves and braziers. The aim of this study was to use alumina-clay or silica- alumina-clay to the industrial RN, for the production of refractory bricks semi-refractory burning light. Clay and Kaolin were characterized for their chemical and mineralogical composition, immediately after ceramic bodies were made with different concentrations of the components, they were raised, pressed and sintered. After sintering the resulting products were characterized in terms of mechanical, thermal and dimensional than the characterization by X-ray diffraction and scanning electron microscopy. After obtaining the results, we concluded that the studied clay can be used for the production of semi-refractory bricks / O segmento da ind?stria cer?mica estrutural ? um dos mais importantes para a economia do Rio Grande do Norte. A cadeia produtiva soma um total de 206 empresas que est?o distribu?das em 39 munic?pios e concentradas em tr?s p?los regionais: Serid?, Apodi/Assu e na grande Natal. A produ??o da ind?stria cer?mica no Estado gira em torno de 80 milh?es de pe?as/m?s, sendo 50.186 milh?es delas telhas, o que faz do Rio Grande do Norte um dos maiores fabricantes do produto no Pa?s. Diferentes produtos cer?micos podem ser fabricados atrav?s da mistura de duas ou mais argilas com minerais acess?rios. As misturas adquirem caracter?sticas pr?prias e formam o que se denomina massa cer?mica. Massas refrat?rias apresentam alto ponto de fus?o e suportam choque t?rmico. Sua composi??o cont?m argilas refrat?rias pobres em ?xido de ferro e materiais fundentes. Uma linha de produtos cer?micos semi-refrat?rios que se destaca pelo seu alto valor agregado s?o os tijolos aparentes na cor marfim ou avermelhado, utilizados na constru??o de churrasqueiras, lareiras, fog?es a lenha e braseiros. O objetivo do presente trabalho foi estudar a utiliza??o de argilas aluminosas ou s?lico-aluminosas do parque industrial do RN, para a produ??o de tijolos semi-refrat?rios de queima clara. A argila e o caulim foram, caracterizadas quanto ? sua composi??o qu?mica e mineral?gica, logo ap?s foram formuladas massas cer?micas com diferentes concentra??es dos componentes, estas foram formuladas, prensadas e sinterizadas. Ap?s a sinteriza??o os produtos resultantes foram caracterizados do ponto de vista mec?nico, t?rmico e dimensional al?m da caracteriza??o por difratometria de raios-X e microscopia eletr?nica de varredura. Com a obten??o dos resultados pudemos concluir que a argila estudada pode ser utilizada para a produ??o de tijolos semi-refrat?rios

Made available in DSpace on 2014-12-17T14:58:25Z (GMT). No. of bitstreams: 1 EylissonAS.pdf: 1489335 bytes, checksum: 8fcffdaaafca0f8691545bd2bc5dd5fc (MD5) Previous issue date: 2007-07-26 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / With the current growth in consumption of industrialized products and the resulting increase in garbage production, their adequate disposal has become one of the greatest challenges of modern society. The use of industrial solid residues as fillers in composite materials is an idea that emerges aiming at investigating alternatives for reusing these residues, and, at the same time, developing materials with superior properties. In this work, the influence of the addition of sand, diatomite, and industrial residues of polyester and EVA (ethylene vinyl acetate), on the mechanical properties of polymer matrix composites, was studied. The main objective was to evaluate the mechanical properties of the materials with the addition of recycled residue fillers, and compare to those of the pure polyester resin. Composite specimens were fabricated and tested for the evaluation of the flexural properties and Charpy impact resistance. After the mechanical tests, the fracture surface of the specimens was analyzed by scanning electron microscopy (SEM). The results indicate that some of the composites with fillers presented greater Young s modulus than the pure resin; in particular composites made with sand and diatomite, where the increase in modulus was about 168 %. The composites with polyester and EVA presented Young s modulus lower than the resin. Both strength and maximum strain were reduced when fillers were added. The impact resistance was reduced in all composites with fillers when compared to the pure resin, with the exception of the composites with EVA, where an increase of about 6 % was observed. Based on the mechanical tests, microscopy analyses and the compatibility of fillers with the polyester resin, the use of industrial solid residues in composites may be viable, considering that for each type of filler there will be a specific application / Com o crescimento acelerado do consumo de produtos industrializados, principalmente de produtos descart?veis, o aumento excessivo de lixo e sua disposi??o em lugares inadequados tornaramse um dos grandes problemas da sociedade moderna. A utiliza??o de res?duos s?lidos industriais como carga em comp?sitos ? uma id?ia que surge com o intuito de buscar alternativas adequadas para o reaproveitamento desses res?duos, visando tamb?m o desenvolvimento de materiais com propriedades superiores ?quelas dos materiais convencionais. Neste trabalho, estudouse a influ?ncia da adi??o de res?duos industriais de poli?ster e EVA (Etileno Acetato de Vinila), al?m de cargas de areia e diatomita, nas propriedades mec?nicas de comp?sitos de matriz poli?ster. O principal objetivo foi avaliar o comportamento mec?nico desses materiais com a adi??o de cargas de res?duo industrial, comparandoos com as propriedades da resina pura. Corposdeprova foram confeccionados e as propriedades mec?nicas dos comp?sitos obtidos foram analisadas, atrav?s de testes de flex?o e de impacto. Ap?s os ensaios mec?nicos, a superf?cie de fratura dos corposdeprova foi analisada por microscopia eletr?nica de varredura (MEV). Os resultados dos ensaios de flex?o mostraram que alguns comp?sitos apresentaram maior m?dulo, quando comparados com os resultados da resina pura; com destaque para os confeccionados com areia e diatomita, em que o aumento do m?dulo chegou a 168 %. Os comp?sitos confeccionados com adi??o de poli?ster e de EVA apresentaram m?dulo mais baixo que o da resina pura. Tanto o limite de resist?ncia quanto ? deforma??o m?xima, apresentaram redu??o nos seus valores, quando da adi??o de cargas. A resist?ncia ao impacto, em rela??o ? resina pura, foi reduzida em todos os comp?sitos com adi??o de cargas, exceto nos comp?sitos com a adi??o de EVA, onde houve um aumento de aproximadamente 6 %. Com base nos ensaios mec?nicos realizados, nas an?lises microsc?picas e na compatibilidade das cargas com a resina poli?ster, a utiliza??o das cargas de res?duos s?lidos industriais em comp?sitos mostrouse vi?vel, considerando que para cada tipo de carga haver? uma aplica??o espec?fica

Made available in DSpace on 2014-12-17T14:58:25Z (GMT). No. of bitstreams: 1 JairJF.pdf: 2118610 bytes, checksum: 58b235c37b06aad236571a4bddf0bd41 (MD5) Previous issue date: 2007-07-06 / Improving the adherence between oilwell metallic casing and cement sheath potentially decrease the number of corrective actions present/y necessary for Northeastern wells submitted to steam injection. In addition to the direct costs involved in the corrective operations, the economic impact of the failure of the primary cementing aIso includes the loss in the production of the well. The adherence between casing and cement is current/y evaluated by a simple shear tests non standardized by the American Petroleum Institute (API). Therefore, the objective of the present is to propose and evaluate a standardized method to assess the adherence of oilwell metallic casing to cement sheath. To that end, a section of a cemented oilwell was simulated and used to test the effect of different parameters on the shear stress of the system. Surface roughness and different cement compositions submitted or not to thermal cycling were evaluated. The results revealed that the test geometry and parameters proposed yielded different values for the shear stress of the system, corresponding to different adherent conditions between metallic casing and cement sheath / A boa ader?ncia mec?nica entre o revestimento met?lico e a bainha cimentante de po?os de petr?leo pode diminuir a freq??ncia de opera??es de cimenta??o corretivas hoje verificadas, principalmente na regi?o Nordeste, em po?os sujeitos ? inje??o de vapor. Al?m do custo direto de cada opera??o corretiva, o impacto econ?mico da falha da cimenta??o prim?ria tamb?m inclui a parada de produ??o do po?o. Atualmente, a ader?ncia entre o cimento e o revestimento ? aferida por meio de uma metodologia de ensaio, n?o padronizada pelas normas do American Petroleum Institute (API), que consiste em mensurar a resist?ncia ao cisalhamento entre um tubo de a?o e o cimento. Este trabalho tem por meta criar uma proposta de metodologia para padronizar os ensaios de ader?ncia de cimentos para po?os de petr?leo sobre revestimentos met?licos. Para isso utilizou-se a simula??o de um trecho de po?o cimentado. Tamb?m se usou o ensaio para caracterizar a sensibilidade das condi??es superficiais dos tubos, sem tratamento e com tratamento de hidrojateamento, assim como o comportamento termo-mec?nico de cimentos em contato com revestimento. Estes ensaios foram usados para validar novas pastas cimentantes desenvolvidas em fun??o de diferentes condi??es de po?o e m?todos avan?ados de recupera??o de ?leo. Por meio desses ensaios, com o uso de diferentes condi??es de superf?cie, aplica??o de diferentes composi??es de cimentos e varias formas de aquecimento ao sistema, foi poss?vel constatar que a geometria de ensaios proposta ? sens?vel a altera??es na ader?ncia do conjunto, causadas por situa??es reais encontradas nas condi??es. de po?os, especialmente aqueles sujeitos ? inje??o de vapor

Made available in DSpace on 2014-12-17T14:58:25Z (GMT). No. of bitstreams: 1 EleniseBBA.pdf: 2555564 bytes, checksum: 204e9e7884310336d7433cc3d80fd571 (MD5) Previous issue date: 2007-01-24 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / It?s been motivating motivated by the current rulers as an energy solution the use of the biodiesel as source of energy, that doesn't damage the environment and promotes the development of the areas where the base plant are grown. The process of production of the biodiesel, starting from the castor oil plant and its derivers, generates a known product as castor oil plant pie that has been used as fertilizer. Once disintoxicated, it can serve as animal ration, because it contains high content of proteins, presenting larger joined value. The disintoxication process, can be obtained through the process of drying the pie with the construction and use of models of dryers capable to elevate the temperature of the castor oil plant pie to approximately 60?C.In this temperature the product tends to eliminate the ricina, with the aid of an aqueous solution of hydroxide of calcium, or still reach higher temperatures to make the disintoxication without a chemical treatment. It was made a bibliographical research about known processes of disintoxication of the castor oil plant pie from the autoclave use to the drying direct exposure to the sun. Starting from the state of the art and identification of the object, it was chosen solar dryers to eliminate the ricina. It was applied two types of solar dryers: the one of solar direct exposure, and the one with concentrador. The castor oil plant pie was separated in samples, with measurement of its initial mass, codified and placed in the dryers. The results were presented in graphs and tables forms, with the values of temperatures noticed. It was noticed the variations of temperature and the relationships analyzed related with the ricina content eliminated from the pie. The analysis of the ricina content was accomplished by Embrapa - Campina Grande, by eletroforese method. The analysis of the result of considering the content of ricina of the samples. It was observed that, we obtained lower rate of ricina in samples that had larger drying time and average value temperature above 60?C. Comparing with the ones submitted to higher temperatures and in a shorter period of time. It was possible to evaluate the efficiency of the dryers in the desintoxication process of the samples, as well as the type of more appropriate dryer for the drying pie process. Finally, it was concluded that the solar dryer with concentrador presents higher values temperatures than the direct exposure one. So, it?s being more opportune applied in the castor oil plant pie drying process. However, more than one hour for drying time is needed / O uso do biodiesel como fonte de energia, que n?o danifica o meio ambiente e promove o desenvolvimento das regi?es que plantam as mat?rias primas para sua fabrica??o, ? uma alternativa energ?tica incentivada pelos atuais governantes. O processo de fabrica??o do biodiesel, a partir do ?leo de mamona e seus derivados, gera um subproduto conhecido como torta de mamona que vem sendo utilizada como adubo. Desintoxicada ela poder? servir como ra??o animal, tendo em vista o alto teor de prote?nas, apresentando, assim, maior valor agregado. A desintoxica??o pode ser obtida por meio do processo de secagem da torta com a constru??o e utiliza??o de modelos de secadores capazes de elevar a temperatura da torta de mamona a aproximadamente 60?C. Ao atingir essa temperatura, o produto tende a eliminar a ricina, com o aux?lio de uma solu??o aquosa de hidr?xido de c?lcio ou ainda atingir temperaturas maiores para realizar a desintoxica??o sem o tratamento qu?mico. Realizou-se um levantamento bibliogr?fico quanto aos processos conhecidos para a desintoxica??o da torta de mamona que v?o desde o uso de autoclave at? a secagem ao sol. A partir do estado da arte e identifica??o do objeto optou-se eliminar a ricina por meio de secadores solares, sendo utilizados dois tipos de secadores o solar de exposi??o direta e o solar com concentrador. A torta de mamona foi separada em amostras, com medi??o de sua massa inicial, codificada e colocada nos secadores. Os resultados apresentados sob a forma de gr?ficos e tabelas, com valores de temperaturas, permitiram que fossem analisadas suas varia??es e as rela??es com o teor de ricina eliminado da torta. A an?lise do teor de ricina foi realizada pela Embrapa -Campina Grande, pelo m?todo de eletroforese. No resultado da an?lise do teor de ricina das amostras, observou-se que aquelas que tiveram maior tempo de secagem e valor de temperatura em m?dia acima de 60?C apresentavam uma menor taxa de ricina em compara??o com as submetidas a maiores temperaturas por um curto per?odo de tempo, assim foi poss?vel avaliar a efici?ncia dos secadores na desintoxica??o das amostras, bem como o tipo de secador mais apropriado para o processo de secagem da torta. Conclui-se, finalmente, que o secador solar com concentrador apresenta valores de temperaturas mais elevados quando comparado com o de exposi??o direta, sendo ent?o mais oportuno na secagem da torta de mamona, por?m ? necess?rio um tempo superior a 1 hora de secagem

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2018-01-23T14:20:38Z No. of bitstreams: 1 EduardoCampeloSoeiro_TESE.pdf: 5583136 bytes, checksum: 5052818cde51c6a095f3a8e0f7fa74bc (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2018-01-24T15:35:17Z (GMT) No. of bitstreams: 1 EduardoCampeloSoeiro_TESE.pdf: 5583136 bytes, checksum: 5052818cde51c6a095f3a8e0f7fa74bc (MD5) / Made available in DSpace on 2018-01-24T15:35:17Z (GMT). No. of bitstreams: 1 EduardoCampeloSoeiro_TESE.pdf: 5583136 bytes, checksum: 5052818cde51c6a095f3a8e0f7fa74bc (MD5) Previous issue date: 2017-09-25 / Nos ?ltimos anos, a preocupa??o com a preserva??o do meio ambiente tem incentivado as pesquisas de novos materiais que utilizem mat?rias primas de fontes naturais renov?veis. Neste trabalho, foram produzidos materiais comp?sitos a partir da associa??o da espuma r?gida de poliuretano, derivado do ?leo de mamona, e o p? de macambira (Brom?lia Laciniosa). Produziram-se tr?s composi??es em molde fechado com 5, 10 e 15% em massa do p? de macambira, denominados PU5, PU10 e PU15, al?m da espuma r?gida de poliuretano puro, PU. As espumas r?gidas de PU e seus comp?sitos foram caracterizados fisicamente atrav?s da densidade aparente, absor??o de ?gua e teor de umidade. A morfologia foi observada atrav?s de imagens feitas por micrografia eletr?nica de varredura (MEV). A identifica??o dos principais grupos org?nicos foi poss?vel com a espectroscopia de infravermelho com transformada de Fourier (FTIR). Foram realizados ensaios de compress?o, tra??o, flex?o em tr?s pontos e dureza para avaliar o comportamento mec?nico. Al?m disso, as an?lises de DRX possibilitaram a determina??o da cristalinidade do material. A termogravimetria possibilitou determina??o das temperaturas limite de resist?ncia ? degrada??o t?rmica dos materiais. Par?metros como a capacidade calor?fica, a condutividade, difusividade e resistividade t?rmicas tamb?m foram determinados. Os comp?sitos PU10 e PU15 apresentaram propriedades t?rmicas semelhantes ao poliuretano puro. Isso mostrou que a utiliza??o do p? de macambira como carga nas propor??es de 10 e 15% em massa ? vi?vel, uma vez que, apesar das semelhan?as nas propriedades, as espumas comp?sitos apresentam vantagens do ponto de vista ambiental e econ?mico, pois parte do volume da espuma ? ocupado pelo p? de macambira, um material biodegrad?vel originado de fonte renov?vel. / In recent years, concern for the preservation of the environment has encouraged research into new materials that use raw materials from renewable natural sources. In this work, composite materials were produced from the association of rigid polyurethane foam derived from castor oil and macambira powder (Bromelia Laciniosa). Three compositions in closed mold with 5, 10 and 15% by mass of the macambira powder, denominated PU5, PU10 and PU15, were produced in addition to the rigid polyurethane rigid PU foam. The rigid PU foams and their composites were physically characterized by apparent density, water absorption and moisture content. The morphology was observed through images made by scanning electron micrograph (SEM). The identification of the main organic groups was possible with Fourier Transform Infrared Spectroscopy (FTIR). Compression, tensile, three point bending and hardness tests were performed to evaluate the mechanical behavior. In addition, the XRD analyzes enabled the determination of the crystallinity of the material. Thermogravimetry allowed the determination of the limiting temperatures of resistance to the thermal degradation of the materials. Parameters such as heat capacity, conductivity, diffusivity and thermal resistivity were also determined. The PU10 and PU15 composites presented thermal properties similar to pure polyurethane. This showed that the use of the macambira powder as a filling in the proportions of 10 and 15% by mass is feasible, because, despite the similarities in properties, the composite foams have advantages from the environmental and economic point of view, since part of the volume of the foam is occupied by the macambira powder, a biodegradable material originating from a renewable source.

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2018-01-23T14:20:39Z No. of bitstreams: 1 ElisangelaBezerraDasNevesHolanda_TESE.pdf: 6612707 bytes, checksum: f9d2acfe515476ab9c03e0ac3ce7b4c2 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2018-01-24T15:42:12Z (GMT) No. of bitstreams: 1 ElisangelaBezerraDasNevesHolanda_TESE.pdf: 6612707 bytes, checksum: f9d2acfe515476ab9c03e0ac3ce7b4c2 (MD5) / Made available in DSpace on 2018-01-24T15:42:12Z (GMT). No. of bitstreams: 1 ElisangelaBezerraDasNevesHolanda_TESE.pdf: 6612707 bytes, checksum: f9d2acfe515476ab9c03e0ac3ce7b4c2 (MD5) Previous issue date: 2017-08-14 / Os nanotubos de carbono de multicamadas (MWCNT) incorporados ? materiais de origem proteicas podem contribuir para o surgimento de interessantes biomateriais comp?sitos com grande potencial de aplica??es biol?gicas. Os MWCNT s?o promissores vetores de DNA em c?lulas e embri?es de seres vivos. Por?m, o desencadeamento do seu uso na ?rea biom?dica est? relacionado ? padroniza??o de sistemas e protocolos para avaliar os potenciais impactos na sa?de humana e no meio ambiente. O objetivo geral deste estudo foi avaliar o efeito da funcionaliza??o, a citotoxicidade e a ades?o celular dos nanotubos de carbono na sua forma comercial e modificados por diferentes processos em c?lulas macr?fagos (J774 e RAW). Nesta pesquisa, inicialmente foram realizados diferentes processos de funcionaliza??o nos MWCNT visando a inser??o de grupos funcionais e poss?vel compatibilidade com biopol?meros. Ap?s a funcionaliza??o os MWCNT foram caracterizados por diferentes t?cnicas e realizados os ensaios de citotoxicidade e a eletroan?lise. Os biopol?meros utilizados para a funcionaliza??o do substrato t?xtil da prote?na da soja foram o col?geno extra?do da pele da til?pia e o col?geno comercial. Os substratos t?xtis foram funcionalizados atrav?s do processo Dip coating e em seguida, foram incorporados os nanotubos de carbono pelo mesmo processo. Os resultados obtidos atrav?s das an?lises do processo de funcionaliza??o dos MWCNT revelaram que as amostras funcionalizadas com a quitosana tende a aumentar o di?metro do tubo devido a forma??o de uma monocamada polim?rica em sua superf?cie e que os melhores resultados de oxida??o foram para as amostras que passaram pelo processo de funcionaliza??o ?cida e funcionaliza??o ?cida com quitosana. Os resultados obtidos pela Espectroscopia Raman comprovaram que o processo de funcionaliza??o foi realizado com ?xito, possibilitando a inser??o de grupos funcionais sobre os nanotubos. A eletroan?lise nos nanotubos mostraram que os maiores valores da capacit?ncia por massa e por ?rea foram para as amostras funcionalizadas com ?cidos e que a adi??o da quitosana durante a funcionaliza??o aumenta a resist?ncia ? passagem da corrente, al?m de provocar um efeito isolante. Os ensaios de citotoxicidade dos MWCNT realizadas em macr?fagos nas concentra??es de 100, 75, 50, 25 e 5 ?g/mL demonstraram um percentual em torno de 95% de viabilidade celular para as amostras funcionalizadas com ?cido e quitosana para todas as concentra??es. Os ensaios de ades?o celular nos MWCNT revelaram excelentes intera??es em concentra??es mais elevadas para todas as amostras de nanotubos. A observa??o visual do efeito da modifica??o do substrato t?xtil com o col?geno indicou que o tipo e a origem da prote?na interferem no efeito da imobiliza??o dos nanotubos de carbono. Em conclus?o, as exposi??es de macr?fagos a baixas concentra??es de MWCNT funcionalizados n?o causaram impacto na viabilidade celular, o que abre as possibilidades de diversos estudos para potencializar aplica??es na ?rea biol?gica. / The multiwalled carbon nanotubes (MWCNT) incorporated into the materials of protein origin can contribute to the emergence of interesting composite biomaterials with great potential of biological applications. MWCNT are promising DNA vectors in living cells and embryos. However, the triggering of its use in the biomedical area is related to the standardization of systems and protocols to assess the potential impacts on human health and the environment. The general objective of this study was to evaluate the effect of functionalization, cytotoxicity and cellular adhesion of carbon nanotubes in their commercial form and modified by different processes in macrophages (J774 and RAW). In this research, different functionalization processes were initially performed in the MWCNT, aiming at the insertion of functional groups and possible compatibility with biopolymers. After functionalization, the MWCNT were characterized by different techniques and performed the cytotoxicity and electroanalysis tests. The biopolymers used for the functionalization of the textile substrate of the soy protein were the collagen extracted from the skin of the tilapia and the commercial collagen. The textile substrates were functionalized through the dip coat process and then the carbon nanotubes were incorporated by the same process. The results obtained through the analysis of the functionalization process of the MWCNT revealed that the functionalized samples with chitosan tend to increase the diameter of the tube due to the formation of a polymeric monolayer on its surface and that the best oxidation results were for the samples that passed by the process of acid functionalization and acid functionalization with chitosan. The results obtained by Raman Spectroscopy proved that the functionalization process was successful, allowing the insertion of functional groups on the nanotubes. The electroanalysis in the nanotubes showed that the highest values of capacitance per mass and per area were for the acid functionalized samples and that the addition of chitosan during functionalization increases the resistance to current flow, besides provoking an insulating effect. The cytotoxicity tests of MWCNT performed on macrophages at concentrations of 100, 75, 50, 25 and 5 ?g / mL demonstrated a percentage of around 95% cell viability for acid and chitosan functionalized samples at all concentrations. Cell adhesion assays in MWCNTs showed excellent interactions at higher concentrations for all nanotube samples. Visual observation of the effect of modification of the textile substrate with collagen indicated that the type and origin of the protein interfere with the immobilization effect of the carbon nanotubes. In conclusion, macrophage exposures at low concentrations of functionalized MWCNT had no impact on cell viability, which opens the possibilities of several studies to potentiate applications in the biological field.