Made available in DSpace on 2014-06-11T19:35:13Z (GMT). No. of bitstreams: 0 Previous issue date: 2012-04-05Bitstream added on 2014-06-13T21:07:35Z : No. of bitstreams: 1 watanabe_s_dr_araca.pdf: 1959528 bytes, checksum: 1744de13ccd7ec1e15e0ab0dbd88c788 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / O objetivo deste estudo foi avaliar a resposta tecidual frente ao implante de tubos de polietileno preenchidos pelos cimentos Sealapex®, Endo-CPM-Sealer® e MTA Fillapex® em tecido subcutâneo de ratos, bem como avaliar o processo de reparo de dentes de cães com lesão periapical, obtida experimentalmente, obturados com os mesmos cimentos. Para o teste de biocompatibilidade foram utilizados 30 ratos, os quais receberam individualmente três implantes de tubos de polietileno contendo os cimentos a serem testados e mais um tubo vazio como controle. Os períodos de avaliação foram de 7, 15, 30, 60 e 90 dias. Os espécimes foram processados laboratorialmente e analisados nas colorações de Hematoxilina e Eosina, Von Kossa e sem coloração para análise sob luz polarizada. Foram atribuídos escores e os dados obtidos foram analisados pelo teste Kruskal Wallis. Todos os materiais causaram reações moderadas no tempo experimental de 7 dias. A resposta foi moderada e similar para o grupo controle no 15° dia com Sealapex® e Endo-CPM-Sealer®. O grupo MTA Fillapex® apresentou reações leves a partir do 15° dia. Mineralizações e granulações brirrefringentes à luz polarizada foram observadas com todos os materiais. Foi possível concluir que todos os materiais testados apresentaram resultados similares, sendo considerados biocompatíveis e estimulantes de mineralização. Para a avaliação do processo de reparo de dentes de cães com lesão periapical, obtida experimentalmente, foram empregados 62 canais radiculares de 2 cães machos da raça Beagle. Os animais foram anestesiados, as polpas foram extirpadas e os canais ficaram expostos ao meio oral para o desenvolvimento de lesões periapicais. Após 6 meses os dentes foram tratados endodonticamente e foram divididos em 5 grupos experimentais... / The aim of this study was to evaluate the tissue response to implanted polyethylene tubes filled with Sealapex®, Endo-CPM-Sealer® and MTA Fillapex® in rat subcutaneous tissue, and to evaluate the healing process of dogs' teeth with experimental periapical lesions filled with the same sealers. For the biocompatibility test, it were used thirty rats, which received three individual implants of polyethylene tubes containing the sealers to be tested and an empty tube as control. Evaluations periods were on 7, 15, 30, 60 and 90 days. The specimens were laboratory processed and analyzed in Hematoxylin and Eosin, Von Kossa and without staining for polarized light. Scores were assigned and data were analyzed by Kruskal Wallis test. Both materials caused mild to moderate reactions on 7 days. The response was moderate and similar to the control at the 15th day with Sealapex® and Endo-CPM-Sealer®. MTA Fillapex® evoked mild reactions from the 15th day on. Mineralization and granulations birefringent to the polarized light were observed with all materials. It was possible to conclude that all materials tested showed similar results and they are considered biocompatible and stimulating mineralization. For the evaluation of the healing process of dogs' teeth with periapical lesions, sixty-two roots canals of two male beagle dogs were used. The animals were anesthetized, pulpectomy were performed and the canals remained open and exposed to the oral environment to induce a periapical lesion. After 6 months the teeth were endodontically treated and divided into 5 experimental groups, according to the filling material: Group I Sealapex®; Group II – Endo-CPM-Sealer®; Group III – MTA Fillapex®; Group IV – positive control; Group V – negative control. After 180 days, the animals were killed, the specimens were removed... (Complete abstract click electronic access below)

Made available in DSpace on 2015-05-14T16:53:13Z (GMT). No. of bitstreams: 0 Previous issue date: 2014-04-08Bitstream added on 2015-05-14T16:59:11Z : No. of bitstreams: 1 000822661.pdf: 3005956 bytes, checksum: aa617124450c9641b6ecb66c3cbbdaa9 (MD5) / Comparou-se a resistência de união (RU) dos cimentos resinosos Panavia F (P) (Kuraray) e RelyX U200 (R) (3M ESPE) à cerâmica zircônia através de três diferentes métodos de tratamento da superfície: 1- silicatização triboquímica (ST) (Rocatec Soft - 3M ESPE); 2- glaze (G) (Akyzent glaze spray- VITA); 3- aplicação de vidro bioativo (VBA). Blocos pré-sinterizados do sistema Zirkonzahn (Zirkonzahn) foram seccionados de modo a produzir 90 blocos menores (5 x 4 x 3 mm). Os blocos foram polidos em Politriz com lixas d’água de granulação fina 1000 e 1200 (3M ESPE) e limpos em banho ultrassônico contendo álcool isopropílico a 96% durante 5 min. Após a sinterização dos blocos cerâmicos, foi realizada a aplicação do tratamento de superfície. O Rocatec Soft foi jateado com 2,8 bar, ângulo de incidência perpendicular e distância padrão de 10 mm por 25 s em movimentos circulares. O Akyzent Glaze Spray foi pulverizado por 2 s e em seguida sinterizado em forno Vacumat (Vita) de acordo com recomendações do fabricante. Após a aplicação de 1 gota do vidro bioativo, procedeu-se a secagem e sinterização a 1200 ºC deste material. Em todos os grupos aplicou-se agente de união silano Monobond-S (Ivoclar Vivadent). Nos grupos 3, 4, 5 e 6 a superfície foi primeiramente condicionada com ácido hidrofluorídrico (HF) a 5% durante 2 min, lavada e depois silanizada. A cimentação foi realizada com um dispositivo (Ultradent), produzindo cilindros de cimento resinoso com 2 x 1mm.! Após 24 h os espécimes foram envelhecidos em termocicladora com 5.000 ciclos com banhos de temperatura entre 5 e 55 ºC e submetidos ao ensaio de cisalhamento na Shear Bond Tester (Bisco). O VBA foi analisado qualitativamente por meio de análise térmica diferencial (DTA), através de difração de raios-x (DRX)(Panalytical) e espectroscopia de energia dispersiva de raio-x (EDS) (Oxford Instruments)... / The bond strength of resin cements Panavia F (P) (Kuraray) and RelyX U200 (R) (3M ESPE) to zirconia using three different surface treatments: 1 - triboquemical silicatization (ST); 2 - glaze (G) 3 - bioactive glass (VBA) was compared. Blocks of Zirkonzahn system were cut producing 90 smaller blocks (5 x 4 x 3 mm). The blocks were polished with water finegrained 1000 and 1200 sandpaper in Politriz and cleaned with 96% isopropyl alcohol for 5 min. The Rocatec Soft was etched with 2.8 bar, in a perpendicular way and a distance of 10 mm for 25 s in a circular motion. The Akyzent Glaze Spray was sprayed by 2s and then sintered in oven Vacumat (Vita) according to manufacturer's recommendations. After application of 1 drop of bioactive glass, the material was dried and sintered at 1200 °C. In all groups was applied silane coupling agent Monobond- S (Ivoclar Vivadent). In groups 3, 4, 5 and 6 the surface was first etched with 5% hydrofluoric acid (HF) and then silanized. The cementing was carried out with a device (Ultradent), producing cured cement cylinders of 2 x 1mm. After 24 h the specimens were aged in thermocycler with 5,000 cycles at a temperature of 5 and 55 ºC and subjected to microshear test on Shear Bond Tester (Bisco). VBA was analyzed by means of DTA, XRD and EDS. Optical profilometry (PO) was performed to obtain roughness. After fracture the samples were analyzed through SEM. It was found that XRD revealed the formation of a glass ceramic film. DTA shows that the temperature of 1200 °C is the most suitable for sintering. DRX showed the formation of a glass ceramic film. According to ANOVA, the interaction effect was significant (p = 0.003 < 0.05). The test for multiple comparison of means, Tukey (5%) showed that the TBS (MPa) for VBA were significantly higher than the other groups (with 26.94 ± 3.50 to P and 28.36 ± 3.32 to R), regardless cement kind used. The lowest result...

Made available in DSpace on 2015-06-17T19:33:56Z (GMT). No. of bitstreams: 0 Previous issue date: 2015-02-23. Added 1 bitstream(s) on 2015-06-18T12:47:49Z : No. of bitstreams: 1 000830347.pdf: 242986 bytes, checksum: 3957e431d5fb3368b3a93a697bd645dd (MD5) / Enterococcus faecalis é uma bactéria Gram-positiva que pode resistir ao tratamento endodôntico e manter a infecção presente no sistema de canais radiculares. Assim, o uso de cimentos endodônticos com atividade antimicrobiana pode ajudar a eliminar microrganismo residuais que sobreviveram após o tratamento endodôntico. Diante dessa realidade, o presente estudo teve por objetivo avaliar comparativamente a ação antimicrobiana dos cimentos endodônticos Acroseal, Sealapex e AH Plus em um modelo de biofilme in vitro. Para a realização do estudo foram confeccionados 144 espécimes de dentina bovina, sendo doze blocos para cada cimento em cada tempo experimental que permaneceram em placas contendo meio de cultura inoculado com E. faecalis (ATCC 51299) para permitir a formação de biofilme. Decorrido 14 dias, os espécimes foram transferidos para outra placa onde discos dos cimentos testados foram colocados sobre o biofilme formado. As placas de cultura foram deixadas em estufa a 37°C e 5% de CO2 por 2, 7 e 14 dias. Espécimes sem aplicação dos cimentos foram utilizados como controle para cada período. Após cada tempo experimental, as amostras foram agitados em sonicador. As suspensões foram agitadas em vortex e foi realizada uma diluição seriada decimal em solução salina, sendo estas diluições plaqueadas em triplicata em meio de cultura m-Enterococcus ágar. As unidades formadoras de colônia foram contadas e os dados analisados estatisticamente usando os teste ANOVA, Shapiro-Wilk e Kruskal-Wallis one-way (p<0,05) para determinação do potencial antimicrobiano. Resultados: O Sealapex apresentou diferença estatística em todos os tempos experimentais quando comparado com os demais grupos. O AH Plus e o Acroseal mostraram atividade antimicroabina apenas no 14o dia de experimento. Conclusão: Nenhum... / Enterococcus faecalis is a gram positive bacteria that can resist to the endodontic therapy and maintain the infection present in the root canal system. Therefore, the use of endodontic sealers with antimicrobial activity could help to eliminate residual microorganism that have survived after endodontic treatment. The present study aimed to compare the antimicrobial activity of the endodontic sealers Acroseal, Sealapex and AH Plus in vitro biofilm model. It were prepared 144 bovine dentin specimens, twelve blocks for each cement in each experimental time that remained in plates containing culture medium inoculated with E. faecalis (ATCC 51299) for biofilm formation. After 14 days, the samples were transferred to another plate with test sealers and were kept at 37oC and 5% CO2 for 2, 7 and 14 days. Specimens without sealers were used as a control for each period. After each experimental, the samples were agitated in sonicator. The suspensions were agitated in vortex and serially diluted in saline and triple plaqued in m-Enterococcus agar. Colony forming unit were counted and the data were statistically analyzed using ANOVA, Shapiro-Wilk and Kruskal-Wallis one-way test (p<0.05) for the antimicrobial potential determination. Results: Sealapex showed significant difference in all experimental times in comparison to all other groups. AH Plus and Acroseal showed antimicrobial activity just at 14th experimental day. Conclusion: Neither of sealers setting tested was able to remove biofilm . The Sealapex showed higher antimicrobial activity in all experimental periods. All sealers examined the antimicrobial effectiveness was higher with over time

Made available in DSpace on 2015-09-17T15:24:52Z (GMT). No. of bitstreams: 0 Previous issue date: 2014-12-18. Added 1 bitstream(s) on 2015-09-17T15:47:05Z : No. of bitstreams: 1 000843350.pdf: 2776777 bytes, checksum: 117622a7940320916a6831aad9adae9a (MD5) / Objetivo: O objetivo deste estudo foi avaliar a influência do tempo de endurecimento sobre as propriedades físicas (teste de push-out) e biológicas (XTT, MNT) de sete cimentos endodônticos: Apexit Plus, Real Seal, Endo Rez, Roeko Seal, AH Plus, Endomethasone N e o cimento biocerâmico iRoot SP. Material e Métodos: Para a análise da citotoxicidade (XTT), foram utilizados fibroblastos do ligamento periodontal humano (PDLF). Para o número de micronúcleos (MNT), este estudo avaliou culturas de células expostas a diluições dos cimentos testados sobre células V79 No teste de push-out foram usados cento e quarenta dentes humanos unirradiculares que tiveram suas coroas removidas. Os canais radiculares foram preparados biomecanicamente com o sistema rotatório Mtwo (VDW GmbH, München, Alemanha) até o número de série 702 a 25 mm (25-40). Durante todo o preparo biomecânico, os canais foram irrigados com 2 ml de hipoclorito de sódio. Os espécimes foram seccionados em fatias de 2 mm nos terços cervical, médio e apical. O teste de Push-out foi realizado a uma velocidade de 1 mm / min e célula de carga de 50 Kgf. Os testes biológicos foram avaliadas após 24 h, 72 h, 1 semana, 1 mês, 3 meses, 6 meses e um ano após a manipulação e o teste de push-out 15 dias e 1 ano.Os dados foram analisados pelo teste de Kruskal-Wallis e teste de Dunn (p = 0,05). Resultados: IRooot SP, Roeko seal, Apexit Plus, AH Plus e Real Seal não mostraram citotoxicidade nas células PDLF. AH Plus, Real Seal, IRooot SP e Endomethasone N não apresentaram genotoxicidade. Roeko Seal e Apexit Plus mostraram ser genotóxico e EndoRez apresentou alta genotoxicidade. Roeko Seal, IRooot SP e EndoRez tiveram menor resistência à tração nos terços apical, médio e cervical, tanto em 15 dias e 1 ano de análise. Além disso, Endomethasone N, Real Seal e AH Plus apresentaram uma força de adesão satisfatória após 1 ano em todos os terços. Conclusão: conclui-se que... / Objective: The aim of this study was to evaluate the influence of curing time on physical (push-out test) and biological properties (XTT, MNT) of seven sealers: Apexit Plus, Royal Seal, Endo Rez, Roeko Seal, AH Plus, Endomethasone, and bioceramic cement iRoot SP. Material and Methods: To the citotoxity analysis (XTT), fibroblasts of the human periodontal ligament were used (PDLF). To the number of micronuclei (MNT), this study evaluated cell cultures exposed to dilutions of the tested sealers, among them from causing excessive cytotoxic effects on V79 cells. To push-out test was used one hundred and forty single-rooted teeth which had the crowns removed. The root canals were prepared biomechanically with the rotary system Mtwo (VDW GmbH, München, Alemanha) until to series number 702 to file 25 mm (25-40). Throughout the biomechanical preparation, the canals were irrigated with 2 ml of sodium hypochlorite. The specimens were sectioned in slices of 2 mm in cervical, middle and apical. The push-out test was performed at speed of 1 mm/min and 50 kgf load cell. The tests were evaluated after 24 h, 72 h, 1 week, 1 month, 3 months, 6 months and one year after manipulation. Data were analyzed by Kruskal-Wallis and Dunn test (p = 0.05). Results: IRooot SP, Roeko Seal, Apexit Plus, AH plus and Real Seal showed no cytotoxicity in PDLF cells. AH plus, Real Seal, IRooot SP and Endomethasone N showed no genotoxicity. Roeko Seal and Apexit Plus have shown to be genotoxic and EndoRez showed high genotoxicity. Roeko Seal, IRooot SP and EndoRez had lower bond strength in the apical, middle and cervical thirds in both the 15-day and 1 year analysis. Apexit Plus, Endomethasone N, Real Seal and AH plus had a satisfactory bond strength after 1 year in all thirds. Conclusion: It is conclude that AH plus and Real Seal were the sealer with lower cytotoxicity and genotoxicity, with good values of bond strength in all third, keeping as the material of choice for....

Made available in DSpace on 2014-08-13T14:51:01Z (GMT). No. of bitstreams: 0 Previous issue date: 2013-11-28Bitstream added on 2014-08-13T17:59:34Z : No. of bitstreams: 1 000776628.pdf: 1391190 bytes, checksum: 0560fce743da2fc01c2682581e067e18 (MD5) / Comparar a retenção de coroas de zircônia YTZP em função do protocolo de cimentação. Foram preparados para coroa total 108 molares extraídos (n = 12). Pinos de fibra de vidro foram cimentados e núcleos de resina composta construídos. Infraestruturas de zircônia YTZP foram fresadas e 72 espécimes foram alocados em 6 grupos conforme os fatores: cimento - Multilink (Mult) e Relyx ARC (Rel); e tratamento de superfície da zircônia – álcool (controle) (C), silicatização (S) e vitrificação (V). Os outros 36 espécimes foram divididos em 3 grupos cimentados com Relyx Luting (Ion), Relyx U100 (Self) e fosfato de zinco (Zinc) sem tratamento da zircônia. Todos os espécimes foram termociclados (5 - 55 ºC, 6000 ciclos) e os dados do teste de tração foram analisados pelo teste de Kruskal Wallis e Dunn. Os valores da mediana e distância interquartil foram os seguintes: MultC: 20,0 (± 5,5); MultS: 28,5 (± 22,0); MultV: 32,5 (± 28,5); RelC: 21,5 (± 8,5); RelS: 22,0 (± 10,0); RelV: 24,0 (± 7,3); Ion: 5,1 (± 6,4); Self: 3,5 (± 5,2); Zinc: 7,7 (± 14,2). O tipo de cimento resinoso (a base de Bis-GMA e HEMA) não afetaram os valores de retenção das coroas. O tratamento de superfície da cerâmica vitrificação somente foi capaz de melhorar os valores de retenção para o cimento a base de HEMA. Para superfícies cerâmicas não tratadas, os cimentos resinosos mostraram significantemente maiores valores de retenção do que aqueles obtidos para os cimentos auto-adesivo, de inonômero de vidro e de fosfato de zinco / To compare the retention of YTZP zirconia crowns cemented to different cementation protocols. 108 extracted molars were prepared for full crown (n = 12); and the core was reconstructed with glass fiber post and composite resin core. YTZP zirconia copings were milled and 72 specimens were divided into 6 groups according to the factors: cements- Multilink (Mult) and Relyx ARC (Rel); and zirconia surface treatments- alcohol (control) (C), silica coating (S) and vitrification (V). The remaining 36 specimens were divided into 3 groups cemented with Relyx Luting (Ion), Relyx U100 (Self) and Zinc phosphate (Zinc) on untreated zirconia. The specimens were thermally cycled (5 - 55 °C, 6000 cycles) and data from the tensile test were analyzed by Kruskal Wallis and Dunn test. The median and interquartil range were: MultC: 20.0 (± 5.5); MultS: 28.5 (± 22.0); MultV: 32.5 (± 28.5); RelC: 21.5 (± 8.5); RelS: 22.0 (± 10.0); RelV: 24.0 (± 7.3); Ion: 5.1 (± 6.4); Self: 3.5 (± 5.2); Zinc: 7.7 (± 14.2). The type of resin cement (BIS-GMA- or HEMA- based) did not affect the crown retention values. The treatment involving vitrification of the cementation surface was only capable to improve the retention force for the HEMA based-cement. For untreated intaglio surfaces of YTZP crowns, resin cements showed significantly higher retention than those obtained for self-adhesive, glass ionomer and zinc phosphate cements

Made available in DSpace on 2014-12-02T11:16:36Z (GMT). No. of bitstreams: 0 Previous issue date: 2014-02-18Bitstream added on 2014-12-02T11:21:10Z : No. of bitstreams: 1 000793946.pdf: 1058988 bytes, checksum: ce3649bc54da6962a44fe15e7b1cbe9d (MD5) / A adição de nanopartículas aos materiais odontológicos busca melhorar principalmente suas propriedades antibacterianas sem, contudo, alterar suas propriedades mecânicas e físicas. O objetivo deste estudo foi avaliar a influência da incorporação de nanopartículas de dióxido de titânio (TiO2) a um CIV convencional (Ketac Molar EasyMix) sobre suas propriedades mecânicas (dureza Vickers e resistência a compressão axial) e físicas (rugosidade e porosidade). Para todos os testes foram adotados quatro grupos (n=10): controle (sem adição de nanopartículas), 1, 2 e 5% em peso de TiO2. A dureza Vickers foi avaliada por meio do microdurômetro digital (Micromet 2100), a compressão axial por máquina de testes universais (EMIC-DL 2000), a rugosidade por rugosímetro (Mitutoyo SJ-400) e a porosidade por imagens de microscopia eletrônica de varredura (SM-300), analisadas pelo software Image J. Os dados foram analisados pela Análise de variância (ANOVA) a um critério fixo seguida do pós-teste de Tukey, com nível de significância de 5%. Houve diferença estatisticamente significativa para os experimentos dureza Vickers (p ≤ 0.001) e rugosidade (p = 0.010). Observamos que o CIV contendo 1% ou 2% de nanopartículas apresentou valores mais baixos para dureza. A rugosidade de superfície mostrou-se menor ao adicionar 2% e 5% de nanopartículas. Imagens em MEV mostraram não haver mudanças significativas na morfologia da porosidade na superfície do CIV. A adição de 5% de nanopartículas de TiO2 ao CIV convencional proporcionou resultados promissores, uma vez que não comprometeu suas propriedades mecânicas e físicas, e melhorou a rugosidade de superfície. Assim, a adição da nanopartícula de TiO2 a 5% ao Ketac Molar EasyMix sugere sua indicação clínica. / The addition of nanoparticles to dental materials mainly searches to improve the antibacterial properties without changing their mechanical and physical properties. The aim of this study was to evaluate the influence of the incorporation of titanium dioxide (TiO2) nanoparticles to conventional glass ionomer cement (GIC) (Ketac Molar EasyMix) on mechanical (Vickers hardness and compressive strength) and physical (roughness and porosity) properties. For all experiments four groups (n=10) were used: control (without addition of nanoparticles), 1%, 2%, 5% (w/w) of TiO2. The Vickers hardness was measured using a digital hardness (Micromet 2100), compressive strength using a universal testing machine (EMIC-DL 2000), the roughness using a profilometer (Mitutoyo SJ-400) and for porosity, images were made using scanning electron microscopy (SM-300) and analyzed by Image J-software. The data were analyzed by one-way ANOVA and Tukey's post hoc test, with the level of significance set at 5%. There were statistically significant differences for the experiments of Vickers hardness (p ≤ 0.001) and roughness (p = 0.010). We observed that the GIC containing 1% or 2% of nanoparticles had lower values for hardness and the surface roughness was lower by adding 2% and 5% of nanoparticles. SEM images showed no significant changes in surface morphology of the GIC. The addition of 5% (w/w) TiO2 nanoparticles to conventional GIC provides promising results, since it does not compromise the physical and mechanical properties and improves surface roughness. The addition of TiO2 nanoparticle to Ketac Molar EasyMix suggests clinical indication.

Made available in DSpace on 2014-12-02T11:16:38Z (GMT). No. of bitstreams: 0 Previous issue date: 2014-02-25Bitstream added on 2014-12-02T11:21:06Z : No. of bitstreams: 1 000796605.pdf: 2231117 bytes, checksum: 2cb8d762ad76e855d47d13daf8e4e4f2 (MD5) / O objetivo deste estudo foi avaliar a citotoxicidade de cimentos resinosos quando aplicados sobre cultura de células odontoblastóides (MDPC-23) e pulpares humanas (HDPC). Os seguintes grupos foram formados: G1 - controle (sem tratamento); G2 - Rely X Luting 2; G3 - Rely X U200; G4 - Rely X ARC. Corpos de prova padronizados, preparados com os cimentos, foram imersos em 1 mL de meio de cultura (DMEM) por 24hs para obtenção dos extratos (DMEM + componentes liberados dos cimentos). Após aplicar os extratos sobre as células por 24hs, a viabilidade (MTT assay) e tipo de morte celular (Anexina/PI), bem como a morfologia das células (MEV) foram avaliados. Os dados obtidos foram submetidos à análise estatística de Kruskal-Wallis complementada por Mann-Whitney (α=5%). A análise química dos extratos foi realizada por cromatografia liquida de alta performance (HPLC). Nos grupos G2, G3 e G4, observou-se redução de 95,8%, 31,5% e 22,7% na viabilidade das células MDPC-23, respectivamente. Redução de 89,4% para G2 e aumento em 11,3% e 29% para G3 e G4, respectivamente, foram observados para as HDPCs. Para as células MDPC-23, redução significativa de viabilidade ocorreu em G2 e G3 quando comparado à G1; todavia, para as HDPCs esta redução foi observada apenas em G2 (p<0,05). Para ambas as culturas usadas no estudo, ocorreu 100% de morte celular por necrose apenas em G2, onde o pH do extrato era ácido. Em G3, onde uma pequena quantidade de TEGDMA foi detectado no extrato, houve reduzida morte celular por necrose e discreta alteração morfológica nas células. Todavia, nenhum dano celular ocorreu em G4. De maneira geral, a células MDPC-23 são mais sensíveis do que as HDPCs. Concluiu-se que apenas o cimento Rely X Luting 2 causou intenso efeito citotóxico para ambas culturas de células pulpares usadas neste estudo. Rely X U200 apresentou discreta citotoxicidade, enquanto o cimento Rely X ARC não foi tóxico para as células pulpares... / The aim of this study was to evaluate the cytotoxicity of luting cements on cultured MDPC-23 odontoblast-like cells and human dental pulp cells (HDPCs). The following groups were formed: G1 - control (no treatment), G2 - Rely X Luting 2, G3 - Rely X U200; G4 - Rely X ARC. Standard round specimens prepared with resin cements were immersed in 1 ml of culture medium (DMEM) for 24 hours to obtain the extract (DMEM + components released from the cement). After applying the extracts to the cells for 24 hours, the viability (MTT assay) and type of cell death (Annexin/PI) as well as cell morphology (SEM) were evaluated. The data obtained was submitted to Kruskal-Wallis statistical analysis complemented by Mann-Whitney test (α=5%). The chemical analysis of the extracts was performed by high performance liquid chromatography (HPLC). In G2, G3 and G4, there was a reduction of 95.8 %, 31.5 % and 22.7 % in the MDPC-23 cells viability, respectively. A reduction of 89.4 % for G2, as well as an increase of 11.3 % and 29% for G3 and G4 was observed for the HDPCs, respectively. Significant reduction of MDPC-23 viability occurred for G2 and G3 compared to G1. However, for HDPCs this reduction was only observed in G2 (p<0.05). For both cell cultures used in this study, there was 10 % of cell death by necrosis only in G2, in which the pH of the extract was acid. In G3, where a small amount of TEGDMA was detected in the extracts, there was reduced cell death by necrosis and a discrete morphological alteration in cells. No cellular damage occurred in G4. In general, the MDPC-23 cells are more sensitive than HDPCs against the toxicity of resin cement components. It was found that only the Rely X Luting cement caused intense cytotoxic effect for both pulp cell cultures used in this study. Rely X U200 showed mild cytotoxicity, whereas the cement Rely X ARC was not toxic to the pulp cells.

Made available in DSpace on 2015-01-26T13:21:24Z (GMT). No. of bitstreams: 0 Previous issue date: 2014-05-20Bitstream added on 2015-01-26T13:30:33Z : No. of bitstreams: 1 000802293.pdf: 2259138 bytes, checksum: 29dc545448ea7b06e965e799eb83bf4c (MD5) / Avaliou-se a atividade antibacteriana de diferentes concentrações de nanopartículas de óxido de zinco incorporadas a um cimento de ionômero de vidro (CIV) quimicamente ativado e outro modificado por resina fotopolimerizável sobre o biofilme de Streptococcus mutans em diferentes tempos de maturação. As concentrações de nanopartícula foram 0%, 1% e 2%, os CIVs utilizados foram o Fuji II (GC América) e Fuji II LC (GC América) e os tempos de maturação foram 24 horas e 7 dias. Confeccionou-se corpos de prova (N=108) circulares (4mm x 2mm). A atividade antibacteriana foi avaliada pela contagem das Unidades Formadoras de Colônia por Mililitro (UFC/ml). Analisou-se a morfologia celular em Microscopia Eletrônica de Varredura (MEV). Os dados obtidos para cada material atenderam os pressupostos de normalidade e homocedasticidade. Procedeu-se a Análise de Variância a dois fatores (tempo de maturação do biofilme e concentração de nanopartículas) ( =5%). Para o CIV quimicamente ativado encontrou-se diferença não significativa na atividade antibacteriana segundo o tempo de maturação do biofilme (p=0,744), concentração de nanopartículas (p=0,966) e a interação entre eles (p=0,800). Para o CIV modificado por resina, observou-se que a média de UFC/ml do biofilme com 7 dias foi significativamente superior à do biofilme de 24 horas (p=0,034). A concentração de nanopartículas (p=0,570) e a interação entre os dois fatores (p=0,756) não foi significativa. Na análise em MEV não foi observada mudança na morfologia celular do Streptococcus mutans. Conclui-se que a inclusão de nanopartículas de óxido de zinco à 1% e 2% aos CIVs avaliados não alterou sua atividade antibacteriana. / This study evaluated the antibacterial activity of different concentrations of zinc oxide nanoparticles incorporated into a self-cured glass ionomer cement (GIC) and a light-cured resin-reinforced glass ionomer cement on Streptococcus mutans biofilm at different maturation times. Nanoparticles concentrations were 0%, 1% e 2%, the GICs were Fuji II (GC America) and Fuji II LC (GC America) and the maturation times were 24 hours and 7 days. Were prepared circular (4mm x 2mm) specimens (N= 108). The antibacterial activity was evaluated by the number of Colony Forming Unit per militers (CFU/ml). Morphological analysis of biofilm was taken by scanning electron microscopy (SEM). The data obtained for each material attended the assumptions of normality and homoscedasticity and a two-way ANOVA ( =5%). No significant difference was observed according to the time of biofilm maturation (p=0.744), concentration of nanoparticles (p=0.966) and their interaction (p=0.800). Resin-reinforced GIC showed significantly higher CFU/ml mean for 7-day biofilms compared to 24h-biofilms (p=0.034). The concentration of nanoparticles (p=0.570) and the interaction (p=0.756) between the two factors was not significant. SEM analysis showed no change in cell morphology of S. mutans according to the type of GIC, maturation time and nanoparticles concentration. We conclude that the inclusion of zinc oxide nanoparticles at concentrations of 1% and 2% into the glass ionomer cement evaluated did not promote antimicrobial activity against Streptococcus mutans.

Made available in DSpace on 2015-01-26T13:21:30Z (GMT). No. of bitstreams: 0 Previous issue date: 1997-06-27Bitstream added on 2015-01-26T13:30:17Z : No. of bitstreams: 1 000126156.pdf: 4088167 bytes, checksum: 897cd22c86f9dc36f2eb1dddb6805462 (MD5) / Foi feita uma análise das discrepâncias de assentamento ocorridas na cimentação de coroas totais metálicas aliviadas ou não, internamente, sobre preparos com término cervical em chanfro; linha zero ou lâmina de faca; plano inclinado em 135°; ombro reto ou degrau em 90° e ombro reto ou degrau em 90°, associado a um bisel em 45°. Empregaram-se quatro tipos de cimentos, sendo três classificados como temporários à base de óxido de zinco e eugenol (Temp Bond e Provy) e outro sem eugenol (Temp Bond NE); e um quarto indicado para cimentações definitivas, cimento de Fosfato de Zinco. Idealizou-se modelos-padrão usinados em aço inoxidável, com características de um preparo para coroa total metálica em um primeiro molar inferior variando-se os términos cervicais conforme estabelecido. Foram obtidas cápsulas metálicas usinadas em aço inoxidável e perfeitamente adaptadas aos modelos-padrão com os términos cervicais correspondentes, nas condições de estarem aliviadas internamente ou não. Empregou-se uma técnica de cimentação padronizada para assentamento destas cápsulas metálicas nos modelos-padrão respectivos. Através de metodologia original promoveu-se a mensuração da discrepância de assentamento nos corpos-de-prova, com o aparelho Metroscópio Horizontal. Concluiu-se que: a) o alívio executado nas superfícies internas das coroas diminui de forma estatisticamente significante a discrepância marginal após a cimentação, independentemente do tipo de cimento empregado e da forma do término cervical adotada; b) o término cervical do preparo no modelo-padrão tipo Lâmina de Faca foi o que apresentou menor discrepância, independente do cimento empregado, seguido pelo Plano Inclinado, Chanfro, Ombro Biselado e Ombro Reto; c) os términos cervicais em Chanfro, Plano Inclinado e Lâmina de Faca, quando analisadas as amostras dos corpos-de-prova com alívio, .... / Seating discrepancies during cementation of complete metal crowns internally relieved or not with various finishing lines and cementing agents. This study evaluated the discrepancies during cementation of complete metal crowns either relieved or not on preparation with various margin designs: chamfer, knife edge, 135 degree shoulder, 90 degree shoulder, 90 degree shoulder with 45 degree bevel. Four types of cements, three temporary and one definitive were used: 1- zinc oxide and eugenol temporary cement (Temp Bond); 2- zinc oxide and eugenol temporary cement (Provy); 3- no eugenol temporary cement (Temp Bond NE) and 4- zinc phosphate cement (S.S.White). Machined stainless dies were fabricated to resemble complete crown preparations for a lower first molar with various finishing lines. Machined stainless steel copings, either internally relieved or not were also fabricated to fit the metal dies. A controlled technique was developed to assess seating discrepancies under the horizontal metroscope. Results showed: a) the internally relieved crowns showed after cementation statistically significant reduction of marginal discrepancies regardless of cement type or margin desing; b) knife edge finishing lines showed least dicrepancies regardless of cement type followed by the 135 degree shoulder, chamfer, bevelled 90 degree shoulder and 90 degree shoulder; c) internally relieved copings with chamfer, 135 degree shoulder and knife edge finishing lines showed no statiscally significant marginal discrepancies. This indicates that any of them yields favorable results; d) regarding cements, the least marginal discrepancies were found with Temp Bond NE followed by Temp Bond, Provy and finally by the Zinc Phosphate Cement (S.S.White)

Made available in DSpace on 2015-01-26T13:21:31Z (GMT). No. of bitstreams: 0 Previous issue date: 2001-06-28Bitstream added on 2015-01-26T13:30:16Z : No. of bitstreams: 1 000138163.pdf: 5037696 bytes, checksum: 2e83c40009b352ce450b85f1a580ef36 (MD5) / A biocompatibilidade de quatro agentes para cimentação de peças protéticas foi avaliada por meio de implantes em tecido conjuntivo subcutâneo de ratos. Neste trabalho foram avaliados um cimento de fosfato de zinco (Lee Smith - Vigodent), um cimento de ionômero de vidro (Ketac-Cem - ESPE) e dois cimentos resinosos (Panavia Ex 21 - Kuraray Co.; Enforce- Dentsply). Após a manipulação dos cimentos, os implantes foram realizados, utilizando-se tubos de polietileno preenchidos com os agentes cimentantes e inseridos em lojas cirúrgicas preparadas no dorso dos animais, os quais foram sacrificados nos períodos de observação de 14, 30, 60 e 84 dias. Os tecidos circunjacentes aos implantes foram removidos, incluídos em parafina e corados com hematoxilina e eosina para análise em microscopia óptica. Os resultados mostraram que todos os agentes de cimentação causaram uma resposta tecidual nos períodos avaliados; o cimento de fosfato de zinco apresentou um menor grau de reação tecidual nos períodos de 14, 30 e 60 dias; o cimento de ionômero de vidro apresentou as piores características de biocompatibilidade quando em contata com o tecido conjuntivo de ratos / The biocompatibility of four luting agents was evaluated in rats subcutaneous connective tissue implants. Polyethylene lubes filled with the luting agents were surgically implanted into the dorsal subcutaneous tissue of rats. The tube was left implanted for periods of 14, 30, 60 and 84 days, following wich the animals were killed and the implants, together with the surrounding tissue, were excised. The specimens were then fixed in 10 per cent formalin, sectioned serially and stained with hematoxylin and eosin and then, examined by light microspic . The results showed that all the luting caused an tissue answer in the appraised periods; the phosphate of zinc cement presented a smaller degree of tissue reaction in the periods of 14, 30 and days; the of glass ionomer cement presented the worst characteristics of biocompatibility when in contact with the conjunctive tissue in rats