AMARO, L. O. Estudo da resistência à corrosão do aço inoxidável duplex UNS S31803 ou SAF 2205 submetido a processo de soldagem. 2006. 72 f. Dissertação (Mestrado em Ciência de Materiais) – Centro de Tecnologia, Universidade Federal do Ceará, Fortaleza, 2006. / Submitted by Marlene Sousa (mmarlene@ufc.br) on 2016-03-31T18:25:36Z No. of bitstreams: 1 2006_dis_loamaro.pdf: 5065360 bytes, checksum: cd8a5eb5b5b003484ec6bd7d404097c0 (MD5) / Approved for entry into archive by Marlene Sousa(mmarlene@ufc.br) on 2016-03-31T18:40:49Z (GMT) No. of bitstreams: 1 2006_dis_loamaro.pdf: 5065360 bytes, checksum: cd8a5eb5b5b003484ec6bd7d404097c0 (MD5) / Made available in DSpace on 2016-03-31T18:40:49Z (GMT). No. of bitstreams: 1 2006_dis_loamaro.pdf: 5065360 bytes, checksum: cd8a5eb5b5b003484ec6bd7d404097c0 (MD5) Previous issue date: 2006-10-04 / The aim of this work is to study the influence of the welding energy in the corrosion resistance of UNS S31803 or SAF 2205, duplex stainless steel. For this purpose, double loop electrochemical potentiokinetic reactivation and cyclic polarization were the electrochemicaltechniques used to evaluate the susceptibility of the welded steel to intergranular and pitting corrosion, respectively. The microstructure observed using an optical microscope wich also made possible to assess the phase quantification. Hardness measurements were also carried out. The electrochemical results showed that the welded steel is not susceptible to the intergranular. On the other hand, all the welded steel were susceptibles to pitting corrosion wich is rising with the welding energy. Aditionally, the pitting potencial increase with the ferrite content in the welded steel, while the hardness is not strongly influenced by the welding energy / Este trabalho objetiva estudar a influência da energia de soldagem na resistência à corrosão do aço inoxidável duplex UNS S31803 ou SAF 2205. Para isto foi avaliada a susceptibilidade do material soldado à corrosão intergranular e por pite e sua relação com a microestrutura da zona afetada termicamente pelo calor durante o processo de soldagem. Foram também avaliadas a microdureza e a quantificação de fases para correlacioná-los com a microestrutura. As técnicas eletroquímicas utilizadas neste estudo foram a de reativação e a de polarização potenciodinâmica cílcica. A avaliação da microestrutura foi feita por microscopia ótica. A energia dispersiva de raios X foi usada para terminar a composição química do material como recebido. Os resultados mostraram que na faixa de energia utilizada (4 a 18KJcm-1) não houve corrosão intergranular na zona afetada pelo calor. Os testes eletroquímicos e de imersão em FeCl36% mostraram que o material soldado é susceptível a corrosão por pite e que a susceptibilidade é maior com o aumento da energia de soldagem. O potencial de pite aumenta com o percentual de ferrita, enquanto a dureza é pouco influenciada pela energia de soldagem

Made available in DSpace on 2014-06-11T19:26:48Z (GMT). No. of bitstreams: 0 Previous issue date: 2011-02-18Bitstream added on 2014-06-13T20:34:48Z : No. of bitstreams: 1 brandao_gms_me_botfm.pdf: 1478164 bytes, checksum: 2a2a85c3df30f48b27dadc4c51f20e91 (MD5) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / Universidade Estadual Paulista (UNESP) / A trombose venosa profunda (TVP) dos membros inferiores é doença grave, potencialmente fatal e pode levar à síndrome pós-trombótica (SPT). A SPT é doença crônica, com consideráveis conseqüências socioeconômicas para os pacientes serviços de saúde. Sua fisiopatologia relaciona-se com o surgimento de hipertensão venosa, que ocorre devido à incompetência valvular e a obstrução da veia pelo trombo residual. Assim, é importante conhecer o processo de recanalização das veias trombosadas para melhor compreensão das seqüelas da TVP. Avaliar e quantificar o processo inicial de recanalização das veias dos membros inferiores após um episódio de TVP aguda pelo mapeamento dúplex em cores (MDC). Estudou-se pelo MDC 12 pacientes na fase aguda (até 10 dias), no 1°, 3º e 6º mês após o episódio agudo de TVP. Os pacientes foram mantidos com terapia anticoagulante adequada por 6 meses e orientados a usar meias de compressão elástica. Para avaliar e quantificar a recanalização foram utilizados o escore trombótico (ET) e a variação percentual do diâmetro venoso na máxima compressibilidade em relação a sua ausência (Δ%Øvmax/Øvsem). O ET foi verificado em 18 segmentos venosos (veias ilíaca externa; femoral comum; femoral profunda; femoral ao nível da junção e a 10 cm da prega inguinal; poplítea supra patelar e cavo; fibulares; tibiais posteriores; gastrocnêmias; soleares; veia safena magna ao nível da crossa, terço proximal, médio e distal; veia safena parva ao nível da crossa, terço proximal e médio). Segmentos venosos patentes tiveram ET de zero. A TVP foi considerada parcialmente oclusiva quando o segmento venoso foi não compressível com um sinal Doppler presente (ET = 1). Considerou-se a TVP totalmente oclusiva quando o segmento venoso foi não compressível e o sinal Doppler não foi encontrado (ET = 2). Para cada membro foi calculado o ET total... / The deep vein thrombosis (DVT) of the lower limbs is a serious, potentially fatal disease and it can lead to the post-thrombotic syndrome (PTS). The PTS is a chronic disease, with considerable social and economical consequences for the patients and health services. His physiopathology is connected with the appearance of vein high blood pressure that takes place due to the valval incompetence and the obstruction of the vein for the residual thrombus. So, it is important to know the process of recanalization of the thrombosed veins for better understanding of the sequels of the DVT. The objective of this study was to evaluate and quantify the early recanalization of the vein of the lower limbs after acute DVT by duplex ultrasound scanning (DUS). Twelve elegible patients were examined by DUS at acute phase (less than 10 days), 1°, 3º and 6º months after the first episode of DVT. All patients were treated initially with unfractionated heparin or low-molecular-weightheparin followed by oral anticoagulation for 6 months and strongly encouraged to use compression stockings. To evaluate and quantify the recanalization of the veins were used the thrombus escore (TS) and the percentage variation of the vein diameter during the maximal compressibility regarding his absence (PVVDMA). The thrombus score (TS) assigned to 18 vein segments: external iliac vein; common femoral vein; deep femoral vein; confluence of femoral and deep femoral vein; femoral vein 10 cm at the inguinal ligament; popliteal vein suprapatellar; popliteal vein fossa; fibular veins; posterior tibial veins; gastrocnemius veins; soleal veins; sapheno-femoral junction; grate saphenous... (Complete abstract click electronic access below)

Made available in DSpace on 2018-08-02T00:03:13Z (GMT). No. of bitstreams: 1 tese_9255_EDUARDO SARCINELLI FARIA.pdf: 2805720 bytes, checksum: a977ea8ab4f6bc7f9b8ae13fbc804ba2 (MD5) Previous issue date: 2015-09-18 / Na presente dissertação foram avaliadas diferentes técnicas eletroquímicas visando detectar a suscetibilidade à corrosão do aço inoxidável dúplex UNS S31803. Este aço foi estudado na condição como recebido (CR) e após tratamento térmico nas temperaturas de 645°C e 820°C, por tempos que variam de 4 horas, 8 horas e 12 horas. Estes tratamentos levam à precipitação, principalmente, da fase sigma, e também, de carbonetos e nitretos de cromo. Foi preparada um solução de 2M H2SO4 + 0,5M NaCl + 0,01M KSCN para então ser conduzido ao ensaio de polarização de reativação potenciocinética de ciclo duplo (DL-EPR) e a espectroscopia de impedância eletroquímica (EIE) após o potencial de corrosão (OCP) e logo após a formação de filme que acontece no final da ativação do ensaio de ciclo duplo. Nos ensaios de DL-EPR foi constatado a presença de picos de reativação nas amostras de 645°C e 820°C devido à sensitização dos materiais. Nos ensaios de impedância, valores inconsistentes para a resistência de transporte de carga (Rct), além de um alto valor para elementos de fase constante (CPE) para amostra tratada a 645°C que indicaria que há mais transporte de íons nessas amostras do que na amostra tratada a 820°C, e também valores de indutância (L) e de resistência de adsorção (Rads) maiores para as amostras tratadas do que para amostra CR leva a uma falsa impressão que a amostra tratada a 820°C possui uma resistência à corrosão melhor do que a amostra CR. Diante desse fato, uma correção foi proposta na área sujeita à corrosão para que os valores estejam mais plausíveis com o contexto real. Palavras chave: Aço Inoxidável Duplex UNS S31803. Corrosão. Sensitização. Impedância.

Multiple antennas combined with cooperative relaying, called multiple-input multiple-output (MIMO) relay communications, can be used to improve the reliability and capacity of wireless communications systems. The precoding design is crucial to realize the full potential of MIMO relay systems. Full-duplex (FD) relay communications has become realistic with the development of effective loop interference (LI) cancellation techniques. The focus of this dissertation is on the precoding design for MIMO FD amplify-and-forward (AF) relay communication systems. First, the transceiver design for MIMO FD AF relay communication systems is considered with residual LI, which will exist in any FD system. Then the precoding design is extended to two-way MIMO FD relay communication systems. Iterative algorithms are presented for both systems based on minimizing the mean squared error (MSE) to obtain the source and relay precoders and destination combiner.Finally, the precoding design for MIMO FD relay communication systems with multiple users is investigated.Two systems are examined, namely a multiuser uplink system and a multiuser paired downlink system. By converting the original problems into convex subproblems, locally optimal solutions are found for these systems considering the existence of residual LI. The performance improvement for the proposed FD systems over the corresponding half-duplex (HD) systems is evaluated via simulation. / Graduate

No description available.

No presente trabalho foram estudados os fenômenos de encruamento e, principalmente, a formação e reversão da martensita alfa-linha (a\', cúbica de corpo centrado, CCC, ferromagnética) induzida por deformação em um aço inoxidável dúplex UNS S31803 e um super dúplex UNS S32520. Inicialmente, as microestruturas dos dois materiais na condição solubilizada foram caracterizadas com auxílio de várias técnicas complementares de análise microestrutural. Foram determinadas fração volumétrica, estrutura cristalina, composição química, tamanho e morfologia das duas fases (ferrita e austenita). Posteriormente, os dois aços foram deformados por dois métodos: a laminação a frio, dividida em vários estágios, com menores graus de deformação e a limagem, sendo que o cavaco limado resultante apresenta altos graus de deformação. Algumas amostras deformadas foram recozidas. Os fenômenos de encruamento, formação e reversão de martensita induzida por deformação na austenita, recuperação, recristalização da austenita e da ferrita no cavaco limado foram estudados predominantemente por difratometria de raios X e usando o método de Rietveld. A difratometria de raios X também foi utilizada para determinação das microdeformações residuais e tamanhos de cristalito (subgrão), calculadas a partir do alargamento dos picos de difração causado pelas deformações. Desta forma, puderam-se comparar os níveis de deformação da laminação e limagem. Qualitativamente, a formação e reversão da martensita induzida por deformação também foi estudada por meio de medidas magnéticas utilizando-se dados de saturação magnética das curvas de histerese obtidas com o auxílio de um magnetômetro de amostra vibrante. Observou-se que para o aço inoxidável dúplex, tanto a laminação quanto a limagem causaram a formação de martensita induzida por deformação e para o aço inoxidável super dúplex, apenas a limagem promoveu essa transformação. Em comparação com o aço dúplex, o aço super dúplex apresentou maior resistência à formação de martensita induzida por deformação, pois apresenta uma austenita mais rica em nitrogênio e uma maior propensão à formação de fase sigma durante o recozimento, pois apresenta uma ferrita mais rica em cromo e nitrogênio. / In the present work the phenomena of strain hardening, formation and reversion of the strain induced alpha-prime martensite (a\', body centered cubic, BCC, Ferromagnetic) in an UNS S31803 duplex and UNS S32520 super duplex stainless steels have been studied. Firstly, the microstructures of both materials in the solution annealed condition were characterized with the aid of several microstructural analysis complementary techniques. The volume fraction, crystalline structure, chemical composition, size and morphology of the two phases (ferrite and austenite) have been determined. Further, both steels were deformed by two methods: cold rolling, divided into several stages, with lower strain levels than filing, which the chips resulting had higher strain levels. The phenomena of strain hardening, formation and reversion of strain induced martensite in the austenite phase, recovery and recrystallization of austenite and ferrite phases have been studied, mainly using X-ray diffraction and the Rietveld method. X-ray diffraction was also used to determine the residual microstrain and crystallite size (sub grain), calculated from the diffraction peak broadening caused by straining. Thus, the levels of cold rolling and filing strains could be compared. Qualitatively, the formation and reversion of strain induced martensite was also studied by magnetic measurements using data from magnetic saturation of hysteresis curves obtained with the aid of a vibrating sample magnetometer. It has been observed that for the duplex stainless steel, both filing as well as cold rolling promoted strain induced martensite. On the other hand, for the super duplex stainless steel, just filing promoted this transformation. In the comparing with duplex, the super duplex stainless steel austenite is more stable that is why is richer in nitrogen, so, the strain induced martensite formation is more difficult. The easier sigma phase precipitation during annealing as well in the super duplex stainless steel is due higher levels of chrome and molybdenum than the duplex stainless steel.

In order to achieve Full Duplex (FD) communication, currently studied solutionsfor the commercial sector rely on advanced Self-Interferece Cancellation (SIC)techniques to remove the transmitted signal from the received one. This thesis expandsthe research of these techniques by evaluating their potential usage in militarycommunication scenarios where requirements and conditions are distinct,firstly, by identifying, categorizing and describing a set of previously proposedsic techniques and secondly, by performing a comprehensive simulation andanalysis of two suggested sic techniques as part of a FD transceiver. Though themajority of the considered SIC techniques was determined to be potentially implementablein military FD transceivers, some frequency-dependent techniquesand techniques prohibiting omnidirectional communication could not be used.The simulation and analysis of the two suggested SIC techniques show that undercertain conditions, such as limited transmission power and/or reflective environment,close to complete suppression could be realized even with high nonlineardistortion in the transmit chain.

Fatias de rochas compreendendo granitóides, gnaisses bandados, anfibolitos, quartzitos e metapelitos formam um sistema imbricado situado na porção oeste do Lineamento Patos (Província Borborema, NE do Brasil). A estrutura situada no sul do estado do Ceará, inserida no Bloco Assaré, nesse momento ainda carece de estudos geológicos que permitam a sua melhor compreensão. Neste contexto, o presente trabalho foi realizado com o objetivo de trazer novos dados geocronológicos e estruturais para acrescentar no entendimento do duplex transcorrente. Datações de rochas situadas no interior das escamas imbricadas em zircões (U-Pb) via LA-ICP-MS indicam que o duplexé constituído por unidades (escamas) de idades diferentes. Gnaisses bandados, diques de anfibolito e metaultramáficas da unidade Granjeiro forneceram idades arqueanas (gnaisses: c. 2.8 Ga, LM10; c. 3.2 Ga, LM3; dique: c. 3.0 Ga, LM2). Idades siderianas e riacianas foram encontradas em gnaisses e anfibolitos a oeste de Cajazeiras (c. 2.4 Ga, LM1; c.2.4, LM13) e em augen gnaisses a sul de Cedro (c. 2.2 Ga, LM11), respectivamente. Essas sequencias do embasamento encontram-se em contato alóctone com metapelitos e quartzitos agrupados na Formação neoproterozoica Lavras da Mangabeira. Critérios cinemáticos derivados doestudo das microestruturas e das tramas cristalográficas de milonitos ricos em quartzo mostram que a sequência metassedimentar foi empurrada para nordeste. Eixos-c e eixos- de quartzo indicam a ativação de sistemas de deslizamento de alta temperatura durante o desenvolvimento da trama. Estimativas de temperaturas baseadas na abertura de ângulo da trama de eixos-c e em contatos suturados entre grãos de quartzo indicam que a deformação dúctil ocorreu entre 500 e 700 °C. A formação do duplex transcorrente, que constitui uma estrutura única na Província Borborema, possivelmente foi facilitada pela presença de rochas arqueanas que provavelmente se comportaram de forma mais rígida durante a deformação facilitando o cavalgamento oblíquo dos conjuntos litológicos. O arranjo estrutural das fatias imbricadas é portanto consistente com um duplextranscorrente compressivo induzido pela deformação cisalhante destral. / Slices of metaplutonic rocks, banded gneiss, amphibolites and metasedimentary sequences form a strike-slip duplex situated in the west portion of the Patos Lineament (Borborema Province, Northeastern Brazil). U-Pb (LA-ICP-MS) data in zircons from the imbricate slices indicate they are constituted by rocks of different ages. Banded gneiss, orthogneisses and metaultramafic dikes assembled in the Granjeiro Complex yielded Archean ages between 2.8 and 3.2 Ga. In contrast, biotite gneisses and amphibolites produced a Siderian (ca. 2.4 Ga) age and an augen gneiss apparently intrusive in the Siderian sequences yielded a Rhyacian (ca. 2.2 Ga) age. These basement sequences are in allochtonous contact with metapelites and quartzites grouped in the Lavras da Mangabeira Formation of Neoprotrozoic age. Kinematic criteria deduced from the study of the microstructures and crystallographic fabric of quartz-rich mylonites show that the metasedimentary sequence was thrusted to the northeast direction. Crystalligraphic c- and a- axis of quartz indicated that medium- to high temperature slip-systems were active during the fabric development. Temperature estimations based on the opening-angle of the c-axis fabric and the sutured contacts between quartz-quartz grains indicated that the ductile deformation occurred at 500 and 700°C. The development of the tectonic duplex was likely facilitated by the occurrence of Archean rocks involved in the shear deformation. They would have acted as a rigid (competent) material that induce the stacking of the sequences during the bulk dextral transcurrent deformation of the Patos Lineament.

Os aços inoxidáveis duplex se caracterizam por terem boas propriedades mecânicas e de resistência a corrosão, no entanto as suas propriedades de resistência ao desgaste são baixas. Para melhorar as propriedades superficiais desses materiais são utilizados tratamentos termoquímicos como a nitretação a plasma. Este tratamento é feito em temperaturas baixas para evitar a formação de nitretos de cromo, os quais quando são formados empobrecem o teor de cromo da matriz metálica, evitando que se forme a camada passiva, que confere resistência a corrosão a este tipo de material. Também, a nitretação a plasma permite que a dureza superficial atinja até dez vezes o valor da dureza inicial do material, o que melhora notavelmente as propriedades de resistência ao desgaste destes aços. Este estudo tem por objetivo avaliar camadas nitretadas formadas por nitretação a plasma em um aço inoxidável duplex AISI 2205. Para isto foram feitas várias experiências onde se estudou o efeito das variáveis do processo na formação da camada nitretada. Foram feitos tratamentos na temperatura de 400ºC sob pressões de 1,8 e 3,6 Torr por 720 min. Outra série de experimentos foi feita entre 350 e 500º por 240 min, para avaliar o efeito da temperatura nesse tratamento. Além disso, foi estudado o efeito de diferentes porcentagens de ferrita (40 e 64%) incialmente presente na microestrutura do material. Para isto foi feito um tratamento térmico de solubilização com têmpera em água a partir de 1200°C por uma hora, no material como recebido. A caracterização das camadas formadas foi feita por microscopia eletrônica de varredura, microscopia de força atômica, difração de raios x com radiação Cu K e difração de raios x de ângulo rasante a 5º. 7 Obtiveram-se camadas nitretadas com espessuras entre 3 µm e 18 µm. As espessuras das camadas sugerem que as variáveis: temperatura, tempo e pressão se relacionam com a espessura de forma direta, à medida que aumentam cada uma dessas variáveis, há um aumento da espessura da camada. As imagens obtidas por AFM sugerem que a nitretação a plasma induz mudanças na topografia da superfície, mudando com isto os valores de rugosidade. Também, foi observado que a espessura da camada nitretada é maior na amostra com menor percentagem de ferrita (40%). Nos difratogramas foi possível identificar a formação de austenita expandida e nitretos de cromo CrN. / The duplex stainless steels are characterized by their good mechanical properties and corrosion resistance, but their wear resistance is low. To improve the surface properties of these materials plasma nitriding thermochemical treatments are used. This treatment is done at low temperatures to avoid chromium nitrides precipitation. CrN precipitation promotes the depletion of chromium of the metallic matrix preventing the formation of the chromium oxide layer that passivates these kind of materials. In addition, the plasma nitriding treatment allows reaching hardness values up to ten times greater the characteristic values of the untreated material, greatly improving the wear resistance of these steels. The aim of this work is to study nitrided layers formed by plasma nitriding in an AISI 2205 duplex stainless steel. For this, there were made several experiments where it was studied the effect of process variables on the nitrided layer formation. Treatments were performed at temperature of 400 °C under 1.8 and 3.6 Torr pressures during 720 min. Another series of experiments was tested between 350 °C and 500 °C during 240 min, to study the temperature effect. In addition, the effect of different ferrite percentages (40 and 64%) in the microstructure was studied. The ferrite percentage variation was obtained by a heat treatment of quenching in water at 1200 °C for one hour in the material as received. Samples characterization was done by scanning electron microscopy, atomic force microscopy and x-ray diffraction Cu K, glancing angle x-ray diffraction with an incident angle of 5º. There were obtained nitrided layer with a thickness between 3m and 18m. Layer thicknesses suggest that the variables: temperature, pressure and time are related to the thickness directly. AFM images obtained suggest that the plasma nitriding induces changes in surface topography, changing the values of roughness of the surface. In addition, it was observed that the layer thickness is bigger in the sample with less ferrite percentage (40%). X-ray patterns show the presence of expanded austenite and CrN.

O objetivo deste estudo é qualificar reparos realizados através do processo de Soldagem por Fricção com Pino Consumível (SFPC), ou Friction Hydro Pillar Processing (FHPP) em chapas de aços inox duplex SAF 2205 (AID UNS S31803). Em paralelo, fazer uma comparação relativa ao mesmo material reparado com o processo TIG (GTAW). Após a obtenção das juntas reparadas em ambos os processos, estas passaram por rigorosa análise microestrutural e ensaios mecânicos para, dessa forma, qualificá-las através de critéios usuais recomendados em normas para utilização no restauro de estruturas que utilizam o material em questão. Foi utilizada a simulação termodinâmica para prever possíveis fases intermetálicas. Foram investigadas as propriedades metalúrgicas através de microscopia ótica e eletrônica de varredura, fractografia e Difração de Raios-X além de ensaios de corrosão. Já as propriedades mecânicas foram averiguadas através de ensaios de impacto, de dobramento e perfis de microdureza. Após qualificar ambos os processos com o objetivo de reparar estruturas que utilizam AID SAF 2205, foi obtida uma junta soldada livre de defeitos com os parâmetros aplicados: força aplicada em 25 kN, velocidade 7000 RPM, burn-off 9 mm e forjamento pelo período de 10 segundos. Dessa forma, o FHPP provou ser um processo de acordo aos critérios recomendados em normas. / The aim of this study is qualify repairs made through Friction Hydro Pillar Processing (FHPP) in plates of duplex stainless steel SAF 2205 (AID UNS S31803). In same time make a comparation with the Gas Tungsten Arc Welding processing (GTAW) using the same material. The processed joints repairs will be analyzed in microstructural and mechanical tests to qualify using criteria according standards used for structural repairs in this material. Was utilized the thermodinamics simulation to predict possible intermetallic phases. Were investigated the metallurgical properties with scanning electron microscope, fractography and X -ray diffraction in addition to corrosion test. The mechanical properties were investigated with impact tests, bending test and micro hardness profile. After qualify both repair processes using stainless steel sAF 2205, was obtained a weld free of defects with applied parameters: force 25 kN, speed 7000 rpm, bunr-off 9 mm and forging force during 10 seconds. Thus, the FHPP proved a suitable process according standards recommendations.