Organic solar cells (OSC) are interesting as low cost alternative to conventional solar cells. Unsubstituted Metal-phthalocyanines (Pc) are excellent electron donating molecules for heterojunction OSC. Usually organic solar cells with Pcs are produced by vapor deposition, although solution based deposition (like spin casting) is cheaper and offers more possibilities to control the structure of the film. With solution based deposition several parameters (like temperature, solvent and etc.) affect the self-organized structure formation via nucleation and growth. The reason why vapor deposition is typically used is the poor solubility of the metal-phthalocyanines in most common solvents. Furthermore the process of nucleation and growth of Pc aggregates from solution is not well understood. For preparation of Pc films from solution, it is necessary to find the appropriate solvents, assess the solution deposition techniques, such as dip coating, and spin casting. It is necessary to understand the nucleation and growth process for aggregation/precipitation and to use this knowledge to produce nanostructures appropriate for OSC. This is important because the nanostructure of the films determines their performance. In this thesis, optical absorption and the stability of 8 different unsubstituted metal Pc’s were studied quantitatively in 28 different solvents. Among the several solution based deposited thin films produced based on this study, copper phthalocyanine (CuPc) dissolved in trifluoroacetic acid (TFA) is chosen as a model system for an in-depth study. CuPc has sufficient solubility and stability in TFA and upon solution processing forms appropriate structures for OSCs. CuPc molecules aggregate into layers of nanoribbons with a thickness of ~ 1 nm and an adjustable width and length. The morphology and the number of deposited layers in the thin films are controlled by different parameters, like temperature and solution concentration. Material properties of CuPc deposited from TFA are studied in detail via x-ray diffraction, UV-Vis and FT-IR spectroscopy. Atomic force microscopy was used to study the morphology of the dried film. The mechanism of the formation of CuPc nanoribbons from spin casted CuPc/TFA solution in ambient temperature is investigated and explained. The parameters (e.g. solution concentration profile) governing nucleation and growth are calculated based on the spin casting theory of a binary mixture of a nonvolatile solute and evaporative solvent. Based on this and intermolecular interactions between CuPc and substrate a nucleation and growth model is developed explaining the aggregation of CuPc in a supersaturated TFA solution. Finally, a solution processed thin film of CuPc is applied as a donor layer in a functioning bilayer heterojunction OSC and the influence of the structure on OSC performance is studied. / In den vergangenen Jahren wurden kosteneffiziente nasschemische Beschichtungsverfahren für die Herstellung organischer Dünnfilme für verschiedene opto-elektronische Anwendungen entdeckt und weiterentwickelt. Unter anderem wurden Phthalocyanin-Moleküle in photoaktiven Schichten für die Herstellung von Solarzellen intensiv erforscht. Aufgrund der kleinen bzw. unbekannten Löslichkeit wurden Phthalocyanin-Schichten durch Aufdampfverfahren im Vakuum hergestellt. Des Weiteren wurde die Löslichkeit durch chemische Synthese erhöht, was aber die Eigenschaften von Pc beeinträchtigte. In dieser Arbeit wurde die Löslichkeit, optische Absorption und Stabilität von 8 verschiedenen unsubstituierten Metall-Phthalocyaninen in 28 verschiedenen Lösungsmitteln quantitativ gemessen. Wegen ausreichender Löslichkeit, Stabilität und Anwendbarkeit in organischen Solarzellen wurde Kupferphthalocyanin (CuPc) in Trifluoressigsäure (TFA) für weitere Untersuchungen ausgewählt. Durch die Rotationsbeschichtung von CuPc aus TFA Lösung wurde ein dünner Film aus der verdampfenden Lösung auf dem Substrat platziert. Nach dem Verdampfen des Lösungsmittels, die Nanobändern aus CuPc bedecken das Substrat. Die Nanobänder haben eine Dicke von etwa ~ 1 nm (typische Dimension eines CuPc-Molekül) und variierender Breite und Länge, je nach Menge des Materials. Solche Nanobändern können durch Rotationsbeschichtung oder auch durch andere Nassbeschichtungsverfahren, wie Tauchbeschichtung, erzeugt werden. Ähnliche Fibrillen-Strukturen entstehen durch Nassbeschichtung von anderen Metall-Phthalocyaninen, wie Eisen- und Magnesium-Phthalocyanin, aus TFA-Lösung sowie auf anderen Substraten, wie Glas oder Indium Zinnoxid. Materialeigenschaften von aufgebrachten CuPc aus TFA Lösung und CuPc in der Lösung wurden ausführlich mit Röntgenbeugung, Spektroskopie- und Mikroskopie Methoden untersucht. Es wird gezeigt, dass die Nanobänder nicht in der Lösung, sondern durch Verdampfen des Lösungsmittels und der Übersättigung der Lösung entstehen. Die Rasterkraftmikroskopie wurde dazu verwendet, um die Morphologie des getrockneten Films bei unterschiedlicher Konzentration zu studieren. Der Mechanismus der Entstehung der Nanobändern wurde im Detail studiert. Gemäß der Keimbildung und Wachstumstheorie wurde die Entstehung der CuPc Nanobänder aus einer übersättigt Lösung diskutiert. Die Form der Nanobändern wurde unter Berücksichtigung der Wechselwirkung zwischen den Molekülen und dem Substrat diskutiert. Die nassverarbeitete CuPc-Dünnschicht wurde als Donorschicht in organischen Doppelschicht Solarzellen mit C60-Molekül, als Akzeptor eingesetzt. Die Effizienz der Energieumwandlung einer solchen Zelle wurde entsprechend den Schichtdicken der CuPc Schicht untersucht.

Zu Beginn der Arbeit werden thermodynamische, strukturelle und statistische Grundlagen und Modelle wiedergegeben, die einerseits Entmischungssysteme und andererseits flüssige Ober- und Grenzflächen betreffen. Hieran schließt sich eine umfangreiche Darstellung der Meßmethode an, die die theoretischen Zusammenhänge für die Beschreibung der Formen flüssiger Grenzflächen sowie eine Darstellung aller experimentell möglichen Kraftmeßkurven und deren Auswertung beinhaltet. Weiterhin folgt die Darstellung der Dichte-, Dichtedifferenz-, und Grenzflächenspannungsmeßergebnisse separat für die Systeme Ga-Hg, Ga-Pb, Al-Pb und Al-In. Die Temperaturabhängigkeit und die Absolutwerte der Grenzflächenspannung werden mit den vorgestellten Modellen verglichen. Im Anschluß daran werden die Oberflächenspannungsmeßergebnisse für das System Ga-Pb vorgestellt, dies geschieht unter Bezugnahme auf Benetzungsphänomene, Adsorptionserscheinungen und Keimbildungsprozesse. In einem relativ selbständigen Kapitel am Ende der Arbeit werden experimentelle Ergebnisse zur Durchmischung und Entmischung wiedergegeben und mit theoretischen Ergebnissen zum diffusionsgesteuerten Durchmischungsprozeß verglichen.

We report approaches to grow ultrathin Ru films for application as a seed layer and Cu diffusion barrier. For chemical vapor deposition (CVD) with Ru3(CO)12 we show the role surface hydroxyl groups have in nucleating the Ru islands that grow into a continuous film in a Volmer-Weber process, and how the nucleation density can be increased by applying a CO or NH3 overpressure. Thinner continuous films evolve in the presence of a CO overpressure. We report an optimun ammonia overpressure for Ru nucleation and that leads to deposition of smoother Ru thin films. Finally, we report a comparison of amorphous Ru films that are alloyed with P or B and demonstrate 3-nm thick amorphous Ru(B) films function as a Cu diffusion barrier.

Methane hydrate nucleation and growth in porous model carbon materials illuminates the way towards the design of an optimized solid-based methane storage technology. High-pressure methane adsorption studies on pre-humidified carbons with well-defined and uniform porosity show that methane hydrate formation in confined nanospace can take place at relatively low pressures, even below 3 MPa CH4, depending on the pore size and the adsorption temperature. The methane hydrate nucleation and growth is highly promoted at temperatures below the water freezing point, due to the lower activation energy in ice vs. liquid water. The methane storage capacity via hydrate formation increases with an increase in the pore size up to an optimum value for the 25 nm pore size model-carbon, with a 173% improvement in the adsorption capacity as compared to the dry sample. Synchrotron X-ray powder diffraction measurements (SXRPD) confirm the formation of methane hydrates with a sI structure, in close agreement with natural hydrates. Furthermore, SXRPD data anticipate a certain contraction of the unit cell parameter for methane hydrates grown in small pores.

Thema der vorgelegten Dissertation ist der Mechanismus der Keimbildung und des Wachstums von Platinclustern in Lösung und auf Biopolymeren nach der Reduktion von Platin-Salzen. Die Untersuchung wird auf atomarer Skala durch ab-initio Molekulardynamik mit der Methode von Car und Parrinello durchgeführt. In einem klassischen, generell akzeptierten Mechanismus erfolgt die Aggregation von Pt-Atomen nur nach kompletter Reduktion der Pt(II)-Komplexen zum metallischen Pt(0)-Zustand. Im Gegensatz dazu, in der hier beobachteten Reaktionsablauf entstehen stabile Pt-Pt-Bindungen schon nach einem einzigen Reduktionsschritt. Darüber hinaus wird es gefunden, dass kleine Pt-Cluster durch Addition von unreduzierten PtCl2(H2O)2-Komplexen wachsen können. Das stimmt mit einem experimentell beocbachteten autokatalytischen Clusterwachstumsmechanismus überein. Es wird weiterhin gefunden, dass Pt(II)-Komplexe, die kovalent an DNA oder an Proteine gebunden sind, als sehr effiziente Nukleationszentren für das weitere Metallclusterwachstum wirken können. Das ist eine Konsequenz des starken Donor-Charakters der organischen Liganden, in derer Anwesenheit stärkere Metall-Metall-Bindungen als frei in der Lösung gebildet werden können. In der Tat, in Metallisierungsexperimenten können 5 Nanometer dünne, mehrere Mikrometer lange, regelmässige Clusterkette erzeugt werden, die rein heterogen auf das Biomolekulare Templat gewachsen sind. / In this thesis we investigate the molecular mechanisms of platinum cluster nucleation and growth in solution and on biopolymers by means of first-principles molecular dynamics. In contrast with a classical picture where clusters nucleate by aggregation of metallic Pt(0) atoms, we find that Pt--Pt bonds can form between dissolved Pt(II) complexes already after a single reduction step. Furthermore, we observe that small clusters grow by addition of unreduced PtCl2(H2O)2 complexes, consistently with an autocatalytic growth mechanism. Moreover Pt(II) ions covalently bound to biopolymers are found to act as preferred nucleation sites for the formation of clusters. This is a consequence of the strong donor character of the organic ligands which induce the formation of stronger metal-metal bonds than those obtained in solution. In fact, in metallization experiments we obtain a clean and purely heterogeneous metallization of single DNA molecules leading to thin and uniform Pt cluster chains extended over several microns.

In dieser Arbeit wurde der Einfluss verschiedener Additive (Carbonsäuren, Phosphonsäuren und Retardan P) auf die einzelnen Teilprozesse des Abbindens von Gips an technischen und synthetischen Halbhydraten unter vergleichbaren Bedingungen untersucht. Vorrangig bei der Keimbildung und beim Kristallwachstum wurde ein Einfluss der Additive beobachtet. Das pH-abhängige Wirkungsoptimum kann mit der Speziation der Additive erklärt werden. Ihre Wirkung wird durch Adsorption auf CaSO4-Oberflächen verursacht. Die Untersuchungen ergaben eine bevorzugte Ca-Affinität mit den Flächen (120) und (001) zunehmend von Citronensäure über Weinsäure, HEDP zu HDTMP. Die in verdünnten homogenen Lösungen erhaltenen Ergebnisse sind nicht direkt auf den Abbindeprozess in Pasten übertragbar. In-situ Ramanspektroskopie und Auswaschexperimente weisen in Pasten auf irreversible Adsorption und ein Überwachsen der Additive hin, was zur Abnahme ihrer Wirkung führt. Auf die Festigkeit der abgebundenen Gipskörper zeigen die Additive kaum Einfluss.

The iron-group metals and alloys are of interest because of their excellent soft magnetic properties. They have found a wide application field in the storage technology, especially for reading/writing elements in the hard drive head, and in microelectromechanical systems (MEMS). Especially the CoFe system, which possesses the highest, among others, saturation magnetisation of 2.45 T and a relatively low coercivity of about 2×10^-5 T, is of interest. These properties are crucial for the further development in the storage technology. Electrodeposition is a very promising alternative to the physical vapour deposition techniques (PVD) to produce soft magnetic layers and microstructures. The advantage of electrodeposition in comparison to PVD processes is the fact that it is an inexpensive method. Moreover, electrodeposition is the most appropriate process for the writing head fabrication since it allows to deposit high aspect ratio layers with a thickness ranging from a few monolayers up to more than 1 um onto a complex geometry substrate. A superposition of an external magnetic field during the electrodeposition can affect the deposit properties. Mainly the morphology of the deposited layers is influenced. This is mostly caused by the Lorentz force driven convection, i.e. the magnetohydrodynamic (MHD) effect. Whilst the knowledge of uniform external magnetic field effects on the electrodeposition of single metals has been greatly improved during the past decade, an alloy deposition is still a challenging task. Due to a lack of understanding of mechanisms of a magnetic field impact on the deposition of CoFe alloys and their technological importance a detailed investigation is of demand. The aim of this work is to analyse in detail the effects induced by a homogeneous magnetic field with different strength and relative to the electrode surface orientation on the electrodeposition of thin CoFe alloy films of different composition. This study is divided into three major parts: an analysis of the electrochemical behaviour (1), nucleation and growth processes (2) and the determination of the morphology and the physical properties of the deposited layers (3). 1. A detailed analysis of the electrochemical processes is performed. The influence of the magnetic field with respect to its flux density and relative to the electrode surface orientation on the reactions rates has been investigated. A special attention has been given to the side reactions accompanying the metal reduction, i.e. the hydrogen evolution reaction (HER). Which has a significant impact on the layer’s properties. It has been shown that the electrochemical reaction rates are improved in the parallel to the electrode magnetic field due to the classical MHD effect. On the contrary, in the perpendicular to the electrode magnetic field nearly no effect on the metal reduction is observed, whilst the HER rate is significantly increased. The reason of that is seen in the improved desorption of hydrogen bubbles from the electrode surface due to a localized convection in a bubble vicinity, the so called micro- MHD effect. Moreover, the additional convection introduced by a magnetic field, regardless of its relative to the electrode surface orientations, leads to a reduced interface pH value. This, in turn, results in an improved layer quality, i.e. the hydroxides precipitation is inhibited. 2. The nucleation and the very beginning of the layer growth are of particular importance for thin film deposition. Since the deposit properties are determined by these processes an extensive study of the very initial stages of electrocrystallisation is presented. This was performed by an analysis of the current density vs. time transients. It was found that the nucleation behaviour can be altered by a magnetic field. The changes in the nucleation behaviour have been studied on the basis of theoretical models by an current density-time transients analysis. Regardless of the electrolyte chemistry, the magnetic field strength, and its relative to the electrode orientation, similar features in the current density-time transients have been observed. The nucleation and growth are characterised by a layer-by-layer mode. The first nucleation and growth step at the very beginning of the potential step has been attributed to the 2D (most probably epitaxial) layer formation (up to a few monolayers), which was found unaffected by a magnetic field superposition. The 2D step is then followed by the next nucleation and growth step indicated by the occurrence of a maximum in the current density-time transients. This is attributed to the nucleation and 3D diffusion controlled growth and is altered by a magnetic field applied in the parallel-to-electrode configuration. The experimental dependencies have been examined by known theoretical models. This analysis revealed that the superposition of the parallel magnetic field leads to a retardation of the steady state nucleation rate (AN0) due to the MHD effect acting in the electrolyte. A qualitative model was proposed in order to explain this phenomenon. In contrast, the perpendicular to the electrode magnetic field does not change the nucleation behaviour. However, the growth mode of the layer is remarkably changed, i.e. a columnar growth is observed. 3. The magnetic field impact on the electrochemical reaction rates, on the desorption of hydrogen from the electrode surface, and on the nucleation behaviour has strong consequences for the resulting layer characteristics. This can be summarized as follows: • The most pronounced effect is noticed for the morphology of the layers. The quality of the layers deposited in a magnetic field, irrespective of its relative to the electrode orientation, is strongly improved. The reason of this is an enhanced desorption of hydrogen from the electrode surface. As a result large holes left by hydrogen bubbles observed for the layers deposited without a field disappear for the layers deposited under the influence of a magnetic field. The layers deposited under an influence of the parallel to the electrode magnetic field appear denser and more homogeneous than the ones obtained without a magnetic field. On the contrary, the layers deposited in the perpendicular to the electrode magnetic field appeared more diverse. The most remarkable effect has been observed for the layers deposited from the Fe and the CoFe(A) electrolyte in a perpendicular magnetic field where the grains tend to grow as separated columns in the direction of the magnetic field. A scaling analysis has revealed a smoothing effect of a parallel magnetic field manifested in a reduced value of the roughness exponent in comparison to the layers deposited without a magnetic field. On the contrary, the roughness exponent has increased for the layers obtained in the perpendicular to the electrode magnetic field, i.e. a roughening effect of the perpendicular magnetic field is observed. • No magnetic field effects neither on the crystal structure nor on the texture of the deposits have been observed. All layers irrespective of the deposition parameters develop a fibre texture. Nevertheless, the internal stress state of the deposited layers is affected by a magnetic field. A magnetic field applied during the deposition of alloy layers from buffered electrolytes, irrespective of its relative to the electrode orientation, reduces the internal stress of the layer. This effect is attributed to an improved desorption of hydrogen from the electrode surface, which is observed under the influence of a magnetic field. • The chemical composition of the deposited alloy layers, irrespective of the deposition parameters, is unchanged by magnetic fields. • The magnetic properties of the deposits are found to be affected by a magnetic field applied during the deposition. These effects are caused by microstructural changes induced by the magnetic field, i.e. the roughness of the layer, the internal stress state, and the chemical composition of the deposit. A good correlation between the coercivity and the roughness is found. Moreover, an in-plane magnetic anisotropy is observed in the alloy layers deposited under the influence of the parallel to the electrode magnetic field, where, according to the XRD investigations, isotropic properties were expected. The origin of this phenomenon is seen in a preferential same atom couples formation in the magnetic field direction. / Metalle und Legierungen der Eisengruppe sind von großem Interesse insbesondere wegen ihrer exzellenten weichmagnetischen Eigenschaften. Ein breites Anwendungsgebiet liegt in der Speichertechnologie, sie finden vorrangig Einsatz in Lese- und Schreibköpfen und in mikroelektromechanischen Systemen (MEMS). Besonders das CoFe-System, das u.a. die höchste Sättigungsmagnetisierung von 2,45 T bei einer relativ niedrigen Koerzitivfeldstärke von ca. 2×10^-5 T aufweist, ist interessant für zukünftige Entwicklungen in der Speichertechnologie. Im Vergleich zu physikalischen Abscheideverfahren, wie PVD (physical vapor deposition) ist die Elektrokristallisation eine einfache und preiswerte Alternative zur Herstellung von weichmagnetischen Schichten und Strukturen, die sich im Herstellungsprozess von Schreib-und Leseköpfen durchgesetzt hat. Es ist möglich Schichten und komplexe geometrische Strukturen mit einer Stärke von einigen Monolagen bis zu mehr als 1µm und in hohen Aspektverhältnissen abzuscheiden. Durch Überlagerung von externen Magnetfeldern während der Elektrodeposition können die Eigenschaften und insbesondere die Morphologie der Schichten signifikant beeinflusst werden. Die Ursache dafür besteht im Wesentlichen in der durch Lorentzkräfte angetriebenen Konvektion, die als magnetohydrodynamische Konvektion (MHD) bezeichnet wird. Während im letzten Jahrzehnt durch grundlegende Untersuchungen der Kenntnisstand bezüglich der elektrochemischen Abscheidung einzelner Metalle in überlagerten Magnetfeldern vertieft wurde, ist das Verständnis zum Mechanismus der Legierungsabscheidung wenig erforscht und eine Herausforderung. Es besteht kaum Kenntnis zum Mechanismus der CoFe Abscheidung unter dem Einfluss externer Magnetfelder und deren Bedeutung für technologische Prozesse. Das Ziel dieser Arbeit ist es, den Einfluss homogener Magnetfelder unterschiedlicher Stärke und Orientierung bezüglich der Elektrodenoberfläche während der Elektrokristallisation von CoFe Legierungen unterschiedlicher Zusammensetzung zu untersuchen und die magnetfeldinduzierten Effekte detailliert und grundlegend zu analysieren. Die Arbeit ist in drei wesentliche Abschnitte gegliedert, (1) die Analyse des elektrochemischen Verhaltens, (2) die Untersuchung von Keimbildungs- und Wachstumsprozessen, (3) die Charakterisierung der Morphologie und der physikalischen Eigenschaften der Schichten. 1. Die elektrochemischen Prozesse und Abscheideraten wurden in Abhängigkeit von der magnetischen Flussdichte und Orientierung bezüglich der Elektrodenanordnung detailliert analysiert. Besondere Berücksichtigung fand die die Metallabscheidung begleitende Nebenreaktion, die Wasserstoffreduktion (HER), die signifikant die Eigenschaften der Schichten beeinflusst. Es konnte gezeigt werden, dass die Rate der Metallabscheidung in einem Magnetfeld, welches parallel zur Elektrode ausgerichtet ist, erhöht wird, was auf den klassischen MHD-Effekt zurückzuführen ist, der im Elektrolyten eine Strömung generiert. Im Gegensatz dazu wurde in einem homogenen Magnetfeld das senkrecht auf die Probe gerichtet ist, nahezu kein Einfluss auf die Reduktion der Metallionen gefunden, während die HER-Reaktion signifikant erhöht wird. Die Ursache ist in einer beschleunigten Desorption der Wasserstoffblasen von der Elektrodenoberfläche zu sehen, die durch lokale Konvektion in Blasennähe hervorgerufen und als mikro-MHD Effekt bezeichnet wird. Darüber hinaus bewirkt die magnetfeldinduzierte Konvektion unabhängig von der Magnetfeldorientierung einen geringeren Anstieg des oberflächennahen pH-Wertes. Das wiederum führt zu einer verbesserten Schichtqualität, da die spontane Bildung von Hydroxiden inhibiert wird. 2. Die Keimbildung und der Beginn des Schichtwachstums sind von besonderer Bedeutung für die Elektrokristallisation dünner Schichten, da die Schichteigenschaften wesentlich durch diese Prozesse bestimmt werden. Die Initialschritte der Elektrokristallisation wurden im Detail untersucht und dargestellt. Die Analyse erfolgt auf der Grundlage von Stromdichte-Zeit-Transienten. Es konnte gezeigt werden, dass das Keimbildungsverhalten durch ein überlagertes Magnetfeld beeinflusst wird. Unabhängig von der Zusammensetzung des Elektrolyten, der magnetischen Flussdichte und der Orientierung zur Elektrodenoberfläche wurden vergleichbare Stromdichte-Zeit-Verläufe beobachtet. Keimbildung und Wachstum können durch einen Layer-by-Layer Modus charakterisiert werden. Der erste Keimbildungs- und Wachstumsschritt, der unmittelbar nach dem Anlegen des Abscheidepotentials stattfindet, ist durch eine 2D Schichtbildung (wahrscheinlich epitaktisch) gekennzeichnet, die zur Ausbildung von einigen Monolagen führt. Dieser Schritt wird durch ein äußeres Magnetfeld nicht beeinflusst. Dem 2D-Schritt folgen weitere Keimbildungs- und Wachstumsschritte, die durch ein Maximum im Stromdichte-Zeit-Transienten gekennzeichnet sind. Das Verhalten ist auf Keimbildung und 3D diffusionskontrollierte Wachstumsprozesse zurückzuführen und wird durch ein Magnetfeld parallel zur Elektrodenoberfläche beeinflusst. Die experimentellen Ergebnisse wurden mit Hilfe bekannter theoretischer Modelle analysiert. Es wurde gezeigt, dass die Überlagerung eines parallel zur Oberfläche angeordneten Magnetdfeldes zu einer Verringerung der stationären Keimbildungsrate (AN0) führt, was ebenfalls auf die Wirkung des MHD-Effektes zurückzuführen ist. In der Arbeit wird ein qualitatives Modell für die Legierungsabscheidung in einem überlagerten homogenen Magnetfeld vorgeschlagen, das die beobachteten Phänomene erklärt. Im Gegensatz dazu wurde in einem senkrecht zur Elektrodenoberfläche ausgerichteten Magnetfeld kein Einfluss auf den Keimbildungs- und Wachstumsmechanismus anhand der Stromdichte-Zeit-Transienten festgestellt. Trotzdem wird eine stark veränderte Schichtmorphologie, die ein kolumnares Kornwachstum zeigt, beobachtet. 3. Der Einfluss eines äußeren Magnetfeldes auf die elektrochemischen Abscheideraten, auf die Desorption von Wasserstoff von der Elektrodenoberfläche und auf das Keimbildungsverhalten hat Konsequenzen auf die Schichteigenschaften. Diese können wie folgt zusammengefasst werden: • Der Einfluss eines äußeren Magnetfeldes auf die Schichtmorphologie ist auffallend. Die Qualität der Schichten, die in einem Magnetfeld abgeschieden wurden, wird unabhängig von der Orientierung des Magnetfeldes zur Elektrodenoberfläche deutlich verbessert. Als Ursache ist die beschleunigte Desorption der Wassersoffblasen von der Elektrodenoberfläche anzusehen. Ohne äußeres Magnetfeld verbleiben große Defekte in Form von Löchern auf der Oberfläche, die durch anhaftende Wasserstoffblasen verursacht werden, die in einem überlagerten Magnetfeld nicht beobachtet werden. Schichten, die in einem Magnetfeld parallel zur Elektrodenoberfläche erhalten werden, sind dichter und homogener. Im Gegensatz dazu haben Schichten in einem senkrecht zur Oberfläche abgeschiedenen Magnetfeld eine mannigfaltige Morphologie. Schichten aus Fe und CoFe Legierungen mit einem hohen Eisenanteil wachsen in Form von separaten Körnern und Säulen in Richtung des senkrecht ausgerichteten Magnetfeldes. Mittels Scaling-Analyse wurden Rauhigkeitsexponeten ermittelt, die den glättenden Effekt eines parallel zur Elektrode ausgerichteten Magnetfeldes auf die Schichtmorphologie bestätigen im Vergleich zu Schichten, die ohne Magnetfeld abgeschieden wurden. Die Rauhigkeitsexponenten für Schichten, die in einem senkrecht ausgerichteten Magnetfeld abgeschieden wurden, sind hingegen deutlich erhöht. • Weder auf die kristallographische Struktur noch auf die Textur der Schichten konnte ein Einfluss des überlagerten Magnetfeldes nachgewiesen werden. Alle Schichten unabhängig von den Abscheidebedingungen weisen eine Fasertextur auf. Trotzdem konnte ein signifikanter Einfluss des Magnetfeldes auf die innere Spannung der Schichten bestätigt werden. Insbesondere vermindert sich die innere Spannung von Schichten unabhängig von der Orientierung des angelegten Magnetfeldes, die aus einem gepufferten Elektrolyten abgeschieden wurden. Die Ursache ist auch hier auf die verbesserte Desorption von Wasserstoff zurückzuführen. • Die chemische Zusammensetzung der Schicht wird für die untersuchten Systeme durch ein Magnetfeld nicht verändert. • Die magnetischen Eigenschaften der Schichten werden beeinflußt, wenn während der Elektrokristallisation ein Magnetfeld überlagert wird. Diese Effekte werden durch die mikrostrukturellen Veränderungen, die durch ein überlagertes Magnetfeld induziert werden verursacht, d.h. durch die Rauhigkeit der Schicht, die innere Schichtspannung und die chemische Zusammensetzung. Es wird eine gute Korrelation zwischen der Koerzitivfeldstärke und Rauhigkeit der Schichten gefunden. Darüber hinaus wurde eine in-plane Anisotropie beobachtet, wenn während der Elektrokristallisation ein Magnetfeld parallel zur Elektrodenoberfläche angelegt wurde, obwohl aus röntgenographischen Untersuchungen isotrope Eigenschaften erwartet wurden. Als Ursache für dieses Phänomen wird eine bevorzugten Ausbildung und Ausrichtung von gleichatomigen Paaren im Magnetfeld angenommen.

Methane hydrate nucleation and growth in porous model carbon materials illuminates the way towards the design of an optimized solid-based methane storage technology. High-pressure methane adsorption studies on pre-humidified carbons with well-defined and uniform porosity show that methane hydrate formation in confined nanospace can take place at relatively low pressures, even below 3 MPa CH4, depending on the pore size and the adsorption temperature. The methane hydrate nucleation and growth is highly promoted at temperatures below the water freezing point, due to the lower activation energy in ice vs. liquid water. The methane storage capacity via hydrate formation increases with an increase in the pore size up to an optimum value for the 25 nm pore size model-carbon, with a 173% improvement in the adsorption capacity as compared to the dry sample. Synchrotron X-ray powder diffraction measurements (SXRPD) confirm the formation of methane hydrates with a sI structure, in close agreement with natural hydrates. Furthermore, SXRPD data anticipate a certain contraction of the unit cell parameter for methane hydrates grown in small pores.

Zu Beginn der Arbeit werden thermodynamische, strukturelle und statistische Grundlagen und Modelle wiedergegeben, die einerseits Entmischungssysteme und andererseits flüssige Ober- und Grenzflächen betreffen. Hieran schließt sich eine umfangreiche Darstellung der Meßmethode an, die die theoretischen Zusammenhänge für die Beschreibung der Formen flüssiger Grenzflächen sowie eine Darstellung aller experimentell möglichen Kraftmeßkurven und deren Auswertung beinhaltet. Weiterhin folgt die Darstellung der Dichte-, Dichtedifferenz-, und Grenzflächenspannungsmeßergebnisse separat für die Systeme Ga-Hg, Ga-Pb, Al-Pb und Al-In. Die Temperaturabhängigkeit und die Absolutwerte der Grenzflächenspannung werden mit den vorgestellten Modellen verglichen. Im Anschluß daran werden die Oberflächenspannungsmeßergebnisse für das System Ga-Pb vorgestellt, dies geschieht unter Bezugnahme auf Benetzungsphänomene, Adsorptionserscheinungen und Keimbildungsprozesse. In einem relativ selbständigen Kapitel am Ende der Arbeit werden experimentelle Ergebnisse zur Durchmischung und Entmischung wiedergegeben und mit theoretischen Ergebnissen zum diffusionsgesteuerten Durchmischungsprozeß verglichen.

In dieser Arbeit wurde der Einfluss verschiedener Additive (Carbonsäuren, Phosphonsäuren und Retardan P) auf die einzelnen Teilprozesse des Abbindens von Gips an technischen und synthetischen Halbhydraten unter vergleichbaren Bedingungen untersucht. Vorrangig bei der Keimbildung und beim Kristallwachstum wurde ein Einfluss der Additive beobachtet. Das pH-abhängige Wirkungsoptimum kann mit der Speziation der Additive erklärt werden. Ihre Wirkung wird durch Adsorption auf CaSO4-Oberflächen verursacht. Die Untersuchungen ergaben eine bevorzugte Ca-Affinität mit den Flächen (120) und (001) zunehmend von Citronensäure über Weinsäure, HEDP zu HDTMP. Die in verdünnten homogenen Lösungen erhaltenen Ergebnisse sind nicht direkt auf den Abbindeprozess in Pasten übertragbar. In-situ Ramanspektroskopie und Auswaschexperimente weisen in Pasten auf irreversible Adsorption und ein Überwachsen der Additive hin, was zur Abnahme ihrer Wirkung führt. Auf die Festigkeit der abgebundenen Gipskörper zeigen die Additive kaum Einfluss.