Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / This study evaluated the effect of thermally deposited siloxane-methacrylate coating on bond strength glass-fiber post to core materials. Furthermore, evaluated mechanical properties of flexural strength, flexural modulus and stiffness. For bond strength, two types of GFP (Exacto, Angelus and White Post DC, FGM) were divided into eight groups (n = 13): S (control): pre-hydrolyzable silane (Prosil, FGM) was applied on the post surface; SA: silane was applied followed by one layer of adhesive (Scothbond, 3M Espe); HS: etching with 35% H2O2 (Whiteness HP Max, FGM) for one minute followed by silane; HSA: etching with H2O2 followed by silane and adhesive; Si: deposited siloxane-methacrylate coating (Si-O) by means of immersion of post in experimental solutions of5% MPTS fowled by heating at 120°C for one hour; SiS: silane application after Si-O; SiA: application adhesive after Si-O; SiSA: silane and adhesive application after Si-O. The composite resin restorations (AllCem Core, FGM) were simulated using translucent silicone molds. After 24 hours water storage at 37 °C, the post/resin assembly was serially sectioned in beams that were subjected to a microtensile bond strength test. For analysis of mechanical properties, eighteen White Post DC and eighteen Exact were used (n = 6). Post without surface treatment, etched with H2O2 and coated with siloxane methacrylate after thermally deposition had their mechanical properties evaluated skin test flexural strength of three points. The data presented normal and homogeneous distribution and subjected to two-way ANOVA and Tukey test. The results showed that the surface treatment only affected the bond strength in Exacto post (P<0.001), while for the White Post DC all groups were statistically equal to the control (22.5 ± 5.1). The highest bond strength values were obtained in SiS (40.4 ± 6.9) and SiSA (38.8 ± 5.3) groups. The etching with H2O2 (HS: 22.9 ± 2.5 and HSA: 25.5 ± 4.5) promoted increased bond strength when compared to control (15.8 ± 4.1), however, had lower values than the thermally deposition siloxane. The mechanical proprieties were not affected by surface treatment, only by the type of post, wherein Exacto post showed highest means of flexural strength, flexural modulus and lower stiffness. Thus, it is concluded that the thermally deposited siloxane-methacrylate coating is a viable option for increasing the bond strength to the core pins without alterations completion of its mechanical properties. / O objetivo desses estudo foi avaliar o efeito do revestimento de pinos de fibra com siloxano-metacrilato, após deposição térmica, na resistência de união ao núcleo de preenchimento em resina composta. Além disso, avaliou a influência deste tratamento nas propriedades mecânicas de resistência flexural, modulo de flexão e rigidez. Para avaliar a resistência de união dois tipos de pinos (White Post DC3, FGM, Produtos Odontológicos e Exacto 3, Ângelus) foram divididos aleatoriamente em oito grupos (n=13): S (controle): uma camada de silano (Prosil, FMG) foi aplicado sobre a superfície do pino; SA: aplicação de uma camada de silano, seguido do adesivo (Scothbond, 3M Espe); HS: condicionamento com H2O2 35% (Whiteness HP Max, FGM) por um minuto seguido da aplicação de silano; HSA: aplicação de H2O2 seguido da aplicação de silano e adesivo; Si: revestimento com siloxano-metacrilato após deposição térmica (Si-O), por meio da imersão em solução experimental de MTPS a 5% seguido de aquecimento a 120°C por 1 hora. SiS: aplicação de silano após Si-O; SiA: aplicação de adesivo após Si-O; SiSA: aplicação de silano e adesivo após Si-O. As restaurações em resina composta (AllCem Core, FGM) foram simuladas utilizando moldes de silicones translúcidos. Após 24h de armazenagem em água a 37ºC, as amostras foram submetidas a cortes seriados, perpendiculares ao longo eixo do pino, obtendo amostras com dimensões de aproximadamente 1x1mm, com formato de palito. As amostras foram submetidas ao ensaio mecânico de microtração à velocidade de 0,7 mm/min até o rompimento dos espécimes. Para análise das propriedades mecânicas, dezoito White Post DC e dezoito Exacto foram utilizados (n=6). Pinos sem tratamento de superfície, condicionados com H2O2 e revestidos com siloxano-metacrilato após deposição térmica tiveram suas propriedades avaliadas pelo ensaio mecânico de resistência flexural de três pontos. Os dados obtidos apresentaram distribuição normal e homogênea e foram submetidos a análise de variância fatorial de dois fatores e teste de Tukey. Os resultados demostraram que o tratamento de superfície só afetou a resistência de união no pino Exacto (P<0,001), enquanto para o White Post DC todos os grupos foram estatisticamente iguais ao controle (22,5 ± 5,1). Os maiores valores de resistência de união foram obtidos nos grupos SiS (40,4 ± 6,9) e SiSA (38,8 ± 5,3). O condicionamento com H2O2 (HS: 22,9 ± 2,5 e HSA: 25,5 ± 4,5) promoveu o aumento da resistência de união quando comparado com o controle (15,8 ± 4,1), no entanto, obteve valores menores que a deposição térmica de siloxano. As propriedade mecânicas não foram afetadas pelo tratamento de superfície, apenas pelo tipo de pino, sendo que o Exacto apresentou maiores valores de resistência flexural, modulo de flexão e menor rigidez. Dessa forma, conclui-se que a deposição térmica com siloxano-metacrilato é uma opção viável para o aumento da resistência de união dos pinos ao núcleo de preenchimento, sem alterações da suas propriedades mecânicas. / Mestre em Odontologia

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / O presente estudo visa avaliar a influência da espessura do filme de cimento sobre a resistência de união de pinos de fibra de vidro em diferentes regiões do conduto radicular (cervical, médio e apical), cimentados com cimento resinoso autoadesivo, com e sem a adição de Rodamina B, por meio do teste de push-out. Quarenta raízes foram incluídas em resina epóxi, submetidas a tratamento endodôntico e obturadas com guta percha e cimento endodôntico sem eugenol. Após sete dias, os condutos foram desobstruídos e aleatoriamente divididos em 4 grupos (n=10), de acordo com as brocas do sistema de pinos de fibra WhitePost DC (FGM) usadas: (G1) broca #2; (G2) broca #3; (G3) broca #4; (G4) broca #2. O preparo foi realizado a uma profundidade de 10 mm. A cimentação foi realizada com o cimento resinoso autoadesivo RelyX U100 (3M ESPE), e apenas nos grupos G1, G2 e G3 uma pequena quantidade de Rodamina B em pó foi usada como corante no cimento. Após uma semana, cada raiz foi seccionada em máquina de corte, obtendo-se 6 fatias de 1 0,1 mm de espessura. Antes do ensaio de push-out, imagens digitais foram obtidas, por meio de um estereomicroscópio, de ambas as faces de cada fatia, para determinação do raio dos pinos e da espessura do filme de cimento. Após o ensaio mecânico, novas imagens foram obtidas para determinação do modo de falha. Para determinar a espessura de cimento, foi desenvolvida uma rotina (macro) no software KS 400. Os dados foram estatisticamente analisados com análise de variância (ANOVA) 2 fatores (influência do diâmetro da broca e influência dos terços) e Kruskal-Wallis (influência da espessura do filme de cimento). Comparações múltiplas foram realizadas com o teste Duncan. Todos os testes foram aplicados com &#945;=0,05. Houve diferenças significantes entre os grupos em relação ao diâmetro da broca (p<0,0001), sendo G2 (14,62 5,15 MPa) > G1 (10,04 5,13 MPa) > G3 (7,68 6,14 MPa). O terço do conduto exerceu influência significativa sobre a resistência adesiva (p<0,0001), sendo os maiores valores obtidos no terço apical. As espessuras do filme de cimento foram estatisticamente diferentes nos grupos. Os maiores valores de espessura de cimento foram obtidos no G3 (248,78 &#956;m), seguido de G2 (185,91 &#956;m) e G1 (110,16 &#956;m), sendo o último estatisticamente semelhante ao G4 (119,99 &#956;m). Os resultados de G1(10,04 5,13 MPa) e G4 (8,89 + 5,18 MPa) foram estatisticamente semelhantes, indicando que a presença da Rodamina B não influencia significativamente na resistência de união. O tipo de falha predominante no G1 foi mista, no G2, adesiva entre pino e cimento, e no G3 e G4, adesiva entre cimento e dentina. O diâmetro da broca influenciou significativamente nos resultados de resistência de união ao teste de push-out. O ligeiro aumento na espessura do filme de cimento promoveu um aumento nos valores de resistência, quando comparado com filmes de cimento muito finos ou muito espessos. / The present study has the purpose of evaluating the influence of the cement film thickness on the bond strength of glass fiber posts in different portions of the root canal (cervical, medium, and apical), cemented with self-adhesive resin cement, with and without the addition of Rhodamine B, by means of the push-out test. Forty roots were included in epoxy resin, underwent endodontic treatment, and were filled with gutta-percha and endodontic cement without eugenol. After seven days, the canals were de-obstructed and randomly divided into four groups (n=10), according to the WhitePost DC (FGM) fiber glass post systems burs: (G1) bur #2; (G2) bur # 3; (G3) bur #4; (G4) bur #2. The preparation was made at a 10 mm depth. The posts were cemented with RelyX U100 (3M ESPE) self-adhesive resin cement, and only in groups G1, G2, and G3 a small amount of powdered Rhodamine B was used as a stain in the cement. After one week, each root was sliced in a cutting machine, resulting in six slices 1 0,1 mm thick. Before the push-out test, a stereomicroscope was used to obtain digital images of both sides of each slice, in order to determine the radius of the posts, as well as the thickness of the cement film. After the mechanical test, new images were obtained, to determine the failure mode. In order to determine the cement thickness, a macro routine was developed in the software KS 400. The data were analyzed statistically through two-way ANOVA (influence of the bur diameter and influence of the thirds), and Kruskal-Wallis (influence of the cement film thickness). Duncan test was used for multiple comparisons. All tests were run with &#945;=0,05. There were significant differences between the groups regarding the bur diameter (p<0,0001), with G2 (14,62 5,15 MPa) > G1 (10,04 5,13 MPa) > G3 (7,68 6,14 MPa). The canal portion had significant influence on the bond strength, and the highest values were obtained at the apical third (p = 0,0001). The cement film thicknesses were statistically different in all groups. The highest cement thickness values were obtained in G3 (248,78 &#956;m), followed by G2 (185,91 &#956;m), and G1 (110,16 &#956;m), the latter being statistically similar to G4 (119,99 &#956;m). G1 (10,04 5,13 MPa) and G4 (8,89 + 5,18 MPa) showed statistically similar results, which indicates that the presence of Rhodamine B did not significantly influence the bond strength. The predominant type of failure for G1 was mixed, for G2 was adhesion between post and cement, and for G3 and G4 was adhesion between cement and dentin. The bur diameter significantly influenced the results for shear bond strength for the push-out test, as well as the cement film thickness. The slight increase in the cement thickness allowed an increase in the values of shear bond strength in comparison with very thin or very thick cement films.

Objetivo: Este estudo se propõe a verificar a influência do adesivo, material de preenchimento e hibridização da dentina na força de retenção de pinos intra-radiculares na técnica direta indireta e comparar o teste de tração de push out com o pull out. Métodos: 60 raízes de dentes bovinos com comprimento de 12 mm foram tratadas endodonticamente e divididas aleatoriamente em 6 grupos (n=10): grupo 1 (técnica direta-indireta, adesivo fotopolimerizável, cimento resinoso, teste de pull out); grupo 2 (idem ao grupo 1 porém o cimento resinoso foi substituído pela resina composta); grupo 3 (idem ao grupo anterior porém o adesivo fotopolimerizável foi substituído pelo químico); grupo 4 (idem ao anterior porém o teste utilizado foi o de push out); grupo 5 (idem ao grupo anterior porém o adesivo utilizado foi o auto condicionante); e grupo 6 (idem ao grupo anterior porém a dentina foi pré hibridizada). A força de retenção foi determinada através do teste de tração usando Universal Testing Machine (Instron). Todos os dados foram analisados usando one-way analysis of variance (ANOVA) com a significância de p<0.05 e complementadas com teste de Tukey. Após o teste, as interfaces adesivas onde ocorreram as falhas foram examinadas e classificadas. Resultado: Houve diferença estatística na comparação de materiais (adesivo, material de preenchimento). A hibridização da dentina não apresentou melhoras na retenção dos pinos . A maior parte das fraturas ocorreu na interface dentina/resina. Conclusão: Com base nos resultados obtidos, concluímos que material de preenchimento, o tipo de adesivo, influenciaram na retenção de pinos de fibra; e a pré-hibridização da dentina não apresentou melhoras a retenção dos pinos. O teste de push out apresentou mais detalhes para verificar o valor da adesão de cada terço da raiz; e o teste de pull out, para a força de retenção do pino ao longo do interior do conduto e o tipo de falha. / Objective: The aims of this study is to verify the influence of adhesive, filling material and dentin hybridization on fiber post retention force in diretc -indirect technique and compare the tensile test of push out with pull out. Methods: 60 bovine single roots with a length of 12 mm were endodontically treated and randomly divided into 6 groups (n = 10): group 1 (direct-indirect technique, light-curing adhesive, resin cement, pull out test), group 2 (same as group 1 but the resin cement was replaced by composite resin), group 3 (same as previous group but the light-curing adhesive was replaced by the chemical), group 4 (same as group 3 but the test was used was push out test), group 5 (same as group 4 but the adhesive used was the self etching) and Group 6 (same as previous group but the dentin was pre-hybridized). The retention force was determined by Universal Testing Machine (Instron). All data were analyzed using one-way analysis of variance (ANOVA) with significance of p <0.05 and complemented with Tukey test. After testing, the adhesive interfaces were examined and classifie. Result: There was a significant difference between comparison of materials (adhesive and filling material). The hybridization of dentin showed no improvement in the retention post. Most fractures occurred at the interface dentin / resin. Conclusion: Based on the results, we conclude that filling material, adhesive, influenced the retention of fiber posts, and the prehybridization of dentin did not improve the retention of fiber post. The push out test showed more details to verify the bonding between the post and dentin, and the pull out test for the retention force of the post inside the canal.

Este estudo avaliou, in vitro, a influência da radioterapia na resistência de união (RU) e na interface adesiva entre diferentes cimentos resinosos e dentina radicular. Sessenta caninos superiores foram distribuídos em 2 grupos (n=30) de acordo com a irradiação: não irradiados e irradiados. Os dentes do grupo irradiado foram submetidos à radioterapia com raios-X de 6 MV em frações de 2 Gy, com 30 ciclos, perfazendo 60 Gy. Os dentes foram seccionados para obtenção de raízes com 16 mm de comprimento, sendo realizado em seguida o preparo biomecânico com instrumento Reciproc R50 e obturação pela técnica de condensação lateral com cimento a base resina epóxica. Cada grupo foi subdividido de acordo com o cimento resinoso utilizado para a cimentação dos pinos de fibra de vidro (n=10): RelyX U200; Panavia F 2.0; RelyX ARC. Os pinos foram submetidos a tratamento de superfície com ácido fluorídrico 10% e cimentados de acordo com as recomendações de cada fabricante. Após a cimentação dos pinos, os dentes foram seccionados transversalmente em slices de 1 mm de espessura, obtendo-se 3 slices de cada terço da raiz. Os slices mais cervicais de cada terço foram utilizados para avaliar a RU, por meio do teste de push-out com velocidade de 0,5 mm/min, e posterior análise do padrão de falha em estereomicroscópio. Os slices mais apicais de cada terço foram selecionados para análise da interface cimento/dentina em MEV com aumentos de 100, 1000, 2000 e 4000X. Os dados de RU e adaptação da interface cimento/dentina foram submetidos à análise estatística pelos testes de ANOVA e Tukey, e Kruskal-Wallis e Duns, respectivamente. Os espécimes irradiados apresentaram menores valores de RU (8,23&plusmn;4,26) comparados aos dentes não irradiados (11,88&plusmn;6,42) (p<0,00001). Quanto aos cimentos resinosos, o RelyX U200 apresentou maiores valores na RU (15,17&plusmn;5,89) comparado aos cimentos RelyX ARC (7,68&plusmn;4,22) (p<0,0001) e Panavia F 2.0 (7,32&plusmn;2,71) (p<0,0001). O terço cervical apresentou maiores valores de RU (13,08&plusmn;6,10) comparado aos terços médio (9,72&plusmn;5,03) e apical (7,38&plusmn;4,53) (p<0,0001). O padrão de falhas mostrou ocorrência de falhas coesivas na dentina para os espécimes irradiados. Na análise da interface cimendo/dentina por MEV, observou-se maior desadaptação nos dentes submetidos à radioterapia. Em relação aos cimentos resinosos, foi observada maior adaptação com RelyX U200 e RelyX ARC comparados à Panavia F 2.0. Na análise qualitativa em MEV observou-se presença de fraturas e microfraturas na dentina radicular e menor presença de fibras colágenas em dentes irradiados. Para o cimento resinoso RelyX U200 e Panavia F 2.0 observou-se interface justaposta do cimento com a dentina radicular em dentes irradiados e não irradiados, sendo que para o cimento resinoso RelyX ARC foi observada formação de camada híbrida e tags de maneira similar para dentes irradiados e não irradiados. Concluiu-se que a radioterapia resultou na redução da resistência de união e na maior desadaptação da interface cimento resinoso/dentina radicular e que o cimento resinoso autoadesivo se apresentou como melhor alternativa para cimentação de pinos de fibra de vidro em dentes irradiados. / This in vitro study, evaluated the influency of radiotherapy on bond strength (BS) and adhesive interface between different resin cements and root dentin. Sixty maxillary canines were selected and distributed into two groups (n = 30) according to the irradiation protocol: non-irradiated and irradiated. The irradiated group were submitted to X-ray radiotherapy of 6 MV in fractions of 2 Gy, with 30 cycles, until complete 60 Gy. The teeth were sectioned to obtain 16 mm of root length, followed by biomechanical preparation with R50 reciproc instrument and obturation using the lateral condensation technique with epoxy resin-based sealer. Then, each group was subdivided according to the resin cement used for the glass fiber post cementation (n = 10): RelyX U200, Panavia F 2.0 and RelyX ARC. The posts were submitted to surface treatment with 10% hydrofluoric acid, and then cemented according to the manufacturer instructions. After the posts cementation, the teeth were sectioned transversely into 1 mm thick slices, and 3 slices were obtained from each root third. The most cervical slice of each third was used to evaluate the BS by the push-out test at 0.5 mm/min of velocity and the failure pattern was analyzed using stereomicroscopy. The most apical slice of each third was selected for SEM analysis, which were prepared and metalized. The dentin/cement interface analysis was performed at the following magnification: 100, 1000, 2000 and 4000X. The BS data and dentin/cement interface adaptation were submitted to statistical analysis by ANOVA, Tukey and Kruskal-Wallis, and Duns tests respectively. The irradiated specimens had lower BS values (8.23 &plusmn; 4.26) compared to non-irradiated group (11.88 &plusmn; 6.42) (p <0.00001). Regarding the resin cements, the RelyX U200 showed the higher values in BS (15.17 &plusmn; 5.89) compared to RelyX ARC (7.68 &plusmn; 4.22) and Panavia F 2.0 (7 , 32 &plusmn; 2.71) (p <0.0001). In addition, the cervical third presented higher BS values (13.08 &plusmn; 6.10) when compared to the middle (9.72 &plusmn; 5.03) and apical (7.38 &plusmn; 4.53) thirds (p <0.0001). The failure pattern showed cohesive failures in root dentin of the irradiated specimens. In the SEM dentin/cement interface analysis, a greater misadaptation was observed for the teeth submitted to radiotherapy. Regarding the resin cements, a better adaptation was observed for the RelyX U200 and RelyX ARC compared to the Panavia F 2.0. In the SEM qualitative analysis of the irradiated teeth, was possible to observe the presence of fractures and microfractures in the root dentin and a small number of collagen fibers. The resin cements RelyX U200 and Panavia F 2.0 showed a juxtaposed interface of the cement with the root dentin in irradiated and non-irradiated teeth, being that for the RelyX ARC cement the presence of hybrid layer and tags was similar for irradiated and non-irradiated groups. It was concluded that the radiotherapy promoted reduction of the bond strength and increase the gaps in the dentin/resin cement interface and the self-adhesive resin cement is the best alternative for glass fiber posts cementation in irradiated teeth.

Submitted by Renata Lopes (renatasil82@gmail.com) on 2017-01-12T12:51:08Z No. of bitstreams: 1 laragouveaalmeidamartinsatalla.pdf: 1481439 bytes, checksum: 5170ffd61eff8e2caba1d16c0795e644 (MD5) / Approved for entry into archive by Diamantino Mayra (mayra.diamantino@ufjf.edu.br) on 2017-01-31T11:16:46Z (GMT) No. of bitstreams: 1 laragouveaalmeidamartinsatalla.pdf: 1481439 bytes, checksum: 5170ffd61eff8e2caba1d16c0795e644 (MD5) / Made available in DSpace on 2017-01-31T11:16:46Z (GMT). No. of bitstreams: 1 laragouveaalmeidamartinsatalla.pdf: 1481439 bytes, checksum: 5170ffd61eff8e2caba1d16c0795e644 (MD5) Previous issue date: 2009-12-10 / O presente estudo teve como objetivo avaliar a influência do tratamento da dentina radicular com clorexidina a 2% e ácido cítrico a 10% na resistência de união de pinos de fibra de vidro cimentados com cimento resinoso RelyX Ultimate (3M ESPE) associado a um adesivo autocondicionante Single Bond Universal (3M ESPE). Quarenta e cinco dentes humanos unirradiculares foram selecionados e seccionados na junção cemento-esmalte, padronizando-os com 14 mm de comprimento. Após tratamento endodôntico, as raízes foram divididas aleatoriamente em 3 grupos (n=15) de acordo com o tratamento prévio do conduto radicular: G1, nenhum tratamento; G2, aplicação de gel de clorexidina a 2% (Rioquímica®) por 60 segundos; G3, aplicação de ácido cítrico a 10% (Idem per Idem Farmácia de Manipulação Ltda) por 60 segundos. Posteriormente, foi aplicado o adesivo nos condutos e nos pinos de fibra de vidro (White Post, FGM) e estes foram cimentados com cimento resinoso (RelyX Ultimate - 3M ESPE), sendo fotopolimerizados por 40 segundos. As raízes foram seccionadas axialmente em discos de 2 mm e os espécimes foram submetidos ao teste de push-out. As médias dos valores obtidos (MPa) foram analisadas por meio dos testes one-way ANOVA e Tukey (α=0,05) e os tipos de falhas analisadas em estereomicroscópio com aumento de 8,0X. Os resultados mostraram que não houve diferença estatisticamente significativa entres os grupos avaliados, assim como quando comparados os terços radiculares em cada grupo (p>0,05), entretanto resultados significantes foram encontrados entre os grupos G1 e G2 na região cervical (p=0,045). Falhas mista e adesiva entre cimento e dentina foram mais prevalentes. Pôde-se concluir que o uso da clorexidina a 2% no conduto radicular pode interferir na resistência de união de pinos de fibra de vidro e que o ácido cítrico não influenciou nos resultados. / The aim of this study was to investigate the influence of root dentine treatment with 2% chlorhexidine and 10% citric acid on bond strength of fiberglass post cemented with self-etching cement. Forty five human single-rooted teeth were selected and sectioned in the cement-enamel junction, standardizing them with 14 mm length. After endodontic treatment the roots were randomly divided in 3 groups (n=15) according to the previous treatment of the root canal: G1, no treatment; G2, application of 2% chlorhexidine (Rioquímica®) for 60s; G3, application of 10% citric acid (Idem per Idem - Farmácia de Manipulação Ltda) for 60s. Subsequently, the self-etching adhesive Single Bond Universal (3M ESPE) was applied in the canals and on the fiberglass post (White Post, FGM) and these ones were cemented with resin cement (RelyX Ultimate - 3M ESPE), and light polymerized for 40s. The roots were sectioned transversely in slides of 2 mm thickness and the push-out test was performed. Data were analyzed by one-way ANOVA and Tukey test (α=0.05) and the types of failures were analyzed under stereomicroscopy (8.0X). The results show that there was no statistically significant difference between the groups, as well as when comparising bond strength in root thirds in each group (p>0.05), however, significant results were found between groups G1 and G2 in the cervical third (p=0.045). Mixed and adhesive failures between cement and dentine were predominant. It can be concluded that the use of 2% chlorhexidine in the root canal can interfere in the fiberglass posts bond strength.

Made available in DSpace on 2014-07-29T15:03:33Z (GMT). No. of bitstreams: 1 Dissertacao Emmele G Fontenelle.pdf: 3889725 bytes, checksum: 2db009d8581a8358994f13fbf37f6062 (MD5) Previous issue date: 2011-06-27 / Fastenings inserted in concrete are used in order to allow the introduction of these components in concrete structures, enabling the structural link between metal structures and concrete foundation and between prefabricated components and fixing reinforcement elements. This work will study specifically an anchoring system pre-installed (cast-in-place anchor), consisting of single head studs with square head and subjected to tensile force. Assays were performed in 30 headed studs, using self-compacting concrete with compressive strength in the C-30 class. The main variables are the presence and rate of reinforcement, the arrangement of reinforcement in the blocks, and the influence of both the flexural reinforcement (longitudinal and transverse) and the shear reinforcement (hairpins) on the load capacity of the anchorage. The experimental results were compared with five methods of design found in the literature and show that the flexural einforcement has no effect in increasing the load capacity of the anchorage. The use of a shear reinforcement together with the flexural reinforcement can increase the capacity of the anchor up to 64%. Increasing the distance of the hairpins in relation to the head stud reduces the ultimate load achieved by the anchoring system while the increase in diameter and / or in the number of layers of hairpins can increase the ultimate load. / Pinos de ancoragem inseridos em concreto são empregados com a finalidade de permitir a fixação de elementos para a introdução de solicitações nas estruturas de concreto, viabilizando as ligações estruturais entre estruturas metálicas e a fundação de concreto, entre componentes pré-fabricados e na fixação de elementos de reforço. Neste trabalho será abordado e estudado especificamente um sistema de ancoragem pré-instalado, composto por pino de ancoragem único com cabeça quadrada e submetido à força de tração. Foram realizados ensaios em 30 pinos, utilizando-se concreto auto-adensável com resistência à compressão na classe C-30, tendo como principais variáveis a presença e taxa de armadura, e disposição da armadura nos blocos, analisadas tanto na armadura de flexão (longitudinal e transversal) quanto na armadura de cisalhamento (grampos). Os resultados experimentais foram comparados com cinco métodos de cálculo da literatura e mostram que a armadura de flexão não influencia no aumento da capacidade de carga do pino de ancoragem. A utilização de uma armadura de cisalhamento juntamente com a armadura de flexão pode aumentar a capacidade de carga do pino em até 64%. O afastamento dos grampos em relação ao pino diminui a carga última atingida pelo pino de ancoragem, enquanto o aumento do diâmetro e/ou o aumento do número de camadas dos grampos pode aumentar a carga última.

nÃo hà / O objetivo deste trabalho foi avaliar a resistÃncia de uniÃo da interface adesiva de pinos de fibra de vidro e dentina radicular, em trÃs regiÃes do conduto, fixados com trÃs sistemas de cimentaÃÃo. Vinte e quatro dentes humanos hÃgidos, recÃm-extraÃdos por razÃes ortodÃnticas ou periodontais, tiveram suas coroas removidas na junÃÃo cemento-esmalte com um disco diamantado, sob irrigaÃÃo. As raÃzes receberam tratamento endodÃntico e foram obturadas com guta-percha e um cimento endodÃntico contendo eugenol (Endofil). A desobstruÃÃo foi realizada uma semana apÃs o tÃrmino do tratamento endodÃntico em uma profundidade de 9 mm medida da regiÃo cervical da raiz. O pino (Reforpost Fibra de Vidro n 3) foi cimentado no conduto radicular com um dos trÃs sistemas de fixaÃÃo descritos a seguir (n = 8): no grupo 1 foi utilizado o sistema Single Bond 2/ RelyX ARC, no grupo 2 foi utilizado o sistema ED Primer/Panavia 21 e no grupo 3 foi utilizado o cimento RelyX Unicem. Todos os cimentos e sistemas adesivos foram utilizados de acordo com as instruÃÃes dos fabricantes. Posteriormente, as raÃzes foram seccionadas em uma mÃquina de corte, sob irrigaÃÃo, em trÃs porÃÃes, correspondentes aos terÃos cervical, mÃdio e apical da regiÃo do conduto preparada para o pino. Os espÃcimes foram submetidos ao teste de extrusÃo por cisalhamento (âpush-outâ) em uma mÃquina de ensaio universal a uma velocidade de 0,5 mm/min e os valores de resistÃncia de uniÃo mÃxima foram registrados e submetidos à anÃlise estatÃstica (p < 0,05). A anÃlise de variÃncia (ANOVA) mostrou diferenÃa estatÃstica significante entre os terÃos (cervical, mÃdio e apical) somente para o grupo do cimento Panavia 21, no qual o terÃo apical apresentou menor mÃdia de resistÃncia de uniÃo do que os terÃos cervical e mÃdio (teste de Tukey). Quando se comparou a resistÃncia de uniÃo em cada regiÃo da raiz, avaliando-se os materiais de cimentaÃÃo, a anÃlise de variÃncia (ANOVA) mostrou diferenÃa estatÃstica significante para as trÃs regiÃes do conduto. Para os terÃos mÃdio e apical, o cimento Panavia 21 apresentou mÃdia de resistÃncia de uniÃo significativamente menor do que os cimentos Single Bond 2/RelyX ARC e RelyX Unicem, sendo estes estatisticamente iguais entre si. Para o terÃo cervical, o cimento RelyX Unicem apresentou maiores valores de resistÃncia de uniÃo do que o cimento Panavia 21, tendo sido o cimento Single Bond 2/RelyX ARC estatisticamente semelhante aos outros dois materiais / The aim of this study was to assess the bond strength at the adhesive interface of fiber glass posts and root dentin, in three regions of the canal, fixed with three cementation systems. Twenty-four healthy human teeth, recently extracted for orthodontic or periodontal reasons, had their crowns removed at the cement-enamel junction with a diamond disk, under irrigation. The roots were endodontically treated and were filled with gutta percha and an endodontic cement containing eugenol (Endofil). One week after endodontic treatment ended, the obstruction was removed at a mean depth of 9mm in the cervical region of the root. The posts (Reforpost Fibra de Vidro No. 3) were cemented in the canals prepared with one of the three fixation systems described as follows (n = 8): in group 1 the Single Bond 2/ RelyX ARC system was used; in group 2 the ED Primer/Panavia 21 system, and in group 3 RelyX Unicem cement was used. All the cements and adhesive systems were used in accordance with the manufacturersâ instructions. Afterwards, the roots were sectioned in a cutting machine under irrigation, into three portions corresponding to the cervical, middle and apical thirds of the root canal region prepared for the post. The specimens were submitted to the pushout test in a universal test machine at a speed of 0.5 mm/min and the maximum bond strength values were recorded and submitted to statistical analysis (p < 0.05). Analysis of variance (ANOVA) showed statistically significant difference between the cervical, middle and apical thirds only for the Panavia 21 cement group, in which the apical third presented a lower mean bond strength value than the cervical and middle thirds (the TukeyÂs test). When the bond strength in each region of the root was compared to assess the cementing materials, the analysis of variance (ANOVA) showed statistically significant different for the three regions of the canal. For the middle and apical thirds, the Panavia 21 cement presented significantly lower mean bond strength than the Single Bond 2/RelyX ARC and RelyX Unicem cements, these being statistically equal between them. For the cervical third, RelyX Unicem cement presented higher bond strength values than the Panavia 21 cement and the Single Bond 2/RelyX ARC cement was statistically equal to the other two materials

Objetivo: Este estudo se propõe a verificar a influencia do tipo de luz fotopolimerizadora na força de retenção de pinos intra-radiculares, tanto na técnica direta como na direta indireta. Métodos: 40 raízes de dentes bovinos com comprimento de 12 mm foram tratadas endodonticamente e divididas aleatoriamente em 4 grupos de acordo com a técnica de obtenção dos pinos e luz fotopolimerizadora (n=10): grupo 1 (técnica direta associada à lâmpada halogena); grupo 2 (técnica direta ao LED); grupo 3 (técnica direta-indireta associada à lampada halógena); e grupo 4 (técnica direta-indireta associada ao LED). A força de retenção foi determinada através do teste de tração usando Universal Testing Machine (Instron). Todos os dados foram analisados usando one-way analysis of variance (ANOVA) com a significância de p<0.05 e complementadas com teste de Tukey. Após o teste, as interfaces adesivas onde ocorreram as falhas foram examinadas e classificadas. Resultado: Os grupos 3 (246,05N ± 29,51) e 4 (241,60N ± 28,95) não apresentaram força de retenção estatisticamente diferente mas foram maiores que os grupos 1 (142,30N ± 25,60) e 2 (178,56N ± 25,67). A maior parte das fraturas ocorreu na interface dentina/resina. Conclusão: Com base nos resultados obtidos, concluímos que o método direto-indireto proporcionou a melhor retenção dos pinos de fibra de vidro. / Objectives: The purpose of this study is to verify the influence of light curing type on retention force of direct technique and direct-indirect technique. Methods: Fourth bovine single root teeth with 12mm of length were used in this study. The roots were endodontically treated and randomly divided in four groups according to the light curing unit and technique used: group 1(direct technique, halogen lamp), group 2(direct technique, LED), group 3(direct-indirect technique, halogen lamp), group 4(direct-indirect technique, lamp). The retention force was determined sing a Universal Testing Machine (Instron). All data were analyzed using one-way analysis of variance (ANOVA) and Tukey test. After the test, the failure was examined and classified according to the fracture place: post/ resin; resin/dentin; mix. Results: Group 3 (246,05N ± 29,51) and 4(241,60N ± 28,95)4 (95,18N) did not show statistically difference but presented higher retention force than group 1 (142,30N ± 25,60) and 2 (178,56N ± 25,67). Most of fracture occurred in interface between dentin/resin. Conclusion: Based on the obtained results, it was concluded that adhesive cementation technique influenced in the retention of glass fiber post.

Submitted by Marlene Santos (marlene.bc.ufg@gmail.com) on 2016-09-21T13:42:33Z No. of bitstreams: 2 Dissertação - Letícia Nunes de Almeida - 2016.pdf: 4956536 bytes, checksum: ff3b7edcf1cb8b45c40f2292cb032676 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Approved for entry into archive by Luciana Ferreira (lucgeral@gmail.com) on 2016-09-21T13:45:21Z (GMT) No. of bitstreams: 2 Dissertação - Letícia Nunes de Almeida - 2016.pdf: 4956536 bytes, checksum: ff3b7edcf1cb8b45c40f2292cb032676 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Made available in DSpace on 2016-09-21T13:45:21Z (GMT). No. of bitstreams: 2 Dissertação - Letícia Nunes de Almeida - 2016.pdf: 4956536 bytes, checksum: ff3b7edcf1cb8b45c40f2292cb032676 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Previous issue date: 2016-02-25 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / The pre-heating and post-curing can improve the mechanical properties of composites, even though there be no studies of fiber reinforced composites. The aim of this study was to evaluate the effect of pre-heating and post-curing autoclave and microwave in flexural strength (FS), diametral tensile strength (DTS), knoop microhardness (KHN) and degree of conversion (DC) of a experimental fiber- reinfoced composite. The experimental material was prepared with 30% glass fibers (3 mm), 22.5% of the resin matrix (40/60 Bis-GMA / TEGDMA) and 47.5% barium silicate particles. Six experimental groups were created by the interaction between the factors under study: heating, on two levels (without heating and heating at 60°C) and post-curing in 3 levels (conventional curing without post-curing, autoclave (120°C for 15 minutes) and microwaves (540 W for 5 minutes) The groups were: F - curing at 1500 mW/cm2 for 40 seconds; F + M - curing and post- polymerization in microwave; F + A - curing and post-curing in an autoclave , AQ + F - the composite heating prior to curing, AQ + F + M - heating prior to curing and post-curing in microwave;. AQ + F + A - heating prior to curing and post-curing and autoclave heating was conducted digital oven for 5 minutes at 60°C. Ten samples of the RF dimensions 25 x 2 x 2 mm and DTS in dimensions of 3 x 6 mm were tested in a universal testing machine Instron 5965, 0.5 mm/min. the KHN test was performed on samples of 3 x 6 mm with a load of 50 g for 30 sec, totaling 50 indentations per group. GC was obtained by Spectroscopy Fourier Transform Infrared (FTIR) on 5 samples. Data were analyzed by a factorial 2x3 and general linear model ANOVA and Tukey tests (α = 0.05). Factor analysis showed significant interaction between the factors just for RTD (p = 0.0001); preheating was significant factor for RF (p = 0.0001), RTD (p = 0.020) and KHN (p = 0.0001); post-curing factor for KHN was significant (p = 0.0001). ANOVA and Tukey tests showed statistically significant differences between groups for DTS (p = 0.001: AQ + F ≥ AQ + F + M = F + A = AQ + F + A = F + M ≥ F), FS (p = 0.016: AQ + F + M ≥ AQ + F + A + F = AQ = AQ + A + M ≥ F ≥ F) and KHN (p = 0.0001: AQ + F + M ≥ AQ + A + F = F = F + A + M ≥ F ≥ M + AQ). GC results showed no statistically significant difference. Through the Pearson correlation coefficient was observed significant positive correlation between the GC and RTD (r = 0.473, p = 0.008) and between DTS and FS (r = 0.263, p = 0.042). The pre-heating and post- polymerization were shown to be favorable to promote better mechanical properties of fiber reinforced composite by studied, specific for each property being analyzed. / O aquecimento prévio à polimerização e a pós-polimerização podem melhorar propriedades mecânicas em compósitos, embora inexistam estudos em compósitos reforçados com fibra. O objetivo deste estudo foi avaliar o efeito do pré- aquecimento e da pós-polimerização em autoclave e microondas na resistência flexural (RF), resistência à tração diametral (RTD), microdureza knoop (KHN) e grau de conversão (GC) de um compósito experimental reforçado por fibra de vidro. O material experimental foi confeccionado com 30% de fibras de vidro (3 mm), 22,5% de matriz resinosa (40/60 Bis-GMA/TEGDMA) e 47,5% de partículas de silicato de bário. Seis grupos experimentais foram criados pela interação entre os fatores em estudo: aquecimento, em dois níveis (controle sem aquecimento e aquecimento a 60oC) e pós-polimerização, em 3 níveis (fotopolimerização convencional sem pós- polimerização, autoclave (120oC por 15 minutos) e microondas (540 W por 5 minutos). Os grupos foram: F - fotopolimerização à 1500 mW/cm2 por 40 segundos; F+M - fotopolimerização e pós- polimerização em microondas; F+A - fotopolimerizacão e pós-polimerização em autoclave; AQ+F - aquecimento do compósito previamente à fotopolimerização; AQ+F+M - aquecimento previamente à fotopolimerização e pós-polimerização em microondas; AQ+F+A - aquecimento previamente à fotopolimerização e pós-polimerização e autoclave. O aquecimento foi realizado em estufa digital por 5 minutos a 60oC. Dez amostras de RF nas dimensões de 25 x 2 x 2 mm e de RTD nas dimensões de 3 x 6 mm foram testadas em máquina de ensaio universal Instron 5965, a 0,5mm/min. O teste de KHN foi realizado em amostras de 3 x 6 mm com carga de 50 g por 30 s, totalizando 50 indentações por grupo. O GC foi obtido através de Espectroscopia de Infravermelho por Transformada de Fourrier (FTIR) em cinco amostras. Os dados foram analisados por um modelo linear geral fatorial 2x3 e testes de ANOVA e Tukey (α=0,05). A análise fatorial mostrou interação significativa entre os fatores apenas para RTD (p=0,0001); o fator pré-aquecimento foi significante para RF (p=0,0001), RTD (p=0,020) e KHN (p=0,0001); o fator pós-polimerização foi significante para KHN (p=0,0001). Os testes de ANOVA e Tukey mostraram diferença estatística entre os grupos para RTD (p = 0,001: AQ+F ≥ AQ+F+M = F+A = AQ+F+A = F+M ≥ F), RF (p = 0,016: AQ+F+M ≥ AQ+F+A = AQ+F = AQ+A ≥ F+M ≥ F) e KHN (p = 0,0001: AQ+F+M ≥ AQ+F+A = F+A= F+M ≥ AQ+F ≥ F). Os resultados de GC não apresentaram diferença estatisticamente significante. Através do coeficiente de correlação de Pearson foi possível observar correlação positiva significante entre o GC e RTD (r = 0,473, p = 0,008) e entre RTD e RF (r = 0,263, p = 0,042) . O pré- aquecimento e a pós-polimerização mostraram-se favoráveis para promover melhores propriedades mecânicas do compósito reforçado por fibra estudado, sendo específicos para cada propriedade analisada.

Submitted by JÚLIO HEBER SILVA (julioheber@yahoo.com.br) on 2017-05-03T17:14:13Z No. of bitstreams: 3 Tese - Amanda Vessoni Barbosa Kasuya - 2017-1-50.pdf: 15013683 bytes, checksum: f8924a9fa740c813552a7c3316dba183 (MD5) Tese - Amanda Vessoni Barbosa Kasuya - 2017-51-111.pdf: 15359599 bytes, checksum: ea14f282d1609854707110f304682486 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Rejected by Luciana Ferreira (lucgeral@gmail.com), reason: olhe no guia a forma de nomear arquivos divididos on 2017-05-04T11:04:01Z (GMT) / Submitted by JÚLIO HEBER SILVA (julioheber@yahoo.com.br) on 2017-05-04T17:04:01Z No. of bitstreams: 3 Tese - Amanda Vessoni Barbosa Kasuya - 2017- Parte 1.pdf: 15013683 bytes, checksum: f8924a9fa740c813552a7c3316dba183 (MD5) Tese - Amanda Vessoni Barbosa Kasuya - 2017- Parte 2.pdf: 15359599 bytes, checksum: ea14f282d1609854707110f304682486 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Rejected by Luciana Ferreira (lucgeral@gmail.com), reason: No guia está registrado: - Quando o arquivo tiver que ser dividido, por ser grande, cada um deve ser renomeado da mesma forma, adicionando a indicação da parte, entre parênteses, no final. Exemplos: “Tese - João Alves da Silva - 2015 (1)”, “Tese - João Alves da Silva - 2015 (2)”. on 2017-05-05T12:44:32Z (GMT) / Submitted by JÚLIO HEBER SILVA (julioheber@yahoo.com.br) on 2017-05-05T16:53:52Z No. of bitstreams: 3 Tese - Amanda Vessoni Barbosa Kasuya - 2017- Parte 1.pdf: 15013683 bytes, checksum: f8924a9fa740c813552a7c3316dba183 (MD5) Tese - Amanda Vessoni Barbosa Kasuya - 2017- Parte 2.pdf: 15359599 bytes, checksum: ea14f282d1609854707110f304682486 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Rejected by Erika Demachki (erikademachki@gmail.com), reason: on 2017-05-05T17:13:14Z (GMT) / Submitted by JÚLIO HEBER SILVA (julioheber@yahoo.com.br) on 2017-05-05T17:15:42Z No. of bitstreams: 3 Tese - Amanda Vessoni Barbosa Kasuya - 2017 (1).pdf: 15013683 bytes, checksum: f8924a9fa740c813552a7c3316dba183 (MD5) Tese - Amanda Vessoni Barbosa Kasuya - 2017 (2).pdf: 15359599 bytes, checksum: ea14f282d1609854707110f304682486 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Approved for entry into archive by Luciana Ferreira (lucgeral@gmail.com) on 2017-05-08T15:51:39Z (GMT) No. of bitstreams: 3 Tese - Amanda Vessoni Barbosa Kasuya - 2017 (1).pdf: 15013683 bytes, checksum: f8924a9fa740c813552a7c3316dba183 (MD5) Tese - Amanda Vessoni Barbosa Kasuya - 2017 (2).pdf: 15359599 bytes, checksum: ea14f282d1609854707110f304682486 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Made available in DSpace on 2017-05-08T15:51:39Z (GMT). No. of bitstreams: 3 Tese - Amanda Vessoni Barbosa Kasuya - 2017 (1).pdf: 15013683 bytes, checksum: f8924a9fa740c813552a7c3316dba183 (MD5) Tese - Amanda Vessoni Barbosa Kasuya - 2017 (2).pdf: 15359599 bytes, checksum: ea14f282d1609854707110f304682486 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Previous issue date: 2017-03-02 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / The objectives of this work were to evaluate the stress distribution (SD), fracture resistance (RF), adhesive strength (AS) and their respective fracture patterns of weekeaned bovine roots, rehabilitated with customized pins with different resinous materials. In addition, the objective of this study was to evaluate the polymerization depth of the resinous materials by Knoop microhardness method (MH). Eight experimental groups were established (n = 10 for FR and AS; n = 5 for MH), with the factor under study: 1. The post type (industrialized glass fiber post relined (I) and personalized post (P), 2. the relining material only for industrialized glass fiber post (experimental composite (e) and composite resin (R)); 3. the material used only for personalized post (experimental composite (e) and bulk fill resin (b), and 4. the amount of remaining dentin (root embrittlement inner wear, in lengths of 5 mm or 10 mm). One hundred and forty bovine roots of similar size were selected and restored according to the group to which they belonged. For FR, Pperiodontal and alveolar bone were simulated and the specimens were placed in an Instron 5965 machine at a 135 ° angle to the long axis and loaded at a constant velocity of 0.5 mm/min in compression until the fracture. The fracture pattern was classified as: F1- crown; F2- root; F3- crown/root; F4- fracture with displacement of the crown/post. For AS, the specimens were sectioned in slices of 1 mm perpendicular to their long axis. Each specimen was placed in a test machine to received the load in the apical-coronal direction, at a constant velocity of 0.5mm / min, pushing the pin through the largest side of the sample until fracture. The fracture pattern was classified as: F1- cohesive of the pin and/or reline material; F2- cohesive of dentin; F3- adhesive of pin/reline material; F4 - Adhesive bonding cement/ eline material and F5 - mixed. For MH, the specimens were sectioned parallel to their long axis. The tests were performed with a Knoop penetrator under a static charge of 50 grams per 10 seconds. MH was calculated as the average value for each third. Finally, the finite element method was used to analyze the DT. 3D virtual models representative of each experimental group were created and analyzed under von Mises equivalent stresses criterion, simulating loading of 100N at a 45o angle with the long axis. The experimental composite proved to be an alternative for the rehabilitation of weakened roots when used to create personalized posts or when used as a relining material, with FR values similar to the traditional technique, but with more favorable stress distributions. Moreover, it presented excellent adhesive strength to the dentin structure, being comparable to conventional composite resin and bulk fill resin. The bulk fill resin resulted in low values of fracture resistance associated with the fracture and displacement of post/crown. Lower microhardness values were observed in the apical third for bulk fill resin. / Os objetivos deste trabalho foram avaliar a distribuição de tensões (DT), resistência à fratura (RF), resistência adesiva (RA) e seus respectivos padrões de fratura de raízes bovinas fragilizadas, reabilitadas com pinos personalizados com diferentes materiais resinosos. Além disso, objetivou-se avaliar a profundidade de polimerização dos materiais resinosos por meio do método de microdureza Knoop (MD). Oito grupos experimentais foram criados (n=10 para RF e RA; n=5 para MD), tendo como fator em estudo: 1. o tipo de pino utilizado (pino de fibra de vidro industrializado reembasado (I) e pino personalizado (P)); 2. o material de reembasamento apenas para os pinos industrializados (compósito experimental (e) e resina composta (r)); 3. o material utilizado para confecção apenas dos pinos personalizados (compósito experimental (e) e resina bulk fill (b)); e 4. a quantidade de dentina remanescente (fragilização radicular por desgaste interno nos comprimentos de 5 mm ou 10 mm). Cento e quarenta raízes bovinas com dimensões semelhantes foram selecionadas e restauradas de acordo com o grupo ao qual pertenciam. Para RF, ligamento periodontal e osso alveolar foram simulados e os espécimes posicionados em máquina Instron 5965, em um ângulo de 135° em relação ao longo eixo do dente de modo que recebessem carregamento à velocidade constante de 0,5mm/min em compressão até a fratura. Em seguida, o padrão de fratura foi classificado em: F1- coroa; F2- raiz; F3- coroa/raiz; F4- fratura com deslocamento do conjunto coroa/pino. Para RA, os espécimes foram seccionados em fatias 1 mm perpendicularmente ao seu longo eixo. Cada espécime foi posicionado em máquina de ensaio de modo que recebessem a carga no sentido apical-coronal, à velocidade constante de 0,5mm/min, empurrando o pino através do maior lado da amostra até a fratura. O padrão de fratura foi classificado em: F1 - coesiva do pino e/ou material de reembasamento; F2 - coesiva da dentina; F3 - adesiva pino/material de reembasmento; F4 - adesiva material de reembasamento/cimento e F5 – mista. Para MD, os espécimes foram seccionados paralelamente ao seu longo eixo. Os testes foram realizados com um penetrador Knoop sob uma carga estática de 50 gramas por 10 segundos. MD foi calculada como o valor médio para cada terço. E por fim, o método de elementos finitos foi empregado para analisar a DT. Modelos virtuais 3D representativos de cada grupo experimental foram criados e analisados sob critério de tensões equivalentes de von Mises, simulando carregamento de 100N em um ângulo de 45o com o longo eixo. O compósito experimental demostrou ser uma alternativa para a reabilitação de raízes fragilizadas quando utilizado para criar pinos personalizados ou quando utilizado como material de reembasamento de pinos, com valores de resistência à fratura semelhantes à técnica tradicional porém, com distribuição de tensões mais favoráveis. Além disso, apresentou excelente resistência adesiva à estrutura dentinária, sendo comparável à resina composta convencional e à resina bulk fill. Já a resina bulk fill resultou em baixos valores de resistência à fratura associado ao deslocamento do conjunto pino/coroa protética. Valores de microdureza inferiores foram observados no terço apical para a bulk fill.