O objetivo desse estudo foi comparar o desempenho de ligaduras ortodônticas estéticas de 4 marcas comerciais, após 30 dias na cavidade bucal, com o uso de dentifrício clareador e convencional para avaliar: alteração de cor por meio da espectrofotometria; a ultraestrutura da superfície por meio da Microscopia Eletrônica de Varredura (MEV); propriedade elástica por meio do teste de tração. Foram avaliadas as ligaduras seguintes marcas comerciais: American Orthodontics, 3M Unitek, Orthotechnology e Morelli Ortodontia. Foram selecionados, após o cálculo amostral, 20 pacientes que atenderam aos critérios de inclusão. Os pacientes receberam, de forma aleatória, com o auxílio do acessório Shooter (TP Orthodontics, La Porte, IN, EUA) ligaduras nos elementos 13, 23, 33 e 43; 32, 31, 41 e 42. No mesmo dia receberam dentifrício clareador Colgate Luminous White (Colgate-Palmolive Indústria e Comércio, São Bernardo do Campo, SP, Brasil) que foi usado por 30 dias (grupo experimental). Após esse período as ligaduras foram removidas, armazenadas (em saliva artificial) e, imediatamente submetidas aos testes. Os pacientes receberam, então, dentifrício convencional Colgate Máxima Proteção Anti-cáries (Colgate-Palmolive Indústria e Comércio, São Bernardo do Campo, SP, Brasil) (grupo controle). Após 30 dias, foram removidas, armazenadas e submetidas aos ensaios. As ligaduras inseridas nos bráquetes dos caninos foram avaliadas para alteração de cor pelo espectrofotômetro (Vita Easyshade Zahnfabrik, Bad Säckingen, Alemanha). Em seguida, as ligaduras, de cada marca, que apresentaram maior e menor variação de cor com o dentifrício clareador e convencional, bem como ligaduras novas, foram submetidas à avaliação qualitativa com a visualização pelo Microscópio Eletrônico de Varredura (EVO 50, Carl Zeiss, Cambridge, Inglaterra). As ligaduras que estavam inseridas nos bráquetes incisivos inferiores foram submetidas ao teste de tração pela Máquina de Ensaio Mecânico Universal (EMIC DL 2000, São José dos Pinhais, PR, Brasil). Os achados foram submetidos à análise estatística ANOVA e ao teste complementar de Duncan em um nível de significância de 5%. Os resultados mostraram que o dentifrício clareador não conseguiu efetivamente manter a estabilidade de cor das ligaduras ortodônticas estéticas. O valor final para o ΔE (variação total de cor) para todas as marcas foi > 3,3 o que indica uma alteração clinicamente perceptível pelo olho humano e que sinaliza a reposição do material por razões estéticas. Em relação à MEV as imagens obtidas foram heterogêneas e não permitiram caracterizar um padrão para um ou outro dentifrício. No que se refere ao teste de tração, houve melhor desempenho para as marcas 3M Unitek e American Orthodontics. O tipo de dentifrício, clareador ou convencional, não alterou a propriedade elástica entre as marcas estudadas. Pode-se concluir, pela presente pesquisa, que o dentifrício clareador não foi capaz de alterar a estabilidade de cor nas 4 marcas avaliadas por um período de 30 dias. A avaliação qualitativa pela MEV não permitiu concluir se a abrasividade do dentifrício clareador trouxe danos ou injurias à superfície das ligaduras. Apesar disso, o seu uso não alterou a propriedade elástica das mesmas. / The objective of this study was to compare the performance of aesthetic orthodontic ligatures/modules of 4 commercial brands, after 30 days in the oral cavity, with the use of conventional and whitening dentifrice to evaluate: color change by spectrophotometry; the ultrastructure of the surface by Scanning Electron Microscopy (SEM); elastic property by the tensile test. The following brands were evaluated: American Orthodontics, 3M Unitek, Orthotechnology and Morelli Orthodontics. Twenty patients who were included in the inclusion criteria were selected after sample calculation. Patients received, at random, with the aid of the Shooter accessory (TP Orthodontics, La Porte, IN, USA) ligatures on elements 13, 23, 33, 43, 32, 31, 41 e 42 and whitening dentifrice Colgate Luminous White (Colgate-Palmolive Indústria e Comércio, São Bernardo do Campo, SP, Brazil), which was used for 30 days (test group). After this period, the ligatures were removed, stored (in artificial saliva) and immediately submitted to the tests. Patients were then given conventional toothpaste Colgate Maximum Anti-caries Protection (Colgate-Palmolive Indústria e Comércio, São Bernardo do Campo, SP, Brazil). This was the control group. Once again, after 30 days, the modules were removed, stored and submitted to assays. Ligatures inserted into the canine brackets were evaluated by the spectrophotometer (Vita Easyshade Zahnfabrik, Bad Säckingen, Germany) to evaluate the color change. After this step, the ligatures of each brand, which presented greater and lesser color variation, both with the whitening dentifrice as well as the conventional one, and new ligatures, were selected for qualitative evaluation with the visualization by the Scanning Electron Microscope (EVO 50, Carl Zeiss, Cambridge, England). The ligatures that were inserted in the lower incisor brackets were subjected to the tensile test by the Universal Mechanical Testing Machine (EMIC DL 2000, São José dos Pinhais, PR, Brazil). The findings were submitted to ANOVA statistical analysis and Duncan\'s complementary test at a significance level of 5%. The results showed that the whitening dentifrice failed to effectively improve the color stability of aesthetic orthodontic ligatures. The final value for ΔE (total color change) for all brands was > 3.3 which indicates a change clinically perceptible by the human eye and signaling the replacement of the material for aesthetic reasons. In relation to the SEM the images obtained were heterogeneous and did not allow to characterize a standard for one or the other dentifrice. Regarding the tensile test, there was better performance for the brands 3M Unitek and American Orthodontics. The type of dentifrice, whitening or conventional did not alter the elastic property between the brands studied. It can be concluded from the present research that the whitening dentifrice was not able to change the color stability in the 4 brands evaluated for a period of 30 days. The qualitative evaluation by SEM did not allow the conclusion that the abrasiveness of the whitening dentifrice caused damage to the surface of the ligatures. Despite this, their use did not alter their elastic property.

Orientador: Leonor de Castro Monteiro Loffredo / Banca: Celso Luiz de Angelis Porto / Banca: Camila Pinelli / Banca: Rubens Corte Real de Carvalho / Banca: Adair Luis Stefanello Busato / Resumo: Os objetivos deste trabalho foram avaliar a influência de diferentes tempos de condicionamento ácido na resistência de união cerâmica-agente cimentante, por meio do teste de Micro-Tração, bem como análise dos modos de fratura. Foram confeccionados 5 pares de discos de cerâmica de infra-estrutura IPS Empress 2 e divididos aleatoriamente em 5 grupos. As superfícies de união foram regularizadas através de desgaste com lixas abrasivas de granulação seqüencial sob refrigeração. Os espécimes foram nomeados ao acaso e submetidos aos seguintes tratamentos antes da cimentação: G1: sem condicionamento ácido; G2: 20 s de condicionamento com ácido fluorídrico a 10%; G3: 40 s e condicionamento com ácido fluorídrico a 10%; G4: 60 s de condicionamento com ácido fluorídrico a 10% e G5: 2 min de condicionamento com ácido fluorídrico a 10%. Os espécimes, aos pares, foram cimentados com um sistema adesivo e cimento resinoso dual, de acordo com as recomendações do fabricante. Espécimes foram fotopolimerizados, armazenados por 48 h a 37°C e, posteriormente, com auxílio de um disco de diamante perpendicular à superfície de união, "palitos" com 1 mmø de área de seção foram obtidos. Os valores de resistência de união (MPa) foram obtidos com auxílio de uma máquina de teste universal (MTS 800) e submetidos à análise de variância e teste de Tukey. As médias de resistência foram de 30,20 MPa, 36,19 MPa, 38,72 MPa, 41,43 MPa e 42,53 MPa, respectivamente aos grupos G1, G2 G3 G4 e G5. O grupo G1 apresentou menor resistência média de união do que os demais grupos. O grupo G3 teve comportamento semelhante a G2 e a G4, porém estes dois últimos foram diferentes entre si. Os grupos G4 e G5 promoveram resistências médias semelhantes. Concluímos que o aumento do tempo de condicionamento ácido aumentou os valores de resistência de... (Resumo completo, clicar acesso eletrônico abaixo). / Abstract: The purpose of this study was to investigate the effect of different times of acid conditioning on the microtensile bond strength between union-cement and ceramic, and to verify the mode of failure. Five pairs of ceramic disks (IPS Empress 2) were divided, in five groups, by randomized allocation. The bonding surfaces were finished with 600-grit silicon carbide paper. The specimens were nominated at random and submitted to the following treatments before cementation: G1 : without acid etching; G2 : 20 s of etching with 10% hydrofluoric acid; G3 : 40 s of etching with 10% hydrofluoric acid; G4 : 60 s of etching with 10% hydrofluoric acid and G5 : 2 min of etching with 10% hydrofluoric acid. All the pairs were bonded with dual cure resin bonding and dual cure resin cement, according to manufacturer's instructions. The specimens were light-cured and then stored for 48 h at 37°C. Using a diamond disk perpendicular to the bonding interface, 'sticks' with 1.0 mmø cross-sectional area were obtained. Microtensile bond strengths were determined using a MTS 800 Materials Testing Machine at a crosshead speed of 0.5 mm/min. It was applied analysis of variance and Tukey test at p<0.05. The means of microtensile bond strength, in MPa, were 30.20, 36.19, 38.72, 41.43 and 42.53, respectively to the groups G1, G2, G3, G4 and G5. Group G1 had the smallest microtensile bond strength and G3 had similar results when compared to G2 and G4, although G2 and G4 were different between themselves. The groups G4 and G5 showed similar means of microtensile bond strength. Conclusions: The higher the time of acid conditioning higher were the values of microtensile bond strength, and the analysis of mode of failure exhibited prevalence of adhesive failure type. / Doutor

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / O presente estudo teve como objetivo avaliar a influência da variação da intensidade de luz, para uma mesma exposição radiante, na resistência à flexão, na microdureza e na resistência à tração diametral de uma resina convencional e de uma resina de baixa contração. Para a confecção dos corpos de prova foram utilizadas as resinas Filtek Z250 (3M ESPE) e Filtek P90 LS (3M ESPE) fotoativadas por meio dos seguintes protocolos: Convencional (400mW/cm por 60 s), Média intensidade (700mW/cm por 34 s) e Alta intensidade (950mW/cm por 26 s). Todos os corpos de prova receberam a mesma exposição radiante de 24J/cm. A resistência à flexão foi avaliada por meio do ensaio de flexão três pontos. Para este ensaio foram confeccionados trinta corpos de prova de cada material (n=10) com dimensões de 10mm x 2mm x 1mm. A avaliação da microdureza Knoop foi obtida a partir de seis discos de cada resina com 5mm de diâmetro por 2mm de espessura (n=2), sendo realizadas cinco indentações em cada espécime. Trinta corpos de prova cílindricos de cada compósito (n=10) com 3mm de diâmetro por 6mm de altura foram confeccionados para a realização do teste de tração diametral. A análise estatística dos resultados obtidos foi realizada por meio do teste de análise de variância (ANOVA) e do teste de múltiplas comparações de Tukey (p < 0.05). A resistência à flexão da resina P90 não foi influenciada de forma significativa pelas diferentes formas de ativação, enquanto a Z250 obteve resultados significantemente maiores para o protocolo de alta intensidade em relação ao convencional. Em todas as intensidades de luz, os resultados da Z250 foram significativamente maiores que os da P90. A microdureza da resina P90 foi estatisticamente maior para o grupo de média intensidade em relação aos outros, já a Z250 não obteve resultados com diferença estatística em relação às formas de ativação. Para a mesma irradiância, a Z250 obteve maiores valores de microdureza do que a P90, com exceção para o protocolo de média intensidade em que não houve diferença estatística entre os materiais. Os valores de resistência à tração não foram influenciados de forma significativa nem pelas diferentes intensidades de luz, nem pelos materiais utilizados. A influência da variação da intensidade de luz depende do tipo de compósito utilizado e da propriedade mecânica avaliada. / This study has the purpose of evaluating the variation of the intensity of light, for a constant radiation exposure, for flexural strength, for microhardness, and for tensile strength, of a conventional composite and a low shrinkage composite. The test samples were made of Filtek Z250 (3M ESPE) e Filtek P90 LS (3M ESPE) light-activated composites. The following light activating protocol was used: conventional (400mW/cm for 60 s); medium intensity (700mW/cm for 34 s), and high intensity (950mW/cm for 26 s). All of the test samples received the same radiation exposure of 24J/cm. The flexural strength was measured through the three-point bending test. For this test, thirty especimens were made for each material (n=10), measuring 10mm x 2mm x 1mm. The Knoop hardness evaluation was carried out using six discs of each composite measuring 5mm in diameter, and 2mm in height (n=2), with five indentations in each specimen. Thirty cylindrical test samples of each composite (n=10) measuring 3mm in diameter, and 6mm in height were obtained for the diametral tensile test. The statistical analysis of the results was carried out through analysis of variance test (ANOVA) and through Tukeys multiple comparisons test (p < 0.05). The P90 composite flexural strength was not significantly influenced by the different activating methods, while Z250 achieved significantly higher values for the high intensity protocol when compared to the conventional one. For all light intensities, the Z250 results were higher than those for P90. P90's microhardness was statistically higher for the medium intensity group when compared to the others, whereas Z250's results had no statistical difference for the different activating protocols. For the same irradiation, Z250 presented higher values for microhardness than P90, except for the medium intensity protocol, which had no statistical difference between the different materials. The tensile strength values were not significantly influenced neither by the different light intensities, nor by the materials. The influence of the variation of light intensity depends upon the type of composite, as well as the mechanical property to be evaluated.

Submitted by LETÍCIA CARVALHO COUTINHO COSTA PEROTE (leticiaccc@gmail.com) on 2016-04-08T17:53:49Z No. of bitstreams: 1 Tese biblioteca finalizada.pdf: 4785988 bytes, checksum: 99777155681f63934c41a2cacd0892f3 (MD5) / Approved for entry into archive by Ana Paula Grisoto (grisotoana@reitoria.unesp.br) on 2016-04-11T17:17:19Z (GMT) No. of bitstreams: 1 perote_lccc_dr_sjc.pdf: 4785988 bytes, checksum: 99777155681f63934c41a2cacd0892f3 (MD5) / Made available in DSpace on 2016-04-11T17:17:20Z (GMT). No. of bitstreams: 1 perote_lccc_dr_sjc.pdf: 4785988 bytes, checksum: 99777155681f63934c41a2cacd0892f3 (MD5) Previous issue date: 2016-02-17 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O objetivo deste estudo foi avaliar a influência de soluções de clorexidina e de própolis e da simulação de pressão pulpar na resistência de união entre resina e dentina. Para isto, foram obtidos segmentos coronários de 120 dentes humanos. Metade das amostras foram conectadas a um dispositivo de simulação de pressão pulpar, cuja altura foi ajustada para 15 cm de água. Foi realizado condicionamento com ácido fosfórico 37% por 15 s, lavagem e secagem com papel absorvente. Em seguida, foram divididas em 3 grupos, de acordo com a solução aplicada por 30 s: GC(Grupo Controle – nenhuma solução), CLX (Digluconato de Clorexidina 0,2%), PA (Extrato de própolis aquoso). Aplicou-se o adesivo (Single Bond Universal) e resina composta (Filtek Z250) em todos as amostras. Os grupos foram subdivididos de acordo com o tipo de envelhecimento: I (Corte Imediato), C (15000 ciclos térmicos). As amostras foram cortadas em palitos e submetidas ao teste de microtração. Os dados obtidos de resistência de união (MPa) foram submetidos ao teste de ANOVA 3 fatores. Para o fator Solução, não foi encontrada diferença estatisticamente significante entre os grupos (p=0,46), mas sim para os fatores Pressão Pulpar (p=0,00) e Envelhecimento (p=0,00), além das interações entre os fatores Solução e Pressão Pulpar (p= 0,00), Pressão Pulpar e Envelhecimento (p=0,00) e entre os três fatores (p=0,03). Os resultados do teste de Tukey para o fator Pressão Pulpar foram: CPP (com pressão pulpar): 29,19a, SPP (sem pressão pulpar): 32,98b; e para o fator Envelhecimento foram: C (ciclados): 28,12a, I (imediato): 34,05b. Concluiu-se que as soluções de clorexidina e de própolis não interferiram na resistência de união; e que a simulação de pressão pulpar e a termociclagem diminuíram os valores de resistência de união da resina à dentina. / This study aimed to assess the influence of chlorhexidine and propolis solutions and simulated pulpal pressure on the bond strength between resin and dentin. To do so, crown segments of 120 human teeth were obtained. Half of the samples were connected to a pulp pressure simulation device, adjusted to 15 cm H2O. Conditioning was accomplished with 37% phosphoric acid for 15 seconds, washing and drying with absorbing paper. Then, samples were split into 3 groups, according to the solution applied for 30 s: GC (Control group – no solution), CLX (Chlorhexidine digluconate 0.2%), PA (Aqueous propolis extract). Single Bond Universal adhesive and composite resin (Filtek Z250) were applied in all samples. Groups were subdivided according to the aging process: I (Immediate cut) and T (15000 thermal cycles). Samples were cut into beams and went through microtensile bonding tests. Bond strength data (MPa) were analyzed by three-way ANOVA. For the factor Solution, there was no statistically significant difference among the groups (p = 0.46), but was found difference for the factors Pulpal Pressure (p=0.00), Aging (p=0.00), and interaction between Solution and Pulpal Pressure (p=0.00), Pulpal Pressure and Aging (p=0.00) and between the 3 factors (p=0.03). The results from Tukey’s test for Pulpal Pressure factor were: SPP (simulated pulpal pressure): 29,19a, NPP (no pulpal pressure): 32,98b; and for the factor Aging were: T (thermal cycling): 28,12a, I (immediate): 34,05b. It was concluded that chlorhexidine and propolis solutions have not interfered in the bond strength; but simulated pulpal pressure and termal cycling reduced the dentin bond strength.

Made available in DSpace on 2014-06-11T19:31:26Z (GMT). No. of bitstreams: 0 Previous issue date: 2003-03-25Bitstream added on 2014-06-13T19:01:42Z : No. of bitstreams: 1 ahid_fjm_dr_arafo.pdf: 2008823 bytes, checksum: b18425083f7a068d5e614b10728f967b (MD5) / Avaliou-se a influência do tipo de tratamento da superfície de materiais estéticos no processo de adesão do reparo com resina composta, por meio do teste de cisalhamento. Foram preparados 360 corpos-de-prova, sendo 120 em cerâmica, 120 em resina composta e 120 em cerômero os quais receberam 06 tipos de tratamentos de superfície a saber, ponta diamantada (GT1C), ponta diamantada e silano (GT1S), jato abrasivo (GT2C), jato abrasivo e silano (GT2S), ácido hidrofluorídrico (GT3C) e ácido hidrofluorídrico e silano (GT3S). O adesivo do Sistema Scotchbond Multipurpose Plus, silano e resina composta Z100 foram aplicados sobre a superfície e os corpos-de-prova armazenados à temperatura de 37oC, por 24 horas, ciclados e novamente armazenados, para em seguida serem cisalhados. A análise estatística dos resultados mostrou que não houve diferença estatística na resistência adesiva dos reparos em resina composta e cerômero, porém, para o material cerâmico, o silano foi eficiente para aumentar a resistência para os tratamentos mecânicos T1 e T2, entretanto, o T3, com ou sem silano, apresentou resistência maior. Os tipos de fraturas foram 100% coesiva do substrato (CS). A microscopia mostrou superfícies com características diferentes para cada material e tratamento superficial. Concluindo os valores de resistência adesiva para a cerâmica sofreram influência do tipo de tratamento e que estes não influenciaram os materiais resinosos. / The influence of the types of the surface treatment in esthetic materials in adhesive process, was evaluaed through shear strength test. The samples were constructed and polished, that received the treatment with diamond bursh (GT1C), and silane application (GT1S), jet of abrasive air (GT2C), and silane application (GT2S), hydrofluoric acid gel (GT3C) and silane application (GT3S). The adhesive of Scotchbond Multiporpose Plus System, the silane and Z100 composite resin were applied on this surface and the whole resin/substract was stored to the temperature of 37o.C, for 24 hours. They were thermocicled, stored again and tested in tension. The static analyses of results showed there is not difference in adhesive resistence of repair between composite resin and ceromero, however in ceramic, the silane increased the resistance in T1 and T2. The T3 group silanated and non silanated was observed increase of resistance. The types of fractures that occurred were 100% cohesive. Scanning electronic microscopy analysis revealed different surfaces in differentes estetic materials and diferents types de surface treatments. The present study showed that adhesive resistence of ceramic repair were affected for the type of surface treatment. However the type of surface tratment didn't affected the adhesive resistence of other materials.

Made available in DSpace on 2014-06-11T19:31:27Z (GMT). No. of bitstreams: 0 Previous issue date: 2002-10-08Bitstream added on 2014-06-13T19:01:43Z : No. of bitstreams: 1 susin_ah_dr_arafo.pdf: 3155550 bytes, checksum: 3c18f1511d8950d04d4fb3ead12080d0 (MD5) / O objetivo deste trabalho foi realizar, in vitro, avaliação da resistência de união à tração (RUT) e espessura de camada híbrida (ECH), em diferentes condições de substrato dentinário (úmido, S1; desidratado, S2 e reumedecido, S3), proporcionado pelos sistemas adesivos de 4ª geração, Scotchbond Multi Uso (SBMU) - 3M ESPE; Single Bond (SB) - 3M ESPE; Prime & Bond 2.1 (P&B2.1) - Dentsply e One Coat Bond (OCB) - Coltène-Whaledent, e os sistemas adesivos de 5ª geração (autocondicionantes), Clearfil SE Bond (CSEB) - Kuraray e One Up Bond F (OUBF) - Tokuyama. Foram utilizados 180 dentes seccionados na altura do 1/3 médio da coroa, originando duas partes cada um: remanescente dental (utilizado no teste de resistência de união à tração) e fragmento oclusal (utilizado na mensuração de camada híbrida). Para cada um dos 18 grupos foram realizadas 10 repetições em cada um dos dois testes, perfazendo um total de 360 amostras. O teste de RUT, foi realizado na Máquina de Ensaios Mecânicos MTS-810, em velocidade de 2 mm / min., e a ECH, foi mensurada à partir de fotografias obtidas em microscopia eletrônica de varredura (Microscópio Eletrônico JSM 330 A), com o software Image Tool 2.00. No teste de RUT, o desempenho dos sistemas adesivos foi melhor em S1 e, dentre eles, o CSEB foi o que apresentou a maior média, 23,01 MPa, enquanto que a menor, foi apresentada pelo OUBF, 15,69 MPa. Os sistemas adesivos de 4ª geração apresentaram médias intermediárias, às quais não foi possível encontrar diferenças estatisticamente significantes. (SBMU, 18,71 MPa; SB, 19,43 MPa; P&B2.1, 17,45 MPa e OCB, 19,92 MPa). As menores médias de RUT dos sistemas adesivos de 4ª geração, foram constatadas em S2, apresentando a menor média para o SB, 6,64 MPa, enquanto que os sistemas autocondicionantes, apresentaram menores variações de RUT entre os... . / The aim of this work was to perform the evaluation of the tensile bond strength (TBS) and the thickness of the hybrid layer (THL), in different conditions of dentinal substrate (moist, S1; dehydrated, S2 and remoistened, S3), provided by the fourth generation adhesive systems, Scotchbond Multi Uso (SBMU) - 3M ESPE; Single Bond (SB) - 3M ESPE; Prime & Bond 2.1 (P&B2.1) - Dentsply and One Coat Bond (OCB) - Coltène-Whaledent, and the fifth generation adhesive systems (self-etching), Clearfil SE Bond (CSEB) - Kuraray and One Up Bond F - Tokuyama. One hundred and eighty teeth bisected in the 1/3 crown mean level were used, originating two parts each: dental remnant (used in the tensile bond strength testing) and occlusal fragment (used in the hybrid layer measurement). For each of the 18 groups, 10 repetitions were performed for both tests, in a total of 360 samples. The TBS test was performed in a Mechanic Testing Machine MTS-810, in speed 2 mm/ min, and the THL was measured from photographs obtained in scanning electron microscopy (Electron Microscope JSM 330 A), using a software Image Tool 2.00. During the TBS test, the performance of the adhesive systems was better in S1 and, among themselves, CSEB presented the higher average, 23,01 MPa, while the lower average was presented by OUBF, 15,69 MPa. The fourth generation adhesive systems presented intermediate averages, those which did not revealed statistically significant differences. (SBMU, 18,71 MPa; SB, 19,43 MPa; P&B2,1, 17,45 MPa and OCB, 19,92 MPa). The lower averages of the fourth generation adhesive systems in TBS were verified in S2, presenting the lower average for SB, 6,64 MPa, while the self-etching systems presented lower TBS variations among the different substrates. In the THL results, lower variability was verified among the average results obtained, being the higher average presented by SBMU, 4,80 æm... (Complete abstract, click electronic address below).

Made available in DSpace on 2014-06-11T19:35:01Z (GMT). No. of bitstreams: 0 Previous issue date: 2005-02-21Bitstream added on 2014-06-13T19:05:06Z : No. of bitstreams: 1 batista_aud_dr_arafo.pdf: 615250 bytes, checksum: 0ecd726c988be8090372e448348080fd (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O objetivo deste estudo foi analisar a influência da incorporação de três desinfetantes (hipoclorito de sódio a 1%, glutaraldeído alcalino a 2% e digluconato de clorexidina a 2%) em duas diferentes porcentagens de substituição da água da espatulação (50 e 100%) de dois gessos tipo IV, FujiRock EP (M1) e Rock Plus (M2), avaliando-se a resistência à compressão e à tração diametral. Os corpos-de-prova foram obtidos a partir de matrizes metálicas bipartidas com 20 mm de diâmetro e 40 mm de altura (resistência à compressão) e 20 mm de diâmetro e 10 mm de altura (resistência à tração diametral). As matrizes foram fixadas sobre uma placa de vidro, o gesso foi manipulado na proporção água/pó recomendada pelos fabricantes (M1:20ml/100g e M2:19 ml/100g), em um espatulador mecânico por 30 segundos, e vazado sob vibração. Para cada ensaio foram confeccionados sete grupos para cada gesso (n=10). Os grupos foram: CONTROLE (Água destilada), G50 (substituição de 50% da água de espatulação por glutaraldeído), G100 (100% de glutaraldeído), C50 (substituição de 50% da água por clorexidina), C100 (100% de clorexidina), H50 (substituição de 50% da água por hipoclorito) e H100 (100% de hipoclorito). Após a presa os corpos-de-prova foram removidos das matrizes e armazenados à temperatura ambiente. Os ensaio de compressão e tração diametral foram realizados 24 horas após o vazamento, em uma máquina de ensaios MTS-810, com célula de carga de 100 KN à velocidade de 0,5mm/min. Os valores médios de resistência à compressão e à tração diametral (MPa) foram submetidos à análise de variância e teste de Tukey, com nível de significância de 95%, permitindo concluir que: (a) a incorporação das substâncias desinfetantes estudadas afetou a resistência à compressão de ambos os gessos analisados; (b) as diferentes proporções de incorporação das substâncias... / The purpose of this study was to evaluate the compressive and diametral tensile strength of two Type IV dental stones, FujiRock EP (M1) e Rock Plus (M2), mixed with three disinfectant solutions (sodium hypochlorite 1%, chlorhexidine digluconate 2% and glutaraldehyde 2%) in two different proportions of gauging water (50% and 100%). Compressive samples consisted of cylindrical specimens, each having a diameter of 20 mm and length of 40 mm, and diametral tensile specimens consisted of discshaped specimens, having a diameter of 20 mm and length of 10 mm, obtained from split metal molds. The stone was mixed with the solutions previously outlined at the water-powder ratio recommended by the manufacturers (M1:20ml/100g e M2:19 ml/100g), mechanically spatulated under vacuum (Turbomix) for 30 seconds, and gently vibrated in the molds. Seven groups were prepared for each test, with 10 samples each, as follows: CONTROL (distilled water), G50 (substitution of 50% of gauging water by glutaraldehyde), G100 (only glutaraldehyde), C50 (substitution of 50% of gauging water by chlorhexidine digluconate), C100 (only chlorhexidine digluconate), H50 (substitution of 50% of gauging water by sodium hypochlorite) and H100 (only sodium hypochlorite). Specimens were removed from the molds after they set. Compressive strength and diametral tensile strength was determined 24 hours the specimens were cast, in an MTS-810 testing machine, with a cross-head speed of 0,5mm/min. Mean compressive and diametral tensile strength was calculated and expressed in megapascals (MPa). Data from both tests were analyzed by ANOVA and Tukey test, showing that: (a) chemical disinfectants incorporation reduced the compressive strength of type IV dental stones evaluated; (b) the use of two different proportions of gauging water substitution by disinfectants (50% and 100%) has affected the compressive strength of only one die stone (M1); (c) chemical disinfectants incorporation did not reduced.

Orientador: Clovis Pagani / Coorientadora: Anuradha Prakki / Banca: Eduardo Bresciani / Banca: Ricardo Amore / Banca: Eron Toshio Colauto Yamamoto / Banca: Graziela Ribeiro Batista / Resumo: O objetivo deste trabalho, foi avaliar a influência de agentes antiproteolíticos, imediatamente e após 12 meses, na cimentação adesiva. Foram utilizadas as porções coronárias de 64 molares humanos hígidos. As amostras foram divididas aleatoriamente em 4 grupos, de acordo com o tratamento da dentina: CT (grupo controle); CXL (grupo clorexidina); EGCG (grupo epigalocatequina-3-galato); AT (grupo antocianina). Para a restauração, foram confeccionados cilindros em resina composta Filtek Z350 XT. Após o condicionamento ácido da dentina, as soluções antiproteolíticas foram aplicadas e mantidas sobre a superfície por 60 s, em seguida as restaurações foram cimentadas às amostras com o adesivo Adper Single Bond 2 + cimento resinoso Variolink II. Todos os grupos foram subdivididos de acordo com o tempo de armazenamento em água destilada para o ensaio mecânico: I (Imediato = após 24 h); A (Armazenado = após 12 meses). As amostras foram cortadas em palitos e submetidas ao teste de microtração. Os dados obtidos foram submetidos ao teste de ANOVA a 2 fatores, seguido do teste de Tukey (α=5%). Foram encontradas diferenças para os fatores Tratamento (p=0,03) e Armazenamento (p=0,00). Os valores em MPa de média e desvio padrão para interação entre os fatores Tratamento X Armazenamento, foram: CT.I: 42.56 (±7,60) A; EGCG.I: 39.6 (±8,99) A; CLX.I: 39.37 (±9,44) A; AT.I: 38.69 (±8,65) A; CT.A: 31.85 (±6,96) A; AT.A: 31.29 (±4,89) AB; EGCG.A: 30.94 (±9,91) AB; CLX.A: 18.68 (±4,53) B. Foram confe... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract : The aim of this study was to evaluate immediately and longitunally the antiproteolytic agent influence to adhesive cementation. Were used 64 coronary portion of sound human molars. The samples were divided into 4 groups according to the dentin treatment: CG (Control group); CLX (chlorhexidine group); EGCG (epigallocatechin-3- gallate group); AT (anthocyanin group). Cylindrical composite blocks were prepared using a resin composite Filtek Supreme for the restorations. The solutions were applied on the acid-etched dentin and were kept for 60 s. The resin composite blocks were cemented with the adhesive system Adper Single Bond 2 + resin cement Variolink II. All groups were subdivided according to the storage time in distilled water for mechanical testing: I (Immediate = after 24 h); S (Stored = after 12 months). Samples were cut into beams and tested in a universal testing machine at a crosshead speed of 0.5 mm/min until failure. The data were submitted to two-way ANOVA, followed by the Tukey test (α = 5%). Significant differences were found for the Treatment factor (p = 0.03) and Storage factor (p = 0.00). The mean values and standard deviation for interaction between the factors Treatment X Storage, were CG.I: 42.56 (± 7.60) A; EGCG.I: 39.6 (± 8.99) A; CLX.I: 39.37 (± 9.44) A; AT.I: 38.69 (± 8.65) A; CG.S: 31.85 (± 6.96) A; AT.S: 31.29 (± 4.89) AB; EGCG.S: 30.94 (± 9.91) AB; CLX.S: 18.68 (± 4.53) B. Two additional samples from each group were confectioned to descriptive analyses of microhardness knoop of dentin subjacent to the bonding interface and a qualitative interface evaluation with SEM (scanning electron microscope). It can be conclude that EGCG and AT solutions were able to maintain the bond strength stability after 12 months of storage and CLX solution adversely affect the bond strength values compared to other subgroups / Doutor

Orientador : Osmir Batista de Oliveira Júnior / Banca: José Roberto Cury Saad / Banca: Maria Salete Machado Cândido / Banca: Edson Alves de Campos / Banca: Denise Pedrini / Resumo: O objetivo deste trabalho foi realizar, in vitro, avaliação da resistência de união à tração (RUT) e espessura de camada híbrida (ECH), em diferentes condições de substrato dentinário (úmido, S1; desidratado, S2 e reumedecido, S3), proporcionado pelos sistemas adesivos de 4ª geração, Scotchbond Multi Uso (SBMU) - 3M ESPE; Single Bond (SB) - 3M ESPE; Prime & Bond 2.1 (P&B2.1) - Dentsply e One Coat Bond (OCB) - Coltène-Whaledent, e os sistemas adesivos de 5ª geração (autocondicionantes), Clearfil SE Bond (CSEB) - Kuraray e One Up Bond F (OUBF) - Tokuyama. Foram utilizados 180 dentes seccionados na altura do 1/3 médio da coroa, originando duas partes cada um: remanescente dental (utilizado no teste de resistência de união à tração) e fragmento oclusal (utilizado na mensuração de camada híbrida). Para cada um dos 18 grupos foram realizadas 10 repetições em cada um dos dois testes, perfazendo um total de 360 amostras. O teste de RUT, foi realizado na Máquina de Ensaios Mecânicos MTS-810, em velocidade de 2 mm / min., e a ECH, foi mensurada à partir de fotografias obtidas em microscopia eletrônica de varredura (Microscópio Eletrônico JSM 330 A), com o software Image Tool 2.00. No teste de RUT, o desempenho dos sistemas adesivos foi melhor em S1 e, dentre eles, o CSEB foi o que apresentou a maior média, 23,01 MPa, enquanto que a menor, foi apresentada pelo OUBF, 15,69 MPa. Os sistemas adesivos de 4ª geração apresentaram médias intermediárias, às quais não foi possível encontrar diferenças estatisticamente significantes. (SBMU, 18,71 MPa; SB, 19,43 MPa; P&B2.1, 17,45 MPa e OCB, 19,92 MPa). As menores médias de RUT dos sistemas adesivos de 4ª geração, foram constatadas em S2, apresentando a menor média para o SB, 6,64 MPa, enquanto que os sistemas autocondicionantes, apresentaram menores variações de RUT entre os... (Resumo completo, clicar acesso eletrônico abaixo). / Abstract: The aim of this work was to perform the evaluation of the tensile bond strength (TBS) and the thickness of the hybrid layer (THL), in different conditions of dentinal substrate (moist, S1; dehydrated, S2 and remoistened, S3), provided by the fourth generation adhesive systems, Scotchbond Multi Uso (SBMU) - 3M ESPE; Single Bond (SB) - 3M ESPE; Prime & Bond 2.1 (P&B2.1) - Dentsply and One Coat Bond (OCB) - Coltène-Whaledent, and the fifth generation adhesive systems (self-etching), Clearfil SE Bond (CSEB) - Kuraray and One Up Bond F - Tokuyama. One hundred and eighty teeth bisected in the 1/3 crown mean level were used, originating two parts each: dental remnant (used in the tensile bond strength testing) and occlusal fragment (used in the hybrid layer measurement). For each of the 18 groups, 10 repetitions were performed for both tests, in a total of 360 samples. The TBS test was performed in a Mechanic Testing Machine MTS-810, in speed 2 mm/ min, and the THL was measured from photographs obtained in scanning electron microscopy (Electron Microscope JSM 330 A), using a software Image Tool 2.00. During the TBS test, the performance of the adhesive systems was better in S1 and, among themselves, CSEB presented the higher average, 23,01 MPa, while the lower average was presented by OUBF, 15,69 MPa. The fourth generation adhesive systems presented intermediate averages, those which did not revealed statistically significant differences. (SBMU, 18,71 MPa; SB, 19,43 MPa; P&B2,1, 17,45 MPa and OCB, 19,92 MPa). The lower averages of the fourth generation adhesive systems in TBS were verified in S2, presenting the lower average for SB, 6,64 MPa, while the self-etching systems presented lower TBS variations among the different substrates. In the THL results, lower variability was verified among the average results obtained, being the higher average presented by SBMU, 4,80 æm... (Complete abstract, click electronic address below). / Doutor

Orientador: Gelson Luis Adabo / Banca: Luís Geraldo Vaz / Banca: Guilherme Elias Pessanha Henriques / Resumo: O objetivo desta investigação foi determinar se os tratamentos térmicos podem alterar a resistência à tração e a dureza Vickers do Ti c.p. e da liga Ti-6Al-4V. Trinta corpos-de-prova na forma de halteres com 3,0 mm no segmento central e 42 mm de comprimento, obtidos por meio de uma matriz de alumínio, foram fundidos no sistema Rematitan. Os corpos-de-prova de Ti c.p. e Ti-6Al-4V foram divididos aleatoriamente em três grupos de 10 cada, e submetidos às seguintes condições de tratamento térmico: (1) controle; (2) T1 - aquecimento a 750ºC/2 h; (3) T2 - recozimento a 955ºC/1 h e envelhecimento a 620ºC/2 h. Ambos, aquecimento e resfriamento, foram realizados em atmosfera controlada de argônio. O ensaio de tração foi efetivado na máquina de testes mecânicos MTS modelo 810 à velocidade de 1,0 mm/min. Após o teste de tração uma das extremidades do corpo-de-prova foi embutida em resina acrílica, regularizada e polida antes da medida da dureza Vickers no durômetro Micromet 2100. As médias de resistência à tração e dureza Vickers foram comparadas estatisticamente usando o teste não-paramétrico de Kluskall-Wallis. Nos grupos de Ti c.p. não foram observadas diferenças significativas na resistência à tração, entretanto, na dureza Vickers os resultados do grupo T2 foram significativamente maiores que os outros grupos, que se mostraram iguais entre si. Na liga Ti-6Al-4V os grupos controle e T1 revelaram igualdade estatística em relação à resistência à tração, e significativamente superiores ao grupo T2. Quanto à dureza Vickers, diferenças estatisticamente significantes foram observadas entre os três grupos de tratamento térmico: T2>T1>controle. Não foi observada correlação entre as propriedades de resistência à tração e dureza Vickers. ...(Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The aim of this investigation was to determine whether heat treatments could change the tensile strength and Vickers hardness of CP Ti and Ti-6Al-4V alloy castings. Thirty dumbbell rods, 3.0 mm in diameter at the central segment and 42 mm in length, obtained from an aluminum matrix, were cast for each metal in the Rematitan system. The specimens of CP Ti and of alloy Ti-6Al-4V, were divided randomly into three groups of ten each; then submitted to the following heat treatments: (1) control group, without heat treatment; (2) T2 - heat at 750ºC for 2 h; (3) annealing at 955ºC for 1 h and aged at 620ºC for 2 h. The heat treatments, as well as the cooling process were conducted in the furnace with argon atmosphere. The tensile strength was measured by means of a universal testing machine, MTS model 810, at a strain of 1.0 mm/min. After the tensile testing the specimens were embedded in acrylic resin, grounded and polished prior to hardness measurements, using the Vickers tester Micromet 2100. The means and standard deviations of tensile strength and Vickers hardness were statistically compared using Kruskal-Wallis non-parametric test at a=0.05 significance level. In CP Ti groups, no statistically significant differences in tensile strength were observed; however, in Vickers hardness the results of group T2 were significantly higher than the other groups, which showed similar mean values among themselves. In Ti-6Al-4V alloy, the control and T1 groups revealed statistically higher tensile strength when compared to T2 group, with no significant difference between control and T1 group. Regarding Vickers hardness, statistically significant differences were observed among the three heat-treatment groups: T2>T1>control...(Complete abstract, click electronic access below) / Mestre