Dental erosion is a process of wear of the enamel surface, which may be caused by the low pH present in acidic foods and beverages. Changing the tooth surface may influence the bond strength of brackets during the orthodontic treatment. Thus, this study evaluated two erosive challenge protocols from the bond strength of metal orthodontic brackets after changes in bovine enamel due to two acidic drinks. This is an experimental study, in vitro, using 60 bovine incisors. The sample was randomly divided into six groups: G1 (artificial saliva - 7 days); G2 (Coca-Cola® - 7 days); G3 (Lemon juice - 7 days); G4 (artificial saliva - 30 days); G5 (Coca-Cola® - 30 days); G6 (Lemon juice - 30 days). Initially, it was performed the analysis of dental Knoop microhardness to verify the standardization of the samples. Then, the immersion of the specimens was performed in the drinks, following the prescribed protocols. Finishing the erosive protocol, the metal brackets were cemented and, 48 hours later, the resistance was evaluated through the shear test. For statistical analysis of the data, we used the ANOVA test of two factors (solution factor and period of the treatment factor) followed by Tuckey's Post Hoc and the T Test of Student for paired samples, all with α = 5%. The sample presented normal distribution according to the Kolmogorov-Smirnov test (p= 0,77). The mean and the standard deviation of the microhardness of the total samples were 281,89 ± 44,51 KHN. There was no statistically significant difference in shear strength to the period of treatment factor (seven or 30 days F5,54= 0,105; p= 0,901), however, there were statistically significant differences for the solution factor (F5,54= 6,671; p= 0,003). The Tukey's Post Hoc test found that these differences occurred between Saliva x Coca-Cola® solutions (p= 0,003) and Coca-Cola® x Lemon juice (p= 0,029). When comparing if the treatment period would be significant for the shearing results in each solution, the T test did not show any influence of the period to any solution used. When comparing if the treatment time it would be significant for the shearing results in each solution, the T test did not show any influence of the time to any solution used. It is concluded that the period of the protocol used does not influence the bond strength of the bracket to the tooth, but, regarding the immersion substances, Coca-Cola® presented higher shear strength values. / A erosão dental é um processo de desgaste da superfície do esmalte que pode ser provocado pelo baixo pH presente em alimentos e bebidas ácidas. A alteração da superfície dental pode influenciar na resistência adesiva de bráquetes durante o tratamento ortodôntico. Desta forma, este trabalho avaliou dois protocolos de desafio erosivo a partir da resistência adesiva de bráquetes ortodônticos metálicos após alterações provocadas em esmalte bovino por duas bebidas ácidas. Trata-se de um estudo experimental, in vitro, utilizando 60 incisivos bovinos. A amostra foi dividida aleatoriamente em seis grupos: G1 (saliva artificial - 7 dias); G2 (Coca-Cola® - 7 dias); G3 (Suco de limão - 7 dias); G4 (saliva artificial - 30 dias); G5 (Coca-Cola® - 30 dias); G6 (Suco de limão - 30 dias). Inicialmente, foi realizada a análise da microdureza dental Knoop para verificar a padronização das amostras. Em seguida, foi realizada a imersão dos corpos de prova nas bebidas seguindo os protocolos estipulados. Finalizando o protocolo erosivo, os bráquetes metálicos foram cimentados e 48 horas depois foi avaliada a resistência por meio do teste de cisalhamento. Para análise estatística dos dados foi utilizado o Teste ANOVA de dois fatores (fator solução e fator tempo de tratamento) seguido do Post Hoc de Tukey e o Teste T de Student para amostras pareadas, todos com α= 5%. A amostra apresentou distribuição normal segundo o teste de Kolmogorov-Smirnov (p= 0,77). A média e desvio padrão da microdureza das amostras totais foram 281,89 ± 44,51 KHN. Não houve diferença estatisticamente significativa na resistência ao cisalhamento para o fator tempo (sete ou 30 dias; F5,54= 0,105, p= 0,901), contudo, houve diferença estatisticamente significativa para o fator solução (F5,54= 6,671; p= 0,003). O Teste Post Hoc de Tukey identificou que estas diferenças ocorreram entre as soluções Saliva x Coca-Cola® (p= 0,003) e Coca-Cola® x Suco de limão (p= 0,029). Ao se comparar se o tempo de tratamento seria significativo para os resultados do cisalhamento em cada solução, o Teste T não revelou influência do tempo para nenhuma solução utilizada. Conclui-se que o tempo de protocolo utilizado não influencia na resistência adesiva do bráquete ao dente, porém em relação às substâncias de imersão, a Coca-Cola® apresentou maiores valores de resistência ao cisalhamento.

A erosão dentária ocasiona a perda da estrutura dental através da dissolução da sua porção mineralizada por ácidos de origem não bacteriana. Assim, o objetivo deste estudo é avaliar a capacidade de materiais contendo compostos bioativos de remineralizar o esmalte bovino submetido a desafio erosivo e se o método de quantificação da fluorescência induzida por luz (QLF) tem correlação com os resultados do teste de microdureza Knoop. 120 fragmentos de esmalte bovino foram distribuídos entre os grupos experimentais, sendo n=5 para o teste de microdureza (3 x 3 x 2 mm) e n=10 para o método do QLFTM (5 x 5 x 3 mm). Os corpos-de-prova foram analisados em três momentos diferentes (inicial, após 2 dias de protocolo de erosão e após 6 dias de tratamento remineralizador). As amostras foram submetidas a 2 dias de protocolo de erosão, através de imersão em ácido cítrico a 0,3% pH 3,2, por 2 minutos e manutenção das mesmas em saliva artificial (pH 7,0) durante 24 horas. Na sequência, foram realizados os tratamentos remineralizadores por 6 dias consecutivos: 1 gota de saliva foi depositada sobre as amostras e após 1 hora foram imersas por 2 minutos em suspensão aquosa preparada com os seguintes materiais: G1-Pro-Argin+NaMFP, bicarbonato de arginina + carbonato de cálcio + monofluorfosfato de sódio (Colgate® Sensitive Pró-Alívio); G2-Recaldent+NaF, fosfopeptídeo de caseína com fosfato de cálcio amorfo + fluoreto de sódio (MI Paste Plus); G3-ACP+NaF, fosfato de cálcio amorfo + fluoreto de sódio + nitrato de potássio (Relief ACP); G4-CaGP+KF, glicerofosfato de cálcio + fluoreto de potássio (Flúor Protector Gel); G5-NovaMin®+NaF, fosfosilicato de cálcio e sódio + fluoreto de sódio (Nupro® Sensodyne®); G6-NovaMin®+NaMFP, fosfosilicato de cálcio e sódio + monofluorfosfato de sódio (Sensodyne® Repair&Protect); G7-NaF, fluoreto de sódio + nitrato de potássio (Sensodyne® Cool Gel) e G8-saliva artificial (controle negativo). Após 2 horas de imersão em saliva foi repetido o protocolo de erosão. Foram realizadas análises estatísticas para o teste de microdureza e QLF (=0,05). A ANOVA de dois fatores para medidas repetidas mostrou diferenças estatisticamente significativas apenas para os momentos da análise e para a interação dos fatores tratamentos x momentos da análise. O teste de Tukey mostrou diferenças significativas na comparação entre todos os momentos da análise e na interação momentos da análise x tratamentos: valores iniciais x após erosão e após tratamento e entre os valores após erosão x após tratamento (NovaMin®+NaF, NovaMin®+NaMFP, NaF e saliva). O teste de Tukey na comparação dos tratamentos no momento final da análise mostrou diferenças significativas na análise da microdureza para o Recaldent+NaF x NovaMin®+NaF, NovaMin®+NaMFP e NaF; mas no QLF, as diferenças ocorreram entre o Pro-Argin+NaMFP x NaF e saliva; Recaldent+NaF x NovaMin®+NaMFP, NaF e saliva e ACP+NaF x NaF. Nenhum dos tratamentos foi capaz de remineralizar totalmente o esmalte dental, mas os materiais Pro-Argin+NaMFP, Recaldent+NaF, ACP+NaF e CaGP+KF foram capazes de estabilizar o processo de erosão do esmalte com resultado superior aos demais tratamentos. O método do QLF mostrou uma correlação positiva significativa com os resultados do teste de microdureza. / Dental erosion leads to loss of the tooth structure by dissolving its mineral portion by acids for non-bacterial origin. The objective of this study is evaluate the ability of materials with bioactive compounds to remineralize bovine enamel subjected to erosive challenge and verify the possible correlation between the datas from the quantitative light-induced fluorescence method (QLF) and the Knoop surface microhardness test. 120 bovine enamel pieces were distributed among experimental groups with n=5 for microhardness testing (3 x 3 x 2 mm) and n=10 for the QLF method (5 x 5 x 3 mm) and were analysed at three different times (initial, after 2 days of erosion protocol and after 6 remineralizing days of treatment).The samples were subjected to two-days erosion protocol, through its immersion into 0,3% citric acid solution pH 3,2 for 2 minutes and maintaining them into artificial saliva for 24 hours (pH 7,0). Following remineralizing treatments were performed for 6 consecutive days: the samples were covered with 1 drop of saliva and after 1 hour were immersed for 2 minutes in the slurry prepared with the following materials: G1-Pro-Argin+NaMFP, arginine bicarbonate + calcium carbonate + sodium monofluorophosphate (Colgate® Sensitive Pro-Alívio); G2-Recaldent+NaF, casein phosphopeptide-amorphous calcium phosphate + sodium fluoride (MI Paste Plus); G3-ACP+NaF, amorphous calcium phosphate + sodium fluoride + potassium nitrate (Relief ACP); G4-CaGP+KF, calcium glycerophosphate + potassium fluoride (Fluor Protector Gel); G5- NovaMin®+NaF, calcium sodium phosphosilicate + sodium fluoride (Nupro® Sensodyne®); G6-NovaMin®+NaMFP, calcium sodium phosphosilicate + sodium monofluorophosphate (Sensodyne® Repair&Protect); G7-NaF, sodium fluoride + potassium nitrate (Sensodyne® Cool Gel) and G8-Artificial saliva (negative control). After 2 hours of soaking in saliva the erosion protocol was repeated. Statistical analyzes were conducted for microhardness and QLF with coincidence of the results (=0,05). A two-factors ANOVA for repeated measures showed statistically significant differences only for the time of analysis and the interaction treatments x time of analysis. The Tukey test showed statistically significant differences when comparing the three times of analysis and the interaction between times of analysis x treatments: baseline values with values after erosion and after treatment and the values after erosion x after treatment (NovaMin®+NaF, NovaMin®+NaMFP, NaF and saliva). The Tukey test when comparing the treatments x final times of analysis showed statistically significant differences in microhardness test for Recaldent+NaF x NovaMin®+NaF, NovaMin®+NaMFP and NaF; in QLF method the differences occurs between Pro-Argin+NaMFP x NaF and saliva; Recaldent+NaF x NovaMin®+NaMFP, NaF and saliva; ACP+NaF x NaF. None of the treatments was able to completely remineralize bovine enamel, but Pro-Argin+NaMFP, Recaldent+NaF, ACP+NaF and CaGP+KF materials were able to stabilize the eroding enamel, thus demonstrating a score higher than others and the QLF method showed a significant and positive correlation with the microhardness test results.

Objetivo. Este estudo analisou a interação entre fatores sócio-demográficos, ocupacionais e em relação ao estilo de vida associados à saúde bucal dos trabalhadores encaminhados ao CEREST-Guarulhos Método. Este foi um estudo transversal e o cálculo do tamanho da amostra resultou na análise de 100 trabalhadores. Coletaram-se as informações sócio-demográficas, ocupacionais e em relação ao estilo de vida dos trabalhadores com questionários validados para uso no Brasil, e estes foram: o questionário OHIP14 (autopercepção da saúde bucal), o questionário da tolerância de Fagestron (dependência de nicotina), o questionário AUDIT (consumo de álcool), a escala de estresse no trabalho (EET), a prática de atividade física (PAF) e o índice da capacidade para o trabalho (ICT); também foi realizado exame clínico odontológico respeitados os critérios da OMS para verificação da condição de saúde bucal dos trabalhadores. As análises estatísticas utilizadas para associação entre as variáveis foram teste t de student, Mann-Whitney, ANOVA e Kruskall-Wallis. Para análise conjunta dos fatores associados foram realizadas regressões lineares e logísticas múltiplas Resultados. O índice CPO-D variou significativamente conforme avanço dos grupos etários analisados, sendo melhor explicado pelas perdas dentárias (P<0,0001). As LCNCs (lesões cervicais não cariosas) e as condições periodontais (CPI e PIP) variaram significativamente segundo os grupos etários. O escore OHIP14, fagestron, Audit, prática de atividade física, EET e ICT não variaram significativamente conforme avanço dos grupos etários (p>0,05). A presença de LCNCs, através da análise de regressão logística múltipla, esteve associada estatistica e independentemente das demais variáveis, à idade OR=4,27(IC95% 1,89-9,71) e ao grupo ocupacional de exposição a névoas ácidas e produtos químicos OR=4,14 (IC95% 1,15-14,96). As perdas dentárias estiveram associadas, independentemente das demais variáveis, à idade (p<0,0001) e à dependência de nicotina (p=0,007). Os anos de fumo também estiveram associados significativamente ao número de LCNCs (p=0,044), e independentemente das demais variáveis, através da análise de regressão linear múltipla Conclusões. Entre os trabalhadores, as altas taxas de perdas dentárias e de LCNCs estiveram associadas à idade e aos hábitos de fumo. As LCNCs também estiveram associadas aos grupos de exposição a névoas ácidas e produtos químicos no meio ambiente ocupacional, denotando uma multifatorialidade no desenvolvimento destas lesões. A importância de ações de promoção da saúde bucal nas empresas, como, por exemplo, a inclusão de ações em saúde bucal no programa de controle médico em saúde ocupacional (PCMSO), a inclusão de ações em saúde bucal na semana interna de prevenção de acidentes do trabalho (SIPAT) e a realização de exames odontológicos admissionais e periódicos nos trabalhadores, aliadas com estratégias de combate ao fumo, bem como até a própria criação de uma norma regulamentadora (NR) para tratar das questões referentes à saúde bucal dos trabalhadores merecem especial atenção. / Objectives- This study intended to collaborate with relations of social and demographic conditions, occupational factors and lifestyle with oral health of workers in a municipal reference centre of workers health, located in Guarulhos, SP-Brazil. Methods- It was a cross-sectional study and the sample consisted of 100 workers. They answered the questionaries: Work Ability Index (WAI), Baecke Questionaire, Fagerstron Tolerance Questionaire, Audit Test, Work Stress Scale (WSS) and Oral Health Impact Profile-short form (OHIP14). After that, workers were conducted to a clinical dental exam, in respect of WHO parameters. Statistic analyses were performed using student t test, Mann-whitney, analyse of variance (ANOVA), Kruskal-Wallis, multiple regression analysis model and multiple unconditioned logistic regression analysis. Results- There was a significant progressive reduce in DMFT index, associated with increase of age groups, and the missing (M) teeth was responsible for this impact (P<0,0001). The NCCLs (Non carious cervical lesions) and the periodontal conditions including the periodontal attachment loss were significant associated with age groups. Scores of OHIP14, Fagestron, Audit test, Baecke questionnaire, WSS and WAI weren´t associated with age groups. The presence of NCCLs, by unconditional logistic regression, was better explained by age groups OR=4,27(IC95% 1,89-9,71) and occupational exposure to acid mists and chemical products OR=4,14 (IC95% 1,15- 14,96). Missing teeth were better explained by age groups (p<0,0001) and fagestron tolerance (p=0,007). The ages of smoking habits were associated with NCCLs (p=0,044), and independent of other variables, by multiple linear regression. Conclusions- Missing teeh and NCCLs were associated with age groups and smoking habits. The NCCLs were associated to occupational exposure to acid mists and chemical products, implying multifactorial theory in development of NCCLs. Educative and promotion of oral health actions in companies should be suportted by regulation of federal laws, including admissional and periodical clinical dental exams in workers, with stop smoking habits. Public policies should be created to brazilian workers to improve oral health.

Este estudo in situ avaliou o resultado de um ataque erosivo com a presença de biofilme dentário, e o efeito da associação entre desafio erosivo e cariogênico, sobre o esmalte dentário humano por meio da aferição do desgaste e da porcentagem de perda de microdureza superficial (%PDS). Durante duas fases cruzadas de 14 dias, 11 voluntários previamente selecionados utilizaram dispositivos intrabucais palatinos contendo espécimes de esmalte humano, os quais foram submetidos a quatro grupos com tratamentos distintos: (GI) bebida a base de cola, (GII) bebida a base de cola com acúmulo de biofilme dentário, (GIII) bebida a base de cola mais sacarose a 20% com acúmulo de biofilme dentário, (GIV) sacarose a 20% com acúmulo de biofilme dentário. Desta forma, no GI os espécimes foram fixados no nível do dispositivo palatino, já nos GII, GIII e GIV eles foram fixados 1,0 mm abaixo do nível do aparelho e cobertos por uma tela plástica para acúmulo do biofilme dentário. Em uma das fases (na qual GI e GII foram estudados), os voluntários imergiram o dispositivo palatino em 200 ml da bebida a base de cola por 5 minutos, 3 vezes ao dia. Na outra fase, uma solução de sacarose a 20% foi gotejada 8 vezes ao dia nos espécimes dos GIII e GIV, e apenas metade do aparelho, com os espécimes correspondentes ao GIII, foi imersa na bebida como mencionado acima. A concentração de flúor no biofilme, o desgaste e a %PDS foram mensurados. Os dados foram analisados pelos testes ANOVA e Tukey (p<0,05). Os valores médios de desgaste (µm) e %PDS foram respectivamente: GI- 4,82A; 87,45a; GII- 0,14B; 13,47b; GIII- 0,34B; 68,87c; GIV- 0,41B; 86,12a. A bebida a base de cola com acúmulo de biofilme dentário (GII) promoveu maior concentração de flúor no biofilme. Os resultados sugerem que a presença de biofilme dentário pode diminuir o ataque ácido de uma bebida erosiva e que a associação entre desafio erosivo e cariogênico produz menores alterações no esmalte (desgaste e %PDS). / This in situ study evaluated whether an erosive attack with the presence of dental biofilm and the association between erosive and cariogenic challenge could reduce or increase the wear and the percent change in microhardness (%SMH) of human enamel. During 2 experimental 14-day crossover phases, 11 previously selected volunteers wore intraoral devices containing human enamel specimens which were submitted to four groups of separated treatment: (GI) cola drink, (GII) cola drink and biofilm accumulation, (GIII) cola drink plus 20% sucrose and biofilm accumulation, (GIV) 20% sucrose and biofilm accumulation. Thus, on GI the specimens were fixed at the intraoral device level and on GII, GIII and GIV they were fixed 1.0mm under the device level and covered by plastic meshes for biofilm accumulation. In one phase (GI and GII under study), the volunteers immersed the device for 5 minutes in 200ml of cola drink, 3 times per day. On the other phase, 20% sucrose solution was dripped onto the specimens 8 times per day on GIII and GIV and only half of the palatal device, corresponding to GIII, was immerse in cola drink as mentioned above. Biofilm fluoride concentration, changes in wear and %SMH were measured. Data were tested using ANOVA and Tukey?s test (p<0,05). The mean values of wear (µm) and %SMH were respectively: GI- 4.82A, 87.45a, GII- 0.14B, 13.47b, GIII- 0.34B, 68.87c, GIV- 0.41B, 86.12a. The cola drink with biofilm accumulation (GII) promoted greater biofilm fluoride concentration. The data suggest that the presence of dental biofilm can decrease the acid attack of an erosive drink and the association of erosive and cariogenic challenge can reduce the dental enamel alterations (wear and %SMH).

Uma alternativa de tratamento para as lesões iniciais de erosão é a aplicação de materiais resinosos. Porém, não há estudos que avaliem a penetração desses materiais no interior da lesão de erosão, o que poderia interferir em sua adesão e efeito. Portanto, o objetivo do presente estudo foi avaliar a penetração do infiltrante, adesivos e selante de fossas e fissuras, sobre lesões iniciais de erosão, com e sem condicionamento da superfície de esmalte. Utilizando um protocolo in vitro, foram estudados os tipos de tratamento em 5 níveis (Adhese®- sistema adesivo autocondicionante de 2 passos, Tetric N-Bond®- sistema adesivo convencional de 2 passos, Single Bond®- sistema adesivo convencional de 2 passos, Helioseal Clear®- selante resinoso e Icon®- infiltrante) e o tipo de condicionamento do esmalte em 2 níveis (com e sem). Os materiais foram corados com 0,02 mg/ml de solução etanólica de isotiocianato de tetrametilrodamina. Para o desenvolvimento da lesão inicial de erosão, 75 blocos de esmalte bovino (4 x 4 mm) foram imersos em HCl 0,01 M, pH 2,3, durante 30 segundos. Posteriormente, em metade da superfície dos blocos foram aplicados os materiais (marcados com rodamina), seguindo as instruções dos fabricantes. Na outra metade, os materiais foram aplicados da mesma forma, mas sem o condicionamento prévio do esmalte. Os blocos foram avaliados por Microscopia Confocal de Varredura a Laser nos modos de reflexão e fluorescência. Nas imagens geradas foram mensuradas a profundidade de desmineralização, a penetração e a espessura dos materiais, por meio do software ImageJ. Os dados foram analisados pelo teste ANOVA a dois critérios e teste de Tukey (p<0,05). Independentemente do material utilizado, o condicionamento do esmalte resultou em maior profundidade de desmineralização, penetração e espessura dos materiais, do que a situação sem condicionamento (p<0,05). A profundidade de desmineralização foi semelhante para os diferentes materiais (p>0,05), com exceção do Icon® (maior desmineralização) em relação ao Adhese® (p<0,05). Para a penetração dos materiais no esmalte, o Icon® seguido do HeliosealClear® apresentou maior profundidade de penetração, com diferença significativa entre eles (p<0,05) e não houve diferença para o Adhese®, Tetric N-Bond® e Single Bond® (p>0,05). A aplicação do HeliosealClear® resultou em maior espessura de material seguido pelo Icon®, com diferença estatística significativa entre eles (p<0,05), sendo que os outros materiais em estudo apresentaram espessura menor, sem diferença significativa entre eles (p>0,05). Concluiu-se que para todos os materiais resinosos estudados, o condicionamento prévio da superfície de esmalte aumentou a penetração do material no interior da lesão, sendo que o material com maior penetração foi o infiltrante (Icon®). / The application of resin based materials is an alternative of treatment for eroded lesions. Nevertheless, there are no studies about the penetration of these materials into eroded lesion, which might affect its adhesion and effect. Therefore, the purpose of this study was to evaluate the penetration of infiltrant, adhesives and pit and fissure sealant on initial eroded lesion, with and without prior enamel surface conditioning. By using an in vitro protocol, types of treatment were studied at 5 levels (AdheSE®- two-steps self-etching adhesive system, Tetric N-Bond®- two-steps conventional adhesive system, Single Bond® - two-steps conventional adhesive system, Helioseal Clear®- resin sealant and Icon®-infiltrant) and type of enamel conditioning in two levels (with and without). The materials were stained with 0.02 mg/ml ethanolic solution of tetramethylrhodamine isothiocyanate. Bovine enamel samples (4 x 4 mm) were immersed in 0.01 M HCl, pH 2.0, for 30 seconds in order to produce initial eroded lesions. Afterwards, the materials (previously marked with rhodamine) were applied on half of sample enamel surface following the manufacturers instructions. On the other half of sample enamel surface, the materials were applied following the same instructions but without prior enamel surface conditioning. The enamel samples were evaluated by Confocal Laser Scanning Microscope using reflection and fluorescence modes. Depth of demineralization, depth of penetration and thickness of the materials were measured using ImageJ software. Data were analyzed by two-way ANOVA and Tukey test (p<0.05). Regardless of the material, enamel conditioning resulted in higher depth of demineralization, depth of penetration and material thickness than without conditioning (p<0.05). Depth of demineralization was similar on the materials (p>0.05), except Icon® (higher demineralization) compared to AdheSE® (p<0.05). Icon® followed by Helioseal Clear® showed higher penetration depth in enamel, with significant difference between them (p<0.05) and no difference was found among AdheSE®, Tetric N-Bond® and Single Bond® (p>0.05). The application of Helioseal Clear® resulted in increased thickness of material followed by Icon®, with statistically significant difference (p<0.05). The other studied materials showed less thickness, without significant difference among them (p>0.05). It was concluded that for the studied resin based materials, the prior enamel surface conditioning increased penetration of the material into the eroded lesion and the infiltrant (Icon®) presented the highest penetration.

Orientador: Cínthia Pereira Machado Tabchoury / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-24T16:55:42Z (GMT). No. of bitstreams: 1 Romao_DayseAndrade_M.pdf: 1484114 bytes, checksum: 22ae5951c7308f4697935396ac72aaeb (MD5) Previous issue date: 2014 / Resumo: Modelos in vitro devem mimetizar situações próximas das condições reais, entretanto poucos modelos para avaliar erosão em esmalte dentário nestas condições são encontrados na literatura, além de apresentarem algumas limitações. Assim, o objetivo do presente estudo foi validar um modelo de ciclagens erosivas que simule os episódios de erosão/exposição do esmalte dental à saliva, avaliando o efeito dose-resposta para soluções de ácido cítrico com diferentes valores de pH. O modelo de ciclagens erosivas de pH teve uma duração de 5 dias, de forma que blocos de esmalte bovino, selecionados quanto à dureza de superfície e análise de perfilometria, foram imersos em saliva humana estimulada por 1 h a 37ºC sob agitação (100 rpm) antes do primeiro desafio erosivo de cada dia para formação de película adquirida. Em seguida os blocos dentais foram tratados 4 vezes ao dia com a solução de tratamento (2,5 mL/mm2 de área exposta de esmalte dental) sob agitação (100 rpm) por 1 min e nos intervalos entre os tratamentos e durante à noite, os blocos foram imersos em saliva artificial a 37?C sem agitação. Para avaliação do modelo quanto ao efeito dose-resposta ao pH, os blocos (n=12) foram tratados com as seguintes soluções: G1 - cacodilato pH 7,0 (controle); G2 - ácido cítrico pH 2,5; G3 - ácido cítrico pH 3,5; G4 - ácido cítrico pH 4,5; G5 - ácido cítrico pH 5,5; G6 - ácido cítrico pH 7,0. Todas as soluções foram preparadas na concentração de 47,6 mM. Diariamente, ao final da ciclagem e após a imersão na saliva artificial durante à noite, os blocos foram avaliados quanto à dureza de superfície para cálculo da porcentagem de perda de dureza de superfície (%PDS) e ao final do experimento a análise perfilométrica foi novamente realizada. Os resultados foram submetidos à análise de variância e teste de Tukey(p<0,05). Os resultados ao final da ciclagem mostraram que houve um aumento crescente da %PDS em função dos dias na maioria dos grupos e que os blocos tratados com solução de pH 2,5 apresentaram a maior %PDS (p<0,05). Na comparação entre grupos os resultados demonstram que no 4o dia de ciclagem foram verificadas diferenças significativas entre todos os grupos (p<0,05). Já os resultados após saliva apresentaram menores valores de %PDS quando comparados àqueles após ciclagem. Quanto à perfilometria, os blocos dentais tratados com soluções de pH 2,5 e 3,5 apresentaram as maiores perdas de superfície, diferindo entre si e dos demais grupos (p<0,05). Conclui-se que o estudo proposto permitiu a validação de um modelo de ciclagens erosivas que demonstrou efeito dose-resposta para erosão inicial de esmalte dentário após exposição a diferentes valores de pH / Abstract: In vitro models should mimic situations close to the real conditions, however, few models to assess tooth enamel erosion in these conditions are found in the literature, besides presenting some limitations. Thus, the objective of this study was validate a model that simulates cycling episodes of erosion/exposure of dental enamel to saliva, evaluating the dose-response effect for citric acid solutions with different pH values. The model of erosive cycling lasted 5 days, and bovine enamel blocks, selected according to the surface hardness and surface profilometry analysis, were immersed in stimulated human saliva for 1 h at 37°C under agitation (100 rpm) before the first erosive challenge in each day for salivary pellicle formation. Then the dental blocks were treated 4 times daily with the treatment solution (2.5 mL/mm2 per area of exposed enamel) under stirring (100 rpm) for 1 min and in the intervals between treatments and during the nigth the blocks were immersed in artificial saliva at 37?C without stirring. To evaluate the model with regard to the dose-response to pH, blocks (n = 12) were treated with the following solutions: G1 - cacodylate pH 7.0 (control), G2 - citric acid pH 2.5, G3 - acid citric pH 3.5; G4 - citric acid pH 4.5; G5 - citric acid pH 5.5; G6 - citric acid pH 7.0. All the solutions were prepared in a concentration of 47.6 mM. Daily, at the end of the cycling and after immersion in artificial saliva during the night, the blocks were evaluated for surface hardness to calculate the percentage of surface hardness loss (%SHL) and at the end of the experiment profilometry analysis was performed again. The results were submitted to ANOVA and Tukey's test (p<0.05). The results showed a gradual increase in the %SHL at the end of the cycling model as a function of days in most of the groups and the blocks treated with pH 2.5 solution showed the highest %SHL (p<0.05). In the comparison of the groups, the results showed in the 4th cycling day significant differences among all groups (p<0.05). The results after saliva exposure showed lower %SHL when compared to those after cycling. Regarding profilometry, dental blocks treated with solutions pH 2.5 and 3.5 showed the highest surface losses, differing from each other and from the other groups (p<0.05). In conclusion, the proposed study allowed the validation of an erosive cycling model that demonstrated dose-response effect for early tooth enamel erosion after exposure to different pH values / Mestrado / Cariologia / Mestra em Odontologia

Erosão dental é definida como a perda irreversível de tecido duro dental por um processo químico que não envolve bactérias. O objetivo deste trabalho foi comparar in vitro o potencial erosivo de duas fontes ácidas e avaliar métodos de controle da erosão dental em esmalte. Para a comparação das fontes ácidas, coroas de 5 molares inclusos foram seccionadas em quatro, totalizando 20 espécimes. Nos espécimes, uma superfície de esmalte (janela) de 3 x 3 mm foi delimitada. Os espécimes foram submetidos ao desafio erosivo em suco gástrico (obtido durante endoscopia) (n=10), ou suco de laranja (industrializado) (n=10), como segue: 5 minutos em 3 ml de solução ácida, enxágue com água destilada e armazenagem em saliva artificial por 3 horas. Este ciclo foi repetido 4 vezes ao dia por 14 dias. O cálcio (Ca) eliminado dos espécimes na solução ácida foi quantificado por Espectrometria de emissão atômica. A presença de carbonato (CO) e fosfato (PO) foi avaliada nos espécimes antes e após o desafio erosivo pela Espectroscopia FT-Raman. Para a avaliação dos métodos de controle da erosão quarenta espécimes de esmalte de molares inclusos foram distribuídos para cada um dos métodos propostos (n=10): gel de flúor fosfato acidulado (APF 1,23%), laser de Nd:YAG (100 mJ, 1 W, 10 Hz), associação flúor + laser e laser + flúor. Os métodos de controle foram aplicados 1 hora antes do desafio erosivo já descrito, realizado com ácido clorídrico (0,01 M/pH 2,2) como fonte ácida. O flúor foi mantido por 4 minutos sobre a superfície de esmalte. A superfície foi irradiada, com contato, após aplicação de um fotoabsorvedor. As associações foram feitas utilizando o flúor e o laser como descrito anteriormente. A perda de Ca dos espécimes foi quantificada por Espectrometria de emissão atômica e a rugosidade superficial dos espécimes (Ra) foi avaliada antes e após o desafio erosivo. Na comparação das fontes ácidas, os espécimes submetidos à erosão perderam: 12,74 ± 3,33 mg/L de Ca (suco gástrico) e 7,07 ± 1,44 mg/L de Ca (suco de laranja) (p=0,0003). A análise em Espectroscopia FT-Raman não detectou alteração significativa na razão CO/PO após o desafio ácido. Os valores CO/PO antes e depois do desafio foram: 0,16/0,17 (suco gástrico) (p=0,37) e 0,18/0,14 (suco de laranja) (p=0,16). Na avaliação dos métodos de controle da erosão, as perdas de Ca foram (mg/L): APF 1,707a (± 0,113), Nd:YAG 1,638a (±0,080), APF + Nd:YAG 1,385b (±0,078), Nd:YAG + APF 1,484b (±0,068). A rugosidade média inicial dos espécimes foi de 0,14 m. Após o desafio erosivo a rugosidade apresentou significativo aumento (p<0,01): APF 0,69bc (±0,091), Nd:YAG 0,87a (±0,119), APF + Nd:YAG 0,61c (±0,090) e Nd:YAG + APF 0,72b (±0,069). Foi possível concluir que o suco gástrico apresentou potencial erosivo ao esmalte maior que o suco de laranja. A associação entre flúor e laser apresentou-se mais eficaz no controle da erosão dental do que os métodos isoladamente. / Dental erosion is defined as irreversible loss of dental hard tissue due to chemical processes without the involvement of microorganisms. The aim of this study was to compare in vitro the erosive potential of two acidic sources and evaluate the effectiveness of treatments for prevention of dental erosion. To compare the acidic sources, crowns of 5 unerupted human third molars were sectioned in four, totalizing 20 enamel slabs. In the slabs, a test surface (window) of 3 x 3 mm was delimited. The specimens were submitted to erosive challenge into gastric juice (from endoscopy exam) (n=10), or orange juice (industrialized) (n=10), as follows: 5 minutes in 3 ml of acidic solution, rinse with distilled water and stored in artificial saliva for 3 hours. This cycle was repeated for four times a day during 14 days. Calcium (Ca) loss after acid exposure was determined by atomic emission spectroscopy. The presence of carbonate (CO) and phosphate (PO) in the specimens was evaluated before and after the erosive challenge by FT-Raman spectroscopy. To evaluate the treatments for prevention of dental erosion, forty enamel specimens of unerupted human third molars were distributed according to the following treatments (n=10): acidic phosphate fluoride gel (APF 1.23%), Nd:YAG laser (100 mJ, 1 W, 10 Hz), and the associations fluoride + laser and laser + fluoride. These treatments were applied 1 hour before the erosive challenge, which, in this phase was made with hydrochloric acid only (0.01 M/pH 2.2). The fluoride was applied on the enamel surfaces for 4 minutes. The irradiation of enamel surface was made in the contact mode after coating with a photo-activator. The associations were done using fluoride and laser like describe before. The Ca loss was determined by atomic emission spectroscopy and superficial roughness (Ra) was measured before and after the erosive challenge. In the comparison of the acidic sources, the mean loss of Ca were: 12.74 ± 3.33 mg/L Ca (gastric juice) and 7.07 ± 1.44 mg/L Ca (orange juice) (p=0.0003). The FT-Raman spectroscopy found no statistically significant difference in the ratio CO/PO after the erosive challenge. The CO/PO ratios values before and after the challenge were: 0.16/0.17 (gastric juice) (p=0.37) and 0.18/0.14 (orange juice) (p=0.16). In the evaluation of the treatments, the mean Ca loss were (mg/L): APF 1.707a (± 0.113), Nd:YAG 1.638a (±0.080), APF + Nd:YAG 1.385b (±0.078), Nd:YAG + APF 1.484b (±0.068). The mean initial roughness of specimens was 0.14 m. After the erosive challenge the roughness showed a significant increase (p<0.01): APF 0.69bc (±0.091), Nd:YAG 0.87a (±0.119), APF + Nd:YAG 0.61c (±0.090) and Nd:YAG + APF 0.72b (±0.069). It was concluded that gastric juice has higher erosive potential to enamel than orange juice and the association between fluoride and laser was more efficient for the prevention of dental erosion than both methods separately.

Devido a alterações químico-estruturais causadas pelo clareamento, os substratos dentais poderiam tornar-se mais susceptíveis a perda tecidual, principalmente se expostos a desafios erosivo/abrasivos. Desta forma, o presente estudo teve como objetivos: 1) analisar in vitro, se o esmalte e a radicular dentina clareada com diferentes agentes e concentrações, apresenta uma maior susceptibilidade ao desgaste, quando submetido a ciclos de erosão e abrasão; 2) comparar o efeito da aplicação de um agente clareador a base de peróxido de carbamida a 10% a um placebo no desgaste do esmalte e da dentina radicular, através de um modelo in situ. Os resultados do estudo in vitro mostraram que, independentemente do agente usado, o clareamento não aumentou o desgaste do esmalte frente a episódios erosivo-abrasivos. Na dentina, o desgaste foi dependente do agente clareador aplicado. Baseado no protocolo in situ adotado, o peróxido de carbamida a 10% não causou maior desgaste superficial no esmalte, mas aumentou a perda de tecido dentinário comparado ao placebo. Pode-se concluir que, em termos de desgaste superficial, o esmalte não foi afetado pelo tratamento clareador, enquanto a dentina mostrou-se mais susceptível. Assim, sugerem-se cuidados adicionais na seleção do agente clareador em situações clínicas que apresentam dentina radicular exposta. / Due to the chemical and microstructural alterations caused by bleaching, the dental substrates can become more susceptible to tissue loss, mainly if exposed to erosive/abrasive challenges. Therefore, the present study had the following objectives: 1) to analyze in vitro, if enamel and root dentin that had been bleached with different agents and concentrations, were at increased risk of wear when submitted to cycles of erosion and abrasion; 2) to compare the effect of the application of a 10% carbamide peroxide bleaching agent to a placebo on wear of enamel and root dentin, through an in situ model. The results of the in vitro study showed that independent of agent used, the bleaching demonstrated no increase in the wear of enamel when exposed to the erosive-abrasive episodes. In dentin, the wear was dependent on the bleaching agent applied. Based on the in situ protocol adopted, the 10% carbamide peroxide did not cause higher wear on the enamel, but increased the wear of the root dentin compared to the placebo. It could be concluded that in terms of superficial wear, enamel was not affected by bleaching treatment, while dentin showed to be more susceptible. Thus, additional caution is suggested in the choice of the bleaching agent when root dentin is exposed.

O cimento de ionômero de vidro tem mais de 40 anos de uso clínico, com muitas boas qualidades e propriedades de material para forramento e restauração. Como o principal motivo de troca de restaurações é a lesão de cárie secundária, a sua capacidade de indução de remineralização e inibição de desmineralização mostram uma qualidade desejável desse material. Além disso, não se sabe até que ponto o flúor liberado pelos cimentos de ionômeros de vidro é capaz de inibir o processo erosivo. Portanto, o objetivo deste trabalho foi avaliar a capacidade de inibição dos desafios cariogênicos em dentes restaurados com diferentes tipos de materiais ionoméricos restauradores, bem como avaliar a inibição dos mesmos materiais frente a um desafio erosivo. Foram confeccionados 120 fragmentos de dentes bovinos, que foram divididos aleatoriamente em seis grupos, para serem restaurados com diferentes tipos de cimentos de ionômero de vidro (CIV): CIV de alta viscosidade (Fuji IX), CIV modificado por resina (Vitremer), CIV modificado por resina com nanopartículas (N100), CIV modificado por resina encapsulado (Riva Light Cure), CIV de alta viscosidade encapsulado (Riva Self Cure) e um grupo controle com resina composta (Filtek Z350). Após a restauração de tamanho padronizado, seguindo as indicações do fabricante, os espécimes foram submetidos à desafio cariogênico (ciclagem de pH) e erosivo (ácido cítrico). Microdureza superficial do tipo Knoop das amostras foi avaliada inicialmente. Após 24 horas de desafio erosivo, e 5 dias de ciclagem de pH (desafio cariogênico), uma nova avaliação de microdureza foi realizada para avaliar a perda mineral ao redor das restaurações. Na avaliação estatística, utilizou-se o teste de normalidade de Anderson-Darling e teste de homogeneidade de Levene. Para as comparações, foi realizada análise de variância e teste de contraste de Student-Newman Keuls, com nível de significância de 5%. O desafio erosivo reduziu significantemente a dureza superficial, mas nenhuma diferença significante foi observada independentemente do material restaurador (p>0,05). Para análises do esmalte ao redor, diferenças significantes foram observadas com relação aos diferentes materiais (p<0,001) e distâncias das restaurações (p=0,023). Espécimes restauradas com resina apresentaram maior perda mineral e amostras restauradas com CIV convencional de alta viscosidade e CIV encapsulado modificado por resina apresentaram os menores valores de perda mineral. Em conclusão, os CIVs exercem efeito protetor no esmalte apenas contra desafio cariogênico. / The glass ionomer cements (GIC) has more than 40 years been used in clinical practice, with good qualities and properties as dental material of liner and restoration. Since the main reason of restoration replace is secondary caries lesion, the ability of the GIC in inducing remineralization and inhibiting demineralization are important characteristics of this type of material. Furthermore, it is still unclear if the fluoride released by the GIC is able to inhibit the erosive process. Therefore, the aim of this study was to evaluate the ability of inhibition of cariogenic challenge in teeth restored with different types of GIC, as well as to evaluate the inhibition of the same materials concerning erosive challenge. One hundred and twenty samples of bovine teeth were prepared and randomly divided in 6 groups, in order to be submitted to restorative procedures with different types of GIC: High viscous GIC (Fuji IX), resin-modified GIC (Vitremer), resin-modified GIC with nanoparticles (N100), encapsulated resinmodified GIC (Riva Light Cure),encapsulated high viscous GIC (Riva Self Cure) and a control group with resin (Filtek Z350). Knoop microhardness evaluations were initially performed. After performing restorations with standardized dimensions and according to the manufacturers instructions, the samples were submitted to cariogenic challenge (pH cycling) and erosive challenge (citric acid). After 24 h of erosive challenge, and 5 days of pH cycling, new microhardness assessments were performed to evaluate mineral loss around of restorations. For statistical analysis, it was used Anderson-Darling test to test the normality and Levene test to check the homogeneity of the data. To compare the different groups, it was used Analysis of variance and Student-Newman-Keuls post-hoc test, considering the level of significance of 5 %. Erosive challenge significantly reduced enamel surface hardness, but no significant difference was observed irrespectively restorative materials (p>0.05). For enamel analyses, significant differences were observed with respect to the different materials (p<0.001) and distances (p=0.023).Specimens restored with the composite resin presented higher mineral loss and specimens restored with the conventional high viscous GIC and the encapsulated resin-modified GIC presented the lowest values for mineral loss. In conclusion, the GICs exert protective effect only for cariogenic challenge.

A erosão dental provoca alterações histológicas complexas na dentina e, apesar do aumento da ocorrência desta patologia na última década, a literatura apresenta poucos estudos sobre a adesão na dentina erodida. Com o aprimoramento da tecnologia e o conhecimento de que os lasers de érbio apresentam grande afinidade pela água e hidroxiapatita, sua utilização tem sido considerada um método alternativo para tratamento da superfície dentinária antes dos procedimentos adesivos. Assim, o objetivo deste trabalho in vitro foi avaliar o efeito de diferentes tratamentos de superfície (ponta diamantada, laser de Er:YAG 2,94 m, 60 mJ, 2 Hz, 0,2 W, 19,3 J/cm2 - e laser de Er,Cr:YSGG 2,78 m, 50 mJ, 30 Hz, 1,5 W, 4,5 J/cm2), prévios ao tratamento restaurador, tanto na dentina humana hígida quanto na dentina artificialmente erodida. Metade das amostras foi submetida à ciclagem erosiva, a qual foi realizada durante 5 dias por meio da imersão em solução de ácido cítrico 0,05 M (pH 2,3, 10 minutos, 6x/dia) e solução supersaturada (pH 7,0, 60 minutos entre os ataques ácidos). Na fase experimental 1, 32 fragmentos de dentina foram divididos aleatoriamente em 8 grupos (n = 4) e com o auxílio da Microscopia Eletrônica de Varredura (MEV), realizou-se a análise da morfologia da superfície da dentina hígida e da submetida à ciclagem erosiva, após os diferentes tratamentos de superfície. Na fase experimental 2, 192 terceiros molares humanos foram divididos aleatoriamente em 2 grupos (dentina hígida e dentina submetida à ciclagem erosiva) e 8 subgrupos (n = 12) para avaliação da resistência de união entre as superfícies tratadas e 2 sistemas adesivos (01 autocondicionante e 01 com condicionamento ácido prévio), por meio do ensaio de microtração e da análise do padrão de fratura. Para o ensaio de microtração, blocos de resina composta microhíbrida foram confeccionados na superfície de dentina e, após armazenados em água destilada-deionizada por 24h (37oC), palitos foram obtidos para serem tracionados na máquina de ensaio universal (0,5mm/min). A análise do padrão de fratura realizada em microscópio ótico (40x) e as avaliações das eletromicrografias foram feitas de forma descritiva. Os valores obtidos de resistência de união(MPa) foram submetidos aos testes de ANOVA (dois fatores) e de comparações múltiplas de Tukey (p<0,05). A análise morfológica de superfície mostrou alterações significativas da dentina hígida e da dentina artificialmente erodida, submetidas aos diferentes tratamentos de superfície. Quanto à resistência de união, na dentina hígida, o grupo controle, tanto do sistema autocondicionante (54,69 ± 7,80 MPa) quanto do condicionamento ácido total (47,36 ± 9,35 MPa), apresentou valores significativamente maiores que os outros grupos, sendo, porém, diferentes entre si. Na dentina erodida, a maior resistência de união foi alcançada com o grupo tratado com o laser de Er,Cr:YSGG associado ao adesivo autocondicionante (28,26 ± 9,22 MPa), o qual foi significativamente diferente de todos demais grupos. Com base nos parâmetros de irradiação utilizados neste estudo, pode-se concluir que em dentina hígida, os tratamentos de superfície com os lasers de Er:YAG e Er,Cr:YSGG apresentaram resultados de adesão inferiores, mas satisfatórios, em relação ao grupo controle. Já em substrato dentinário erodido, a irradiação com laser de Er,Cr:YSGG, associada ao uso de sistema adesivo autocondicionante, promoveu efeito positivo para a adesão à resina composta. / Dental erosion can cause complex histological changes in dentin and, despite the increase in its incidence during the last decade, limited information is available regarding adhesion to eroded dentin. With improvements in technology and due to the fact that the erbium lasers have high affinity to water and hydroxyapatite, the use of laser can consist on an alternative for the treatment of dentin surface before adhesive procedures. The aim of this in vitro study was to evaluate the effect of different surface treatments (diamond bur, Er:YAG laser 2.94 m, 60 mJ, 2 Hz, 0.2 W, 19.3 J/cm2 - and Er,Cr:YSGG laser 2.78 m, 50 mJ, 30 Hz, 1.5 W, 4.5 J/cm2) prior to restorative treatment, in sound and artificially eroded human dentin. Half of the samples was submitted to the erosive cycling, which was performed by immersion in 0.05 M citric acid (pH 2.3, 10 min, 6x/day) and in supersaturated solution (pH 7.0, 1h, between acid attacks), during 5 days. In phase 1, 32 dentin fragments were randomly divided into 8 groups (n = 4). The analysis of surface morphology of both sound and eroded dentin was performed by Scanning Electron Microscopy (SEM), after the different surface treatments. In phase 2, 192 human third molars were randomly divided into 2 groups (sound and eroded dentin) and 8 subgroups (n=12) to evaluate the bond strength between the treated surfaces and composite resin, with two adhesive systems (self-etching and total-etching) by means of the microtensile bond strength (TBS) test and fracture pattern analysis. For the microtensile bond strength test, blocks of composite resin were bonded to the samples and, after 24 h-storage in distilled/deionized water (37°C), stick-shapped samples were obtained and submitted to TBS test in a universal testing machine (0.5 mm/min). The fracture pattern was performed with an optical microscopy (40x) and the evaluations of the electromicrographs were made under a descriptive mode. The bond strength values (MPa) were analyzed by two-way ANOVA and Tukey tests ( = 0.05). In sound dentin, for the control group, both self-etching (54.69 ± 7.8 MPa) and total-etching adhesive system (47.36 ± 9.3 MPa) showed significantly higher values than all other groups (p<0.05), even though they differ from each other. However, in eroded dentin groups, the self-etching on the samples treated with the Er,Cr:YSGG laser presented the highest mean (28.3 ± 9.2 MPa), which was statistically significant higher than all the other treatments (p<0.05). Based on the irradiation parameters considered for this study, it can be concluded that in healthy dentin, the surface treatment with Er:YAG and Er,Cr:YSGG irradiation showed bonding values lower than the control group, but they presented satisfactory results. However, in eroded dentin, the use of Er,Cr:YSGG laser, associated with the self-etching adhesive system, promoted positive effect on adhesion to composite resin.