Made available in DSpace on 2014-12-17T14:58:00Z (GMT). No. of bitstreams: 1 RuiCSM_MESTRE.pdf: 3074589 bytes, checksum: ce573ec9d691a895e59153850a53bf18 (MD5) Previous issue date: 2010-02-26 / This paper aims to present the feasibility of using a composite using discarded material from the cultivation of banana tree (pseudostem), which is fibrillated together with synthetic resin replacing glass fiber to be used in structural elements that do not demand large mechanical stress such as reservoirs, troughs, domes, sewage pipes etc.. For this, there were studies about the mechanical properties of a composite made with polyester resin and fiber of banana tree (Musa sp, musac), in which the splints were removed from the pseudostem, being made fibrillation by hand, with the aid of a brush steel, followed by natural drying. After treatment for cleaning and removal of wax, the fiber was cut into pieces of approximately 60 mm to 100 mm, for, together with synthetic resin, make cards of a features fiber composite with random orientation relative to the weight of the resin. We used three different percentages of fiber (3%, 6% and 9%), in order to make a comparative study between them and what would be the one with the best performance. Were manufactured specimens of each material and then subjected to uniaxial tensile tests, three point bending, moisture absorption and thermal characteristics. The results show that, in general, the use of banana tree fiber is feasible simply by an improvement in the production process (machining of the procedure) and greater care in the manufacture of parts / Este trabalho tem como objetivo apresentar a viabilidade de um comp?sito utilizando material descartado da lavoura da bananeira (pseudocaule), o qual ? fibrilado juntamente com resina sint?tica em substitui??o ? fibra de vidro, a ser utilizado em elementos estruturais que n?o demandem grandes esfor?os mec?nicos, tais como reservat?rios, calhas, domos, tubula??es de esgotamento etc. Para isso foram efetuados estudos sobre as propriedades mec?nicas de um comp?sito de resina poli?ster e fibra de bananeira (musa s.p., mus?cea), nos quais foram retiradas as talas do pseudocaule, sendo feita a fibriliza??o de forma manual, com o aux?lio de uma escova de a?o, seguido de secagem ao natural. Ap?s tratamento para limpeza e retirada de cera, a fibra foi cortada em peda?os de aproximadamente 60 mm a 100 mm para, juntamente com a resina sint?tica, fabricar placas de um comp?sito de caracter?sticas fibrosas com orienta??o aleat?ria em rela??o ao peso da resina. Foram utilizadas tr?s percentagens distintas de fibras (3%, 6% e 9%), a fim de se efetuar um estudo comparativo entre elas e determinar qual seria aquela com o melhor desempenho mec?nico. Foram fabricados corpos de prova de cada material, sendo ent?o submetida aos ensaios de tra??o uniaxial, flex?o em tr?s pontos, absor??o de umidade e caracter?sticas t?rmicas. Os resultados demonstram que, de forma geral, o uso de fibra de bananeira ? vi?vel, bastando uma melhoria no seu processo de obten??o (mecaniza??o do procedimento) e um maior cuidado durante a fabrica??o das pe?as

Made available in DSpace on 2014-12-17T14:58:01Z (GMT). No. of bitstreams: 1 AndreRS_DISSERT.pdf: 3053585 bytes, checksum: 50d506b11ef1b50e68a6f0ead473ecc8 (MD5) Previous issue date: 2010-08-16 / We built an experimental house on an UFRN?s land using blocks made by a composite consisting of cement, plaster, EPS, crushed rubber and sand. Several blocks were made from various compositions and we made preliminary tests of mechanical and thermal resistance, choosing the most appropriate proportion. PET bottles were used inside the block to provide thermal resistance. In this work, a second function was given to the bottles: to serve as a docking between the blocks, because the ends of the cylinders came out of each block on top as well as at the bottom, with the bottom cut, allowing to fit of the extremities of the upper cylinder of a block in the lower holes of the other one, which were formed by the cutting already mentioned. Minimum compression tests were performed according to ABNT standards for walls closing blocks (fence). With that house built, we did studies of thermal performance in order to ascertain conditions of comfort, checking external and internal temperatures in the walls and in the ambient, among other variables, such as wind speed and relative humidity. The resulting blocks provided adequate thermal insulation to the environment, where the walls presented differences up to 11.7 ?C between the outer and inner faces, getting the maximum temperature inside the house around 31 ?C, within the so-called thermal comfort zone for warm climates. At the end of the experiments it was evident the effectiveness of that construction in order to provide thermal comfort in the internal environment of the house, as well as we could confirm the viability of building houses from recyclable materials, reducing the constructive costs, becoming a suitable alternative for low- incoming families. Moreover, besides the low cost, the proposal represents an alternative use of various recyclable materials, therefore considered an ecological solution / Foi constru?da uma casa experimental em um terreno da UFRN a partir de blocos confeccionados com um comp?sito constitu?do de cimento, gesso, EPS, borracha triturada e areia. Foram confeccionados diversos blocos a partir de composi??es variadas e foram efetuados testes preliminares de resist?ncia mec?nica e t?rmica, escolhendo-se a propor??o mais apropriada. Foram utilizadas garrafas PET no interior dos blocos a fim de proporcionar resist?ncia t?rmica. Neste trabalho, uma segunda fun??o foi conferida ?s garrafas: a de servir de encaixe entre os blocos, pois as extremidades das garrafas sa?am de cada bloco tanto na parte superior, como tamb?m na inferior, sendo a extremidade inferior seccionada, permitindo o encaixe das extremidades superiores das garrafas de um bloco nos orif?cios inferiores de outro bloco, os quais foram formados pela sec??o acima mencionada. Foram realizados ensaios de compress?o m?nima segundo as normas da ABNT para blocos destinados ao fechamento de paredes (blocos de veda??o). Constru?da a referida casa, foram realizados estudos de desempenho t?rmico a fim de averiguar as condi??es de conforto, verificando-se as temperaturas externa e interna nas paredes e a temperatura ambiente, dentre outras vari?veis, tais como a velocidade do vento e a umidade relativa do ar. Os blocos confeccionados proporcionaram isolamento t?rmico adequado para o ambiente, apresentando as paredes diferen?as de at? 11,7? C entre as faces externa e interna, ficando a temperatura m?xima interna da casa em torno de 31?C, dentro da chamada zona de conforto t?rmico para regi?es de clima quente. Ao t?rmino dos experimentos, ficou evidente a efic?cia da constru??o no sentido de proporcionar conforto t?rmino no ambiente interno da casa, bem como foi confirmada a viabilidade da constru??o de casas populares a partir de materiais recicl?veis, reduzindo-se o custo construtivo, sendo uma alternativa apropriada para fam?lias de baixa renda. Ademais, al?m do baixo custo, a proposta representa uma alternativa para o aproveitamento de diversos materiais recicl?veis, sendo ecologicamente correta

Made available in DSpace on 2014-12-17T14:58:09Z (GMT). No. of bitstreams: 1 HallyjusADB_DISSERT.pdf: 2542860 bytes, checksum: a76cbfa6200b38f0f8ff5811d0315d59 (MD5) Previous issue date: 2011-02-18 / Composite materials have a wide application in various sectors, such as the medical field in the manufacture of prostheses, in automotive and aerospace. Thus it is essential to the development of new composite and a better understanding in the face of various loading conditions and service. Several structural elements are manufactured in the presence of geometric discontinuity (notch, hole, etc ) in their longitudinal sections and/or cross-cutting, and these affect the mechanical response of these elements. The objective is to study the mechanical response of laminated polymer matrix hybrid composites reinforced with glass fiber/jute in a uniaxial tensile test. The mechanical response takes in account both the influence of the presence of a geometric discontinuity (semicircular notches) and the orientation of fibers in the layers (anisotropy). The semicircular notches are located in longitudinal section (with a reduction in cross section) of the same. In this analysis, the anisotropy is characterized by types of configurations (with different orientations of fibers in the outer layers). A comparative study of mechanical properties with and without the presence of notches is developed. Both configurations consist of four layers of woven jute fiber bidirectional and a central layer of bidirectional woven glass fibers. In addition to the mechanical properties was also studied the characteristics of the fracture developed in each composite laminate. The results showed that in the comparative study, the anisotropy and the presence of semicircular notches directly influences the mechanical behavior of laminates composites, mainly in reducing the tensile strength, and well as the final characteristics of the fracture / Os materiais comp?sitos t?m uma ampla aplica??o nos mais variados setores, como por exemplo, na ?rea m?dica na confec??o de pr?teses, na ind?stria automotiva e no setor aeroespacial. Assim ? essencial o desenvolvimento de novos comp?sitos e uma melhor compreens?o frente ?s mais diversas condi??es de carga e servi?o. V?rios elementos estruturais s?o fabricados na presen?a de descontinuidade geom?trica (entalhe, furo etc.) em suas se??es longitudinais e/ou transversais, e essas prejudicam a resposta mec?nica desses elementos. O objetivo do trabalho ? estudar a resposta mec?nica de laminados comp?sitos h?bridos de matriz polim?rica refor?ado com fibras de vidro/juta em um ensaio de tra??o uniaxial. A resposta mec?nica leva em conta tanto a influ?ncia da presen?a de uma descontinuidade geom?trica (entalhes semicirculares) quanto da orienta??o das fibras nas camadas (anisotropia). Os entalhes semicirculares est?o localizados na se??o longitudinal (com redu??o da se??o transversal) dos mesmos. Nessa an?lise, a anisotropia ? caracterizada por dois tipos de configura??es (com diferentes orienta??es das fibras nas camadas externas). Um estudo comparativo das propriedades mec?nicas com e sem a presen?a dos entalhes ? desenvolvido. As duas configura??es consistem de quatro camadas de tecidos bidirecionais de fibras de juta e uma camada central de tecido bidirecional de fibras de vidro. Al?m das propriedades mec?nicas, tamb?m foi estudada as caracter?sticas da fratura desenvolvidas em cada laminado comp?sito. Os resultados mostraram que, no estudo comparativo, a anisotropia e a presen?a dos entalhes semicirculares influi diretamente no comportamento mec?nico dos laminados comp?sitos, principalmente na redu??o da resist?ncia ? tra??o, e bem como na caracter?stica final da fratura

Made available in DSpace on 2014-12-17T14:58:13Z (GMT). No. of bitstreams: 1 FlavioASL_DISSERT.pdf: 2460649 bytes, checksum: bed5dd26e82ea61d687c6641214ac014 (MD5) Previous issue date: 2012-04-27 / Space Science was built using a composite made of plaster, EPS, shredded tires, cement and water. Studies were conducted to thermal and mechanical resistance. Inside the mold EPS plates were placed in order to obtain a higher thermal resistance on the wall constructed, as well as to give it an end environmentally friendly in view of both the tire and the EPS occupy a large space in landfills and year need to be degraded when released into the environment. Compression tests were performed according to ABNT blocks to seal, measurements of the temperature variation in the external and internal walls using a laser thermometer and check the temperature of the indoor environment using a thermocouple attached to a digital thermometer. The experiments demonstrated the heat provided by the composite values from the temperature difference between the internal and external surfaces on the walls, reaching levels of 12.4 ? C and room temperature in the interior space of the Science of 33.3 ? C, remaining within the zone thermal comfort for hot climate countries. It was also demonstrated the proper mechanical strength of such a composite for sealing walls. The proposed use of the composite can contribute to reducing the extreme housing shortage in our country, producing popular homes at low cost and with little time to work / Foi constru?do o Espa?o Ci?ncia utilizando um comp?sito constitu?do de gesso, EPS, pneu triturado, cimento e ?gua. Foram realizados estudos de resist?ncias t?rmica e mec?nica. No interior do molde foram colocadas placas de EPS com o intuito de se obter uma maior resist?ncia t?rmica nas paredes constru?das, como tamb?m dar-lhe um fim ecologicamente correto, tendo em vista que tanto o pneu quanto o EPS ocupam grande espa?o em aterros sanit?rios e necessitam de anos para serem degradados quando lan?ados ao meio ambiente. Foram realizados ensaios de compress?o segundo as normas da ABNT para blocos de veda??o, medi??es da varia??o de temperatura nas paredes externas e internas utilizando um term?metro a laser e verifica??o da temperatura do ambiente interno utilizando um termopar acoplado a um term?metro digital. Os experimentos t?rmicos demonstraram os valores proporcionados pelo comp?sito a partir da diferen?a de temperatura entre as superf?cies internas e externas nas paredes, alcan?ando n?veis de 12,4?C e temperatura ambiente no interior do espa?o ci?ncia, de 33,3 ?C ficando dentro da zona de conforto t?rmico para pa?ses de clima quente. Demonstrou-se tamb?m apropriada resist?ncia mec?nica de tal comp?sito para paredes de veda??o. A utiliza??o do comp?sito proposto pode contribuir para a diminui??o do extremo d?ficit habitacional do nosso pa?s, produzindo resid?ncias populares a baixo custo e com pequeno tempo de obra

Made available in DSpace on 2014-12-17T14:58:15Z (GMT). No. of bitstreams: 1 JoseHBL_DISSERT_PARCIAL.pdf: 2505963 bytes, checksum: 1b82ec8a8147b2b7e13d0af6880855f0 (MD5) Previous issue date: 2012-05-02 / Conselho Nacional de Desenvolvimento Cient?fico e Tecnol?gico / Materials denominated technical textiles can be defined as structures designed and developed with function to fulfill specific functional requirements of various industrial sectors as are the cases of the automotive and aerospace industries. In this aspect the technical textiles are distinguished from conventional textile materials, in which the aesthetic and of comfort needs are of primordial importance. Based on these considerations, the subject of this dissertation was established having as its main focus the study of development of textile structures from aramid and glass fibers and acting in order to develop the manufacture of composite materials that combine properties of two different structures, manufactured in an identical operation, where each structure contributes to improving the properties of the resulting composite material. Therefore were created in laboratory scale, textile structures with low weight and different composition: aramid (100%), glass (100%) and aramid /glass (65/35%), in order to use them as a reinforcing element in composite materials with polyester matrix. These composites were tested in tension and its fracture surface, evaluated by MEV. Based on the analysis of mechanical properties of the developed composites, the efficiency of the structures prepared as reinforcing element were testified by reason of that the resistance values of the composites are far superior to the polyester matrix. It was also observed that hybridization in tissue structure was efficient, since the best results obtained were for hybrid composites, where strength to the rupture was similar to the steel 1020, reaching values on the order of 340 MPa / Os materiais denominados t?xteis t?cnicos podem ser definidos como estruturas projetadas e desenvolvidas com a fun??o de atender a requisitos funcionais espec?ficos de diversos setores da ind?stria, caso da ind?stria automotiva e aeroespacial. Nesse aspecto, distinguem-se dos materiais t?xteis convencionais, nos quais as necessidades est?ticas e de conforto t?m import?ncia primordial. Com base nessas considera??es, o tema dessa disserta??o foi estabelecido tendo como enfoque principal o estudo do desenvolvimento de estruturas t?xteis a partir de fibras de aramida e de vidro, atuando no sentido de elaborar a fabrica??o de materiais comp?sitos que combinem propriedades de duas estruturas diferentes, fabricadas em uma mesma opera??o, onde cada estrutura contribui para melhoria das propriedades do material comp?sito resultante. Para tanto foram desenvolvidas em escala laboratorial estruturas t?xteis de baixa gramatura e composi??o diferenciada de aramida (100%), vidro (100%) e aramida/vidro (65/35%) para utiliza??o como elemento refor?ante em comp?sitos com matriz de poli?ster. Os comp?sitos produzidos foram ensaiados em tra??o e sua superf?cie de fratura avaliada por MEV. Com base nas analises das propriedades mec?nicas dos comp?sitos desenvolvidos, observou-se a efici?ncia das estruturas ou elaboradas como elemento refor?ante tendo em vista que os valores de resist?ncia dos comp?sitos foram muito superiores ? matriz de poli?ster. Tamb?m foi observado que a hibridiza??o na estrutura dos tecidos foi eficiente, uma vez que os melhores resultados obtidos foram para os comp?sitos h?bridos, onde a resist?ncia na ruptura foi semelhante ? do a?o 1020, atingindo valores na ordem de 340 MPa

Made available in DSpace on 2014-12-17T14:58:20Z (GMT). No. of bitstreams: 1 AlanJLM_DISSERT.pdf: 1835050 bytes, checksum: 47bf4fbd76665d11995bd7eb5bd3522a (MD5) Previous issue date: 2013-07-23 / Materials known as technical textiles can be defined as structures designed and developed to meet specific functional requirements of various industry sectors, which is the case in automotive and aerospace industries, and other specific applications. Therefore, the purpose of this work presents the development and manufacture of polymer composite with isophthalic polyester resin. The reinforcement of the composite structure is a technical textile fabric made from high performance fibers, aramid (Kevlar 49) and glass fiber E. The fabrics are manufactured by the same method, with the aim of improving the tensile strength of the resulting polymer composite material. The fabrics, we developed some low grammage technical textile structures in laboratory scale and differentiated-composition type aramid (100%), hybrid 1 aramid fiber / glass (65/35%) and hybrid 2 aramid fiber / glass (85/15% ) for use as a reinforcing element in composite materials with unsaturated isophthalic polyester matrix. The polymer composites produced were tested in uniaxial tensile fracture surface and it?s evaluated by SEM. The purpose of this work characterize the performance of polymer composites prepared, identifying changes and based on resistance to strain corresponding to the mechanical behavior. The objectives are to verify the capability of using this reinforcement structure, along with the use of high performance fibers and resin in terms of workability and mechanical strength; verify the adherence of the fiber to the matrix and the fracture surface by electron microscopy scanning and determination of tensile strength by tensile test. The results indicate that, in a comparative study to the response of uniaxial tensile test for tensile strength of the composites and the efficiency of the low percentage of reinforcement element, being a technical textile fabric structure that features characteristic of lightness and low weight added in polymer composites / Os materiais denominados de tecidos t?cnicos podem ser definidos como estruturas projetadas e desenvolvidas com a fun??o de atender a requisitos funcionais espec?ficos de diversos setores da ind?stria com aplica??es espec?ficas. Nesse sentido, este trabalho apresenta o desenvolvimento e a fabrica??o de comp?sito polim?rico com resina poli?ster isoft?lico. O refor?o do comp?sito ? uma estrutura de tecido t?xtil t?cnico confeccionado com fibras de alto desempenho de aramida (Kevlar 49) e fibra de vidro E. Os tecidos s?o fabricados pelo mesmo m?todo, com o objetivo do aprimorar a resist?ncia a tra??o do material comp?sito polim?rico resultante. Os tecidos, foram desenvolvidos em escala laboratorial com baixa gramatura e composi??o diferenciada de aramida (100%), h?brido 1 fibra de aramida/vidro (65/35%) e h?brido 2 fibra de aramida/vidro (85/15%) para utiliza??o como elemento refor?ante em comp?sitos com matriz de poli?ster insaturada isoft?lico. Os comp?sitos polim?ricos produzidos foram ensaiados em tra??o uniaxial e sua superf?cie de fratura avaliada por MEV. A proposta do trabalho ? caracterizar o desempenho dos comp?sitos polim?ricos elaborados, identificando as altera??es e baseando-se na resist?ncia ao ensaio de tra??o correspondente a comportamento mec?nico. Os objetivos s?o verificar a potencialidade da utiliza??o desta estrutura de refor?o, juntamente com a utiliza??o das fibras de alto desempenho e a resina, em termos de trabalhabilidade e resist?ncia mec?nica; verificar a ader?ncia da fibra ? matriz e a superf?cie de fratura atrav?s de microscopia eletr?nica de varredura e determina??o de resist?ncia ? ruptura por ensaio de tra??o. Os resultados indicam que, em um estudo comparativo para a resposta dos ensaios mec?nicos de tra??o uniaxial h? resist?ncia ? ruptura dos comp?sitos e a efici?ncia da baixa porcentagem do elemento de refor?o, sendo uma estrutura de tecido t?xtil t?cnico que apresenta caracter?stica de leveza e baixa gramatura adicionada nos comp?sitos polim?ricos

Made available in DSpace on 2014-12-17T14:58:25Z (GMT). No. of bitstreams: 1 RicardoFS_DISSERT.pdf: 1728822 bytes, checksum: b1de7d66ecdbf708be30f5dcf1f5d8fc (MD5) Previous issue date: 2014-07-28 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / Presents a composite formed by orthophthalic resin and fiber loading of carnauba straw. The fibers were first dried in direct sun exposure and subsequently ground into fodder for the reduction in size. Various formulations of the composite were preliminarily tested by choosing the one presenting the best processability in applying the mold. The composite produced is used for the manufacture of a parabolic surface subsequently coated with mirror segments, flexible plastic, for reflecting the solar rays incident on it. The reflective parable represents the main element of the solar cooker that works with the concentration of sunlight and has dimensions of 1.14 m in diameter and area of 1.0 m?. Manufacturing processes and assembly of solar cooker concentration produced are presented. The results of tests for cooking and baking various foods, including rice, pasta, beans, cake, cassava, shrimp, beef, breaded demonstrating the competitiveness of solar cooker studied with other stoves already manufactured and tested in Brazil are presented and in the world. It was also demonstrated the feasibility of the proposed composite for Prototypes manufacture of solar and other structures that do not require great efforts resistance / Apresenta-se um comp?sito formado por resina ortoft?lica e carga de fibra da palha da carna?ba. As fibras foram inicialmente secadas em exposi??o direta ao sol e posteriormente trituradas em forrageira para a diminui??o do seu tamanho. V?rias formula??es do comp?sito foram preliminarmente ensaiados, escolhendo-se a que apresentava a melhor processabilidade na aplica??o ao molde. O comp?sito produzido ? utilizado para a fabrica??o de uma superf?cie parab?lica, posteriormente revestida com segmentos de espelho pl?stico, flex?vel, para a reflex?o dos raios solares nela incidentes. A par?bola refletora representa o principal elemento do fog?o solar que trabalha com a concentra??o dos raios solares e possui dimens?es de 1,14m de di?metro e ?rea de 1,0m?. S?o apresentados os processos de fabrica??o e montagem do fog?o solar ? concentra??o produzido. S?o apresentados os resultados dos ensaios para o cozimento e assamento de v?rios alimentos, dentre eles arroz, macarr?o, feij?o, bolo, macaxeira, camar?o, carne, empanados que demonstraram a competitividade do fog?o solar estudado com outros fog?es j? fabricados e ensaiados no Brasil e no mundo. Tamb?m foi comprovada a viabilidade do comp?sito proposto para a fabrica??o de prot?tipos solares e outras estruturas que n?o requerem resist?ncia a grandes esfor?os

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2018-03-20T17:21:11Z No. of bitstreams: 1 CamillaDeMedeirosDantasAzevedo_TESE.pdf: 4219113 bytes, checksum: 435317fad552ba84e55910c905f4e93f (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2018-03-22T12:38:32Z (GMT) No. of bitstreams: 1 CamillaDeMedeirosDantasAzevedo_TESE.pdf: 4219113 bytes, checksum: 435317fad552ba84e55910c905f4e93f (MD5) / Made available in DSpace on 2018-03-22T12:38:32Z (GMT). No. of bitstreams: 1 CamillaDeMedeirosDantasAzevedo_TESE.pdf: 4219113 bytes, checksum: 435317fad552ba84e55910c905f4e93f (MD5) Previous issue date: 2017-10-10 / As propriedades mec?nicas dos materiais comp?sitos, das mais diversas aplica??es industriais, podem ser reduzidas significativamente pela ocorr?ncia de impactos de baixas velocidades. Esses impactos podem provocar danos internos no material comprometendo sua integridade. Assim, o presente estudo tem como objetivo fazer uma an?lise experimental da resist?ncia residual ? flex?o em tr?s pontos e compress?o ap?s o impacto (CAI), de dois tipos de laminados comp?sitos de matriz polim?rica ortoft?lica, sendo um deles refor?ado a com 7 camadas de tecido bidirecional de Vidro E (CV) e o outro refor?ado com 7 camadas de tecido bidirecional de Kevlar 49 (CK), sujeitos a impactos de baixa velocidade. Esse estudo ? de grande import?ncia pelo fato de tentar conduzir ao aparecimento prematuro de instabilidade estrutural e a consequente restri??o do seu uso. A energia utilizada nesse trabalho para os dois tipos de laminados foi de aproximadamente 96J. Al?m disso, para o material comp?sito refor?ado com fibra de kevlar, foram feitos sucessivos impactos com a mesma energia verificando sua influ?ncia nas propriedades do laminado. Sendo aplicadas 5 vezes, e 10 vezes a energia m?xima de 96J. Como resultado verificou-se que no laminado CV, tanto as propriedades de compress?o como de flex?o em tr?s pontos, a resist?ncia se manteve praticamente inalterada enquanto que o m?dulo teve uma diminui??o depois do impacto. J? no laminado CK houve um decr?scimo tanto nas propriedades de compress?o como flex?o em tr?s pontos ap?s o impacto. Essa perda da integridade desses materiais pode ser justificada pela ocorr?ncia de delamina??o nas interfaces dos comp?sitos. / The mechanical properties of the composite materials, used in the most diverse industrial applications, can be significantly reduced by the occurrence of low speed impacts. These impacts can cause internal damage to the material and compromise its integrity. Thus, the present study aims to perform an experimental analysis of the residual resistance to three-point flexural test and compression after impact (CAI), in two types of composite laminates of orthophthalic polymeric matrix, being one of them reinforced with 7 layers of E-Glass bidirectional tissue (CV) and the other reinforced with 7 layers of Kevlar 49 bidirectional tissue (CK), subject to low speed impacts. This study is of great importance because it tries to lead to the premature appearance of structural instability and the consequent restriction of its use. The energy used in this work for the two types of laminates was approximately 96J. In addition, for the Kevlar fiber reinforced composite material, were made successive impacts with the same energy being checked its influence on the properties of the laminate, where it was tested with a repetition of 5 times and 10 times the maximum energy of 96J.As result, it was found that in the CV laminate, both in the compression properties and three-point flexural properties, the resistance remained practically unchanged while the modulus had a decrease after impact. In the CK laminate, there was a decrease both in compression properties and three-point flexural properties after impact. This integrity loss of these materials can be justified by the occurrence of delamination at the interfaces of the composites.

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2016-12-29T16:57:52Z No. of bitstreams: 1 RobertoJoseDeMedeiros_TESE.pdf: 7235998 bytes, checksum: b68f913160c40f812b2fd7d6568b2bb6 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2017-01-02T19:22:06Z (GMT) No. of bitstreams: 1 RobertoJoseDeMedeiros_TESE.pdf: 7235998 bytes, checksum: b68f913160c40f812b2fd7d6568b2bb6 (MD5) / Made available in DSpace on 2017-01-02T19:22:06Z (GMT). No. of bitstreams: 1 RobertoJoseDeMedeiros_TESE.pdf: 7235998 bytes, checksum: b68f913160c40f812b2fd7d6568b2bb6 (MD5) Previous issue date: 2016-06-17 / Constitu?dos de uma fase aglutinante (matriz) e outra (refor?os) que lhes conferem sustentabilidade e capacidade de suporte de carga, os materiais comp?sitos encontram-se cada vez mais consagradamente estabelecidos no meio tecnol?gico, tanto das pesquisas quanto do uso industrial, em face da variedade de suas aplica??es, possibilidades de utiliza??o e configura??es sempre inovadoras de concep??o. Matrizes e refor?os ligam-se sem fus?o permitindo a conserva??o de suas caracter?sticas particulares, mas conferem novas propriedades ao novo material, que originam, possibilitando a prepara??o deste, segundo conforma??o desejada para uma finalidade determinada. Neste sentido, no trabalho de pesquisa que ora se apresenta, foi idealizado um comp?sito laminado a base de uma resina polim?rica termofixa do tipo Ep?xi ?ster Vin?lica, refor?ada com 8 (oito) camadas de um tecido h?brido bidirecional constitu?do por fibras kevlar na dire??o urdume e fibras de carbono na dire??o trama; esse material comp?sito foi definido como LC (Laminado Comp?sito a base de tecido h?brido bidirecional carbono/kevlar). O estudo do comportamento mec?nico desse comp?sito laminado LC foi realizado segundo enfoques experimental, anal?tico e num?rico com o objetivo geral de determinar suas respectivas propriedades mec?nicas (principalmente, resist?ncia ?ltima e m?dulo el?stico), levando em conta a propriedade de anisotropia do tecido h?brido e a presen?a de descontinuidade geom?trica (furo circular conc?ntrico). No caso da descontinuidade geom?trica, foram determinados os par?metros ?ao? e ?do? correspondentes, respectivamente, aos crit?rios de falha ASC (Average Stress Criterion) e PSC (Point Stress Criterion), os quais caracterizam as dist?ncias da regi?o de concentra??o de tens?es na vizinhan?a do furo. O enfoque num?rico consistiu em analisar o comportamento de dois modelos num?ricos semi-emp?ricos propostos, simulados pelo M?todo dos Elementos Finitos (MEF) e, respectivamente, referenciados como IFA-CTPF/SF, para os grupos de corpos de prova sem furo, ou como IFA-CTPF/CF, para os grupos de corpos de prova com presen?a de furo conc?ntrico. A partir do crit?rio de falha PSC, os resultados obtidos para propriedades e par?metros averiguados, tanto sob o enfoque anal?tico quanto sob o enfoque num?rico, apresentam-se coerentemente consistentes com os dados experimentais, nas duas dire??es consideradas para solicita??o do laminado LC (dire??o fibras de carbono ou dire??o fibras kevlar); resultados an?logos, provenientes da aplica??o do crit?rio de falha ASC sob enfoque num?rico, n?o se mostraram t?o satisfat?rios em face dos dados experimentais correspondentes ou dos oriundos da avalia??o sob enfoque anal?tico. Todo o estudo do comportamento mec?nico foi com base no ensaio de tra??o uniaxial. A caracteriza??o f?sica do laminado LC foi feita mediante ensaios de Densidade Volum?trica e Calcina??o, este ?ltimo para obten??o dos teores (em termos percentuais) dos par?metros microestruturais (matriz, fibras e vazios). A an?lise da fratura mec?nica foi realizada a partir da Microscopia Eletr?nica de Varredura (MEV), com o objetivo de identificar os danos originados em suas microestruturas. / Composite materials consist of an agglutinative phase (matrix) and another (reinforcements) that provides them with sustainability and load bearing capacity. Their multiple applications, possible uses and always innovative conceptions mean they are being increasingly used in technological fields, in both research and industrial use. Matrices and reinforcements bind without fusion, conserving their particular characteristics, but providing novel properties to the new material formed for a given purpose. In this respect, the present study designed a based epoxy vinyl ester thermoset polymer resin laminate composite, reinforced with eight layers of a bidirectional hybrid fabric consisting of Kevlar fibers in the warp direction and carbon fibers in the weft direction; this composite material was denominated CL (carbon/Kevlar bidirectional hybrid fabric-based composite laminate). The mechanical behavior study of this CL laminate composite was conducted using an experimental, analytical and numerical approach with the general aim of determining its mechanical properties (primarily ultimate tensile strength and modulus of elasticity), considering the anisotropy of the hybrid fabric and the presence of geometric discontinuity (circular hole). In the event of geometric discontinuity, distances characteristics ?ao? and ?do?, corresponding to the Average Stress Criterion (ASC) and Point Stress Criterion (PSC), were determined, characterizing the extent of stress concentration around the hole. Numerical focus consists of analyzing the behavior of two proposed semiempirical models, simulated using the finite element method (FEM) and referenced respectively as HA-SFFP/H (Influence of the Concentric Hole/Anisotropy in the Stress Field and Failure Prevention), for the test specimens with concentric hole and HA-SFFP/O for the test specimens without concentric hole (original condition). The entire mechanical behavior study was based on the uniaxial tensile test. The physical characterization of the CL laminate was conducted using volumetric density and calcination tests, the latter to obtain levels (percentages) of microstructural parameters (matrix, fibers and voids). Mechanical fracture analysis was carried out using a scanning electron microscope (SEM), in order to identify microstructural damage. In general, anisotropy and the presence of a circular hole directly influenced the results. The semiempirical models proposed were satisfactory in their predictions, mainly the model based on the Point Stress Criterion. / 2018-07-23

Made available in DSpace on 2014-12-17T14:06:48Z (GMT). No. of bitstreams: 1 WersonMC.pdf: 1184207 bytes, checksum: f2f0598e463a68730749344c713c5bff (MD5) Previous issue date: 2008-02-22 / The Tungsten/copper composites are commonly used for electrical and thermal objectives like heat sinks and lectrical conductors, propitiating an excellent thermal and electrical conductivity. These properties are dependents of the composition, crystallite size and production process. The high energy milling of the powder of W-Cu produces an dispersion high and homogenization levels with crystallite size of W very small in the ductile Cu phase. This work discusses the effect of the HEM in preparation of the W-25Cu composite powders. Three techniques of powder preparation were utilized: milling the dry with powder of thick Cu, milling the dry with powder of fine Cu and milling the wet with powder of thick Cu. The form, size and composition of the particles of the powders milled were observed by scanning electron microscopy (SEM). The X-ray diffraction (XRD) was used to analyse the phases, lattice parameters, size and microstrain of the crystallite. The analyse of the crystalline structure of the W-25Cu powders milled made by Rietveld Method suggests the partial solid solubility of the constituent elements of the Cu in lattice of the W. This analyse shows too that the HEM produces the reduction high on the crystallite size and the increase in the lattice strain of both phases, this is more intense in the phase W / Os comp?sitos de Tungst?nio/Cobre (W-Cu) s?o geralmente usadas para fins el?tricos e t?rmicos como dissipadores de calor e condutores el?tricos, devido as suas excelentes propriedades de condutividades t?rmica e el?trica. Essas propriedades s?o dependentes da composi??o, do tamanho de cristalito e principalmente do processo de fabrica??o. A moagem de alta energia de p?s W-Cu produz alto n?vel de homogeneiza??o e dispers?o com cristalitos de W muito fino na fase d?ctil Cu. Este trabalho discute o efeito da MAE na prepara??o dos p?s comp?sitos W-25Cu. Tr?s t?cnicas de prepara??o dos p?s foram utilizadas: moagem a seco com p? de Cu grosso, moagem a seco com p? de Cu fino e moagem a ?mido com p? de Cu grosso. A forma, tamanho e a composi??o das part?culas dos p?s mo?dos foram observadas por microsc?pio eletr?nico de varredura (MEV). A difra??o de raios-X(DRX) foi usada para observar as fases, par?metros de rede, tamanho e microtens?o dos cristalitos. A an?lise da estrutura cristalina dos p?s mo?dos de W-25Cu feita pelo m?todo de Rietveld sugere uma solubilidade s?lida parcial dos elementos constituintes do cobre (Cu) na rede do tungst?nio (W). Essa an?lise tamb?m mostra que a MAE produz uma alta redu??o no tamanho dos cristalitos e um aumento de tens?o na rede de ambas as fases, isto ocorre com maior intensidade na fase do W