Made available in DSpace on 2014-08-20T14:30:07Z (GMT). No. of bitstreams: 1 Dissertacao_Caroline_Ely.pdf: 855676 bytes, checksum: 3b493898d992f4952a9932fd00c16707 (MD5) Previous issue date: 2011-01-01 / The aim of this project will be to investigate the influence of the addition of light and co-initiators in self-etching primers, in relation to microtensile bond strength (μTBS) and on morphological pattern of hybrid layer of an experimental adhesive system. An experimental self-etching primer will be formulated and on which will be added the initiators of polymerization, resulting in a total of 6 experimental groups: PCONTROL, PCQ, PQTX, PDPI, PBAR and PSUL. A coating adhesive resin compound by Bis-GMA, TEGDMA and HEMA will be formulated. For μTBS test, forty-eight bovine incisors will be randomized and allocate in the six groups. Vestibular enamel will be grounded to expose the superficial coronal dentin, which that will be polished wet to create a standardized smear layer with 600 grit silicon paper. After rinsing, water will be removed with a piece of absorbent paper, leaving the surface visibly dried. The prepared dentin surfaces will be etched with primer and air-dried, after coating adhesive resin will be applied and light activated. The composite resin will be inserted in two increments and will be light activated according to the manufacturer s recommendations. After storage for 24 hours, the specimens will be sectioned with a refrigerated diamond saw at lowspeed. After check normal distribuition and equal variances as assumptions to carry out parametric statistics data obtained on μTBS, will be submitted to two-way ANOVA (factor time and factor initiator of (polymerization) test to verify differences between means (p<0.05). Fractographic analysis will be performed using optical microscopy to describe failure patterns. The morphological pattern of hybrid layer will be examined by scanning electron microscopy (Shimadzu SSX550), after 24 hours and 2 years of storage, using 3 teeth for each experimental group. Teeth will be sectioned with a refrigerated diamond saw, in order to obtain 2 or 3 slices per tooth, with 2mm thickness. Restorative procedure will take place, following the same steps of sample preparation 9 for μTBS test. Then, samples will pass through a sequence of polishing with grit silicon paper and diamond pastes of different granulations. Between each stage of polishing, samples will be placed in one ultrasonic tank to complete removal of waste. After, will undertake the procedures of decalcification with solution of phosphoric acid 50%, deproteinization with sodium hypochlorite solution 2.5%, dehydration with silica at room temperature for 2 hours and coating with gold/palladium. Finally, images of hybrid layer will be observed in SEM, on 3000 and 5000 fold increas / O objetivo deste projeto será avaliar a influência da adição de iniciadores de polimerização em primer autocondicionante experimental, na resistência de união e no padrão morfológico da camada híbrida de sistemas adesivos. Será formulado um primer experimental modelo, ao qual serão adicionados fotoiniciadores e co-iniciadores, obtendo-se um total de 6 grupos experimentais: PCONTROLE, PCQ, PQTX, PDPI, PBAR e PSUL. Como adesivo de cobertura, será formulado um co-monômero constituído de Bis-GMA, TEGDMA e HEMA. Para o ensaio de resistência de união à microtração (RU) serão utilizados 48 incisivos bovinos, distribuídos aleatoriamente entre os grupos . Na face vestibular dos dentes será realizado desgaste até a exposição de dentina e, posteriormente, polimento com lixa de SiC granulação 600 para padronização da smear layer. O primer será aplicado vigorosamente sobre a dentina previamente seca com papel absorvente e após será realizada a volatilização do solvente com jato de ar. Em seguida o adesivo de cobertura será aplicado e fotoativado com um aparelho fotopolimerizador de lâmpada halógena. A restauração será confeccionada em incrementos de compósito restaurador, fotoativados de acordo com as recomendações do fabricante. Após armazenagem por 24h em água destilada a 37°C, os dentes serão seccionados em cortadeira de precisão a fim de obterem-se palitos de aproximadamente 0,5mm2 de área de secção transversal. A RU em dentina será avaliada após 24h, 1 e 2 anos de armazenagem em água destilada. Os dados obtidos serão avaliados quanto à normalidade e igualdade de variâncias como condição para utilização de análise estatística paramétrica Preenchendo os requisitos anteriores será aplicada Análise de variância segundo dois critérios (fator tempo e fator iniciador de polimerização), e teste complementar de Tukey para detectar diferenças entre médias (α=5%). Os corpos de prova fraturados a partir do ensaio de microtração serão avaliados por microscopia óptica e classificados quanto ao modo de fratura em adesiva, 7 coesiva ou mista. A análise do padrão morfológico da camada híbrida será realizada por microscopia eletrônica de varredura MEV (SSX-550, Shimadzu), após 24 horas e 2 anos de armazenagem, utilizando-se 3 dentes para cada grupo experimental. Os dentes serão seccionados em cortadeira de precisão a fim de obter-se 2 ou 3 fatias por dente, com 2,0 mm de espessura cada uma. Será realizado então o procedimento restaurador, seguindo os mesmos passos utilizados para avaliar a RU. A seguir, as amostras passarão pelo protocolo de polimento com a seqüência de lixas de SiC e, em seguida, com discos de feltro e suspensões diamantadas, em granulações decrescentes.. Após, serão realizados os procedimentos de descalcificação com solução de ácido fosfórico 50% por 5 segundos, desproteinização com solução de hipoclorito de sódio 2,5% por 10 minutos, desidratação com sílica em temperatura ambiente e metalização. Por fim, serão obtidas fotomicrografias da camada híbrida em aumento de 3000 e 5000 vezes, através de Microscopia Eletrônica de Varrredura

Ainda que quando aplicada como primer antiproteolítico a clorexidina (CHX) minimize, embora não indefinidamente, a degradação de interfaces adesivas, parece não ser capaz de tornar os valores de resistência de união (RU) à dentina erodida equivalentes àqueles à dentina normal. Talvez seja possível, porém, que sua aplicação como agente para prevenção/controle do desgaste erosivo influencie o estabelecimento de tais interfaces, já que pode inibir completamente o processo. Este estudo in vitro avaliou, pois, o papel da aplicação da CHX como agente antiproteolítico para prevenção/controle do desgaste, ou seja, da condição do substrato dentinário no tocante à erosão, ou como parte do tratamento adesivo (primer antiproteolítico), na RU do conjunto sistema adesivo condicione e lave simplificado-resina composta à dentina. Para se determinar os diferentes níveis do fator substrato dentinário, a dentina superficial oclusal de terceiros molares (n=48) foi submetida exclusivamente à ação de uma lixa de SiC (#600; 1 min), configurando-se o que se denominou dentina normal - N, ou subsequentemente tratada com solução de digluconato de CHX a 2% (60 s) e erodida por um refrigerante à base de cola, determinando-se a dentina tratada com CHX para prevenção/controle do desgaste e então erodida - CHX.E, ou apenas erodida pelo refrigerante, estabelecendo-se a dentina erodida - E. Já para se determinar os diferentes níveis do fator CHX como parte do tratamento adesivo, a dentina dos grupos N, CHX.E e E foi, então, condicionada, lavada, seca e reidratada com 1,5 ?l, respectivamente, de água destilada (controle - Nc / CHX.Ec / Ec; n=8) ou de digluconato de CHX a 2% (primer antiproteolítico - Npa / CHX.Epa / Epa; n=8). O adesivo Adper Single Bond 2 foi aplicado em todos os espécimes e a porção coronária, reconstruída com a resina Filtek Z350. Após 24 h (água destilada/37?C), os espécimes foram seccionados em palitos e imediatamente testados (?TBS; 0,5 mm/min). As superfícies fraturadas de cada palito foram analisadas com o auxílio de um microscópio digital (50x de aumento). Um dente extra para cada grupo foi tratado exatamente como os outros, mas o corante fluorescente rodamina B foi previamente adicionado ao sistema adesivo para permitir a avaliação qualitativa da interface adesiva por meio de Microscopia Confocal de Varredura a Laser. Os valores de RU obtidos foram organizados de forma a se considerar cada dente como unidade experimental e, então, os testes de Análise de Variância a 2 critérios e de Tukey foram aplicados, com nível de significância de 5%. Apenas o substrato normal, quando reidratado, após condicionamento ácido, com água destilada (controle), é que apresentou valores de RU à dentina significativamente superiores aos demais. Quanto ao padrão de fratura dos palitos testados, as falhas adesivas e mistas foram predominantes em relação às coesivas, independentemente se em dentina ou em resina. Qualitativamente, a hibridização da dentina erodida pareceu menos satisfatória que a da dentina tratada com CHX como agente antiproteolítico para prevenção/controle do desgaste e então erodida, que, por sua vez, pareceu também menos satisfatória que a da dentina normal, particularmente se reidratadas com CHX a 2% como primer antiproteolítico. Ademais, a hibridização de cada substrato, individualmente, pareceu inferior quando da aplicação da CHX a 2% como primer antiproteolítico, se comparada com a da água destilada. Conclui-se, ora, que o uso da CHX como agente para prevenção/controle do desgaste erosivo parece, contrariamente ao que se observa para essa finalidade, não interessante de modo pleno quando, do ponto de vista da resistência de união, na sequência, há que se restaurar o substrato dentinário utilizando-se sistema adesivo do tipo condicione e lave simplificado em associação a resina composta. Quando aplicada como primer antiproteolítico, ainda, a CHX pode prejudicar a adesão à dentina normal, ainda que não o faça, nem o contrário, para a dentina tratada com CHX como agente antiproteolítico para prevenção/controle do desgaste e então erodida ou tão-somente erodida. / Even if when applied as a antiproteolytic primer the chlorhexidine (CHX) minimizes, although not indefinitely, degradation of adhesive interfaces, it seems not to be able to make bond strength (BS) values to eroded dentin equivalent to those to normal dentin. It may be possible, though, that its application as an agent for the prevention/control of the erosive wear influences the establishment of such interfaces, as it can completely inhibit the process. This in vitro study evaluated, thus, the role of CHX application as an antiproteolytic agent for preventing/controlling the wear, that is, the condition of the dentin substrate with respect to erosion,or as part of the adhesive treatment (antiproteolytic primer), on BS of a simplified etch-and-rinse adhesive plus a composite resin to dentin. In order to determine the different levels of the factor dentin substrate, superficial occlusal dentin of third molars (n=48) was only ground with a SiC paper (600-grit; 1 min), what was called normal dentin - N, or subsequently treated with 2% CHX digluconate (60 s) and eroded by a regular-cola soft-drink, determining the dentin treated with CHX to prevent/control the wear and then eroded - CHX.E, or only eroded by the soft-drink, establishing the eroded dentin - E. To determine the different levels of the factor CHX as part of the adhesive treatment, dentin of N, CHX.E and E groups was then acid-etched, washed, dried and rehydrated with 1.5 ?L, respectively, of distilled water (control - Nc / CHX.Ec / Ec; n=8) or of 2% CHX (antiproteolytic primer - Nap / CHX.Eap / Eap; n=8). Adper Single Bond 2 was applied in all specimens and resin composite buildups were constructed with Filtek Z350. After 24 h (distilled water/37?C), specimens were sectioned in beams and immediately tested (?TBS; 0.5 mm/min). Fractured surfaces of each beam were observed under a digital microscope (50X magnification). An extra tooth for each group was treated just like the others, but the fluorescent dye rhodamine B was previously added to the adhesive system to allow a qualitative evaluation of the adhesive interface by means of Laser Scanning Confocal Microscopy. Obtained BS values were organized in order to consider each tooth as an experimental unit and, then, two-way ANOVA and Tukey tests were applied, with a significance level of 5%. Only the normal substrate, when rehydrated, after acid etching, with distilled water (control), is the one that presented BS values to the dentin significantly higher to the others. As for the fracture pattern of the tested beams, adhesive and mixed failures were predominant in relation to the cohesive failures, regardless of whether in dentin or in resin. Qualitatively, the hybridization of eroded dentin appeared less satisfactory than that of the dentin treated with CHX to prevent/control the wear and then eroded, which, in turn, also appeared less satisfactory than that of normal dentin, particularly if rehydrated with 2% CHX as antiproteolytic primer. In addition, the hybridization of each substrate individually appeared to be inferior for the application of the 2% CHX as antiproteolytic primer, when compared to distilled water. It is concluded, therefore, that the use of CHX as an agent for preventing/controlling the erosive wear seems, contrary to what is observed for this purpose, not fully interesting when, from the point of view of the bond strength, in the sequence, the dentin substrate must be restored using a simplified etch-and-rinse adhesive system plus a composite resin. When applied as an antiproteolytic primer, moreover, CHX may impair bonding to normal dentin, even if not doing this, nor the opposite, for the dentin treated with CHX to prevent/control the wear and then eroded or for the only eroded dentin.

Ainda que quando aplicada como primer antiproteolítico a clorexidina (CHX) minimize, embora não indefinidamente, a degradação de interfaces adesivas, parece não ser capaz de tornar os valores de resistência de união (RU) à dentina erodida equivalentes àqueles à dentina normal. Talvez seja possível, porém, que sua aplicação como agente para prevenção/controle do desgaste erosivo influencie o estabelecimento de tais interfaces, já que pode inibir completamente o processo. Este estudo in vitro avaliou, pois, o papel da aplicação da CHX como agente antiproteolítico para prevenção/controle do desgaste, ou seja, da condição do substrato dentinário no tocante à erosão, ou como parte do tratamento adesivo (primer antiproteolítico), na RU do conjunto sistema adesivo condicione e lave simplificado-resina composta à dentina. Para se determinar os diferentes níveis do fator substrato dentinário, a dentina superficial oclusal de terceiros molares (n=48) foi submetida exclusivamente à ação de uma lixa de SiC (#600; 1 min), configurando-se o que se denominou dentina normal - N, ou subsequentemente tratada com solução de digluconato de CHX a 2% (60 s) e erodida por um refrigerante à base de cola, determinando-se a dentina tratada com CHX para prevenção/controle do desgaste e então erodida - CHX.E, ou apenas erodida pelo refrigerante, estabelecendo-se a dentina erodida - E. Já para se determinar os diferentes níveis do fator CHX como parte do tratamento adesivo, a dentina dos grupos N, CHX.E e E foi, então, condicionada, lavada, seca e reidratada com 1,5 ?l, respectivamente, de água destilada (controle - Nc / CHX.Ec / Ec; n=8) ou de digluconato de CHX a 2% (primer antiproteolítico - Npa / CHX.Epa / Epa; n=8). O adesivo Adper Single Bond 2 foi aplicado em todos os espécimes e a porção coronária, reconstruída com a resina Filtek Z350. Após 24 h (água destilada/37?C), os espécimes foram seccionados em palitos e imediatamente testados (?TBS; 0,5 mm/min). As superfícies fraturadas de cada palito foram analisadas com o auxílio de um microscópio digital (50x de aumento). Um dente extra para cada grupo foi tratado exatamente como os outros, mas o corante fluorescente rodamina B foi previamente adicionado ao sistema adesivo para permitir a avaliação qualitativa da interface adesiva por meio de Microscopia Confocal de Varredura a Laser. Os valores de RU obtidos foram organizados de forma a se considerar cada dente como unidade experimental e, então, os testes de Análise de Variância a 2 critérios e de Tukey foram aplicados, com nível de significância de 5%. Apenas o substrato normal, quando reidratado, após condicionamento ácido, com água destilada (controle), é que apresentou valores de RU à dentina significativamente superiores aos demais. Quanto ao padrão de fratura dos palitos testados, as falhas adesivas e mistas foram predominantes em relação às coesivas, independentemente se em dentina ou em resina. Qualitativamente, a hibridização da dentina erodida pareceu menos satisfatória que a da dentina tratada com CHX como agente antiproteolítico para prevenção/controle do desgaste e então erodida, que, por sua vez, pareceu também menos satisfatória que a da dentina normal, particularmente se reidratadas com CHX a 2% como primer antiproteolítico. Ademais, a hibridização de cada substrato, individualmente, pareceu inferior quando da aplicação da CHX a 2% como primer antiproteolítico, se comparada com a da água destilada. Conclui-se, ora, que o uso da CHX como agente para prevenção/controle do desgaste erosivo parece, contrariamente ao que se observa para essa finalidade, não interessante de modo pleno quando, do ponto de vista da resistência de união, na sequência, há que se restaurar o substrato dentinário utilizando-se sistema adesivo do tipo condicione e lave simplificado em associação a resina composta. Quando aplicada como primer antiproteolítico, ainda, a CHX pode prejudicar a adesão à dentina normal, ainda que não o faça, nem o contrário, para a dentina tratada com CHX como agente antiproteolítico para prevenção/controle do desgaste e então erodida ou tão-somente erodida. / Even if when applied as a antiproteolytic primer the chlorhexidine (CHX) minimizes, although not indefinitely, degradation of adhesive interfaces, it seems not to be able to make bond strength (BS) values to eroded dentin equivalent to those to normal dentin. It may be possible, though, that its application as an agent for the prevention/control of the erosive wear influences the establishment of such interfaces, as it can completely inhibit the process. This in vitro study evaluated, thus, the role of CHX application as an antiproteolytic agent for preventing/controlling the wear, that is, the condition of the dentin substrate with respect to erosion,or as part of the adhesive treatment (antiproteolytic primer), on BS of a simplified etch-and-rinse adhesive plus a composite resin to dentin. In order to determine the different levels of the factor dentin substrate, superficial occlusal dentin of third molars (n=48) was only ground with a SiC paper (600-grit; 1 min), what was called normal dentin - N, or subsequently treated with 2% CHX digluconate (60 s) and eroded by a regular-cola soft-drink, determining the dentin treated with CHX to prevent/control the wear and then eroded - CHX.E, or only eroded by the soft-drink, establishing the eroded dentin - E. To determine the different levels of the factor CHX as part of the adhesive treatment, dentin of N, CHX.E and E groups was then acid-etched, washed, dried and rehydrated with 1.5 ?L, respectively, of distilled water (control - Nc / CHX.Ec / Ec; n=8) or of 2% CHX (antiproteolytic primer - Nap / CHX.Eap / Eap; n=8). Adper Single Bond 2 was applied in all specimens and resin composite buildups were constructed with Filtek Z350. After 24 h (distilled water/37?C), specimens were sectioned in beams and immediately tested (?TBS; 0.5 mm/min). Fractured surfaces of each beam were observed under a digital microscope (50X magnification). An extra tooth for each group was treated just like the others, but the fluorescent dye rhodamine B was previously added to the adhesive system to allow a qualitative evaluation of the adhesive interface by means of Laser Scanning Confocal Microscopy. Obtained BS values were organized in order to consider each tooth as an experimental unit and, then, two-way ANOVA and Tukey tests were applied, with a significance level of 5%. Only the normal substrate, when rehydrated, after acid etching, with distilled water (control), is the one that presented BS values to the dentin significantly higher to the others. As for the fracture pattern of the tested beams, adhesive and mixed failures were predominant in relation to the cohesive failures, regardless of whether in dentin or in resin. Qualitatively, the hybridization of eroded dentin appeared less satisfactory than that of the dentin treated with CHX to prevent/control the wear and then eroded, which, in turn, also appeared less satisfactory than that of normal dentin, particularly if rehydrated with 2% CHX as antiproteolytic primer. In addition, the hybridization of each substrate individually appeared to be inferior for the application of the 2% CHX as antiproteolytic primer, when compared to distilled water. It is concluded, therefore, that the use of CHX as an agent for preventing/controlling the erosive wear seems, contrary to what is observed for this purpose, not fully interesting when, from the point of view of the bond strength, in the sequence, the dentin substrate must be restored using a simplified etch-and-rinse adhesive system plus a composite resin. When applied as an antiproteolytic primer, moreover, CHX may impair bonding to normal dentin, even if not doing this, nor the opposite, for the dentin treated with CHX to prevent/control the wear and then eroded or for the only eroded dentin.

Orientador: Luís Alexandre Maffei Sartini Paulillo / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-17T23:46:46Z (GMT). No. of bitstreams: 1 SouzaJunior_EduardoJoseCarvalhode_M.pdf: 3521538 bytes, checksum: c8b050fbf4fb259c0dc4d1925121d22a (MD5) Previous issue date: 2011 / Resumo: Os objetivos deste estudo foram: a) avaliar o efeito do condicionamento seletivo do esmalte cavosurperficial e da fonte de luz LED na resistência à microtração em dentina de restaurações Classe I em compósito utilizando adesivos autocondicionantes; b) avaliar a dureza Knoop (KHN) de restaurações de cavidades Classe I em compósito utilizando adesivos autocondicionantes fotoativados com diferentes fontes de luz LED; c) Avaliar a formação de fendas antes e após ciclagem termomecânica de restaurações em compósito fotoativadas por LED e utilizando adesivos autocondicionantes em diferentes protocolos de aplicação. No experimento 1, noventa e seis cavidades Classe I foram preparadas em molares humanos, e restauradas com compósito micro-híbrido. Os espécimes foram distribuídos em 12 grupos (n=8), de acordo com a fonte de luz LED (Radii-Cal - RD, Flash Lite 1401 - FL e Ultra-Lume 5 - UL), sistema adesivo autocondicionante (Clearfil SE Bond - CSE e Clearfil S3 Bond - S3) e condicionamento seletivo do esmalte com ácido fosfórico (com e sem). Após o acabamento e polimento das restaurações as mesmas foram submetidas à fadiga termo-mecânica e os palitos para o ensaio de microtração foram obtidos da interface de união entre a parede pulpar dentinária e a restauração. Após o teste mecânico os dados foram submetidos à análise estatística (ANOVA três fatores e teste de Tukey com ?=0.05). O condicionamento seletivo do esmalte para o S3 diminuiu a resistência de união em dentina e não afetou o desempenho do CSE. Além disso, o LED de terceira geração promoveu maiores valores de resistência à microtração para o adesivo de dois passos. Para o S3 as fontes de luz promoveram resistência adesiva semelhante em dentina. No estudo 2, utilizou-se o mesmo método de preparo das amostras do primeiro estudo, formando-se 6 grupos (n=16) pela interação entre os fatores em estudo, LED (RD, FL e UL), sistema adesivo autocondicionante (CSE e S3). As parcelas subdivididas foram diferentes profundidades (superficial, média e profunda). Após a confecção das restaurações, as mesmas também foram submetidas à fadiga termo-mecânica e em seguida, seccionadas no sentido longitudinal para avaliação da KHN nas diferentes profundidades. Após análise estatística (ANOVA dois fatores com parcela subdividida e teste de Tukey com ?=0.05), observou-se que o LED de terceira geração promoveu valores de KHN semelhante aos aparelhos de pico único e que a região superficial, em geral, apresentou melhor qualidade de polimerização. No estudo 3, utilizou-se 192 terceiros molares, onde cavidades Classe I foram preparadas e restauradas com o mesmo método utilizado no primeiro estudo, 12 grupos (n=16) pela interação entre os fatores em estudo, LED (RD, FL e UL), sistema adesivo autocondicionante (CSE e S3) e condicionamento seletivo do esmalte com ácido fosfórico (com e sem), antes e após a termociclagem. Após a restauração, réplicas em resina epóxica foram confeccionadas e as margens foram analisadas em microscópio eletrônico de Varredura (MEV). Após submeter os espécimes da restauração à fadiga termo-mecânica, novamente réplicas em resina epóxica foram feitas e analisadas em MEV. Após análise estatística (Kruskal Wallis e teste de Wilcoxon pareado, ?=0.05), observou-se que o condicionamento seletivo do esmalte promoveu maior integridade marginal para o S3, mostrando ser um passo adicional eficiente na técnica de aplicação desse adesivo em restaurações Classe I em compósito. Além disso, a formação de fendas para adesivo autocondicionante de dois passos não foi influenciado pelo condicionamento ácido prévio do esmalte, nem pelo LED utilizado para fotoativação / Abstract: The aim of this work was to: a) evaluate the effect of enamel selective enamel etching and LED curing units on dentin microtensile bond strength of Class I composite restorations; b) evaluate the effect of different LED light units and self-etch adhesives on the Knoop hardness profile (KHN) of Class I composite restorations; c) evaluate the gap formation before and after thermomechanical loading of Class I composite restorations photocured by LED and using different application protocols of self-etch adhesives systems. In experiment 1, ninety-six Class I cavities were made in human molars and restored with a microhybrid composite. For the restorative procedure, teeth were assigned in 12 groups (n=8) formed by the studied factors interactions, LED curing unit (Radii-Cal - RD, Flash Lite 1401 -FL and Ultra-Lume 5 - UL), self-etch adhesives (Clearfil SE Bond - CSE and Clearfil S3 Bond - S3) and selective enamel acid etching (with and without). After finishing and polishing approach, specimens were submitted to thermo-mechanical ageing and sticks were obtained from the bonding interface between adhesive and pulpal wall which were submitted to a microtensile load in a universal testing machine. After statistical analysis, (three-way ANOVA and Tukey test with ?=0.05) it was shown that the pre-etched enamel approach for Clearfil S3 decreased dentin bond strength while it did not affect the bond performance of Clearfil SE. Thus, the polywave LED promoted higher microtensile bond strength values for the two-step adhesive. When Clearfil S3 was used, the light curing units yielded similar dentin bond strength. In the experiment 2, 96 Class I cavities were prepared in the same way as the previous experiment. Teeth were assigned to 18 groups (n=8) by the interaction among the studied factors, LED curing source (RD, FL and UL), self-etch bond system (CSE and S3), depth (superficial, medium and deep). After the restorative procedure, specimens were submitted to thermo-mechanical ageing and then sectioned in the longitudinal direction for the Knoop hardness measurement in the different depths. Data were submitted to three-way ANOVA and Tukey test with a pre-set alpha of 0.05). The results showed that the third generation LED promoted similar KHN values to the single-peak ones and the superficial surface, in general, presented greater cure quality compared to the others surface depths. In the experiment 3, 192 third molars were used and Class I preparations were restored in the same way as the first study. Specimens were assigned to 12 groups (n=16) formed by the studied factors interaction, LED (RD, FL and UL), self-etch adhesives (CSE and S3), selective enamel acid etching (with and without) and before and after thermomechanical loading. After the restoration procedure, epoxy resin replicas were made and the marginal adaptation was analyzed in a scanning electron microscope (SEM). Then specimes were submitted to thermalmechanical loading and again, epoxy resin replicas were made and analyzed by SEM. After statistical analysis (Kruskal Wallis and Wilcoxon matched-pairs signed-ranks test, with a pre-set alpha of 0.05), it was shown that selective enamel etching yielded higher marginal integrity for S3, showing to be an efficient additional step for the bonding technique of this adhesive in Class I composite restorations. Also, the two-step self-etch adhesive gap formation was not influenced by the selective enamel etching, neither by the LED curing light / Mestrado / Dentística / Mestre em Clínica Odontológica

Orientador: Marcelo Giannini / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-06T14:18:38Z (GMT). No. of bitstreams: 1 Garcia_RubensNazareno_D.pdf: 8662671 bytes, checksum: 0068fe648efbd833ec4737acd0f008f2 (MD5) Previous issue date: 2006 / Resumo: O atual conceito de união aos tecidos duros dentais é baseado na infiltração de sistemas adesivos em esmalte e dentina, no processo chamado de hibridização. Enquanto a união ao esmalte tem sido considerada um procedimento confiável devido a sua uniforme composição, a união à dentina continua sendo um desafio. O objetivo deste estudo foi avaliar e discutir os conceitos que envolvem os sistemas adesivos odontológicos e as técnicas de cimentação adesiva. O estudo compreendeu quatro avaliações que propuseram analisar: 1- a resistência de união (RU) de alguns sistemas autocondicionantes após uma semana e um ano de armazenamento em água; 2- a RU de cimentos resinosos aos compósitos utilizados na reconstrução dental; 3 e 4- a RU de técnicas de cimentação adesiva. Foram utilizados dentes bovinos nos experimentos 1, 2 e 3; e ensaios de microcisalhamento. Para o experimento 4 foram utilizados dentes humanos e o ensaio de microtração. Os resultados indicaram que: 1- entre todos adesivos testados, o adesivo autocondicionante One-Up Bond F não apresentou redução na RU após um ano; 2- a RU foi maior quando se aplicou adesivo hidrófobo entre o compósito restaurador e o cimento resinoso; 3 e 4- o uso de uma camada intermediária de resina de baixa viscosidade e fotoativação dos cimentos resinosos resultou em maiores valores de RU entre o cimento resinoso e a dentina. Os resultados sugerem que a união à dentina ainda é instável para a maioria dos sistemas adesivos; na união do cimento resinoso ao compósito restaurador, os adesivos hidrófobos são as melhores opções; e as técnicas de cimentação adesiva apresentam melhor desempenho com aplicação de uma camada intermediária de resina de baixa viscosidade e fotoativação do cimento resinoso / Abstract: The current concept of bonding to hard dental tissues is based on the infiltration of adhesive systems in enamel and dentin, in the so-called hybridization process. While the enamel bond has been considered a reliable procedure due to its uniform composition, bonding to dentin continues to present challenges. The objective of this study was to assess and discuss the concepts involving dental adhesive systems and the techniques of adhesive cementation. The study included four evaluations to determine: 1- the bond strength (BS) of some self-etching adhesive systems after one week and one year of storage in water; 2- The BS of the resin cements to composites used in dental restoration; 3 and 4- The BS of adhesive cementation techniques. Bovine teeth and micro-shear bond strength tests were used for experiments 1, 2 and 3. For experiment 4, human teeth and micro-tensile tests were used. The results indicated that: 1- among the adhesives tested, the self-etching adhesive One-Up Bond F did not show reduction in BS after one year; 2- the BS was higher when the hydrophobic bond was applied between the filling composite and the resin cement; 3 and 4- the use of an intermediary layer of low viscosity resins, and photoactivation of the resin cements, resulted in higher BS values between the resin cement and the dentin. The results suggest that bonding to dentin is still unstable for the majority of adhesive systems; in the union of the resin cement to the filling composite, hydrophobic adhesives are the best options; and the techniques of adhesive cementation present better performance with the application of an intermediate layer of low viscosity resin and photoactivation of resin cement / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários

Orientador: Regina Maria Puppin Rontani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-12T19:22:08Z (GMT). No. of bitstreams: 1 Carvalho_FabiolaGalbiattide_D.pdf: 3340202 bytes, checksum: 3dfefda6770edf12e25a625fcffd516d (MD5) Previous issue date: 2009 / Resumo: O monômero antibacteriano 12-metacriloxidodecilpiridinio de brometo (MDPB) foi incorporado, juntamente com o flúor, ao sistema adesivo Clearfil Protect Bond (CPB) para auxiliar na prevenção de cárie secundária. Desta forma, o objetivo deste estudo foi avaliar em três experimentos in vitro o efeito desses componentes na desinfecção de cavidade, durabilidade da união à dentina afetada por cárie (DAC) e prevenção de cárie secundária. No Capítulo 1, o efeito antibacteriano do MDPB foi avaliado em biofilme de S. mutans presentes na superfície de dentina a partir de quatro tempos de aplicação do primer contendo MDPB (20s, 90s, 300s e 590s). A viabilidade celular foi avaliada utilizando microscópio confocal de varredura a laser (CLSM) e contagem de unidades formadoras de colônias. Somente a partir de 300s de aplicação do primer foi verificado o efeito bactericida do MDPB contra biofilme de S. mutans na dentina. No Capítulo 2, a degradação à DAC artificial foi avaliada utilizando teste de microtração (µTB) após a aplicação dos sistemas adesivos CPB e Adper Scotchbond Multi-Purpose (SBM) e armazenamento em cultura de S. mutans por três dias e água deionizada por três meses. A presença do flúor e MDPB no sistema adesivo CPB não preveniu a degradação da união à DAC, pois não houve diferença nos valores de µTB entre CPB e SBM nos dois métodos de degradação. Assim, o meio de armazenamento dos espécimes com S. mutans por 3 dias foi tão eficaz na degradação à DAC quanto o armazenamento em água por 3 meses. No Capítulo 3, a inibição da cárie secundária por CPB e SBM foi avaliada após 5 dias de desafio cariogênico com métodos químico (gel ácido) e biológico (meio com S. mutans). A formação da zona de inibição à cárie (IZ) pelos sistemas adesivos foi avaliada por CSLM e a distribuição de cálcio e fósforo para investigar a perda mineral na dentina ao longo da interface dentina/restauração foi avaliada por análise de fluorescência por raios-x (µ-EDX). O sistema adesivo CPB produziu IZ mais espessa e menor perda mineral quando submetido ao desafio químico, mas produziu a menor espessura de IZ e a maior perda mineral quando submetido ao desafio biológico. O sistema adesivo SBM induziu valores intermediários de perda mineral e IZ frente aos dois desafios. Desta forma, o método de desenvolvimento de cárie secundária artificial e a camada híbrida criada por CPB e SBM influenciaram na inibição de cárie secundária por sistemas adesivos. Dentro das limitações deste trabalho pode-se concluir que o monômero MDPB presente no sistema adesivo CPB possuiu efeito bactericida contra biolfime de S. mutans na superfície de dentina após 300 s de sua aplicação. Além disso, este monômero não preveniu a degradação da união após armazenamento em cultura de S. mutans e água deionizada, bem como a desmineralização da dentina na interface dente/restauração após desafio cariogênico químico e biológico. / Abstract: The antibacterial monomer 12-methacryloyloxydodecylpyridinium bromide (MDPB) was incorporated with fluoride component in Clearfil Protect Bond adhesive system to help in secondary caries prevention. Thus, the present study conducted three in vitro experiments with the aim to evaluate the fluoride and MDPB effects in cavity disinfection, bonding durability on caries-affected dentin (CAD) and secondary caries prevention. In Chapter 1, the MDPB antibacterial effect was evaluate against S. mutans biofilm on dentin surface after four application times of MDPB primer (20s, 90s, 300s e 590s). The cellular viability was evaluated by confocal laser scanning microcopy (CLSM) and viable count test. MDPB had bactericidal effect against S. mutans biofilm on dentin after 300s of primer application. In Chapter 2, the artificial CAD bonding degradation was evaluated using microtensile bonding strength test (µTB) after CPB and Adper Scotchbond Multi-Purpose (SBM) adhesive systems application and storage in S. mutans culture for three days and deionized water for three months. The fluoride and MDPB in CPB adhesive system did not prevent the CAD bonding degradation because there was no statistical difference between µTB values of CPB and SBM in both degradation methods. Therefore, S. mutans culture was an effective method to produce degradation in vitro in a short period of time as 3 months of water storage. In Chapter 3, the secondary caries inhibition by CPB and SBM was evaluated after chemical (acidic gel) and biological (S. mutans culture) challenges during 5 days. The inhibition zone formation (IZ) by adhesive systems used was evaluated by CLSM. The calcium and phosphorus distribution was evaluate by X-Ray fluorescence analysis (µ-EDX) to investigate the mineral loss on dentin along dentin/restoration interface. CPB adhesive system produced the thickest IZ and lowest mineral loss when it was submitted to chemical challenge; however the same adhesive system produced the lowest value of IZ thickness and the highest mineral loss in the biological challenge. SBM adhesive system showed intermediate mineral loss and IZ thickness values in both cariogenic challenges. Thus, the artificial caries method and the hybrid layer quality of CPB and SBM affected the secondary caries inhibition by adhesive systems. Based on the findings of this study, and within the limitation of this investigation, could be concluded that the MDPB monomer in CPB adhesive system had bactericidal effect after 300 s of its application. Furthermore, this monomer did not prevent the bonding degradation after S. mutans culture and water storage, as well as the dentin demineralization at tooth/restoration interface after chemical and biological cariogenic challenges. / Doutorado / Doutor em Materiais Dentários

Orientador: Lourenço Correr Sobrinho / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-08T10:12:27Z (GMT). No. of bitstreams: 1 Alonso_RenataCamilaBruschi_M.pdf: 1462277 bytes, checksum: 2005c106fdedd696c9baa0d0a44fc8ca (MD5) Previous issue date: 2007 / Resumo: O objetivo desse estudo foi avaliar in vitro o efeito de diferentes materiais e técnicas de colagem de fragmentos na resistência ao impacto de dentes anteriores, comparando-a com a resistência à fratura dos dentes hígidos. Para isso, foram selecionados 90 incisivos inferiores bovinos recém-extraídos, com dimensões da coroa de aproximadamente 15 mm de largura mésio-distal e 25 mm de comprimento inciso-cervical. Para a obtenção de fragmentos padronizados, foi realizada secção da coroa de 80 dentes a 12 mm da borda incisal com o uso de disco diamantado em cortadeira Isomet 1000. Remanescentes dentais e fragmentos foram submetidos ao ultrassom em banho de água por 2 horas para remoção da smear layer. Em seguida, os dentes foram embutidos em tubos de PVC com resina acrílica, e o ligamento periodontal foi simulado com poliéter (Impregum Soft). Os dentes seccionados foram distribuídos em 8 grupos (n=10), segundo os materiais e a técnica de colagem de fragmento: G1 - Colagem Direta (CD) + Single Bond (SB) + Filtek Z350 Flow (FF); G2 - CD + Clearfil SE Bond (CSE) + FF; G3 - CD + SB + Rely X CRA (RX); G4 - CD + CSE + RX; G5 - Chanfro Circunferencial (CC) + SB + FF; G6 - CC + CSE + FF; G7 - CC + SB + RX; G8 -CC + CSE + RX. O chanfro circunferencial foi confeccionado após o reposicionamento do fragmento utilizando ponta diamantada esférica (#1016) e, em seguida, restaurado com compósito Filtek Z250 (A3). Todos os materiais foram aplicados de acordo com as instruções dos fabricantes. Dez dentes foram mantidos hígidos para compor o grupo controle. Em seguida, as amostras foram armazenadas em água deionizada a 37oC, durante 24h e submetidas a acabamento e polimento utilizando pontas diamantadas (#3195 F/FF) e sistema Sof-Lex. Para análise da resistência ao impacto, as amostras foram posicionadas em uma máquina universal de testes mecânicos (Instron) de modo que uma carga compressiva foi aplicada na face vestibular a 2 mm do bordo incisal com velocidade de 500 mm/min até a fratura da amostra. Os dados obtidos foram submetidos à Análise de Variância e as médias comparadas pelo teste de Ryan-Einot-Gabriel-Welsch a 5% de significância. Os resultados obtidos, em Kgf, foram, em ordem decrescente: G controle - 64,8; G7 - 43,36; G5 - 37,82; G6 - 37,44; G8 - 26,68; G1 - 26,48; G3 - 23,59; G4 - 17,55; G2 -12,42. A técnica de colagem utilizando Chanfro Circunferencial foi significativamente superior à técnica de Colagem Direta. A utilização do sistema adesivo de condicionamento ácido total Single Bond promoveu aumento significativo na resistência ao impacto quando comparado ao sistema autocondicionante Clearfil SE Bond. Não houve diferença significativa entre os agentes cimentantes Rely X e Filtek Z350 Flow. Nenhuma técnica ou material considerado individualmente foi capaz de devolver ao dente restaurado a resistência mecânica do dente hígido. Somente a associação entre técnica de colagem com Chanfro Circunferencial e sistema de união Single Bond foi capaz de devolver ao dente restaurado a resistência mecânica do dente hígido / Abstract: The objective of this in vitro study was to evaluate the effect of different materials and reattachment techniques on the resistance to impact of anterior teeth and also to compare the resistance to fracture shown by both, sound and restored anterior teeth, considering the different reattachment techniques used. Ninety fresh bovine incisors with crown dimensions of approximately 15 mm of mesiodistal width and 25 mm of incisocervical length were selected. In order to obtain standardized fragments, 80 crowns was sectioned 12 mm from the incisal edge buy means of a diamond saw in an ISOMET 1000 machine. Dental remnants and incisal fragments were submitted to ultrasonic bath for 2 hours, so as to remove smear layer. After the teeth were mounted in PVC rings and embedded in acrylic resin, the periodontal tissue was simulated using polyether (Impregum Soft). The sectioned teeth were distributed in 8 groups (n=10) according to material and reattachment technique: G1 - Direct bonding (DB) + Single Bond (SB) + Filtek Z350 Flow (FF); G2 - DB + Clearfil SE Bond (CSE) + FF; G3 - DB + SB + Rely X CRA (RX); G4 - DB + CSE + RX; G5 - Circumferential Chamfer (CC) + SB + FF; G6 - CC + CSE + FF; G7 - CC + SB + RX; G8 - CC + CSE + RX. The circumferential chamfer was prepared after the bonding of the fragment by means of a spherical diamond point (# 1016). The chamfer was filled with the restorative composite Filtek Z250 (A3). All materials were applied according to the manufacturers' instructions. Ten sound teeth were used as control group. The embedded specimens were stored for 24 hours in deionized water at 37oC and then submitted to finishing and polishing procedures using diamond points (#3195F/FF) and the Sof-Lex system. To evaluate their resistance to impact, the specimens were positioned in a universal testing machine (Instron). A compressive load was applied on the buccal surface, 2 mm from the incisal edge and at a crosshead speed of 500 mm/min, until the failure. The resulting data were submitted to ANOVA One Way and Ryan-Einot-Gabriel-Welsch Multiple Range test at 5% significance. The results (Kgf), were, in decreasing order: G control - 64.8; G7 - 43.36; G5 - 37.82; G6 - 37.44; G8 - 26.68; G1 - 26.48; G3 - 23.59; G4 - 17.55; G2 - 12.42. The fragment reattachment using the circumferential chamfer technique showed results which were significantly better than those shown by direct bonding. In addition, the use of the conventional total-etching bonding system Single Bond caused a significant increase in impact resistance when compared to the use of the self-etching bonding system Clearfil SE Bond. There was no significant difference among the luting agents (Rely X and Filtek Z350 Flow). No technique or material, when individually considered, was capable of achieving the mechanical strength of the sound teeth. Only the association of reattachment technique using circumferential chamfer with the bonding system Single Bond was capable of giving back to the restored teeth the resistance to impact shown by the sound teeth / Mestrado / Materiais Dentarios / Mestre em Materiais Dentários

Orientador: Luís Alexandre Maffei Sartini Paulillo / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-21T22:44:51Z (GMT). No. of bitstreams: 1 Humel_MariaMalerbaColombi_D.pdf: 11561780 bytes, checksum: 79e3ed8605dc03bf07a59b8bb75596c5 (MD5) Previous issue date: 2013 / Resumo: Este estudo teve como objetivo avaliar a influência de diferentes concentrações destas soluções na resistência à flexão (FS), módulo de Elasticidade (E) e grau de conversão (DC) de sistemas adesivos convencionais, e ainda, sua influência na cinética (K) e taxa de conversão (RP). Para isso foram realizados dois trabalhos experimentais, sendo que no primeiro avaliaram-se as quantidades de primer nos adesivos, e no segundo trabalho avaliou-se a influência das soluções de enxague de cavidade, água, EtOH e CHX, quando em excesso, nos sistemas adesivos. Para se avaliar as diferentes concentrações do primer residual dois adesivos foram manipulados, M1 e M2 e testados com quatro concentrações de primer: 0, 5, 10 e 15%. Já para se avaliar o excesso de água, EtOH e CHX, dois adesivos foram testados: M1, adesivo manipulado, e o adesivo comercial SBMP; diluídos com 0, 2 e 9% para cada uma das soluções. Para se avaliar as propriedades mecânicas, nos dois estudos, foram preparadas amostras a partir de moldes de silicone em forma de barras (7 x 2 x 1mm) e após armazenamento por 24h, foram testadas em máquina de ensaio mecânico para o teste de FS a uma velocidade de 0,5 mm/min. DC foi mensurado utilizando Espectroscopia Transformada Infravermelha de Fourier (FTIR). Para cinética de conversão, a polimerização em cada diluição foi monitorada por FTIR pelo tempo de 60s, sendo que a conversão foi calculada a cada dois 2s de polimerização, avaliando-se também RP. No primeiro estudo, as diferentes concentrações da diluição com primer não mostrou diferença no teste de FS entre os adesivos testados, independente da concentração avaliada. Os dois adesivos testados apresentaram redução nos valores de DC com o aumento das quantidades de primer, sendo o adesivo M2 o mais susceptível às diluições. No segundo trabalho, para as diluições com água, EtOH, independente da quantidade testada, uma redução nas propriedades mecânicas e DC puderam ser observadas. As diluições em água e CHX alteraram mais as propriedades mecânicas quando comparadas as diluições com EtOH. Para K e RP com o aumento da concentração de primer residual todos adesivos apresentaram redução quando se avaliou os gráficos de conversão. Para as diluições em água, o aumento de sua concentração levou a queda progressiva na K e as diluições com CHX apresentaram menor influência na K, com redução apenas para 9% de diluição. Porém, para as diluições em EtOH houve aumento na K e RP especialmente para o adesivo SBMP. Assim, para o primeiro estudo, os resultados sugerem que as diferentes quantidades de primer usadas na diluição do adesivo não influenciam as propriedades mecânicas dos adesivos testados, porém, interferem na sua reação química de polimerização, uma vez que a velocidade reação foi reduzida (K e RP). Por outro lado, no segundo estudo, para as soluções residuais de água, EtOH e CHX, uma diminuição nas propriedades mecânicas dos adesivos ocorreu somente quando quantidades residuais de 9% foram simuladas. No entanto, pequenas quantidades de EtOH e CHX parecem não afetar as propriedades e velocidade de reação de polimerização dos adesivos / Abstract: The present study evaluates the influence of these solutions in different concentrations on flexural strength (FS), elastic modulus (E) and degree of conversion (DC) of conventional adhesives evaluating also the kinetic of conversion (K) and rate of polymerization (RP). Two distinct experiments were plotted, the first one evaluating the primer amount diluted in adhesives, and the second experiment evaluating rinse solutions amounts like water, ethanol and chlorexidine diluted in different adhesives. For different concentrations of primer solutions, two manipulated adhesives; M1 and M2 were tested at 0, 5, 10 and 15% of dilution. For different concentrations of water, ethanol (EtOH) and chlorexidine (CHX) dilutions, two adhesives were evaluated: M1, a manipulated adhesive, and the SBMP; diluted at 0, 2 and 9% of dilutions. Both studies, for mechanical properties, specimens were obtained by silicon mold bars (7 x 2 x 1mm), and after 24h, FS were performed at Mechanical Test Machine at cross speed of 0.5 mm/min. DC were measured with a Fourier Transformed Infrared Spectroscopy (FTIR). For K test, Infrared Spectroscopy monitored each 2 seconds of conversion for 60sec of polymerization, and the RP were evaluated. The first experiment, for different concentrations of primer dilutions, the FS for all adhesives tested was not affected by primer concentrations. All adhesives tested showed a decrease for DC as increased the primer dilution, with M2 presenting as the most sensitive for primer concentration. For second experiment, for all concentrations dilution of water, EtOH and CHX, a decrease on mechanical properties and DC was noted. Water and chlorexidine seems to affect more mechanical properties when compared to EtOH results. For K and RP results, increasing primer concentration, all adhesives presented a decrease of conversion and RP. For water dilutions, increasing water concentrations on tested adhesives, a progressive decrease could be noted on K graphics. CHX dilutions presented less influence on K, with decreasing RP and K only with 9% dilution. Although, EtOH dilutions presented an improve K as the RP, especially to SBMP adhesive. The results suggested that mechanical properties were not affected regardless of the primer amount diluted on adhesives, interfering only on chemistry of polymer reaction, once reaction speedy were affected (K and RP). However, for second experiment, a decrease on mechanical properties of adhesive solutions could be noted only when extreme amounts of residual solution where diluted. Notwithstanding, at lowest concentrations, EtOH and CHX seems not interfere on K and RP of adhesives / Doutorado / Dentística / Doutora em Clínica Odontológica

Ce travail de thèse est scindé en 4 parties. La première partie est une approche originale en odontologie par modélisation de la pénétration de colorants à l'interface des matériaux pour obturation radiculaire. Les deux situations extrêmes ont été envisagées. Lorsque l'interface est remplie uniquement par de l'air à pression atmosphérique, la pénétration s'effectue par capillarité. Lorsque l'interface est remplie d'eau, la pénétration s'effectue par diffusion. Les différentes équations physiques qui régissent ces phénomènes ont été déterminées. Les différents paramètres d'influence ont été quantifiés. La seconde partie et la troisième partie est une revue de littérature critique concernant l'influence de l'humidité relative et de la température du milieu buccal sur l'adhérence et l'étanchéité des matériaux adhésifs pour obturation coronaire. Une corrélation a été recherchée entre les études de laboratoire et les études cliniques. La quatrième partie est la mise au point d'un modèle permettant d'évaluer la pénétration de l'eau liquide et de l'eau gazeuse à la surface des matériaux adhésifs utilisés en odontologie. L'analyse de surface est réalisée par Spectroscopie Raman et le degré de conversion de ces résines méthacryliques est quantifié. La couche d'inhibition par l'oxygène de l'air est caractérisée en épaisseur et en degré de conversion. Une comparaison est effectuée entre les composites d'obturation, les composites flow et différents systèmes adhésifs amélo-dentinaires. / This thesis is divided into 4 partsThe first part is an original approach in dentistry by modeling the penetration of dyes at the interface of root filling materials. The two extreme situations were considered. When the interface is filled only with air at atmospheric pressure, the penetration is by capillary action. When the interface is filled with water, the penetration is by diffusion. The different physical equations governing these phenomena have been determined. The influence of the various parameters were quantified. The second part and third part are a review of critical literature on the influence of relative humidity and temperature of the oral environment on adhesion and sealing material for sealing coronary adhesives. A correlation was sought between laboratory studies and clinical trials.The fourth part is the development of a model to assess the penetration of liquid water and water vapor on the surface of the adhesive materials used in dentistry. Surface analysis is carried out by Raman spectroscopy and the degree of conversion of the methacrylate resins is quantified. Layer inhibition by oxygen is characterized by thickness and degree of conversion. A comparison is made between the composite filling, the composite flow and various adhesive systems enamel-dentin.

<p>U savremenoj restaurativnoj stomatologiji dentalni kompoziti su materijal izbora za rekonstrukciju izgubljenog čvrstog zubnog tkiva. Kako je u kliničkoj praksi primećeno, pozitivna svojstva svetlosno-aktiviranih dentalnih kompozita su ugrožena pojavom polimerizacione kontrakcije kompozitnih ispuna tokom polimerizacije. Naime, tokom svetlosne polimerizacije usled konverzije molekula monomera u dugačke izukr&scaron;tane lance polimera, razvija se napon na adhezivnom spoju kompozitnog ispuna i zida kaviteta. Kada vrednost napona nadma&scaron;i jačinu adhezivne veze kompozita i zida kaviteta, formira se marginalna mikropukotina praćena kliničkim manifestacijama u vidu postoperativne osetljivosti, marginalne diskoloracije ispuna, razvoja sekundarnog karijesa i sledstvenih ireverzibilnih promena pulpe zuba. Cilj istraživanja je bio da se uporedi uticaj primene različitih tehnika postavljanja i svetlosne polimerizacije na marginalnu adaptaciju kompozitnih ispuna. Materijal i metode: Ispitivanje marginalne adaptacije kompozitnih ispuna urađeno je u dentinskim kavitetima, na bukalnim i oralnim povr&scaron;inama humanih trećih molara u laboratorijskim uslovima. Oralni i bukalni deo krunice zuba je bru&scaron;en dijamantskim diskom uz stalno hlađenje radnog polja vodenim mlazom, kako bi se izložila ravna dentinska povr&scaron;ina promera 4x4 mm. Standardizovani cilindrični dentinski kaviteti, dimenzija 3x3 mm, preparisani su dijamantskim cilindričnim svrdlima uz obilno hlađenje radnog polja mlazom vode. Eksperimentalni deo doktorske teze, imajući u vidu postavljeni cilj istraživanja, podeljen je u dva dela. Prvi deo je obuhvatio ukupno 80 dentinskih kaviteta u koje je postavljen isti kompozitni sistem (Adper Single Bond Plus-Filtek Ultimate Flowable), različitim tehnikama postavljanja: u jednom sloju-bulk tehnikom,&nbsp; inkrementalnom tehnikom, prethodno zagrejani kompoziti i eliminisanjem jedinstvene tačke stresa-postavljanjem pin-a. Za svetlosnu polimerizaciju kompozita primenjene su dve tehnike, kontinuirana i diskontinuirana, odnosno polimerizacija sa prekidom od 10 sekundi (dark interval), nakon inicijalnog perioda prosvetljavanja. Drugi deo istraživanja je obuhvatio 20 istovetnih dentinskih kaviteta u kojima su postavljeni bulk-fill kompozitni sistemi (Filtek Bulk Fill Flowable i SDR) uz kontinuiranu svetlosnu polimerizaciju, prema uputstvu proizvođača. Nakon poliranja ispuna, zubi sa postavljenim ispunima svih grupa su čuvani u uslovima 100 % vlažnosti u trajanju od 24 časa u cilju prevencije dehidratacije. Za evaluaciju marginalne adaptacije kori&scaron;ćena je analiza epoksi replika adhezivnog spoja kompozitnog ispuna i dentina skening elektonskom mikroskopijom (SEM). Naime, nakon uzimanja otiska ispuna i okolnog dentina polivinilsiloksanom izrazito niske viskoznosti (Ghenesyl, Super Light Body, Lascod, Florence, Italy), izlivene su replike u epoksi smoli koje su pripremljene za SEM analizu (Jeol, JSM-6460 Low Vacuum, Tokyo, Japan). Dužina marginalne pukotine je izmerena u mikrometrima pomoću ImageJ računarskog programa (National Institute of Health, Bethesda, USA) i prikazana procentualno u odnosu na ukupnu dužinu marginalnog spoja ispun-dentin. Međusobno su upoređeni rezultati marginalne adaptacije različitih tehnika postavljanja i polimerizacije kompozitnih ispuna kao i rezultati marginalne adaptacije različitih kompozita postavljenih bulk tehnikom i polimerizovanih kontinuirano. Statističke razlike su obrađivane primenom ne-parametrijskog Mann-Whitney U-testa. Rezultati: Analizom numeričkih rezultata utvrđen je statistički značajno vi&scaron;i kvalitet marginalne adaptacije kada su kompozitni sistemi postavljeni u kavitete eliminisanjem jedinstvene tačke stresa-postavljanjem pin-a i diskontinuirano polimerizovani, u odnosu na ostale ispitane tehnike postavljanja. Statistčki značajno niži kvalitet marginalne adaptacije utvrđen je u grupi ispuna postavljenih uz prethodno zagrevanje i diskontinuirano polimerizovanih. Nisu dobijene statistički značajne razlike u kvalitetu marginalne adaptacije kompozitnih ispuna postavljenih različitim tehnikama u dentinske kavitete, uz istovetni, kontinuirani režim svetlosne polimerizacije. Nisu dobijene statistički značajne razlike u kvalitetu marginalne adaptacije između kompozitnih ispuna postavljenih istom tehnikom, uz različit režim svetlosne polimerizacije. Nisu dobijene statistički značajne razlike u vrednostima marginalne adaptacije između dva ispitana bulk-fill kompozitna sistema. Takođe, ni njihovim poređenjem sa vrednostima marginalne adaptacije kompozitnih ispuna postavljenih bulk tehnikom i polimerizovanih kontinuirano nisu dobijene statistički značajne razlike. Zaključak: Tehnika postavljanja i polimerizacije značajno utiče na kvalitet marginalne adaptacije kompozitnih ispuna u dentinskim kavitetima. Novi proizvod na trži&scaron;tu ne znači uvek i bolja svojstva materijala u pogledu kvaliteta marginalne adaptacije.</p> / <p>In contemporary restorative dentistry, dental composites become material of choice for reconstruction of lost tooth structure. In clinical practice it is noticed that positive properties of light-activated composites are compromised by polymerization shrinkage appearance during polymerization. The conversion of monomer molecules into polymer network is accompanied by stress transmitting to the adhesive bond what leads to the formation of microgap with clinical symptoms such as postoperative sensitivity, marginal discoloration, secondary caries and pulp pathology. The aim of this study was to compare the influence of different placing and light polymerization techniques on marginal adaptation of composite restorations. Material and Methods Examination of marginal adaptation of composites was done in dentin cavities, prepared on the buccal and oral surfaces of human third molars in laboratory conditions. The buccal and oral enamel was ground using model trimmer under running water to expose a flat dentin surface area dimension 4x4mm. Standardized cylindrical cavities (3 mm diameter, 3 mm deep) with all dentin margins were prepared using diamond cylindrical burs with copious water cooling of the working field. Taking into account the goal of this study, research was consisted of two parts. First part included 80 dentin cavities with composite system (Adper Single Bond Plus-Filtek Ultimate Flowable) placed using different placing techniques: bulk, incremental, preheated composite and by elimination of singular stress point-with pin. There were applied two light-activation techniques: continuous (40 seconds) and discontinuous (2 seconds of activation, followed by 10 seconds of dark interval, and then the polymerization is set continuously). Second part of this study included 20 the same manner prepared dentin cavities with bulk-fill composites (Filtek Bulk Fill Flowable i SDR) placed and continuously polymerized, according to the manufactures instructions. After polishing, the restored teeth were stored in a container with 100% relative humidity for 24 h to prevent dehydration. Evaluation of marginal adaptation was done using SEM analysis of replicas. After making impressions with low viscosity polyvinyl siloxane material (Ghenesyl, Super Light Body, Lascod, Florence, Italy), epoxy resin replicas were prepared for SEM analysis (Jeol, JSM-6460 Low Vacuum, Tokyo, Japan). The length of marginal gap was measured with ImageJ software (National Institute of Health, Bethesda, USA) and shown in percentage relative to total length of the margin composite/dentin. Results of marginal adaptation were compared according to application of different placing and polymerization techniques and also results of marginal adaptation of different composites bulk placed and continuously polymerized. Statistical differences were calculated using the non-parametric Mann-Whitney U-test. Results: With statistical significance there was better quality of marginal adaptation when composite was placed with pin in order to eliminate singular stress point and discontinuously polymerized, compared to other applied placing and polymerization techniques. Contrary, there was significantly higher percentage of marginal gap obtained when using pre-heated, discontinuous polymerized composites. Marginal adaptation of composite materials placed in dentin cavities using different techniques and same, continuously polymerization technique didn&rsquo;t show statistically different results. Marginal adaptation of composite materials placed in dentin cavities using same technique and different, continuously or discontinuously polymerization technique didn&rsquo;t show statistically different results. Marginal adaptation of two &ldquo;bulk-fill&rdquo; composite materials didn&rsquo;t show statistically different results. Also, compared to composites placed using bulk technique and polymerized continuously, their lower values of marginal adaptation didn&rsquo;t show significant difference. Conclusion: Placing and polymerization techniques have significant influence on the quality of marginal adaptation of composite restorations in dentin cavities. New product on the market doesn&rsquo;t always mean better marginal adaptation properties.</p>