Resumo: Os espinélios compreendem um grande grupo de compostos com aplicações tecnológicas, sendo que tais aplicações são, fundamentalmente, por sua capacidade de acomodar diferentes cátions em sua estrutura cristalina e essas propriedades estão diretamente correlacionadas ao método de preparação. Neste trabalho as ferritas...(Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The spinels include a great group of composites with technological applications, being that such applications are, basically, for its capacity to accommodate different cations in its crystalline structure and these properties directly are correlated to the preparation method. In this work the ferrites...(Complete abstract, click electronic address below) / Orientador: Carlos de Oliveira Paiva Santos / Coorientador: Lucianna da Gama F. Vieira / Banca: Elisabete Inácio Santiago / Banca: Paulo Roberto Bueno / Mestre

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / In this work, zinc ferrite oxide was performed (ZnFe2O4) was synthesized by the solvothermal conventional method and the microwave-assisted solvothermal route. The influence of different synthesis as well as their variables on the physical properties of the material were investigated. The powders were characterized by X-ray diffraction (XRD), infrared spectroscopy (FTIR), nitrogen adsorption/desorption measurements by the Brunauer-Emmett-Teller method (BET), and atomic force microscopy (AFM). The produced ferrite was used as catalyst and its activity was investigated in the photo-Fenton reaction for the degradation of textile organic dye (Procion Red H-E7b) under visible light irradiation. In the experiments, different process variables such as dye and hydrogen peroxide concentrations, pH and reaction time were analyzed. The rate constants for the photo-Fenton reactions were determined for both materials prepared by different routes. The synthesis results demonstrated the formation of particles with different physical properties such as surface area, pore volume and size. The experiments of photo-Fenton reaction indicated that the materials prepared in this work present satisfactory activity for the degradation of organic pollutant, 97% de decolorization and 60% de mineralization, in aqueous solution. All studied variables of the reaction process significantly influenced on the catalytic process. / Neste trabalho, foi realizada a síntese do óxido ferrita de zinco (ZnFe2O4) pelo método solvotérmico convencional e pela rota solvotérmica assistida por microondas. A influência das diferentes rotas de síntese, bem como de suas variáveis de síntese sobre as propriedades físicas do material foi investigada. Os pós obtidos foram caracterizados por difração de raios-X (DRX), espectroscopia no infravermelho (FTIR), medições de adsorção-dessorção de nitrogênio pelo método Brunauer-Emmett-Teller (BET), e microscopia de força atômica (MFA). A ferrita produzida foi usada como catalisador e sua atividade foi investigada na reação de foto-Fenton para a degradação de um corante orgânico têxtil (Vermelho Procion H-E7B) sob irradiação de luz visível. Nos experimentos, foram analisadas diferentes variáveis de processo, tais como concentrações de corante e peróxido de hidrogênio, pH e tempo. As constantes de velocidade das reações de foto-Fenton foram determinadas para ambos os materiais preparados pelas diferentes rotas. Os resultados das sínteses demonstraram a obtenção de partículas com diferentes propriedades físicas, tais como área superficial, volume e tamanho de poros. Os testes da reação foto-Fenton indicaram que o material preparado neste trabalho apresenta satisfatória atividade para a degradação do poluente orgânico, até 97% de remoção de cor e 60% de mineralização, em solução aquosa. Todas as variáveis do processo reacional estudadas influenciaram significativamente no processo catalítico.

Made available in DSpace on 2014-06-11T19:24:49Z (GMT). No. of bitstreams: 0 Previous issue date: 2006-01-20Bitstream added on 2014-06-13T19:31:54Z : No. of bitstreams: 1 goes_ms_me_bauru_prot.pdf: 10083876 bytes, checksum: 94a71b64f0fd1aecca45156ef778d101 (MD5) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / Os espinélios compreendem um grande grupo de compostos com aplicações tecnológicas, sendo que tais aplicações são, fundamentalmente, por sua capacidade de acomodar diferentes cátions em sua estrutura cristalina e essas propriedades estão diretamente correlacionadas ao método de preparação. Neste trabalho as ferritas... / The spinels include a great group of composites with technological applications, being that such applications are, basically, for its capacity to accommodate different cations in its crystalline structure and these properties directly are correlated to the preparation method. In this work the ferrites...(Complete abstract, click electronic address below)

Made available in DSpace on 2015-03-03T15:15:26Z (GMT). No. of bitstreams: 1 BrunoFA_DISSERT.pdf: 1242758 bytes, checksum: 3fd41c76d37384c7bc0008cfd31e4a64 (MD5) Previous issue date: 2011-08-05 / Conselho Nacional de Desenvolvimento Cient?fico e Tecnol?gico / The calcium ferrite (Ca2Fe2O5) has a perovskite-type structure with oxygen deficiency and is used as a chemical catalyst. With the advent of nanoscience and nanotechnology, methods of preparation, physical and chemical characterizations, and the technological applications of nanoparticles have attracted great scientific interest. Calcium nanostructured ferrites were produced via high-energy milling, with subsequent heat treatment. The milling products were characterized by X-ray diffraction, magnetization and M?ssbauer spectroscopy. Samples of the type Ca2Fe2O5 were obtained from the CaCO3 and Fe2O3 powder precursors, which were mixed stoichiometrically and milled for 10h and thermally treated at 700?C, 900?C and 1100?C. The M?ssbauer spectra of the treated samples were adjusted three subespectros: calcium ferrite (octahedral and tetrahedral sites) and a paramagnetic component, related to very small particles of calcium ferrite, which are in a superparamagnetic state. For samples beats in an atmosphere of methyl alcohol, there is a significant increase in area associated with the paramagnetic component. Hysteresis curves obtained are characteristic of a weak ferromagnetic-like material / A ferrita de c?lcio (Ca2Fe2O5) possui uma estrutura do tipo perovskita com defici?ncia de oxig?nio e ? utilizada como catalisador qu?mico. Com o advento da nanoci?ncia e da nanotecnologia, os m?todos de prepara??o, as caracteriza??es f?sicas e qu?micas, e as aplica??es tecnol?gicas de nanopart?culas t?m despertado grande interesse cient?fico. Ferritas de c?lcio nanoestruturadas foram produzidas via moagem de alta-energia, com subsequente tratamento t?rmico. Os produtos da moagem foram caracterizados por difra??o de raios X, magnetiza??o e espectroscopia M?ssbauer. Amostras do tipo Ca2Fe2O5 foram obtidas a partir dos p?s-precursores Fe2O3 e CaCO3, os quais foram estequiometricamente misturados e mo?dos por 10h e tratados termicamente a 700 C, 900 C e 1100 C. Os espectros M?ssbauer das amostras tratadas foram ajustados com tr?s subespectros que correspondem ? ferrita de c?lcio (s?tios octaedrais e tetraedrais) e a uma componente paramagn?tica, relacionada com part?culas muito pequenas da ferrita de c?lcio, as quais est?o em estado superparamagn?tico. Para as amostras batidas em atmosfera de ?lcool met?lico, observa-se um aumento significativo da ?rea associada ? componente paramagn?tica. As curvas de histerese obtidas s?o caracter?sticas de um material antiferromagn?tico com uma fraca componente ferromagn?tica.

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2016-07-20T22:04:59Z No. of bitstreams: 1 MoacirBispoRamos_TESE.pdf: 16232608 bytes, checksum: 452eef16e8cb0bb6456bb9da73f46508 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2016-07-21T21:33:32Z (GMT) No. of bitstreams: 1 MoacirBispoRamos_TESE.pdf: 16232608 bytes, checksum: 452eef16e8cb0bb6456bb9da73f46508 (MD5) / Made available in DSpace on 2016-07-21T21:33:32Z (GMT). No. of bitstreams: 1 MoacirBispoRamos_TESE.pdf: 16232608 bytes, checksum: 452eef16e8cb0bb6456bb9da73f46508 (MD5) Previous issue date: 2015-12-07 / O presente trabalho prop?e a modifica??o do revestimento de eletrodos de baixo hidrog?nio, propiciando uma alternativa para execu??o de soldagem com o AWS E-7018 sem precisar resseca-los, reduzindo por conseguinte os custos financeiros e o tempo de fabrica??o de soldas estruturais de alta resist?ncia. As soldas deste estudo foram produzidas a partir de eletrodos com revestimento b?sico (higrosc?picos) - processo manual - pintados com tinta spray de alum?nio para altas temperaturas ou revestidos com filmes finos de PVC e de papel alum?nio (99,9%), comumente utilizados para prote??o de alimentos. A premissa b?sica ?, que estabelecendo uma barreira entre a atmosfera e o revestimento do eletrodo, poder-se-? diminuir os efeitos da alta higroscopicidade apresentada pelo revestimento, minimizando assim, a principal fonte de fornecimento de hidrog?nio ? po?a de fus?o durante a soldagem, tamb?m ? esperado, que a adi??o de novos materiais no revestimento ? po?a de fus?o, provoque altera??es metal?rgicas no metal depositado e consequentemente altera??es nas propriedades mec?nicas. Mensurar o hidrog?nio dissolvido no metal depositado ap?s soldado com os eletrodos modificados, avaliar a influencia dessas modifica??es nas microestruturas produzidas, nas propriedades mec?nicas da solda resultante e comparar esses resultados obtidos com procedimentos de soldagem padr?o normatizados e com os novos eletrodos imperme?veis recentemente desenvolvidos, balizou o estudo. Os resultados obtidos, na maioria das amostras soldadas com eletrodos modificados, apresentaram aumento significativo da resist?ncia mec?nica e de tenacidade, justificados pelo aumento percentual de ferrita acicular no metal depositado, sem, contudo, eleva??o significativa da dureza, quando comparados com a soldagem com eletrodo AWS E-7018 da forma tradicional. O hidrog?nio difus?vel nos eletrodos modificados manteve-se dentro do estabelecido pelos c?digos internacionais. / This paper suggests modifications in coating of electrodes providing an alternative for execution of welding with low hydrogen electrode AWS E7018 without having to dry it, reducing thus the cost and time of manufacturing of high resistance welds. The welds in this research were developed with basic coated electrodes (hygroscopic) ? SMAW process ? externally painted with aluminum spray paint for high temperatures or wrapped with thin plastic films (PVC) and aluminum foil films used commonly for food protection. The basic premise is that establishing a barrier between the atmosphere and the electrode coating could reduce the effects of high hygroscopicity presented by coatings of low hydrogen, minimizing this way the main source of supply of hydrogen to the fusion pool during welding. It is also expected that the addition of new materials from the electrode coating to the fusion pool would induce metallurgical changes in the deposited metal and, as a consequence, modifications in its mechanical properties. This research dealt with measuring the dissolved hydrogen in the deposited metal after welding with modified electrodes, evaluating the influence of these changes in the produced microstructures and in the mechanical properties of the resulting weld, and comparing the obtained results with the standard welding procedures and with the recently developed waterproof electrodes. The results obtained in most samples welded with modified electrodes showed increased mechanical resistance and increased tenacity due to the increased percentage of acicular ferrite in metal deposited without significant elevation of hardness, when compared with the traditional welding with AWS E7018 electrode and with ELBR?S BRH4R waterproof electrode. The diffusing hydrogen measured in the modified electrodes was kept inside the parameters defined by international codes.

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2018-02-15T11:17:50Z No. of bitstreams: 1 CiceroLeonardoPereiraDeSouza_DISSERT.pdf: 12093980 bytes, checksum: 07b7fe22cb40d5bdd02b643fb06ab78a (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2018-02-16T11:10:32Z (GMT) No. of bitstreams: 1 CiceroLeonardoPereiraDeSouza_DISSERT.pdf: 12093980 bytes, checksum: 07b7fe22cb40d5bdd02b643fb06ab78a (MD5) / Made available in DSpace on 2018-02-16T11:10:32Z (GMT). No. of bitstreams: 1 CiceroLeonardoPereiraDeSouza_DISSERT.pdf: 12093980 bytes, checksum: 07b7fe22cb40d5bdd02b643fb06ab78a (MD5) Previous issue date: 2017-03-10 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior (CAPES) / A soldagem a arco el?trico por eletrodo revestido (SMAW) ? uma das mais antigas t?cnicas de soldagem e a primeira a ser utilizada industrialmente em grande escala. Durante o s?culo XX a soldagem SMAW foi a mais usada como t?cnica de uni?o permanente de metais, sendo at? hoje, mesmo com coexist?ncia de diversas outras t?cnicas, uma das que possuem maior utiliza??o no mercado brasileiro. Nesse tipo de soldagem uma das maiores preocupa??es ? o cuidado no armazenamento do eletrodo, pois o mesmo n?o pode ficar exposto a atmosfera ambiente, j? que absorveria umidade, que ? danoso para a qualidade da solda. A umidade introduz na zona fundida o hidrog?nio que pode levar ao surgimento de trincas a frio. A solu??o normalmente usada ? a da ressecagem em temperaturas at? 450? C, acompanhada de armazenamento em estufas, pr?tica que gera custos adicionais para um projeto de fabrica??o. Nesse contexto o presente trabalho teve a inten??o de caracterizar a zona fundida de soldas feitas com eletrodos revestidos E7018 encobertos com filmes de alum?nio e PVC, aplicados com o intuito de resguarda-los contra a umidade ambiente, diminuindo custos e tempo com secagem, tamb?m variando o valor de aporte t?rmico utilizado durante a soldagem. Essa atual investiga??o d? continuidade ? pesquisa recente sobre a influ?ncia de tais filmes protetores na composi??o e, em especial, na microestrutura do metal de solda depositado, onde a quantifica??o dos constituintes e caracteriza??o microestrutural ocorreu atrav?s de um software para avalia??o de imagens. No presente caso, com a utiliza??o de um microsc?pio com emiss?o de campo, MEV-FEG, foram obtidas imagens com elevado contraste, que permitiram um levantamento detalhado dos tipos de constituintes presentes, assim como uma an?lise mais precisa de sua morfologia. Em particular foi poss?vel avaliar quantitativamente o efeito dos filmes protetores no tamanho de gr?o e na raz?o de aspecto do microconstituinte AF (ferrita acicular). Com base numa revis?o da literatura ? apresentada uma an?lise cr?tica acerca dos par?metros que tiveram maior relev?ncia na forma??o da microestrutura final e nas propriedades mec?nicas obtidas. Os resultados conduziram a constata??o de que para maiores valores de aporte t?rmico a microestrutura, em especial a ferrita acicular, tende a ser mais grosseira. Com a utiliza??o dos revestimentos de PVC e tinta de alum?nio obteve-se uma leve diminui??o nessa granulometria, j? que a microestrutura apresentou-se mais refinada do que com os eletrodos de refer?ncia (E7018 puro e BRH4R). / The shield metal arc welding (SMAW) is one of the oldest welding processes and the first one to be used in large industrial scale. During the XX century the SMAW was the most applied process for metal joining, remaining until nowadays as one of the most used in the Brazilian market. In this kind of welding one of the biggest problems is to avoid the hydrogen induced cold cracking, what imposes rigid requirements in the storing of the weld consumables. In order to avoid the humidity absorption, the consumables must be dried out in special ovens at temperatures in the order of 450 C, what implies in additional and higher manufacturing costs. In this context a recent research suggested modifications in coating of electrodes providing an alternative for execution of welding with low hydrogen electrode AWS E7018 without having to dry it, The welds were developed with basic coated electrodes (hygroscopic) externally painted with aluminum spray paint for high temperatures or wrapped with thin plastic films (PVC) and aluminum foil films. The induced metallurgical changes in the deposited metal, associated with the addition of new materials to the electrode coating, were investigated, wereby the microconstituents in the fusion zone were quantified using a software for image analysis. In the actual work, with the use of a field emission microscope, MEV-FEG, high contrast images could be obtained, this allowed a detailed characterization of the various microconstituents and a more precise description of their morphology. In special it was possible to evaluate the influence of the protective films in the grain size and aspect ratio of the microconstituent AF (acicular ferrite). On base of a literature review a critical analysis is presented, that embraces the effect of the more relevant parameters on the final microstructure and resulting mechanical properties. The results showed that for higher values of heat input the microstructure, especially the acicular ferrite, tends to be coarser. With the use of PVC coatings and aluminum paint, a slight reduction was achieved in this granulometry, since the microstructure was more refined than with reference electrodes (E7018 pure and BRH4R).

Submitted by Marlene Santos (marlene.bc.ufg@gmail.com) on 2018-08-08T19:44:23Z No. of bitstreams: 2 Tese - Nícholas Zufelato - 2017.pdf: 11515357 bytes, checksum: 7bb562f8d99c81648650d6ed80ce19bb (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Approved for entry into archive by Luciana Ferreira (lucgeral@gmail.com) on 2018-08-09T11:55:07Z (GMT) No. of bitstreams: 2 Tese - Nícholas Zufelato - 2017.pdf: 11515357 bytes, checksum: 7bb562f8d99c81648650d6ed80ce19bb (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Made available in DSpace on 2018-08-09T11:55:07Z (GMT). No. of bitstreams: 2 Tese - Nícholas Zufelato - 2017.pdf: 11515357 bytes, checksum: 7bb562f8d99c81648650d6ed80ce19bb (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Previous issue date: 2018-02-22 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / In this work, we developed a multifunctional nanocarrier that has diagnostics and therapeutic applications in oncology, and evaluated the magnetothermal efficiency (SLP) properties in a comparative manner with respect to magnetic fluids. The nanocarrier consists of Mn-ferrite magnetic nanoparticles, a near-infrared fluorescent molecule IR-780, that are surface-coated with albumin proteins (BSA). The samples were characterized by dynamic light scattering (DLS), electron microscopy (TEM and MEV-FEG), vibrating sample magnetometer (VSM), fluorescence molecular tomography (FMT). FMT data proved the coupling of IR-780 to the protein allowing the fabrication of a magnetofluorescent nanostructure. Magnetic hyperthermia data as function of field amplitude (60-200 Oe) and frequency (170-990 kHz) were obtained for all samples containing the same magnetic particle volume fraction in the liquid carrier, but with distinct agregate sizes. The sizes were controlled by tuning the ionic force, and monitored experimentally using DLS. Magnetization curves revealed a (quasi-static) superparamagneticlike behavior, and was used to extract the particle concentration. The hyperthermia efficiency SLP of the magnetic fluids decreased increasing the hidrodynamic diameter. On the contrary, the nanocarrier showed a maximum of SLP, that can be optimized for hyperthermia and is more efficient than the ferrofluid. SLP data as function of frequency revealed a relaxation time of the order of 10-7 s and an equilibrium susceptibility lower than the Langevin value. A theoretical analysis of SLP at the linear responde regime was developed taking into account the dipolar interaction of nanoparticles organized in distinct arrangements. In magnetic fluids we considered a linear chain using the longitudinal configuration (anisotropy axis aligned), while for the nanocarriers we considered spherical agregates where the anisotropy axis of the nanoparticles are arranged randomly. The theoretical analysis indicate that the relaxation time cannot be explained by brownian relaxation or the Néel relaxation of single particle (even considering the dipolar effect). But instead, a mechanism of collective relaxation, mediated by dipolar interaction, is responsible for heat generation. It also indicates that only a fraction of agregates in the colloid is responsible for heating. In addition, the theoretical model revealed the existence of a transition from single particle relaxation to collective relaxation only if the dipolar interaction for the aggregate is higher than a critical value, which depends on material parameters, as for instance anisotropy field and saturation magnetization. Indeed, the model indicates that collective states are more easily achieved on soft magnets, and therefore suggests enhanced magnetothermal properties for this kind of materials. / Neste trabalho desenvolvemos um nanocarreador multifuncional, que possui aplicações diagnósticas e terapêuticas para tratamento oncológico, e avaliamos sua eficiência magnetotérmica (SLP) de forma comparativa com fluidos magnéticos. O nanocompósito contém nanopartículas magnéticas à base de ferrita de manganês, molécula fluorescente na faixa do infravermelho próximo IR-780, sendo recobertas por proteínas de albumina (BSA). As amostras foram caracterizadas por diversas técnicas experimentais, entre elas: espalhamento dinâmico de luz (DLS), microscopia eletrônica (TEM e MEV-FEG), magnetometria de amostra vibrante (VSM), tomografia por fluorescência molecular (FMT). Dados de FMT provaram o acoplamento do IR-780 à proteína e a construção de nanoestrutura magnetofluorescente. Dados de hipertermia magnética em função da amplitude do campo magnético (60-200 Oe) e frequência (170-990 kHz) foram obtidos para diversas amostras contendo a mesma fração de partículas magnéticas, mas tamanho de agregados distintos. O tamanho dos agregados foi controlado variando a força iônica, e monitorados experimentalmente por DLS. Curvas de VSM revelaram comportamento tipo superparamagnético (quasi-estático) e foram usadas para determinar a concentração de partículas. A eficiência magnetotérmica (SLP) revelou, para os fluidos magnéticos, que o SLP diminui aumentando o diâmetro hidrodinâmico. Ao contrário, no nanocarreador, o SLP apresentou um máximo indicando uma hipertermiaotimizada e mais eficiente que o fluido magnético. Os dados de SLP em função da frequência revelaram um tempo de relaxação da ordem de 10-7 s e susceptibilidade de equilíbrio menor que a de Langevin. Aavaliação teórica do SLP foi feita no regime da teoria de resposta linear e baseou-se no cálculo do efeito dipolar de nanopartículas organizadas de forma distinta. No caso do fluido magnético cadeias lineares na configuração longitudinal, enquanto os nanocarreadores consistiram de agregados esféricos com eixos de anisotropia organizados de forma randômica. A análise teórica indicou que o tempo de relaxação não pode ser explicado pela relaxação browniana, tão pouco por uma relaxação de Néel de partícula simples (mesmo considerando efeito dipolar). De fato, demonstramos teoricamente que o mecanismo de relaxação coletivo, mediado pela interação dipolar, é responsável pela geração de calor. A análise indica ainda que somente uma fração de partículas dos colóides, formando agregados específicos, é responsável pelo aquecimento.O modelo teórico revelou que existe uma transição entre o regime de relaxação de partícula isolada (mesmo interagente) para o regime coletivo apenas se a interação dipolar da configuração do agregado magnético for maior que um valor crítico, o qual depende de parâmetros como campo de anisotropia e magnetização de saturação das nanopartículas. Tal teoria indica que a transição ocorre mais facilmente para amostras magnéticas macias, sugerindo maior potencial magnetotérmico para estes materiais.

In this work we studied the magnetic properties referring to the MgFe2O4 nanoparticles precipitated in monocrystalline solid solution of [Mg, Fe]O, with 2.2% iron, obtained at different temperatures and times. These particles grow coherently with the matrix lattice and present shapes of small octahedrons whose diagonals are parallel to the [100] directions. The results presented here refer to samples treated in the temperature range between 400 and 900 º C for 2, 6 and 10 hours. They were analyzed by X-ray diffraction (XRD), magnetization as a function of field (hysteresis curves) and magnetization as a function of temperature (Zero Field Cooled e Field Cooled Warming). It was observed that in samples treated for 6 hours, the system shows increasing values of magnetization remanent and coercive field for temperatures of precipitation from 600 º C, which can be attributed to the precipitation and growth of nanoparticles magnesioferrite matrix. The variation of coercive field with temperature measurement was studied using two different theoretical models. By comparing the remanent magnetization and coercive field of the samples, it was found that the variation of the inversion parameter of magnesioferrite in the studied range of precipitation temperature decreases as reported by other authors. / Neste trabalho foram estudadas as propriedades magnéticas do sistema de nanopartículas de MgFe2O4 obtidas por precipitação em solução sólida monocristalina de [Mg;Fe]O, com 2,2% de ferro, em diferentes tempos e temperaturas de precipitação. Estas partículas crescem de forma coerente com a matriz, exibindo a forma de pequenos octaedros cujas diagonais são paralelas às direções [100] da rede cristalina da matriz, que possui simetria cúbica. Os resultados aqui apresentados são referentes a amostras tratadas no intervalo de temperaturas entre 400 e 900ºC durante 2, 6 e 10 horas. As mesmas foram analisadas por difração de raios X (DRX), magnetização em função do campo (curvas de histerese) e magnetização em função da temperatura (Zero Field Cooled e Field Cooled Warming). Observou-se que, em amostras tratadas durante 6 horas, o sistema apresenta valores crescentes de magnetização remanente e campo coercivo para temperaturas de precipitação a partir de 600ºC, fato que pode ser atribuído à precipitação e ao crescimento de nanopartículas de magnesioferrita na matriz. A variação do campo coercivo com a temperatura de medição foi estudada utilizando-se dois diferentes modelos teóricos e, a partir da comparação da magnetização remanente e do campo coercivo das amostras tratadas em diferentes temperaturas, verificou-se que a variação do parâmetro de inversão da magnesioferrita na faixa de temperaturas de precipitação estudada decresce como reportado por outros autores.

Submitted by Luciana Ferreira (lucgeral@gmail.com) on 2016-07-25T10:59:35Z No. of bitstreams: 2 Dissertação - Sara Alves Maciel - 2016.pdf: 11054901 bytes, checksum: 8cddf79cb5700731533eb7125fe234a3 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Approved for entry into archive by Luciana Ferreira (lucgeral@gmail.com) on 2016-07-25T11:13:28Z (GMT) No. of bitstreams: 2 Dissertação - Sara Alves Maciel - 2016.pdf: 11054901 bytes, checksum: 8cddf79cb5700731533eb7125fe234a3 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Made available in DSpace on 2016-07-25T11:13:28Z (GMT). No. of bitstreams: 2 Dissertação - Sara Alves Maciel - 2016.pdf: 11054901 bytes, checksum: 8cddf79cb5700731533eb7125fe234a3 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Previous issue date: 2016-04-05 / Fundação de Amparo à Pesquisa do Estado de Goiás - FAPEG / In this work, structural, morphological and magnetic properties of cobalt ferrite/zirconium oxide composites prepared via mechanical mixing of the powders were evaluated. Cobalt ferrite powders were obtained by coprecipitation, and some synthesis parameters were optimized, such as the speed of stirring , the concentration of base and metal solutions, in order to obtain stoichiometric ferrites (Fe3+/Co2+ = 2: 1) or near to it. Zirconium oxide powders were synthesized via sol-gel. The composites were analyzed by Atomic Absorption, Field Emission Scanning Electron Microscopy and Spectroscopy Dispersive Energy, Diffraction of X-rays, Infrared Spectroscopy and Vibranting Sample Magnetometry. It was observed the migration of cations between the ferrite and zirconia structures as a result of high diffusion between phases due to heat treatment. The analysis by Field Emission Scanning Electron Microscopy and Spectroscopy Dispersive Energy showed the different microstructures of aggregates present in the composites and the average diameter of the grains. The insertion of a magnetic phase on a non-magnetic matrix caused an increase in the saturation magnetization and the remanent magnetization, and decrease in coercivity as the cobalt ferrite content increases. / Neste trabalho, foram avaliadas propriedades estruturais, morfológicas e magnéticas de compósitos de ferrita de cobalto/óxido de zircônio, preparados via mistura mecânica dos pós. Os pós de ferrita de cobalto foram obtidos pelo método da coprecipitação, tendo seus parâmetros de síntese otimizados, tais como velocidade de agitação, concentração das soluções de base e dos metais, a fim de se obter ferritas estequiométricas (Fe3+/Co2+ = 2:1) ou próximas disso. Os pós de óxido de zircônio foram sintetizados via sol-gel. Os compósitos foram analisados por Absorção Atômica, Microscopia Eletrônica de Varredura com Emissão de Campo e Espectroscopia por Energia Dispersiva, Difratometria de Raios X, Espectroscopia na Região do Infravermelho e por Magnetometria de Amostra Vibrante. Foi observada a migração de cátions entre as estruturas da ferrita e da zircônia como consequência da alta difusão entre as fases devido ao tratamento térmico. A análise por Microscopia Eletrônica de Varredura com Emissão de Campo e Espectroscopia por Energia Dispersiva permitiu verificar as diferentes microestruturas dos agregados presentes nos compósitos e o diâmetro médio dos grãos. A inserção de uma fase magnética em uma matriz não magnética provocou aumento na magnetização de saturação e na magnetização remanescente, além de uma diminuição na coercividade à medida que o teor de ferrita de cobalto aumenta.

Orientador: Hugo Enrique Hernández Figueroa / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Elétrica e de Computação / Made available in DSpace on 2018-08-26T15:57:35Z (GMT). No. of bitstreams: 1 ArrietaConcha_JoseLuis_M.pdf: 2860251 bytes, checksum: a9513ec6b0227b83e8ccdb097adfef27 (MD5) Previous issue date: 2014 / Resumo: Redes de comunicação ópticas são parte da sociedade de informação de hoje, em que as fibras ópticas têm um papel muito importante, uma vez que são amplamente utilizados em redes de comunicação e outros sistemas de comunicação atuais. No entanto, o uso de dispositivos eletrônicos em várias redes eletro-ópticas representam um grande engarrafamento para a utilização ideal da grande largura de banda e as taxas de dados de alta velocidade permitida por fibras ópticas. A fim de evitar tal congestionamento de tráfego da rede, dispositivos baseados em tecnologias fotônicas são uma das soluções propostas, porque eles fornecem a capacidade de manter altas velocidades de transmissão com taxas elevadas de dados e baixas perdas. Por isso, tais dispositivos fotônicos são continuamente pesquisados, a fim de melhorar a sua eficácia, a obtenção do maior confinamento e encaminhamento do sinal óptico, e melhorar a perda de inserção quando ele é integrado com outros dispositivos. Para alcançar uma maior compreensão dos dispositivos fotônicos, o trabalho apresentado aqui permite uma compreensão pedagógica e ainda completa de cristais fotônicos e efeitos magnéticos. Esta abordagem pedagógica permite uma experiência em mãos para os estudantes e pesquisadores sobre um tema complexo, um tipo de implementação experimental que normalmente exige sofisticados recursos de fabricação fotônicos. A abordagem em micro-ondas permite construir protótipos conceitualmente equivalentes e manipuláveis. Aqui, apresentamos um estudo teórico, análise numérica, modelagem de computador e simulações eletromagnéticas para um circulador de ferrita de 3 portas em uma estrutura de grade fotônico construído para a faixa de micro-ondas de 2,3GHz - 2,9GHz / Abstract: Optical communication networks are part of today¿s information based society, in which optical fibers play a very important role, since they are widely used in such communication networks and other state of the art communication systems. However, the use of electronic devices in various electronic-optical networks represent a major bottleneck for the optimal utilization of the large bandwidth and high speed data rates allowed by optical fibers. In order to avoid such congestion of network traffic, devices based on photonic technologies are one of the proposed solutions, because they provide the capability to maintain transmission speeds with both high data rates and low losses. That is why such photonic devices are continuously being researched in order to improve their effectiveness, obtain greater confinement and guiding of the optical signal, as well as to reduce the insertion loss when it is integrated with other devices. To achieve a greater understanding of photonic devices, the work presented in this paper allow for a pedagogical and yet thorough understanding of photonic crystals and magnetic effects. This pedagogical approach permits a hands-on experience for students and researchers on a complex subject, a kind of experimental implementation that usually demands sophisticated photonic fabrication resources. The microwave approach allows one to construct conceptually equivalent but hand-manipulable prototypes. Here, we present the theoretical study, numerical analysis, computer modeling and electromagnetic simulations for a 3-port ferrite circulator in a photonic grid structure built for the 2.3 GHz to 2.9 GHz microwave range. For a photonic device operating in the optical communication range, we may expect a qualitative analogous behavior / Mestrado / Telecomunicações e Telemática / Mestre em Engenharia Elétrica